WO2000044830A1 - Light-reflecting molded - Google Patents
Light-reflecting molded Download PDFInfo
- Publication number
- WO2000044830A1 WO2000044830A1 PCT/US2000/002149 US0002149W WO0044830A1 WO 2000044830 A1 WO2000044830 A1 WO 2000044830A1 US 0002149 W US0002149 W US 0002149W WO 0044830 A1 WO0044830 A1 WO 0044830A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- article
- percent
- filler
- light
- particles
- Prior art date
Abstract
Description
Claims