WO1997030118A1 - Solutions de resines dotees d'une stabilite accrue - Google Patents

Solutions de resines dotees d'une stabilite accrue Download PDF

Info

Publication number
WO1997030118A1
WO1997030118A1 PCT/US1997/002168 US9702168W WO9730118A1 WO 1997030118 A1 WO1997030118 A1 WO 1997030118A1 US 9702168 W US9702168 W US 9702168W WO 9730118 A1 WO9730118 A1 WO 9730118A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
resin solution
aminopolyamide
acrylamide
epichlorohydrin
Prior art date
Application number
PCT/US1997/002168
Other languages
English (en)
Inventor
Richard Underwood
Original Assignee
Callaway Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Callaway Corporation filed Critical Callaway Corporation
Priority to AU19565/97A priority Critical patent/AU1956597A/en
Publication of WO1997030118A1 publication Critical patent/WO1997030118A1/fr

Abstract

On améliore les résultats relatifs à la stabilité et à la durée de conservation d'une solution aqueuse de résine d'un copolymère glyoxylé de chlorure de diallyldiméthyle ammonium et d'acrylamide en incorporant à ladite solution une résine d'aminopolyamide et d'épichlorohydrine.
PCT/US1997/002168 1996-02-16 1997-02-11 Solutions de resines dotees d'une stabilite accrue WO1997030118A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU19565/97A AU1956597A (en) 1996-02-16 1997-02-11 Resin solutions having enhanced stability

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US60129796A 1996-02-16 1996-02-16
US08/601,297 1996-02-16

Publications (1)

Publication Number Publication Date
WO1997030118A1 true WO1997030118A1 (fr) 1997-08-21

Family

ID=24406981

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1997/002168 WO1997030118A1 (fr) 1996-02-16 1997-02-11 Solutions de resines dotees d'une stabilite accrue

Country Status (5)

Country Link
AR (1) AR005741A1 (fr)
AU (1) AU1956597A (fr)
ID (1) ID18934A (fr)
WO (1) WO1997030118A1 (fr)
ZA (1) ZA971186B (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5976196A (en) * 1998-06-15 1999-11-02 Callaway Corporation Process for preparing a dyed textile fabric wherein the dyed fabric is coated with a mixture of resins
WO2004061235A1 (fr) * 2002-12-20 2004-07-22 Kimberly-Clark Worldwide, Inc. Systeme de renforcement a deux constituants pour papier
US7034087B2 (en) * 2004-08-17 2006-04-25 Georgia-Pacific Resins, Inc. Aldehyde scavengers for preparing temporary wet strength resins with longer shelf life
US7488403B2 (en) 2004-08-17 2009-02-10 Cornel Hagiopol Blends of glyoxalated polyacrylamides and paper strengthening agents
US7897013B2 (en) 2004-08-17 2011-03-01 Georgia-Pacific Chemicals Llc Blends of glyoxalated polyacrylamides and paper strengthening agents

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3556932A (en) * 1965-07-12 1971-01-19 American Cyanamid Co Water-soluble,ionic,glyoxylated,vinylamide,wet-strength resin and paper made therewith
GB1561727A (en) * 1975-11-20 1980-02-27 Basf Ag Comprising water-soluble acrylamides polymers and water-soluble resinous amine condensation products
EP0278336A2 (fr) * 1987-02-11 1988-08-17 Wolff Walsrode Aktiengesellschaft Agents pour la fabrication de papier
EP0662542A1 (fr) * 1993-12-31 1995-07-12 Hercules Incorporated Composition pour fabriquer un papier résistant à l'état humide

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3556932A (en) * 1965-07-12 1971-01-19 American Cyanamid Co Water-soluble,ionic,glyoxylated,vinylamide,wet-strength resin and paper made therewith
GB1561727A (en) * 1975-11-20 1980-02-27 Basf Ag Comprising water-soluble acrylamides polymers and water-soluble resinous amine condensation products
EP0278336A2 (fr) * 1987-02-11 1988-08-17 Wolff Walsrode Aktiengesellschaft Agents pour la fabrication de papier
EP0662542A1 (fr) * 1993-12-31 1995-07-12 Hercules Incorporated Composition pour fabriquer un papier résistant à l'état humide

