WO1998058796A1 - Etoffe composite - Google Patents

Etoffe composite Download PDF

Info

Publication number
WO1998058796A1
WO1998058796A1 PCT/GB1998/001867 GB9801867W WO9858796A1 WO 1998058796 A1 WO1998058796 A1 WO 1998058796A1 GB 9801867 W GB9801867 W GB 9801867W WO 9858796 A1 WO9858796 A1 WO 9858796A1
Authority
WO
WIPO (PCT)
Prior art keywords
ptfe
expanded
layer
membrane
porous
Prior art date
Application number
PCT/GB1998/001867
Other languages
English (en)
Inventor
Norman Ernest Clough
Original Assignee
W.L. Gore & Associates (Uk) Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by W.L. Gore & Associates (Uk) Ltd. filed Critical W.L. Gore & Associates (Uk) Ltd.
Priority to AU82240/98A priority Critical patent/AU8224098A/en
Publication of WO1998058796A1 publication Critical patent/WO1998058796A1/fr

Abstract

L'invention concerne une étoffe perméable à la vapeur d'eau utilisée pour des vêtements, des chaussures, des chapeaux, des gants, etc., et comprenant un stratifié formé d'une feuille de membrane (2) de polytétrafluoroéthylène (PTFE) expansée et d'une couche de PTFE poreux non expansé (4) disposée au-dessus. Le PTFE non expansé est de préférence un réseau fritté de particules de PTFE de type granules réunis par fusion et formés in situ sur la membrane de PTFE expansée.
PCT/GB1998/001867 1997-06-25 1998-06-25 Etoffe composite WO1998058796A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU82240/98A AU8224098A (en) 1997-06-25 1998-06-25 Composite fabric

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB9713300.3A GB9713300D0 (en) 1997-06-25 1997-06-25 Composite fabric
GB9713300.3 1997-06-25

Publications (1)

Publication Number Publication Date
WO1998058796A1 true WO1998058796A1 (fr) 1998-12-30

Family

ID=10814836

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB1998/001867 WO1998058796A1 (fr) 1997-06-25 1998-06-25 Etoffe composite

Country Status (3)

Country Link
AU (1) AU8224098A (fr)
GB (2) GB9713300D0 (fr)
WO (1) WO1998058796A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004060657A2 (fr) * 2003-01-02 2004-07-22 3M Innovative Properties Company Nappe acoustique
US6805963B2 (en) 2002-12-12 2004-10-19 Kimberly-Clark Worldwide, Inc. Elastomeric articles with improved damp slip
US6972148B2 (en) 2003-06-23 2005-12-06 Kimberly-Clark Worldwide, Inc. Glove having improved donning characteristics
WO2011140494A1 (fr) * 2010-05-06 2011-11-10 Gore Enterprise Holdings, Inc Tissu stratifié perméable à l'air résistant à la contamination et vêtements fabriqués à partir dudit tissu
WO2016115644A1 (fr) 2015-01-22 2016-07-28 Betty Bossi Ag Serpillière multifonctionnelle

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7624456B2 (en) 2004-11-24 2009-12-01 Gore Enterprise Holdings, Inc. Windproof waterproof breathable seamed articles
US8256030B2 (en) 2004-11-24 2012-09-04 W. L. Gore & Associates, Inc. Windproof waterproof breathable seamed articles
KR101589573B1 (ko) * 2014-07-07 2016-01-28 주식회사 시즈글로벌 투습과 방수 기능을 갖고 외피와 내피에 동시에 결합하기 위한 장갑용 중간피와 이를 이용한 장갑 및 이들의 제조방법

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3775170A (en) * 1965-02-18 1973-11-27 Chemplast Inc Plastic duplicate of cellulosic or proteinaceous material, article or object
US4194041A (en) * 1978-06-29 1980-03-18 W. L. Gore & Associates, Inc. Waterproof laminate
US5418054A (en) * 1993-03-16 1995-05-23 W. L. Gore & Associates, Inc. Flame-retardant, waterproof and breathable expanded PTFE laminate
WO1996040510A1 (fr) * 1995-06-07 1996-12-19 W.L. Gore & Associates (Uk) Ltd. Materiau composite poreux

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4983434A (en) * 1989-04-07 1991-01-08 W. L. Gore & Associates, Inc. Filter laminates

