WO2002008514A2 - Emulsions d'encollage et leurs procedes d'elaboration - Google Patents

Emulsions d'encollage et leurs procedes d'elaboration Download PDF

Info

Publication number
WO2002008514A2
WO2002008514A2 PCT/US2001/021809 US0121809W WO0208514A2 WO 2002008514 A2 WO2002008514 A2 WO 2002008514A2 US 0121809 W US0121809 W US 0121809W WO 0208514 A2 WO0208514 A2 WO 0208514A2
Authority
WO
WIPO (PCT)
Prior art keywords
sizing agent
polyaluminum
water
emulsion
inorganic particulate
Prior art date
Application number
PCT/US2001/021809
Other languages
English (en)
Other versions
WO2002008514A3 (en
Inventor
John F. L. Newport
Jennifer Weatherdon
Original Assignee
Hercules Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hercules Incorporated filed Critical Hercules Incorporated
Priority to AU2001273345A priority Critical patent/AU2001273345A1/en
Publication of WO2002008514A2 publication Critical patent/WO2002008514A2/fr
Publication of WO2002008514A3 publication Critical patent/WO2002008514A3/en

Abstract

L'invention porte sur des procédés de préparation d'émulsions comprenant de l'eau, un agent d'encollage, et un agent émulsifiant de particules minérales capable de former une émulsion entre la phase aqueuse et la phase huileuse de l'agent d'encollage, et sur des émulsions comprenant de l'eau, un agent d'encollage, et un agent émulsifiant de particules minérales capable de former une émulsion entre la phase aqueuse et la phase huileuse de l'agent d'encollage.
PCT/US2001/021809 2000-07-26 2001-07-09 Emulsions d'encollage et leurs procedes d'elaboration WO2002008514A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2001273345A AU2001273345A1 (en) 2000-07-26 2001-07-09 Method of making sizing emulsion and sizing emulsion

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US62616000A 2000-07-26 2000-07-26
US09/626,160 2000-07-26

Publications (2)

Publication Number Publication Date
WO2002008514A2 true WO2002008514A2 (fr) 2002-01-31
WO2002008514A3 WO2002008514A3 (en) 2002-04-25

Family

ID=24509203

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2001/021809 WO2002008514A2 (fr) 2000-07-26 2001-07-09 Emulsions d'encollage et leurs procedes d'elaboration

Country Status (2)

Country Link
AU (1) AU2001273345A1 (fr)
WO (1) WO2002008514A2 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004059082A1 (fr) 2002-12-17 2004-07-15 Lanxess Corporation Systeme de compositions d'anhydride alcenylsuccinique et son procede d'utilisation
FR2897280A1 (fr) * 2006-02-13 2007-08-17 Arjowiggins Soc Par Actions Si Procede pour fabriquer une emulsion de collage et procede de fabrication de papier utilisant cette emulsion
US7943789B2 (en) 2002-12-17 2011-05-17 Kemira Oyj Alkenylsuccinic anhydride composition and method of using the same
CN110080039A (zh) * 2019-04-26 2019-08-02 邱振权 一种asa乳液的复合乳化剂及asa施胶剂乳液
WO2023130058A1 (fr) * 2021-12-30 2023-07-06 Kemira Oyj Amidon cationique à charge élevée en tant que promoteur dans des émulsions d'encollage de dimère akd
US12031274B2 (en) 2021-12-30 2024-07-09 Kemira Oyj High cationic starch as a promoter in AKD sizing emulsions

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB800750A (en) * 1956-05-07 1958-09-03 Patent & Licensing Corp Improvements in or relating to emulsions for making moisture impermeable paper and the like
CA2092955C (fr) * 1992-04-06 1999-01-12 Sunil P. Dasgupta Melange stable d'une colle a base d'un dimere cetenique et de silice sous forme colloidale
GB9603909D0 (en) * 1996-02-23 1996-04-24 Allied Colloids Ltd Production of paper
EP1099795A1 (fr) * 1999-06-24 2001-05-16 Akzo Nobel N.V. Emulsion de collage

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004059082A1 (fr) 2002-12-17 2004-07-15 Lanxess Corporation Systeme de compositions d'anhydride alcenylsuccinique et son procede d'utilisation
US7943789B2 (en) 2002-12-17 2011-05-17 Kemira Oyj Alkenylsuccinic anhydride composition and method of using the same
FR2897280A1 (fr) * 2006-02-13 2007-08-17 Arjowiggins Soc Par Actions Si Procede pour fabriquer une emulsion de collage et procede de fabrication de papier utilisant cette emulsion
CN110080039A (zh) * 2019-04-26 2019-08-02 邱振权 一种asa乳液的复合乳化剂及asa施胶剂乳液
CN110080039B (zh) * 2019-04-26 2022-01-04 苏州赛维科环保技术服务有限公司 一种asa乳液的复合乳化剂及asa施胶剂乳液
WO2023130058A1 (fr) * 2021-12-30 2023-07-06 Kemira Oyj Amidon cationique à charge élevée en tant que promoteur dans des émulsions d'encollage de dimère akd
US12031274B2 (en) 2021-12-30 2024-07-09 Kemira Oyj High cationic starch as a promoter in AKD sizing emulsions

Also Published As

Publication number Publication date
AU2001273345A1 (en) 2002-02-05
WO2002008514A3 (en) 2002-04-25

Similar Documents

Publication Publication Date Title
US6093217A (en) Sizing of paper
US4816073A (en) Aqueous dispersions, a process for their preparation and the use of the dispersions as sizing agents
US6165259A (en) Aqueous dispersions of hydrophobic material
US5876562A (en) Sizing dispersions
US20080289787A1 (en) Paper and Materials and Processes for Its Production
US5510003A (en) Method of sizing and aqueous sizing dispersion
JP4262302B2 (ja) サイジング組成物
MX2013010757A (es) Composiciones de apresto.
CA2280094C (fr) Dispersions aqueuses de materiau hydrophobe
EP0200755B1 (fr) Agent a pouvoir hydrophobe pour les fibres cellulosiques, son procede de preparation et son emploi pour rendre hydrophobe la pate
PL208342B1 (pl) Kompozycja wodna oraz sposób zaklejania produktu opartego na celulozie
JP3998638B2 (ja) 紙のサイジング方法及びサイジング組成物
WO2002008514A2 (fr) Emulsions d'encollage et leurs procedes d'elaboration
AU758182B2 (en) Sizing emulsion
CN103774496A (zh) 一种改性水滑石稳定的akd乳液施胶剂的制备方法
JP6825977B2 (ja) 紙質向上剤
WO2000047819A1 (fr) Dispersion d'encollage
NZ614875B2 (en) Sizing compositions

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP