Classifications

• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B26/00—Obtaining alkali, alkaline earth metals or magnesium
  • C22B26/20—Obtaining alkaline earth metals or magnesium
  • C22B26/22—Obtaining magnesium
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B22—CASTING; POWDER METALLURGY
  • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
  • B22D1/00—Treatment of fused masses in the ladle or the supply runners before casting
  • B22D1/002—Treatment with gases
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B22—CASTING; POWDER METALLURGY
  • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
  • B22D21/00—Casting non-ferrous metals or metallic compounds so far as their metallurgical properties are of importance for the casting procedure; Selection of compositions therefor
  • B22D21/002—Castings of light metals
  • B22D21/007—Castings of light metals with low melting point, e.g. Al 659 degrees C, Mg 650 degrees C
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C45/00—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds
  • C07C45/61—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups
  • C07C45/67—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups by isomerisation; by change of size of the carbon skeleton
  • C07C45/68—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups by isomerisation; by change of size of the carbon skeleton by increase in the number of carbon atoms
  • C07C45/69—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups by isomerisation; by change of size of the carbon skeleton by increase in the number of carbon atoms by addition to carbon-to-carbon double or triple bonds
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C45/00—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds
  • C07C45/78—Separation; Purification; Stabilisation; Use of additives
  • C07C45/85—Separation; Purification; Stabilisation; Use of additives by treatment giving rise to a chemical modification
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C49/00—Ketones; Ketenes; Dimeric ketenes; Ketonic chelates
  • C07C49/04—Saturated compounds containing keto groups bound to acyclic carbon atoms
  • C07C49/16—Saturated compounds containing keto groups bound to acyclic carbon atoms containing halogen
  • C07C49/167—Saturated compounds containing keto groups bound to acyclic carbon atoms containing halogen containing only fluorine as halogen
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C49/00—Ketones; Ketenes; Dimeric ketenes; Ketonic chelates
  • C07C49/385—Saturated compounds containing a keto group being part of a ring
  • C07C49/457—Saturated compounds containing a keto group being part of a ring containing halogen
  • C07C49/463—Saturated compounds containing a keto group being part of a ring containing halogen a keto group being part of a six-membered ring
• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B21/00—Obtaining aluminium
  • C22B21/0084—Obtaining aluminium melting and handling molten aluminium
• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B21/00—Obtaining aluminium
  • C22B21/06—Obtaining aluminium refining
• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B21/00—Obtaining aluminium
  • C22B21/06—Obtaining aluminium refining
  • C22B21/064—Obtaining aluminium refining using inert or reactive gases
• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B9/00—General processes of refining or remelting of metals; Apparatus for electroslag or arc remelting of metals
  • C22B9/006—General processes of refining or remelting of metals; Apparatus for electroslag or arc remelting of metals with use of an inert protective material including the use of an inert gas
• • C—CHEMISTRY; METALLURGY
  • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
  • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
  • C22B9/00—General processes of refining or remelting of metals; Apparatus for electroslag or arc remelting of metals
  • C22B9/05—Refining by treating with gases, e.g. gas flushing also refining by means of a material generating gas in situ
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
  • Y02P10/00—Technologies related to metal processing
  • Y02P10/10—Reduction of greenhouse gas [GHG] emissions
  • Y02P10/122—Reduction of greenhouse gas [GHG] emissions by capturing or storing CO2
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
  • Y02P10/00—Technologies related to metal processing
  • Y02P10/10—Reduction of greenhouse gas [GHG] emissions
  • Y02P10/146—Perfluorocarbons [PFC]; Hydrofluorocarbons [HFC]; Sulfur hexafluoride [SF6]

