WO1999048682A1 - Tarnish resistant article, preparation, manufacture and methods of use of same - Google Patents
Tarnish resistant article, preparation, manufacture and methods of use of same Download PDFInfo
- Publication number
- WO1999048682A1 WO1999048682A1 PCT/US1999/006775 US9906775W WO9948682A1 WO 1999048682 A1 WO1999048682 A1 WO 1999048682A1 US 9906775 W US9906775 W US 9906775W WO 9948682 A1 WO9948682 A1 WO 9948682A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- self
- alkylthiol
- article
- assembled monolayer
- silver
- Prior art date
Abstract
Description
Claims