Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
  • A61C7/00—Orthodontics, i.e. obtaining or maintaining the desired position of teeth, e.g. by straightening, evening, regulating, separating, or by correcting malocclusions
  • A61C7/12—Brackets; Arch wires; Combinations thereof; Accessories therefor
  • A61C7/14—Brackets; Fixing brackets to teeth
  • A61C7/16—Brackets; Fixing brackets to teeth specially adapted to be cemented to teeth
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/70—Preparations for dentistry comprising inorganic additives
  • A61K6/71—Fillers
  • A61K6/76—Fillers comprising silicon-containing compounds
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
  • A61C2202/00—Packaging for dental appliances

Definitions

• Orthodontic treatment involves movement of malpositioned teeth to orthodontically correct positions.
• Tiny orthodontic appliances known as brackets are connected to exterior surfaces of the patient's teeth, and an archwire is placed in a slot of
• each bracket The archwire forms a track to guide movement of the teeth to desired positions for correct occlusion. End sections of the archwire are often received in appliances known as buccal tubes that are fixed to the patient's molar teeth. In recent years it has become common practice to bond orthodontic appliances directly to the surface of the tooth.
• Adhesive precoated brackets are known and offer significant advantages to the orthodontist. Adhesive precoated brackets have a bonding base upon which the manufacturer may apply a precise quantity of adhesive such as a photocurable adhesive.
• the bracket When it is desired to mount the bracket on a tooth, the bracket is simply removed from the package and placed directly onto the tooth surface.
• Adhesives used on precoated brackets are, in general, more viscous (i.e., less fluid) than other available orthodontic bonding adhesives. The higher viscosity ensures that the adhesive retains its shape and does not separate or distort when the bracket is lifted from the package for use.
• some orthodontists prefer the use of less viscous (i.e., more fluid) adhesives in order to facilitate manipulation of the bracket before the adhesive is cured.
• brackets with less viscous adhesives are relatively easy to slide along the tooth surface when an effort is made to align the bracket in a proper, precise orientation on the tooth before the adhesive is cured.
• Brackets precoated with one part of a two-part adhesive on the base of the bracket have been reported. After the bracket is removed from the package, a second part is applied to the bracket base and/or the tooth surface, and the bracket is then applied to the surface of the patient's tooth.
• Reported packages for brackets precoated with one part of a two-part chemical-cure adhesive include, referring to Fig. 1, an assembly 10 having a carrier 12 with arms 14 and 15 to suspend the bracket 16 with adhesive 22 in the container 18, and, referring to Fig.
• the present invention provides an article including an orthodontic bracket having a base for bonding the bracket to a tooth, a first part of an at least two-part adhesive on the base of the bracket, and a release substrate including a surface in contact with the first part.
• the first part of the at least two-part adhesive includes a polymerizable component, a polymerization initiator, and at least about 10% by weight, based on the total weight of the first part, of a filler including a silica filler.
• the first part has a static yield stress at 28°C of at least about 4000 dynes/cm 2 .
• the first part has a steady state viscosity of about 3 x 10 2 Pa-s to about 7 x 10 4 Pa-s at 28°C.
• the orthodontic bracket may optionally be provided in a kit that includes, for example, a second part of the at least two-part adhesive including a polymerizable component and an activator.
• the present invention provides a method for bonding an orthodontic bracket to a tooth.
• the method includes providing an orthodontic bracket having a base for bonding the bracket to a tooth, a first part of an at least two-part adhesive on the base, and a release substrate including a surface in contact with the first part, wherein the first part includes a polymerizable component, a polymerization initiator, and at least about 10% by weight, based on the total weight of the first part, of a filler including a silica filler; applying a second part of the at least two-part adhesive to the tooth surface, the second part including a polymerizable component and an activator for the polymerization initiator in the first part; separating the orthodontic bracket having the first part on the base from the release substrate; and applying the base of the bracket to the tooth surface having thereon the second part of the at least two-part adhesive.
• the orthodontic bracket bonds to the tooth with an adhesion of at least about 7 Mpa.
• the present invention provides a method for bonding an orthodontic bracket to a tooth.
• the method includes providing an orthodontic bracket having a base for bonding the bracket to a tooth, a first part of an at least two-part adhesive on the base, and a release substrate including a surface in contact with the first part, wherein the first part includes a polymerizable component, a polymerization initiator, and at least about 10% by weight, based on the total weight of the first part, of a filler including a silica filler; separating the orthodontic bracket having the first part on the base from the release substrate; applying a second part of the at least two- part adhesive to the first part on the base of the bracket, the second part including a polymerizable component and an activator for the polymerization initiator in the first part; and applying the base of the bracket to the tooth surface.
• the orthodontic bracket bonds to the tooth with an adhesion of at least about 7 MPa.
• orthodontic bracket refers to any device with open or closed archwire slots intended to be bonded to the teeth including, for example, buccal tubes, lingual buttons, and cleats. Thus, the term “orthodontic bracket” does not encompass orthodontic bands.
• the bracket has a base for receiving adhesive and it can be made of metal, plastic, ceramic, and combinations thereof.
• a "two-part” adhesive refers to an adhesive composition having components in two separate parts, with each part being stable to hardening when stored separately. The adhesive is hardened upon contacting the two parts.
• the term “adhesive” may refer to the first and/or second part of a two-part adhesive.
• “filler” means a particulate material (e.g., an inorganic oxide) in dry powder form capable of being dispersed in a resin.
• a dental composite preferably includes a powder dispersed in a resin.
• sica refers to the compound silicon dioxide. See Kirk- Othmer Encyclopedia of Chemical Technology, 4th Ed., Vol. 21, pp. 977-1032 (1977).
• amorphous silica refers to silica that does not have a crystalline structure as defined by x-ray diffraction measurements.
• examples of amorphous silica include silica sols, silica gels, precipitated silica, and pyrogenic silica.
• pyrogenic silica and “fumed silica” are used interchangeably and refer to amorphous silicas formed in the vapor phase.
• Pyrogenic silica may contain, for example, a few hundred primary particles fused into branched- chain, three-dimensional aggregates.
