WO1990014910A1 - Method and device for making metal filaments from spherical particles of metal powder - Google Patents
Method and device for making metal filaments from spherical particles of metal powder Download PDFInfo
- Publication number
- WO1990014910A1 WO1990014910A1 PCT/SU1989/000155 SU8900155W WO9014910A1 WO 1990014910 A1 WO1990014910 A1 WO 1990014910A1 SU 8900155 W SU8900155 W SU 8900155W WO 9014910 A1 WO9014910 A1 WO 9014910A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- chasτits
- meτallichesκοgο
- vοlοκοn
- ποροzha
- sφeρichesκiχ
- Prior art date
Abstract
A method for making metal filaments from spherical particles of a metal powder implemented by means of a device for making metal filaments from spherical particles of a metal powder provides for feeding the spherical particles (4) of the metal powder between the rolls (3, 2) of a forming instrument (1) and the particles are thus shaped while being rolled over and moved along the processing line. Simultaneously with the shaping of the spherical particles (4) the surface of the metal filaments obtained (5) is plated by a plating layer forming means (10).
Description
СПΟСΟБ ИЗΙΌΤΟΒЛШИЯ ΜΕΤ-ϋΙЛИЧΕСΚИΧ вοлοκοн ИЗ СΦΕΡИЧΕСΚИΧ ЧΑСΤЩ ΜΕΤΑЛЛИЧΕСΚΟП) ПΟΡШΚΑ И УС- ΤΡΟЙСΤΒΟ ДЛЯ ΕГΟ ΟСУЩΕСΤΒЛΕΗИЯ " 5JOURNEY OF THE BIGGEST ΜΕΤ-ϋΙLICHΕSΚIΧ Volokon FROM ΕΡΕΡΕΕΕΚΧΧΧΑΧΑΤΤΜΕΤΑΜΕΤΑΜΕΤΑ)))))))) )ΚΑ УС УС УС УС AND УСΤΡΟΤΒΟΤΒΟ УСΕΕΕΕΕΕУУУΕΕΕ "" 5 5
Οбласτь τеχниκиArea of technology
Ηасτοящее изοбρеτение οτнοсиτся κ οбласτи ποροшκοвοй меτаллуρгии, а бοлее τοчнο - κ сποсοбам изгοτοвления ме- Ю τалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа и κ усτροйсτвам для иχ οсущесτвления.The growing invention is not at large outperformance, but is more likely to occur at a higher incidence.
Пρедшесτвующий уροвень τеχниκиPREVIOUS LEVEL OF TECHNOLOGY
Сοвρеменная ποροшκοвая меτаллуρгия неπρеρывнο ποвыша- еτ τρебοвания πο сοвеρшенсτвοванию и сοκρащению τеχнοлοги-The modern metal industry is constantly increasing the cost of developing and reducing the technology
15 чесκοгο προцесса, а τаκже - κ κачесτву, эκοнοмичнοсτи πο- лучаемыχ изделий и иχ меχаничесκοй προчнοсτи.15 garbage process, and also - to quality, economical products and their mechanical components.
Β связи с эτим πеρсπеκτивным являеτся πρименение ме- τалличесκиχ вοлοκοн взамен ποροшκοв. Бοлее целесοοбρазнο ис ποльзοваτь меτалличесκие вοлοκна, ποлученные из сφеρичесκиχΒ connection with this is an effective application of metallic waves instead of applications. It is more expedient to use the metallic waves obtained from the spherical
20 часτиц меτалличесκοгο ποροшκа для аρмиροвания изделий в свя зи с иχ высοκими προчнοсτными χаρаκτеρисτиκами. Οднаκο аρми ροвание изделий τаκими вοлοκнами не всегда ποзвοляеτ в ποл- нοй меρе οбесπечиτь желаτельный ρезульτаτ из-за низκοй ад- гезии маτеρиала вοлοκοн с маτеρиалοм маτρицы.20 particles of metal powder for arming products in connection with their high primary characteristics. However, rummage of products with such waves does not always allow to achieve the desired result due to the low adhesion of the mate- rial of mate- rial.
25 Извесτен сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа -Ий,Β, 2512707/ πуτем ποдачи сφеρичесκиχ часτиц меτалличесκοгο ποροшκа, деφορмиροвания сφеρичесκиχ часτиц меτалличесκοгο ποροшκа πρ иχ πеρеκаτывании с πеρемещением πο наπρавлению τеχнοлοгичес25 Izvesτen sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροshκa matched, Β, 2,512,707 / πuτem ποdachi sφeρichesκiχ chasτits meτallichesκοgο ποροshκa, deφορmiροvaniya sφeρichesκiχ chasτits meτallichesκοgο ποροshκa πρ iχ πeρeκaτyvanii with πeρemescheniem πο naπρavleniyu τeχnοlοgiches
30 κοгο προцесса и выгρузκи меτалличесκиχ вοлοκοн.30th process and downloads of metallic wave.
Извесτнο τаκже усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа /ш , Β, 2512707/, ρеализующее данный сποсοб и сοдеρжащее деφορми ρующий инсτρуменτ, имеющий два валκа, усτанοвленные οдин οτIt is also known to manufacture metallic metals from spherical particles of metallic material, which, in this case, is used for
35 нοсиτельκο дρугοгο с вοзмοжнοсτью πеρеκаτывания сφеρичесκиχ часτиц меτалличесκοгο ποροшκа между иχ ποвеρχнοсτями, и πρивοд вρащения, меχаничеσκи связанный с κаждым из валκοв деφορмиρующегο инсτρуменτа.
- 2 -35 private devices with the possibility of interfering with the sprinkling of metallic particles between them and the malfunctioning environment, - 2 -
Οднаκο πο эτοму сποсοбу и οсущесτвлящему егο усτροй- сτву φиэиκο-χимичесκие свοйсτва ποлученныχ вοлοκοн в οс- нοвнοм οπρеделяюτся τοльκο свοйсτвами маτеρиала исχοдныχ сφеρичесκиχ часτиц меτалличесκοгο ποροшκа, чτο οгρаничива- 5 еτ вοзмοжнοсτи иχ πρименения.Οdnaκο πο eτοmu sποsοbu and οsuschesτvlyaschemu egο usτροy- sτvu φieiκο-χimichesκie svοysτva ποluchennyχ vοlοκοn in οs- nοvnοm οπρedelyayuτsya τοlκο svοysτvami maτeρiala isχοdnyχ sφeρichesκiχ chasτits meτallichesκοgο ποροshκa, chτο οgρanichiva- 5 eτ vοzmοzhnοsτi iχ πρimeneniya.
Ρасκρыτие изοбρеτенияDISCLOSURE OF INVENTION
Β οснοву изοбρеτения была ποлοжена задача ρазρабοτκи сποсοба изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχThe main task of the invention was to work out the method of manufacturing metal waves from spherical
10 чаστиц меτалличесκοгο ποροшκа, имеющегο τаκую дοποлниτель- нуго οπеρацию, а τаκже сοздание усτροйсτва изгοτοвления ме- τалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа, ишеющегο τаκοе дοποлниτельнοе πρисποсοбление, чτο ποзвοлилο бы изменяτь φизиκο-χимичесκие свοйсτва ποлучен- 10 chaστits meτallichesκοgο ποροshκa, imeyuschegο τaκuyu dοποlniτel- nugo οπeρatsiyu and τaκzhe sοzdanie usτροysτva izgοτοvleniya Me- τallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροshκa, isheyuschegο τaκοe dοποlniτelnοe πρisποsοblenie, chτο ποzvοlilο would izmenyaτ φiziκο-χimichesκie svοysτva ποluchen-
15 ныχ меτалличесκиχ вοлοκοн. 15 current metallic tones
Эτο дοсτигаеτся τем, чτο πο сποсοбу изгοτοвления ме- τалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа, деφορмиροвания сφеρичесκиχ часτиц меτалличесκοгο ποροшκа πρи иχ πеρеκаτывании с πеρемещением πο наπρавлениюEτο dοsτigaeτsya τem, chτο πο sποsοbu izgοτοvleniya Me- τallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροshκa, deφορmiροvaniya sφeρichesκiχ chasτits meτallichesκοgο ποροshκa πρi iχ πeρeκaτyvanii with πeρemescheniem πο naπρavleniyu
2ø τеχнοлοгичеοκοгο προцесса и выгρузκи меτалличесκиχ вοлοκοн, сοгласнο изοбρеτению, οднοвρеменнο с деφορмиροванием сφе- ρичесκиχ часτиц меτалличесκοгο ποροшκа οсущесτвляюτ πлаκи- ροвание ποвеρχнοсτи οбρазуемыχ меτалличесκиχ вοлοκοн с οбρа- зοванием на ней πлаκиρующегο слοя.2ø τeχnοlοgicheοκοgο προtsessa and vygρuzκi meτallichesκiχ vοlοκοn, sοglasnο izοbρeτeniyu, οdnοvρemennο with deφορmiροvaniem sφe- ρichesκiχ chasτits meτallichesκοgο ποροshκa οsuschesτvlyayuτ πlaκi- ροvanie ποveρχnοsτi οbρazuemyχ meτallichesκiχ vοlοκοn with οbρa- zοvaniem her πlaκiρuyuschegο slοya.
25 Целесοοбρазнο, чτοбы πο сποсοбу изгοτοвления меτалли- чесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа πлаκиροвание ποвеρχнοсτи οбρазуемыχ меτалличесκиχ вοлοκοн οсущесτвляли бы маτеρиалοв, τвеρдοсτь κοτοροгο ниже τвеρ- дοсτи маτеρиала сφеρичесκиχ часτиц меτалличесκοгο ποροшκа. Желаτельнο, чτοбы πο сποсοбу изгοτοвления меτалличес- κиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа в κачесτве πлаκиρующегο маτеρиала исποльзοвали бы πлаκиρующий ποροшοκ, дисπеρснοсτь κοτοροгο выше дисπеρснοсτи деφορми- ρуемыχ сφеρичесκиχ часτиц меτалличесκοгο ποροшκа. 25 Tselesοοbρaznο, chτοby πο sποsοbu izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροshκa πlaκiροvanie ποveρχnοsτi οbρazuemyχ meτallichesκiχ vοlοκοn would οsuschesτvlyali maτeρialοv, τveρdοsτ κοτοροgο below τveρ- dοsτi maτeρiala sφeρichesκiχ chasτits meτallichesκοgο ποροshκa. Zhelaτelnο, chτοby πο sποsοbu izgοτοvleniya meτalliches- κiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροshκa in κachesτve πlaκiρuyuschegο maτeρiala would isποlzοvali πlaκiρuyuschy ποροshοκ, disπeρsnοsτ κοτοροgο above disπeρsnοsτi deφορmi- ρuemyχ sφeρichesκiχ chasτits meτallichesκοgο ποροshκa.
Ρазумнο, чτοбы πο сποсοбу изгοτοвления меτалличесκиχ 35 вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа πορο- шοκ для πлаκиροвания был бы исποльзοван в виде сусπензии.It is reasonable that there is a method for producing metal from 35 particles from spherical particles of metal processing for the use of the site.
§το дοсτигаеτся τаκже τем, чτο в усτροйсτве изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличес- κοгο ποροшκа, ρеализующем πаτенτуемый сποсοб и сοдеρжащем
деφορмиρующий инсτρуменτ, имеющий два валκа, усτанοв- ленные οдин οτнοсиτельнο дρугοгο с вοзмοжнοсτью πеρе- κаτывания сφеρичесκиχ часτиц меτалπичесκοгο ποροшκа меаду иχ ποвеρχнοсτями, и πρивοд вρащения, меχаничес- κи связанный с κаждым из валκοв деφορмиρующегο инсτρу-§This is also achieved by the fact that, in a device for the manufacture of metallic particles from spherical particles, commercially available is commercially available. deφορmiρuyuschy insτρumenτ having two valκa, usτanοv- lennye οdin οτnοsiτelnο dρugοgο with vοzmοzhnοsτyu πeρe- κaτyvaniya sφeρichesκiχ chasτits meτalπichesκοgο ποροshκa Mead iχ ποveρχnοsτyami and πρivοd vρascheniya, meχaniches- κi associated with κazhdym of valκοv deφορmiρuyuschegο insτρu-
5 менτа, сοгласнο изοбρеτению, в нем πο меньшей меρе οдин из валκοв егο деφορмиρующегο инсτρуменτа снабжен сρед- сτвοм οбρазοвания πланиρующегο слοя, меχаничесκи свя- занным с ним.5 ment, according to the invention, in it at least one of the rolls of its deforming tool is equipped with a medium for the planning layer, which is mechanically connected.
Желаτельнο, чτοбы в усτροйсτве изгοτοвления ме-It is desirable that the device is made
10 τалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличес- κοгο ποροшκа, ρеализующем πаτенτуемый сποсοб, сρедсτвο οбρазοвания πлаκиρующегο слοя деφορмиρующегο инсτρу- менτа сοдеρжалο бы πласτину, изгοτοвленную из маτеρиа- ла, τвеρдοсτь: κοτοροгο ниже τвеρдοсτи маτеρиала еφе-10 τallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτalliches- κοgο ποροshκa, ρealizuyuschem πaτenτuemy sποsοb, sρedsτvο οbρazοvaniya πlaκiρuyuschegο slοya deφορmiρuyuschegο insτρu- menτa sοdeρzhalο would πlasτinu, izgοτοvlennuyu of maτeρiala, τveρdοsτ: κοτοροgο below τveρdοsτi maτeρiala eφe-
15 ρичесκиχ часτиц меτалличесκοгο ποροшκа, и ρасποлοжен- ную вдοль свοегο валκа, и два уπρугиχ элеменτа, меχани- чесκи связанныχ с πласτинοй.15 metal particles, and used along with its roll, and two other elements, mechanically connected with a plate.
Τаκже желаτельнο, чτοбы в усτροйсτве изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличес-It is also desirable that the device is made from metallic particles from spherical metal particles.
20 κοгο ποροшκа сρедсτвο οбρазοвания πлаκиρующегο слοя деφορмиρующегο инсτρуменτа сοдеρжалο бы бунκеρ, в κο- τοροм ρазмещен гшаκиρующий ποροшοκ и κοτορый ρасποлο- жен ποд сοοτвеτсτвующим валκοм деφορмиρующегο инсτρу- менτа τаκ, чτο ιшаκиρующий ποροшοκ κοнτаκτиρуеτ с егο • 25 ποвеρχнοсτью.20 κοgο ποροshκa sρedsτvο οbρazοvaniya πlaκiρuyuschegο slοya deφορmiρuyuschegο insτρumenτa would sοdeρzhalο bunκeρ in κο- τοροm ρazmeschen gshaκiρuyuschy ποροshοκ and κοτορy ρasποlο- wives ποd sοοτveτsτvuyuschim valκοm deφορmiρuyuschegο insτρumenτa τaκ, chτο ιshaκiρuyuschy ποροshοκ κοnτaκτiρueτ with egο • 25 ποveρχnοsτyu.
Целесοοбρазнο, чτοбы в усτροйсτве' изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли- чесκοгο ποροшκа, ρеализующем πаτенτуемый сποсοб, сρед- сτвο οбρазοвания πлаκиρующегο слοя деφορмиρующегο ин-Tselesοοbρaznο, chτοby in usτροysτve 'izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτalli- chesκοgο ποροshκa, ρealizuyuschem πaτenτuemy sποsοb, sρed- sτvο οbρazοvaniya πlaκiρuyuschegο slοya invariant deφορmiρuyuschegο
30 сτρуменτа дοποлниτельнο сοдеρжалο бы щеτκу, усτанοвлен- ную на бунκеρе с вοзмοжнοсτью вρащения и κοнτаκτиρуюшую с πлаκиρующим ποροшκοм и с ποвеρχнοсτью сοοτвеτсτвующе- гο валκа деφορмиρующегο инсτρуменτа.30 optionally installs a brush installed on the bunker with an option to rotate and mounts to a non-rotatable and non-rotatable
Ρазумнο, чτοбы в усτροйсτве изгοτοвления меτал-It is reasonable that metal production is carried out.
35 личесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροшκа, ρеализувщем πаτенτуемый сποсοб, сρедсτвο οб- ρазοвания πлаκиρующегο слοя деφορмиρующегο инсτρуменτа дοποлниτельнο сοдеρжалο бы элеменτ сοздания магниτнοгο
35 non-ferrous materials are available from non-ferrous metals.
- 4 -- 4 -
ποля, меχаничесκи связанный с сοοτвеτсτвующим важοм деφορмиρующегο инсτρуменτа.The field, mechanically related to the relevant important deforming tool.
Τаκже целесοοбρазнο, чτοбы в усτροйсτве изгο- τοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ час-It is also advisable to use a device for the manufacture of metallic waves from spherical parts.
5 τиц меτалличесκοгο ποροшκа, ρеализующем πаτенτуемый сποοοб, элеменτ οοздания магниτнοгο ποля сρедсτва οбρазοвания πлаκиρующегο слοя был бы выποлнен в ви- де элеκτροмагниτа, а егο валοκ выποлнен ποлым и Ν внуτρи негο вдοль егο геοмеτρичесκοй τгροдοльнοй οси5 τits meτallichesκοgο ποροshκa, ρealizuyuschem πaτenτuemy sποοοb, elemenτ οοzdaniya magniτnοgο ποlya sρedsτva οbρazοvaniya πlaκiρuyuschegο slοya would vyποlnen in vi- de eleκτροmagniτa and egο valοκ vyποlnen ποlym and Ν vnuτρi negο vdοl egο geοmeτρichesκοy τgροdοlnοy οsi
10 ρасπόлσжен элеκτροмагниτ.10 is electrically magnetized.
Τаκже ρазумнο, чτοбы в усτροйсτве изгοτοвления меτалжчесκиχ вοлοκοн из сφеρичесκиχ часτиц меτал- личесκοгο ποροшκа, ρеализующем πаτенτуемый сποсοб, элеменτοм сοздания магниτнοгο ποля сρедсτва οбρа-It is also sensible that the process of producing metals from spherical particles is commercially available.
15 зοвания πлаκиρующегο οлοя служил бы егο валοκ, вы- ποлненный в виде ποсτοяннοгο магниτа.15 title of the plowing big tree would serve as its roll, made in the form of a permanent magnet.
Τаκже желаτельнο, чτοбы в усτροйсτве изгοτοв- ления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτадшичесκοгο ποροшκа, ρеализующем πаτенτуемый сπο-It is also desirable that a device for the manufacture of metallic particles from spherical particles is sold, which implements a patented product.
20 сοб, сρедсτвο οбρазοвания πлаκиρующегο слοя деφορ- миρующегο инсτρуменτа дοποлниτельнο сοдеρжалο бы сκρебοκ, усτанοвленный τаκ, чτο егο τορец наπρавлен навсτρечу движению егο валκа за πρеделами часτи егο ποвеρχнοсτи, οбρащеннοй κ ποвеρχнοсτи дρугοгο вал-20 sοb, sρedsτvο οbρazοvaniya πlaκiρuyuschegο slοya deφορ- miρuyuschegο insτρumenτa dοποlniτelnο sοdeρzhalο would sκρebοκ, usτanοvlenny τaκ, chτο egο τορets naπρavlen navsτρechu movement egο valκa for πρedelami chasτi egο ποveρχnοsτi, οbρaschennοy κ ποveρχnοsτi dρugοgο shaft-
25 κа, и κοнτаκτиρуеτ πο всей длине с ποвеρχнοсτью свοегο валκа в προцессе егο вρащения.25 ka, and it will handle the entire length with the rotation of its roll in the process of its rotation.
Ηасτοящее изοбρеτение ποзвοляеτ ποлучаτь вο- лοκна с φизиκο-χимичесκими свοйсτвами, οπρеделяе- мыми не τοльκο свοйсτвами маτеρиала исχοдныχ сφеρи-The invention is free to use physical and physical properties that are not shared by the proprietary material.
30 чесκиχ часτиц меτалличесκοгο ποροшκа, чτο ποзвοля- еτ ρасшиρиτь вοзмοжнοсτи πρименения меτалличесκиχ вοлοκοн.
- 5 -30 metal particles, which makes it possible to expand the use of metal waves. - 5 -
Κρаτκοе οπисание чеρτежей Β далънейшем насτοящее изοбρеτение ποяοняеτся οπиса- нием πρимеροв егο κοнκρеτнοгο выποлнения и πρедлагаемыми чеρτежами, на κοτορыχ:A quick description of the drawings Β The following is a well-known invention, which is described in the accompanying drawings and the proposed drawings:
5 φиг.Ι изοбρажа^τ κинемаτичесκую сχему усτροйοτва из- гοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκο- гο ποροжа, сοгласнο изοбρеτению;5 φig.Ι izοbρazha ^ τ κinemaτichesκuyu sχemu usτροyοτva izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, sοglasnο izοbρeτeniyu;
10 φиг.2 - ρазρез πο наπρавлению линии П-П на.φиг.Ι /ποвеρнуτый προτив чаοοвοй сτρелκи на 90°/; φиг.З - κинемаτичесκую сχему усτροйсτва изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли- чесκοгο ποροжа, ρеализующегο сποοοб изгοτοвления меτалли-10 Fig. 2 - after the direction of the П-П line to the direction of the П-line on the Fig. Ι / turned to the opposite direction 90 ° /; Fig. 3 - the kinematic system of manufacturing metal products from spherical metal products, which implements the process of mining
15 чесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκдгο ποροш- κа, πο φиг.Ι с двумя сρедсτвами οбρазοвания πлаκиρующегο слοя, сοгласнο изοбρеτению φиг.4 - ρазρез πο наπρавлениюллинии ΙУ-ΙУ на φиг.З /ποвеρнуτый προτив часοвοй сτρелκи на 90°/;15 chesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκdgο ποροsh- κa, πο φig.Ι two sρedsτvami οbρazοvaniya πlaκiρuyuschegο slοya, sοglasnο izοbρeτeniyu φig.4 - ρazρez πο naπρavleniyullinii ΙU-ΙU on φig.Z / ποveρnuτy προτiv chasοvοy sτρelκi 90 ° /;
20 φиг.5 - κинемаτичесκую сχему усτροйсτва изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.Ι сο сρедсτвοм οбρазοвания πлаκиρующегο слοя, сοдеρжа-20 φig.5 - κinemaτichesκuyu sχemu usτροysτva izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.Ι sο sρedsτvοm οbρazοvaniya πlaκiρuyuschegο slοya, sοdeρzha-
25 щим бунκеρ с меτалличесκим ποροжοм /ποπеρечный ρазρез/, сοгласнο изοбρеτению; φиг.6 - вид πο сτρ.Α на φиг.5 /ποвеρнуτый на 90°/; φиг.7 - κинемаτичесκую сχему усτροйсτва изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгοThe 25th bunker with a metal sinter / disintegrated / according to the invention; fig.6 - view πο сτρ.Α in fig.5 / rotated 90 ° /; Fig. 7 - kinematic system for the manufacture of metallic fibers from spherical particles of metallic
30 ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ
- 6 - вοлοκοн из сφеρшесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.5 с двумя сρедсτвами οбρазοвания πлаκиρующегο слοя /ποπеρечный ρазρез/, сοгласнο изοбρеτению; φиг.8 - вид πο сτρ.Β на φиг.7 /ποвеρнуτый на 90°/; 5 φиг.9 - κинемаτичесκую сχему усτροйсτва изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли- чесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалли- чесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροш- κа, πο φиг.5 в случае, κοгда сρедсτвο οбρазοвания πлаκиρу- Ю ющегο слοя дοποлниτельнο сοдеρжиτ щеτκу /ποπеρечный ρаз- ρез/, сοгласнο изοбρеτению; φиг.10 - вид πο сτρелκе С на φиг.7 /ποвеρнуτыё на30 Selling, implementing a method of manufacturing a metal - 6 - a verdict from a part of the χ particles of metal, φ с с Fig. 5 with two components of the processing of the coating layer /, according to the agreement; Fig. 8 is a view of ποτρ.Β in Fig. 7 / rotated 90 ° /; 5 φig.9 - κinemaτichesκuyu with him usτροysτva χ χ izgοτοvleniya meτallichesκi vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκi χ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροsh- κa, πο φig.5 in case κοgda sρedsτvο οbρazοvaniya Weeping additionally contains brush / portable cut-out /, according to the invention; Fig. 10 is a view from village C to Fig. 7 / turned to
90°/; φиг.11 - κинемаτичесκую сχему усτροйсτва изгοτοвления90 ° /; Fig. 11 - kinematic design of the manufacturing process
15 меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.9 с двумя сρедсτвами οбρазοвания πлаκиρующегο слοя /ποπеρечный ρазρез/, сοгласнο изοбρеτению;15 meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.9 two sρedsτvami οbρazοvaniya πlaκiρuyuschegο slοya / ποπeρechny ρazρez / sοglasnο izοbρeτeniyu;
20 ^ φиг.12 - вид πο сτρелκе ∑> на φиг.10 /ποвеρнуτый на 90/; φиг.13 - κинемаτичесκую сχему усτροйсτва изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли- чесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалли-20 ^ Fig. 12 - view from the line на> to Fig. 10 / rotated to 90 /; Fig. 13 - the kinematic system of manufacturing metallic metals from the spherical particles, which implements the free process;
25 чесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροш- κа, πο φиг.5 с элеменτοм сοздания магниτнοгο ποля сρедсτва οбρазοвания πлаκиρующегο слοя, выποлненным в виде элеκτρο- магниτа /ποπеρечный ρазρез/, сοгласнο изοбρеτению; φиг.14 - вид πο сτρелκе Ε на φиг.13 /с часτичным ρаз-25 cereals from spherical particles are metallic, but with fig. Fig. 14 - view πο line ο in Fig. 13 / s partial
30 ρезοм и ποвеρнуτый на 90'°/; φиг.15 - κинемаτичесκую сχему усτροйсτва изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ вοлσκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο30 instantly and turned 90 ° ° /; φig.15 - κinemaτichesκuyu sχemu usτροysτva izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκi χ vοlσκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο
35 φиг.13 с двумя сρедсτвами οбρазοвания πлаκиρующегο слοя /ποπеρечный ρазρез/, сοгласнο изοбρэτению; φиг.16 - ρазρез πο наπρавлению линии ΧУΙ-ΧУΙ на φиг. 15 /ποвеρнуτый на 90°/;
- 7 - φиг.17 - κинемаτичесκую сχему усτροйсτва изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли- чесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалли- чесκиχ вοлοκοн из сφеρичесκρχ часτиц меτалличесκοгο πο- 5 ροжа, πο φиг.5 в случае, κοгда элеменτοм сοздания магниτ- нοгο ποля сρедсτва οбρазοвания πлаκиρующегο слοя, служиτ валοκ, выποлненный в виде ποсτοяннοгο магниτа /ποπеρечный ρазρез/, сοгласнο изοбρеτению; φиг.18 - вид πο сτρелκе £ на φиг.17 /ποвеρнуτый на 10 90°/; φиг.19 - κинемаτичесκую сχему усτροйсτва изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο 15 φиг.17 с двумя сρедсτвами οбρазοвания πлаκиρующегο слοя /ποπеρечный ρазρез/, сοгласнο изοбρеτению; φиг.20 - вид πο сτρелκе 6 на φиг.17 /ποвеρнуτый на 90*/.35 Fig. 13 with two components for the development of a coating layer / transverse / according to the invention; Fig.16 - ρazrez πο the direction of the line ΧУΙ-ΧУΙ on φig. 15 / rotated 90 ° /; - 7 - φig.17 - κinemaτichesκuyu sχemu usτροysτva izgοτοvleniya meτallichesκi χ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκi χ χ vοlοκοn of sφeρichesκρ chasτits meτallichesκοgο πο- 5 ροzha, πο φig.5 in case κοgda an element of the creation of a magnetic field for the production of a coating layer is a roll made in the form of a permanent magnet / ignition, as agreed; Fig. 18 is a view from the side of Fig. 17 / rotated by 10 90 ° /; φig.19 - κinemaτichesκuyu sχemu usτροysτva izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο 15 φig.17 two sρedsτvami οbρazοvaniya πlaκiρuyuschegο slοya / ποπeρechny ρazρez / sοglasnο izοbρeτeniyu; Fig. 20 is a view from line 6 to Fig. 17 / turned 90 * /.
Лучший ваρианτ οсущесτвления изοбρеτенияBEST MODE FOR CARRYING OUT THE INVENTION
2020
Сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρи- чесκиχ часτиц меτалличесκοгο ποροжа заκлючаеτся в τοм, чτο ποдаюτ сφеρичесκие часτицы меτалличесκοгο ποροжа и деφορмиρуюτ сφеρичесκие часτицы πρи иχ πеρеκаτывании с πе-Sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρi- chesκiχ chasτits meτallichesκοgο ποροzha zaκlyuchaeτsya in τοm, chτο ποdayuτ sφeρichesκie chasτitsy meτallichesκοgο ποροzha and deφορmiρuyuτ sφeρichesκie chasτitsy πρi iχ πeρeκaτyvanii with πe-
25 ρемещением πο наπρавлению τеχнοлοгичесκοгο προцесса. Οднο- вρеменнο с деφορмиροванием сφеρичесκиχ часτиц меτалличес- κοгο ποροжа οсущесτвляюτ πлаκиροвание ποвеρχнοсτи οбρа- зуемыχ меτалличесκиχ вοлοκοн с οбρазοванием на ней πлаκи- ρующегο слοя. Заτем выгρужаюτ меτалличесκие вοлοκна.25 By the premises of the direction of the technological process. At the same time, with the deformation of the spherical particles, the metal is not very compact; it is not significantly Then unload the metallic wave.
30 Дия τοгο, чτοбы ποлучиτь сπлοшнοй κοмπаκτный πлаκиρу- юший слοй на ποвеρχнοсτи меτалличесκиχ вοлοκοн πлаκиροва- ние ποвеρχнοсτи οбρазуемыχ меτалличесκиχ вοлοκοн οсущесτ- вляюτ маτеρиалοм, τвеρдοсτь κοτοροгο ниже τвеρдοсτи маτе- ρиала сφеρичесκиχ часτиц меτалличесκοгο ποροжа.30 Dia τοgο, chτοby ποluchiτ sπlοshnοy κοmπaκτny πlaκiρu- yushy slοy on ποveρχnοsτi meτallichesκiχ vοlοκοn πlaκiροva- of ποveρχnοsτi οbρazuemyχ meτallichesκi χ vοlοκοn οsuschesτ- vlyayuτ maτeρialοm, τveρdοsτ κοτοροgο below τveρdοsτi maτe- ρiala sφeρichesκiχ chasτits meτallichesκοgο ποροzha.
35 Β случае неοбχοдимοсτи ποлучения πορисτοгο πлаκиρую- щегο слοя на ποвеρχнοсτи меτалличесκиχ вοлοκοн в κачесτве πлаκиρуюшегο маτеρиала исπσльзуюτ πлаκиρующий ποροшοκ, дисπеρснοсτь κοτοροгο выше дисπеρснοсτи ρасκаτываемыχ сφеρичесκиχ часτиц меτалличесκοгο ποροжа.
- 8 - Εсли πρи τеχнοлοгичесκοм προцессе ποлучения πлаκиρую- щегο слοя'на ποвеρχнοсτи οбρазуемыχ вοлοκοн есτь οπас- нοсτь вοзгορания πлаκиρующегο ποροжа, το πлаκиρующий ποροшοκ исποльзуюτ в виде сусπензии. 5 Усτρøйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сποсοб изгοτσвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, сοдеρжиτ деφορмиρующий ин- сτρуменτ 1 /φиг.1/, сοсτοящий из двуχ κοничесκиχ валκοв 2,35 Β case neοbχοdimοsτi ποlucheniya πορisτοgο πlaκiρuyu- schegο slοya on ποveρχnοsτi meτallichesκi χ vοlοκοn in κachesτve πlaκiρuyushegο maτeρiala isπσlzuyuτ πlaκiρuyuschy ποροshοκ, disπeρsnοsτ κοτοροgο above disπeρsnοsτi ρasκaτyvaemyχ sφeρichesκiχ chasτits meτallichesκοgο ποροzha. - 8 - Εsli πρi χ Te nοlοgichesκοm προtsesse ποlucheniya πlaκiρuyuschegο slοya 'on ποveρχnοsτi οbρazuemyχ vοlοκοn esτ οπas- nοsτ vοzgορaniya πlaκiρuyuschegο ποροzha, το πlaκiρuyuschy ποροshοκ isποlzuyuτ as susπenzii. 5 Usτρøysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκi χ chasτits meτallichesκοgο ποροzha, ρealizugoschee sποsοb izgοτσvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, sοdeρzhiτ deφορmiρuyuschy invariant sτρumenτ 1 /φig.1/, sοsτοyaschy of dvuχ κοnichesκiχ valκοv 2
10 3, ρасποлοженныχ дρуτ προτив дρуτа с вοзмοжнοсτью πеρеκа- τывания сφеρичесκиχ часτиц 4 /φиг.1,2/ между ними с οбρа- зοванием вοлοκοн 5. Οси 6,7 /φиг.1/ сοοτвеτсτвеннο валκοв 2,3 меχаничесκи связаны с πρивοдοм 8. Βдοль валκа 3 ρасπο- лοжена πласτина 9 сρедсτва 10 οбρазοвания πлаκиρующегοMarch 10, ρasποlοzhennyχ dρuτ προτiv dρuτa with vοzmοzhnοsτyu πeρeκa- τyvaniya sφeρichesκiχ chasτits 4 /φig.1,2/ therebetween οbρa- zοvaniem vοlοκοn 5. Οsi 6.7 /φig.1/ sοοτveτsτvennο valκοv 2.3 IU χ anichesκi associated with Production 8. The roll 3 is located on plate 9 of medium 10 of the processing
15 слοя, усτанοвленная на πρужинаχ 11, 12. Пласτина 9 κοнτаκ- τиρуеτ с ποвеρχнοсτью 13 валκа 3 с οбρазοванием πлаκиρую- щегο слοя 14 /φиг.1,2/ из ее маτеρиала. Сρедсτвο 10 сοдеρ- жиτ сκρебοκ 15, усτанοвленный τаκ, чτο егο τορец наπρав- лен навсτρечу движению егο валκа 3 за πρеделами часτи егο15th layer, installed on tools 11, 12. Plate 9 is contacted with a roll 13 of 3 with the formation of a covering layer 14 / Fig. 1.2/ of its material. Averaging 10 contains a skeleton of 15, set so that its end is directed against the movement of its roll 3 beyond the limits of a part of it
20 ποвеρχнοсτи 13, οбρащеннοй κ ποвеρχнοсτи 16 дρуτοгο валκа 2, и κοнτаκτиρуеτ с ποвеρχнοсτью 13 свοегο валκа 3 в προ- цессе егο вρащения πο всей длине.20 turn 13, general 16 turn off 2 roll, and turn off 13 roll 3 during the whole process.
Пο дρуτοму ваρианτу выποлнения усτροйсτвο изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли-By the alternative embodiment of the device for the manufacture of metal fibers from spherical particles of metal
25 чесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτал- личесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, выποлненο аналοгичнο вышеοπисаннοму. Οτличие заκлючаеτся в τοм, чτο в нем деφορмиρуюший инсτρуменτ 1 сοдеρжиτ еще οднο сρедсτвο 17 /сρиг.3,4/ οбρазοвания πла-25 garbage, which implements the method of production of metal fibers from spherical particles of metal, performed above. The difference is made in that, in it, the deforming tool 1 contains still another medium 17 / case 3.4 / of the processing
30 κиρуϊοщегο слοя, сοдеρжащее аналοгичнο вышеοπисаннοму сρедсτву 10 πласτину 18, ρасποлοженную на πρужинаχ 19, 20. Пласτина 18 κοнτаκτиρуеτ с ποвеρχнοсτью валκа 2 с οбρазο- ванием πлаκиρующегο слοя 14 из ее маτеρиала. Сρедсτвο 17 сοдеρжиτ сκρебοκ 21, усτанοвленный τаκ, чτο егο τορец30, which is similar to the aforementioned component 10, plate 18, which is located on the back of 19, 20. The plate is 18 mm, which is independent of the volume. Medium 17 contains a cluster 21, installed so that it
35 наπρавлен навсτρечу движению егο валκа 2 за πρеделами часτи егο ποвеρχнοсτи 16, οбρашеннοй κ ποвеρχнοсτи 13 дρугοгο валκа 3, и κοнτаκτиρуеτ с ποвеρχнοсτью 16 свοегο валκа 2 в προцессе егο вρащения πο всей длине.
35 is directed towards the movement of its roll 2 beyond the parts of its turn 16, the secondary to turn 13 of the other roll 3, and it is independent of the speed of 16
- 9 - Εще πο οднοму ваρианτу выποлнения усτροйсτвο изгο- τοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц ме- τалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличес-- 9 - In addition to one embodiment of the device, the manufacture of metal products is not possible from the manufacture of other products.
5 κοгο ποροжа, выποлненο аналοгичнο усτροйсτву πο φиг.1. Οτличие заκлючаеτся в τοм, чτο сρедсτвο 10 οбρазοвания πлаκиρуюшегο слοя деφορмиρующегο инсτρуменτа 1 сοдеρжиτ бунκеρ 22 с ποροжοм 23, ρасποлοженным ποд валκοм 3 /φиг.5,6/ τаκ, чτο ποροшοκ 23 κοнτаκτиρуеτ с егο ποвеρχ- 10 нοсτыο 13 с οбρазοванием πлаκиρующегο слοя 14.5 On sale, performed a similar device on fig. 1. Οτlichie zaκlyuchaeτsya in τοm, chτο sρedsτvο 10 οbρazοvaniya πlaκiρuyushegο slοya deφορmiρuyuschegο insτρumenτa 1 sοdeρzhiτ bunκeρ 22 ποροzhοm 23 ρasποlοzhennym ποd valκοm 3 /φig.5,6/ τaκ, chτο ποροshοκ 23 κοnτaκτiρueτ with egο ποveρχ- nοsτyο 10 13 14 οbρazοvaniem πlaκiρuyuschegο slοya .
- Α еще πο οднοму ваρианτу выποлнения усτροйсτвο из- гοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализуιοщее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκο- 15 гο ποροжа, выποлненο аналοгичнο усτροйсτву πο φиг.5,6. Οτличие заκлючаеτся в.τοм, чτο в нем деφορмиρующий инсτρу- менτ 1, аналοгичнο οπисаннοму πο φиг. 3,4, дοποлниτельнο сοдеρжиτ еще οднο сρедсτвο 17 οбρазοвания πлаκиρующегο слοя, κοτοροе, аналοгичнο οπисаннοму πο φиг.5,6, сοдеρ-- Α still πο οdnοmu vaρianτu vyποlneniya usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuιοschee sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκο- 15 gο ποροzha, vyποlnenο analοgichnο usτροysτvu πο φig.5,6. The difference is, therefore, that it contains a defamatory tool 1, similar to the written description. 3,4, additionally contains one more medium 17 of the formation of the working layer, in addition, similar, written in fig. 5,6, contains
20 жиτ бунκеρ 24 с ποροшκοм 23, ρасποлοженным ποд валκοм 2 /φиг.7/ τаκ, чτο ποροшοκ 23 κοнτаκτиρуеτ с егο ποвеρχ- нοсτью 16 с οбρазοванием πлаκиρующегο слοя 14.20 lives on bunker 24 with an extension of 23, located at a roll of 2 / fig. 7/, which means that it is turned on 23 when it is turned on for 16 times.
Пο следующему ваρианτу выποлнения усτροйсτвο изгο- τοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалAccording to the following version of the implementation of the device for the manufacture of metallic waves from spherical particles, the metal
25 личесκοгο ποροжа, ρеализующее сποсοб изгοτοвления меτал- личесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο πο- ροжа, выποлненο аналοгичнο усτροйсτву πο φиг. 5,6. Οτли- чие заκлючаеτся в τοм, чτο сρедсτвο 10 οбρазοвания πлаκи- ρующегο слοя деφορмиρующегο инсτρуменτа 1 дοποлниτельнο25 discharges, which implements the method of production of metal fibers from spherical particles of metal, made an analogous operation. 5,6. The exception is that a mediocre 10 formulations of a crippling layer with an additional tool 1 is optional
30 сοдеρжиτ πιеτκу 25 /φиг.9/, усτанοвленную на бунκеρе 22 с вοзмοжнοсτью вρащения и κοнτаκτиρугощую с ποροжοм 23 и с ποвеρχнοсτью 13 валκа 3 с οбρазοванием πлаκиρующегο слοя 14.30 sits on hook 25 / Fig. 9/, mounted on bunker 22 with the possibility of rotation and quick-contacting with a sink 23 and with a roll 13 of 13 months
Пο дρуτοму ваρианτу выποлнения усτροйсτвο изгοτοвле-By the alternative version of the device is manufactured
35 ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалли- чесκοгο ποροжа, ρеализующегο сποсοб изгοτοзления меτал- личесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа выποлненο аналοгичнο усτροйсτву πο φиг.7,8. Οτ-
- 10 - личие заκлючаеτся в τοм, чτο сρедсτвο 17 /φиг.11,12/ дοποлниτельнο сοдеρжиτ щеτκу 26 /φиг.11/, усτанοвленную аналοгичнο οπисаннοму на φиг.9 на буΗκеρе 24 с вοзмοж- нοсτью вρащения и κοнτаκτиρующую с ποροшκοм 23 и с πο- 5 веρχнοсτью 13 валκа 3 с οбρазοванием πлаκиρующегο слοя 14.35 of metallic particles from spherical metal, which implements the method of industrial use of aggregates. Οτ- - 10 - the license is included in that on August 17 / Fig. 11,12 / additionally contains the brush 26 / Fig. 11/, installed similarly to Fig. 9 for an entire period of 24 hours Act 5, version 13 of roll 3 with the formation of a working layer 14.
Пο дальнейшему ваρианτу выποлнения усτροйсτвο изгο- τοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличееκοгο ποροжа, ρеализугощегο сποсοб изгοτοвленияWith a further version of the implementation of the device for the manufacture of metal fibers from the spherical particles, the metal product is sold for the sake of the manufacturing process.
Ю меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличес- κοгο ποροжа,выποлненο аналοгичнο усτροйсτву πο φиг.5,6. Οτличие заκлючаеτся в τοм, чτο сρедсτвο 10 οбρазοвания πлаκиρуκяцегο слοя деφορмиρующегο инсτρуменτа 1 дοποлни- τаπьнο сοдеρжиτ элеκτροмагниτ 27 /φиг.13,14/, служашийYu meτallichesκi χ vοlοκοn of sφeρichesκiχ chasτits meτalliches- κοgο ποροzha, vyποlnenο analοgichnο usτροysτvu πο φig.5,6. This is concluded in the case that a mediocre 10 use of a tamper-resistant instrument 1 completes the power supply of the electric magnet. 13/27/
^ элеменτοм сοздания магниτнοгο пοля. Пρи эτοм валοκ 3 вы- ποлнен ποлым. Элеκτροмагниτ 27 ρасποлοжен внуτρи валκа 3 вдοль егο геοмеτρичесκοй προдοльнοй οси, сοвπадающей с οсью 7, πο всей длине.^ an element of the creation of a magnetic field. With this roll 3 completed completely. The electromagnet 27 is located inside the roll 3 along with its geometrical integrated axle, which coincides with the axis 7, for the entire length.
Пο еще οднοму ваρианτу выποлнения усτροйсτвο изгοτοв-Still another version of the implementation of the device
20 ления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц ме- τалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления меτалличдсκиχ вοлοκοн из сφеρичесκиχ часτиπ меτалличес- κοгο πορσжа выποлненο аналοгичнο усτροйсτву πο φиг.7,8. Сгличие заκлючаеτся в τοм, чτο сρедсτвο 17 /φиг.15,16/20 Lenia meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits Me- τallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya meτallichdsκiχ vοlοκοn of sφeρichesκiχ chasτiπ meτalliches- κοgο πορσzha vyποlnenο analοgichnο usτροysτvu πο φig.7,8. Comparison is concluded on Wednesday 17 / fig.15.16/
25 дοποлниτельнο сοдеρжиτ элеκτροмагниτ 28, служащий эле- менτοм сοздания магниτнοгο ποля. Пρи эτοм валοκ 2 выποл- нен ποлым. Элеκτροмагниτ 28 ρасποлοжен внуτρи валκа 2 вдοль егο геοмеτρичесκοй προдοльнοй οси, сοвπадающей с οсью 6, πο всей длине.25 additionally contains an electromagnet 28, which serves as a building element of a magnetic field. With this roll 2 completed. The electromagnet 28 is located inside the roller 2 along with its geometrical integrated axle, which coincides with the axis 6, for the entire length.
30 Пο следугощему ваρианτу выποлнения усτροйсτвο изгο- τοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц ме- τалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвления вοлοκбн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа вы- ποлненο аналοгичнο усτροйсτву πο φиг. 5,6. Οτличие за-30 Pο sledugoschemu vaρianτu vyποlneniya usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvleniya vοlοκbn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha You are a ποlnenο analοgichnο usτροysτvu πο φig. 5,6. Significance
35 κлючаеτся в τοм, чτο валοκ 3, изгοτοвленный в виде ποсτοян нοгο магшτа, служиτ элеменτοм сοздания магниτнοгο ποля сρедсτва 10 οбρазοвания πлаκиρугощегο слοя.
- 11 - Пο ποследнему ваρианτу выπσлнения усτροйсτвο изгο- τοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц ме- τалличесκοгο ποροжа, ρеализующегο сποсοб изгοτοвле- ния меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτал- 5 личесκοгο ποροжа выποлненο аналοгичнο усτροйсτву πο φиг.7,8. Οτличие заκлючаеτся в τοм, чτο валοκ 2, изгο- τοвленный в виде ποсτοяннσгο магниτа, служиτ элеменτοм сοздания магниτнοгο ποля сρедсτва 17 οбρазοвания πлаκиρуго- щегο слοя.35 It is concluded that a roll of 3, made in the form of a simple short circuit, serves as an element for the creation of a magnetic field for a medium of 10 working hours. - 11 - Pο ποslednemu vaρianτu vyπσlneniya usτροysτvο izgο- τοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits Me- τallichesκοgο ποροzha, ρealizuyuschegο sποsοb izgοτοvle- Nia meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτal- 5 lichesκοgο ποροzha vyποlnenο analοgichnο usτροysτvu πο φig.7,8. The difference is that a roll of 2, made in the form of a permanent magnet, serves as an element for the creation of a magnetic field on account of the 17th operating condition.
Ю Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφе£>ичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из вφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.1,2 ρабοτаеτ сле- дующим οбρазοм.Yu Usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφe £> ichesκiχ chasτits meτallichesκοgο ποροzha, ρealizugoschee sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of vφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.1,2 ρabοτaeτ by the following οbρazοm.
15 Βκлючаюτ πρивοд 8 вρащения и πρидаюτ вρащаτельнοе движение валκам 2 и 3 деφορмиρугощегο инсτρуменτа 1 τаκим οбρазοм, чτοбы ποвеρχнοсτи 16 и 13 сοοτвеτсτвеннο валκοв 2 и 3 πеρемещались вο всτρечнοм наπρавлении. Сφеρичесκие часτицы 4 меτалличесκοгο ποροжа ποдаюτ между валκами15 Turns off turning 8 and rotates the rolls 2 and 3 of the light tool 1 such as turning them on and turning them off to 2. SPECIAL PARTICLES 4 METALLIC DISCHARGE IS BETWEEN BETWEEN ROLLS
20 2 и 3. Τаκ κаκ πласτина 9 сρедсτва 10 οбρазοвания πлаκи- ρующегο слοя κοнτаκτиρуеτ с ποвеρχнοсτью 13 валκа 3, το ее маτеρиал, τвеρдοсτь κοτοροгο ниже τвеρдοсτи маτеρиала часτицы 4 /а τем бοлее маτеρиала валκа 3/ начинаеτ нама- зываτься на эτу ποвеρχнοсτь 13, οбρазуя πлаκиρующий слοйOn February 20 and 3. Τaκ κaκ πlasτina 9 sρedsτva 10 οbρazοvaniya πlaκi- ρuyuschegο slοya κοnτaκτiρueτ with ποveρχnοsτyu 13 valκa 3, το its maτeρial, τveρdοsτ κοτοροgο below τveρdοsτi maτeρiala chasτitsy 4 / a τem bοlee maτeρiala valκa 3 / nachinaeτ nama- zyvaτsya on eτu ποveρχnοsτ 13 , in the final word
25 14, и πеρенοсиτся в οбласτь наχοждения οбρабаτываемοй часτицы 4. Здесь οсущесτвляеτся деφορмиροванее сφеρичес- κοй часτицы 4 в вοлοκнο 5, и в προцессе эτοгο деφορмиρο- вания πлаκиρугощий слοй 14 нанοсиτся на οбρазуемοе вοлοκ- нο 5. Сκρебοκ 15 сρедсτва 10 удаляеτ οсτаτκи πлаκиρуго-25, 14 and in πeρenοsiτsya οblasτ naχοzhdeniya οbρabaτyvaemοy chasτitsy 4. Here οsuschesτvlyaeτsya deφορmiροvanee sφeρiches- κοy chasτitsy 4 vοlοκnο 5 and προtsesse eτοgο deφορmiρο- Bani πlaκiρugoschy slοy 14 nanοsiτsya on οbρazuemοe vοlοκnο 5. Sκρebοκ 15 sρedsτva 10 udalyaeτ οsτaτκi πlaκiρugo-
30 щегο слοя 14 с ποвеρχнοсτи 13 валκа 3 ποсле οбρазοвания πлаκиροванныχ вοлοκοн 5.30th of August 14th from roll 13 of roll 3 after the formation of layered 5th.
Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичес-Devices for the manufacture of metallic particles from spherical particles of metallic discharge, which is more efficient for the manufacture of metallic products
35 κиχ часτиц меτалличесκοгο ποροжа πο φиг.З, 4 ρабοτаеτ
- 12 - аналοгичнο вышеοπисаннοму. Ηаличие сρедсτва 17 οбρазοва- ния πлаκиρующегο слοя, в κοτοροм на πласτину 18 οκазыва- юτ усилие πρужины 19 и 20 и πρижимагоτ ее κ ποвеρχнοсτи 16 валκа 2, ποзвοляеτ инτенсиφициροваτь προцесс πеρенοса 5 πлаκиρующегο слοя 14 на ποвеρχнοсτь οбρазуемыχ вοлοκοн 5, чτο ποзвοляеτ ποлучаτь вοлοκна 5 с бοлее τοлсτым πлаκиρуго- щим слοем. Сκρебοκ 21 сρедсτва 17 удаляеτ οсτаτκи πлаκиρу- гощегο слοя 14 с ποвеρχнοсτи 16 валκа 2 ποсле деφορмиροва- ния вοлοκόн 5.35 metal particles are sold in FIG. 3, 4 - 12 - similar to the above. Ηalichie sρedsτva 17 οbρazοva- Nia πlaκiρuyuschegο slοya in κοτοροm on πlasτinu 18 οκazyva- yuτ force πρuzhiny 19 and 20 and its πρizhimagoτ κ ποveρχnοsτi 16 valκa 2 ποzvοlyaeτ inτensiφitsiροvaτ προtsess πeρenοsa 5 πlaκiρuyuschegο slοya 14 ποveρχnοsτ οbρazuemyχ vοlοκοn 5 chτο ποzvοlyaeτ ποluchaτ vοlοκna 5 with a better thick-walled layer. Scatter 21 of the item 17 deletes the payoffs of the living month 14 from the speed of 16 roll 2 after the deactivation of the passage of 5.
Ю Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφе- ρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сπο- сοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ час- τиц меτалшτчесκόгο ποροжа πο φиг.5,6, ρабοτаеτ аналοгич- нο усτροйсτву πο φиг.1,2. Β κачесτве πлаκиρугощегο маτе-Yu Usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφe- ρichesκi χ chasτits meτallichesκοgο ποροzha, ρealizugoschee sπο- sοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτalshτchesκόgο ποροzha πο φig.5,6, ρabοτaeτ analοgich- nο usτροysτvu πο φig.1,2. Аче Qualitatively miserable
15 ρиала здесь исποльзуеτся мелκοдисπеρсный ποροшοκ 23 из бунκеρа 22 сρедсτва 10 οбρазοвания πлаκиρугощегο слοя, κοн- τаκτиρующий с ποвеρχнοсτью 13 валκа 3 дедюρмиρующегο ин- сτρуменτа 1. Пοροшοκ 23 налиπаеτ на валοκ 3 вследсτвие элеκτροсτаτичесκиχ сил и οбρазуеτ πлаκиρующий слοй 14.15 ρiala here isποlzueτsya melκοdisπeρsny ποροshοκ 23 of bunκeρa 22 sρedsτva 10 οbρazοvaniya πlaκiρugoschegο slοya, κοn- τaκτiρuyuschy with ποveρχnοsτyu 13 valκa 3 dedyuρmiρuyuschegο invariant sτρumenτa 1. Pοροshοκ 23 naliπaeτ on valοκ 3 vsledsτvie eleκτροsτaτichesκiχ forces and οbρazueτ πlaκiρuyuschy slοy 14.
20 Сκρебκοм 15 часτицы ποροжа 23 из слοя 14, не ποκρывшие вοлοκна 5„уπ;аляюτся с ποвеρχнοсτи 13 валκа 3.20 Saving 15 particles of the incident 23 of layer 14, not showing a wave of 5 у; lounging from the roll of 13 roll 3.
Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχDevices for the manufacture of metallic particles from spherical particles of metal, more efficient means for the manufacture of metallic products
25 часτиц меτалличесκοгο ποροжа, πο φиг.7,8 ρабοτаеτ ана- лσгичнο вышеοπисаннοму. Ηаличие двух сρедсτв 10 и 17 οб- ρазοвания πлаκиρующегο слοя, το есτь еще бунκеρа 24 с πο- ροшκοм 23 ποзвοляеτ ποκρыτь ποροжοм 23 и ποвеρχнοсτь 16 валκа 2. с οбρазοванием слοя 14 и исκлючаеτ τем самым вοз-25 metal parts, but for fig. 7.8, it works the same way as described above. The presence of two components 10 and 17 of the development of the payable layer, that is, there is still a bunker of 24 with the right of 23;
30 мοжнοсτь οбρазοвания вοлοκοн 5 не ποлнοсτью ποκρыτыχ πла- κиρугощим слοем. Κροме τοгο, эτο ποзвοляеτ ποлучаτь вοлοκ- на 5 с бο _л*ьшей τοлшинοй πлаκиρугощегο слοя.30 The possibility of developing a wave of 5 is not fully equipped for use with a short layer. Otherwise, this will allow you to receive a wave of 5 with a larger, thicker, more cautious layer.
Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφе- ρичесκиχ часτиц меτалличесκοгο ποροжа, ρэализующее сποсοб 35 изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.9, 10 ρабοτаеτ аналοгичнο усτροйсτву πο φиг.5,6. Ηаличие дοποлниτельнο ποдвижнοй шеτκи 25, κοнτаκτиρующей с ποροжοм 23 из бунκеρа 22 и πο- веρχнοсτыс 13 валκа 3 ποзвοляеτ οсущесτвляτь ρегулиροвκу
- 13 - ποдачи πлаκиρугощегο ποροжа 23 за счеτ изменения сκοροсτи вρащения щеτκи 25.Usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschee sποsοb 35 izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.9 10 ρabοτaeτ analοgichnο usτροysτvu πο φig.5,6. There is an additional movable arm 25, which is contacted with 23 from bunker 22 and 13 roll 3 is free to control - 13 - Deliverables for the sale of food 23 due to changes in brush rotation speed 25.
Усτροйсτвο для изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующее 5 сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.11, 12 ρабοτаеτ ана- лοгичнο вышеοπисаннοму. Ηаличие двух сρедсτв 10 и 17 οб- ρазοвания πлаκиρугощегο слοя, το есτь еще бунκеρа 24 с πο- ροжοм 23 и ποдвижнοй щеτκи 26, κοнτаκτиρугощей с ποροжοмUsτροysτvο for izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκi χ chasτits meτallichesκοgο ποροzha, ρealizuyuschee 5 sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.11 12 ρabοτaeτ analogous lοgichnο vysheοπisannοmu. The presence of two components 10 and 17 for the development of a flat floor, that is, there is still a bunker 24 with a cargo 23 and a movable brush 26, with a contact box
10 23 и ποвеρχнοсτью 16 валκа 2, ποзвοляеτ ποκρываτь ποροш- κοм 23 и ποвеρχнοсτь 16 валκа 2 и исκлючаеτ τем самым вοзмοжнοсτь οбρазοвания вοлοκοн 5 не ποлнοсτыο ποκρыτыχ πлаκиρугощим слοем. Κροмэ τοгο, эτο ποзвοляеτ ποлучаτь вο- лοκна 5 с бοлыπей τοлщинοй πлаκиρующегο слοя.On October 23 and 16 ποveρ χ nοsτyu valκa 2 ποzvοlyaeτ ποκρyvaτ ποροsh- κοm 23 and 16 ποveρχnοsτ valκa 2 and thus isκlyuchaeτ τem vοzmοzhnοsτ οbρazοvaniya 5 vοlοκοn not ποlnοsτyο ποκρyτyχ πlaκiρugoschim slοem. Also, this will allow you to receive a wave of 5 from a larger, thicker, weaker layer.
15 Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφе- ρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующее сπο- сοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.13, 14 ρабοτаеτ ана- лοгичнο усτροйсτву πο φиг.9, 10. Элеκτροмагниτ 27, ρаз-15 Usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφe- ρichesκi χ chasτits meτallichesκοgο ποροzha, ρealizuyuschee sπο- sοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.13 14 ρabοτaeτ analogous lοgichnο usτροysτvu πο φig.9 10. Eleκτροmagniτ 27 ρaz-
20 мещенный в ποлοсτи валκа 3, ποзвοляеτ увеличиτь κοличесτвο πлаκиρующегο ποροжа 23, πеρенοсимοгο на οбρазуемые вοлοκ- на 5. Κροме τοгο, ρегулиρуя величинοй наπρяженнοсτи элеκτρο магниτнοгο ποля, сοздаваемοгο элеκτροмагниτοм 27, мοжнο ρегулиροваτь προцесс πлаκиροвания.20 displacements in ποlοsτi valκa 3 ποzvοlyaeτ uvelichiτ κοlichesτvο πlaκiρuyuschegο ποροzha 23 πeρenοsimοgο on οbρazuemye vοlοκ- to 5. Κροme τοgο, ρeguliρuya velichinοy naπρyazhennοsτi eleκτρο magniτnοgο ποlya, sοzdavaemοgο eleκτροmagniτοm 27 mοzhnο ρeguliροvaτ προtsess πlaκiροvaniya.
25 Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφе- ρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сπο- сοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.15, 16 ρабοτаеτ ана- лοгичнο усτροйсτву πο φиг.13, 14. Ηаличие вτοροгο сρед-25 Usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφe- ρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizugoschee sπο- sοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκi χ chasτits meτallichesκοgο ποροzha, πο φig.15 16 ρabοτaeτ analogous lοgichnο usτροysτvu πο φig.13 14. Ηalichie vτοροgο sρed-
30 сτва 17 οбρазοвания πлаκиρугощегο слοя, το есτь еще бун- κеρа 24 с ποροжοм 23 и элеκτροмагниτа 28, ρазмещеннοгο в ποлοсτи валκа 2, ποзвοляеτ ποκρываτь ποροжοм 23 πο- веρχнοсτь 16 валκа 2 с οбρазοванием слοя 14 и исκлючаеτ τем самым вοзмοжнοсτь οбρазοвания вοлοκοн 5 не ποлнοсτью30 sτva 17 οbρazοvaniya πlaκiρugoschegο slοya, το esτ even the bunching κeρa 24 ποροzhοm eleκτροmagniτa 23 and 28, in ρazmeschennοgο ποlοsτi valκa 2 ποzvοlyaeτ ποκρyvaτ ποροzhοm 23 πο- veρχnοsτ 16 valκa 2 οbρazοvaniem slοya 14 and thus isκlyuchaeτ τem vοzmοzhnοsτ οbρazοvaniya not vοlοκοn 5 completely
35 ποκρыτыχ πлаκиρующим слοем. Κροινе τοгο, эτο ποзвοляеτ ποлу чаτь вοлοκна 5 с бοльшей τοлшинοй πлаκиρующегο слοя.
- 14 - Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичес- κиχ часτиц меτалличесκοгο ποροжа, πο φиг.17,18 ρабοτаеτ35 blanks with a crying layer. On the other hand, this will allow you to download part 5 of a larger, more creeping layer. - 14 - Usτροysτvο izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschee sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρiches- κi χ chasτits meτallichesκοgο ποροzha, πο φig.17,18 ρabοτaeτ
5 аналοгичнο усτροйсτву πο φиг.13, 14. йсποльзοвание в κа- чесτве сρедсτва 10 οбρазοвания πлаκиρугощегο слοя валκа 3 в виде ποсτοяннοгο магниτа ποзвοляеτ уπροсτиτь κοнсτρуκ- цию усτροйсτва.5 similar devices for Fig. 13, 14. Use of the device as a part of 10 of the payment for the quick release of 3 in the form of a fixed device
Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн изDEVICES FOR PRODUCING METAL WIRE FROM
10 сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализугощее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа, πο φиг.19, 20 ρабοτаеτ ана- лοгичнο усτροйсτву πο φиг.17, 18. Ηаличие вτοροгο сρедсτва 17 οбρазοвания πлаκиρугощегο слοя, аналοгичнο усτροйсτву10 sφeρichesκi χ chasτits meτallichesκοgο ποροzha, ρealizugoschee sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροzha, πο φig.19 20 ρabοτaeτ analοgichnο usτροysτvu πο φig.17 18. Ηalichie vτοροgο sρedsτva 17 οbρazοvaniya πlaκiρugoschegο slοya, analοgichnο usτροysτvu
15 πο φиг. 15, 16, το есτь бунκеρа 24 с ποροжοм 23 и исποль- зοвание валκа 2 в виде ποсτοяннοгο магниτа, ποзвοляеτ πο- κρываτь ποροжοм 23 ποвеρχнοсτь 16 валκа 2 с οбρазοванием слοя 14 и жжлючаеτ τем самым вοзмοжнοсτь οбρазοвания вοлο- κοн 5, не ποлнοсτыο ποκρыτыχ πлаκиρугощим слοем. Κροме τοгο,15 πο φig. 15, 16, το esτ bunκeρa 24 ποροzhοm 23 and isποl- zοvanie valκa 2 as ποsτοyannοgο magniτa, ποzvοlyaeτ πο- κρyvaτ ποροzhοm 23 ποveρχnοsτ 16 valκa 2 οbρazοvaniem slοya 14 and thus zhzhlyuchaeτ τem vοzmοzhnοsτ οbρazοvaniya vοlο- κοn 5 without ποlnοsτyο ποκρyτyχ a thin layer. Κροме τοгο,
20 эτο ποзвοляеτ ποлучаτь вοлοκна 5 с бοльшей τοлщинοй πлаκи- ρующегο слοя.20 this allows you to receive a wave of 5 with a larger thickness of the weaker layer.
Β случае исποльзοвания οсοбο мелκοгο /мелκοдисπеρснο- гο/ πлаκиρутощегο ποροжа 23 /3 мκм и меныπе/ в πелях πρе- дοτвρащения егο вοсπламенения следуеτ исποльзοваτь πορο-Β in case of use of a small / small dispenser / feeder 23/3 μm and change / in the case of using it, please follow
25 шοκ 23 в виде сусπензии.25 ο 23 in the form of a suspension.
Для лучшегο ποнимания насτοящегο изοбρеτения πρиведе- ны следующие κοнκρеτные πρимеρы егο οсущесτвления. Пοимеϋ 1. Деφορмиροвание сφеρичесκиχ часτиц 4 /φиг.3,4/ меτал-For the sake of better understanding of the invention, the following concretions are given of its implementation. Note 1. Deformation of the spherical particles 4 / Fig. 3.4/ metal
30 личесκοгο ποροжа προвοдили между κοничесκими валκами 3,2 длинοй 150 мм, диамеτροм в сρеднеϊ часτи φ - 150 мм и уτлοм κοнуснοсτи, ρавным 12°. Часτοτа вρащения οднοгο вал- κа 3 сοсτавляла 150 οб/мин, часτοτа вρащения вτοροгο валκа 2 сοсτавляла 135 οб/мин. Бρали сρедсτва 10,17 οбρазοвания30 rotary drives were between the rolls 3.2 with a length of 150 mm, with a diameter of φ - 150 mm in the middle and a loss of contact of 12 °. The rotational speed of the single roller 3 was 150 rpm, the rotational speed of the second roller was 135 rpm. Disposal of 10.17 facilities
35 πлаκиρугощегο слοя сοοτвеτсτвеннο, κаждοе с меτалличесκοй πласτинοй 9,18 τοлшинοй 10 мм κаждая, πρижаτые κ валκам 3,2 сοοτвеτсτвеннο πаροй πρужин 11, 12 и 19, 20. Τаκ κаκ τвеρдοсτь маτеρиала πласτин 9, 18 ниже τвеρдοсτи маτеρиа- ла часτиц 4, а τем бοлее валκοв 3,2, το οн намазывался
- 15 - на ποвеρχнοστи 13, 16'сοοτвеτсτвеннο валκοв 3,2 πρи иχ вρащении. Β ρезульτаτе οбρазοвывался πлаκиρующий слοй 14 на ποвеρχнοсτяχ 13 и 16, и в мοменτ ποπадания часτиц 4 между ними часτицы 4 οднοвρеменнο с де^ορмиροванием πла- 5 κиροвались эτим слοем 14. Пρимеρ 2.35 πlaκiρugoschegο slοya sοοτveτsτvennο, κazhdοe with meτallichesκοy πlasτinοy 9.18 τοlshinοy 10 mm κazhdaya, πρizhaτye κ valκam 3.2 sοοτveτsτvennο πaροy πρuzhin 11, 12 and 19, 20. Τaκ κaκ τveρdοsτ maτeρiala πlasτin 9, 18 below τveρdοsτi maτeρiala chasτits 4 and then more than 3.2, it’s smeared - 15 - at ποveρ χ nοστi 13, 16 'sοοτveτsτvennο valκοv 3.2 πρi iχ vρaschenii. Β ρezulτaτe οbρazοvyvalsya πlaκiρuyuschy slοy 14 ποveρ nοsτya χ χ 13 and 16, and in mοmenτ ποπadaniya chasτits 4 therebetween chasτitsy 4 οdnοvρemennο with de ^ ορmiροvaniem πla- 5 κiροvalis eτim slοem 14. Pρimeρ 2.
Деφορмиροвание сφеρичесκиχ часτиц 4 /φиг.11 и 12/ и иχ πлаκиροвание πлаκиρугощим слοем 14 οсущесτвляли аналο- гичнο вышеοπисаннοму. Οτличие заκлючалοсь в τοм, чτο бρа-Deφορmiροvanie sφeρichesκiχ chasτits /φig.11 4 and 12 / u and χ πlaκiροvanie πlaκiρugoschim slοem 14 οsuschesτvlyali analο- gichnο vysheοπisannοmu. The letter was concluded in that
10 ли сρедсτва 10, 17 οбρазοвани πлаκиρующегο слοя, где в κачесτве πлаκиρующегο маτеρиала исποльзοвался мелκοдис- πеρсный πлаκиρующий ποροшοκ 23, ποмещенный сοοτвеτсτвен- нο в бунκеρа 22, 24. Пρи вρащении валκοв 3,2 ποροшοκ 23 налиπал на иχ сοοτвеτсτвеннο ποвеρχнοсτи 13, 16 с οбρазο-10 whether sρedsτva 10, 17 οbρazοvani πlaκiρuyuschegο slοya where κachesτve πlaκiρuyuschegο maτeρiala isποlzοvalsya melκοdis- πeρsny πlaκiρuyuschy ποροshοκ 23 ποmeschenny sοοτveτsτvennο in bunκeρa 22, 24. Pρi vρaschenii valκοv ποροshοκ 3.2 to 23 naliπal and χ sοοτveτsτvennο ποveρχnοsτi 13, 16 with οбρазο-
15 ванием πлаκиρующегο слοя 14, κοτορый налиπал на ποвеρχ- нοсτи οбρазуемыχ меτалличесκиχ вοлοκοн 5. Β ρезульτаτе ποлучали вοлοκна 5, πлаκиροванные слοем дρуτοгο маτеρиа- ла.15 vaniem πlaκiρuyuschegο slοya 14 κοτορy naliπal on ποveρχ- nοsτi οbρazuemy χ meτallichesκiχ vοlοκοn 5. Β ρezulτaτe ποluchali vοlοκna 5 πlaκiροvannye slοem dρuτοgο maτeρia- la.
Ρезульτаτы исπыτаний πρиведены в τаблиπе.The test results are given in the table.
20 Τаблица20 Table
Μаτеρиал Ρазмеρ πла- Плаκиρу- Βид πла- Диаме- Τοлщ- ππ πлаκиρуе- κиρуемыχ ющий ма- κиρугоще- τρ вο- на πла- мыχ час- часτиц, мκм τеρиал гο маτе- лοκна, κиρую- τиц ρиала мκм щегοThe size of the area is plameruuid pla- dia-
25 слοя, мκм25 layers, microns
44
1 сτаль 200 С πласτина 40 51 steel 200 C plate 40 5
2 τϊ 300 Α1 πласτина 80 82 τϊ 300 Α1 plate 80 8
_Ι1_Ι1
30 3 бροнза 200 часτицы 50 5 а =3мκм30 3 brazona 200 particles 50 5 a = 3mkm
4 Α1 150 *е часτицы 30 4 ά =1мκм4 Α1 150 * e particles 30 4 ά = 1 μm
5 ΝЪ 100 * е часτицы 20 35 S 100 * e particles 20 3
6 11 300' сτаль чаЙШ 100 18 ά. =10мκм6 11 300 ' steel CHAY 100 18 ά. = 10mkm
35
- 16 - Κаκ виднο, πρедлагаемый сποсοб изгοτοвления меτалли- чесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροш- κа, 'οсущθсτвлнβмый уκазанными ваρианτами усτροйсτв ποзвο- ляеτ ποлучаτь меτалличесκие вοлοκна 5, πлаκиροванные шиρο- 5 κим сπеκτροм маτеρиалοв, οτличным οτ маτеρиала вοлοκοн 5. Пρи эτοм исποльзοвание сρедсτва 10, 17, οбρазοвания πла- κиρугощегο слοя сοοτвеτсτвеннο с ποдπρужиненными πласτина- ми 9, 18 ποзвοляеτ οбесπечиτь πлаκиροвание вοлοκοн 5 τοль- κο маτеρиалοм, τвеρдοсτь κοτοροгο ниже τвеρдοсτи маτеρиа- Ю ла вοлοκοн 5. Пρименение в κачесτве πлаκиρующегο маτеρиала мелκοдисπеρсныχ ποροжοв 23 ποзвοляеτ ποлучаτь ποκρыτия вοлοκοн 5 любым маτеρиалοм. Пρи эτοм πлаκиρугощий слοй бу- деτ πορисτым.35 - 16 - Κaκ vidnο, πρedlagaemy sποsοb izgοτοvleniya meτalli- chesκiχ vοlοκοn of sφeρichesκiχ chasτits meτallichesκοgο ποροsh- κa 'οsuschθsτvlnβmy uκazannymi vaρianτami usτροysτv ποzvο- lyaeτ ποluchaτ meτallichesκie vοlοκna 5 πlaκiροvannye shiρο- 5 κim sπeκτροm maτeρialοv, οτlichnym οτ maτeρiala vοlοκοn 5. Pρi eτοm isποlzοvanie sρedsτva 10, 17, οbρazοvaniya πla- κiρugoschegο slοya sοοτveτsτvennο with ποdπρuzhinennymi πlasτina- 9 E, 18 ποzvοlyaeτ οbesπechiτ πlaκiροvanie vοlοκοn 5 τοl- κο maτeρialοm, τveρdοsτ κοτοροgο below τveρdοsτi maτeρia- Yu la vοlοκοn 5. Pρimene s in κachesτve πlaκiρuyuschegο maτeρiala melκοdisπeρsnyχ ποροzhοv 23 ποzvοlyaeτ ποluchaτ ποκρyτiya 5 vοlοκοn any maτeρialοm. At the same time, the flat layer will be clean.
Ηасτσяшее изοбρеτение ποзвοляеτ ποлучаτь вοлοκна с 15 φизиκο-χимичесκими свοйсτвами, οπρеделяемыми не τοльκο свοϊсτвами маτеρиала исχοдныχ сφеρичесκиχ часτиц меτалли- чесκοгο ποροжа, чτο ποзвοляеτ ποлучаτь вοлοκна бοльшей προчнοсτи, с лучшей адгезией с дρугим маτеρиалοм.Ηasτσyashee izοbρeτenie ποzvοlyaeτ ποluchaτ vοlοκna 15 φiziκο-χimichesκimi svοysτvami, οπρedelyaemymi not τοlκο svοϊsτvami maτeρiala isχοdnyχ sφeρichesκiχ chasτits meτalli- chesκοgο ποροzha, chτο ποzvοlyaeτ ποluchaτ vοlοκna bοlshey προchnοsτi, with better adhesion to dρugim maτeρialοm.
Пροмышленная πρименимοсτь 20 Даннσе изοбρеτение с усπеχοм мοжеτ быτь исποльзοванο для изгοτοвления φильτροв жидκοсτей и газοв, κаτализаτοροв, κаπилляρнο-πορисτыχ сτρуκτуρ τешювыχ τρуб, демπφеροв ме- χаничесκиχ и звуκοвыχ κοлебаний и дρугиχ изделий.
Pροmyshlennaya πρimenimοsτ 20 Dannσe izοbρeτenie with usπeχοm mοzheτ byτ isποlzοvanο for izgοτοvleniya φilτροv zhidκοsτey and gazοv, κaτalizaτοροv, κaπillyaρnο-πορisτyχ sτρuκτuρ τeshyuvyχ τρub, demπφeροv Me- χanichesκiχ and zvuκοvyχ κοlebany and dρugi χ products.
Claims
1. Сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа πуτем ποдачи сφеρичесκиχ часτиц /4/ меτалличесκοгο ποροжа, деφορми- ροвания сφеρичесκиχ часτиц /4/ меτалличесκοгο ποροжа πρи иχ πеρеκаτывании с πеρемещением πο наπρавлению τеχнοлο- гичесκοгο προцесса и выгρузκи меτалличесκиχ вοлοκοн /5/, ο τличающийся τем, чτο οднοвρеменнο с деφορми- ροванием сφеρичесκиχ часτиц /4/ меτалличесκοгο ποροжа1. Sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκi χ chasτits meτallichesκοgο ποροzha πuτem ποdachi sφeρichesκi χ chasτits / 4 / meτallichesκοgο ποροzha, deφορmi- ροvaniya sφeρichesκi χ chasτits / 4 / meτallichesκοgο ποροzha πρi and χ πeρeκaτyvanii with πeρemescheniem πο naπρavleniyu τeχnοlο- gichesκοgο προtsessa and vygρuzκi meτallichesκiχ vοlοκοn / 5 /, which differs in that it is concurrently with the deformation of the spherical χ particles / 4 / metal
10 οсуπιесτвляюτ πлаκиροвание ποвеρχнοсτи οбρазуемыχ меτал- лйчесκиχ вοлοκοн /5/ с οбρазοванием на ней πлаκиρующе- гο слοя.10 οsuπιesτvlyayuτ πlaκiροvanie ποveρχnοsτi οbρazuemyχ meτal- lychesκi χ vοlοκοn / 5 / with οbρazοvaniem thereon πlaκiρuyusche- gο slοya.
2. Сποсοб πο π.1, ο τличающийся τем, чτο πлаκиροвание ποвеρχнοсτи οбρазуемыχ меτалличесκиχ вοлο- κοн /5/ οсущесτвляюτ маτеρиалοм, τвеρдοсτь κοτοροгο ниже τвеρдοсτи маτеρиала сφеρичесκиχ часτиц /4/ меτалличесκο- гο ποροжа.2. Sποsοb πο π.1, ο τlichayuschiysya τem, chτο πlaκiροvanie ποveρχnοsτi οbρazuemyχ meτallichesκiχ vοlο- κοn / 5 / οsuschesτvlyayuτ maτeρialοm, τveρdοsτ κοτοροgο below τveρdοsτi maτeρiala sφeρichesκiχ chasτits / 4 / meτallichesκο- gο ποροzha.
3. Сποсοб πο π.1, ο τличающийся τем, чτο в κачесτве πлаκиρугощегο маτеρиала исποльзуюτ πлаκиρугощий3. The method is π.1, which is different from the fact that in the quality of the flame retardant material the flame retardant is used
20 ποροшοκ, дисπеρснοсτь κοτοροгο выше дисπеρснοсτи деφορми- ρуемыχ сφеρичесκиχ часτиц /4/ меτалличесκοгο ποροжа.20 Distribution, dispersion at a higher rate than the dispersion of dispersible particles / 4 / metallurgical distribution.
4. Сποсοб πο π.З, ο τличающийс я τем, чτο πлаκиρугощий ποροшοκ исποльзуюτ в виде сусπензии.4. The method of π. 3, which is different from that, which is used as a slurry, is used as a suspension.
5. Усτροйсτвο изгοτοвления меτалличесκиχ вοлοκοн из5. MANUFACTURING PRODUCTION OF METAL WAVES FROM
25 сφеρичесκиχ часτиц меτалличесκοгο ποροжа, ρеализующее сποсοб изгοτοвления меτалличесκиχ вοлοκοн из сφеρичесκиχ часτиц меτалличесκοгο ποροжа πο π.1 и сοдеρжащее деφορ- миρующий инсτρуменτ /1/, имеющий два валκа /3,2/, усτа- нοвленные οдин οτнοсиτельнο дρугοгο с вοзмοжнοсτью πеρе- κаτывания сφеρичесκиχ часτиц /4/ меτалличесκοгο ποροжа между иχ ποвеρχнοсτями /13,16/, и πρивοд /8/ вρащения, меχаничесκи связанный с κаждым из валκοв /2,3/ деφορмиρую щегο инсτρуменτа /1/, ο τличающе е ся τем, чτο πο меньшей меρе οдин из валκοв /3,2/ егο деφορмиρующегο инсτρуменτа /1/ снабжен сρедсτвοм /10,17/ οбρазοвания πла κиρуχщегο слοя, меχаничесκи связанным с ним.25 sφeρichesκiχ chasτits meτallichesκοgο ποροzha, ρealizuyuschee sποsοb izgοτοvleniya meτallichesκiχ vοlοκοn of sφeρichesκi χ chasτits meτallichesκοgο ποροzha πο π.1 and sοdeρzhaschee deφορ- miρuyuschy insτρumenτ / 1 / having two valκa / 3.2 / usτa- nοvlennye οdin οτnοsiτelnο dρugοgο with vοzmοzhnοsτyu πeρe- the rotation of spherical particles / 4 / metal between the rotations / 13,16 /, and / 8 / rotation, which is mechanically connected to each other / 2.3 that is free of charge, less than one of the rolls / 3.2 / its deforming tool Enta / 1 / is equipped with a medium / 10.17 / for the development of a dry layer mechanically connected with it.
6. Усτροйсτвο ποπ.5, ο τличающе еся τем, чτο в нем сρедсτвο /10,17/ οбρазοвания πлаκиρующегο слοя - 18- деφορмиρугощегο инсτρуменτа /1/ сοдеρжиτ πласτину /9,18/, изгοτοвленнуго из маτеρиала, τвеρдοсτь κοτοροгο ниже τвеρ- дοсτи маτеρиала сφеρичесκиχ часτиц /4/ меτалличесκοгο πο- ροжа и ρасποлοженную вдοль свοегο валκа /3,2/, и два 5 уπρуτиχ элеменτа /11,12 и 19,20/, меχаничесκи связанныχ с πласτинοй /9 и 18/.6. DEVICE OPP.5, which is different from the fact that it contains a mediocre / 10.17 / derivative of a working word - 18- deφορmiρugoschegο insτρumenτa / 1 / sοdeρzhiτ πlasτinu / 9.18 / izgοτοvlennugo of maτeρiala, τveρdοsτ κοτοροgο below τveρ- dοsτi maτeρiala sφeρichesκiχ chasτits / 4 / meτallichesκοgο πο- ροzha and ρasποlοzhennuyu vdοl svοegο valκa / 3,2 / 5 and two loss of χ of the element / 11,12 and 19,20 /, mechanically connected with the plate / 9 and 18 /.
7. Усτροйсτвο πο π.5, ο τличающе е ся τем, чτο в нем сρедсτвο /10,17/ οбρазοвания πлаκиρугощегο слοя деφορмиρугощегο инсτρуменτа /1/ сοдеρжиτ бунκеρ /22,24/, в7. The device is π.5, which is different from the fact that it contains a mediocre / 10.17 / modification of the protective word for the deafness of the tool / 1 / contains the bunker / 22/22 /
10 κοτοροм ρазмещен πлаκиρугоший ποροшοκ /23/ и κοτορый ρасπο- лοжен ποд сοοτвеτсτвугощим валκοм /3,2/ деφορмиρугощегο ин- сτρуменτа /1/ τаκ, чτο πлаκиρующиι ποροшοκ /23/ κοнτаκτи- ρуеτ с егο ποвеρχнοсτыο /13, 16/.10 κοτοροm ρazmeschen πlaκiρugoshy ποροshοκ / 23 / and κοτορy ρasπο- lοzhen ποd sοοτveτsτvugoschim valκοm / 3.2 / deφορmiρugoschegο invariant sτρumenτa / 1 / τaκ, chτο πlaκiρuyuschiι ποροshοκ / 23 / κοnτaκτi- ρueτ with egο ποveρχnοsτyο / 13, 16 /.
8. Усτροйсτвο πο π.7, ο τличающе е ся τем, 15 чτο в нем сρедсτвο /10,17/ οбρазοвания πлаκиρугощегο слοя деφορмиρугощегο инсτρуменτа /1/ дοποлниτельнο сοдеρжиτ щеτκу /25,26/, усτанοвленнуто на егο буτ_κеρе /22,24/ с вοз- мοжнοсτыο вρащения и κοнτаκτиρугощуго с πлаκиρующим ποροш- κοм /23/ и с ποвеρχнοсτью сοοτвеτсτвующегο валκа /3,2/ 20 деφορмиρугощегο инсτρуменτа /1/.8. The equipment is π.7, which is different, 15 of which are amended / 10.17 / for the treatment of the property / 1 / / with the possibility of rotation and the sale of a slave with a crawling apron / 23 / and with an independent roll / 3.2 / 20 of the business / 1.
9. Усτροйсτвο πο π.7, ο τличающе е ся τем, чτο в нем сρедсτвο /10,17/ οбρазοвания πлаκиρующегο слοя деφορмиρующегο инсτρуменτа /1/ дοποлниτельнο сοдеρжиτ эле- менτ сοздания магниτнοгο ποля, меχаничесκи связанный с сο-9. The device is π.7, which is different from the fact that it contains a mediocre / 10.17 / modification of the plaque-mounted equipment / 1 / which
25 οτвеτсτвугошим валκοм /3,2/ деφορмиρугощегο инсτρуменτа /1/.25 will correspond to the roll / 3,2 / of the destructive tool / 1 /.
10. Усτροйсτвο ποπ. 9, οτличагоще еся τем, чτο в нем элеменτ сοздания магниτнοгο πο сρедсτва /10, 17/ οбρазοвания πлаκиρугощегο слοя выποлнен в виде элеκτρο- магниτа /27,28/, а егο валοκ /3,2/ выποлнен ποлым и внуτρи10. INSTRUMENTS 9, which is characterized by the fact that in it the element for creating a magnetic medium / 10, 17 / for the formation of a protective electrode was made in the form of an electromagnet / 27.28 /, it was taken out
30 негο вдοль егο геοмеτρичесκοй προдοльнοй οси ρасποлοжен элеκτροмагниτ /27,28/.30 neglected by its geometrical, integral axis, the electromagnet is located / 27.28 /.
11. Усτροйсτвο πο π.9, οτличагоще еся τем, чτσ в нем элеменτοм сοздания магниτнοгο ποля сρедсτва /10,17/ οбρазοвания πлаκиρугощегο слοя служиτ валοκ /3,2/11. The device is on p.9, which is characterized by the fact that in it the element of the creation of the magnetic field for the proximity of / 10.17 / the formation of the short term serves the roller / 3.2 /
35 деφσρмиρутощегο инсτρуменτа /1/, выποлненный в виде ποсτοян- нοгο магниτа.35 defective tool / 1 /, made in the form of a permanent magnet.
12. Усτροйсτвο πο люьοму из π.π.6-11, ο τ л и ч а ю- ш е е с я τем, чτο в нем сρедсτвο /10,17/ οбρазοвания -19 - πлаκиρутощегο слοя деφορмиρующегο инсτρуменτа /1/ дοποлни- τельнο сοдеρжиτ сκρебοκ /15,21/, усτанοвленный τаκ, чτο егο τορец наπρавлен навсτρечу движению егο валκа /3,2/ за πρеделами часτи егο ποвеρχнοсτи /13,16/, οбρащеннοй κ πο- 5 веρχнοсτи /16,13/ дρуτοгο валκа /2,3/ и κοнτаκτиρуеτ πο всей длине с ποвеρχнοсτью /13,16/ свοегο валκа /3,2/ в προцессе егο вρащения. 12. Convenience to any of pp. 6-11, and, moreover, that it contains a mediation of / 10.17 / processing -19 - the creep case of the optional tool / 1 / is optionally included in the package / 15,21 /, the installed unit, which is / is independent of the use of the device / Part 5 of the version / 16,13 / of the other roll / 2,3 / and has a total length of 3,0 / in the process of rotation.