WO1990003954A1 - Milieu incorporant de la melanine comme pigment absorbant pour la protection contre le rayonnement electromagnetique - Google Patents

Milieu incorporant de la melanine comme pigment absorbant pour la protection contre le rayonnement electromagnetique Download PDF

Info

Publication number
WO1990003954A1
WO1990003954A1 PCT/US1989/004417 US8904417W WO9003954A1 WO 1990003954 A1 WO1990003954 A1 WO 1990003954A1 US 8904417 W US8904417 W US 8904417W WO 9003954 A1 WO9003954 A1 WO 9003954A1
Authority
WO
WIPO (PCT)
Prior art keywords
melanin
radiation
plastic
lens
solid
Prior art date
Application number
PCT/US1989/004417
Other languages
English (en)
Inventor
James M. Gallas
Original Assignee
Photoprotective Technologies Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Photoprotective Technologies Incorporated filed Critical Photoprotective Technologies Incorporated
Publication of WO1990003954A1 publication Critical patent/WO1990003954A1/fr

Abstract

La présente invention concerne un milieu incorporant de la mélanine pour la protection contre le rayonnement.
PCT/US1989/004417 1988-10-06 1989-10-05 Milieu incorporant de la melanine comme pigment absorbant pour la protection contre le rayonnement electromagnetique WO1990003954A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US25590588A 1988-10-06 1988-10-06
US255,905 1988-10-06

Publications (1)

Publication Number Publication Date
WO1990003954A1 true WO1990003954A1 (fr) 1990-04-19

Family

ID=22970339

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1989/004417 WO1990003954A1 (fr) 1988-10-06 1989-10-05 Milieu incorporant de la melanine comme pigment absorbant pour la protection contre le rayonnement electromagnetique

Country Status (2)

Country Link
AU (1) AU4622689A (fr)
WO (1) WO1990003954A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2303484A1 (es) * 2007-10-15 2008-08-01 Universidad Complutense De Madrid Material de cobertura, revestimiento o pantalla para la proteccion y terapia de ojos contra los efectos de la luz azul.
ES2312284A1 (es) * 2007-10-26 2009-02-16 Universidad Complutense De Madrid Gafas de seguridad y prevencion con superficie tratada para la proteccion y terapia de ojos en oficios y deportes.

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1060780A (en) * 1949-05-02 1967-03-08 Dynamit Nobel Ag Improvements in or relating to the manufacture of goggles,eye shields and the like
JPS4971149A (fr) * 1972-11-10 1974-07-10
US4404257A (en) * 1981-04-13 1983-09-13 General Electric Company Coated and ultraviolet radiation stabilized polycarbonate article
US4419405A (en) * 1981-01-15 1983-12-06 General Electric Company Ultraviolet light absorbing agents and compositions and articles containing same
US4464525A (en) * 1983-04-11 1984-08-07 Ppg Industries, Inc. Near infrared absorbing polymerizate, from dicarboxylic compound, diol bis(allyl carbonate) and metal hexacarbonyl

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1060780A (en) * 1949-05-02 1967-03-08 Dynamit Nobel Ag Improvements in or relating to the manufacture of goggles,eye shields and the like
JPS4971149A (fr) * 1972-11-10 1974-07-10
US4419405A (en) * 1981-01-15 1983-12-06 General Electric Company Ultraviolet light absorbing agents and compositions and articles containing same
US4404257A (en) * 1981-04-13 1983-09-13 General Electric Company Coated and ultraviolet radiation stabilized polycarbonate article
US4464525A (en) * 1983-04-11 1984-08-07 Ppg Industries, Inc. Near infrared absorbing polymerizate, from dicarboxylic compound, diol bis(allyl carbonate) and metal hexacarbonyl

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2303484A1 (es) * 2007-10-15 2008-08-01 Universidad Complutense De Madrid Material de cobertura, revestimiento o pantalla para la proteccion y terapia de ojos contra los efectos de la luz azul.
WO2009050308A1 (fr) * 2007-10-15 2009-04-23 Universidad Complutense De Madrid Matériau de couverture, de revêtement ou écran pour la protection et le traitement des yeux contre les effets de la lumière bleue
US8570648B2 (en) 2007-10-15 2013-10-29 Universidad Complutense De Madrid Material for covering, coating or screening for eye protection and therapy against the effects of blue light
ES2312284A1 (es) * 2007-10-26 2009-02-16 Universidad Complutense De Madrid Gafas de seguridad y prevencion con superficie tratada para la proteccion y terapia de ojos en oficios y deportes.

Also Published As

Publication number Publication date
AU4622689A (en) 1990-05-01

Similar Documents

Publication Publication Date Title
US5112883A (en) Medium incorporating melanin as an absorbing pigment against electromagnetic radiation
US5047447A (en) Medium incorporating melanin as an absorbing pigment for protection against electromagnetic radiation
US4698374A (en) Optical lens system incorporating melanin as an absorbing pigment for protection against electromagnetic radiation
JP3625097B2 (ja) 着色コンタクトレンズおよびその製造法
EP1412784B1 (fr) Nouveau film de polarisation de lumiere avec de la melanine
US8133414B2 (en) Light filters using yellow melanin and melanin-like oligomers and photochromic dyes
US20070298242A1 (en) Lenses having dispersed metal nanoparticles for optical filtering including sunglasses
US8048343B2 (en) Light filters using yellow melanin and melanin-like oligomers and photochromic dyes
JP2019530892A (ja) カプセル封入された光吸収剤を含む眼鏡用レンズ
US6066272A (en) Fullerene-containing optical materials with novel light transmission characteristics
AU2002355836A1 (en) Light polarizing film with melanin
US20050041299A1 (en) Light filters using the oxidative polymerization product of 3-hydroxykynurenine (3-OHKyn)
US5187207A (en) Melanin hydrophilic contact lenses
JP2023116551A (ja) カプセル封入された光吸収剤を含む眼鏡用レンズの製造のための組成物
WO2008134555A2 (fr) Filtres lumineux comprenant des dérivés de l'acide (p-nitrophénylazo)salicylique
US5036115A (en) Optical lens system incorporating melanin as an absorbing pigment for protection against electromagnetic radiation
JPS63275682A (ja) 酸化チタンを含有する塗料
EP2247976B1 (fr) Lentille ophtalmique dotée d un composant bloquant la lumière et d un colorant jaune
EP0639209B1 (fr) Melanine synthetique pure utilisee notamment dans des dispositifs optiques a leger voile
US6825975B2 (en) Light filters using the oxidative polymerization product of 3-Hydroxykynurenine (3-OHKyn)
EP1388749B1 (fr) Lentilles photochromiques plastiques pour lunettes et procede de production desdites lentilles
EP0380518B1 (fr) Lentilles de contact hydrophiles a la melanine
WO1990003954A1 (fr) Milieu incorporant de la melanine comme pigment absorbant pour la protection contre le rayonnement electromagnetique
US5116884A (en) Melanin hydrophilic contact lenses
EP0311290A2 (fr) Lentilles de contact hydrophiles contenant de la mélanine

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AT AU BB BG BR CH DE DE DK FI GB HU JP KP KR LK LU MC MG MW NL NO RO SD SE SU US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE BF BJ CF CG CH CM DE FR GA GB IT LU ML MR NL SE SN TD TG

COP Corrected version of pamphlet

Free format text: PAGES 1-47,DESCRIPTION,REPLACED BY NEW PAGES BEARING THE SAME NUMBER,PAGES 48-52,CLAIMS,REPLACED BYNEW PAGES BEARING THE SAME NUMBER,PAGES 1/3-3/3,DRAWINGS,REPLACED BY NEW PAGES BEARING THE SAME NUMBER;DUE TO LATE TRANSMITTAL BY THE RECEIVING OFFICE

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642