• Examples of pyrogenic silica include products available under the trade designations AEROSIL OX-50, AEROSIL-130, AEROSIL-150,
• AEROSIL-200 and AEROSIL R-972 available from DeGussa AG, (Hanau, Germany) and CAB-O-SIL M5 and CAB-O-SIL TS720 available from Cabot Corp. (Boston, MA).
• base filler refers to fillers other than fumed silica fillers.
• Base fillers include, for example, non-reactive fillers (e.g., quartz fillers), reactive fillers (e.g., fluoroaluminosilicate glass), and combinations thereof.
• silane treated means that the surface of a particle has been modified by application of a silane (e.g., dichlorodimethylsilane).
• the silane may be a coupling agent that includes a reactive functionality (e.g., ⁇ - methacryloxypropyltrimethoxysilane, A 174) .
• aggregate length means the longest dimension of the aggregate.
• aggregate is descriptive of strongly associated primary particles often bound together by, for example, by residual chemical treatment, covalent chemical bonds, ionic chemical bonds, or hydrogen bonds.
• slump refers to the phenomenon of flow under the force of gravity. It is desirable that orthodontic adhesives do not slump because after they are placed in the mouth, the practitioner wants the imparted shape to remain unchanged until the materials are cured. It is also preferable that the adhesive can support the weight of the appliance without slumping. Slumping can lead to bracket drift and skating of the adhesive coated bracket on the tooth. Materials with a sufficiently high yield stress will not slump; that is, they will not flow under the stress of gravity. The yield stress of a material is the minimum stress required to cause the material to flow, and is described in Rheology Principles, Measurements, and Applications, C. W. Macosko, VCH Publishers, Inc., New York, 1994, p. 92.
• the yield stress of an orthodontic adhesive be sufficiently high that the material does not slump in all types and sizes of uses.
• the yield stress of an orthodontic adhesive will be sufficiently high that the material does not substantially slump when supporting a bracket on top of the adhesive. If the adhesive does flow out from underneath the bracket, preferably it will remain on the release substrate when the bracket is removed.
• the pre-cured adhesive be preapplied to an orthodontic appliance and the resulting adhesive precoated appliance packaged for later use by a practitioner.
• the adhesive can be preapplied to a release substrate and then packaged for later use by a practitioner to adhere an orthodontic appliance to a tooth.
• the preapplied (or precoated) adhesive does not slump under typical package storage and shipping conditions, for example, storage for up to 6 months, preferably for up to about 1 year, and more preferably for up to about 3 years.
• typical package storage and shipping conditions for example, storage for up to 6 months, preferably for up to about 1 year, and more preferably for up to about 3 years.
• ambient temperature i.e., room temperature
• the adhesive can be evaluated for adhesive/bracket flow-out (or "flow-out”) and/or adhesive/bracket vertical slip (or “slip”) according to the test methods described herein.
• flow-out measures the tendency over time of an adhesive to flow outwardly on a horizontally mounted release substrate beneath an orthodontic bracket
• slip measures the tendency of an adhesive-coated bracket vertically mounted on a release substrate to slip downward over time.
• the flow-out (after one week at 40°C) and slip values are less than about 0.4 mm, more preferable less than about 0.25 mm, and most preferable 0 (zero).
• Flow-out or slip values greater than about 0.5 mm are readily apparent to the naked eye and can lead to significant problems during storage and/or shipping of the packaged adhesive. Such problems can include, for example, shape distortion of the adhesive on a release liner or, more seriously, separation of an orthodontic appliance from the adhesive when the appliance is removed from the package.
• the adhesive have a static yield stress at 28 °C of about 4000 dynes/cm 2 to about 100,000 dynes/cm 2 ; and have a steady state viscosity at 28°C of about 3 x 10 2
• Pascal-seconds (Pa-s) to about 7 x 10 4 Pa-s.
• (meth)acrylate is a shorthand reference to acrylate, methacrylate, or combinations thereof
• (meth) acrylic is a shorthand reference to acrylic, methacrylic, or combinations thereof.
• chemical term "group" allows for substitution.
• Figure 1 is a side cross-sectional view of a prior art assembly that includes an orthodontic appliance.
• Figure 2 is a cross-sectional view of a prior art assembly that includes an orthodontic appliance.
• Figure 3 is a perspective view of an orthodontic article according to one embodiment of the present invention.
• the present invention provides article 10 including orthodontic bracket 16 having a base 20 for bonding the bracket 16 to a tooth, a first part of an at least two-part adhesive 22 on the base 20, and a release substrate 26 including a surface 24 in contact with the first part of the at least two-part adhesive 22.
• the release substrate 26 may be selected from a number of materials including, for example, polyolefins, poly( vinyl chloride), polyurethanes, and poly(tetrafluoroethylene).
• the surface 24 of release substrate 26 comprises a number of pores, and no more than about 50% by weight of the first part 22 is within the pores.
• the orthodontic bracket 16 is capable of bonding to a tooth when the base 20 of the bracket 16, after being separated from the release substrate 26, is applied to a tooth surface having a second part of the at least two-part adhesive on the surface.
• the first part of the at least two-part adhesive on the bracket includes a polymerizable component, a polymerization initiator, and a filler.
• the second part of the at least two-part adhesive preferably includes a polymerizable component and an activator.
• the article is preferably packaged in a container that provides barriers to the transmission of light, water vapor, and/or oxygen.
• the article is preferably provided as a kit.
• the present invention preferably provides a method of bonding an orthodontic bracket to a tooth.
• the first part of the at least two-part adhesive preferably has a static yield stress at 28 °C of at least about 4000 dynes/cm .
• the first part of the at least two-part adhesive preferably has a steady state viscosity of about 3 x 10 2 Pa-s to about 7 x 10 4 Pa-s at 28°C.
• the first part of the at least two-part adhesive preferably includes at least about 10% by weight, based on the total weight of the adhesive, of a filler comprising a silica filler.
• the first part further includes a base filler.
• the adhesives used in the present invention are preferably substantially free of solvent, and substantially free of added water.
