WO2004017341A1 - Procede de production de films magnetiques composites - Google Patents

Procede de production de films magnetiques composites Download PDF

Info

Publication number
WO2004017341A1
WO2004017341A1 PCT/CA2003/001228 CA0301228W WO2004017341A1 WO 2004017341 A1 WO2004017341 A1 WO 2004017341A1 CA 0301228 W CA0301228 W CA 0301228W WO 2004017341 A1 WO2004017341 A1 WO 2004017341A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
inorganic
composite material
polymer matrix
magnetic
Prior art date
Application number
PCT/CA2003/001228
Other languages
English (en)
Inventor
Igor Zhitomirsky
Marek Niewczas
Anthony Petric
Original Assignee
Mcmaster University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mcmaster University filed Critical Mcmaster University
Priority to AU2003257328A priority Critical patent/AU2003257328A1/en
Publication of WO2004017341A1 publication Critical patent/WO2004017341A1/fr

Abstract

L'invention a trait à un procédé de préparation de films hybrides superparamagnétiques et de nanoparticules encapsulées dans une matrice polymérique. Ledit procédé se fonde sur la synthèse in situ de nanoparticules inorganiques dans une matrice organique, à partir de solutions de sels métalliques contenant des additifs de traitement et un polymère dissous. Les films hybrides contenant les nanoparticules encapsulées dans la matrice polymérique sont formés par l'électrodéposition de nanoparticules inorganiques formées à partir des métaux, et par le dépôt simultané d'un film polymérique, à travers lequel les nanoparticules sont dispersées.
PCT/CA2003/001228 2002-08-19 2003-08-19 Procede de production de films magnetiques composites WO2004017341A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2003257328A AU2003257328A1 (en) 2002-08-19 2003-08-19 Method for producing composite magnetic films

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US40415102P 2002-08-19 2002-08-19
US60/404,151 2002-08-19

Publications (1)

Publication Number Publication Date
WO2004017341A1 true WO2004017341A1 (fr) 2004-02-26

Family

ID=31888331

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA2003/001228 WO2004017341A1 (fr) 2002-08-19 2003-08-19 Procede de production de films magnetiques composites

Country Status (2)

Country Link
AU (1) AU2003257328A1 (fr)
WO (1) WO2004017341A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7569254B2 (en) * 2005-08-22 2009-08-04 Eastman Kodak Company Nanocomposite materials comprising high loadings of filler materials and an in-situ method of making such materials
US8101680B1 (en) 2010-10-12 2012-01-24 Sabic Innovative Plastics Ip B.V. Methods of preparing polymer nanocomposites
CN102568744A (zh) * 2012-02-22 2012-07-11 南京航空航天大学 一种复合永磁薄膜的制备方法及复合永磁薄膜
CN103329221A (zh) * 2011-01-26 2013-09-25 罗伯特·博世有限公司 磁性复合材料的合成

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06176915A (ja) * 1992-12-07 1994-06-24 Ricoh Co Ltd 磁性材料およびその製造方法
JPH06338432A (ja) * 1993-05-28 1994-12-06 Ricoh Co Ltd 磁性薄膜の製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06176915A (ja) * 1992-12-07 1994-06-24 Ricoh Co Ltd 磁性材料およびその製造方法
JPH06338432A (ja) * 1993-05-28 1994-12-06 Ricoh Co Ltd 磁性薄膜の製造方法

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
AMIGO R ET AL: "ELECTROCHEMICAL SYNTHESIS OF NEW MAGNETIC MIXED OXIDES OF SR AND FE: COMPOSITION, MAGNETIC PROPERTIES, AND MICROSTRUCTURE", CHEMISTRY OF MATERIALS, AMERICAN CHEMICAL SOCIETY, WASHINGTON, US, vol. 12, no. 2, February 2000 (2000-02-01), pages 573 - 579, XP000927813, ISSN: 0897-4756 *
PATENT ABSTRACTS OF JAPAN vol. 018, no. 504 (E - 1608) 21 September 1994 (1994-09-21) *
PATENT ABSTRACTS OF JAPAN vol. 1995, no. 03 28 April 1995 (1995-04-28) *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7569254B2 (en) * 2005-08-22 2009-08-04 Eastman Kodak Company Nanocomposite materials comprising high loadings of filler materials and an in-situ method of making such materials
US8101680B1 (en) 2010-10-12 2012-01-24 Sabic Innovative Plastics Ip B.V. Methods of preparing polymer nanocomposites
CN103329221A (zh) * 2011-01-26 2013-09-25 罗伯特·博世有限公司 磁性复合材料的合成
CN102568744A (zh) * 2012-02-22 2012-07-11 南京航空航天大学 一种复合永磁薄膜的制备方法及复合永磁薄膜

Also Published As

Publication number Publication date
AU2003257328A1 (en) 2004-03-03

Similar Documents

Publication Publication Date Title
Behrens et al. Magnetic nanocomposites
Sharifi et al. Ferrite-based magnetic nanofluids used in hyperthermia applications
Karimzadeh et al. Effective preparation, characterization and in situ surface coating of superparamagnetic Fe3O4 nanoparticles with polyethyleneimine through cathodic electrochemical deposition (CED)
Karimzadeh et al. Preparation, characterization and PEGylation of superparamagnetic Fe3O4 nanoparticles from ethanol medium via cathodic electrochemical deposition (CED) method
Karaagac et al. A simple way to synthesize superparamagnetic iron oxide nanoparticles in air atmosphere: iron ion concentration effect
Tan et al. Room-temperature soft magnetic iron oxide nanocrystals: synthesis, characterization, and size-dependent magnetic properties
Chiang et al. Synthesis of monodisperse FeAu nanoparticles with tunable magnetic and optical properties
Amirabadizadeh et al. Synthesis of ferrofluids based on cobalt ferrite nanoparticles: Influence of reaction time on structural, morphological and magnetic properties
Wong et al. Layer-by-layer assembly of a magnetic nanoparticle shell on a thermoresponsive microgel core
Granitzer et al. Magnetic study of Fe3O4 nanoparticles incorporated within mesoporous silicon
Wang et al. Core− shell-structured magnetic ternary nanocubes
Riaz et al. Controlled nanostructuring of multiphase core-shell iron oxide nanoparticles
Parekh et al. Ternary monodispersed Mn0. 5Zn0. 5Fe2O4 ferrite nanoparticles: preparation and magnetic characterization
Anokhin et al. Silica coated hard-magnetic strontium hexaferrite nanoparticles
Gandha et al. Effect of ${\rm RuCl} _ {3} $ on Morphology and Magnetic Properties of CoNi Nanowires
Heydaryan et al. Tuning specific loss power of CoFe2O4 nanoparticles by changing surfactant concentration in a combined co-precipitation and thermal decomposition method
Jadhav et al. The influence of coating on the structural, magnetic and colloidal properties of LSMO manganite and the heating mechanism for magnetic fluid hyperthermia application
Ehsani et al. Magnetic evaluation of the nanoparticles coated with polyvinylpyrrolidone and polyvinyl chloride nanoparticles synthesized by electro-deposition method for hyperthermia application
Choudhary et al. Low temperature field dependent magnetic study of the Zn0. 5Co0. 5Fe2O4 nanoparticles
Pinkas et al. Sonochemical synthesis of amorphous yttrium iron oxides embedded in acetate matrix and their controlled thermal crystallization toward garnet (Y3Fe5O12) and perovskite (YFeO3) nanostructures
Zhitomirsky et al. Electrodeposition of hybrid organic–inorganic films containing iron oxide
Sánchez et al. Synthesis of MnxGa1− xFe2O4 magnetic nanoparticles by thermal decomposition method for medical diagnosis applications
Rezaei et al. An investigation on magnetic-interacting Fe 3 O 4 nanoparticles prepared by electrochemical synthesis method
Ali et al. Size and shape control synthesis of iron oxide–based nanoparticles: Current status and future possibility
KR101505210B1 (ko) 니켈-철-아연 합금 나노입자

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP