WO1995017463A1 - Polyethylene compatible sulphonic acids as silane crosslinking catalysts - Google Patents

Polyethylene compatible sulphonic acids as silane crosslinking catalysts Download PDF

Info

Publication number
WO1995017463A1
WO1995017463A1 PCT/SE1994/001028 SE9401028W WO9517463A1 WO 1995017463 A1 WO1995017463 A1 WO 1995017463A1 SE 9401028 W SE9401028 W SE 9401028W WO 9517463 A1 WO9517463 A1 WO 9517463A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer composition
silanol condensation
formula
set forth
catalyst
Prior art date
Application number
PCT/SE1994/001028
Other languages
French (fr)
Inventor
Ruth Dammert
Bill Gustafsson
Bernt-Åke SULTAN
Original Assignee
Borealis Holding A/S
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Borealis Holding A/S filed Critical Borealis Holding A/S
Priority to AU12853/95A priority Critical patent/AU683120B2/en
Priority to US08/666,427 priority patent/US6005055A/en
Priority to BR9408390A priority patent/BR9408390A/en
Priority to KR1019960703274A priority patent/KR100281749B1/en
Priority to JP51703895A priority patent/JP3148245B2/en
Priority to EP95919918A priority patent/EP0736065B1/en
Priority to CA002179506A priority patent/CA2179506C/en
Priority to DE69423002T priority patent/DE69423002T2/en
Publication of WO1995017463A1 publication Critical patent/WO1995017463A1/en

Abstract

A crosslinkable polymer composition contains a crosslinkable polymer with hydrolysable silane groups and at least one silanol condensation catalyst. The polymer composition is distinguished by the silanol condensation catalyst being a compound of the formula ArSO3H (I) or a precursor thereof, Ar being a substituted benzene or naphthalene ring, the substituent or substituents containing 4-20 carbon atoms, preferably 10-18 carbon atoms. The precursor may be an anhydride of the sulphonic acid of formula (I), or a sulphonic acid of formula (I) provided with a hydrolysable protective group, e.g. an acetyl group. Specific examples of compounds of formula (I) are dodecyl benzene sulphonic acid and tetrapropyl benzene sulphonic acid.

Description

POLYETHYLENE COMPATIBLE SULPHONIC ACIDS AS SILANE CROSSLINKING CATALYSTS
The present invention relates to a crosslinkable polymer composition containing a crosslinkable polymer with hydrolysable silane groups and at least one silanol condensation catalyst.
It is known to crosslink different polymers by means of additives. Crosslinking improves such properties of the polymer as its mechanical strength and heat resistance.
Polymers normally considered to be thermoplastics, and not crosslinkable, can also be crosslinked by introducing crosslinkable groups in the polymer. An example thereof is the crosslinking of polyolefins, such as polyethylene. A silane compound can be introduced as a crosslinkable group, e.g. by grafting the silane compound onto the pre¬ pared polyolefin, or by copolymerisation of the olefin and the silane compound. This technique is previously known, and further details may be obtained from US Patent Speci- fications 4,413,066; 4,297,310; 4,351,876; 4,397,981; 4,446,283; and 4,456,704, all of which are incorporated herein by reference.
The crosslinking of polymers with hydrolysable silane groups is carried out by so-called moisture curing. In a first step, the silane groups are hydrolysed under the influence of water, resulting in the splitting-off of alcohol and the formation of silanol groups. In a second step, the silanol groups are crosslinked by a condensation reaction splitting off water. In both steps, a so-called silanol condensation catalyst is used as catalyst.
Prior-art silanol condensation catalysts include car- boxylates of metals, such as tin, zinc, iron, lead and cobalt; organic bases; inorganic acids; and organic acids. Mention should here especially be made of dibutyl tin dilaurate (DBTDL), dibutyl tin diacetate, dioctyl tin dilaurate, stannous acetate, stannous caprylate, lead naphthenate, zinc caprylate, cobalt naphthenate, ethyl amines, dibutyl a ine, hexylamines, pyridine, inorganic acids, such as sulphuric acid and hydrochloric acid, as well as organic acids, such as toluene sulphonic acid, acetic acid, stearic acid and maleic acid. Especially the tin carboxylates are much used as catalysts.
EP 0 475 064 further teaches the crosslinking of silane-containing polymer compositions with hydrolysable groups by means of a zeolite that has been modified by being reacted with at least one carboxylic acid and/or sulphonic acid at a temperature of at least 150°C. Exam¬ ples of sulphonic acids are toluene sulphonic acid and alpha- and beta-naphthalene sulphonic acid. The crosslink is said to be of essentially non-hydrolytic type.
WO 91/09075 further discloses the use of a blocked acid, such as an acid anhydride, e.g. stearic acid anhy¬ dride or benzoic acid anhydride, as silanol condensation catalyst. Such catalysts counteract undesirable premature crosslinking, commonly referred to as scorching or precur- ing, of the polymer composition. GB 2,028,831 and EP 0,193,317 may be mentioned as examples of the prior art relating to the crosslinking of polymers containing hydrolysable silane groups by means of the above-mentioned silanol condensation cata¬ lysts. EP 0,207,627 also discloses the use of a special silanol condensation catalyst in the form of a tin-con¬ taining polymer.
Although the above silanol condensation catalysts, and in particular the tin carboxylates, are frequently used in the crosslinking of polymer compositions con- taining silanol groups, they are disadvantageous in some respects. Thus, efforts are being made to find silanol condensation catalysts reducing or obviating these disad¬ vantages. • , For instance, prior-art silanol condensation cata- lysts function satisfactorily only at elevated tempera¬ tures in the order of 80-100°C and give a poor performance at normal ambient temperatures and relative humidities, such as room temperature (about 20-25CC) and 50% RH. In many contexts, such as the production of cable insulations or water pipes, it is desirable that the silane-containing polymer composition can be crosslinked at room tempera- ture without the use of water baths or steam cabinets. The degree of crosslinking of the polymer composition is mea-, sured as the gel content after crosslinking at a certain temperature for a certain period of time. It is desirable that crosslinking at room temperature for four days should result in a gel content of at least about 65% and a cata¬ lyst loading of about 1 mmole/kg composition. This is not achieved by existing silanol condensation catalysts, and it would therefore be a considerable step forward to pro¬ vide a silanol condensation catalyst meeting this require- ment.
The present invention relates to a new kind of sila¬ nol condensation catalyst reducing or obviating the draw¬ backs of prior-art catalysts in the crosslinking of poly¬ mer compositions containing polymers with hydrolysable silane groups. More precisely, the inventive silanol con¬ densation catalyst consists of certain lipophilic alkyl benzene or naphthalene sulphonic acids, or precursors of such acids, which permit crosslinking of silane-containing polymer compositions at room temperature. The invention thus provides a crosslinkable poly¬ mer composition containing a crosslinkable polymer with hydrolysable silane groups and at least one silanol con¬ densation catalyst, said polymer composition being char¬ acterised in that the silanol condensation catalyst com- prises a compound of formula I
ArS03H (I) or a hydrolysable precursor thereof, Ar being a substitut¬ ed aryl group, and the total compound containing 14-28 carbon atoms. Preferably, the aryl group is an alkyl-sub- stituted benzene ring with the alkyl substituent contain¬ ing 8-20 carbon atoms. Further characteristics and advantages of the inven¬ tion appear from the appended claims and the following description.
The inventive silanol condensation catalyst is dis- tinguished by being a benzene or naphthalene sulphonic acid that is sufficiently lipophilic to be compatible with the polymer composition to be crosslinked, e.g. polyethy¬ lene containing hydrolysable silane groups. To achieve such lipophilicity, the hydrocarbon group of the alkyl- aryl sulphonic acid must have a certain size and must, e.g. in the case where the acid is a benzene sulphonic acid, have an alkyl substituent containing at least 8 car¬ bon atoms, as indicated in the foregoing. If the alkyl group does not have such a size that the lipophilicity requirement is met, the catalyst is not compatible with the polymer composition but will be released therefrom upon crosslinking in aqueous solution, thus impairing crosslinking efficiency.
In the inventive silanol condensation catalyst of formula I, Ar preferably is an alkyl-substituted aryl group containing a benzene or naphthalene ring, substi¬ tuted by an alkyl group, the size of which is 8-20 carbon atoms in the benzene case and 4-18 carbon atoms in the naphthalene case. Due to commercial availability, it is most preferred that the aryl group is a benzene ring, sub¬ stituted with an alkyl substituent containing 12 carbon atoms.
The currently most preferred compounds of formula I are dodecyl benzene sulphonic acid and tetrapropyl benzene sulphonic acid.
The inventive silanol condensation catalyst may also be a precursor of a compound of formula I, i.e. a compound that is converted by hydrolysis to a compound of formula I. Such a precursor is the acid anhydride of the sulphonic acid compound of formula I. Another instance is a sulpho¬ nic acid of formula I that has been provided with a hydro¬ lysable protective group, e.g. an acetyl group, which can be removed by hydrolysis to give, the sulphonic acid of formula I.
According to the invention, the amount of silanol condensation catalyst present in the crosslinkable polymer composition generally is in the order of about 0.0001-3% by weight, preferably about 0.001-2% by weight and most preferably about 0.005-1% by weight, as based on the amount of silanol-group containing polymers in the compo¬ sition. It will be appreciated that the effective amount of catalyst depends on the molecular weight of the cata¬ lyst. Thus, a smaller amount is required of a catalyst having a low molecular weight, than of a catalyst having a high molecular weight.
The inventive catalyst is preferably added to the crosslinkable polymer in the form of a master batch, i.e. mixed with a polymer, such as a homo- or copolymer of ethylene, e.g. PE-LD or EBA containing 3-30% by weight of butyl acrylate. The master batch contains a minor amount of the catalyst, generally about 0.02-5% by weight, pre- ferably about 0.05-2% by weight.
The inventive catalyst may be used in the crosslink¬ able polymer composition alone or combined with other silanol condensation catalysts, such as other catalysts of the formula I or conventional silanol condensation cata- lysts, e.g. carboxylic acid salts of the metals tin, zinc, iron, lead and cobalt; hydrolysis products of alkyl tin trichlorides; organic bases; inorganic acids; and organic acids.
The crosslinkable polymer composition according to the invention chiefly corresponds to prior art crosslink- able polymer compositions containing hydrolysable silane groups, but differs therefrom by containing the silanol condensation catalyst described above.
Thus, the invention generally concerns crosslinkable polymers containing hydrolysable silane groups, and more precisely it relates to olefin copolymers or graft poly¬ mers which contain hydrolysable silane groups and which are crosslinked under the influence of water and at least one silanol condensation catalyst. Specifically, the crosslinkable polymer is an ethylene homopolymer or copo¬ lymer containing crosslinkable silane groups introduced either by copolymerisation or graft polymerisation.
Preferably, the silane-containing polymer has been obtained by copolymerisation of an olefin, suitably ethy¬ lene, and an unsaturated silane compound represented by the formula 'RlSiR'nY3_n (II) wherein R. is an ethylenically unsaturated hydrocarbyl, hydrocar- byloxy or (meth)acryloxy hydrocarbyl group, R' is an aliphatic saturated hydrocarbyl group, Y which may be same or different, is a hydrolysable orga¬ nic group, and n is 0, 1 or 2.
If there is more than one Y group, these do not have to be identical. Special examples of the unsaturated silane compound are those wherein R. is vinyl, allyl, isopropenyl, bute- nyl, cyclohexenyl or gamma-(meth)acryloxy propyl; Y is methoxy, ethoxy, formyloxy, acetoxy, propionyloxy or an alkyl- or arylamino group; and R', if present, is a methyl, ethyl, propyl, decyl or phenyl group.
A preferred unsaturated silane compound is repre¬ sented by the formula
CH2=CHSi(0A)3 (III)
wherein A is a hydrocarbyl group having 1-8 carbon atoms, preferably 1-4 carbon atoms.
The most preferred compounds are vinyl tri ethoxy- silane, vinyl bismethoxyethoxysilane, vinyl triethoxy- silane, gamma-( eth)acryloxypropyltrimethoxysilane, gamma- (meth)acryloxypropyltriethoxysilane, and vinyl triacetoxy- silane. The copolymerisation of the olefin (ethylene) and the unsaturated silane compound may be carried out under any suitable conditions resulting in the copolymerisation of the two monomers. Moreover, the copolymerisation may be implemented in the presence of one or more other comonomers which can be copolymerised with the two monomers. Such comonomers include (a) vinyl carboxylate esters, such as vinyl ace¬ tate and vinyl pivalate, (b) alpha-olefins, such as pro- pene, 1-butene, 1-hexene, 1-octene and 4-methyl-l-pentene, (c) (meth)acrylates, such as methyl(meth)aerylate, ethyl- (meth)acrylate and butyl(meth)acrylate, (d) olefinically unsaturated carboxylic acids, such as (meth)acrylic acid, maleic acid and fumaric acid, (e) (meth)acrylic acid deri- vatives, such as (meth)acrylonitrile and (meth)acrylic amide, (f) vinyl ethers, such as vinyl methyl ether and vinyl phenyl ether, and (g) aromatic vinyl compounds, such as styrene and alpha-methyl styrene. Amongst these comono¬ mers, vinyl esters of monocarboxylic acids having 1-4 car- bon atoms, such as vinyl acetate, and (meth)acrylate of alcohols having 1-4 carbon atoms, such as methyl(meth)- acrylate, are preferred. Especially preferred comonomers are butyl acrylate, ethyl acrylate and methyl acrylate. Two or more such olefinically unsaturated compounds may be used in combination. The term ' (meth)acrylic acid' is intended to embrace both acrylic acid and methacrylic acid. The comonomer content of the copolymer may amount to 70% by weight of the copolymer, preferably about 0.5-35% by weight, most preferably about 1-30% by weight. If using a graft polymer, this may have been produced e.g. by any of the two methods described in US 3,646,155 and US 4,117,195, respectively.
The silane-containing polymer according to the inven¬ tion suitably contains 0.001-15% by weight of the silane compound, preferably 0.01-5% by weight, most preferably 0.1-3% by weight. As is usually the case for polymer compositions, the crosslinkable polymer may contain various additives, such as miscible thermoplastics, stabilisers, lubricants, fil¬ lers, colouring agents and foaming agents. As to the miscible thermoplastics added, mention may be made of miscible polyolefins, such as polyethylene of low density, medium density and high density, polypropy¬ lene, chlorinated polyethylene, as well as various copo- ly ers including ethylene and one or more other comono- mers, e.g. vinyl acetate, methyl acrylate, propene, butene, hexene and the like. One may use either a single polyolefin or a mixture of several polyolefins. The poly¬ olefin content of the composition may be up to 70% by weight, as based on the total amount of this polyolefin and the silane-containing polymer.
As to fillers, mention may be made of inorganic fil¬ lers, such as silicates, e.g. kaolin, talc, montmorillo- nite, zeolite, mica, silica, calcium silicate, asbestos, powdered glass, glass fibre, calcium carbonate, gypsum, magnesium carbonate, magnesium hydroxide, aluminium hydroxide, carbon black and titanium oxide. The content of the inorganic filler may be up to 60% by weight, as based on the sum of the weights of the filler and the silane- containing polymer. Finally, it should be observed that the crosslinkable polymer used in the invention is previously known and that the novel and distinctive feature of the invention thus does not reside in this polymer, but in the special sila¬ nol condensation catalyst added to the polymer to form the inventive polymer composition.
