Classifications

• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K3/00—Apparatus or processes for manufacturing printed circuits
  • H05K3/30—Assembling printed circuits with electric components, e.g. with resistors
  • H05K3/32—Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits
  • H05K3/34—Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits by soldering
  • H05K3/3465—Application of solder
  • H05K3/3485—Application of solder paste, slurry or powder
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10D—INORGANIC ELECTRIC SEMICONDUCTOR DEVICES
  • H10D62/00—Semiconductor bodies, or regions thereof, of devices having potential barriers
  • H10D62/10—Shapes, relative sizes or dispositions of the regions of the semiconductor bodies; Shapes of the semiconductor bodies
  • H10D62/117—Shapes of semiconductor bodies
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10W—GENERIC PACKAGES, INTERCONNECTIONS, CONNECTORS OR OTHER CONSTRUCTIONAL DETAILS OF DEVICES COVERED BY CLASS H10
  • H10W72/00—Interconnections or connectors in packages
  • H10W72/01—Manufacture or treatment
  • H10W72/012—Manufacture or treatment of bump connectors, dummy bumps or thermal bumps
• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
  • H05K2201/09—Shape and layout
  • H05K2201/09145—Edge details
  • H05K2201/09154—Bevelled, chamferred or tapered edge
• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
  • H05K2201/09—Shape and layout
  • H05K2201/09818—Shape or layout details not covered by a single group of H05K2201/09009 - H05K2201/09809
  • H05K2201/099—Coating over pads, e.g. solder resist partly over pads
• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
  • H05K2203/05—Patterning and lithography; Masks; Details of resist
  • H05K2203/0562—Details of resist
  • H05K2203/0568—Resist used for applying paste, ink or powder
• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
  • H05K2203/13—Moulding and encapsulation; Deposition techniques; Protective layers
  • H05K2203/1377—Protective layers
  • H05K2203/1394—Covering open PTHs, e.g. by dry film resist or by metal disc
• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K3/00—Apparatus or processes for manufacturing printed circuits
  • H05K3/30—Assembling printed circuits with electric components, e.g. with resistors
  • H05K3/32—Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits
  • H05K3/34—Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits by soldering
  • H05K3/3452—Solder masks
• • H—ELECTRICITY
  • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
  • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
  • H05K3/00—Apparatus or processes for manufacturing printed circuits
  • H05K3/40—Forming printed elements for providing electric connections to or between printed circuits
  • H05K3/403—Edge contacts; Windows or holes in the substrate having plural connections on the walls thereof
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10W—GENERIC PACKAGES, INTERCONNECTIONS, CONNECTORS OR OTHER CONSTRUCTIONAL DETAILS OF DEVICES COVERED BY CLASS H10
  • H10W72/00—Interconnections or connectors in packages
  • H10W72/20—Bump connectors, e.g. solder bumps or copper pillars; Dummy bumps; Thermal bumps
  • H10W72/251—Materials
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10W—GENERIC PACKAGES, INTERCONNECTIONS, CONNECTORS OR OTHER CONSTRUCTIONAL DETAILS OF DEVICES COVERED BY CLASS H10
  • H10W72/00—Interconnections or connectors in packages
  • H10W72/20—Bump connectors, e.g. solder bumps or copper pillars; Dummy bumps; Thermal bumps
  • H10W72/251—Materials
  • H10W72/252—Materials comprising solid metals or solid metalloids, e.g. PbSn, Ag or Cu

Definitions

• solder is a material that typically contains tin and lead and that is commonly used during the manufacturing of electronic circuit boards. Solder generally has a lower melting temperature than the metals that may be included, as lines or layers, in the circuit boards. Hence, once two or more metal lines or layers have been formed in a circuit board, solder may be used to form an electrical contact between the layers and/or lines.
• FIGURES 1A-1E show cross-sections of semiconductor device structures after various steps of a process for depositing solder on a planar semiconductor substrate surface have been performed according to the related art.
• FIGURE 1A is a cross- sectional view of a semiconductor substrate 100, sich as silicon or gallium arsenide, and of an organic film 110, such as a photoresist film, that has been deposited on the semiconductor substrate 100.
• the organic film 110 according to the related art, is typically spun onto the substrate 100 and is typically in contact with the entire surface of the semiconductor substrate 100.
• FIGURE IB is a cross -sectional view of the layers 100, 110 discussed above after the organic film 110 has been selectively etched to form a series of holes 120 (or channels, troughs, grooves, or openings) above the substrate 100.
• the holes 120 in the organic film 110 may be fonned via photo- lithography or by any other process known in the art of semiconductor device manufacturing.
• FIGURE 1C is a cross -sectional view of the substrate 100 and organic film 110 discussed above after the holes 120 in the organic film 110 have been filled, at least partially, with solder paste 130.
• Solder paste in general, typically includes an admixture of flux and solder particles.
• the solder paste 130 shown in FIGURE 1C may be deposited in the holes 120 by any process known in the art. For example, a process similar to the stencil printing process used in the surface mount assembly process can be used. Specifically, a squeegee can be used to "rdl" a bead of solder paste 130 across the organic film 110 to deposit the solder paste 130 into the holes 120.
• FIGURE ID is a cross -sectional view of the substrate 100 after the solder paste 130 has been heat-treated to fonn solder bumps 140 on the substrate 100.
• the temperature of the solder paste 130 that had been in the holes 120 of the organic film 110 was raised. The higher temperature caused the flux portion that had been in the paste 130 to liquefy and activate the metal surfaces and caused the solder particles in the paste to melt. In the molten phase, the solder will wet to a solderable pad on the substrate surface while the surface tension of the liquid solder will cause the molten solder to form the shape of the solder bump.
• solid solder bumps 140 were formed.
• FIGURE IE is a cross-sectional view of the substrate 100 and the solder bumps 140 after the organic film 110 has been removed.
• the organic film 110 may be removed by any process that known in the art.
• the substrate 100 may have additional structures, such as metal layers and metal lines, deposited thereon, and the solder bumps 140 can be used to electrically connect two or more metal layers or lines.
• a method of depositing solder including the steps of providing a substrate that includes a substantially planar surface and a sloped surface adjacent to the substantially planar surface, forming a wettable layer on a portion of the sloped surface, and forming a solder layer on a first portion of the wettable layer.
• a semiconductor device including a substrate having a substantially planar surface and an interior sloped surface, a wettable layer adhered to a portion of the interior sloped surface, and a solder layer adhered to a first portion of the wettable layer.
• FIGURES 1A-E show the steps of a process for depositing solder on a planar surface according to the related art
• FIGURES 2A-I illustrate step of a process for depositing solder on a sloped surface.
• DETAILED DESCRIPTION The following detailed description is presented to enable any person skilled in the art to make and use devices that include solder. For purposes of explanation, specific nomenclature is set forth to provide a thorough understanding of making and using such devices. However, it will be apparent to one skilled in the art that these specific details are not required to make and use the devices. Descriptions of specific applications are provided only as representative examples.
• solder bumps have been deposited exclusively on substantially planar surfaces, such as the surface of the substrate 100 shown in FIGURES 1A-E and discussed in detail above. However, solder bumps have generally not been deposited on sloped surfaces. Since semiconductor devices typically include both substantially planar and sloped surfaces, the need exists for methods to deposit solder on sloped ( i.e. , non-planar) surfaces.
• FIGURES 2A-I illustrate various embodiments of methods of depositing solder and solder bumps on sloped surfaces.
• FIGURE 2A of the Drawings there is illustrated a cross- sectional view of a substrate 200 that includes two substantially planar surfaces 210 and two sloped surfaces 220.
• the two sloped surfaces 220 may be on opposite sides of the same square hole or rectangular channel fonned in the substrate 200, as is well understood in the art.
• each of the sloped surfaces 220 may be positioned adjacent to a substantially planar surface 210 of the substrate 200.
