WO2005017024A2 - Membranes presentant des proprietes de barriere de fluide et articles contenant des membranes de ce type - Google Patents

Membranes presentant des proprietes de barriere de fluide et articles contenant des membranes de ce type Download PDF

Info

Publication number
WO2005017024A2
WO2005017024A2 PCT/US2004/021745 US2004021745W WO2005017024A2 WO 2005017024 A2 WO2005017024 A2 WO 2005017024A2 US 2004021745 W US2004021745 W US 2004021745W WO 2005017024 A2 WO2005017024 A2 WO 2005017024A2
Authority
WO
WIPO (PCT)
Prior art keywords
bladder
membrane
filler
thermoplastic
polymeric
Prior art date
Application number
PCT/US2004/021745
Other languages
English (en)
Other versions
WO2005017024A3 (fr
Inventor
Yihua Chang
Richard L. Watkins
Original Assignee
Nike, Inc.
Nike International, Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nike, Inc., Nike International, Ltd. filed Critical Nike, Inc.
Priority to EP04777683A priority Critical patent/EP1651525A4/fr
Publication of WO2005017024A2 publication Critical patent/WO2005017024A2/fr
Publication of WO2005017024A3 publication Critical patent/WO2005017024A3/fr

Abstract

Membrane qui comporte au moins une matière élastomère, au moins une matière polymère à fonction de barrière de fluide et une nano-charge lamellaire à épaisseur moyenne des plaquettes allant jusqu'à 10 nanomètres et à rapport de forme moyen d'au moins 200, et qui possède une apparence désirée et des caractéristiques de faible transmission de gaz. Ladite membrane peut comporter une seule couche, mais elle comporte de préférence au moins une couche de matière élastomère et au moins une couche d'une matière polymère barrière. La couche de matière élastomère et / ou la couche de matière polymère barrière contiennent la nano-charge lamellaire.
PCT/US2004/021745 2003-08-04 2004-07-08 Membranes presentant des proprietes de barriere de fluide et articles contenant des membranes de ce type WO2005017024A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP04777683A EP1651525A4 (fr) 2003-08-04 2004-07-08 Membranes presentant des proprietes de barriere de fluide et articles contenant des membranes de ce type

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US10/633,764 2003-08-04
US10/633,764 US20050031816A1 (en) 2003-08-04 2003-08-04 Membranes with fluid barrier properties and articles containing such membranes

Publications (2)

Publication Number Publication Date
WO2005017024A2 true WO2005017024A2 (fr) 2005-02-24
WO2005017024A3 WO2005017024A3 (fr) 2005-06-23

Family

ID=34115882

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2004/021745 WO2005017024A2 (fr) 2003-08-04 2004-07-08 Membranes presentant des proprietes de barriere de fluide et articles contenant des membranes de ce type

Country Status (5)

Country Link
US (1) US20050031816A1 (fr)
EP (1) EP1651525A4 (fr)
KR (1) KR20060076272A (fr)
TW (1) TWI290941B (fr)
WO (1) WO2005017024A2 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2578398A1 (fr) * 2010-05-31 2013-04-10 Sumitomo Bakelite Co., Ltd. Film multicouche et matériau d'emballage
WO2016040893A1 (fr) * 2014-09-12 2016-03-17 Nike Innovate C.V. Membranes et leurs utilisations
CN109776752A (zh) * 2019-01-22 2019-05-21 华大化学(安徽)有限公司 一种超软质肤感干法用面层树脂及其制备方法和应用
US11528958B2 (en) 2016-06-29 2022-12-20 Nike, Inc. Multi-layered structures and uses thereof

Families Citing this family (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050090616A1 (en) * 2003-10-27 2005-04-28 Dias Anthony J. Microlayered composites and processes for making the same
EP1894750B1 (fr) * 2005-06-15 2010-02-17 Bridgestone Corporation Vessie d'air pour pneu de sécurité et pneu de sécurité utilisant la vessie d'air
WO2007100884A2 (fr) * 2006-02-28 2007-09-07 E.I. Du Pont De Nemours And Company Modification de materiaux polymeriques pour une adhesion accrue
US20070249754A1 (en) * 2006-04-25 2007-10-25 Medtronic, Inc. Methods of modifying polyurethanes using surface treated clay
US8210973B2 (en) * 2008-06-27 2012-07-03 Nike, Inc. Sport ball bladder
US8012572B2 (en) 2009-03-06 2011-09-06 Cryovac, Inc. Multilayer, heat-shrinkable film comprising a plurality of microlayers
US9192754B2 (en) * 2011-01-27 2015-11-24 Carefusion 303, Inc. Low permeability silicone rubber tubing
US8789294B2 (en) * 2011-03-16 2014-07-29 Nike, Inc. Contoured fluid-filled chamber with tensile structures
US20120288696A1 (en) * 2011-05-09 2012-11-15 Jenkins Shawn E Multi-Layer Elastic Films
JP2018532846A (ja) 2015-09-30 2018-11-08 エクソンモービル ケミカル パテンツ インコーポレイテッド 機能性ポリマーコームアームを有するイソブチレンコポリマー主鎖のコーム−ブロックコポリマー
US9914817B2 (en) 2015-09-30 2018-03-13 Exxonmobil Chemical Patents Inc. Polycyclic aromatic hydrocarbon functionalized isobutylene copolymers for dispersing graphene and graphite
EP3356469B1 (fr) * 2015-09-30 2020-04-29 ExxonMobil Chemical Patents Inc. Copolymères d'isobutylène fonctionnalisés par hydrocarbure aromatique polycyclique pour la dispersion de graphène et de graphite
CN111880256B (zh) * 2017-09-29 2022-03-08 耐克创新有限合伙公司 结构着色的物品以及制造和使用结构着色的物品的方法
US20210291480A1 (en) * 2018-07-25 2021-09-23 Sealed Air Corporation (Us) Inflatable cellular cushioning article with enhanced performance properties
CN109171092B (zh) * 2018-08-20 2021-02-26 中国科学院化学研究所 一种弹性体鞋及其制鞋工艺
EP3761824B1 (fr) * 2018-10-19 2021-08-04 Nike Innovate C.V. Structure de semelle de chaussure ayant un élément composite et ses procédés de fabrication
US11028954B2 (en) * 2019-06-20 2021-06-08 Freudenberg-Nok General Partnership Accumulator having a diaphragm or bladder with a metallized barrier film
CN114008493A (zh) 2019-06-26 2022-02-01 耐克创新有限合伙公司 结构着色的物品以及用于制造和使用结构着色的物品的方法
EP3963376A1 (fr) 2019-07-26 2022-03-09 Nike Innovate C.V. Articles structurellement colorés et procédés de fabrication et d'utilisation d'articles structurellement colorés
WO2021080913A1 (fr) 2019-10-21 2021-04-29 Nike, Inc. Articles structurellement colorés
US20210370713A1 (en) 2020-05-29 2021-12-02 Nike, Inc. Structurally-colored articles and methods for making and using structurally-colored articles
CN113999514B (zh) * 2020-07-27 2023-04-28 万华化学集团股份有限公司 一种分散相形态可控的聚氨酯组合物及其制备方法和应用
US11889894B2 (en) 2020-08-07 2024-02-06 Nike, Inc. Footwear article having concealing layer
US11129444B1 (en) 2020-08-07 2021-09-28 Nike, Inc. Footwear article having repurposed material with concealing layer
US11241062B1 (en) 2020-08-07 2022-02-08 Nike, Inc. Footwear article having repurposed material with structural-color concealing layer
CN111959538B (zh) * 2020-08-28 2022-02-08 株洲时代新材料科技股份有限公司 轨道交通车辆的耐火轮罩及其制作方法
EP4214037B1 (fr) 2021-02-24 2024-05-01 Nike Innovate C.V. Articles en mousse et leurs procédés de fabrication
EP4175807B1 (fr) * 2021-02-24 2024-03-27 Nike Innovate C.V. Articles en mousse et leurs procédés de fabrication
CN116056860A (zh) 2021-02-24 2023-05-02 耐克创新有限合伙公司 发泡的物品以及制造发泡的物品的方法
CN117580478A (zh) * 2021-07-27 2024-02-20 耐克创新有限合伙公司 用于气囊和鞋类的多层膜
CN116438071A (zh) 2021-07-27 2023-07-14 耐克创新有限合伙公司 用于气囊和鞋类的多层膜
US20230043845A1 (en) * 2021-07-27 2023-02-09 Nike, Inc. Multi-layered films for use in airbags and footwear
WO2023010027A1 (fr) * 2021-07-27 2023-02-02 Nike, Inc. Films multicouches destinés à être utilisés dans des coussins d'air et articles chaussants
CN113659923B (zh) * 2021-09-14 2023-06-06 宁波勤邦新材料科技有限公司 一种使用多层pet基膜的光伏发电设备
CN115103806A (zh) * 2021-11-16 2022-09-23 宝洁公司 用于制品的包装系统

