WO1998004449A1 - Becquets arriere - Google Patents

Becquets arriere Download PDF

Info

Publication number
WO1998004449A1
WO1998004449A1 PCT/EP1997/004028 EP9704028W WO9804449A1 WO 1998004449 A1 WO1998004449 A1 WO 1998004449A1 EP 9704028 W EP9704028 W EP 9704028W WO 9804449 A1 WO9804449 A1 WO 9804449A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
component
graft
particle size
use according
Prior art date
Application number
PCT/EP1997/004028
Other languages
German (de)
English (en)
Inventor
Herbert Naarmann
Graham Edmund Mc Kee
Alfred Pirker
Hans-Josef Sterzel
Franz Brandstetter
Bernd-Steffen Von Bernstorff
Bernhard Rosenau
Ulrich Endemann
Burkhard Straube
Original Assignee
Basf Aktiengesellschaft
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Aktiengesellschaft filed Critical Basf Aktiengesellschaft
Priority to EP97936653A priority Critical patent/EP0912389A1/fr
Publication of WO1998004449A1 publication Critical patent/WO1998004449A1/fr

Abstract

L'invention concerne l'utilisation d'une matière moulable thermoplastique pour produire des bécquets arrière et les dispositifs de fixation requis. Cette matière, différente de l'ABS, contient, par rapport à la somme des quantités des composants A et B, et éventuellement C et/ou D, représentant 100 % en poids, a) comme composant A, 1 à 99 % en poids, de préférence 15 à 60 % en poids, notamment 25 à 50 % en poids d'un polymère obtenu par émulsion, se présentant sous forme de particules et ayant une température de transition vitreuse inférieure à 0 °C et une taille moyenne de particules comprise entre 50 et 1000 nm, de préférence entre 50 et 500 nm, b) comme composant B, 1 à 99 % en poids, de préférence 40 à 85 % en poids, notamment 50 à 75 % en poids d'au moins un polymère amorphe ou semi-cristallin, c) comme composant C, 0 à 50 % en poids de polycarbonates et d) comme composant D, 0 à 50 % en poids de charges sous forme de fibres ou de particules, ou de mélange de ces charges.
PCT/EP1997/004028 1996-07-25 1997-07-24 Becquets arriere WO1998004449A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP97936653A EP0912389A1 (fr) 1996-07-25 1997-07-24 Becquets arriere

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19630116.5 1996-07-25
DE19630116A DE19630116A1 (de) 1996-07-25 1996-07-25 Heckspoiler

Publications (1)

Publication Number Publication Date
WO1998004449A1 true WO1998004449A1 (fr) 1998-02-05

Family

ID=7800875

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1997/004028 WO1998004449A1 (fr) 1996-07-25 1997-07-24 Becquets arriere

Country Status (4)

Country Link
EP (1) EP0912389A1 (fr)
KR (1) KR20000029503A (fr)
DE (1) DE19630116A1 (fr)
WO (1) WO1998004449A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000020084A1 (fr) * 1998-10-07 2000-04-13 Basf Aktiengesellschaft Jouets d'exterieur

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0320836A2 (fr) * 1987-12-17 1989-06-21 BASF Aktiengesellschaft Matières à mouler exemptes d'halogènes et résistant au feu, procédé pour leur préparation et leur utilisation
EP0429957A2 (fr) * 1989-11-25 1991-06-05 BASF Aktiengesellschaft Masse à mouler thermoplastique ayant une résistance élevée aux chocs à froid
DE4342048A1 (de) * 1993-12-09 1995-06-14 Basf Ag Dreistufige Pfropfcopolymerisate und solche enthaltende thermoplastische Formmassen mit hoher Zähigkeit
EP0676449A2 (fr) * 1994-04-04 1995-10-11 Mitsubishi Gas Chemical Company, Inc. Composition de résine thermoplastique pour extrusion de profile
DE19536892A1 (de) * 1995-10-04 1997-04-10 Basf Ag Formteile aus thermoplastischen Formmassen

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0320836A2 (fr) * 1987-12-17 1989-06-21 BASF Aktiengesellschaft Matières à mouler exemptes d'halogènes et résistant au feu, procédé pour leur préparation et leur utilisation
EP0429957A2 (fr) * 1989-11-25 1991-06-05 BASF Aktiengesellschaft Masse à mouler thermoplastique ayant une résistance élevée aux chocs à froid
DE4342048A1 (de) * 1993-12-09 1995-06-14 Basf Ag Dreistufige Pfropfcopolymerisate und solche enthaltende thermoplastische Formmassen mit hoher Zähigkeit
EP0676449A2 (fr) * 1994-04-04 1995-10-11 Mitsubishi Gas Chemical Company, Inc. Composition de résine thermoplastique pour extrusion de profile
DE19536892A1 (de) * 1995-10-04 1997-04-10 Basf Ag Formteile aus thermoplastischen Formmassen

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000020084A1 (fr) * 1998-10-07 2000-04-13 Basf Aktiengesellschaft Jouets d'exterieur

Also Published As

Publication number Publication date
DE19630116A1 (de) 1998-01-29
EP0912389A1 (fr) 1999-05-06
KR20000029503A (ko) 2000-05-25

Similar Documents

Publication Publication Date Title
EP1123353B1 (fr) Corps moules pour le secteur du batiment, utilises a l'exterieur
WO1998004628A2 (fr) Elements d'amenagement interieur pour vehicules sur rails
EP0914374B1 (fr) Dispositif pour elever et nourrir de petits animaux
EP0912353A1 (fr) Enjoliveurs
EP0914373B1 (fr) Utilisation d'une matière moulable pour des abris pour outils de jardinage
EP0912389A1 (fr) Becquets arriere
WO2000020505A1 (fr) Corps moules pour le secteur du batiment, utilises a l'interieur
WO1998004625A1 (fr) Boitiers pour dispositifs de securite
WO1998004631A1 (fr) Pieces moulees pour equipements sanitaires et de salles de bains
EP0914383A1 (fr) Plaques a grille pour obturer des orifices de ventilation
WO1998004329A1 (fr) Voitures miniatures pour enfants
WO1998004629A1 (fr) Pieces moulees pour abris de jardin
WO1998004630A1 (fr) Boitiers pour appareils de traitement et de transmission de donnees
EP0914384A2 (fr) Panneaux prefabriques minces
WO1998004232A1 (fr) Appareils de massage et boitiers correspondants
DE19630103A1 (de) Wärmeisolierte Transportbehältnisse
WO2000020509A1 (fr) Article de sport realise a partir de melanges de polycarbonates
WO1998004624A1 (fr) Boitiers et elements d'habillage pour instruments medicaux
EP1123149A1 (fr) Jouets d'exterieur
WO2000020511A1 (fr) Matiere moulable thermoplastique pour la fabrication de demi-produits d'elements de carrosserie pour vehicules
EP1123352A1 (fr) Carters et elements de recouvrement pour filtres, pompes et moteurs
WO2000020503A1 (fr) Appareils de massage et boitiers correspondants

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CN JP KR US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 09230324

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 1019997000537

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 1997936653

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1997936653

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 1998508485

Format of ref document f/p: F

WWP Wipo information: published in national office

Ref document number: 1019997000537

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1997936653

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1019997000537

Country of ref document: KR