• the slope of the sloped surfaces 220 relative to the planar surface 210 may be at any angle greater than 0° and less than 90°, measured relative to a line extending horizontally from the planar surface 210. However, the 5°, 10°, 20°, 30°, 45°, 60°, 70°, and 80° angles, plus or minus 2.5°, are preferred in certain embodiments.
• the sloped surfaces 220 may be fonned by etching the substrate 200.
• the etching step that forms the sloped surfaces 220 may include anisotropically etching completely through the substrate 200 to form a hole. Alternately, the etching step may form a channel in the substrate 200 and/or may not etch completely through the substrate 200.
• FIGURE 2B is a cross -sectional view of the substrate 200 shown in FIGURE 2 A and of a wettable layer 230 that has been formed on a portion of one of the sloped surfaces 220 of the substrate 200.
• the wettable layer 230 may include a metal that is wettable by solder ⁇ i.e. , a metal on which solder can spread evenly, as opposedto beading up on).
• the wettable layer 230 may be fonned by any process known in the art including, but not limited to, evaporation, sputtering, and plasma deposition.
• Metals that may be included in the wettable layer 230 include, but are not limited to, gold, silver, and copper. Compounds that are solder-wettable may also be used.
• the wettable layer 230 may be formed partially on the sloped surface 220 and partially on the planar surface 210 of the substrate 200.
• the portion of the wettable layer 230 that is formed on the planar surface 210 of the substrate 200 may be substantially planar.
• the wettable layer 230 may be deposited exclusively on the sloped surfaces 220. The benefits of forming a portion of the wettable layer 230 on the planar surface 210 will become apparent from the discussion below, as will the benefits of forming the wettable layer 230 exclusively on the sloped surface 220.
• FIGURE 2C is a cross -sectional view of the substrate 200 and wettable layer 230 discussed above, after a coating layer 240 has been formed on a portion of the wettable layer 230 and of the substrate 200.
• the coating layer 240 may include one or more dielectric materials that are not solder-wettable. Such materials include, but are not limited to, oxides, polyimides and solder masks.
• the coating layer 240 may be fonned by any method known in the art and may be thought of as a mask for the wettable layer 230 during solder deposition, as will be seen below.
• FIGURE 2D is a cross -sectional view of the structure shown in FIGURE 2C after an organic film 250 or organic layer has been adhered to a portion of the substantially planar surface 210 of the substrate 200.
• the organic film 250 or layer may or may not be adhered to the wettable layer 230 or the coating layer 240, but may be in contact with both the wettable layer 230 and the coating layer 240.
• the organic film 250 is not in contact with the sloped surfaces 220 of the substrate 200. Rather, the organic film 250 forms a bridge over the sloped surfaces 220 and over any hole or cavity that has been etched or otherwise formed in the substrate 200.
• a convenient method for substantially preventing the organic film 250 from adhering to or contacting the sloped surfaces 220 of the substrate 200 involves using a rigid or semi-rigid and substantially planar sheet of material as the organic film 250.
• the sheet may be adhered to the substantially planar surfaces 210 of the substrate 200 after the wettable layer 230 and the coating layer 240 have been formed. Then, because of the inherent rigidity of the substantially planar sheet, the organic film 250 will not dip into the etched portion of the substrate 200 and will therefore not contact the sloped surfaces 220, as shown in FIGURE 2D.
• No limitations are made on the materials that may be included in the organic film 250. However, polymers that can form thin sheets with enough rigidity to bridge the etched portion of the substrate 200 are prefened.
• the organic film 250 may be fixed or held in place relative to the substrate 200 via electrostatic forces, a chemical adhesive, and/or mechanical forces.
• the organic film 250 may be rolled out over the substrate 200 or may be wrapped around the substrate 200 like plastic food wrap around a plate.
• FIGURE 2E is a cross-sectional view of the structure shown in FIGURE 2D after a section of the organic film 250 has been removed, leaving an empty volume 255 above portions of the wettable layer 230 and coating layer 240.
• the removed section of the organic film 250 is divided into two portions to facilitate description.
• the first portion of the removed section designated by the reference numeral 256, is positioned above one of the planar surfaces 210 of the substrate 200 and contacts a planar portion of the wettable layer 230 before removal.
• the first portion 256 is supported from underneath by the substrate 200, the wettable layer 230, and the coating layer 240.
• the second portion of the removed section designated by the reference numeral 257, is positioned above the etched portion of the substrate 200 before removal and is not supported by the substrate 200. Instead, the second portion 257 of the removed section is bridging the etched portion of the substrate 200.
• the remaining organic film 250 retains its substantially planar shape and continues to bridge across the etched portion of the substrate 200. In other words, the organic film 250 does not dip or droop into the etched portion of the substrate 200 and does not contact the sloped surface 220.
• FIGURE 2E a gap 260 or unfilled space is formed between the organic film 250 and the wettable layer 230.
• the gap 260 is fonned adjacent to one of the sloped surfaces 220 of the substrate 200.
• FIGURE 2F is a top view of the structure illustrated in FIGURE 2E.
• the removed section of the organic film 250 represented by the empty volume 255, has a rectangular shape and a width that is slightly larger than the width of the wettable layer 230 and the coating layer 240. Accordingly, the substrate 200 is exposed on both sides of the wettable layer 230 and the coating layer 240.
• FIGURE 2G is a cross -sectional view of the structure illustrated in FIGURES 2E and 2F, after the empty volume 255 has been substantially filled with solder paste 270.
• the solder paste 270 may be placed in the volume 255 by any means known in the art of semiconductor device manufacturing and does not have to exactly fill the entire volume 255. Any solder paste that is deposited on the organic film 250 may, optionally, be removed after the volume 255 has been substantially filled.
• the solder paste 270 is viscous enough and the gap 260 is small enough such that little or none of the solder paste 270 flows through the gap 260 until the solder paste 270 is heated.
• FIGURE 2H is a cross -sectional view of the structure shown in FIGURE 2G after the solder paste 270 has been heated and processed to form a solder layer 280 on at least a portion of the wettable layer 230.
• the solder layer 280 may be fonned on a portion of or all of the wettable layer 230 that is not covered by the coating layer 240.
• the solder layer 280 may be formed by thermally treating the solder paste 270 in such a way that the flux in the paste 270 liquifies and activates the metal surfaces and the solder particles in the paste melt together to form the denser solder layer 280.
• the solder layer 280 may be formed by heating the solder paste 270 to about 180°C or less, plus or minus approximately 5°C. Although a solder layer 280 is shown in FIGURE 2G, solder bumps may also be formed if more solder paste 270 is used, as is understood in the art.
• FIGURE 21 is a cross-sectional view of the structure shown on the left-hand side of FIGURE 2H after the organic film 250 has been removed. The organic film 250 may be removed by any method known in the art such as, but not limited to, chemical dissolution, heating, and application of mechanical force to cause de -lamination.
• the structure shown in FIGURE 21 includes a substrate 200 having a substantially planar surface 210 and an interior sloped surface 220. Also included is a wettable layer 230, which may include a metal, and that is adhered to a portion of the interior sloped surface. According to alternate structures, the entire wettable layer 230 may be adhered to the sloped surface 220, if desired. Adhered to a portion of the wettable layer 230 is the solder layer 280. In FIGURE 21, the solder layer 280 is positioned over both a portion of the slopedsurface 220 and a portion of the planar surface 210. However, according to alternate structures, the solder layer 280 may be formed and/or positioned exclusively over all or a portion of the sloped surface 220.
• the wettable layer 230 When the wettable layer 230 is fonned over a portion of the planar surface 210, the wettable layer may be used to provide an electrical contact to a line or layer formed on the planar surface 210. As illustrated in FIGURE 21, a coating layer 240 adheres to a portion of the wettable layer 230.
• the coating layer 240 during the manufacturing of the structure shown in FIGURE 21, can assist in preventing deposition of the solder layer 280 in undesired locations by effectively masking the wettable layer 230.
• the coating layer 240 may, optionally, be removed from the structure to facilitate the formation of electrical connections to lines and/or layers on the adjacent planar surface 210.
• the coating layer 240 may include any material that is not wettable by solder ⁇ i.e., on which solder does not readily spread).
• the coating layer 240 may include a dielectric material or, more specifically, an oxide.
• the solder layer 280 may, among other materials, include a tin-bismuth compound or a eutectic, tin-lead compound.
• no particular restrictions are placed on the materials that may be used to build the structure illustrated in FIGURE 21. While the aforementioned and illustrated methods for forming a solder on a sloped surface have been described in connection with exemplary embodiments, those skilled in the art will understand that many modifications in light of these teachings are possible, and this application is intended to cover any variation thereof.

Landscapes

• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Microelectronics & Electronic Packaging (AREA)
• Electric Connection Of Electric Components To Printed Circuits (AREA)
• Wire Bonding (AREA)

Priority Applications (2)

Applications Claiming Priority (2)

Publications (2)

Family

ID=32681800

Family Applications (1)

Country Status (4)

Families Citing this family (2)

Family Cites Families (6)

• 2003
  • 2003-03-12 US US10/385,487 patent/US6764937B1/en not_active Expired - Fee Related
  • 2003-10-30 US US10/698,725 patent/US6979906B2/en not_active Expired - Fee Related
• 2004
  • 2004-03-04 WO PCT/US2004/006912 patent/WO2004082347A2/en not_active Ceased
  • 2004-03-04 JP JP2006509212A patent/JP2006520543A/ja not_active Withdrawn
  • 2004-03-04 EP EP04717495A patent/EP1602265A2/en not_active Withdrawn

Also Published As

Similar Documents

Legal Events