The following nonrestrictive Examples are incorpo¬ rated herein to further illustrate the invention.
Example 1 A silanol condensation catalyst was added to a cross¬ linkable polymer with hydrolysable silane groups. The polymer was a copolymer of ethylene and vinyl tri ethoxy- silane. The amount of vinyl trimethoxysilane was 2% by weight. A crosslinkable composition was prepared by add¬ ing to the polymer a silanol condensation catalyst accord¬ ing to the invention. The catalyst was added in the form of a master batch of low-density polyethylene containing 8 mmole catalyst/kg master batch. The master batch was added in such quantities that the amount of catalyst in the total composition in each case became that given in Table 1 below. The composition was then crosslinked. The degree of crosslinking at different points of time was measured by decalin extraction according to the UNI 459 method, which is in accordance with ASTM D 2765, except that, after decalin extraction for 6 h, extraction is continued for 1 h in pure, boiling decalin. The results are given in Table 1 below, in which the values given are mean values of two determinations.
TABLE 1
Crosslinking temperature 23°C; 50% relative humidity Amount, Crosslinking time
Catalyst mmole/kg 2 days 4 days 7 days 10 days 15 days
Dodecy1-benzene 0.4 70 sulphonic acid (=Ufacid K) 0.8 27 69 77 77
Tetrapropyl- 0.4 72 benzene sul¬ 0.8 45 70 77 75 78 phonic acid 1.6 52 78 79 (=Ufacid TPB) 2.3 64 80 80
Acetyl p-dodecyl- 0.8 74 76 79 79 benzene sulpho- nate
Example 2
For comparative purposes, tests were performed under essentially the same conditions as in Example 1, using
'various compounds of conventional type or otherwise lying outside the invention as catalysts. The results are given in Table 2 below, in terms of gel content in % by weight: TABLE 2
Crosslinking temperature 23°C; 50% relative humidity Amount Crosslinking time
Catalyst mmole/kg 2 days 4 days 7 days 10 days 15 days
DBTDL 0.79 55 46 59
1.58 65 62 72
2.34 68 65 72
Sn(II)octoate 0.79 10 13 19
1.58 60 53 60
2.34 60 63 59 p-toluene sul- 0.8 66 68 74 phonic acid 4.5 73 72 78
1-naphthalene 0.8 68 74 75 77 sulphonic acid
2-naphthalene 0.8 70 74 77 76 sulphonic acid
Acetyl methane 0.8 52 60 64 66 sulphonate
Acetyl p-toluene 0.8 73 75 79 78 sulphonate
As is evident from Tables 1 and 2, the inventive catalysts provide more rapid crosslinking at room temperature than do the conventional catalysts DBTDL and Sn(II)octoate at corresponding contents. The likewise conventional toluene and naphthalene sulphonic acids, although providing rapid crosslinking, have the disadvantage of discolouring the polymer considerably. Neither can these acids be used for crosslinking in water baths, since they are then rapidly dissolved into the aqueous phase, which diminishes their catalytic activity. The same disadvantages arise also with the acetyl methane and toluene sulphonates tested.
Example 3
The test according to Example 1 was repeated, using tetrapropyl benzene sulphonic acid (TPBSA) as catalyst. Crosslinking was performed at 40°C in the presence of water and with different contents of the catalyst. For comparati purposes, corresponding tests were carried out using dibut tin dilaurate (DBTDL) and tin(II)octoate as catalysts. The results appear from Table 3 below.
TABLE 3
Amount of Crosslinking degree (%) catalyst at 40°C after
Catalyst (mmole/kg) 5 h 16 h 24 h 48 h 96 h
DBTDL 99 0.79 8 39 50 59 61
Sn(II)octoate 0.79 44 60 63 61 68
TPBSA 0.79 38 67 78 75
1.58 53 71 76 77
2.34 62 76 77 77
As is evident from Table 3, the inventive catalyst provides more rapid crosslinking at 40°C than do the con¬ ventional catalysts at corresponding contents.