Definitions

• This invention relates to a method for preventing the ignition of molten magnesium by contacting the molten magnesium with a gaseous mixture comprising a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones, and mixtures thereof.
• This invention also relates to molten magnesium and solid magnesium comprising a film formed on a surface of the magnesium. This film is comprised of a reaction product of molten magnesium and a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones, and mixtures thereof.
• the solid magnesium may be in the form of ignots or castings.
• the invention also relates to extinguishing a fire on the surface of magnesium by contacting the surface with the gaseous mixture described above.
• Molded parts made of magnesium are finding increasing use as components in the automotive and aerospace industries. These parts are typically manufactured in a foundry, where the magnesium is heated to a molten state in a crucible to a temperature as high as 1400 °F (760 °C), and the resulting molten magnesium is poured into molds or dies to form ingots or castings. During this casting process, protection of the magnesium from atmospheric air is essential to prevent a spontaneous exothermic reaction from occurring between the reactive metal and the oxygen in the air. Protection from air is also necessary to minimize the propensity of reactive magnesium vapors to sublime from the molten metal bath to cooler portions of a casting apparatus. In either situation, an extremely hot magnesium fire can result within a few seconds of air exposure, causing extensive property damage and, most catastrophically, serious injury to and devastating loss of human life.
• the flux film itself can oxidize in the atmosphere to harden into a thick oxychloride deposit, which is easily cracked to expose molten magnesium to the atmosphere.
• the salt fluxes are typically hygroscopic and, as such, can form salt inclusions in the metal surface which can lead to corrosion.
• fumes and dust particles from fluxes can cause serious corrosion problems to ferrous metals in the foundry.
• salt sludge can form in the bottom of the crucible. Fifth, and not least, removal of such fluxes from the surface of cast magnesium parts can be difficult.
• Cover gases can be described as one of two types: inert cover gases and reactive cover gases.
• Inert cover gases can be non-reactive (e.g., argon or helium) or slowly reactive (e.g., nitrogen, which reacts slowly with molten magnesium to form Mg 3 N 2 ).
• nitrogen e.g., which reacts slowly with molten magnesium to form Mg 3 N 2 .
• air must be essentially excluded to minimize the possibility of metal ignition, i.e., the system must be essentially closed.
• workers either have to be equipped with a cumbersome self- contained breathing apparatus or they have to be located outside of the dimensions of the processing area (e.g., by using remote control).
• inert cover gases are incapable of preventing molten metal from subliming.
• Reactive cover gases are gases used at low concentration in a carrier gas, normally ambient air, that react with the molten magnesium at its surface to produce a nearly invisible, thermodynamically stable film. By forming such a tight film, the aerial oxygen is effectively separated from the surface of the molten magnesium, thus preventing metal ignition and minimizing metal sublimation.
• SO 2 has been investigated in the past as a reactive cover gas, as SO 2 reacts with molten magnesium to form a thin, nearly invisible film of magnesium oxysulfides.
• SO is low in cost and is effective at levels of less than 1% in air in protecting molten magnesium from ignition.
• SO 2 is very toxic and consequently requires significant measures to protect workers from exposure (permissible exposure levels are only 2 ppm by volume or 5 mg/m by volume).
• Another problem with SO 2 is its reactivity with water in humid air to produce very corrosive acids (H 2 SO 4 and H 2 SO 3 ). These acids can attack unprotected workers and casting equipment, and they also contribute significantly to acid rain pollution when vented out of the foundry.
• SO 2 also has a tendency to form reactive deposits with magnesium which produce metal eruptions from the furnace (especially when SO 2 concentrations in the air are allowed to drift too high).
• SO 2 has been used commercially on a large scale for the casting of magnesium alloys, these drawbacks have led some manufacturers to ban its use.
• Fluorine-containing reactive cover gases provide an inert atmosphere which is normally very stable to chemical and thermal breakdown. However, such normally stable gases will decompose upon contact with a molten magnesium surface to form a thin, thermodynamically stable magnesium oxyfluoride protective film.
• 1,972,317 (Reimers et. al.) describes the use of fluorine-containing compounds which boil, sublime or decompose at temperatures below about 750 °C to produce a fluorine- containing atmosphere which inhibits the oxidation of molten magnesium.
• Suitable compounds listed include gases, liquids or solids such as BF 3 , NF 3 , SiF 4 , PF 5 , SF 6 , SO 2 F 2 , (CC1F 2 ) 2 , HF, NH 4 F and NH 4 PF 6 .
• gases, liquids or solids such as BF 3 , NF 3 , SiF 4 , PF 5 , SF 6 , SO 2 F 2 , (CC1F 2 ) 2 , HF, NH 4 F and NH 4 PF 6 .
• BF 3 , SF 6 , CF 4 and (CC1F 2 ) 2 as fluorine- containing reactive cover gases is disclosed in J. W. Fraehling
• Each of these fluorine-containing compounds has one or more deficiencies. Though used commercially and effectively at lower levels than SO 2 , BF 3 is toxic and corrosive and can be potentially explosive with molten magnesium. NF 3 , SiF 4 , PF 5 , SO 2 F 2 and HF are also toxic and corrosive. NH ⁇ and NH 4 PF 6 are solids which sublime upon heating to form toxic and corrosive vapors. CF has a very long atmospheric lifetime. (CC1F 2 ) 2 , a chlorofluorocarbon, has a very high ozone depletion potential (ODP).
• ODP ozone depletion potential
• the ODP of a compound is usually defined as the total steady-state ozone destruction, vertically integrated over the stratosphere, resulting from the unit mass emission of that compound relative to that for a unit mass emission of CFC-11 (CC1 F).
• CFC-11 CFC-11
• SF 6 was considered the optimum reactive cover gas for magnesium.
• SF 6 is effective yet safe (essentially inert, odorless, low in toxicity, nonflammable and not corrosive to equipment). It can be used effectively at low concentrations either in air ( ⁇ 1 %) or in CO 2 to form a very thin film of magnesium oxyfluorides and oxysulfides on the surface of molten magnesium.
• This magnesium oxyfluoride/oxysulfide film is far superior at protecting the magnesium from a vigorous exothermic oxidation reaction than is the magnesium oxide film inherently present on the metal surface.
• the magnesium oxysulfide/oxyfluoride film is sufficiently thin (i.e., nearly invisible to the naked eye) that the metal surface appears to be metallic. This superior protection is believed to result from the greater thermodynamic stability of a magnesium oxysulfide and/or magnesium oxyfluoride film as compared to the stability of a thick porous magnesium oxide, sulfide or fluoride film.
• This invention relates to a method for treating molten magnesium to protect the magnesium from reacting with oxygen in air.
• the method comprises providing molten magnesium and exposing the magnesium to a gaseous mixture comprising a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones, and mixtures thereof.
• the gaseous mixture may further comprise a carrier gas.
• the carrier gas may be selected from the group consisting of air, carbon dioxide, argon, nitrogen and mixtures thereof.
• This invention also relates to a method for protecting molten magnesium from reacting with oxygen in air.
• the exposed surface of molten magnesium is exposed to or contacted with a gaseous mixture comprising a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones, and mixtures thereof.
• the gaseous mixture can react with the molten magnesium at its exposed surface to produce a nearly invisible, thermodynamically stable film.
• the oxygen in air can be effectively separated from the surface of the molten magnesium and thus can prevent metal ignition and can minimize metal sublimation.
• This invention also relates to molten magnesium protected from reacting with oxygen in air in accordance with the method of the present invention.
• this invention relates to molten magnesium wherein a protective film is formed on a surface of the magnesium.
• This film is formed by a reaction of the magnesium with a gaseous mixture comprising a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones and mixtures thereof.
• This film can be nearly invisible and thermodynamically stable and can effectively separate oxygen in air from the surface of the magnesium and thus can prevent metal ignition and can minimize metal sublimation.
• this invention relates to solid magnesium comprising a film formed on a surface of the magnesium.
• This film is comprised of a reaction product of molten magnesium and a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones, and mixtures thereof.
• This solid magnesium may be in the form of ignots or castings.
• this invention relates to a method for extinguishing a fire on the surface of magnesium comprising contacting a gaseous mixture comprising a fluorocarbon selected from the group consisting of perfluoroketones, hydrofluoroketones, and mixtures thereof, with said surface of said magnesium.
• magnesium means magnesium and all alloys formed therefrom.
• One advantage of the present invention over the known art is that the Global Warming Potentials of perfluoroketones and hydrofluoroketones are quite low. Therefore, the present inventive process is more environmentally friendly.
• Fluorocarbons of the present invention include perfluoroketones (PFKs), and hydrofluoroketones (HFKs) which incorporate limited amounts of hydrogen in their structures. These fluorocarbons can be effective as reactive cover gases to protect reactive molten reactive metals such as molten magnesium from ignition. As is the case with known fluorine-containing reactive cover gases, these fluorocarbons can react with the molten metal surface to produce a protective surface film, thus preventing ignition of the molten metal.
• PFKs perfluoroketones
• HFKs hydrofluoroketones
• fluorocarbons of the present invention are desirable alternatives to the most commonly used cover gas currently, SF 6 .
• the fluorocarbons of the present invention are low GWP fluorocarbon alternatives to SF 6 , i.e., the fluorocarbons of the present invention have measurably lower global warming potential relative to SF 6 (i.e., significantly less than 22,200) and are not significantly worse in atmospheric lifetime, ozone depletion potential, or toxicity properties.
• Perfluorinated ketones (PFKs) useful in the present invention include ketones which are fully fluorinated, i.e., all of the hydrogen atoms in the carbon backbone have been replaced with fluorine atoms.
• the carbon backbone can be linear, branched, or cyclic, or combinations thereof, and will preferably have about 5 to about 9 carbon atoms.
• Representative examples of perfluorinated ketone compounds suitable for use in the processes and compositions of the invention include CF 3 CF 2 C(O)CF(CF 3 ) , (CF 3 ) 2 CFC(O)CF(CF 3 ) 2 , CF 3 (CF 2 ) 2 C(O)CF(CF 3 ) 2 , CF 3 (CF 2 ) 3 C(O)CF(CF 3 ) 2 , CF 3 (CF 2 ) 5 C(O)CF 3 , CF 3 CF 2 C(O)CF 2 CF 2 CF 3 , CF 3 C(O)CF(CF 3)2 , perfluorocyclohexanone, and mixtures thereof.
• perfluorinated ketones can offer additional important benefits in safety of use and in environmental properties.
• CF 3 CF 2 C(O)CF(CF 3 ) 2 has low acute toxicity, based on short-term inhalation tests with mice exposed for four hours at a concentration of 100,000 ppm in air.
• CF 3 CF 2 C(O)CF(CF 3 ) 2 has an estimated atmospheric lifetime of 5 days.
• Other perfluorinated ketones show similar absorbances and thus are expected to have similar atmospheric lifetimes.
• Perfluorinated ketones which are straight chain or cyclic can be prepared as described in U.S. Patent No. 5,466,877 (Moore et al.) which in turn can be derived from the fluorinated esters described in U.S. Patent No. 5,399,718 (Costello et al.).
• Perfluorinated ketones that are branched can be prepared as described in U.S. Patent No. 3,185,734 (Fawcett et al).
• Hydrofluoroketones that are useful in the present invention include those ketones having only fluorine and hydrogen atoms attached to the carbon backbone.
• the carbon backbone can be linear, branched, or cyclic, or combinations thereof, and preferably will have about 4 to about 7 carbon atoms.
• hydrofluoroketone compounds suitable for use in the processes and compositions of this invention include: HCF 2 CF 2 C(O)CF(CF 3 ) 2 , CF 3 C(O)CH 2 C(O)CF 3 , C 2 H 5 C(O)CF(CF 3 ) 2 , CF 2 CF 2 C(O)CH 3 , (CF 3 ) 2 CFC(O)CH 3 , CF 3 CF 2 C(O)CHF 2 , CF 3 CF 2 C(O)CH 2 F, CF 3 CF 2 C(O)CH 2 CF 3 , CF 3 CF 2 C(O)CH 2 CH 3 , CF 3 CF 2 C(O)CH 2 CHF 2 , CF 3 CF 2 C(O)CH 2 CHF 2 , CF 3 CF 2 C(O)CH 2 CHF 2 , CF 3 CF 2 C(O)CH 2 CHF 2 , CF 3 CF 2 C(O)CH 2 CH 2 F, CF 3 CF
• hydrofluoroketones can be prepared by reacting a fluorinated acid with a Grignard reagent such as an alkylmagnesium bromide in an aprotic solvent, as described in Japanese Patent No. 2,869,432.
• a Grignard reagent such as an alkylmagnesium bromide in an aprotic solvent
• CF 2 CF 2 C(O)CH 3 can be prepared by reacting pentafluoropropionic acid with magnesium methyl bromide in dibutyl ether.
• Other hydrofluoroketones can be prepared by reacting a partially fluorinated acyl fluoride with hexafluoropropylene in an anhydrous environment in the presence of fluoride ion at elevated temperature, as described in U.S. Patent Application Ser. No. 09/619306.
• HCF 2 CF 2 C(O)CF(CF 3 ) 2 can be prepared by oxidizing tetrafluoropropanol with acidic dichromate, then reacting the resulting HC 2 H COOH with benzotrichloride to form HC 2 H 4 C(O)Cl, converting the acyl chloride to the acyl fluoride by reaction with anhydrous sodium fluoride, and then reacting the HC 2 H 4 C(O)F with hexafluoropropylene under pressure.
• the gaseous mixture that comprises a fluorocarbon selected from the group consisting of perfluoroketones and hydrofluoroketones further comprises a carrier gas or carrier gases.
• carrier gases include air, CO 2 , argon, nitrogen and mixtures thereof.
• the carrier gas that is used with the perfluroketones is dry air.
• the gaseous mixture comprises a minor amount of the fluorocarbon and a major amount of the carrier gas.
• the gaseous mixture consists of less than about 1% of the fluorocarbon and the balance carrier gas. More preferably, the gaseous mixture contains less than 0.5% by volume (most preferably less that 0.1% by volume) fluorocarbon, selected from the group consisting of perfluoroketones, hydrofluoroketones and mixtures thereof.
• a cover gas composition is of low toxicity both as it is applied to the molten magnesium and as it is emitted from the process in which it is used. Cover gases comprising low toxicity hydrofluoroketones and perfluoroketones, and mixtures thereof, will be safe mixtures as applied to magnesium.
• all fluorine containing cover gas composition produce measurable amounts of hydrogen fluoride upon contact with the molten magnesium due to some level of thermal degradation and reaction with magnesium at temperatures of 650 to 750°C. Hydrogen fluoride is corrosive and toxic and its concentration in the emitted gas should be minimized.
• a preferred cover gas composition will, therefore, produce minimal hydrogen fluoride. See Examples, below.
• the perfluoroketones and hydrofluoroketones of the invention have much lower global warming potential (GWP) than the fluorocarbons known in the art such as SF 6 , hydrofluorocarbons, and hydrofluoroethers.
• GWP global warming potential
• the GWP of a compound as defined by the Intergovernmental Panel on Climate Change (IPCC) in 1990 and updated in Scientific Assessment of Ozone Depletion: 1998 (World Meteorological Organization, Scientific Assessment of Ozone Depletion: 1998, Global Ozone Research and Monitoring Project - Report No. 44, Geneva, 1999), is calculated as the warming due to the release of 1 kilogram of a compound relative to the warming due to the release of 1 kilogram of CO 2 over a specified integration time horizon (ITH).
• ITH integration time horizon
• F is the radiative forcing per unit mass of a compound (the change in the flux of radiation through the atmosphere due to the IR absorbance of that compound)
• C is the atmospheric concentration of a compound
• ⁇ is the atmospheric lifetime of a compound
• t is time
• x is the compound of interest.
• the commonly accepted ITH is 100 years representing a compromise between short-term effects (20 years) and longer-term effects (500 years or longer).
• the concentration of an organic compound, x, in the atmosphere is assumed to follow pseudo first order kinetics (i.e., exponential decay).
• the concentration of CO 2 over that same time interval incorporates a more complex model for the exchange and removal of CO 2 from the atmosphere (the Bern carbon cycle model).
• Carbonyl compounds such as aldehydes and ketones have been shown to have measurable photolysis rates in the lower atmosphere resulting in very short atmospheric lifetimes.
• Compounds such as formaldehyde, acetaldehyde, propionaldehyde, isobutyraldehyde, n-butyraldehyde, acetone, 2-butanone, 2-pentanone and 3-pentanone have atmospheric lifetimes by photolysis ranging from 4 hours to 38 days (Martinez, R.D., et al, 1992, Atmospheric Environment, 26, 785-792, and Seinfeld, J.H. and Pandis, S.N., Atmospheric Chemistry and Physics, John Wiley & Sons, New York, p.
• CF 3 CF 2 C(O)CF(CF 3 ) 2 has an atmospheric lifetime of approximately 5 days based on photolysis studies at 300 nm.
• Other perfluoroketones and hydrofluoroketones show similar absorbances near 300 nm and are expected to have similar atmospheric lifetimes.
• the GWP for HCF 2 CF 2 C(O)CF(CF 3 ) 2 is calculated to be 9.
• the perfluoroketones and hydrofluoroketones of the invention typically have a GWP less than about 10.
• the perfluoroketones and hydrofluoroketones have short lifetimes and would not be expected to contribute significantly to global warming.
• the low GWP of the perfluoroketones make them well suited for use as an environmentally preferred cover gas.
• the PFKs and HFKs of this invention can react more fully with molten magnesium than does SF 6 .
• less unreacted cover gas can be emitted to the atmosphere; less cover gas can be required to produce a comparably performing protective film; or both. Consequently, useful concentrations of the cover gas can be lowered, thus reducing the global warming impact.
• the full substitution of fluorocarbons of the present invention for SF 6 can be accomplished without increasing the risk to worker safety since these materials (PFKs, and HFKs) are of low toxicity, are non-flammable, and are generally very innocuous materials.
• Substitution for SF 6 with a PFK, or HFK, alone or as a mixture thereof, can provide protection of molten magnesium in various processes, such as magnesium refining, alloying, formation of ingots or casting of parts.
• This substitution can be straightforward and can provide the same utility as a reactive cover gas that only SF 6 does currently.
• Surface films produced with the fluorocarbons of the present invention can be more stable to higher temperatures than those formed with SO 2 , enabling work with higher melt temperatures (e.g., additional alloys, more complex casting parts).
• fluorocarbons of the present invention as reactive cover gases can include a significant reduction in the emission of a potent greenhouse gas (i.e., SF 6 ), a potential reduction in the amount of fluorine-containing reactive cover gas required to provide protection, and a reduction in total emissions.
• a potent greenhouse gas i.e., SF 6
• This substitution can be done without increasing risks for workers since the fluorocarbons of the present invention are all safe materials with which to work, have low toxicity, are nonflammable, and are not a detriment to production equipment.
• perfluoroketones, or hydrofluoroketones, or mixtures thereof, in a gaseous mixture demonstrate the ability to also put out fires that are already occurring on the surface of molten magnesium. Therefore, the gases also may be used to extinguish fires on molten magnesium.
• FTIR spectrophotometer Modac 12000 Gas Phase FTIR with a mercury cadmium telluride (MCT) detector.
• MCT mercury cadmium telluride
• EPA Method 320 Modified Extractive FTIR
• concentrations were measured over a period of 5 to 10 minutes, average values of these concentrations were calculated, and those average values were used to make a relative comparison of the test cover gases.
• initial magnesium melting was done using a standard cover gas of 0.5% SF 6 in CO 2 at a flow rate of 5.9 L/min.
