WO2005035257A1 - Elastomeric stamp, patterning method using such a stamp and method for producing such a stamp - Google Patents
Elastomeric stamp, patterning method using such a stamp and method for producing such a stamp Download PDFInfo
- Publication number
- WO2005035257A1 WO2005035257A1 PCT/IB2004/052010 IB2004052010W WO2005035257A1 WO 2005035257 A1 WO2005035257 A1 WO 2005035257A1 IB 2004052010 W IB2004052010 W IB 2004052010W WO 2005035257 A1 WO2005035257 A1 WO 2005035257A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- stamp
- ink
- elastomeric stamp
- barrier layer
- elastomeric
- Prior art date
Abstract
Description
Claims