• substantially free of added water means that the composition does not contain water that is intentionally added as a non-complexed or coordinated entity. It is understood that many materials, such as metals or glasses, contain water that is taken up from the atmosphere or is present as a coordination complex in its normal state. Water taken up by hygroscopic materials or present as a hydrate is permissibly present in the compositions described herein. Any water that is present in the composition, regardless of source, should not be present in amounts such that the water will have a deleterious effect on the long term properties of the composition. For example, water should not be present in an amount that would facilitate reaction of an acid-reactive filler with an acidic component so that lumpiness or graininess of the material develops during commercially desired storage times.
• the adhesives used in the present invention are at least two-part adhesives.
• the article disclosed in the present invention includes a first part of the at least two-part adhesive on the base of an orthodontic bracket.
• a second part of the at least two-part adhesive is applied to a tooth surface.
• the adhesive hardens and bonds the orthodontic bracket to the tooth.
• the second part may be applied to the first part on the base of the bracket, and the bracket is then applied to the tooth surface.
• the first part of the at least two-part adhesive includes a polymerizable component, a polymerization initiator, and a filler.
• the second part of the at least two-part adhesive includes a polymerizable component and an activator.
• the second part of the at least two- part adhesive may optionally include a polymeric material including, for example, poly(methyl methacrylate).
• Exemplary two-part adhesives are disclosed, for example, in U.S. Pat. No. 5,221,202 (James). Such adhesives, however, lack high levels of silica filler, and do not provide rheological properties and bond strengths desired by some practitioners for precoated adhesives.
• Adhesives used in the present invention include a polymerizable component.
• the polymerizable component is a monomer, oligomer, or polymer that includes a polymerizable group.
• Exemplary polymerizable components are disclosed, for example, in U.S. Pat. No. 6,126,922 (Rozzi et al.) and International Patent Application Publication No. WO 00/69393 (Brennan et al.).
• the polymerizable component may also be selected from hydrophilic and acidic components disclosed herein that are polymerizable.
• Polymerizable groups may be selected from free radically polymerizable groups, cationically polymerizable groups, or combinations thereof.
• at least some of the polymerizable material is relatively lower in viscosity than other ingredients of the composition so that it serves a viscosity lowering function in the overall uncured material.
• Preferred polymerizable groups are free radically polymerizable groups.
• Preferred free radically polymerizable components are esters of (meth)acrylic acid, including, for example, methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate (“HEMA”), hydroxypropyl (meth)acrylate, tetrahydrofurfuryl (meth)acrylate, glycidyl (meth)acrylate, the diglycidyl methacrylate of bisphenol A (“Bis-GMA”), glycerol mono(meth)acrylate, glycerol di(meth)acrylate, ethylene glycol di(meth)acrylate, poly(ethylene glycol) di(meth)acrylate (where the number of repeating ethylene oxide units vary from 2 to 30, including, for example, triethylene glycol dimethacrylate (“TEGDMA”)), neopentyl glyco
• (meth)acrylates of pentaerythritol and dipentaerythritol 1 ,3-butanediol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1 ,6-hexanediol di(meth)acrylate, di-2- methacryloyloxethyl hexamethylene dicarbamate, di-2-methacryloyloxyethyl trimethylhexamethylene dicarbamate, di-2-methacryloyloxyethyl dimethylbenzene dicarbamate, methylene-bis-2-methacryloxyethyl-4-cyclohexyl carbamate, di-2- methacryloxyethyl-dimethylcyclohexane dicarbamate, di- 1 -methyl-2-methacryloxyethyl- trimethyl-hexamethylene dicarbamate, di- 1 -methyl-2-methacryloxyethy
• the first part of the at least two-part adhesive includes at least about 28% by weight, more preferably at least about 30% by weight, and most preferably at least about 32% by weight polymerizable component, based on the total weight of the first part of the at least two-part adhesive.
• the first part of the at least two-part adhesive includes at most about 40% by weight, more preferably at most about 38% by weight, and most preferably at most about 36% by weight polymerizable component, based on the total weight of the first part of the at least two-part adhesive.
• the polymerizable component may optionally include a hydrophilic component.
• a hydrophilic component is a hydrophilic monomer, oligomer, or polymer.
• Exemplary hydrophilic components are disclosed, for example, in U.S. Pat. No. 6,126,922 (Rozzi et al.) and International Patent Application Publication No. WO 00/69393 (Brennan et al.).
• Preferred hydrophilic components include, for example, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate (HEMA), hydroxypropyl (meth)acrylate, glycerol di(meth)acrylate, poly(ethylene glycol) methacrylate, poly(ethylene glycol) di(meth)acrylate, poly ⁇ ropylene glycol) (meth)acrylate, tetrahydrofurfuryl (meth)acrylate, glycidyl (meth)acrylate, and combinations thereof.
• HEMA 2-hydroxyethyl methacrylate
• glycerol di(meth)acrylate poly(ethylene glycol) methacrylate
• poly(ethylene glycol) di(meth)acrylate poly ⁇ ropylene glycol) (meth)acrylate
• tetrahydrofurfuryl (meth)acrylate glycidyl (meth)acrylate, and combinations thereof.
• hydrophilic monomers include glycerol (meth)acrylate, glycerol di(meth)acrylate, ethylene glycol di(meth)acrylate, poly(ethylene glycol) di(meth)acrylate (where the number of repeating ethylene oxide units varies from 2 to 30, including, for example, tri(ethylene glycol) dimethacrylate (TEGDMA)).
• hydrophilic components include monomers and polymers such as pyrrolidone, a moiety containing hydroxy groups and polyether groups, a moiety containing a sulfonate group, a moiety containing a sulfinate group, N-oxysuccinimide, N- vinylacetamide, and acrylamide.
• the first part of the at least two-part adhesive includes at least about 0.05% by weight, more preferably at least about 1% by weight, and most preferably at least about 3% by weight hydrophilic component, based on the total weight of the first part of the at least two-part adhesive.
• the first part of the at least two-part adhesive includes at most about 40% by weight, more preferably at most about 38% by weight, and most preferably at most about 36% by weight hydrophilic component, based on the total weight of the first part of the at least two-part adhesive.
• the polymerizable component may optionally include an acidic component.
• the acidic component is an acidic monomer, oligomer, or polymer.
• the acidic component includes at least one acidic group.
• the acidic group is preferably selected from oxyacids or thio-oxy acids of C and P. More preferably, the acidic component is a compound that is an acid of C or P.
• a precursor to the acid such as an acid anhydride, e.g., 4-methacryloxyethyl trimellitate anhydride (4-META), or ester can be used in place of the acid itself.
• the desired acid may be generated in situ.
• Preferred acids include, for example, carboxylic acids, sulfonic acids, and phenols, with carboxylic acids, alkylsulfonic acids, arylsulfonic acids, and phosphonic acids being more preferred.
• Exemplary hydrophilic components are disclosed, for example, in U.S. Pat. No. 6,126,922
• Preferred acidic groups are carboxylic acids, sulfonic acids, phosphoric acids, phosphonic acids, and boric acids, the salts of the foregoing acids or precursors of the foregoing acids that are easily converted to these acids in conditions encountered during an orthodontic procedure.
• acidic components include, for example, (mefh)acryloyl substituted carboxylic acids; phosphoric acid esters of hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and glycerol di(meth)acrylate; (meth)acrylates of pentaerythritol (e.g., pentaerythritol di(meth)acrylate); and (meth)acrylates of dipentaerythritol (e.g., dipentaerythritol penta(meth)acrylate), and combinations thereof.
• pentaerythritol e.g., pentaerythritol di(meth)acrylate
• dipentaerythritol e.g., dipentaerythritol penta(meth)acrylate
• Preferred acidic components include, for example, derivatives of amino acids, and acids such as tartaric acid, citric acid, malic acid that have been functionalized with an ethylenically unsaturated functionality.
• citric acid may be functionalized by incorporating an acryloyl or methacryloyl functionality.
• CDMA is the reaction product of citric acid and isocyanatoethyl methacrylate.
• the first part of the at least two- part adhesive includes at least about 0.01% by weight, more preferably at least about 0.05% by weight, and most preferably at least about 1% by weight acidic component, based on the total weight of the first part of the at least two-part adhesive.
• the first part of the at least two-part adhesive includes at most about 40% by weight, more preferably at most about 38% by weight, and most preferably at most about 36% by weight acidic component, based on the total weight of the first part of the at least two-part adhesive.
• the first part of the at least two-part adhesives used in the present invention includes a polymerization initiator.
• the polymerization initiator is a free radical generator.
• Useful free radical generators include, for example, peroxides (e.g., benzoyl peroxide, dicumyl peroxide, di-t-butyl peroxide) and iodonium salts (e.g., diphenyliodonium chloride, bromide, iodide, or hexafluorophosphate).
• Exemplary polymerization initiators are disclosed, for example, in U.S. Pat. No. 6,126,922 (Rozzi et al.) and International Patent Application Publication No. WO 00/69393 (Brennan et al.).
• Preferred polymerization initiators include, for example, benzoyl peroxide.
• Adhesives used in the present invention may optionally include reactive or non-reactive fillers.
• the filler can have a unimodal or polymodal (e.g., bimodal) particle size distribution.
• the filler can be an inorganic material. It can also be a crosslinked organic material that is insoluble in the polymerizable resin, and is optionally filled with inorganic filler.
• the filler is preferably non-toxic and suitable for use in the mouth.
• the filler can be radiopaque, radiolucent, or non-radiopaque.
• Reactive fillers include those that are commonly used with ionomers to form ionomer cements.
• suitable reactive fillers include metal oxides such as zinc oxide and magnesium oxide, and ion-leachable glasses including, for example, those described in U.S. Pat. Nos. 3,655,605 (Smith); 3,814,717 (Wilson et al.); 4,143,018 (Crisp et al.); 4,209,434 (Wilson et al.); 4,360,605 (Schmitt et al.), and 4,376,835 (Schmitt et al.).
• Such reactive fillers may be incorporated to modify the handling characteristics or to affect the setting properties of the ultimate composition.
• the reactive filler is preferably a finely divided reactive filler.
• the filler should be sufficiently finely divided so that it can be conveniently mixed with the other ingredients and used in the mouth.
• Average particle sizes for the filler are preferably at least about 0.2 micron and more preferably at least about 1 micron.
• Average particle sizes for the filler are preferably at most about 15 microns and more preferably at most about 10 microns. Average particle sizes may be measured by using, for example, a sedimentation analyzer.
• Preferred fillers for use in adhesives used in the present invention include acid- reactive fillers. Suitable acid-reactive fillers include metal oxides, metal salts, and glasses.
• Preferred metal oxides include barium oxide, calcium oxide, magnesium oxide, and zinc oxide.
• Preferred metal salts include salts of multivalent cations including, for example, aluminum acetate, aluminum chloride, calcium chloride, magnesium chloride, zinc chloride, aluminum nitrate, barium nitrate, calcium nitrate, magnesium nitrate, strontium nitrate, and calcium fluoroborate.
• Preferred glasses include borate glasses, phosphate glasses, and fluoroaluminosilicate glasses.
• acid reactive fillers are those that release fluoride.
• Fluoride releasing glasses in addition to providing good handling and final composition properties as discussed herein, provide the benefit of long-term release of fluoride in use including, for example, use in the oral cavity. Fluoroaluminosilicate glasses are particularly preferred.
• Suitable acid reactive fillers are also available from a variety of commercial sources familiar to those skilled in the art. Mixtures of fillers can be used if desired.
• acid reactive fillers can be subjected to a surface treatment.
• Suitable surface treatments include acid washing, treatment with phosphates, treatment with chelating agents such as tartaric acid, and treatment with a silane or silanol coupling agent.
• Particularly preferred acid reactive fillers are silanol treated fluoroaluminosilicate glass fillers, as described in U.S. Patent No. 5,332,429 (Mitra et al.).
• Non-acid reactive fillers may be selected from one or more of any material suitable for incorporation in compositions used for medical applications, such as fillers currently used in dental restorative compositions and the like.
