WO2000051799A1 - Additifs migratoires pour masque integral d'un materiau en couche decoratif - Google Patents
Additifs migratoires pour masque integral d'un materiau en couche decoratif Download PDFInfo
- Publication number
- WO2000051799A1 WO2000051799A1 PCT/US2000/040003 US0040003W WO0051799A1 WO 2000051799 A1 WO2000051799 A1 WO 2000051799A1 US 0040003 W US0040003 W US 0040003W WO 0051799 A1 WO0051799 A1 WO 0051799A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- paint film
- sheet material
- layer
- decorative
- mask
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU32495/00A AU3249500A (en) | 1999-03-01 | 2000-02-16 | Migratory additives for mask layer of decorative sheet material |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US25969999A | 1999-03-01 | 1999-03-01 | |
US09/259,699 | 1999-03-01 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2000051799A1 true WO2000051799A1 (fr) | 2000-09-08 |
Family
ID=22985994
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2000/040003 WO2000051799A1 (fr) | 1999-03-01 | 2000-02-16 | Additifs migratoires pour masque integral d'un materiau en couche decoratif |
Country Status (2)
Country | Link |
---|---|
AU (1) | AU3249500A (fr) |
WO (1) | WO2000051799A1 (fr) |
Cited By (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2375722A (en) * | 2001-03-28 | 2002-11-27 | Lintec Corp | Application sheet used for attaching a paint adhesive sheet to a surface |
WO2003016095A1 (fr) * | 2001-08-16 | 2003-02-27 | Basf Coatings Ag | Feuilles conferant une couleur et/ou un effet, leur procede de production et leur utilisation |
WO2003020528A3 (fr) * | 2001-08-29 | 2003-10-09 | Wipak Walsrode Gmbh & Co Kg | Systeme de transfert de decor colore |
US6824818B2 (en) * | 2001-12-27 | 2004-11-30 | Soliant Llc | Wet on wet process for producing films |
WO2007082906A2 (fr) * | 2006-01-20 | 2007-07-26 | Alice Engineering Di Bondesan Valerio E Caenazzo Santo (Associazione Di Professionisti) | Film de transfert extensible pour revetement de surface, procede de production et d'application du film |
EP1859932A1 (fr) * | 2006-05-22 | 2007-11-28 | Yamaha Hatsudoki Kabushiki Kaisha | Feuille décorative, produit formé et appareil de transport |
EP1876035A1 (fr) * | 2005-03-31 | 2008-01-09 | Yoshino Kogyosho Co., Ltd. | Film de transfert |
GB2440609A (en) * | 2006-06-23 | 2008-02-06 | Kent Phillips | Self-adhesive paint film for motorcycles |
WO2008042883A3 (fr) * | 2006-10-04 | 2009-03-26 | 3M Innovative Properties Co | Procédé de fabrication d'un film de protection multicouche en polyuréthanne |
WO2014039841A1 (fr) * | 2012-09-06 | 2014-03-13 | Xamax Industries, Inc. | Matériau composite en feuilles et son procédé de formage |
US9138974B2 (en) | 2012-09-06 | 2015-09-22 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
CN110230201A (zh) * | 2019-06-20 | 2019-09-13 | 广州百思创科技有限公司 | 一种低温耐久性聚三嗪类亲水整理剂的制备方法与应用 |
CN111645383A (zh) * | 2019-03-04 | 2020-09-11 | Oppo广东移动通信有限公司 | 电池盖的制作方法和移动终端 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5127974A (en) * | 1989-05-15 | 1992-07-07 | Kansai Paint Co., Ltd. | Method of protecting coating film |
WO1994003337A2 (fr) * | 1992-07-31 | 1994-02-17 | Minnesota Mining And Manufacturing Company | Film de peinture et son procede de fabrication |
US5725712A (en) * | 1987-03-27 | 1998-03-10 | Avery Dennison Corporation | Dry paint transfer process for making high DOI automotive body panels |
WO1999008870A1 (fr) * | 1997-08-18 | 1999-02-25 | Minnesota Mining And Manufacturing Company | Ensemble de film de peinture a film de masquage |
-
2000
- 2000-02-16 AU AU32495/00A patent/AU3249500A/en not_active Abandoned
- 2000-02-16 WO PCT/US2000/040003 patent/WO2000051799A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5725712A (en) * | 1987-03-27 | 1998-03-10 | Avery Dennison Corporation | Dry paint transfer process for making high DOI automotive body panels |
US5127974A (en) * | 1989-05-15 | 1992-07-07 | Kansai Paint Co., Ltd. | Method of protecting coating film |
WO1994003337A2 (fr) * | 1992-07-31 | 1994-02-17 | Minnesota Mining And Manufacturing Company | Film de peinture et son procede de fabrication |
WO1999008870A1 (fr) * | 1997-08-18 | 1999-02-25 | Minnesota Mining And Manufacturing Company | Ensemble de film de peinture a film de masquage |
Cited By (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2375722A (en) * | 2001-03-28 | 2002-11-27 | Lintec Corp | Application sheet used for attaching a paint adhesive sheet to a surface |
GB2375722B (en) * | 2001-03-28 | 2004-09-08 | Lintec Corp | Application sheet used for pressure-sensitive adhesive sheet for painting and method of attaching the pressure-sensitive adhesive sheet for painting |
US7005183B2 (en) | 2001-03-28 | 2006-02-28 | Lintec Corporation | Application sheet used for pressure-sensitive adhesive sheet for painting |
WO2003016095A1 (fr) * | 2001-08-16 | 2003-02-27 | Basf Coatings Ag | Feuilles conferant une couleur et/ou un effet, leur procede de production et leur utilisation |
US7682666B2 (en) | 2001-08-16 | 2010-03-23 | Basf Coatings Ag | Method of producing a color and/or effect film exhibiting an isotropic flop behavior and an isotropic color locus |
WO2003020528A3 (fr) * | 2001-08-29 | 2003-10-09 | Wipak Walsrode Gmbh & Co Kg | Systeme de transfert de decor colore |
US6824818B2 (en) * | 2001-12-27 | 2004-11-30 | Soliant Llc | Wet on wet process for producing films |
EP1876035A1 (fr) * | 2005-03-31 | 2008-01-09 | Yoshino Kogyosho Co., Ltd. | Film de transfert |
EP1876035A4 (fr) * | 2005-03-31 | 2012-08-15 | Yoshino Kogyosho Co Ltd | Film de transfert |
WO2007082906A3 (fr) * | 2006-01-20 | 2007-11-15 | Alice Engineering Di Bondesan | Film de transfert extensible pour revetement de surface, procede de production et d'application du film |
WO2007082906A2 (fr) * | 2006-01-20 | 2007-07-26 | Alice Engineering Di Bondesan Valerio E Caenazzo Santo (Associazione Di Professionisti) | Film de transfert extensible pour revetement de surface, procede de production et d'application du film |
EP1859932A1 (fr) * | 2006-05-22 | 2007-11-28 | Yamaha Hatsudoki Kabushiki Kaisha | Feuille décorative, produit formé et appareil de transport |
US7678469B2 (en) | 2006-05-22 | 2010-03-16 | Yamaha Hatsudoki Kabushiki Kaisha | Decorative sheet, formed product and transportation apparatus |
GB2440609A (en) * | 2006-06-23 | 2008-02-06 | Kent Phillips | Self-adhesive paint film for motorcycles |
US8128779B2 (en) | 2006-10-04 | 2012-03-06 | 3M Innovative Properties Company | Method of making multilayer polyurethane protective film |
KR101442280B1 (ko) * | 2006-10-04 | 2014-09-22 | 쓰리엠 이노베이티브 프로퍼티즈 컴파니 | 다층 폴리우레탄 보호 필름의 제조 방법 |
US8551285B2 (en) | 2006-10-04 | 2013-10-08 | 3M Innovative Properties Company | Method of making multilayer polyurethane protective film |
WO2008042883A3 (fr) * | 2006-10-04 | 2009-03-26 | 3M Innovative Properties Co | Procédé de fabrication d'un film de protection multicouche en polyuréthanne |
US9205635B2 (en) | 2012-09-06 | 2015-12-08 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
US9138974B2 (en) | 2012-09-06 | 2015-09-22 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
US9138943B2 (en) | 2012-09-06 | 2015-09-22 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
US9138975B2 (en) | 2012-09-06 | 2015-09-22 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
US9199440B2 (en) | 2012-09-06 | 2015-12-01 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
WO2014039841A1 (fr) * | 2012-09-06 | 2014-03-13 | Xamax Industries, Inc. | Matériau composite en feuilles et son procédé de formage |
US9339987B2 (en) | 2012-09-06 | 2016-05-17 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
US9566769B2 (en) | 2012-09-06 | 2017-02-14 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
US9889637B2 (en) | 2012-09-06 | 2018-02-13 | Xamax Industries, Inc. | Composite sheet material and method for forming the same |
EP3888903A1 (fr) * | 2012-09-06 | 2021-10-06 | Xamax Industries, Inc. | Procédé de formage pour un metériau composite en feuilles |
CN111645383A (zh) * | 2019-03-04 | 2020-09-11 | Oppo广东移动通信有限公司 | 电池盖的制作方法和移动终端 |
CN111645383B (zh) * | 2019-03-04 | 2022-12-13 | Oppo广东移动通信有限公司 | 电池盖的制作方法和移动终端 |
CN110230201A (zh) * | 2019-06-20 | 2019-09-13 | 广州百思创科技有限公司 | 一种低温耐久性聚三嗪类亲水整理剂的制备方法与应用 |
Also Published As
Publication number | Publication date |
---|---|
AU3249500A (en) | 2000-09-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1948262B1 (fr) | Procédé pour obtenir un film de peinture decoratif stratifie, procédé pour appliquer un film décoratif sur une pièce, et pièce composite ainsi formée | |
US6565955B2 (en) | Bright indium-metallized formable film laminate | |
US6440546B1 (en) | Gloss-adjusting mask layer with particulate filler | |
JP6005911B2 (ja) | 真空圧空成形または真空成形により一体化された構造体、およびその製造方法 | |
CA2266873C (fr) | Systeme de pellicule de fini permettant l'emploi des motifs | |
KR101009968B1 (ko) | 장식성 자동차 부품용 고광택 라미네이트 | |
US6824818B2 (en) | Wet on wet process for producing films | |
JPH06501215A (ja) | 熱成形可能な支持層を有する表面フィルム | |
US7507363B2 (en) | Methods of thermoforming non-self-supporting polymeric films and articles made therefrom | |
WO2000051799A1 (fr) | Additifs migratoires pour masque integral d'un materiau en couche decoratif | |
AU4001400A (en) | Decorative sheet material with chlorinated polyolefin adhesive layer | |
WO2000051798A1 (fr) | Materiau decoratif en feuille comportant une couche de masquage | |
JP3137618B2 (ja) | インサート成形品製造用積層フィルムとこれを用いたインサートフィルムの製造方法、インサート成形品の製造方法 | |
WO2002000448A2 (fr) | Film de masquage de protection extensible, et pieces fabriquees avec ce film | |
US20020192440A1 (en) | Bright tin-metallized formable film laminate | |
JP2016147505A (ja) | 真空圧空成形または真空成形により一体化された構造体、およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AL AM AT AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ CZ DE DE DK DK DM EE EE ES FI FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
122 | Ep: pct application non-entry in european phase |