WO2005051523A1 - Catalyst for a diesel particulate filter - Google Patents
Catalyst for a diesel particulate filter Download PDFInfo
- Publication number
- WO2005051523A1 WO2005051523A1 PCT/US2004/039704 US2004039704W WO2005051523A1 WO 2005051523 A1 WO2005051523 A1 WO 2005051523A1 US 2004039704 W US2004039704 W US 2004039704W WO 2005051523 A1 WO2005051523 A1 WO 2005051523A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- oxide
- amount
- platinum
- present
- Prior art date
Abstract
Description
Claims