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5976196A (en) * 1998-06-15 1999-11-02 Callaway Corporation Process for preparing a dyed textile fabric wherein the dyed fabric is coated with a mixture of resins
WO2004061235A1 (fr) * 2002-12-20 2004-07-22 Kimberly-Clark Worldwide, Inc. Systeme de renforcement a deux constituants pour papier
KR101029658B1 (ko) * 2002-12-20 2011-04-15 킴벌리-클라크 월드와이드, 인크. 종이를 위한 2-성분 강화계
US7034087B2 (en) * 2004-08-17 2006-04-25 Georgia-Pacific Resins, Inc. Aldehyde scavengers for preparing temporary wet strength resins with longer shelf life
US7488403B2 (en) 2004-08-17 2009-02-10 Cornel Hagiopol Blends of glyoxalated polyacrylamides and paper strengthening agents
US7897013B2 (en) 2004-08-17 2011-03-01 Georgia-Pacific Chemicals Llc Blends of glyoxalated polyacrylamides and paper strengthening agents

Also Published As

Publication number Publication date
AU1956597A (en) 1997-09-02
AR005741A1 (es) 1999-07-14
ZA971186B (en) 1997-08-25
ID18934A (id) 1998-05-20

Similar Documents

Publication Publication Date Title
US5783041A (en) Method for imparting strength to paper
US5674362A (en) Method for imparting strength to paper
US3049469A (en) Application of coating or impregnating materials to fibrous material
US7863395B2 (en) Polyacrylamide-based strengthening agent
EP0960237B1 (fr) Procedes de fabrication de papier et compositions afferentes
CA1313672C (fr) Composes hydrosolubles contenant de l'azote
US3332901A (en) Cationic water-soluble polyamide-epichlorohydrin resins and method of preparing same
CA2048045C (fr) Procede d'obtention de resines ameliorees d'epichlorohydrine et de polyaminopolyamide
KR20050114697A (ko) 아민 말단의 폴리아미드로부터의 고 고형분 수지의 합성
US4263182A (en) Stable dispersions of fortified rosin
US3951921A (en) Cationic water soluble resinous reaction product of polyaminopolyamide-epichlorohydrin and nitrogen compound
CA1152693A (fr) Polymeres ameliorant la resistance a l'etat humide
CA2138891C (fr) Procede et composition servant a la fabrication de papier renforce a l'etat humide
US3941736A (en) Stable aqueous dispersions of hydrocarbon resins and water soluble polyaminopolyamide-epichlorohydrin resin as dispersing agent
US4065608A (en) Process for the preparation of cationic paper sizing agents
WO1997030118A1 (fr) Solutions de resines dotees d'une stabilite accrue
US4035229A (en) Paper strengthened with glyoxal modified poly(β-alanine) resins
US4082730A (en) Glyoxal modified poly (beta-alanine) strengthening resins for use in paper
US3966684A (en) Cationic water soluble polymeric reaction product of polyaminopolyureylene-epichlorohydrin and nitrogen compound
KR100989204B1 (ko) 비닐아민 단위 또는 에틸렌이민 단위를 함유하는 소수성개질 중합체, 그의 제조 방법, 및 그의 보유제로서의 용도
JPH028219A (ja) 窒素含有高分子化合物
US3535288A (en) Cationic polyamide-epichlorohydrin resins
CA2469024C (fr) Resines polyalkyldiallylamine-epihalohydrine utilisees comme additifs de resistance humide dans la fabrication du papier et processus de fabrication de ces resines
GB1575951A (en) Glyoxal poly(beta-alanine) strengthening resins for use in paper

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BB BG BR BY CA CH CN CZ DE DK EE ES FI GB GE HU IL IS JP KE KG KP KR KZ LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG UZ VN AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 97529446

Format of ref document f/p: F

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase