WO2005047021A1 - Plaque de porcelaine a imitation de motifs de pierre tridimensionnels realisee par des motifs de micropoudres, procede de fabrication et produits finis fabriques a partir de ladite plaque - Google Patents

Plaque de porcelaine a imitation de motifs de pierre tridimensionnels realisee par des motifs de micropoudres, procede de fabrication et produits finis fabriques a partir de ladite plaque Download PDF

Info

Publication number
WO2005047021A1
WO2005047021A1 PCT/CN2004/001305 CN2004001305W WO2005047021A1 WO 2005047021 A1 WO2005047021 A1 WO 2005047021A1 CN 2004001305 W CN2004001305 W CN 2004001305W WO 2005047021 A1 WO2005047021 A1 WO 2005047021A1
Authority
WO
WIPO (PCT)
Prior art keywords
pattern
powder
porcelain plate
area
imitation stone
Prior art date
Application number
PCT/CN2004/001305
Other languages
English (en)
French (fr)
Inventor
Dening Yang
Original Assignee
Dening Yang
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dening Yang filed Critical Dening Yang
Priority to EP04797337A priority Critical patent/EP1688271A1/en
Publication of WO2005047021A1 publication Critical patent/WO2005047021A1/zh
Priority to US11/434,123 priority patent/US20060204682A1/en

Description

含微粉图案的三维仿石图案瓷质板材友其制造方法与制品 技术领域
本发明涉及一种陶瓷领域建筑材料中用作装饰材料的仿石装饰板 材及其制造方法与制品， 特别是涉及一种适用于永久性地面、 墙面及 家具面板装饰的仿石图案板材中的含微粉图案的三维仿石图案瓷质板 材及其制造方法与制品。 背景技术 '
当今随着科技的发展和人们生活水平的提高， 作为地面和墙面的 装饰材料， 人们希望其具有天然石材的表面外观, 例如仿花岗石、 大 理石的图案， 以增加产品的高档感。
因此， 业界便不断改进仿天然石材的装饰板材结构，本发明人是在 陶瓷装饰板材领域拥有多项中国及欧、 美、 曰等国外专利的研发者，在陶瓷 领域达十多项专利， 如曾提出一种立体瓷质花岗石、 大理石技术的专利,其 公告号为 WO 97/36840 ( 1997年 10月 9日公开）， 根据该专利技术所制成 的仿石材料， 其表面形成有清晰分界的图案， 并且在进行表面加工时， 其 图案基本上不会变化， 如此能有效提升其整体结构在使用上的稳固性。 然 而这种现有技术描述的仿石材料， 其图案之间.的交界线成垂直状， 使得彩 ,色的图案交界过渡不如真石材一样交混自然， 所以仍然显得不够"天然，，，距 离人们的需求仍有一定的差距。 . 为了满足人们的实用性需求， 本发明人又提出了 "瓷质仿花岗石板材 及其制造方法"的专利， ^^号为 W099/28262 ( 1999年 6月 10日^ ), 该 专利技术虽然可以提供给使用者一更具有实用功效的瓷质仿花岗石板材， 确 实具有进步性， 但是在实际使用时却发现其结构中还存在不足。 根据该技 术的制品只具有其表面的图案， 没有制品在三维空间的图案， 而且没有如 同天然熔岩流动形成图案的质感， 所以产品不能很真实地反映天然花岗石 由里到外的图案质感， 尤其是边部的中下部没有图案效果， 如果在用于家 具台面和建筑装修的墙或柱的外露边缘必须要对边部进行磨边抛光时， 由 于其中、 下部没有与表层为一体的颗粒图案， 所以在实用中较天然石材有 不真实、 不完全的重大缺陷。
. 现有技术中的自由布料产品， 从制品表层到内部的三维空间图案比较 乱， 不能形成如同克隆天然石材一样的从制品表面到制品下部都有稳定的 同一色区的完全均匀一致的彩色图案区域， 故较天然石材亦存在有不能真 实仿真的缺陷。
尽管现有技术的微粉类产品能够产生大小不一、 图案边沿过渡较妤、 小 块图案自然、 有天然大理石、 花岗石中如月牙状内凹的如岩流动出现般特 别图案效果好的特点， 而且有若干大小不一的小色块等优点， 但是， 整块 产品如同只有一个大的色区，不能克隆天然花岗石、 大理石的如同大花白、 大 花绿、 爵士白、 啡钻、 金彩钻、 加州金麻等很有图案规律特点的由 1 到 5 类大的图案区组成的规范图案， 所以其存在有很大局限性。
为了满足人们的实用性需求, 本发明人又曾提出一种 "瓷质粉料烧结 的三维彩色图案板材" 的专利， 其公开号为 CN 1339363A ( 2002年 3月 13 曰公开）， 上述的瓷质粉料烧结的三维彩色图案板材 , 虽提出了其是利用瓷 质彩色原料的粉料， 经压制， 并烧制成的瓷 ^产品，其制品具有不同色彩或 同一色彩但具不同色泽深浅度或不同混合色组成的轮廓清晰的瓷质烧成图 案区,图案区从制品表层到底部厚度的 70%〜 100%区域中都是均匀分布，而 可制成如同天然石材的三维空间的仿石材料； 虽在功效上有很大进步， 能 使粉料在不同色区有规定分布, 有三维效果，但在不同的图案大块区中， 只 能反映一些混合粉料色， 加含大颗粒的图案色或加渗花色的图案色， 而缺 乏天然大理石、 花岗石的图案区中有如同天然熔岩流动时产生的在不同图 案区中的丰富的多边形的、 边沿过渡柔和的、 还有若干内凹月牙状的大图 案区中丰富精细的小图案， 而且还有的精细图案中还会包含另外的小块其 它色图案， 也有的精细小块图案的边沿和二种色区交界， 产生如同天然熔 岩流动之效果， 尤其有这种效果的面积在 1cm2〜 2cm2的精细图案采用本发 明人以前提出的模具模口工艺是不易在大生产中实现的。
综由上述， 现有技术中的仿天然石材的装饰板材都存在有不能真实地 仿制天然石材的缺陷。
为了解决现有的仿天然石材的装饰板材存在的缺陷， 相关厂商莫不费 尽心思来谋求解决之道， 但长久以来一直未见适用的设计被发展完成， 此 显然是相关业者急欲解决的问题。
