WO2001007676A1 - Appareil de revetement de cables - Google Patents

Appareil de revetement de cables Download PDF

Info

Publication number
WO2001007676A1
WO2001007676A1 PCT/EP2000/006177 EP0006177W WO0107676A1 WO 2001007676 A1 WO2001007676 A1 WO 2001007676A1 EP 0006177 W EP0006177 W EP 0006177W WO 0107676 A1 WO0107676 A1 WO 0107676A1
Authority
WO
WIPO (PCT)
Prior art keywords
molten metal
channel
massive block
wire
metal bath
Prior art date
Application number
PCT/EP2000/006177
Other languages
English (en)
Inventor
Thomas Lagodny
Original Assignee
Trefilarbed Bissen S.A.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Trefilarbed Bissen S.A. filed Critical Trefilarbed Bissen S.A.
Priority to AU58233/00A priority Critical patent/AU5823300A/en
Publication of WO2001007676A1 publication Critical patent/WO2001007676A1/fr

Abstract

Un appareil (10) de revêtement de câbles comprend un bain de métal (14), un dispositif pour tirer n (n≥2) fils (16) en parallèle à travers ledit bain de métal (14), et un bloc massif (20) partiellement submergé dans ledit bain (14). Ce bloc massif (20) présente n canaux (22), chaque câble étant tiré hors dudit bain (14) à travers un des canaux (22).
PCT/EP2000/006177 1999-07-23 2000-07-03 Appareil de revetement de cables WO2001007676A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU58233/00A AU5823300A (en) 1999-07-23 2000-07-03 Wire coating apparatus

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
LU90422A LU90422B1 (en) 1999-07-23 1999-07-23 Wire coating apparatus
LU90422 1999-07-23

Publications (1)

Publication Number Publication Date
WO2001007676A1 true WO2001007676A1 (fr) 2001-02-01

Family

ID=19731826

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2000/006177 WO2001007676A1 (fr) 1999-07-23 2000-07-03 Appareil de revetement de cables

Country Status (3)

Country Link
AU (1) AU5823300A (fr)
LU (1) LU90422B1 (fr)
WO (1) WO2001007676A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2320129A (en) * 1939-06-23 1943-05-25 American Steel & Wire Co Metal coating
US2934458A (en) * 1953-05-21 1960-04-26 Goodrich Co B F Method for coating filaments of glass
FR1460653A (fr) * 1965-09-02 1966-01-07 Armco Steel Corp Dispositif pour le revêtement en continu de fils métalliques avec un métal fondu
US4178397A (en) * 1978-07-12 1979-12-11 Bethlehem Steel Corporation Method and apparatus for treating one side of a strip
US4412503A (en) * 1982-07-28 1983-11-01 United States Steel Corporation Sinker assembly for hot-dip coating applications
JPH04285145A (ja) * 1991-03-15 1992-10-09 Furukawa Electric Co Ltd:The 溶融めっき装置
JPH0688195A (ja) * 1992-09-04 1994-03-29 Furukawa Electric Co Ltd:The 溶融メッキ方法

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2320129A (en) * 1939-06-23 1943-05-25 American Steel & Wire Co Metal coating
US2934458A (en) * 1953-05-21 1960-04-26 Goodrich Co B F Method for coating filaments of glass
FR1460653A (fr) * 1965-09-02 1966-01-07 Armco Steel Corp Dispositif pour le revêtement en continu de fils métalliques avec un métal fondu
US4178397A (en) * 1978-07-12 1979-12-11 Bethlehem Steel Corporation Method and apparatus for treating one side of a strip
US4412503A (en) * 1982-07-28 1983-11-01 United States Steel Corporation Sinker assembly for hot-dip coating applications
JPH04285145A (ja) * 1991-03-15 1992-10-09 Furukawa Electric Co Ltd:The 溶融めっき装置
JPH0688195A (ja) * 1992-09-04 1994-03-29 Furukawa Electric Co Ltd:The 溶融メッキ方法

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 017, no. 093 (C - 1029) 24 February 1993 (1993-02-24) *
PATENT ABSTRACTS OF JAPAN vol. 018, no. 351 (C - 1220) 4 July 1994 (1994-07-04) *

Also Published As

Publication number Publication date
AU5823300A (en) 2001-02-13
LU90422B1 (en) 2001-01-24

Similar Documents

Publication Publication Date Title
US20150368776A1 (en) Apparatus for Hot Dip Coating Metal Strip
JP4256929B2 (ja) 亜鉛めっき方法及びシステム
EP0038036B1 (fr) Dispositif travaillant sous une atmosphère protectrice et utilisant un gaz pour éliminer l'excès de métal fondu ainsi que méthode d'utilisation dudit dispositif
EP3827903A1 (fr) Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré
US20040052958A1 (en) Method and installation for dip coating of a metal strip
US6214420B1 (en) Process and plant for metallization of cast-iron pipes
KR0128161B1 (ko) 제트 세척 노즐
US4155235A (en) Production of heavy pure aluminum coatings on small diameter tubing
WO2001007676A1 (fr) Appareil de revetement de cables
US20040052959A1 (en) Method and installation for hot process and continuous dip coating of a metal strip
HUP0302619A2 (hu) Eljárás és berendezés fémszalag folyamatos rákristályosító bemerítő bevonására
US5391135A (en) Rolls for hot dipping bath
US3727895A (en) Cooling coated wires, strips and the like
JPS6157885B2 (fr)
US5512321A (en) Process for coating elongated materials with multiple layers
JP3514130B2 (ja) 鋼帯の竪型冷却装置及び冷却方法
US4207831A (en) Apparatus for one side coating of a continuous strip
US5451429A (en) Method and apparatus for treating freshly metallized substrates
JPH1143752A (ja) 溶融金属メッキラインのクリーニングノズル配置構造
JPH11158593A (ja) 溶融めっき設備の空中浮揚ポット
ZA200200122B (en) Gas wiping nozzle for a wire coating apparatus.
US2166251A (en) Apparatus for coating metallic materials
JPH07150320A (ja) 溶融金属めっき方法及び装置
JPH07157854A (ja) 溶融金属めっきのスナウト内清浄化方法及び装置
JP3767895B2 (ja) めっき鋼線の冷却装置

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP