WO2003000950A1 - Topologically tailored sputtering targets - Google Patents
Topologically tailored sputtering targets Download PDFInfo
- Publication number
- WO2003000950A1 WO2003000950A1 PCT/US2002/006146 US0206146W WO03000950A1 WO 2003000950 A1 WO2003000950 A1 WO 2003000950A1 US 0206146 W US0206146 W US 0206146W WO 03000950 A1 WO03000950 A1 WO 03000950A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sputtering target
- forming
- target
- indentations
- surface material
- Prior art date
Abstract
Description
Claims