WO2005051568A1 - Feeder element for metal casting - Google Patents
Feeder element for metal casting Download PDFInfo
- Publication number
- WO2005051568A1 WO2005051568A1 PCT/GB2004/004451 GB2004004451W WO2005051568A1 WO 2005051568 A1 WO2005051568 A1 WO 2005051568A1 GB 2004004451 W GB2004004451 W GB 2004004451W WO 2005051568 A1 WO2005051568 A1 WO 2005051568A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- feeder element
- feeder
- sidewall
- sleeve
- regions
- Prior art date
Abstract
Description
Claims