WO1999047723A1 - Forming a plain bearing lining - Google Patents
Forming a plain bearing lining Download PDFInfo
- Publication number
- WO1999047723A1 WO1999047723A1 PCT/GB1999/000748 GB9900748W WO9947723A1 WO 1999047723 A1 WO1999047723 A1 WO 1999047723A1 GB 9900748 W GB9900748 W GB 9900748W WO 9947723 A1 WO9947723 A1 WO 9947723A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- layer
- group
- deposited
- bearing
- Prior art date
Abstract
Description
Claims