物件表层粘覆钛金属层的制造方法 技术领域 Manufacturing method of object surface-adhesive titanium metal layer TECHNICAL FIELD
本发明是涉及一种物件表层粘覆钛金属层的制造方法, 特别是针对一 般金属材质或非金属材质所制成的物件表层粘覆钛金属层的制造方法, 通 过此粘覆钛金属层的制造方法, 可促使物件与钛金属的粘覆得以更加平 整、 牢固。 The present invention relates to a method for manufacturing a titanium metal layer on the surface of an object, and in particular, to a method for manufacturing a titanium metal layer on the surface of an object made of a general metal material or a non-metal material. The manufacturing method can make the adhesion between the object and titanium more smooth and firm.
背景技术 Background technique
对目前坊间已普遍存在的粘覆方式为在常温下直接在钛金属层下缘 涂抹粘着剂, 并使钛金属层与物件粘合 (如图 1所示)。 但是, 此一粘覆方 式存有如下弊端- At present, the common adhesion method is to apply an adhesive directly at the lower edge of the titanium metal layer at normal temperature, and make the titanium metal layer adhere to the object (as shown in Fig. 1). However, this sticking method has the following disadvantages-
1.如图 1所示, 在粘覆时, 必需先在钛金属层 93下缘涂抹层粘着剂 92, 为此, 除造成涂抹不均匀外, 并浪费工时。 1. As shown in FIG. 1, it is necessary to apply a layer of adhesive 92 to the lower edge of the titanium metal layer 93 during adhesion. For this reason, in addition to causing uneven application and wasting labor.
2. 在常温下进行粘覆工作, 其空气密度高, 易造成物件 91与钛金属 层 93间存有气孔, 并使其粘覆不能平整、 牢固。 2. Adhesion work at normal temperature, its high air density, it is easy to cause air holes between the object 91 and the titanium metal layer 93, and make the adhesion cannot be flat and firm.
发明内容 Summary of the Invention
本发明的目的是实现一种物件表层粘覆钛金属层的制造方法。 该方法 可促使物件与钛金属的粘覆更加平整、 牢固。 The object of the present invention is to realize a method for manufacturing an object surface layer coated with a titanium metal layer. This method can make the adhesion between the object and titanium more smooth and firm.
为了实现上述目的, 本发明采取以下技术方案: 这种物件表层粘覆钛 金属层的制造方法包括下述步骤: a、在容室里设有加热装置及扩散层。 b、 并在工作台预设一道或一道以上的贯孔, 工作台的贯孔连接抽气装置。 (:、 在物件表层置放粘剂层 (常温下为固态)及钛金属层。 d、 通过加热装置及 扩散层促使容室内温度升高至某一预定的温度, 并使热力得以均匀地传导 至钛金属层、 粘剂层、 物件, 且使粘剂层形成熔融状态及使容室内空气变 为稀薄。 e、 通过贯孔连接抽气装置进行抽气动作, 使钛金属层与粘剂层 同时受到抽气装置的吸吮, 而平整、 牢固地粘覆在物件表层。 In order to achieve the above object, the present invention adopts the following technical solutions: The manufacturing method of the surface-coated titanium metal layer of the object includes the following steps: a. A heating device and a diffusion layer are provided in the container. b. One or more through holes are preset on the workbench, and the through holes of the workbench are connected with the suction device. (:, Place an adhesive layer (solid state at normal temperature) and a titanium metal layer on the surface of the object. D. Promote the temperature in the container to a predetermined temperature through the heating device and the diffusion layer, and allow the heat to be evenly transmitted. To the titanium metal layer, the adhesive layer, and the object, and the adhesive layer is formed into a molten state and the air in the container is thinned. E. The through-hole connection air extraction device is used to perform an air extraction operation, so that the titanium metal layer and the adhesive layer At the same time, it is sucked by the suction device, and is flat and firmly adhered to the surface of the object.
在本发明的方法中, 该粘剂层在常温下为固态。 In the method of the present invention, the adhesive layer is solid at normal temperature.
在本发明的方法中, 该粘剂层可为聚烯烃 (P0LY0LEFIN)。 In the method of the present invention, the adhesive layer may be a polyolefin (POLYLEFIN).
在本发明的方法中, 该粘剂层可为聚酰胺 (P0LYAMIDE)。 In the method of the present invention, the adhesive layer may be polyamide.
在本发明的力法中, 该粘剂层可为聚亚胺脂、 聚氨基甲酸乙脂 (P0LYURETHANE)。 In the force method of the present invention, the adhesive layer may be polyurethane or polyurethane (POLYURETHANE).
附图说明 BRIEF DESCRIPTION OF THE DRAWINGS
图 1为已知的粘覆方式示意图
图 2为本发明的流程方块图 Figure 1 is a schematic diagram of a known adhesion method FIG. 2 is a flow block diagram of the present invention
图 3为本发明的加工步骤示意图 Figure 3 is a schematic diagram of the processing steps of the present invention
图 4为本发明另一加工步骤示意图 Figure 4 is a schematic diagram of another processing step of the present invention
具体实施方式 detailed description
本发明提供一种物件表层粘覆钛金属层的制造方法, 如图 2、 图 3、 图 4所示, 其加工步骤为包括有: The present invention provides a manufacturing method of an object surface-coated titanium metal layer, as shown in FIG. 2, FIG. 3, and FIG. 4. The processing steps include:
a. 容室 (70)里设有加热装置 (60)及扩散层 (50); a. The chamber (70) is provided with a heating device (60) and a diffusion layer (50);
b. 工作台(10)的贯孔 (11)可连接抽气装置 (80) ; b. The through-hole (11) of the worktable (10) can be connected to the suction device (80);
c 物件表层置放粘剂层 (30) (常温下为固态)及钛金属层 (40) ; c Place an adhesive layer (30) on the surface of the object (solid at room temperature) and a titanium metal layer (40);
d. 通过加热装置 (60)及扩散层 (50)使容室(70)内温度升高至某一预 定的温度, 并使加热装置 (60)所产生的热力透过扩散层 (50)得以均匀地传 导至钛金属层 (40)、 粘剂层 (30)、 物件 (20), 且使粘剂层 (30)形成熔融状 态及使容室 (70)内空气变为稀薄; d. heating the device (60) and the diffusion layer (50) to increase the temperature in the chamber (70) to a predetermined temperature, and to allow the heat generated by the heating device (60) to penetrate the diffusion layer (50) to Uniformly conduct to the titanium metal layer (40), the adhesive layer (30), and the object (20), and make the adhesive layer (30) form a molten state and make the air in the chamber (70) thin;
e . 通过抽气装置 (80)经由贯孔 (11)进行抽气动作, 使钛金属层 (40) 及粘剂层 (30)同时受到吸吮而平整、 牢固地粘覆在物件 (20)表层。
e. The suction device (80) performs a suction action through the through hole (11), so that the titanium metal layer (40) and the adhesive layer (30) are sucked at the same time, and are flat and firmly adhered to the surface layer of the object (20). .