WO2005012989A1

WO2005012989A1 - Optical compensator, process of its fabrication, and liquid crystal display

Info

Publication number: WO2005012989A1
Application number: PCT/US2004/022944
Authority: WO
Inventors: James Frank Elman; Dennis Jon Massa; Charles Chester Anderson; Tomohiro Ishikawa
Original assignee: Eastman Kodak Co
Current assignee: Eastman Kodak Co
Priority date: 2003-07-31
Filing date: 2004-07-16
Publication date: 2005-02-10
Anticipated expiration: 2006-01-31
Also published as: KR101096972B1; CN1829938A; US7163724B2; JP2007500866A; US20060193975A1; US20050024561A1; TWI363217B; JP4636622B2; TW200528853A; CN100426096C; KR20060054391A; US7083835B2

Abstract

A multilayer compensator comprising one or more polymeric layers A and one or more polymeric layers B, wherein said layers A comprise a polymer having an out-of-plane birefringence not more negative than -0.01, said layers B comprise an amorphous polymer having an out-of-plane birefringence more negative than -0.01, and the overall in-plane retardation (Rin) of said multilayer compensator is greater than 20nm and the overall out-of-plane retardation (Rth) of said multilayer compensator is more negative than -20nm.

Description

OPTICAL COMPENSATOR, PROCESS OF ITS FABRICATION, AND LIQUID CRYSTAL DISPLAY

FIELD OF THE INVENTION The present invention relates to a multilayer optical compensator for liquid crystal displays comprising polymeric A and polymeric B layers exhibiting particular birefringent properties. The invention also relates to a process for making such a compensator and liquid crystal displays using the compensator.

BACKGROUND OF THE INVENTION Liquid crystals are widely used for electronic displays. In these display systems, a liquid crystal cell is typically situated between a pair of polarizer and analyzers. An incident light polarized by the polarizer passes through a liquid crystal cell and is affected by the molecular orientation of the liquid crystal, which can be altered by the application of a voltage across the cell. The altered light goes into the analyzer. By employing this principle, the transmission of light from an external source, including ambient light, can be controlled. The energy required to achieve this control is generally much less than required for the luminescent materials used in other display types such as cathode ray tubes (CRT). Accordingly, liquid crystal technology is used for a number of electronic imaging devices, including but not limited to digital watches, calculators, portable computers, electronic games for which light-weight, low- power consumption and long-operating life are important features. Contrast, color reproduction, and stable gray scale intensities are important quality attributes for electronic displays, which employ liquid crystal technology. The primary factor limiting the contrast of a liquid crystal display (LCD) is the propensity for light to "leak" through liquid crystal elements or cells, which are in the dark or "black" pixel state. Furthermore, the leakage and hence contrast of a liquid crystal display are also dependent on the direction from which the display screen is viewed. Typically the optimum contrast is observed only within a narrow viewing angle range centered about the normal incidence to the display and falls off rapidly as the viewing direction deviates from the display normal. In color displays, the leakage problem not only degrades the contrast but also causes color or hue shifts with an associated degradation of color reproduction. LCDs are quickly replacing CRTs as monitors for desktop computers and other office or house hold appliances. It is also expected that the number of LCD television monitors with a larger screen size will sharply increase in the near future. However, unless problems of viewing angle dependence such as coloration, degradation in contrast, and an inversion of brightness are solved, LCD's application as a replacement of the traditional CRT will be limited. A Vertically-Aligned liquid crystal display (VA-LCD) offers an extremely high contrast ratio for normal incident light. FIG. 2A and FIG. 2B are the schematics of VA liquid crystal cell in OFF 201 and ON 203 states. In its OFF state, the liquid crystal optic axis 205 is almost perpendicular to the substrate 207, FIG. 2A. With an applied voltage, the optic axis 205 is tilted away from the cell normal, FIG. 2B. In the OFF state, light does not see the birefringence in the normal direction 209, giving the dark state that is close to that of orthogonally crossed polarizers. However, obliquely propagated light 211 picks up phase retardation giving light leakage. This results in a poor contrast ratio in some viewing angle range. A bend aligned nematic liquid crystal display, also referred as an Optically Compensated Bend Liquid Crystal Display (OCB-LCD) uses a nematic liquid crystal cell based on the symmetric bend state. In its actual operation, the brightness of the display using the bend aligned nematic liquid crystal cell is controlled by an applied voltage or field that leads to a different degree in the bend orientation within the cell as shown in FIG. 3A (OFF) 301 and FIG.3B (ON) 303. In both states, the liquid crystal optic axis 305 takes symmetric bend state around the cell middle plane 307. In the On state, the optic axis becomes substantially perpendicular to the cell plane except near the cell substrates 309. OCB mode offers faster response speed that is suitable to the liquid crystal display television (LCD-TV) application. It also has advantages in viewing angle characteristic (VAC) over conventional displays, such as Twisted Nematic liquid crystal display (TN-LCD) The above-mentioned two modes, due to their superiority over the conventional TN-LCD, are expected to dominate the high-end application such as LCD-TV. However, practical applications of both OCB and VA-LCDs require optical compensating means to optimize the VAC. In both modes, due to the birefringence of liquid crystal and crossed polarizer, VAC suffers deterioration in contrast when the displays are viewed from oblique angles. Use of biaxial films have been suggested to compensate the OCB (US 6,108,058) and VA ( JP1999- 95208 ) LCDs. In both modes, liquid crystals align sufficiently perpendicular to the plane of the cell in ON (OCB) or OFF (VA) states. This state gives positive R_th, thus the compensation films have to have sufficiently large negative R_th for satisfactory optical compensation. The need for a biaxial film with a large Rth is also common for Super Twisted Nematic Liquid Crystal Display (STN-LCD). Several methods of manufacturing biaxial films with sufficient negative value of R_t suitable for compensating LCD modes such as OCB, VA and STN have been suggested. US 2001/0026338 discloses a use of retardation increasing agent in combination with triacetylcellulose (TAG). The retardation-increasing agent is chosen from aromatic compounds having at least two benzene rings. By stretching agent doped TAC, one can generate both R_th and Rj_n . The problems with this method is that the amount of the doping of the agent. To generate the desired effects of increasing R_th and Ri_n,the necessary amount of agent is high enough to cause coloration. With this method, it is difficult to control the values of R_th and Ri_n independently. Sasaki et al. proposes (US2003/0086033) the use of cholesteric liquid crystal disposed on the positively birefringent thermoplastic substrate. The pitch of the cholesteric liquid crystal (CHLC) is shorter than the wavelength of the visible light, thus properly aligned CHLC exhibits form birefringence giving negative R_th- Ri_n is controlled by adjusting the stretching amount of the thermoplastic substrate. The method enables one to adjust R_th and Rj_n separately. However, the use of short pitch CHLC not only makes the manufacturing cost high but also complicates the processing due to the alignment procedure. JP2002-210766 discloses the use of propionyl or butyryl substituted TAC. They show higher birefringence than ordinary TAC. Thus, by biaxially stretching the substituted TAC film, one generates Rj_n and R_tll. The method does not require any additional coating or layer but it suffers a difficulty of independent control of R;_n and R_th. Thus, it is a problem to be solved to provide a multilayer optical compensator with independently controlled R_th and R;_nthat can be readily manufactured. SUMMARY OF THE INVENTION The invention provides a multilayer compensator comprising one or more polymeric A layers and one or more polymeric B layers, wherein said A layers comprise a polymer having an out-of-plane birefringence not more negative than -0.01, and said B layers comprise an amorphous polymer having an out-of- plane birefringence more negative than -0.01, and the overall in-plane retardation (Ri_n) of said multilayer compensator is greater than 20nm and the out-of-plane retardation (R_th) of said multilayer compensator is more negative than -20nm. The invention also provides a LCD and a process for preparing a compensator of the invention. The invention multilayer optical compensator is readily manufactured and provides the required value of the R_ln and the R_th values. BRIEF DESCRIPTION OF THE DRAWINGS While the specification concludes with claims particularly pointing out and distinctly claiming the subject matter of the present invention, it is believed that the invention will be better understood from the following description when taken in conjunction with the accompanying drawings, wherein: FIG.1 is a view of a typical layer with thickness d and x-y-z coordinate system attached to the layer. FIG.2A and FIG. 2B are schematics showing, respectively, the typical ON and OFF state of the VA liquid crystal cell. FIG. 3A and FIG. 3B are schematics showing, respectively, the typical ON and OFF states of the OCB liquid crystal cell. FIG. 4A, FIG. 4B and FIG. 4C are elevation schematics of the multilayer optical compensator of the invention. FIG. 5A, FIG. 5B and FIG. 5C are schematics of a liquid crystal display with multilayer optical compensators of the invention.

DETAILED DESCRIPTION OF THE INVENTION The following definitions apply to the description herein: Optic axis refers to the direction in which propagating light does not see birefringence.

ON and OFF state refers to the state with and without applied voltage to the liquid crystal cell.

In-plane phase retardation, Rjn, of a layer 101 shown in FIG. 1 is a quantity defined by (nx-ny)d, where nx and ny are indices of refraction in the direction of x and y. The x axis is taken as a direction of maximum index of refraction in the x- y plane and the y direction is perpendicular to the x axis. For stretched positively birefringent layers, x corresponds to the direction of primary stretch. The x-y plane is parallel to the plane 103 of the layer, d is a thickness of the layer in the z- direction. The quantity (nx-ny) is referred to as in-plane birefringence, Δn;„. The values of Δnj_n and Rj_n hereafter are given at wavelength λ= 550nm.

Out of-plane phase retardation, Rth, of a layer 101 shown in FIG. 1, herein, is a quantity defined by [nz-(nx+ny)/2]d. nz is the index of refraction in z-direction.

The quantity [nz-(nx+ny)/2] is referred to as out-of-plane birefiingence, Δn_th. If nz>(nx+ny)/2, Δn,_his positive, thus the corresponding Rt_h is also positive. If nz<(nx+ny)/2, Δn_th is negative and R_th is also negative. The values of Δn_th and R_th hereafter are given at λ=550nm.

Intrinsic Birefringence Anj_nt of a polymer herein refers to the quantity defined by

(n_e-n₀), where n_e, and n₀ are extraordinary and ordinary index of the polymer, respectively. Intrinsic birefringence is determined by factors, such as the polarizabilities of functional groups and their bond angles with respect to the polymer chain. The actual birefringence (in-plane Δnj_n or out-of-plane Δn_th) of a polymer layer depends on the process of forming it, thus the order parameter, and the Δn;_nt.

Amorphous means a lack of long-range order. Thus an amorphous polymer does not show long-range order as measured by techniques such as X-ray diffraction. Chromophore means an atom or group of atoms that serve as a unit in light adsorption. (Modern Molecular Photochemistry Nicholas J. Turro Editor, Benjamin Cummings Publishing Co., Menlo Park, CA (1978) Pg 77). Typical chromophore groups include vinyl, carbonyl, amide, imide, ester, carbonate, aromatic (i.e. heteroaromatic or carbocylic aromatic such as phenyl, naphthyl, biphenyl, thiophene, bisphenol), sulfone, and azo or combinations of thesegroups. Non-visible chromophore means a chromophore that has an absorption maximum outside the range of 400-700nm. Contiguous means that articles are in contact with each other. In two contiguous layers, one layer is in direct contact with the other. Thus, if a polymer layer is formed on the substrate by coating, the substrate and the polymer layers are contiguous. The invention provides a multilayer compensator comprising one or more polymeric A layers and one or more polymeric B layers, wherein said A layers comprises a polymer having an out-of-plane birefringence not more negative than -0.01, and said B layer comprises an amorphous polymer having an out-of-plane birefringence more negative than -0.01, and the overall in-plane retardation (R_ln) of said multilayer compensator is greater than 20nm and the out- of-plane retardation (R_tn) of said multilayer compensator is more negative than - 20nm. The A layer is made from polymer film other than one containing a chromophore group in the backbone. The A layer has positive intrinsic birefringence, Δnj_nt- Examples of such a polymer include, TAC, cellulose acetate butylate (CAB), cyclic polyolefin, polycarbonate, polysulfonate, and other polymers known to those skilled in the art. These polymeric materials can be made into a film form by solvent casting, heat extrusion, or other methods. To generate R;_n that is greater than 20nm in the A layer, any viable methods can be used, however, most commonly practiced procedure is stretching. As the A layers are made from polymer film with positive Δn;_nt, indices of refraction in the plane of the layer satisfies nx>ny, where "x" denotes the primary direction of stretching and "y" is the direction perpendicular to x. By stretching polymeric materials, individual polymer chain segments are oriented predominantly to the direction of primary stretch, thus increase the birefringence of polymer layer. As it is necessary to orient the polymer segment, the stretching has to be done above the glass transition temperature of the polymeric materials. Thus, the polymeric film is heated above T_g and stretched. Other method is to stretch the film while solvents are incorporated within the film. With this method, the film can be stretched immediately after the polymer is solvent-cast into a film form. The film can be stretched uniaxially or biaxially. In uniaxial stretching, the film is stretched into one direction. However, by unxiaxial stretching, it is difficult to control the films three indices of refraction, nx, ny and nz, where nz is an index of refraction in the film normal direction. This is particularly true when the stretching of the film in the x direction is large enough so that there is a contraction in the y direction. This contraction effectively gives stretching in the film normal direction z, thus increases nz. In biaxial stretching, where two stretching directions x and y are perpendicular to each other, the undesired shrinkage caused by the stretch in the primary stretching direction (say in x direction) is prevented by simultaneous stretch in the secondly direction (y). Thus the increase in nz can effectively be prevented. Means to stretch are not particularity limited so long the stretched film has sufficient uniformity in three indices of refraction. The polymeric A layer has Δnh not more negative than -0.01. The polymeric A layers of the multilayer compensator are such that the overall in-plane retardation (Rj_n) of said multilayer compensator is suitably greater than 20nm, desirably between than 30 and 200nm, and conveniently between 30nm and 150nm. The polymeric B layers will typically be solvent coated onto the A layer. This solvent coating could be accomplished by spin coating, hopper coating, gravure coating, wire bar coating or other coating methods known to those skilled in the art. The coated B layers are contiguous to the A layer. The B layer is coated from a solution containing a polymer that yields high negative birefiingence that is more negative than -0.01 upon solvent coating. To produce negative Δn_th (or R_th), polymers with positive Δn;_nt are used. Such polymers usually contain non-visible chromophore groups such as vinyl, carbonyl, amide, imide, ester, carbonate, sulfone, azo, and aromatic groups (i.e. benzene, naphthalate, biphenyl, bisphenol A) in the polymer backbone. Examples of such polymers are polyesters, polycarbonates, polyimides, polyetherimides, and polythiophenes. One could also add fillers and non-polymeric molecules to these polymers for the second layer. Desirably, polymers to be used in the B layers will not have chromophores off of the backbone. An example of such an undesirable polymer with chromophores in and off the backbone would be polyarylates possessing the fluorene group. The glass transition temperature (T_g) of the polymers used in the B layer is significant. It should be above 180° C to achieve the desired results. The polymers used in the B layers could be synthesized by a variety of techniques: condensation, addition, anionic, cationic or other common methods of synthesis could be employed. The thickness of each B layer should be less than 30μm. Typically it should be from 0.1 μm to 20μm. Conveniently it should be from 1.Oμm to lOμm. Desirably it should be from 2μm to 8μm. The combined thickness of the multilayer optical compensator should be less than 200μm. Typically it should be from 40μm to 150μm. Desirably it should be from 80μm to 1 lOμm. The B layers should be of sufficient thickness so that the out-of-plane retardation of the B layers is more negative than -20nm. Typically it should be from -600nm to -60nm. Conveniently it should be from -500nm to -50nm. Desirably it should be from -400nm to -50nm. Reference will now be made to the drawings in which the various elements of the present invention will be given numerical designations and in which the invention will be discussed so as to enable one skilled in the art to make and use the invention. It is to be understood that elements not specifically shown or described may take various forms well known to those skilled in the art. FIG. 4A, FIG. 4B and FIG.4C are elevation schematics of the exemplary multilayer optical compensators in accordance with the invention. Compensator 401 in FIG. 4A has a structure in which a B layer 409 is disposed on an A layer 407. The A layer 407 and the B layer 409 are contiguous. It is also possible to have two B layers 413, 415 disposed on one A layer 411 such as the compensator 403 in FIG. 4B. In other case 405, one B layer 417 is sandwiched by two A layers 419, 421. The compensator 405 can be formed, for example, by laminating contiguous layers of A 421 and B 417, and the single layer of A 419. The lamination is done at the interface of B layer 417 and A layer 419, and the two layers 417 and 419 may or may not be contiguous depending on the method of the lamination. One skilled in the art could conceive of more complex structures. In LCD 501 shown in FIG. 5A, the liquid crystal cell 503 is placed between the polarizer 505 and analyzer 507. Transmission axis of the polarizer 509 and analyzer 511 form angle 90±10° thus, pair of polarizer 509 and analyzer 511 are said to be "crossed polarizer". A multilayer optical compensator 512 is placed between the polarizer 505 and the liquid crystal cell 503. It can also be placed between the liquid crystal cell 503 and the analyzer 507. LCD 513 shown schematically in FIG. 5B has two multilayer optical compensators 515, 517 placed on the both sides of the liquid crystal cell 503. FIG. 5C shows an application example of multilayer optical compensator in a reflective type LCD 519. The liquid crystal cell 503 is located between the polarizer 505 and a reflective plate 521. In the figure, the multilayer compensator 523 is placed between the liquid crystal cell 503 and the polarizer 505. However, it can also be placed between the reflective plate 521 and the liquid crystal cell 503. Compared to the prior art, embodiments of the present invention avoids retardation increasing agent that causes coloration, do not require the use of liquid crystal compounds and its alignment procedure, provide enhanced optical compensation in a relatively thin (<200μm) structure, and are easily manufactured. As a further attribute, embodiments enable the control of Rj_n, which is primarily the responsibility of the A layer while control of R_th is primarily the responsibility of the B layer. In the prior art, R;_n and R_tll are often coupled and are not controlled independently. The present invention is further illustrated by the following non- limiting examples of its practice.

Example:

Polymer 1 (synthesis): To a stirred mixture of 4,4'-hexafluoroisopropylidenediphenol (23.53 g, 0.07 mole), 4,4'-(2-norbornylidene) bisphenol (8.4 g, 0.03 mole) and triethylamine (22.3 g, 0.22 mole) in methyl ethyl ketone (100 mL) at 10° C. was added a solution of terephthaloyl chloride (16.23 g, 0.8 mole) and isophthaloyl chloride (4.08g, 0.2 mole) in methyl ethyl ketone (60 mL). After the addition, the temperature was allowed to rise to room temperature and the solution was stirred under nitrogen for 4 hours, during which time triethylamine hydrochloride precipitated in a gelatinous form and the solution became viscous. The solution was then diluted with toluene (160 mL) and washed with dilute hydrochloric acid, (200 mL of 2% acid) followed three times by water (200 mL). The solution was then poured into ethanol with vigorous stirring, and a white bead like polymer precipitated, collected and dried at 50° C. under vacuum for 24 hours. The glass transition temperature of this polymer was measured by differential scanning calorimetry to be 265° C

Poly(4,4'-hexafluoroisopropylidene-bisphenol-co- 4,4'-(2-norbornylidene) bisphenol) terephthalate-co-isophthalate. Polymer 1 Polymer 1 was spun cast (8% solids in 80% propylacetate 20% toluene) onto both a glass slide and a stretched polymer substrate sample, and was analyzed with an ellipsometer (model M2000V, J.A. Woollam Co.) at 550nm wavelength to obtain the R_th and R;_n. These values are listed in TABLE I.

TABLE I

The layer of polymer 1 also did not show any sign of a long-range order therefore the layer was determined to be comprised of an amorphous polymer.

PARTS LIST

101 film

103 plane of the film

201 VA liquid crystal cell in OFF state

203 VA liquid crystal cell in ON state

205 liquid crystal optic axis

207 liquid crystal cell substrate

209 light propagating cell normal direction

211 light propagating oblique direction

301 OCB liquid crystal cell in OFF state

303 OCB liquid crystal cell in ON state

305 liquid crystal optic axis

307 cell middle plane

309 cell boundaries

401 multilayer optical compensator

403 multilayer optical compensator

405 multilayer optical compensator

407 A layer

409 B layer

411 A layer

413 B layer

415 B layer

417 B layer

419 A layer

421 A layer

501 LCD

503 liquid crystal cell

505 polarizer

507 analyzer

509 transmission axis of polarizer

511 transmission axis of analyzer

512 multilayer optical compensator 515 multilayer optical compensator

517 multilayer optical compensator

519 LCD

521 reflective plate

523 multilayer optical compensator nx index of refraction in x direction ny index of refraction in y direction nz index of refraction in z direction no ordinary index of refraction ne extraordinary index of refraction

Δn_th out-of-plane birefringence

Δnin in-plane birefiingence

Δni„t intrinsic birefringence of polymer d thickness of the layer or film

Rth out-of-plane phase retardation

Rin in-plane phase retardation λ wavelength

Tg glass transition temperature

Claims

Claims:

1. A multilayer compensator comprising one or more polymeric A layers and one or more polymeric B layers, wherein: said A layers comprise a polymer having an out-of-plane (Δn_th) birefringence not more negative than -0.01 ; said B layers comprise an amorphous polymer having an out-of-plane birefringence more negative than -0.01; and the overall in-plane retardation (R;_n) of said multilayer compensator is greater than 20nm and the out-of-plane retardation (R_h) of said multilayer compensator is more negative than -20nm.

2. The multilayer compensator of claim 1 wherein at least two of the layers are contiguous.

3. The multilayer compensator of claim 1 wherein all of said A and said B layers are contiguous.

4. The multilayer compensator of claim 1 wherein the combined B layers have a thickness of less than 30 micrometers.

5. The multilayer compensator of claim 1 wherein the combined B layers have a thickness of from 1.0 to 10 micrometers.

6. The multilayer compensator of claim 1 wherein the combined B layers have a thickness of from 2 to 8 micrometers.

7. The multiplayer compensator of claim 1 wherein the combined A layers are such that the overall in-plane retardation (R;_n) of said multilayer compensator is greater than 20nm

8. The multiplayer compensator of claim 1 wherein the combined A layers are such that the overall in-plane retardation (R;_n) of said multilayer compensator is between 30 and 200nm.

9. The multiplayer compensator of claim 1 wherein the combined A layers are such that the overall in-plane retardation (Rj_n) of said multilayer compensator is between 30 and 150nm.

10. The multiplayer compensator of claim 1 wherein the combined A layers are such that the overall in-plane retardation (Ri„) of said multilayer compensator is between 30 andlOOnm.

11. The multilayer compensator of claim 1 wherein the thickness of the combined A and B layers of the compensator is less than 200 micrometers.

12. The multilayer compensator of claim 1 wherein the thickness of the combined A and B layers of the compensator is from 40 to 150 micrometers.

13. The multilayer compensator of claim 1 wherein the thickness of the combined A and B layers of the compensator is from 80 to 110 micrometers.