有鉴于上述现有的仿天然石材的装饰板材存的缺陷，本发明人基于从事 此类产品设计制造多年丰富的实务经验及专业知识，积极加以研究创新， 以期 创设一种新型结构的含微粉图案的三维仿石图案瓷质板材及其制造方法与 制品， 能够改进一般市面上现有常规瓷质仿天然石材的装饰板材结构, 使 其更具有实用性， 经过不断的研究、 设计， 并经反复试作样品及改进后，尤 其为解决微粉的大生产流动性、 配比、 水份和生产设备的技术、 排气、 图 案选择、 色彩配合等复杂问题后， 现在终于创设出确具实用价值的本发明。 发明内容
本发明的主要目的在于， 克服现有的仿天然石材的装饰板材存在 的缺陷， 而提供一种新的含微粉图案的三维仿石图案瓷质板材， 所要 解决的主要技术问题是使其提供一种能够制成具有如同天然石材一样 能在 1 〜 5种大的图案区中能出现微粉特征的并且能在三维空间仿石 材图案的仿石材料，
本发明的另一个目的在于， 提供一种含微粉图案的三维仿石图案 瓷质板材的制造方法。
本发明的再一个目的在于， 提供一种利用含微粉图案的三维仿石 图案瓷质板材制成的制品。
本发明的目的及解决其主要技术问题是采用以下的技术方案来实现 的。 依据本发明提出的含微粉图案的三维仿石图案瓷质板材， 包括色泽明 显可辨的两种不同颜色或相同颜色、不同色泽深浅度的图案 1类区和图案 2 类区， 图案 1类区或图案 2类区的总面积不少于制品表面积的 3%〜 50%; 在图案 1类区或图案 2类区中的 1种或 1〜4种大的图案区之内， 有 1种或 1 ~ 5种颜色、 由 3 ~ 1000个面积在 lcm2 ~ 150cm2、 呈内凹月牙形状的、 多 边形的、 具有微粉料特征的图案， 该内凹月牙状最突出的二个端点连成的 直线与其内凹部最凹点的距离为 1.5mm ~ 10mm;该含獨：粉图案的三维仿石 图案瓷质板材的表层有 20 - 1000个面积在 3mm2〜 1000mm2的、 与内凹月 牙状图案色彩一致的小图案色块， 该图案的三维仿石图案瓷质板材中含有 的 1种或 1 ~ 4种以上色彩明显可辨的、具有微粉料特征的、面积为 lcm2〜 150cm2 的内凹月牙状多边形小图案在图案 1类区或图案 2类区中的数量差别比例为 2：1 ~ 2： 0; 该图案 1类区和 2类区的厚度为 Iran！〜 60mm。
本发明的目的及解决其技术问题还可以采用以下的技术措施来进一步 实现。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 和图案 2类区中各有一种不同色泽的、 面积为 lcm2〜 150cm2的、 具有微粉 料特征的多边形内凹月牙状的小图案。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的
所述的图案 1类区内有一种不同色泽的、 面积为 lcm2〜 150 cm2、 具有 微粉料特征的多边形内凹月 牙状的小图案； 所述的图案 2类区 内含有与图案 1 类区微粉料特征的内 凹月 牙状小图案的色彩 '不同的、 占表层面积 1 0% 〜 70%的、 直径为 2mm〜20mm的颗粒。
前述的含 粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 和 /或图案 2类区中的图案的块数为 50〜 3000 ik,该图案的长宽比例不大于 3。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 和 /或图案 2类区的形状为互相联结的网状， 该类图案区的 1 〜 20个网状支 部伸延到含 t粉图案的三维仿石图案瓷质板材的四个边部。 前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的含微粉图案 的三维仿石图案瓷质板材的剖面具有不同颜色的 6〜 20条相交线,该相交线 从所述的含^:粉图案的三维仿石图案瓷质板材的的表层伸延至其下部，其伸 延的长度为所述的含微粉图案的三维仿石图案瓷质板材厚度的 80% ~ 100%。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 70% - 100%的面积为纯白色或纯黑色或深兰色的图案区； 图案 2类区为含 有浅灰色的或浅灰兰色或黑色或黄色的图案区， 并含有 10 - 3000个具有微 粉料特征的内凹月牙状的小块图案。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 和图案 2类区各自的总面积， 不少所述的含微粉图案的三维仿石图案瓷质 板材的表面积的 10%〜 90%。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 或图案 2类区中，有 6块以上大的色块图案区的形状和位置在所述含微 粉图案的三维仿石图案瓷质板材的表面是可以叠合的，其在表层图案 的上、 下、 左、 右位置的叠合误差不超过 ± 5cm。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的的含有微粉 特征的多边形内 月牙状小图案的边沿与至少 2种或 2 - 5种颜色的粉料区 或小的含有 粉特征的图案块交界。
前述的含^:粉图案的三维仿石图案瓷质板材， 其中所述的含微 #分图案 的三维仿石图案瓷质板材中有 1块或 1 〜 1000块含有微粉特征的多边形小 图案包围了另一块其它颜色的更小块的图案。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的具有微粉特 征的内凹月牙状图案的最突出的二个点连成的直线与其内凹部最凹点的距 离为 3 mm〜 10mm。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的由瓷质材料 所组成的含微粉料特征的图案， 是由含有直径在 0.1mm 〜 0.3mm的细小粉 料烧结而成的图案。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 和图案 2类区中， 含有 1 - 5种直径为 1.5mm〜 20mm的彩色颗粒材料， 该 彩色颗粒材料占所述含微粉图案的三维仿石图案瓷质板材的表面积的 2% ~ 80%。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的图案 1 类区 和图案 2类区中， 含有直径为 lmm〜 5mm的花岗石颗粒。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的含微粉图案 的三维仿石图案瓷质板材的表平面为不抛光的表平面和 /或抛光的表平面。
前述的含微粉图案的三维仿石图案瓷质板材,其中所述的表平面上， 设 有由深度为 0.1mm 〜 5mm凹凸防滑图案与之配合组成有立体感的图案^ ¾ 其凸出的表平面图案部分为抛光的表平面和 /或不抛光的表平面。 .
