WO1999005550A1 - Fibres de verre optique a plusieurs coeurs et procedes de fabrication de ces fibres - Google Patents

Fibres de verre optique a plusieurs coeurs et procedes de fabrication de ces fibres Download PDF

Info

Publication number
WO1999005550A1
WO1999005550A1 PCT/US1998/013373 US9813373W WO9905550A1 WO 1999005550 A1 WO1999005550 A1 WO 1999005550A1 US 9813373 W US9813373 W US 9813373W WO 9905550 A1 WO9905550 A1 WO 9905550A1
Authority
WO
WIPO (PCT)
Prior art keywords
fiber
multicore
cores
canes
core
Prior art date
Application number
PCT/US1998/013373
Other languages
English (en)
Inventor
Richard M. Fiacco
Michael J. Hackert
Daniel W. Hawtof
Ted M. Vanryn
Original Assignee
Corning Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Incorporated filed Critical Corning Incorporated
Priority to AU83766/98A priority Critical patent/AU8376698A/en
Priority to JP2000504477A priority patent/JP2001511538A/ja
Priority to EP98934184A priority patent/EP1002249A1/fr
Priority to KR1020007000792A priority patent/KR20010022219A/ko
Publication of WO1999005550A1 publication Critical patent/WO1999005550A1/fr

Abstract

Cette fibre de verre optique (20) comprend plusieurs coeurs (14) fusionnés en une fibre unique. Cette fibre est cohérente en ce sens que les coeurs conservent chacun leur position relative sur toute la longueur de la fibre. Dans l'un des aspects de l'invention, la fibre possède une coupe transversale circulaire, dans un autre, elle possède une coupe transversale elliptique dotée d'une plus grande excentricité et ce, afin de faciliter l'orientation des coeurs à l'intérieur de la fibre aux fins d'une connexion à d'autres composants optiques. La fibre peut avantageusement être pourvue d'un coeur orienteur (226), ce qui permet de mieux orienter son extrémité. Lors de la fabrication de cette fibre optique, on bourre un tube de silice (12) de tiges de coeur (14). L'ensemble résultant est alors fondu ou fusionné, de préférence tout en étant étiré sous vide, afin de produire une ébauche de fibre intégrée (10) à plusieurs coeurs pouvant ensuite être étirée jusqu'à avoir un diamètre normalisé et ce, au moyen de techniques classiques d'étirage de fibre. Selon une variante de l'invention, il est possible d'associer en une seule opération la fusion et l'étirage.
PCT/US1998/013373 1997-07-25 1998-06-24 Fibres de verre optique a plusieurs coeurs et procedes de fabrication de ces fibres WO1999005550A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
AU83766/98A AU8376698A (en) 1997-07-25 1998-06-24 Multicore glass optical fiber and methods of manufacturing such fibres
JP2000504477A JP2001511538A (ja) 1997-07-25 1998-06-24 多心ガラス光ファイバおよびかかるファイバの製造方法
EP98934184A EP1002249A1 (fr) 1997-07-25 1998-06-24 Fibres de verre optique a plusieurs coeurs et procedes de fabrication de ces fibres
KR1020007000792A KR20010022219A (ko) 1997-07-25 1998-06-24 멀티코아 유리 광섬유 및 이의 제조방법

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US5385797P 1997-07-25 1997-07-25
US60/053,857 1997-07-25

Publications (1)

Publication Number Publication Date
WO1999005550A1 true WO1999005550A1 (fr) 1999-02-04

Family

ID=21987027

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1998/013373 WO1999005550A1 (fr) 1997-07-25 1998-06-24 Fibres de verre optique a plusieurs coeurs et procedes de fabrication de ces fibres

Country Status (6)

Country Link
EP (1) EP1002249A1 (fr)
JP (1) JP2001511538A (fr)
KR (1) KR20010022219A (fr)
AU (1) AU8376698A (fr)
TW (1) TW367311B (fr)
WO (1) WO1999005550A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001092929A2 (fr) * 2000-05-30 2001-12-06 Infineon Technologies North America Corp. Connecteurs à plusieurs fibres optiques
WO2002016985A1 (fr) * 2000-08-21 2002-02-28 Corning Incorporated Procede de fabrication des fibres optiques separables a plusieurs noyaux, structures de fibres ainsi obtenues et leurs utilisations
US6611648B2 (en) 2001-05-09 2003-08-26 Corning Incorporated Optical fibers having cores with different propagation constants, and methods of manufacturing same
EP2336813A1 (fr) * 2008-10-03 2011-06-22 National University Corporation Yokohama National University Fibre multic ur d'un système couplé, multiplexeur et démultiplexeur en mode couplage, système de transmission utilisant une fibre multic ur et procédé de transmission utilisant une fibre multic ur
CN103253859A (zh) * 2013-05-09 2013-08-21 中国科学院上海光学精密机械研究所 涂覆层d形磷酸盐微结构带隙型光纤的制备方法
US8611716B2 (en) 2009-09-30 2013-12-17 Corning Incorporated Channeled substrates for integrated optical devices employing optical fibers
US9586852B2 (en) 2013-02-05 2017-03-07 Fujikura Ltd. Method of manufacturing preform for multicore fiber and method of manufacturing multicore fiber

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013020075A (ja) * 2011-07-11 2013-01-31 Hitachi Cable Ltd マルチコアファイバの製造方法
JP6291892B2 (ja) * 2014-02-19 2018-03-14 住友電気工業株式会社 マルチコア光ファイバ母材製造方法
WO2022236305A1 (fr) 2021-05-06 2022-11-10 Heraeus Quartz North America Llc Procédé de fabrication d'une préforme de fibre multi-cœur par intégration de tiges centrales et de cylindre de gainage
WO2023137269A1 (fr) 2022-01-14 2023-07-20 Heraeus Quartz North America Llc Réduction de distorsion géométrique de préforme à fibre multicœur

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS566202A (en) * 1979-06-29 1981-01-22 Nippon Telegr & Teleph Corp <Ntt> Multicore fiber and its production
JPS5741602A (en) * 1980-08-26 1982-03-08 Nippon Telegr & Teleph Corp <Ntt> Plural core optical fiber and its production
JPS59217632A (ja) * 1983-05-23 1984-12-07 Furukawa Electric Co Ltd:The マルチコアフアイバプリフオ−ムの製造方法
EP0695003A1 (fr) * 1994-07-27 1996-01-31 Hitachi Cable, Ltd. Fibre optique à coeur multiple dotée de terres rares, méthode de fabrication et amplificateur optique utilisant celle-ci
JPH08119656A (ja) * 1994-10-17 1996-05-14 Shin Etsu Chem Co Ltd マルチコアファイバ母材の製造方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS566202A (en) * 1979-06-29 1981-01-22 Nippon Telegr & Teleph Corp <Ntt> Multicore fiber and its production
JPS5741602A (en) * 1980-08-26 1982-03-08 Nippon Telegr & Teleph Corp <Ntt> Plural core optical fiber and its production
JPS59217632A (ja) * 1983-05-23 1984-12-07 Furukawa Electric Co Ltd:The マルチコアフアイバプリフオ−ムの製造方法
EP0695003A1 (fr) * 1994-07-27 1996-01-31 Hitachi Cable, Ltd. Fibre optique à coeur multiple dotée de terres rares, méthode de fabrication et amplificateur optique utilisant celle-ci
JPH08119656A (ja) * 1994-10-17 1996-05-14 Shin Etsu Chem Co Ltd マルチコアファイバ母材の製造方法

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 005, no. 052 (P - 056) 11 April 1981 (1981-04-11) *
PATENT ABSTRACTS OF JAPAN vol. 006, no. 112 (P - 124) 23 June 1982 (1982-06-23) *
PATENT ABSTRACTS OF JAPAN vol. 009, no. 082 (C - 275) 11 April 1985 (1985-04-11) *
PATENT ABSTRACTS OF JAPAN vol. 096, no. 009 30 September 1996 (1996-09-30) *

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001092929A2 (fr) * 2000-05-30 2001-12-06 Infineon Technologies North America Corp. Connecteurs à plusieurs fibres optiques
WO2001092929A3 (fr) * 2000-05-30 2003-03-06 Infineon Technologies Corp Connecteurs à plusieurs fibres optiques
WO2002016985A1 (fr) * 2000-08-21 2002-02-28 Corning Incorporated Procede de fabrication des fibres optiques separables a plusieurs noyaux, structures de fibres ainsi obtenues et leurs utilisations
US6539151B2 (en) 2000-08-21 2003-03-25 Corning, Incorporated Method for making separable multiple core optical fibers, the resulting fiber structures, and uses thereof
US6611648B2 (en) 2001-05-09 2003-08-26 Corning Incorporated Optical fibers having cores with different propagation constants, and methods of manufacturing same
EP2336813A1 (fr) * 2008-10-03 2011-06-22 National University Corporation Yokohama National University Fibre multic ur d'un système couplé, multiplexeur et démultiplexeur en mode couplage, système de transmission utilisant une fibre multic ur et procédé de transmission utilisant une fibre multic ur
CN102203648A (zh) * 2008-10-03 2011-09-28 国立大学法人横滨国立大学 耦合多芯光纤、耦合模合波分波器、多芯光纤传输系统、以及多芯光纤传输方法
EP2336813A4 (fr) * 2008-10-03 2012-06-20 Nat University Corp Yokohama Nat University Fibre multic ur d'un système couplé, multiplexeur et démultiplexeur en mode couplage, système de transmission utilisant une fibre multic ur et procédé de transmission utilisant une fibre multic ur
US8811786B2 (en) 2008-10-03 2014-08-19 National University Corporation Yokohama National University Coupled system multi-core fiber, coupling mode multiplexer and demultiplexer, system for transmission using multi-core fiber and method for transmission using multi-core fiber
US8611716B2 (en) 2009-09-30 2013-12-17 Corning Incorporated Channeled substrates for integrated optical devices employing optical fibers
US9586852B2 (en) 2013-02-05 2017-03-07 Fujikura Ltd. Method of manufacturing preform for multicore fiber and method of manufacturing multicore fiber
CN103253859A (zh) * 2013-05-09 2013-08-21 中国科学院上海光学精密机械研究所 涂覆层d形磷酸盐微结构带隙型光纤的制备方法

Also Published As

Publication number Publication date
JP2001511538A (ja) 2001-08-14
KR20010022219A (ko) 2001-03-15
AU8376698A (en) 1999-02-16
TW367311B (en) 1999-08-21
EP1002249A1 (fr) 2000-05-24

Similar Documents

Publication Publication Date Title
US6154594A (en) Multicore glass optical fiber and methods of manufacturing such fibers
EP0606583B1 (fr) Coupleur achromatique pour fibres optiques
EP2548057B1 (fr) Techniques et dispositifs pour un couplage à faible perte adapté en champ modal à une fibre multicoeur
US5553179A (en) Varied insertion loss fiber optic coupling and method of making same
US4842359A (en) Optical star coupler and method of manufacturing the same
EP0193921B1 (fr) Procédé de fabrication de fibres optiques à plusieurs noyaux
US5353363A (en) Optical fiber bendable coupler/switch device
US3990779A (en) Single optical fiber connector
US4859223A (en) Method of manufacturing polarization-maintaining optical fibers
EP0628839B1 (fr) Coupleur à faibles pertes
EP1002249A1 (fr) Fibres de verre optique a plusieurs coeurs et procedes de fabrication de ces fibres
CN111796361B (zh) 一种宽带平坦透过的多芯光纤耦合器的制备方法及其应用
US4836644A (en) Fiber optic star coupler
GB2319355A (en) Expanded core optical fibre coupler using UV curing resin
CA2422011A1 (fr) Methode de raccordement de fibres optiques et element multi-fibres
US5594822A (en) Fiber optic couplers, preform and method of making same
US5160522A (en) Method for producing preform for polarization retaining optical fiber
AU2020100756A4 (en) A multi-core optical fiber Fan-in/out device with a concave triple-clad transition fiber
AU657023B2 (en) Optical connection arrangement
JP3355575B2 (ja) 単一モード光ファイバ及び単一モード光ファイバのコア拡大方法
CN115373076A (zh) 一种光纤模场匹配器及其制备方法
NAGASAWA et al. Multi-Glass-Rod Optical-Fiber Splicers and Connectors Made by Drawing Technique
JP2000206361A (ja) 光ファイバ型多分岐カプラ―及びその製造方法
JPH01154006A (ja) 光ファイバカプラの製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 1020007000792

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 1998934184

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1998934184

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

NENP Non-entry into the national phase

Ref country code: CA

WWP Wipo information: published in national office

Ref document number: 1020007000792

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1020007000792

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1998934184

Country of ref document: EP