WO2001082269A2 - Display member having metallic luster - Google Patents
Display member having metallic luster Download PDFInfo
- Publication number
- WO2001082269A2 WO2001082269A2 PCT/US2001/012823 US0112823W WO0182269A2 WO 2001082269 A2 WO2001082269 A2 WO 2001082269A2 US 0112823 W US0112823 W US 0112823W WO 0182269 A2 WO0182269 A2 WO 0182269A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- display member
- metallic
- thickness
- substrate
- Prior art date
Abstract
Description
Claims