• suitable non-acid reactive inorganic fillers are naturally-occurring or synthetic materials such as quartz (e.g., microcrystalline silicas including, for example, those available under the trade designations JJVISIL from Unimim Specialty Minerals (Elco, 111) and CONCISE from 3M Espe (St.
• nitrides e.g., silicon nitride
• glasses derived from, for example Ce, Sb, Sn, Zr, Sr, Ba, and Al, colloidal silica, feldspar, borosilicate glass, kaolin, talc, titania, and zinc glass; low Mohs hardness fillers such as those described in U.S. Pat No. 4,695,251 (Randklev); and submicron silica particles (e.g., pyrogenic silicas such as the
• Non-reactive organic filler particles include filled or unfilled pulverized polycarbonates, polyepoxides, and the like.
• Preferred non-acid reactive filler particles include quartz, submicron silica, and non- vitreous microparticles of the type described in
• the surface of the filler particles is treated with a coupling agent in order to enhance the bond between the filler and the polymerizable resin.
• suitable coupling agents include, for example, gamma- methacryloxypropyltrimethoxysilane, gamma-mercaptopropyltriethoxysilane, gamma- aminopropyltrimethoxysilane, and combinations thereof.
• the adhesive preferably includes one or more silica fillers having a surface area of at least about 70 m 2 /g, more preferably at
• the adhesive preferably includes one or more silica fillers having a surface area of at most about 1000 m 2 /g, more preferably at most about 500 m 2 /g, and most preferably at most about 150 m"/g.
• the adhesive includes at least about 10% by weight, more preferably at least about 45% by weight, and most preferably at least about 50% by weight, based on the total weight of the adhesive, of a base filler.
• the adhesive includes at most about 87% by weight, more preferably at most about 85% by weight, and most preferably at most about 83% by weight, based on the total weight of the adhesive, of a base filler.
• the adhesive includes at least about 0.1% by weight, more preferably at least about 0.2% by weight, and most preferably at least about 5% by weight, based on the total weight of the adhesive, of a fumed silica filler having a surface area of at least about 70 m 2 /g.
• the adhesive includes at most about 50% by weight, more preferably at most about 15% by weight, and most preferably at most about 10% by weight, based on the total weight of the adhesive, of a fumed silica filler having a surface area of at least about 70 m 2 /g.
• base filler will preferably allow lower levels of fumed silica fillers to reach the desired rheological properties, and likewise lower levels of base filler will preferably allow higher levels of fumed silica fillers to reach the desired rheological properties.
• the adhesive includes a fumed silica filler having an average aggregate length of at least about 0.01 micron, more preferably at least about 0.05 micron, and most preferably at least about 0.1 micron.
• the adhesive includes a fumed silica filler having an average aggregate length of at most about 1 micron, more preferably at most about 0.5 micron, and most preferably at most about 0.4 micron.
• adhesives used in the present invention may optionally include adjuvants.
• adjuvants include, for example, cosolvents, pigments, inhibitors, accelerators, viscosity modifiers, surfactants, rheology modifiers, colorants, medicaments, adhesion promoters and other ingredients that will be apparent to those skilled in the art.
• compositions may contain stabilizers.
• Suitable adjuvants include, for example, those disclosed in International Patent Application Publication No. WO 00/69393 (Brennan et al.).
• Adhesives used in the present invention preferably have physical properties that are desired for precoated and/or packaged orthodontic adhesives.
• Desirable properties include, for example, adequate handling properties, no slump that would be observable by a practitioner, no substantial flow-out, suitable operatory light stability, no observable slip when placed on liner or tooth, suitable aesthetic color, color stability under office light conditions (e.g., white light stability), and sufficient tack such that the precoated bracket does not fall off the tooth when placed there prior to curing.
• the first part of the at least two-part adhesive used in the present invention preferably has a steady state viscosity at 28 °C of at least about 3 x 10 2 Pa-s, more preferably at least about 5 x 10 3 Pa-s, and most preferably at least about 1 x 10 4 Pa-s.
• the first part of the at least two-part adhesive used in the present invention preferably has a steady state viscosity at 28 °C of at most about 7 x 10 4 Pa-s, more preferably at most about
• the first part of the at least two-part adhesives used in the present invention preferably have a static yield stress at 28°C of at least about 4,000 dynes/cm , more preferably at least about 8,000 dynes/cm 2 , and most preferably at least about 9,000 dynes/cm 2 .
• the first part of the at least two-part adhesives used in the present invention preferably have a static yield stress at 28°C of at most about 100,000 dynes/cm 2 , more preferably at most about 60,000 dynes/cm , and most preferably at most about 25,000 dynes/cm 2 .
• the first part of the at least two-part adhesives used in the present invention may be applied to the base of the orthodontic appliance by methods known in the art. Suitable methods include, for example, application with a syringe or other suitable dispensing devices as disclosed, for example, in U.S. Pat. No. 5,552,177 (Jacobs et al.). SECOND PART OF AN AT LEAST TWO-PART ADHESIVE
• the second part of the at least two-part adhesive is also known as a primer.
• the second part of the at least two-part adhesive includes a polymerizable component, as described herein, and an activator.
• the second part of the at least two-part adhesive may optionally include a polymeric material including, for example, poly(methyl methacrylate) and/or a coupling agent (e.g., ⁇ -methacryloxypropyltrimethoxysilane available under the trade designation A 174 from Witco Osi Specialties (Danbury, CT)).
• a coupling agent e.g., ⁇ -methacryloxypropyltrimethoxysilane available under the trade designation A 174 from Witco Osi Specialties (Danbury, CT)
• the second part of the at least two-part adhesives used in the present invention includes an activator.
• the activator interacts with the polymerization initiator to cause the production of free radicals.
• Useful activators for free radical polymerization initiators include, for example, electron donors (e.g., sodium benzene sulfinate, amines, and amino alcohols). Exemplary activators are disclosed, for example, in U.S. Pat. No. 6,126,922 (Rozzi et al.) and International Patent Application Publication No. WO 00/69393 (Brennan et al.).
• Preferred activators are electron donors, and amines are more preferred.
• Preferred amine electron donors include, for example, N,N-bis-(2- hydroxyethyl)-p-toluidine.
• the second part of the at least two-part adhesive includes at least about 3% by weight, more preferably at least about 5% by weight, and most preferably at least about 7% by weight activator, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive includes at most about 30% by weight, more preferably at most about 25% by weight, and most preferably at most about 20% by weight activator, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive includes at least about 80% by weight, more preferably at least about 82% by weight, and most preferably at least about 85% by weight polymerizable component, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive includes at most about 95% by weight, more preferably at most about 93% by weight, and most preferably at most about 90% by weight polymerizable component, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive includes at least about
• the second part of the at least two-part adhesive includes at most about 10% by weight, more preferably at most about 7% by weight, and most preferably at most about 5% by weight polymeric material, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive includes at least about 0.1% by weight, more preferably at least about 0.25% by weight, and most preferably at least about 0.5% by weight of a coupling agent, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive includes at most about 2% by weight, more preferably at most about 1.5% by weight, and most preferably at most about 1.25% by weight of a coupling agent, based on the total weight of the second part of the at least two-part adhesive.
• the second part of the at least two-part adhesive used in the present invention preferably has a steady state viscosity at 28°C of at least about 0.1 Pa-s, more preferably at least about 0.15 Pa-s, and most preferably at least about 0.175 Pa-s.
• the second part of the at least two-part adhesive used in the present invention preferably has a steady state viscosity at 28°C of at most about 0.4 Pa-s, more preferably at most about 0.35 Pa-s, and most preferably at most about 0.3 Pa-s.
• Articles of the present invention preferably include a release substrate in contact with the adhesive.
• a surface of the release substrate includes a number or pores, and no more than about 50% by weight of the adhesive is in the pores.
• the release substrate includes a foam.
• Suitable release substrates are disclosed, for example in U.S. Pat. No. 6,183,249 (Brennan et al.).
• the release substrate is a crosslinked polyethylene foam available under the trade designation MINICEL (e.g., MINICEL M200) from Voltek (Lawrence, MA).
• the release substrate provides for easy release of the appliance and reduced slip and flow-out.
• the release substrates used in the present invention may be applied to the adhesive on the base of the orthodontic appliance by methods known in the art. Suitable methods include, for example, placing the release substrate on the bottom of a container well and then lightly inserting the bracket in the well such that the adhesive is in contact with the release substrate.
• a robotic arm may be used, for example, as described in U.S. Pat. No. 5,552,177 (Jacobs et al.).
• Suitable containers include, for example, those disclosed, for example, in U.S. Pat. Nos. 4,978,007 (Jacobs et al.), 5,172,809 (Jacobs et al.), 5,328,363
• the container may include a release substrate.
• the release substrate may optionally be part of the container, but preferably the release substrate is a release liner.
• kits may include additional components including, for example, instructions for using the orthodontic appliance, a second part of the at least two-part adhesive, etching compositions, swabs or brush tips for etching compositions, appliance placement guides or jigs, extra quantities of adhesive, primer, sealant, and mix pads.
• Methods of using the presently disclosed article include separating the orthodontic bracket from the release substrate, wherein the first part of the at least two-part adhesive preferably remains on the base of the orthodontic bracket.
• the second-part of the at least two-part adhesive is applied to the surface of the tooth by the practitioner, although the second part of the at least two-part adhesive may also be applied to the first part on the orthodontic bracket by the practitioner.
• the orthodontic bracket is then applied to the tooth surface and positioned properly by the practitioner so that the adhesive is in intimate contact with the surface of the tooth. When properly positioned and the two parts of the adhesive are in intimate contact, the adhesive hardens and bonds the orthodontic bracket to the tooth.
• the surface of the tooth may be etched and dried before adhering the adhesive-coated bracket to the tooth.
• the adhesive sets at about 15 seconds to about 50 seconds at room temperature. Setting can be determined by probing the adhesive mix with a sharp probe. The adhesive is set when hand pressure with the probe does not cause the adhesive to yield.
• the bracket is bonded to the tooth with a bond strength of at least about 7 MPa, more preferably at least about 9 MPa, and most preferably at least about 11 MPa.
• the bracket is bonded to the tooth with a bond strength of at most about 25MPa.
• the rheometer was then programmed to wait for 10 minutes for the temperature to stabilize at 28°C before beginning the measurement. The rheometer was then programmed to shear the adhesive sample at a shear rate of 0.01 second "1 for 30 seconds followed by shearing at 0.1 second "1 for 4.5 minutes. During each of these periods the rheometer collected stress measurements.
• the yield stress of an adhesive sample was defined as the point at which the stress vs. time curve deviated from an initially linear trajectory. Practically, this was determined by constructing a tangent to the stress vs. time curve. The tangent was then shifted by 0.06 seconds to the right and the intercept with the stress vs. time curve determined. This intercept, being very close to the point of deviation from linearity, was defined as the static yield stress (or as the transition from elastic deformation to viscoelastic flow) and reported as dynes/cm for the adhesive sample. Reported values were from single measurements of the samples. The adhesive samples were thixotropic, meaning that the viscosity under constant shear rate changes with time.
• the viscosity of an adhesive sample was defined as the viscosity measured after a given time under shear. This time was chosen such that any yield stresses would have been overcome. A period of 3.5 minutes at 28°C under a shear rate of 0.1 second "1 ) was chosen since by that time all of the adhesive samples measured were well beyond yielding. The results were reported as steady state viscosity values (from single measurements) in units of Pa-s (Pascal-seconds). ADHESIVE/BRACKET FLOW-OUT
• the Adhesive/Bracket Flow-Out Test Method was used to determine the tendency of an adhesive to flow on a liner beneath an orthodontic bracket, a phenomenon called
• flow-out If an adhesive exhibits flow-out on a specific liner in this test, then the adhesive would be expected to flow-out within a blister package containing the adhesive precoated on a bracket and covered with the same liner. Flow-out can produce stringing of the adhesive away from the bracket base as the adhesive precoated bracket is removed from the liner. This result can cause difficulties for a practitioner who must then make adjustments to the shape of the adhesive pad (or pillow) prior to placement of the adhesive precoated bracket on the tooth. In the worst case, flow-out prevents full release of the adhesive from the liner, which may even cause separation of the adhesive from the precoated bracket.
• Mini Twin N-slot brackets (3M Unitek, Ref # 017-333 or 017-334) were coated by application from a syringe with about 8 mg of adhesive placed on a SCOTCHPAK 1022 release liner (3M Company) with the adhesive in contact with the liner, and held for one week in a 40°C oven. (Time and temperature of the test was varied depending upon the test sample.) The adhesive precoated brackets were placed on liners that were held to cardboard via double stick tape in order to keep the brackets in a horizontal position in the oven. Special precaution was taken to ensure that no adhesive was visible beyond the bracket base at the start of the test.
• the Adhesive/Bracket Vertical Slip Test Method was developed to determine if adhesive precoated brackets using specific adhesive compositions would slip on specific release liners in blister packages. If an adhesive exhibits slippage on a specific liner in this test, then the adhesive would be expected to slip (e.g., during transit to the customer) within a blister package containing the adhesive precoated on a bracket and covered with the same liner. In the worst case, the adhesive precoated brackets may slip entirely off the liner, destroying the product functionality. Or, the adhesive precoated bracket may rotate in the package, which would result in improper orientation for placement of the bracket on the tooth by the practitioner. • 3M Unitek Mini Twin V-slot, (Ref. 017-333 or 017-334) or buccal tubes (Ref.
• brackets were coated by application from a syringe with about 8 mg of adhesive (with the exception of buccal tubes which were coated with about 16 mg of adhesive).
• the adhesive precoated brackets were placed on MINICEL M200 foam liner (Voltek Corp, Division of Sekisui America, Lawrence, MA). Each liner containing the adhesive precoated bracket was held to a piece of cardboard via double stick tape. Special precaution was taken to ensure that no adhesive was visible beyond the bracket base at the start of the test. A "starting line" was drawn near the top edge of the bracket to ensure measurement of the exact distance of slippage.
• the cardboard containing the brackets was held vertically in an oven (set at a predetermined temperature, typically 40°C or 50°C) for predetermined period of time (typically 3 to 14 days). Slippage of the adhesive coated bracket on the liner was measured as flow-out beyond the top edge of the bracket base and was measured using RAM Optical Instrumentation as described in the preceding test method. The slippage values reported (in mm) were an average of at least 3 adhesive precoated bracket samples per test.
• IMSIL A- 10 Unimin Specialty Minerals, Inc. Elco, IL
• IMSIL A- 10 Unimin Specialty Minerals, Inc. Elco, IL
• This solution was stirred continuously using a non metallic mixer.
• Silane A- 174 was added to the water while stirring at high speed.
• the amount of silane was 5.25% of the IMSIL to be treated.
• Mixing was continued for 45 to 50 minutes.
• IMSIL was slowly added into the vortex of the mixer. After all the IMSIL was added stirring was continued for 2 to 2.5 hours.
• the mixer was removed, the container was covered, and the IMSIL was allowed to settle. After the IMSIL had settled, the liquid was decanted off.
• the wet IMSIL was placed into shallow glass dishes and placed in a 40°C oven for several days until dry. The temperature was raised to 120°C and the dried material was heated for 16 to 24 hours. The material was allowed to cool to room temperature. The dry material was sifted through a fine mesh nylon screen.
• the first part of a two-part adhesive was made by combining the following ingredients:
• the first part was prepared according to the following general procedure. A premeasured amount of BisGMA was removed from the refrigerator and allowed to warm to room temperature. TegDMA was weighed into a separate container. The BisGMA and TegDMA containers were placed into an oven preheated to about 45°C to about 55°C for about 2-3 hours. The TegDMA was then poured into the BisGMA with manual stirring. After a uniform solution was obtained, the material was cooled to less than about 30°C. Weighed amounts of BPO and BHT were added to the material and the material was stirred for at least 4 hours until a uniform solution was obtained.
• the material was then transferred to a tared Hobart mixing bowl. Aerosil R972 was weighed into the bowl and a weighed amount of silanated IMSIL was sprinkled onto the Aerosil and resin mixture. The material was mixed at low or medium speed for at least 75 minutes while scraping the material from the sides of the bowl, until a uniform mixture was obtained. Mixing was started immediately after addition of the IMSIL and Aerosil to the mixer. A minimum amount of Cab-O-Sil TS720 was then added to the mixing bowl, and it was stirred at the lowest speed until a uniform mixture is obtained. Additional Cab- O-Sil may be added to provide a material with increased viscosity.
• the second part of the two-part adhesive was made by combining the following ingredients:
• the second part was prepared according to the following general procedure.
• a premeasured amount of BisGMA was placed in a container sufficient to hold the completed batch was removed from regrigerated storage and allowed to warm to room temperature.
• TegDMA was measured into a separate container. Both containers were placed in an oven preheated to 45°C to about 55°C for about 2-3 hours. The TegDMA was then poured into the BisGMA with manual stirring. Mechanical stirring was then started, and the container was heated on a hot plate until the temperature was about 50°C to 55°C.
• Comparative Example I The first part of a comparative two-part adhesive was made by combining the following ingredients:
• the comparative first part was prepared according to the following general procedure.
• BisEMA (7.03 g) was placed in a mixing cup.
• BHT (0.203 g) was weighed into the cup.
• the cup was then placed in a centrifugal mixer (SPEED MIXER DAC 150 FVZ, FlackTek, Inc.) and spun at 3000 revolutions per minute (rpm) for 2 minutes.
• the BHT was not fully dissolved, so the cup was spun for another 2 minutes at 3000 rpm.
• the BHT was still not fully dissolved, so the cup was placed in an oven at 50°C for 10 minutes. After spinning for 2 minutes at 3000 rpm, the BHT was dissolved.
• BPO (0.6008 g) was weighed into the cup. Spinning at 3000 rpm for 2 minutes dispersed the powder throughout the resin. The paste was then warmed at 40°C and stirred with a magnetic stir bar overnight to dissolve the BPO. BisGMA (10.96 g) was weighed into the cup. The cup was placed in an oven at 50°C for 30 minutes then mixed with a magnetic stir bar on a hot plate. Aerosil R974 (1.3995 g) was added to the cup, followed by spinning at 3000 rpm for 2 minutes. Visual inspection revealed the paste to be very uniform.
• the comparative second part of the two-part adhesive was made by combining the following ingredients:
• the comparative second part was prepared according to the following general procedure. TegDMA (6.00 g) was weighed into a mixing cup. DHEPT (0.6005 g) was added to the cup. The mixture was then warmed at 40°C and stirred with a magnetic stir bar overnight to dissolve the DHEPT. BisGMA (14.04 g) was added to the cup. The cup was then placed in an oven at 50°C for 30 minutes. Aerosil R974 (1.400 g) was added to the cup. Spinning at 3000 rpm for 2 minutes yielded a uniform mixture.
• the two-part adhesives were employed to bond brackets to bovine teeth using the following procedure. Bovine teeth were mounted in acrylic denture base material so that the labial surfaces were exposed. The mounted teeth were cleaned with a slurry of pumice in water. The teeth were then etched with Transbond XT etching gel (3M Unitek) for 15 seconds apiece before rinsing with water. The teeth were then dried with oil-free compressed air and examined to ensure the presence of a chalky white texture that indicates a sufficient etch. The first part of the two-part adhesive was applied via syringe to the bonding base of VICTORY SERIES REF 017-401 (or equivalent) upper central brackets (3M Unitek).
• the second part of the two-part adhesive was painted onto the surface of each tooth.
• Each bracket was pressed in place on a tooth. Excess flash was cleaned from the periphery of the bonding base. The bonded brackets were allowed to sit at room temperature for a period of 10 minutes before submerging them in 37°C water for
• the bonded brackets were removed from the water and mounted with the gingival tie wings pointing vertically in a test fixture attached to an Instron 4204 testing machine.
• a 0.020 inch diameter standard round wire was looped under the occlusal tie wings and attached to the crosshead of the testing machine. After moving the crosshead to make the wire snug, it was set to move at 5 mm/minute until the bracket was debonded.
• Comparative Example 1 produced much lower bond strength.
• Qualitative inspection of the teeth post-debonding revealed that the Comparative Example 1 paste was still soft underneath the bracket, indicating that it was not fully-cured. During bonding, the first and second parts of the
• Comparative Example 1 two-part adhesive were found to be very gooey and difficult to work with. Upon cleaning the excess from the periphery of the bonding base, some of the paste tended to get stuck on the tie wings.
• Biscupid brackets (e.g., having a curved base) were bonded to bovine teeth to determine the bond strength for thicker cross-section adhesives using the following procedure.
• Bovine teeth (20) were pumiced, rinsed, and dried. The teeth were then etched with 37% phosphoric acid for 15 seconds, rinsed, and dried. All the teeth were primed with a light coat of the Example 1, second part of the two-part adhesive.
• Ten brackets were primed with a light coat of the Example 1, second part of the two-part adhesive, and ten brackets were not primed.
• a small amount of the Example 1 , first part of the two-part adhesive was applied to each bracket. The brackets were placed on the bovine teeth, the flash was cleaned, and after 5 minutes, the teeth were placed in 37°C water for 24 hours. The bond strength was tested as described in Example 2.
• the unprimed brackets resulted in a bond strength of 17 MPa.
• the primed brackets resulted in a bond strength of 20 MPa.
• the bond strengths for the unprimed brackets suggest that the first part of the two-part adhesive is suitable for use as on precoated brackets.
• Example 4 PACKAGING Some of the requirements of the packaging for a precoated adhesive are that the adhesive support the appliance, the adhesive remain on the bonding base upon removal from the package, and that the package ensures that the adhesive is still functional after some years in storage.
• Example 1 and Comparative Example 1 two-part adhesives in supporting a buccal tube were tested. When placed on a sheet of polyvinyl chloride
• Example 1 first part samples and placed on a sample of Minicell M200 foam liner. Some of the samples were placed vertically on a laboratory bench for 1 week at room temperature. Minimal sliding of the brackets and adhesive on the foam liner material was observed. Additional samples were placed horizontally on a laboratory bench for 1 week at room temperature. Minimal flow of the adhesive from under the brackets was observed.
• Precoated Example 1 first part samples were stored at elevated temperature (40°C) for up to sixteen weeks with little or no effect on bonding effectiveness. After this treatment, the paste still gave a bond strength of 12.6 MPa.

Landscapes

• Health & Medical Sciences (AREA)
• Animal Behavior & Ethology (AREA)
• Oral & Maxillofacial Surgery (AREA)
• Epidemiology (AREA)
• Life Sciences & Earth Sciences (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Inorganic Chemistry (AREA)
• Chemical & Material Sciences (AREA)
• Dentistry (AREA)
• Dental Tools And Instruments Or Auxiliary Dental Instruments (AREA)
• Dental Preparations (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=29214908

Family Applications (1)

Country Status (7)

Families Citing this family (20)

Citations (11)

Family Cites Families (34)

• 2002
  • 2002-04-18 US US10/126,019 patent/US7217124B2/en not_active Expired - Fee Related
• 2003
  • 2003-02-27 JP JP2003585616A patent/JP4602673B2/ja not_active Expired - Fee Related
  • 2003-02-27 DE DE60325034T patent/DE60325034D1/de not_active Expired - Lifetime
  • 2003-02-27 AT AT03709373T patent/ATE415893T1/de not_active IP Right Cessation
  • 2003-02-27 WO PCT/US2003/005928 patent/WO2003088861A1/en not_active Ceased
  • 2003-02-27 AU AU2003212433A patent/AU2003212433A1/en not_active Abandoned
  • 2003-02-27 EP EP03709373A patent/EP1494609B1/en not_active Expired - Lifetime

Patent Citations (11)

Also Published As

Similar Documents

Legal Events