14. The multilayer compensator of claim 1 wherein the combined R_th of the B layers is -20nm or more negative.

15. The multilayer compensator of claim 1 wherein the combined R_th of the B layers is from -600 to -60nm.

16. The multilayer compensator of claim 1 wherein the combined R_tn of the B layers is from -500 to -50nm.

17. The multilayer compensator of claim 1 wherein at least one B layer comprises a polymer containing in the backbone a non-visible chromophore group and has a T_g above 180°C.

18. The multilayer compensator of claim 1 comprising a polymer in an

A layer wherein the T_g of said A polymer is above 180°C.

19. The multilayer compensator of claim 1 wherein a B layer comprises a polymer containing in the backbone a nonvisible chromophore containing a vinyl, carbonyl, amide, imide, ester, carbonate, aromatic, sulfone, or azo, phenyl, naphthyl, biphenyl, bisphenol, or thiophene group.

20. The multilayer compensator of claim 1 wherein a B layer comprises a copolymer containing 1) a poly(4,4'-hexafluoroisopropylidene- bisphenol) terephthalate-co-isophthalate, 2) a poly(4,4'-hexahydro-4,7- methanoindan-5-ylidene bisphenol) terephthalate, 3) a poly(4,4'-isopropylidene- 2,2'6,6'-tetrachlorobisphenol) terephthalate-co-isophthalate, 4) a poly(4,4'- hexafluoroisopropylidene)-bisphenol-co-(2-norbornylidene)-bisphenol terephthalate, 5) a poly(4,4'-hexahydro-4,7-methanoindan-5-ylidene)-bisphenol- co-(4,4'-isopropylidene-2,2',6,6'-tetrabromo)-bisphenol terephthalate, 6) a poly(4,4'-isopropylidene-bisphenol-co- 4,4'-(2-norbornylidene) bisphenol) terephthalate-co-isophthalate, or 7) a poly(4,4'-hexafluoroisopropylidene- bisphenol-co- 4,4'-(2-norbornylidene) bisphenol) terephthalate-co-isophthalate.

21. The multiplayer compensator of claim 1 wherein a B layer comprises a copolymer of a poly(4,4'-hexafluoroisopropylidene-bisphenol-co- 4,4'-(2-norbornylidene) bisphenol) terephthalate-co-isophthalate

22. The multilayer compensator of claim 1 wherein an A layer comprises a polymer other than a polymer containing in the backbone a non- visible chromophore group having a T_g above 180°C.

23. The multilayer compensator of claim 18 wherein a B layer comprises a polymer containing in the backbone a non- visible chromophore group that does not contain a chromophore off of the backbone

24. The multilayer compensator of claim 1 wherein A layer contains a polymer that comprises triacetylcellulose, cellulose diacetate, cellulose acetate butyrate, polycarbonate, cyclic polyolefin or polyarylate containing fluorene groups.

25. The multilayer compensator of claim 1 wherein an A layer comprises amorphous polymer stretched above glass transition temperature.

26. The multilayer compensator of claim 1 wherein a polymer in an A layer is triacetylcellulose (TAC) or cellulose aceate butylate (CAB).

27. A liquid crystal display comprising a liquid crystal cell, a pair of crossed polarizers located one on each side of the cell, and at least one compensator of claim 1.

28. The liquid crystal display of claim 27 wherein said liquid crystal cell is a vertically aligned or twisted nematic cell.

29. The liquid crystal display of claim 27 employing optically compensated bend liquid crystal cell.

30. A liquid crystal display comprising a liquid crystal cell, at least one polarizer, a reflective plate, and at least one compensator of claim 1.

31. The liquid crystal display of claim 30 wherein said liquid crystal cell is a vertically aligned, twisted nematic liquid crystal cell.

32. A process for forming a compensator for an LC display comprising coating a B layer in a solvent onto an A layer wherein one or more A layers have in-plane retardation greater than 20nm and one or more B layers that contain an amorphous polymer and have a out-of-plane birefiingence more negative than -0.01 and comprise selected polymeric materials having sufficient thickness so that the overall in-plane retardation (Rj_n) of the said compensator is greater than 20nm and the overall out-of-plane retardation (R_th) is more negative than -20nm.