WO2004058390A1 - Method for encapsulating phase transitional paraffin compounds using melamine-formaldehyde and microcapsule resulting therefrom - Google Patents
Method for encapsulating phase transitional paraffin compounds using melamine-formaldehyde and microcapsule resulting therefrom Download PDFInfo
- Publication number
- WO2004058390A1 WO2004058390A1 PCT/CN2003/001106 CN0301106W WO2004058390A1 WO 2004058390 A1 WO2004058390 A1 WO 2004058390A1 CN 0301106 W CN0301106 W CN 0301106W WO 2004058390 A1 WO2004058390 A1 WO 2004058390A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- formaldehyde
- melamine
- solution
- weight
- mixture
- Prior art date
Abstract
Description
Claims