WO2003104346A1 - Haftklebemasse für ein- oder beidseitig haftklebrige klebefolienstreifen und verfahren zur herstellung hierzu - Google Patents
Haftklebemasse für ein- oder beidseitig haftklebrige klebefolienstreifen und verfahren zur herstellung hierzu Download PDFInfo
- Publication number
- WO2003104346A1 WO2003104346A1 PCT/EP2003/004825 EP0304825W WO03104346A1 WO 2003104346 A1 WO2003104346 A1 WO 2003104346A1 EP 0304825 W EP0304825 W EP 0304825W WO 03104346 A1 WO03104346 A1 WO 03104346A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive
- psa
- sensitive adhesive
- mixture
- pressure
- Prior art date
Abstract
Description
Claims