前述的含微粉图案的三维仿石图案瓷质板材,其中所述的含微粉图案的 三维仿石图案瓷质板材的整体几何形状为平面板形、 圆柱形、 弧面板形、局部 圆柱形、 球形、 半球形、 锥圆状半球形或由平面与半锥圆状或半圆状组合 而成型的任一形状。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的含微粉图案 的三维仿石图案瓷质板的瓷质图案区域中， 具有玻璃相成份大于 70%的无 色透明、 半透明、 或者黑、 绿、 白、 紫、 啡、 蓝、 红、 黄类色彩的透明或 不透明或高折光率的有闪烁性能的硅酸盐成份的图案。
前述的含微粉图案的三维仿石图案瓷质板材， 其中所述的含微粉图案 的三维仿石图案瓷质板的瓷质图案区域中含有渗花色图案。
本发明提出的含微粉图案的三维仿石图案瓷质板材 , 可以通过下 方 法进行制造,该制造方法包括以下步骤:
将直径为 0.1mm〜 0.3mm的 1种或 1 〜 10种明显可辨的、 不同装饰颜 色的、 彩色的、 流动性不好的微粉原料， 与不同颜色的或相同颜色不同色 泽深浅的流动性较好的普通瓷质砖粉料进行混合；
通过一个与每一种大的、 与所需图案形状一样的平面模板图案的空洞 区入口， 根据大图案区种类的多少， 采用相对应种类的不同的模板， 按每 一类不同的大图案区与所需图案色类型、 数量， 分次进入或落入一个预定 的图案格栅模具或一个平面载体中， 并保持其含微粉特征的彩色图案区的 平面形状；
然后再送入并落入冲压成型模具模框中， 经陶瓷压机冲压成型， 得到 砖坯， 经烘干、 烧成、 抛光得到含 ^敖粉图案的三维仿石图案瓷质板材。. 同时， 本发明还提供了一种利用含微粉图案的三维仿石图案瓷质板材 制成的制品， 该制品的上层为具有含微粉图案的三维仿石图案瓷质板材的 厚度为 1mm ~ 15mm的瓷质材质层， 下层是厚度为 1mm〜 15mm的普通单 色或含有 1 〜 5个色的瓷质材质层。
上述说明仅是本发明技术方案的概述， 为了能够更清楚了解本发明的 技术手段， 并可依照说明书的内容予以实施， 以下以本发明的较佳实施例 并配合附图详细说明如后。
附图说明
图 1 是本发明的仿大花绿大理石第 1 实施例和第 2 实施例的尺寸为 600mm 600mm的制品的平面结构示意图。 N2004/001305 图 2是本发明笫 1实施例和第 2实施例的不同色彩的色区交界线和微 粉图案的平面局部放大部分的结构示意图。
图 3是本发明第 1 实施例的不同色彩的色区交界线和微粉图案的厚度 为 10mm的制品剖面局部放大部分的结构示意图。
图 4是本发明含微粉图案的三维仿石图案瓷质板材及其制造工艺方法 的制品第 2 实施例的上层为不同色彩的色区交界线和微粉图案的剖面局部 放大部分和下部为普通瓷质粉料的结构示意图。
图 5是本发明第 1实施例和第 2实施例所必须的钢材质的模口模具的 平面结构示意图。
1、 瓷质材料的墨绿色图案区
2、 瓷质粉料绿、 灰二种混合烧结的色区
- 3、 瓷质材料的黑色色区
4、 黑色微 的有内凹月牙状的多边形状的烧结图案区
5、 灰色的又一种小块微粉区
6、 面积为 3mm2〜 1000mm2的黑色小粉料色块
7、 普通黑、 绿混合的瓷质砖粉料烧结区 '
8、 瓷质粉料绿、 灰粉料烧结区色 2与墨绿色区 1， 两类粉料自然交混 而形成的二种颜色的粉料自然交混的过渡区
10、 组合模具
101、 墨绿色料的模口通过区
102、 绿、 灰二种混合粉料和灰色、 黑色二种微粉料的模口通过区
103、 黑色粉的模口通过区
104、 平面俯视位置的钢质模口 具体实施方式
下面结合附图及较佳实施例， 对依据本发明提出的含微粉图案的三维 仿石图案瓷质板材及其制造方法与制品的具体实施方式、 结构、 特征及其 功效， 详细说明如后。
请参阅图 1 所示， 是本发明含微粉图案的三维仿石图案瓷质板材的仿 大花绿大理石第 1实施例和第 2实施例的尺寸为 600mm X 600mm的制品的 平面结构示意图。 大黑点部分的图案区 1 表示是瓷质材料的墨绿色区； 小 黑部分的图案区 2表示是瓷质粉料绿、 灰二种混合烧结的色区； 斜线部分 的图案区 3表示是瓷质材料的黑色色区； 大的十字交叉部分图案区 4表示 黑色微粉的有内凹月牙状的多边形状的烧结图案区； 黑色部分图.案区 5表 示灰色的又一种小块微粉区； 小的十字交叉部分图案区 6表示面积为 3mm2 - 1000mm2的黑色小粉料色块； 还可见到图案区 5与月牙状的大的 十字交叉部分图案区 4 以及图案区 2边沿相交， 形成自然的流动状 ί青细图 案。
请参阅图 2所示,是本发明含微粉图案的三维仿石图案瓷质板材第 1实 施例和第 2 实施例的不同色彩的色区交界线和微粉图案的平面局部放大部 分的结构示意图。 大黑点部分的图案区 1 表示是瓷质材料的墨绿色区； 小 黑部分的图案区 2表示是瓷质粉料绿、 灰二种混合烧结的色区； 二条虚线 之间的部分表示墨绿色区 1和绿、 灰粉料烧结区 .2 自然交混而形成的二种 色的粉料自然交混的过渡区 8, 该过渡区 8的交混比例为 1： 5 〜 3： 5; 大 的十字交叉部分图案区 4表示黑色微粉的有内凹月牙状的多边形状的烧结 图案区； 黑色部分图案区 5 表示一种灰色的小块 吏粉区； 小的十字交叉部 分图案区 6表示面积为 3mm2〜 1000mm2的黑色小粉料色块； 还可见到图案 区 5与月牙状的大的十字交叉部分图案区 4以及图案区 2边沿相交， 形成 自然的流动状精细图案。 小黑色块 5表示被黑色敖粉图案区 4包围的灰色 微粉图案块区。
请参阅图 3 所示， 是本发明含微粉图案的三维仿石图案瓷质板材第 1 实施例的不同色彩的色区交界线和微粉图案的厚度为 10mm的制品剖面局 部放大部分的结构示意图。 大黑点部分的图案区 1 表示是瓷质材料的墨绿 色区； 小黑部分的图案区 2表示是瓷质 绿、 灰 、； ¾^烧结的色区； 二条 虚线之间的部分表示墨绿色区 1和绿、 灰粉料烧结区 2 自然交混而形成的 二种颜色的粉料自然交混的过渡区 8, 该过渡区 8的交混比例达 1： 5 ~ 3： 5以 内；大的十字交叉部分图案区 4表示黑色微粉的有内凹月牙状的多边形状的 烧结图案区； 黑色部分图案区 5表示灰色的又一种小块敫粉区； 小的十字 交叉部分图案区 6表示面积为 3mm2 ~ 1000mm2的黑色小粉料色块。
请参阅图 4所示， 是本发明含微粉图案的三维仿石图案瓷质板材的制 品第 2 实施例的上层为不同色彩的色区交界线和微粉图案的剖面局部放大 部分和下部为普通瓷质粉料的结构示意图。 上层为 5mm厚， 下层也为 5mm 厚。 大黑点部分的图案区 1 表示是瓷质材料的墨绿色区； 小黑部分的图案 区 2表示是瓷质粉料绿、 灰二种混合烧结的色区； 二条虚线之间的部分表 示墨绿色区 1和绿、 灰粉料烧结区 2 自然交混而形成的二种色的粉料自然 交混的过渡区 8， 该过渡区 8的交混比例达 10： 50到 30： 50以内； 大的十 字交叉部分图案区 4表示黑色微粉的有内凹月牙状的多边形状的烧结图案 区； 黑色部分图案区 5 表示灰色的又一种小块敫粉区； 小的十字交叉部分 图案区 6表示面积为 3mm2 ~ 1000mm2的黑色小粉料色块； 下层的圆圈图案 部分表示制品下层部分厚度为上层厚度 50%的 5mm厚的普通黑、 绿混合的 瓷质砖粉料烧结区 7。 请参阅图 5所示， 是本发明含微粉图案的三维仿石图案瓷质板材的制 造方法的第 1实施例和第 2实施例所必须的钢材质的模口模具 10的平面结 构示意图。 大黑点部分表示墨绿色料的模口通过区 101; 小黑部分表示绿、灰 二种混合粉料和灰色、 黑色二种微粉料的模口通过区 102; 斜线部分表示是 黑色粉的模口通过区 103; 粗黑线部分表示钢质模口平面 104的俯视位置。 实施例 1
现将本发明含微粉图案的三维仿石图案瓷质板材的制造方法， 其制造 过程包括以下一些步骤： '
( 1 )瓷质墨绿色粉料 1为第一组； 第二组为绿、 灰色料各 40%, 加入 10%直径在 0.1mm - 0.3mm的黑色微粉料和 10%的直径在 0.1mm 〜 0.3mm 的灰色微粉料， 第三组为黑色粉料， 把三组材料分别装入三个容器之中；
( 2 )再将一套按产品规定图案形状制造的具有三个大图案色区的模口 的组合模具 10放在容器之下，其中第一组落入墨绿色料的模口通过区 101大 图案区， 第二组落入绿、 灰二种混合粉料和灰色、 黑色二种微粉料的模口 通过区 102大图案区， 第三组落入黑色粉料的模口通过区 103大图案区；
( 3 )使各种色的原材料按图 5的规定， 每一个大图案区一次， 分三次 把三个区的原材料落入、 注入、 装入各自模具格栅区域； 或者使各种色的 原材料按图 5 的规定， 用管路把三个区的原材料同时落入、 注入、 装入各 自模具格栅区域；
( 4 )用高速机械动作在平面上前、 后、 左、 右方向运动或振动钢材质 模具 10, 形成不同色区域的粉料在交界处有一定自然交混状， 形成十分真 实地仿大花绿大理石图案的三维结构， 使各色粉料和微粉按图案要求通过 組合模具 10的模口落入压机的冲压模框内。 由于小直径的微粉流动性不佳 且水份较多的原因，在混合中会出现混不均匀而成粘合状的多边形块状， 从 而形成了在模具格栅区域控制中的大图案区中的小图案区， 使其如同天然 熔岩流动时产生的在不同图案区中的丰富的多边形的图案， 能控制出 现边沿过渡柔和的、 有若干内凹月牙状的丰富精细的微粉小图案， 而 且还有的精细图案中还会包含另外的小块其它色图案， 也有的精细小 块图案的边沿和二种色区交界， 产生如同天然熔岩流动之效果， 而使 这些效果有控制地分别进入设计的大图案区中 , 这是本发明的皮明 点， 由此可以仿制出很多不同类型的精美的石材三维图案效果；
( 5 )以 3000T陶瓷压机冲压成型， 然后在 60米长的、 温度在 100°C~20(rC的供干窑中洪干，再在 130米长的 ¾A窑中经 1200 °C~ 122(TC温度 区烧制成制品成品
从实施例的图 1可见， 在大图案区 2中， 面积超过 lcm2的呈内凹 月牙状的具有 粉特征的黑色图案区 4的内凹深度为 3mm以上， 其黑色图 案区 4在一块制品中达 3块以上， 而且面积超过 3mm2的小黑色图案块 6 达 20块以上； 从其与其它大图案区的比较可见， 黑色图案大区 3区和墨绿 色图案大区 1区中， 都没有大图案区 2区中的黑色有救粉特征的面积超过 1 cm2的有内凹月牙状而且内凹深度在 3mm以上的黑色图案 4, 可见 大图案区 2与另一类大图案区 1和 3之间， 这种黑色的有微粉特征的 图案的数量差别比例为 2： 0〜 3： 0。 从实施例可见， 由此形成了仿石大 图案区之间的反差， 因为在天然石中， 这种月牙状的多边形小图案如同岩 浆流动一样， 在不同大区图案之中如同小的有微粉特征的图案色泽都不一 样， 不会形成在各个大图案区中小的自然流动色块都是一种色彩的情况， 这是仿 高档天然石的图案差别的重要特征所在。 还因为如果各大区中的小图案如 果都是一色， 或同一数量比例， 则其就没有高档仿石效果的漂亮的大图案 区别自然组合之效果。 本领域的技术人员可以理解， 形成上述红、 黄、 白、 蓝、 黑、 绿、 橙、 紫等不同色的硅酸盐转体色块可以例如通过釆用或 加入 F e203、 Na20、 V205、 CoO 、 Mn02、 Cr203、 CuO等来实现。 实施例 2
现将本发明含微粉图案的三维仿石图案瓷质板材的制造方法， 其制造 过程包括一下一些步骤：
( 1 )先将压机冲压模具框内装入 50%厚度的绿、 黑二色混合的普通粉 料；
( 2 )瓷质墨绿色粉料 1为笫一组； 第二组为绿、 灰色料各 40%, 加入 10%直径在 0.1mm ~ 0.3mm的黑色微粉料和 10%的直径在 0.1mm〜 0.3mm 的灰色微粉料， 第三组为黑色粉料， 把三组材料分别装入三个容器之中；
( 3 )再将一套按产品规定图案形状制造的具有三个大图案色区的模口 的组合模具 10放在容器之下： 其中第一组落入墨绿色料的模口通过区 101 大图案区， 第二组落入绿、 灰二种混合粉料和灰色、 黑色二种微粉料的模 口通过区 102大图案区， 第三组落入.黑色粉料的模口通过区 103大图案区。
( 4 )使各种色的原材料按图 5的规定， 每一个大图案区一次， 分三次 把三个区的原材料落入、 注入、 装入各自模具格栅区域； 或者使各种色的 原材料按图 5 的规定， 用管路把三个区的原材料同时落入、 注入、 装入各 自模具格栅区域；
( 5 )用高速机械动作在平面上前、 后、 左、 右方向运动或振动钢材质 模具 10, 形成不同色区域的粉料在交界处有一定自然交混状， 形成十分真 实地仿大花绿大理石图案的三维结构， 使各色粉料和微 4分按图案要求通过 组合模具 10的模口落入压机的冲压模框内。 由于小直径的微粉流动性不佳 且水份较多的原因，在混合中会出现混不均匀而成粘合状的多边形块状， 从 而形成了在模具格栅区域控制中的大图案区中的小图案区， 使其如同天然 熔岩流动时产生的在不同图案区中的丰富的多边形的图案， 能控制出 现边沿过渡柔和的、 有若干内凹月牙状的丰富精细的微粉小图案， 而 且还有的精细'图案中还会包含另外的小块其它色图案， 也有的精细小 块图案的边沿和二种色区交界， 产生如同天然熔岩流动之效果， 而使 这些效果有控制地分别进入设计的大图案区中， 这是本发明的发明 点， 由此可以仿制出很多不同类型的精美的石材三维图案效果。
( 6 ) 以 3000T 陶瓷压机冲压成型， 然后在 60 米长的温度在 100°C~200°C的烘干窑中烘干， 再在 130米长的烧成窑中经 1200° (〜 1220°C温度 区烧制成制品成品。 '
从实施例 2的图 1可见， 在大图案区 2中， 面积超过 lcm2的呈内 凹月牙状的有孩史粉特征的黑色图案区 4的内凹深度为 3mm以上， 其黑色图 案区 4在一块制品中达 3块以上， 而且面积超过 3mm2的小黑色图案块 6 达 20块以上； 从其与其它大图案区的比较可见， 黑色图案大区 3区和墨绿 色图案大区 1区中， 都没有大图案区 2区中的黑色有^:粉特征的面积超过 1 cm2的有内凹月牙状而且内凹深度在 3mm以上的黑色图案 4 , 可见 大图案区 2与另一类大图案区 1和 3之间， 这种黑色的有微粉特征的 图案的数量差别比例为 2： 0〜 3： 0。 从实施例 2可见， 由此形成了仿石 大图案区之间的反差， 因为在天然石中， 这种月牙状的多边形小图案如同 岩浆流动一样,在不同大区图案之中如同小的有微粉特征的图案色泽都不一 样， 不会形成在各个大图案区中小的自然流动色块都是一种色彩的情况， 这是仿 高档天然石的图案差别的重要特征所在。 还因为如果各大区中的小图案如 果都是一色， 或同一数量比例， 则其就没有高档仿石效果的漂亮的大图案 区别自然组合之效果。 本领域的技术人员可以理解， 形成上述红、 黄、 白、 蓝、 黑、 绿、 橙、 紫等不同色的硅酸盐砖体色块可以例如通过采用或 加入 F e203、 Na20、 V205、 CoO 、 Mn02、 Cr203、 CuO等来实现。 产业上的利用性
本发明与现有技术相比具有明显的优点和有益效果。 由以上技术方案 可知， 为了达到前述发明目的， 本发明的主要技术内容如下：
将瓷质彩色原料的粉料和微粉料， 经压制， 并烧制而形成一种新 的板材制品， 使彩色瓷质类硅酸盐原料的局部分布的密度和位置在制 品内部三维空间能按天然石材图案的特征， 进行有控制的制造， 从而 具有能够真实地仿制天然石材的优良功效。 同时又能在克隆天然石的 图案区域中出现各种彩色大图案区中的具有微粉特征的小图案， 即能 如同天然熔岩流动时产生的边沿过渡很好,形态丰富多彩的多边形、 多 棱形图案， 还会有若干内凹月牙状的或多月牙状的丰富精细图案。 另 外， 有的精细图案中还包含了其他色彩的小块图案， 也有的精细小块 图案的边沿不是和一种色区交界， 而是和二种或二种以上更多的色区 犬牙交错地交界， 产生如同天然熔岩流动的效果， 尤其在瓷质材料微 粉加工的过程中， 加入含有 0.1mm - 0.25mm的细小粉料， 能够达到微 粉边沿过渡的效果， 同时通过流动性差异的效果， 达到制造出瓷质材 料微粉工艺特征的仿天然熔岩流动效果的目的， 从而能够更真实地仿 制诸如大理石中的大花白、 爵士白、 大花绿、 万寿红、 香槟红、 #罗 红、 银海米黄、 挪威红以及花岗石类的金彩钻、 金彩麻、 啡钻、 绿钻、 幻 彩红、 幻彩绿等天然经典石材。
经过上述可知， 本发明和现有技术相比， 至少具有如下的一些优点： ( 1 )本发明提出的含微粉图案的三维仿石图案瓷质板材， 更能表现 出不同的在大的图案区中出现天然石材熔岩流动形成的若干不同色彩的犬 牙交错的小图案自然效果； 材料仿诸如大花白、 雪花白、 大; ^录、 皇 室啡、 加州金麻等等顶级石材、 玉石等有规律的三维彩色规范图案， 又能 在不同大图案区中克隆出仿熔岩流动的不同色的犬牙交错的自然小图案； 同 时本发明制品比天然石材还具有吸水率低、 色差小、 光洁度高、 无放射性 元素污染等优点， 而成为一种相当具有实用性及进步性的新设计， 适亍产 业界广泛推广应用。
( 2 )本发明提出的含微粉图案的三维仿石图案瓷质板材的制造方 法， 可以在不同的大的由模具图案可控制而形成的大图案区中， 加入 不同色的微粉料， 形成不同区域中的不同的色彩的有微粉特征的如火 山熔岩流动的小图案效果， 尤其仿制大花绿、 中花绿、 万寿红等高级 大理石的效果特别好。
( 3 ) 本发明提出的含微粉图案的三维仿石图案瓷质板材的制造方 法， 可以在不同的大的由模具图案可控制而形成的大图案区中， 在图 案 1类区中加入一种颜色的微粉料， 形成这一区域中具有微粉特征的 如火山熔岩流动的小图案效果， 在图案 2类区中加入另一种色的占其 表层制品面积 10% 〜 70%的、 直径在 2mm 〜 20mm的颗粒料， 可以使 仿花岗石的块状部分层次丰富， 形成更好的表现效果。
( 4 ) 本发明提出的含微粉图案的三维仿石图案瓷质板材的制造方 法， 可以在不同的大的由模具图案可控制而形成的大图案区中， 加入 微粉料， 以形成大图案区域中具有微粉特征的如火山熔岩流动的小图 案效果， 又把这类由模具模口形状所规范的大图案区控制在长宽比不 超过 3倍的范围， 同时使图案呈团状、 长方状、 椭圆状等， 对仿制品 钻类花岗石如金彩钻、 绿钻、 啡钻等图案密集的天然高级石材， 有更 好的效果。
( 5 ) 本发明提出的含微粉图案的三维仿石图案瓷质板材的制造方 法， 可以在不同的大的由模具图案可控制而形成的大图案区中， 图案 1类区 70%〜 100%面积为纯白色或纯黑色或深兰色的大图案区， 在另 一类含有浅灰或浅灰兰色或黄色或黑色的图案 2类区的网状区的部分 中， 加入微粉料， 形成有微粉特征的如火山熔岩流动的内月牙状的小 块图案，用于仿制大花白、 爵士白、 黑金花、 兰金花等高级大理石， 有 特别好的效果。
( 6 ) 本发明提出的含微粉图案的三维仿石图案瓷质板材可以在两 种大的图案 1类区和图案 2类区中，有一类图案区形状呈互相^ ^的网 该类 图案区的 1 〜 20个网状支部伸延到了制品的四个边部。 这种工艺产品鲒构 的创新在于运用了本发明人的模板模具技术加入了微粉工艺仿一切网状大 理石，微粉特征可以在网状区中出现,也可以在网状包围的块区中出现,还可以 在网状区、 块状区二类区域同时都出现； 其仿制网状的中花绿、，啡网紋、 紫罗红等大理石效果可达克隆仿真水平。
( 7 )本发明提出的含微粉图案的三维仿石图案瓷质板材对仿天然大 理石、 花岗石装饰板材的结构进行了进一步的改进,其结构仿真性极佳, 且 比天然石还具有吸水率低、 色差小、 光洁度高、 无放射性元素污染的优点，在 使用上更加适于实用， 且可以借由机械加工大批量工业化生产， 使得制造 成本相对减少， 符合经济效益， 而相当具有产业的广泛利用价值。
( 8 )本发明提出的含微粉图案的三维仿石图案瓷质板材， 可以在 两种大的 1类区和 2类区图案区域中,对制品从平面图案向下切割， 最 少可得到一个剖面的不同色的 6 〜 20条相交线是从制品的 ^^伸延到达了制品 的下部， 其相交线伸延的长度达到了制品厚度的 80% ~ 100%, 而这是现有技 术的一切微粉制品不可能实现的， 因为现有技术的 粉图案只在制品的 表层， 而且没有大的不同色的规范图案区， 而本发明大的图案区粉料色 的相交线在三维空间的深度， 为在制造仿大理石图案的家具台面板材或 工程应用中的制品边际打磨、 抛光处理时， 独特地提供了仿真天然大理 石的三维图案的表现力。
综上所述， 本发明含微粉图案的三维仿石图案瓷质板材及其制造方法 与制品相较于现有的仿天然石材更能在仿制天然石材克隆各种色区大的规 范图案之中， 进一层克隆存在于大的不同色区图案之中的有微粉特征的如 同天然石材之若干中、 小形态的熔岩流动形成的自然效果， 而且大的图案 区是呈现三维空间结构， 这是本发明的主要发明点所在， 是对以前本人众 多发明的提升。 本发明制品同时比天然石材还具有吸水率低、 色差小、 光 洁度高、 无放射性元素污染等优点， 是一种适于产业界广泛推广应用， 相 当具有新颖、 实用及进步性的新设计。
以上所述， 仅是为了说明本发明的较佳优选实施例而已， 然而其并非 是对本发明的限制， 任何熟悉本项技术的人员可能利用上述提示的技术内 容加以变更或修饰为等同变化的等效实施例， 都可以按不同要求的图案和 性能作出含微粉图案的三维仿石图案瓷质板材及其制造工艺方法。 可见,凡 是未脱离本发明技术方案的内容， 依据本发明的技术实质对以上实施例所 作的任何简单修改， 等同变化与修饰， 均仍属本发明技术方案的范围内。

Claims

权利 要 求
1、 一种含獨:粉图案的三维仿石图案瓷盾板材， 包括色泽明显可辨的两 种不同颜色或相同颜色、 不同色泽深浅度的图案 1类区和图案 2类区， 图 案 1类区或图案 2类区的总面积不少于制品表面积的 3% - 50%; 在图案 1 类区或图案 2类区中的 1种或 1 〜 4种大的图案区之内， 有 1种或 1 ~ 5种 颜色、 由 3 〜 1000个面积在 1cm2 ~ 150cm2.呈内凹月牙形状的、 多边形的、 具有微粉料特征的图案， 该内凹月牙状最突出的二个端点连成的直线与其 内凹部最凹点的距离为 1.5mm ~ 10mm;该含微粉图案的三维仿石图案瓷质 板材的表层有 20〜 1000个面积 '在 3mm2 ~ 1000mm2的、 与内凹月牙状图案 色彩一致的小图案色块, 其特征在于该图案的三维仿石图案瓷质板材中含 有的 1种或 1 〜 4种以上色彩明显可辨的、 具有凝:粉料特征的、 面积为 lcm2〜 150cm2的内凹月牙状多边形小图案在图案 1类区或图案 2类区中的 数量差别比例为 2： 1〜2： 0; 该图案 1类区和 2类区的厚^ lmm~60mm。
2、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特 征在于其中所述的图案 1类区和图案 2类区中各有一种不同色泽的、 面积 为 lcm2〜 150cm2的、 具有微粉料特征的多边形内凹月牙状的小图案。
3、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特 征在于其中所述的图案 1类区内有一种不同色' ^、面积为 lcm2〜 150cm2、具 有微粉料特征的多边形内凹月牙状的小图案； 所述的图案 2类区内含有与 图案 1类区微粉料特征的内凹月牙状小图案的色彩不同的、 占表层面 积 10% ~ 70%的、 直径为 2mm ~ 20imn的颗粒。
4、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特
Figure imgf000016_0001
1类区和 /或图案 2类区中的图案的块数为 50 - 3000块， 该 图案的长宽比例不大于 3。
5、根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材,其特征 在于其中所述的图案 1类区和 /或图案 2类区的形状为互相 吉的网 该类图 案区的 1 〜 20个网状支部伸延到含微粉图案的三维仿石图案瓷质板材的四 个边部。
6、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特 征在于所述的含微粉图案的三维仿石图案瓷质板材的剖面具有不同颜色的 6〜 20条相交线，该相交线从所述的含微粉图案的三维仿石图案瓷质板材的 的表层伸延至其下部， 其伸延的长度为所述的含 分图案的三维仿石图案 瓷质板材厚度的 80%〜 100%。
7、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特 征在于其中所述的图案 1类区 70% ~ 100%的面积为纯白色或纯黑色或深兰 色的图案区； 图案 2类区为含有浅灰色的或浅灰兰色或黑色或黄色的图案 区， 并含有 10 ~ 3000个具有微粉料特征的内凹月牙状的小块图案。
8、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特 征在于其中所述的图案 1类区和图案 2类区各自的总面积， 不少所述的含 微粉图案的三维仿石图案瓷质板材的表面积的 10%〜 90%。
9、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特 征在于其中所述的图案 1类区或图案 2类区中， 有 6块以上大的色块图案 区的形状和位置在所述含微粉图案的三维仿石图案瓷质板材的表面是可以 叠合的， 其在表层图案的上、 下、 左、 右位置的叠合误差不超过 ± 5cm。
10、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的含有微粉特征的多边形内凹月牙状小图案的边沿与至 少 2种或 2 - 5种颜色的粉料区或小的含有微粉特征的图案块交界。 '
11、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的含微粉图案的三维仿石图案瓷质板材中有 1块或 1块 -1000 块含有微粉特征的多边形小图案包围了另一块其它颜色的更小块的 图案。
12、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材, 其 特征在于其中所述具有微粉特征的内凹月牙状图案的最突出的二个点连成 的直线与其内凹部最凹点的距离为 3mm〜 10mm。
13、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的由瓷质材料所组成的含微粉料特征的图案， 是由含有 直径在 0. lmm〜 0.3mm的细小粉料烧结而成的图案。
14、 根据权利要求 1所述的含微粉图案的三维仿石图案瓷质板材， 其特征在于 其中所述的图案 1类区和图案 2类区中， 含有 1 - 5种直径为 1.5mm〜 20mm的彩 色颗粒材料， 该彩色颗粒材料占所述含微粉图案的三维仿石图案瓷质板材 的表面积的 2% ~ 80%。
15、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特^于其中所述的图案 1类区和图案 2类区中， 含有直径为 lmm〜5mm的花 岗石颗粒。
16、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的含微粉图案的三维仿石图案瓷质板材的表平面为不抛 光的表平面和 /或抛光的表平面。
17、 根据权利要求 16所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的表平面上， 设有由深度为 0.1mm〜 5mm凹凸防滑图案 与之配合组成有立体感的图案结构， 其凸出的表平面图案部分为抛光的表 平面和 /或不抛光的表平面。
18、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的含微粉图案的三维仿石图案瓷质板材的整体几何形状 为平面板形、 圆柱形、 弧面板形、 局部圓柱形、 球形、 半球形、 锥圓状半 球形或由平面与半锥圆状或半圆状组合而成型的任一形状。
19、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的含微粉图案的三维仿石图案瓷质板的瓷质图案区域 中， 具有玻璃相成份大于 70%的无色透明、 半透明、 或者黑、 绿、 白、 紫、 啡、 蓝、 红、 黄类色彩的透明或不透明或高折光率的有闪烁性能的硅酸盐 成份的图案。
20、 根据权利要求 1 所述的含微粉图案的三维仿石图案瓷质板材， 其 特征在于其中所述的含微粉图案的三维仿石图案瓷质板的瓷质图案区域中 含有渗花色图案。
21、 一种制备含微粉图案的三维仿石图案瓷质板材的制造方法， 其特 征在于该制造方法包括以下步骤：
将直径为 0.1mm〜 0.3mm的 1种或 1 ~ 10种明显可辨的、 不同装饰颜 色的、 彩色的、 流动性不好的微粉原料， 与不同颜色的或相同颜色不同色 泽深浅的流动性较好的普通瓷质砖粉料进行混合；
通过一个与每一种大的、 与所需图案形状一样的平面模板图案的空洞 区入口， 根据大图案区种类的多少, 采用相对应种类的不同的模板 , 按每 一类不同的大图案区与所需图案色类型、 数量， 分次进入或落入一个预定 的图案格栅模具或一个平面载体中， 并保持其含^：粉特征的彩色图案区的 平面形状；
然后再送入并落入冲压成型模具模框中， 经陶瓷压机冲压成型， 得到 砖坯， 经烘干、 烧成、 抛光得到含微粉图案的三维仿石图案瓷质板材。
22、一种利用含微粉图案的三维仿石图案瓷质板材制成的制品 ,其特 于 其上层为具有含微粉图案的三维仿石图案瓷质板材的厚度为 lmm〜 15mm的瓷 质材质层，下层为普通单色或含有 1-5个色的厚度为 lmm〜 15mm的瓷质材质层。
PCT/CN2004/001305 2003-11-17 2004-11-16 Plaque de porcelaine a imitation de motifs de pierre tridimensionnels realisee par des motifs de micropoudres, procede de fabrication et produits finis fabriques a partir de ladite plaque WO2005047021A1 (fr)