WO2005016819A1 - Herstellung von aktivkohle - Google Patents
Herstellung von aktivkohle Download PDFInfo
- Publication number
- WO2005016819A1 WO2005016819A1 PCT/EP2004/008314 EP2004008314W WO2005016819A1 WO 2005016819 A1 WO2005016819 A1 WO 2005016819A1 EP 2004008314 W EP2004008314 W EP 2004008314W WO 2005016819 A1 WO2005016819 A1 WO 2005016819A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- starting material
- temperature
- smoldering
- groups
- activated carbon
- Prior art date
Abstract
Description
Claims