WO2005023031A1 - Gants en chlorure de polyvinyle ayant une resistance chimique amelioree - Google Patents
Gants en chlorure de polyvinyle ayant une resistance chimique amelioree Download PDFInfo
- Publication number
- WO2005023031A1 WO2005023031A1 PCT/US2004/019858 US2004019858W WO2005023031A1 WO 2005023031 A1 WO2005023031 A1 WO 2005023031A1 US 2004019858 W US2004019858 W US 2004019858W WO 2005023031 A1 WO2005023031 A1 WO 2005023031A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glove
- barrier layer
- mass
- layer
- substrate body
- Prior art date
Abstract
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP04776878A EP1657989A1 (fr) | 2003-08-27 | 2004-06-18 | Gants en chlorure de polyvinyle ayant une resistance chimique amelioree |
JP2006524626A JP2007503532A (ja) | 2003-08-27 | 2004-06-18 | 耐薬品性が向上したポリ塩化ビニル手袋 |
CA002535907A CA2535907A1 (fr) | 2003-08-27 | 2004-06-18 | Gants en chlorure de polyvinyle ayant une resistance chimique amelioree |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/649,549 | 2003-08-27 | ||
US10/649,549 US20050044609A1 (en) | 2003-08-27 | 2003-08-27 | Polyvinyl chloride glove having improved chemical resistance |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2005023031A1 true WO2005023031A1 (fr) | 2005-03-17 |
Family
ID=34216980
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2004/019858 WO2005023031A1 (fr) | 2003-08-27 | 2004-06-18 | Gants en chlorure de polyvinyle ayant une resistance chimique amelioree |
Country Status (5)
Country | Link |
---|---|
US (1) | US20050044609A1 (fr) |
EP (1) | EP1657989A1 (fr) |
JP (1) | JP2007503532A (fr) |
CA (1) | CA2535907A1 (fr) |
WO (1) | WO2005023031A1 (fr) |
Families Citing this family (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060141186A1 (en) * | 2004-12-28 | 2006-06-29 | Janssen Robert A | Gloves with hydrogel coating for damp hand donning and method of making same |
US20060218697A1 (en) * | 2005-03-31 | 2006-10-05 | Kimberly-Clark Worldwide, Inc. | Gloves with enhanced anti-cuff-slip surface |
US20070026028A1 (en) * | 2005-07-26 | 2007-02-01 | Close Kenneth B | Appliance for delivering a composition |
US20080103461A1 (en) * | 2006-10-31 | 2008-05-01 | Johnson Kroy D | Appliance for delivering a composition, the appliance having an outer fibrous layer and inner liquid-impermeable layer |
US20080103460A1 (en) * | 2006-10-31 | 2008-05-01 | Close Kenneth B | Method for making an appliance for delivering a composition, the appliance having an elastic layer and a shielding layer |
US20080102093A1 (en) * | 2006-10-31 | 2008-05-01 | Close Kenneth B | Appliance for delivering a composition, the appliance having an elastic layer and a shielding layer |
US20080116096A1 (en) * | 2006-11-17 | 2008-05-22 | Johnson Kroy D | Liquid-permeable appliance for delivering a composition |
US20090326622A1 (en) * | 2008-06-26 | 2009-12-31 | Johnson Kroy D | Customizable therapeutic article for applying heat to the body |
EP2515782B1 (fr) * | 2009-12-21 | 2015-12-16 | Ansell Limited | Gant sans poudre avec revêtement stable et antimicrobien à action rapide |
AT511292B1 (de) | 2010-05-26 | 2013-01-15 | Semperit Ag Holding | Handschuh |
US20120232652A1 (en) * | 2011-03-07 | 2012-09-13 | Rolando Mora | Implant with a visual indicator of a barrier layer |
AT513456B1 (de) * | 2012-10-09 | 2016-07-15 | Semperit Ag Holding | Verfahren zur Modifizierung der Oberfläche eines Elastomerproduktes |
USD773744S1 (en) * | 2013-12-13 | 2016-12-06 | Covco (H.K.) Ltd. | Glove former |
USD735968S1 (en) * | 2013-12-13 | 2015-08-11 | Covco Ltd. | Glove |
US10448686B2 (en) * | 2016-09-23 | 2019-10-22 | Medline Industries, Inc. | Glide-on coating for polymeric gloves |
JP2019167636A (ja) * | 2018-03-22 | 2019-10-03 | エステー株式会社 | 塩化ビニル手袋及びその製造方法 |
JP2020026585A (ja) * | 2018-08-10 | 2020-02-20 | エステー株式会社 | 塩化ビニル手袋及びその製造方法 |
CN116199815A (zh) * | 2022-12-29 | 2023-06-02 | 优美特(北京)环境材料科技股份公司 | 聚丙烯酸乳液、涂料及相关的聚氯乙烯复合膜及手套 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6012169A (en) * | 1998-02-17 | 2000-01-11 | Showa Kabushiki Kaisha | Glove made of polyvinyl chloride resin |
WO2000035978A1 (fr) * | 1998-12-17 | 2000-06-22 | Avery Dennison Corporation | Revetements copolymeres en acrylate, silicone, styrene ou urethanne destines aux articles en fibres naturelles ou synthetiques |
WO2003053663A1 (fr) * | 2001-12-20 | 2003-07-03 | Kimberly-Clark Worldwide, Inc. | Article elastomere avec surface de prehension amelioree |
WO2003057750A1 (fr) * | 2001-12-21 | 2003-07-17 | Kimberly-Clark Worldwide, Inc. | Gants en elastomere avec enfilage facilite |
Family Cites Families (43)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3059241A (en) * | 1960-05-04 | 1962-10-23 | Seamless Rubber Co | Dipped plastic glove |
US3278991A (en) * | 1965-07-02 | 1966-10-18 | Mcneil Corp | Dip coating apparatus |
US3761965A (en) * | 1972-06-19 | 1973-10-02 | Becton Dickinson Co | Seamless plastic articles having a textured surface |
US3852826A (en) * | 1974-01-18 | 1974-12-10 | Int Corp | Surgical gloves |
US4143109A (en) * | 1976-07-15 | 1979-03-06 | Arbrook, Inc. | Method of making medical glove |
US4047251A (en) * | 1976-09-20 | 1977-09-13 | Arbrook, Inc. | Glove and form and method for making same |
FR2375839B1 (fr) * | 1977-01-04 | 1980-07-11 | Sofiman Sa | Procede de fabrication d'un article d'habillement et machine pour la mise en oeuvre du procede |
US4589873A (en) * | 1984-05-29 | 1986-05-20 | Becton, Dickinson And Company | Method of applying a hydrophilic coating to a polymeric substrate and articles prepared thereby |
JP2677850B2 (ja) * | 1987-04-21 | 1997-11-17 | アンセル・パーリー・インコーポレーテッド | 手 袋 |
GB8820945D0 (en) * | 1988-09-07 | 1988-10-05 | Smith & Nephew | Medical articles |
US4884300A (en) * | 1988-09-13 | 1989-12-05 | Becton, Dickinson And Company | Glove having improved cuff securing features |
US5524294A (en) * | 1988-09-19 | 1996-06-11 | Richardson; Margaret P. | Tamper- or damage-indicating members |
US6175962B1 (en) * | 1988-10-17 | 2001-01-23 | Gary Karlin Michelson | Surgical glove |
US4939212A (en) * | 1989-03-31 | 1990-07-03 | The B. F. Goodrich Company | Elasticized vinyl dispersion resins having outstanding stability |
US5071648A (en) * | 1989-04-06 | 1991-12-10 | Merocel Corporation | Polymeric broad-spectrum antimicrobial materials |
CA2016167A1 (fr) * | 1989-05-19 | 1990-11-19 | Dominique Petit | Composition de chlorure de polyvinyle modifiee |
US5459879A (en) * | 1989-05-22 | 1995-10-24 | Board Of Regents, The University Of Texas System | Protective coverings |
US5089205A (en) * | 1989-09-25 | 1992-02-18 | Becton, Dickinson And Company | Process for producing medical devices having antimicrobial properties |
US5069965A (en) * | 1989-10-18 | 1991-12-03 | Bioresearch, Inc. | Articles having improved slip coatings |
JPH03199403A (ja) * | 1989-12-27 | 1991-08-30 | Chugoku Pearl Hanbai Kk | 無菌性手袋 |
US5780043A (en) * | 1990-02-22 | 1998-07-14 | Dane; Greg | Infection resistant thermoplastic polyurethane |
US5254391A (en) * | 1990-06-04 | 1993-10-19 | Elbert Davis | Soft, elastomeric, polymer coated contact surface |
US5164231A (en) * | 1990-06-04 | 1992-11-17 | Elbert Davis | Soft, elastomeric, polymer coated contact surface and method of preparing the same |
US5335373A (en) * | 1991-11-29 | 1994-08-09 | Dresdner Jr Karl P | Protective medical gloves and methods for their use |
DE69308172D1 (de) * | 1992-06-10 | 1997-03-27 | Maxxim Med Inc | Biegsamer Gummigegenstand und Verfahren zu seiner Herstellung |
US5442816A (en) * | 1993-02-05 | 1995-08-22 | Seketa; Nicholas F. | Surgical glove |
KR950701369A (ko) * | 1993-03-01 | 1995-03-23 | 에이. 제라드 시에크 | 스퀜셜 공중합체 기재의 장갑 |
US5881386A (en) * | 1993-12-23 | 1999-03-16 | Maxxim Medical, Inc. | Flexible polyvinyl chloride article and method of making |
US5993839A (en) * | 1994-05-09 | 1999-11-30 | Phoenix Medical Technology, Inc. | Antimicrobial gloves and a method of manufacture thereof |
US5906823A (en) * | 1994-05-09 | 1999-05-25 | Mixon; Grover C. | Antimicrobial gloves and a method of manufacture thereof |
US5725867A (en) * | 1994-05-09 | 1998-03-10 | Phoenix Medical Technology, Inc. | Antimicrobial gloves and a method of manufacture thereof |
US5649326A (en) * | 1994-11-18 | 1997-07-22 | Johnson & Johnson Professional, Inc. | Flexible hydrophilic coating for orthopaedic casting gloves and method for making such gloves |
US5700585A (en) * | 1995-02-14 | 1997-12-23 | Avery Dennison Corporation | Acrylic emulsion coatings for formed articles |
US6361786B1 (en) * | 1997-09-15 | 2002-03-26 | Shanbrom Technologies | Microbicide treated polymeric materials |
US5867832A (en) * | 1997-12-08 | 1999-02-09 | Liu; Fang Yi | Disposable vinyl glove having fastening belt |
US6344163B1 (en) * | 1998-04-23 | 2002-02-05 | Louis S. Ashley | Method and apparatus for dipped forming PVC gloves and cot-like articles |
US6016570A (en) * | 1998-05-11 | 2000-01-25 | Maxxim Medical, Inc. | Powderfree medical glove |
US5997969A (en) * | 1998-08-27 | 1999-12-07 | Gardon; John L. | Non-allergenic medical and health care devices made from crosslinked synthetic elastomers |
US6730740B1 (en) * | 1998-09-25 | 2004-05-04 | Akzo Nobel N.V. | Aqueous cross-linkable polymer composition for use in coatings and process for producing the same |
US6274154B1 (en) * | 1999-04-07 | 2001-08-14 | Belle L Chou | Aloe Vera glove and manufacturing method |
US6369154B1 (en) * | 1999-07-26 | 2002-04-09 | Reichhold, Inc. | Compositions suitable for making elastomeric articles of manufacture |
US20030124354A1 (en) * | 2001-12-27 | 2003-07-03 | Maris Vistins | Colored high-protective multi-layered polymer coated articles and method of making same |
US20050015846A1 (en) * | 2003-06-26 | 2005-01-27 | Kimberly-Clark Worldwide, Inc. | Polyvinyl chloride article having improved durability |
-
2003
- 2003-08-27 US US10/649,549 patent/US20050044609A1/en not_active Abandoned
-
2004
- 2004-06-18 CA CA002535907A patent/CA2535907A1/fr not_active Abandoned
- 2004-06-18 JP JP2006524626A patent/JP2007503532A/ja not_active Abandoned
- 2004-06-18 EP EP04776878A patent/EP1657989A1/fr not_active Withdrawn
- 2004-06-18 WO PCT/US2004/019858 patent/WO2005023031A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6012169A (en) * | 1998-02-17 | 2000-01-11 | Showa Kabushiki Kaisha | Glove made of polyvinyl chloride resin |
WO2000035978A1 (fr) * | 1998-12-17 | 2000-06-22 | Avery Dennison Corporation | Revetements copolymeres en acrylate, silicone, styrene ou urethanne destines aux articles en fibres naturelles ou synthetiques |
WO2003053663A1 (fr) * | 2001-12-20 | 2003-07-03 | Kimberly-Clark Worldwide, Inc. | Article elastomere avec surface de prehension amelioree |
WO2003057750A1 (fr) * | 2001-12-21 | 2003-07-17 | Kimberly-Clark Worldwide, Inc. | Gants en elastomere avec enfilage facilite |
Also Published As
Publication number | Publication date |
---|---|
US20050044609A1 (en) | 2005-03-03 |
JP2007503532A (ja) | 2007-02-22 |
CA2535907A1 (fr) | 2005-03-17 |
EP1657989A1 (fr) | 2006-05-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20050044609A1 (en) | Polyvinyl chloride glove having improved chemical resistance | |
EP1511793B1 (fr) | Procede de production d'un gant presentant des caracteristiques d'enfilage ameliorees | |
US8250672B2 (en) | Exterior-coated nitrile rubber article having natural rubber characteristics | |
AU630055B2 (en) | Articles having improved slip coatings | |
EP1581132B1 (fr) | Gant elastomere respirant | |
EP0643743B1 (fr) | Gants a base de copolymere sequentiel | |
IL177600A (en) | On-line making of powder-free rubber gloves | |
WO2000025840A1 (fr) | Gants sans poudre munis d'un revetement interne en polyurethanne impregne de silicone | |
US20080311409A1 (en) | Powder-free coagulants with silicone surfactants | |
EP1509257B1 (fr) | Gants a caracteristiques d'enfilage ameliorees | |
CA2227645A1 (fr) | Articles multicouches, a parois minces, exempts de poudre, fabriques a partir de copolymeres sequences de styrene | |
MXPA06002167A (en) | Polyvinyl chloride glove having improved chemical resistance | |
NZ549327A (en) | An antiblocking coagulant composition for making of powder-free rubber gloves | |
KR20060134158A (ko) | 무분말 고무 장갑의 온―라인 제조 | |
AU5182600A (en) | Articles formed by styrene-ethylene/butylene-styrene block copolymer/oil aqueous dispersions |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
ENP | Entry into the national phase |
Ref document number: 2535907 Country of ref document: CA |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2004776878 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006524626 Country of ref document: JP |
|
WWE | Wipo information: entry into national phase |
Ref document number: PA/a/2006/002167 Country of ref document: MX |
|
WWP | Wipo information: published in national office |
Ref document number: 2004776878 Country of ref document: EP |