Example 4
The test according to Example 3 was repeated, except that crosslinking was carried out at 60°C. The results appear from Table 4 below.
TABLE 4
Amount of Crosslinking degree (%) catalyst at 60°C after
Catalyst (mmole/kg) 2 h 5 h 7 h 17 h 20 h
DBTDL 99 0.79 51 56 64
1.58 62 63 87
2.34 65 70 86
Sn(II)octoate 0.79 63 65 72
1.58 74 75 78
2.34 80 76 79
TPBSA 0.79 56 75 76 78
1.58 64 77 79 79
2.34 73 78 78 79 As is evident from Table 5, the inventive catalyst generally provides more rapid crosslinking at 60°C than do the conventional catalysts at corresponding contents.
Example 5
The test according to Example 3 was repeated, except that crosslinking was carried out at 80°C. The results appear from Table 5 below.
TABLE 5
Amount of Crosslinking degree (%) catalyst at 80°C after
Catalyst (mmole/kg) l h 2 h 4 h 7 h 20 h
DBTDL 0.79 53 57 67 75 1.58 63 66 88 79 2.34 68 76 89 79
Sn(II)octoate 0.79 61 68 71 74 1.58 73 78 77 78 2.34 79 79 80 80
TPBSA 0.79, 73 75 77 79 1.58 76 79 79 80 2.34 78 79 79 80
As is evident from Table 5, the inventive catalyst generally provides more rapid crosslinking at 80°C than do the conventional catalysts at corresponding contents, and especially at low contents.
Example 6
The test according to Example 3 was repeated, except that crosslinking was carried out at 90°C, and that three catalysts according to the invention, as well as several catalysts falling outside the invention, were tested. The results appear from Table 6 below. TABLE 6
Crosslinking degree in % by weight Amount after
Catalyst mmole/kg 0.25h lh 1.5h 2h 5h 20h lOO p-dodecyl benzene sulphonic acid 0.8 64 75 79 81 81
Tetrapropyl ben¬ 0.8 57 76 75 77 78 81 83 zene sulphonic acid 1.6 61 79 80 2.3 70 80 80
Acetyl p-dodecyl 0.8 73 78 78 81 82 benzene sulphonate
DBTDL 0.8 23 53 75 79 79 1.6 62 76 80 2.3 77 80 82
Sn(II)octoate 0.8 57 67 70 71 75 1.6 78 79 77 2.3 78 80 81
1-naphthalene sul- 0.8 38 49 43 57 66 phonic acid
2-naphthalene sul- 0.8 35 40 54 62 69 phonic acid
Acetyl methane 0.8 12 22 sulphonate
Acetyl p-toluene 0.8 38 48 51 54 63 sulphonate
As is evident from Table 6, the inventive catalysts pro¬ vide more rapid crosslinking in water at 90°C than do the conventional catalysts DBTDL and Sn(II)octoate at corre¬ sponding contents. It is also apparent that the non-com¬ patible naphthalene sulphonic acids as well as the acetyl derivatives of the very water-soluble methane and toluene sulphonic acids, which all work fairly well at 23°C and 50% relative humidity, at 90°C in water are dissolved out of the plastic compounds and thus become comparatively much less active as catalysts. Example 7
A number of crosslinking tests were carried out involving inventive silanol condensation catalysts, as well as reference catalysts falling outside the scope of the invention. The tests were performed in accordance with Example 1, and the catalyst content was 0.8 mmole/kg poly¬ mer composition, unless otherwise stated. The tests were performed at the temperatures and for the times indicated in Table 8. Of the tested catalyst compounds 1-13 in Table 8, 1-3 are inventive catalysts and 4-13 are refe¬ rence catalysts. The inventive compound 3 (acetyl p-dode¬ cyl benzene sulphonate) is a precursor compound which, after hydrolysis, gives p-dodecyl benzene sulphonic acid. From the results given in Table 7, it is evident that the inventive catalysts give faster crosslinking than conven¬ tional catalysts 4 and 5, especially at room temperature, but also at elevated temperatures. Some of the other compounds, such as compounds 6 and 7, apparently give good results at room temperature, but discolour the polymer considerably, especially at higher temperatures. Neither can they be used for crosslinking in water baths, since they are then dissolved from the polymer, something which also applies to the hydrolysis products of compound 9 and especially compounds 8 and 10. Further, after hydrolysis, compound 9 of course gives the same discolouration as com¬ pound 7. Compounds 11 and 12 give good results at 23°C, but are extracted from the polymer at temperatures higher than 60°C. It may also be observed that compound 13, i.e. the sodium salt of compound 1 according to the invention, does not act as a silanol condensation catalyst. TABLE 7
Crosslinking degree (%)
90°C 80°C 60°C 23°C, 50% R.H.
Compound 1.5h 4h 17h 5 days
1. Dodecyl benzene 75 78 79 73 sulphonic acid 75 (8 days)
2. Tetrapropyl benzene 75 77 78 72 sulphonic acid 76 (8 days)
10 3. Acetyl-p-dodecyl benzene sulphonate 78 77 76 77
4. DBTL 53 57 58 55 (4 days)
5. Sn(II)octanoate 64 57 65 36 (4 days)
6. Sulphuric acid 39 35 48 71
15 7. p-toluene sulphonic acid 66 (4 days)
(0.8 and 4.5 mmole/kg, respectively) 27 73 (4 days)
8. Acetyl methane sul¬ phonate 5 5 35 62
20 9. Acetyl p-toluene sulphonate 48 53 65 78
10. Octadecanoyl methane sulphonate 22 23 39 53
11. 1-naphthalene sulpho¬
25 nic acid 49 49 65 73
12. 2-naphthalene sulphonic acid 40 53 67 75
13. Dodecyl benzene sul- phonic sodium salt 1.7 0 2.3 0 in
1 compounded on twin-screw extruder
35

Claims

1. A crosslinkable polymer composition containing a crosslinkable polymer with hydrolysable silane groups and at least one silanol condensation catalyst, c h a r a c ¬ t e r i s e d in that the silanol condensation catalyst comprises a compound of formula I
ArS03H (I)
or a precursor thereof, Ar being a hydrocarbyl-substituted benzene or naphthalene ring, the hydrocarbyl radical or radicals containing 8-20 carbon atoms in the benzene case and 4-18 carbon atoms in the naphthalene case.
2. A polymer composition as set forth in claim 1, c h a r a c t e r i s e d in that the hydrocarbyl radical is an alkyl substituent having 10-18 carbon atoms.
3. A polymer composition as set forth in claim 2, c h a r a c t e r i s e d in that the alkyl substituent contains 12 carbon atoms and is selected from dodecyl and tetrapropyl.
4. A polymer composition as set forth in any one of the preceding claims, c h a r a c t e r i s e d in that the silanol condensation catalyst is a precursor of the compound of formula I.
5. A polymer composition as set forth in claim 4, c h a r a c t e r i s e d in that the precursor is an anhydride of the sulphonic acid of formula I.
6. A polymer composition as set forth in claim 4, c h a r a c t e r i s e d in that the precursor is a sul¬ phonic acid of formula I provided with a hydrolysable pro¬ tective group.
7. A polymer composition as set forth in claim 6, c h a r a c t e r i s e d in that the hydrolysable pro¬ tective group is acetyl.
8. A polymer composition as set forth in claim 7, c h a r a c t e r i s e d in that the precursor is acetyl p-dodecyl benzene sulphonate.
9. A polymer composition as set forth in any one of the preceding claims, c h a r a c t e r i s e d in that it contains 0.0001-3% by weight of silanol condensation catalyst.
10. A polymer composition as set forth in any one of the preceding claims, c h a r a c t e r i s e d in that it further contains another silanol condensation catalyst.
PCT/SE1994/001028 1993-12-20 1994-11-03 Polyethylene compatible sulphonic acids as silane crosslinking catalysts WO1995017463A1 (en)