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5221566A (en) * 1991-03-29 1993-06-22 Kuraray Co., Ltd. Multilayered container and package utilizing the same
US5952065A (en) * 1994-08-31 1999-09-14 Nike, Inc. Cushioning device with improved flexible barrier membrane
TW345540B (en) * 1994-08-31 1998-11-21 Nike Inc Laminated resilient flexible barrier membranes (1)
DE69633198T2 (de) * 1995-06-07 2005-09-08 Nike International Ltd., Beaverton Aufgeblasene, verschlossene behälter aus polyesterurethanmembranen und herstellungsverfahren
US6599597B1 (en) * 1995-06-07 2003-07-29 Nike, Inc. Barrier membranes including a barrier layer employing aliphatic thermoplastic urethanes
US6013340A (en) * 1995-06-07 2000-01-11 Nike, Inc. Membranes of polyurethane based materials including polyester polyols
US5905000A (en) * 1996-09-03 1999-05-18 Nanomaterials Research Corporation Nanostructured ion conducting solid electrolytes
US5840825A (en) * 1996-12-04 1998-11-24 Ppg Incustries, Inc. Gas barrier coating compositions containing platelet-type fillers
US6034164A (en) * 1997-02-21 2000-03-07 Exxon Research And Engineering Co. Nanocomposite materials formed from inorganic layered materials dispersed in a polymer matrix
US6087016A (en) * 1997-06-09 2000-07-11 Inmat, Llc Barrier coating of an elastomer and a dispersed layered filler in a liquid carrier
US6117541A (en) * 1997-07-02 2000-09-12 Tetra Laval Holdings & Finance, Sa Polyolefin material integrated with nanophase particles
DE69933878T2 (de) * 1998-09-11 2007-09-06 Nike International Ltd., Beaverton Biegsame membranen
US6127026A (en) * 1998-09-11 2000-10-03 Nike, Inc. Flexible membranes
US6082025A (en) * 1998-09-11 2000-07-04 Nike, Inc. Flexible membranes
DE60004972T2 (de) * 1999-02-12 2004-05-19 The Dow Chemical Co., Midland Nanoverbundgegenstände und herstellungsverfahren dafür
US6403231B1 (en) * 2000-05-12 2002-06-11 Pechiney Emballage Flexible Europe Thermoplastic film structures having improved barrier and mechanical properties
US6737464B1 (en) * 2000-05-30 2004-05-18 University Of South Carolina Research Foundation Polymer nanocomposite comprising a matrix polymer and a layered clay material having a low quartz content
US7229518B1 (en) * 2000-11-02 2007-06-12 Nike, Inc. Process for improving interfacial adhesion in a laminate
US6620871B2 (en) * 2001-06-07 2003-09-16 Nike, Inc. Rubber compositions with increased shelf life and reduced cure temperatures and times
US6790391B2 (en) * 2002-03-07 2004-09-14 Nike International, Ltd. Composition for clear gas barrier laminates
WO2004000546A1 (fr) * 2002-06-25 2003-12-31 University Of Massachusetts Matiere de silicate en couches et applications de matieres en couches a couches poreuses
US7597946B2 (en) * 2003-08-29 2009-10-06 Nike, Inc. Gel reduction in blends of thermoplastic polyurethane and hydroxyl functional polymers
US7211611B2 (en) * 2003-12-11 2007-05-01 Nike, Inc. Rubber compositions with non-petroleum oils
US20050202198A1 (en) * 2004-03-12 2005-09-15 Hogan Richard M. Adhesive sheets and methods for their use

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See references of EP1651525A4 *

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2578398A1 (fr) * 2010-05-31 2013-04-10 Sumitomo Bakelite Co., Ltd. Film multicouche et matériau d'emballage
EP2578398A4 (fr) * 2010-05-31 2014-03-19 Sumitomo Bakelite Co Film multicouche et matériau d'emballage
WO2016040893A1 (fr) * 2014-09-12 2016-03-17 Nike Innovate C.V. Membranes et leurs utilisations
EP3415310A1 (fr) * 2014-09-12 2018-12-19 NIKE Innovate C.V. Membranes et leurs utilisations
US10377112B2 (en) 2014-09-12 2019-08-13 Nike, Inc. Membranes and uses therof
US11528958B2 (en) 2016-06-29 2022-12-20 Nike, Inc. Multi-layered structures and uses thereof
US11903440B2 (en) 2016-06-29 2024-02-20 Nike, Inc. Multi-layered structures and uses thereof
CN109776752A (zh) * 2019-01-22 2019-05-21 华大化学(安徽)有限公司 一种超软质肤感干法用面层树脂及其制备方法和应用

Also Published As

Publication number Publication date
TWI290941B (en) 2007-12-11
KR20060076272A (ko) 2006-07-04
WO2005017024A3 (fr) 2005-06-23
EP1651525A2 (fr) 2006-05-03
US20050031816A1 (en) 2005-02-10
EP1651525A4 (fr) 2010-11-10
TW200505971A (en) 2005-02-16

Similar Documents

Publication Publication Date Title
US20050031816A1 (en) Membranes with fluid barrier properties and articles containing such membranes
US6582786B1 (en) Flexible membranes
US6127026A (en) Flexible membranes
US6082025A (en) Flexible membranes
EP1333878B1 (fr) Procede d'amelioration d'adherence interfaciale dans un stratifie
AU2003220054B2 (en) Composition for clear gas barrier laminates
AU2002245852A1 (en) Process for improving interfacial adhesion in a laminate

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1020067002343

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 2004777683

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 2004777683

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1020067002343

Country of ref document: KR