• the experimental gas mixture was then substituted for the standard cover gas mixture by utilizing a train of rotameters and valves. Dry air (having a -40°C dew point) at a flow rate of 5.9 L/min was used to create the test cover gas by evaporating a flow of test fluid in it such that a volumetric concentration of 0.03 to 1 volume % fluorocarbon in air was produced.
• the molten magnesium was observed for a period of about 20 to 30 minutes (equivalent to 10 to 15 chamber volumes exchanges of cover gas) to monitor any visible changes to the surface that would indicate the start of magnesium burning.
• the existing surface film was then removed by skimming the surface for about 3 - 5 minutes.
• the new surface film that formed was then observed for a period of at 15 - 30 minutes
• the concentration of the fluorocarbon component of the cover gas mixture was started at about 1% by volume in air and reduced sequentially in steps of Vi the previous concentration to a minimum fluorocarbon concentration of 0.03 to 0.06%.
• ⁇ ONECTM HFE-7100 Engineering Fluid from 3M Company, St. Paul, M ⁇ was evaluated as a fluorocarbon cover gas at 1% and at decreasing volumetric concentrations in air. In all cases, the volumetric flow rate for the cover gas/air mixture was 5.9 L/min. At nominal concentrations of about 1, 0.5, 0.25 and 0.125% (corresponds to 10000, 5000, 2500 and 1250 pp V, respectively), C 4 F 9 OCH produced a thin flexible surface film on molten magnesium immediately after skimming so that no evidence of metal burning was observed.
• CF 3 CF 2 C(O)CF(CF 3 ) 2 (l,l,l,2,4,4,5,5,5-nonafluoro-2-trifluoromethyl-pentan-3- one), a perfluoroketone, was evaluated as a cover gas to protect molten magnesium from ignition using essentially the same procedure as described in Comparative Example Cl using G t F OCH 3 .
• the CF 3 CF 2 C(O)CF(CF 3 ) was prepared and purified using the following procedures.
• the reactor contents were allowed to cool and were one-plate distilled to obtain 307.1 g containing 90.6% CF 3 CF 2 C(O)CF(CF 3 ) 2 and 0.37% C 6 F 12 (hexafluoropropylene dimer) as determined by gas chromatography.
• the crude fluorinated ketone was water- washed, distilled, and dried by contacting with silica gel to provide a fractionated fluorinated ketone of 99% purity and containing 0.4% hexafluoropropylene dimers.
• a sample of fractionated CF 3 CF 2 C(O)CF(CF ) 2 made according to the above- described procedure was purified of hexafluoropropylene dimers using the following procedure.
• Into a clean dry 600 mL Parr reactor equipped with stirrer, heater and thermocouple were added 61 g of acetic acid, 1.7 g of potassium permanganate, and 301 g of the above-described fractionated 1,1, 1,2,4,4,5, 5, 5-nonafluoro-2-trifluoromethyl-pentan- 3-one.
• the reactor was sealed and heated to 60°C, while stirring, reaching a pressure of 12 psig (1400 torr).
• a liquid sample was taken using a dip tube, the sample was phase split and the lower phase was washed with water.
• the sample was analyzed using gas-liquid chromatography ("glc") and showed undetectable amounts of hexafluoropropylene dimers and small amounts of hexafluoropropylene trimers.
• a second sample was taken 60 minutes later and was treated similarly. The glc analysis of the second sample showed no detectable dimers or trimers.
• the reaction was stopped after 3.5 hours, and the purified ketone was phase split from the acetic acid and the lower phase was washed twice with water. 261 g of CF CF 2 C(O)CF(CF 3 ) 2 was collected, having a purity greater than 99.6% by glc and containing no detectable hexafluoropropylene dimers or trimers.
• the perfluorinated ketone, CF 3 CF 2 C(O)CF(CF 3 ) 2 was then evaluated as a fluorocarbon cover gas at 1% and at decreasing volumetric concentrations in air (i.e., at about 1.0, 0.5, 0.25, 0.12, 0.06 and 0.03% by volume; corresponds to 10000, 5000, 2500, 1250, 600 and 300 ppm, respectively).
• CF 3 CF 2 C(O)CF(CF 3 ) 2 produced a thin flexible surface film on the molten magnesium during skimming and prevented metal ignition.
• the film visually appeared to be thinner and more elastic than the surface film produced in the initial molten magnesium protection using SF 6 as a cover gas and in Comparative Example Cl using C 4 F 9 OCH. S as a cover gas.
• the silvery-gray film produced was stable and did not change appearance over at least 30 minutes. This is in contrast to the test series using C F OCH 3 , where evidence of metal burning was noted when the cover gas concentration was reduced to about 625 ppm.
• the perfluorinated ketone outperformed the hydrofluoroether as a cover gas for molten magnesium (i.e. protected the molten magnesium at lower concentrations) and also generated less hydrogen fluoride as a degradation product upon exposure to the molten metal surface.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Mechanical Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Materials Engineering (AREA)
• Metallurgy (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Geology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Environmental & Geological Engineering (AREA)
• General Life Sciences & Earth Sciences (AREA)
• General Chemical & Material Sciences (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Manufacture And Refinement Of Metals (AREA)
• Other Surface Treatments For Metallic Materials (AREA)
• Refinement Of Pig-Iron, Manufacture Of Cast Iron, And Steel Manufacture Other Than In Revolving Furnaces (AREA)

Priority Applications (7)

Applications Claiming Priority (4)

Publications (2)

Family

ID=26897426

Family Applications (1)

Country Status (10)

Cited By (7)

Families Citing this family (8)

Family Cites Families (21)

• 2001
  • 2001-02-09 US US09/780,256 patent/US6537346B2/en not_active Expired - Lifetime
  • 2001-03-28 IL IL14720201A patent/IL147202A0/xx unknown
  • 2001-03-28 AU AU2001252990A patent/AU2001252990A1/en not_active Abandoned
  • 2001-03-28 MX MXPA01013455A patent/MXPA01013455A/es unknown
  • 2001-03-28 WO PCT/US2001/009899 patent/WO2001083836A2/en not_active Ceased
  • 2001-03-28 JP JP2001580443A patent/JP4773668B2/ja not_active Expired - Fee Related
  • 2001-03-28 KR KR1020027000054A patent/KR100727502B1/ko not_active Expired - Fee Related
  • 2001-03-28 EP EP01926456A patent/EP1278897B1/en not_active Expired - Lifetime
  • 2001-03-28 DE DE60108371T patent/DE60108371T2/de not_active Expired - Lifetime
• 2002
  • 2002-01-03 NO NO20020027A patent/NO20020027L/no unknown

Also Published As

Similar Documents

Legal Events