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3775170A (en) * 1965-02-18 1973-11-27 Chemplast Inc Plastic duplicate of cellulosic or proteinaceous material, article or object
US4194041A (en) * 1978-06-29 1980-03-18 W. L. Gore & Associates, Inc. Waterproof laminate
US5418054A (en) * 1993-03-16 1995-05-23 W. L. Gore & Associates, Inc. Flame-retardant, waterproof and breathable expanded PTFE laminate
WO1996040510A1 (fr) * 1995-06-07 1996-12-19 W.L. Gore & Associates (Uk) Ltd. Materiau composite poreux

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6805963B2 (en) 2002-12-12 2004-10-19 Kimberly-Clark Worldwide, Inc. Elastomeric articles with improved damp slip
WO2004060657A2 (fr) * 2003-01-02 2004-07-22 3M Innovative Properties Company Nappe acoustique
WO2004060657A3 (fr) * 2003-01-02 2004-09-02 3M Innovative Properties Co Nappe acoustique
US6972148B2 (en) 2003-06-23 2005-12-06 Kimberly-Clark Worldwide, Inc. Glove having improved donning characteristics
WO2011140494A1 (fr) * 2010-05-06 2011-11-10 Gore Enterprise Holdings, Inc Tissu stratifié perméable à l'air résistant à la contamination et vêtements fabriqués à partir dudit tissu
CN103037722A (zh) * 2010-05-06 2013-04-10 戈尔企业控股股份有限公司 耐污染的、可透过空气的织物叠层以及由其制得的服装
RU2527989C2 (ru) * 2010-05-06 2014-09-10 Гор Энтерпрайз Холдингс, Инк Устойчивый к загрязнению, воздухопроницаемый тканевый слоистый материал и одежда из него
JP2016104573A (ja) * 2010-05-06 2016-06-09 ダブリュ．エル．ゴア アンド アソシエイツ，インコーポレイティドＷ．Ｌ． Ｇｏｒｅ ＆ Ａｓｓｏｃｉａｔｅｓ， Ｉｎｃｏｒｐｏｒａｔｅｄ 耐汚染性通気性布帛ラミネート及びそれから作られる衣料品
US9944044B2 (en) 2010-05-06 2018-04-17 W. L. Gore & Associates, Inc. Contamination resistant air permeable fabric laminate and garments made therefrom
WO2016115644A1 (fr) 2015-01-22 2016-07-28 Betty Bossi Ag Serpillière multifonctionnelle

Also Published As

Publication number Publication date
GB9813688D0 (en) 1998-08-26
GB2326606A (en) 1998-12-30
GB9713300D0 (en) 1997-08-27
AU8224098A (en) 1999-01-04

Similar Documents

Publication Publication Date Title
US5981614A (en) Hydrophobic-oleophobic fluoropolymer compositions
CA2703607C (fr) Materiaux de protection thermique
TWI410550B (zh) 改性的全氟聚合物片材料以及製造它之方法
US6143675A (en) Porous composite
JP6437938B2 (ja) 耐汚染性通気性布帛ラミネート及びそれから作られる衣料品
CA2343242C (fr) Lamine imper-respirant et procede de fabrication dudit lamine
US4770927A (en) Reinforced fluoropolymer composite
JP4931938B2 (ja) 透湿性防水シート及びその製造方法
WO1997049552A1 (fr) Composites souples resistants a l'eau et a l'huile
JP2007512987A (ja) 新規ポリマーフィルム及びこのポリマーフィルムを含むテキスタイルラミネート
WO1998058796A1 (fr) Etoffe composite
EP0889928B1 (fr) Dispersions et articles fondus en polytetrafluoroethylene de type granuleux
EP0889930B1 (fr) Dispersions en polytetrafluoroethylene de type granulaire et articles fondus produits a partir de celles-ci
Jeong et al. The transport properties of polymer membrane-fabric composites
WO1999062993A1 (fr) Matiere poreuse a base de polytetrafluorethylene de type poudre fine
EP0125955B1 (fr) Matériau composite renforcé en polymère fluoré et méthode pour sa fabrication
AU2005292A (en) Soft stretchable composite fabric
WO1997036953A1 (fr) Dispersions de polytetrafluoroethylene modifie de type granulaire et articles fondus prepares a partir de celles-ci
WO1999003511A2 (fr) Event sterilisable
CN107825799A (zh) 基于复合膜层结构的防水透湿复合膜及其制备工艺
EP0856550A1 (fr) Textiles antistatiques
EP0634974B1 (fr) Stratifie de protection contre des agents chimiques
JP2024112915A (ja) フッ素樹脂膜、フッ素樹脂膜部材及び電子機器
JPH08183123A (ja) フッ素樹脂を融着保持した無機繊維織布又は不織布からなる表面疎水化積層体およびその製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM GW HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 1999504016

Format of ref document f/p: F

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA