US20230364744A1 - Abrasive system and method of using the same - Google Patents

Abrasive system and method of using the same Download PDF

Info

Publication number
US20230364744A1
US20230364744A1 US18/040,712 US202118040712A US2023364744A1 US 20230364744 A1 US20230364744 A1 US 20230364744A1 US 202118040712 A US202118040712 A US 202118040712A US 2023364744 A1 US2023364744 A1 US 2023364744A1
Authority
US
United States
Prior art keywords
protrusions
abrasive
abrasive article
abrading
canceled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US18/040,712
Other languages
English (en)
Inventor
Tsukio Sato
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to US18/040,712 priority Critical patent/US20230364744A1/en
Assigned to 3M INNOVATIVE PROPERTIES COMPANY reassignment 3M INNOVATIVE PROPERTIES COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SATO, Tsukio
Publication of US20230364744A1 publication Critical patent/US20230364744A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D11/00—Constructional features of flexible abrasive materials; Special features in the manufacture of such materials
    • B24D11/02—Backings, e.g. foils, webs, mesh fabrics
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24B—MACHINES, DEVICES, OR PROCESSES FOR GRINDING OR POLISHING; DRESSING OR CONDITIONING OF ABRADING SURFACES; FEEDING OF GRINDING, POLISHING, OR LAPPING AGENTS
    • B24B1/00—Processes of grinding or polishing; Use of auxiliary equipment in connection with such processes
    • B24B1/04—Processes of grinding or polishing; Use of auxiliary equipment in connection with such processes subjecting the grinding or polishing tools, the abrading or polishing medium or work to vibration, e.g. grinding with ultrasonic frequency
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D11/00—Constructional features of flexible abrasive materials; Special features in the manufacture of such materials
    • B24D11/001—Manufacture of flexible abrasive materials

Definitions

  • Structured abrasive articles have a structured abrasive layer affixed to a backing, and are typically used in conjunction with a liquid such as, for example, water, optionally containing surfactant.
  • the structured abrasive layer has a plurality of shaped abrasive composites (typically having minute size), each having abrasive particles dispersed a binder.
  • the shaped abrasive composites are precisely shaped, for example, according to various geometric shapes (e.g., pyramids). Examples of such structured abrasive articles include those marketed under the trade designation “TRIZACT” by 3M Company, St. Paul, Minnesota.
  • Structured abrasive articles are often used in combination with a backup pad mounted to a tool (e.g., a disk sander or a random orbit sander).
  • structured abrasive articles typically have an attachment interface layer (e.g., a hooked film, looped fabric, or adhesive) that affixes them to the back up pad during use.
  • the system includes a first vibratory structure comprising a first plurality of protrusions.
  • the system also includes a second vibratory structure comprising a second plurality of protrusions.
  • the system also includes an abrasive article contacting the first film.
  • the system also includes a stroke plate coupled to the second film. When the stroke plate is activated, the first and second plurality of protrusions are configured to interlock and slip with respect to each other in a first direction.
  • Systems provided herein provide vibration to an abrasive article during an abrading operation, which increases the abrading efficiency and allows for a larger surface area to be used during a sanding operation than was available in previous systems.
  • FIG. 1 illustrates a schematic view showing the configuration of a super finishing apparatus.
  • FIGS. 2 A- 2 C illustrate schematic views of a linear vibratory finishing apparatus in accordance with embodiments herein.
  • FIGS. 3 A- 3 D illustrate schematic views of microreplicated film structures in accordance with embodiments herein.
  • FIG. 4 illustrates a method of abrading a workpiece in accordance with embodiments herein.
  • FIGS. 5 A- 5 C illustrate images of a linear vibratory finishing system in accordance with embodiments herein.
  • FIGS. 6 A- 6 B illustrates vibratory finishing systems in accordance with embodiments herein.
  • FIGS. 7 A- 7 C illustrate experimental results discussed in the Examples herein.
  • FIG. 1 is a schematic view showing the configuration of a super finishing apparatus.
  • An abrasive material product 11 is fed out of a feeding roll 12 and wound up on a rolling roll 14 via a contact roll 13 .
  • the contact roll is pushed to the outer circumferential face of the cylindrical work piece 16 by an air cylinder 15 . While the cylindrical work piece 16 is rotated in the direction of the arrow, the abrasive material product is fed to the direction opposed to the direction of movement of the object face to be abraded to carry out abrading.
  • robotic sanders utilize abrasive discs for abrasive operations.
  • Contact-wheel based sanding systems present an alternative to sanding disc systems, as they can be used in a role-to-role system and allow for a long abrasive life.
  • Contact-wheel based systems have a small contact area which can result in an applied unit pressure become too high a pressure for a given operation.
  • a system must have a holding method that allows for slippage in the direction of the feed and does not slip in the cross-direction of the feed.
  • contact wheels are not soft or flexible, which is a necessary feature for finishing surfaces with curvature or curved surfaces.
  • Soft contact wheels are not ideal because when the wheel deforms, the soft sheet wrinkles, preventing satisfactory polishing performance. In contrast, contact wheels cannot deform, which presents difficulty in finishing curved surfaces, like a hood of a car.
  • a system utilizing a soft, flexible and deformable abrasive article is desired, to handle curvature of surfaces. Additionally, a flat pad offers a larger and wider surface area. The deformation will have a smaller impact on the area of the flat pad in contact with the surface because of the softness of the article.
  • the term “soft,” with respect to an abrasive pad, is defined by JIS K 7312.
  • the C hardness means hardness immediately after a pressing surface is in close contact by a testing method specified in “Spring Hardness Test Type C Testing Method” in an appendix 2 in JIS K7312: 1996.
  • This testing method uses a spring hardness testing machine having a structure that indicates a distance of an indenter protruding from a hole at a center of the pressing surface by spring pressure being pressed to return by a test specimen when the pressing surface of the testing machine is brought into close contact with a surface of the test specimen by scale as the hardness.
  • the measured surface of the test specimen has a size at least equal to or more than the pressing surface of the testing machine.
  • the C hardness of pads described herein is as low as about 5, or as low as about 10, or as low as about 15, or as low as about 20, or as low as about 25, or as low as about 30.
  • the pads described herein may be used in either a continuous feed or an intermittent feed method.
  • a continuous feed setup dynamic friction is created. Therefore, the system may result in lower polishing performance and/or require equipment with stronger feeding power.
  • Systems and methods herein can use a roll-to-roll feeding system in either a continuous or intermediate feed operation, which presents an improvement over disc-changing systems previously used for many finishing operations. This increases efficiency with the reduced downtime required to change discs. Additionally, disc-changing systems usually see decreased cutting over time. The ability to use a roll of abrasive material results in more stable cut rates over tame, and can result in a long use-life based on the length of the roll. And with respect to existing roll-to-roll systems, the systems and methods described herein allow for a wider surface to be available for an abrading operation, with the benefit of a softer material which allows for abrading curved surfaces.
  • FIGS. 2 A- 2 C illustrate schematic views of a linear vibratory finishing apparatus in accordance with embodiments herein.
  • FIG. 2 A illustrates a perspective view of a linear vibratory finishing apparatus 100 that includes a stroke plate 110 which actuates vibratory abrasive system 150 , which abrades a surface of workpiece 130 .
  • a cushion 120 or pad may be present between stroke plate 110 and vibratory system 150 .
  • Cushion 120 may serve to increase and even out an applied pressure across a rectangular surface area of workpiece 130 .
  • the surface area may be substantially the width of an abrasive article, such as abrasive belt 156 , and may have a length as long as stroke plate 110 , in some embodiments.
  • Cushion 120 is a soft material allowing for the applied pressure to spread across a curved surface.
  • FIG. 2 C is an enlarged cutaway view 104 , which more clearly shows the components of a vibratory system 150 in an embodiment herein.
  • a first structure 152 is coupled to a stroke plate, either directly or through a cushion 120 .
  • First structure 152 is shaped to interlock with corresponding features of a second structure 154 , which contacts an abrasive article 156 .
  • abrasive article 156 may be a seamless abrasive belt fed under tension through system 100 , or may otherwise be a long abrasive article fed from roll-to-roll.
  • Abrasive article 156 may be a coated abrasive article, a nonwoven abrasive article, or a bonded abrasive article.
  • Abrasive article 156 may comprise crushed abrasive particles, formed abrasive particles, shaped abrasive particles, and/or agglomerates, composites or mixtures thereof. Abrasive article 156 , as illustrated in FIG. 2 C , contacts and abrades a surface of workpiece 130 .
  • first and second structure 152 , 154 each include a repeating pattern of substructures that interlock as illustrated in FIG. 2 C .
  • the repeating pattern of substructures may include evenly spaced protrusions, alternating hills and valleys, or a more complex structure, such as the varying heights of teeth on a key.
  • first and second structures 152 , 154 are evenly streaked microreplicated structures. Such a configuration may better cause vibrations to be transmitted mechanically during feeding as the first and second structures 152 , 154 mesh and interlock like teeth on gears. non-evenly streaked micro-replicated structures may was dynamic friction that does not transmit vibration sufficiently.
  • first and second structures 152 , 154 are formed from micro-replicated film.
  • the microreplicated film is made from a resin with flexibility and lubricity is preferable as long as the strength can be secured.
  • micro-replicated film structures 152 , 154 facilitates sanding of a larger surface area that was not previously possible using systems such as that illustrated in FIG. 1 , which provides abrading only along the contact point between roll 13 and surface 16 .
  • a contact angle of about 60° is required to secure the frictional force.
  • the abrasive article 11 In order for the contact to follow a curved surface with the diameter and contact angle, the abrasive article 11 must be elastic. However, handling stretch web is difficult. In contrast, using a pad with film structures 152 , 154 , over a large surface area, the expansion and contraction is slight even following a curved surface. While the system illustrated in FIGS. 2 A- 2 C can polish a flat surface, it presents an improved ability over prior art systems to follow curved surfaces. Cushion 120 compensates, improving the ability to manage curved surfaces. FIGS.
  • a vibratory system includes a first structure 210 and a second structure 220 that allow for movement, or slippage, along a first direction 234 , but no substantial slippage in a second direction 232 . Slippage may be facilitated by the fitting 230 between first and second structures 210 , 220 .
  • fitting 230 may include a gap allowing for freedom of movement.
  • Structure 210 in some embodiment, includes a plurality of protrusions 212 extending from a backing 214 .
  • protrusions 212 are substantially identical in height and width and spacing between adjoining protrusions.
  • protrusions 212 are of the same material as backing 214 .
  • Protrusions 212 may be coextruded, or conformed with backing 214 .
  • Structure 220 in some embodiment, includes a plurality of protrusions 222 extending from a backing 224 .
  • protrusions 222 are substantially identical in height and width and spacing between adjoining protrusions.
  • protrusions 222 are of the same material as backing 224 .
  • Protrusions 222 may be coextruded, or conformed with backing 224 .
  • fitting 230 does not include a gap
  • structure 210 is substantially identical in that dimensions of protrusions 212 are identical to dimensions of protrusions 222 .
  • each of structures 210 , 220 are defined by a width 238 and a length 236 . Slippage between structures 210 , 220 occurs substantially only in direction 234 , along the width.
  • FIGS. 3 A and 3 B illustrate substantially rectangular protrusions 212 , 222 with rounded edges, it is expressly contemplated that other micro-replicated structures are possible, as illustrated in the comparison between FIGS. 3 C and 3 D .
  • FIG. 3 C illustrates a view 250 of a pair of protrusions 260 extending from a support structure.
  • Each of protrusions 260 is identical, having a height 256 extending from the base, a width 252 , where width is substantially perpendicular to height 256 , in the embodiment illustrated in FIG. 3 C .
  • Protrusions 260 are substantially rectangular in shape, with rounded edges. However, other shapes, including a greater degree of rounding, sharp corners are also explicitly envisioned.
  • height 256 of protrusions 260 is a height of the protrusion only, and does not include a thickness of base 258 of structure 250 .
  • thickness 258 is sufficient to allow for stability of structure 250 , but thin enough to allow for some flexibility in structure 250 as protrusions 260 vibrate.
  • Protrusions 260 are spaced apart from each other by space 254 . As illustrated in FIG. 2 C , in some embodiments, space 254 is greater than width 252 , which allows for room for protrusions 260 to vibrate when in an interlocking position. In some embodiments, therefore, width 252 is less than or equal to spacing 254 . Additionally, in some embodiments, the combination of spacing 254 and width 252 is less than twice height 256 , as illustrated in Equation 1 below:
  • FIG. 3 D illustrates another configuration for protrusions 280 extending from a structure 270 with base thickness 278 .
  • Protrusions 280 have a height 276 and a total repeating width of first width 272 and second width 274 .
  • the triangular-shaped protrusions 280 are isosceles triangles, such that widths 272 and 274 are the same.
  • protrusions 280 are scalene triangles, such that widths 272 and 274 are different from each other and from a total width of protrusion 280 . Additionally, while widths 272 and 274 are presented such that no spacing (comparable to spacing 254 ) is present between adjoining protrusions, such an embodiment is expressly contemplated.
  • FIG. 3 D illustrates an embodiment where protrusions 280 have sharp corners both at their tips and where adjoining protrusions touch. However, in other embodiments, these may be rounded. In an extreme embodiment, protrusions 280 are rounded to the point of resembling sine or cosine waves.
  • the combination of width 254 and width 252 is less than twice height 256 , as illustrated in Equation 2 below:
  • FIG. 4 illustrates a method of abrading a workpiece in accordance with embodiments herein.
  • an abrasive article is coupled to a vibratory system.
  • the vibratory system in some embodiments, includes a vibration source, an abrasive feed source, and a vibration assembly.
  • the vibration assembly may include, as described above with respect to FIGS. 2 A- 2 C , opposing structures may be placed in interlocking positions 316 with respect to each other, and the abrasive article may be interact with only one of the structures, on a side opposite the plurality of protrusions.
  • Abrasive article may be moveably coupled to vibratory system, as indicated in block 312 .
  • the abrasive article may be a seamless belt that is fed through the vibratory system such that a surface area of the abrasive article in contact with a workpiece is constantly, or frequently, changing during an abrasive operation. This may include abrasive article being in a non-fixed position, as indicated in block 314 , with respect to the vibratory system.
  • the abrasive article may be a coated abrasive article that is fixed to the vibratory system, for example using a hook and loop or adhesive-based coupling.
  • a workpiece is abraded.
  • the workpiece is abraded using a surface area 332 of the abrasive article in contact with the workpiece.
  • a square or rectangular surface area of an abrasive article is available during an abrading operation, resulting in a greater area being abraded at any given time, speeding up an abrasive operation.
  • a length and width of an abrasive area may be similar, in contrast to previous systems, such as that of FIG. 1 , where the length and width of an abrading operation may differ by a factor of 5 or 10 or more.
  • Either the abrasive article or the workpiece may be fed through the vibratory system as a linear feed 334 .
  • the abrasive article may be a seamless belt fed through the system, as illustrated in the example of FIGS. 5 and 6 , presented below.
  • the abrasive article may be a coated abrasive article and the workpiece may be fed through the vibratory system.
  • the vibratory system is moved with respect to a workpiece, as described with respect to the robotic repair unit embodiment of FIG. 6 , discussed below.
  • the vibratory system vibrates during an abrading operation.
  • the vibration may be caused by stroke plate movement 332 , movement of a coupler 324 , or through another movement mechanism 326 .
  • FIGS. 5 A- 5 C illustrate images of a linear vibratory finishing system in accordance with embodiments herein.
  • FIG. 5 A illustrates a view of a system 500 , illustrating stroke directionality 510 , and feed direction 520 .
  • a stroke plate can facilitate vibration at rates at least as high as 30 strokes/min, or at least as high as 100 strokes/minute, or at least as high as 500 strokes/minute, or at least as high as 1000 strokes/minute, or at least as high as 5000 strokes/min, or at least as high as 8000 strokes/minute, or at least as high as 10,000 strokes/minute, or at least as high as 12,000 strokes/minute, or at least as high as 15,000 strokes/min.
  • the stroke is long, the number of strokes is small, and when the stroke is short, the number of strokes is large.
  • the system 500 is designed to receive an abrasive belt moving at a feed rate, in feed direction 520 , at a rate of at least 1 mm/min, at least 10 mm/min, at least 20 mm/min, at least 50 mm/min, at least 100 mm/min, at least 150 mm/min or as high as 200 mm/min.
  • FIG. 5 B illustrates a view of system 500 with an abrasive article 530 in place.
  • abrasive article is fed linearly through system 500 .
  • an entire width 532 or substantially an entire width is available for use within system 500 , allowing for a larger surface area 534 to be used during an abrading operation at a time.
  • FIG. 5 C illustrates a closer view of the feed area of system 500 , including a workpiece 540 .
  • FIGS. 6 A and 6 B illustrates vibratory finishing systems in accordance with embodiments herein.
  • FIG. 6 A illustrates a robotic repair mounted finishing system 600 that includes a vibratory finishing system 620 mounted to a robotic repair unit 610 .
  • Robotic repair unit 610 can automatically move finishing system 620 into place above a workpiece needing finishing work.
  • Vibratory finishing system 620 includes a vibratory system 622 , which may include a compressible cushion that allows system 620 to provide finishing to surfaces with curvature, such as automobile hoods, doors, etc.
  • System 622 also includes interlocking structures, such as those described with respect to FIGS. 2 - 3 , positioned in between abrasive article 630 and stroke plate 626 such that slippage can occur in the direction perpendicular to the movement of abrasive article 630 , e.g. into and out of the plane of view of FIG. 6 A .
  • Abrasive article 630 in the embodiment of FIG. 6 A , is a belt that moves from one of rolls 624 to the other during an abrasive operation.
  • the abrasive article 630 is stabilized by guides 628 which ensure that that abrasive article 630 is held tightly against vibration system 622 . This may be helpful to ensure that while the interlocking structures can move into and out of the plane of FIG. 6 A , they do not have enough free movement to fall out of alignment. Abrasive article 630 is maintained under tension during operation.
  • vibratory system 622 includes an upper and lower structure, with interlocking features that behave like gear teeth, allowing for movement in a single direction, e.g. into and out of the plane of FIG. 6 A , but not in the direction of movement of abrasive article 630 .
  • System 650 may also be mountable to a robotic repair unit, or may operate independently. As illustrated in FIG. 6 B , an abrasive article 660 is fed from a first roll 652 to a second roll 654 , under tension provided by guides 656 .
  • a vibratory system 680 is provided that, as discussed above, includes a first and second interlocking structures that allow for slippage in direction 682 , e.g. into and out of the plane of FIG. 6 B .
  • Vibratory system 680 may also include a cushion that ensures a surface area 684 of worksurface 670 is in contact with abrasive article 660 during an entirety of an abrasive operation.
  • Abrasive articles as described herein can be formed of any suitable material and can include any suitable abrasive particles.
  • Suitable backings include, for example, polymeric films (including primed polymeric film), cloth, paper, foraminous and non-foraminous polymeric foam, vulcanized fiber, fiber reinforced thermoplastic backing, meltspun or meltblown nonwovens, treated versions thereof (e.g., with a waterproofing treatment), and combinations thereof.
  • Suitable thermoplastic polymers for use in polymeric films include, for example, polyolefins (e.g., polyethylene, and polypropylene), polyesters (e.g., polyethylene terephthalate), polyamides (e.g., nylon-6 and nylon-6,6), polyimides, polycarbonates, blends thereof, and combinations thereof.
  • polyolefins e.g., polyethylene, and polypropylene
  • polyesters e.g., polyethylene terephthalate
  • polyamides e.g., nylon-6 and nylon-6,6
  • polyimides e.g., polyimides, polycarbonates, blends thereof, and combinations thereof.
  • At least one major surface of the backing is smooth (for example, to serve as the first major surface).
  • the backing may contain various additive(s).
  • suitable additives include colorants, processing aids, reinforcing fibers, heat stabilizers, UV stabilizers, and antioxidants.
  • useful fillers include clays, calcium carbonate, glass beads, talc, clays, mica, wood flour; and carbon black.
  • the backing may be a composite film such as, for example, a coextruded film having two or more discrete layers.
  • the abrasives particles may include particles of any suitable shape and composition, including crushed abrasive particles, formed abrasive particles, precision shaped abrasive particles; and/or agglomerates, mixtures or composites thereof.
  • Suitable abrasive particles for first and/or second sets of abrasive particles include: fused aluminum oxide; heat-treated aluminum oxide; white fused aluminum oxide; ceramic aluminum oxide materials such as those commercially available under the trade designation 3M CERAMIC ABRASIVE GRAIN from 3M Company, St.
  • Abrasive material that cannot be processed by a sol-gel route may be molded with a temporary or permanent binder to form shaped precursor particles which are then sintered to form shaped abrasive particles, for example, as described in U. S. Pat. Appln. Publ. No. 2016/0068729 A1 (Erickson et al.).
  • sol-gel-derived abrasive particles examples include abrasive agglomerates such, for example, as those described in U.S. Pat. No.
  • first and/or abrasive particles may be surface-treated with a coupling agent (e.g., an organosilane coupling agent) or other physical treatment (e.g., iron oxide or titanium oxide) to enhance adhesion of the abrasive particles to the binder (e.g., make and/or size layer).
  • a coupling agent e.g., an organosilane coupling agent
  • other physical treatment e.g., iron oxide or titanium oxide
  • the abrasive particles may be treated before combining them with the corresponding binder precursor, or they may be surface treated in situ by including a coupling agent to the binder.
  • first and/or second abrasive particles are ceramic abrasive particles such as, for example, sol-gel-derived polycrystalline alpha alumina particles.
  • Abrasive particles composed of crystallites of alpha alumina, magnesium alumina spinel, and a rare earth hexagonal aluminate may be prepared using sol-gel precursor alpha alumina particles according to methods described in, for example, U.S. Pat. No. 5,213,591 (Celikkaya et al.) and U. S. Pat. Appln. Publ. Nos. 2009/0165394 A1 (Culler et al.) and 2009/0169816 A1 (Erickson et al.).
  • Alpha alumina-based triangular abrasive particles can be made according to well-known multistep processes. Briefly, the method includes the steps of making either a seeded or non-seeded sol-gel alpha alumina precursor dispersion that can be converted into alpha alumina; filling one or more mold cavities having the desired outer shape of the abrasive particle with the sol-gel, drying the sol-gel to form precursor triangular abrasive particles; removing the precursor abrasive particles from the mold cavities; calcining the precursor abrasive particles to form calcined, precursor abrasive particles, and then sintering the calcined, precursor abrasive particles to form the first and/or second set of abrasive particles.
  • the process will now be described in greater detail.
  • the abrasive particles are precisely-shaped in that individual abrasive particles will have a shape that is essentially the shape of the portion of the cavity of a mold or production tool in which the particle precursor was dried, prior to optional calcining and sintering.
  • Abrasive particles used in the present disclosure can typically be made using tools (i.e., molds) cut using precision machining, which provides higher feature definition than other fabrication alternatives such as, for example, stamping or punching.
  • tools i.e., molds
  • sol-gel-derived alpha alumina (i.e., ceramic) abrasive particles can be found in U.S. Pat. No. 5,201,916 (Berg); U.S. Pat. No. 5,366,523 (Rowenhorst (Re 35,570)); and U.S. Pat. No. 5,984,988 (Berg). Details concerning such abrasive particles and methods for their preparation can be found, for example, in U.S. Pat. No.
  • Slurry derived alpha alumina abrasive particles can be found in WO 2014/070468, published on May 8, 2014.
  • Slurry derived particles may be formed from a powder precursor, such as alumina oxide powder.
  • the slurry process may be advantageous for larger particles that can be difficult to make using sol-gel techniques.
  • the abrasive particles may undergo a sintering process, such as the process described in U.S. patent Ser. No. 10/400,146, issued on Sep. 3, 2019, for example. However, other processing techniques are expressly contemplated.
  • Ultra-fine grain PSG may also be used in abrasive articles described herein. Ultra-fine grain PSG can be formed using techniques described in U.S. PAP 2019/0233693, published on Aug. 1, 2019, or in WO 2018023177, published on Dec. 20, 2018, or in WO 2018/207145, published on Nov. 15, 2018.
  • Softer PSG particles with Mohs hardness' between 2.0 and 5.0, that can be used for abrasive particles herein, particularly where non-scratch applications are anticipated, can be made according to methods described in WO 2019/215539, published on Nov. 14, 2019.
  • the shaped abrasive particles can have at least one sidewall, which may be a sloping sidewall. In some embodiments, more than one (for example two or three) sloping sidewall can be present and the slope or angle for each sloping sidewall may be the same or different. In other embodiments, the sidewall can be minimized for particles where the first and the second faces taper to a thin edge or point where they meet instead of having a sidewall.
  • the sloping sidewall can also be defined by a radius, R (as illustrated in FIG. 5 B of US Patent Application No. 2010/0151196). The radius, R, can be varied for each of the sidewalls.
  • roof-shaped particles for example particles as illustrated, in FIG. 4 A to 4 C of WO 2011/068714.
  • roof-shaped particles include particles having the shape of a hip roof, or hipped roof (a type of roof wherein any sidewalls facets present slope downwards from the ridge line to the first side.
  • a hipped roof typically does not include vertical sidewall(s) or facet(s)).
  • Shaped abrasive particles can also include a plurality of ridges on their surfaces.
  • the plurality of grooves (or ridges) can be formed by a plurality of ridges (or grooves) in the bottom surface of a mold cavity that have been found to make it easier to remove the precursor shaped abrasive particles from the mold.
  • the shaped abrasive particles may also have one or more notches on one of the faces of the abrasive particle, as described in PCT Application Ser. No. IB2019/060861, filed on Dec. 16, 2019.
  • Shaped abrasive particles can have an opening (preferably one extending or passing through the first and second side). Methods for making shaped abrasive particles having an opening are for example described in US Patent Application Publication No. 2010/0151201 and 2009/0165394.
  • Shaped abrasive particles can also have at least one recessed (or concave) face or facet; at least one face or facet which is shaped outwardly (or convex).
  • Methods for making dish-shaped abrasive particles are for example described in US Patent Application Publication Nos. 2010/0151195 and 2009/0165394. Additionally, shaped abrasive particles may also have a multifaceted surface as described in U.S. Pat. No. 10,150,900, issued on Dec. 11, 2018.
  • Shaped abrasive particles can also have at least one fractured surface.
  • Methods for making shaped abrasive particles with at least one fractured surface are for example described in US Patent Application Publication Nos. 2009/0169816 and 2009/0165394.
  • Shaped abrasive particles can also have a cavity. Shaped abrasive particles may also include an aperture, such as that described in U.S. Pat. No. 8,142,532, issued on Mar. 27, 2012, herein incorporated by reference.
  • Shaped abrasive particles can also have a low roundness factor.
  • Methods for making shaped abrasive particles with low Roundness Factor are for example described in US Patent Application Publication No. 2010/0319269.
  • Shaped abrasive particles may have a second vertex on a second side, as described in U.S. Pat. No. 9,447,311, issued on Sep. 16, 2016.
  • Methods for making abrasive particles wherein the second side is a vertex (for example, dual tapered abrasive particles) or a ridge line (for example, roof shaped particles) are for example described in U.S. PAP 2012/022733, published on Sep. 13, 2012.
  • Shaped abrasive particles may be formed to have sharp tips, such as those described in U.S. PAP 2019/0233693, published on Aug. 1, 2019, or in U.S. Provisional Application with Ser. No. 62/877,443, filed on Jul. 23, 2019.
  • Shaped abrasive particles may also be formed to include a rake angle, such as those described in WO 2019/207423, published on Oct. 31, 2019, or in WO 2019/207417, published on Oct. 31, 2019, or in PCT Application Ser. No. IB 2019/059112, filed on Oct. 24, 2019.
  • Shaped abrasive particles may also be formed to have a precision shaped portion and a non-shaped portion, such as a crushed portion, as described in U.S. Provisional Patent Application 62/833,865, filed on Apr. 15, 2019.
  • Shaped abrasive particles can also have a combination of one or more of shape features discussed herein, including a sloping sidewall, a groove, a recess, a facet, a fractured surface, a cavity, more than one vertex, sharp edges, a non-shaped portion, a notch, a rake angle and/or a low roundness factor.
  • the shaped abrasive particles may be agglomerates of shaped and/or crushed abrasive particles.
  • the term “length” refers to the maximum dimension of a triangular abrasive particle. “Width” refers to the maximum dimension of the triangular abrasive particle that is perpendicular to the length. The terms “thickness” or “height” refer to the dimension of the triangular abrasive particle that is perpendicular to the length and width. For abrasive particles with shapes other than triangles, length refers to a longest dimension, and width refers to the maximum dimension perpendicular to the length, while thickness refers to a dimension perpendicular to both the length and width.
  • the shaped abrasive particles may have an elongated shape, such as that described in U.S. PAP 2019/0106362, published on Apr. 11, 2019, or in WO 2019/069157, published on Apr. 11, 2019.
  • the elongate shape may be triangular-prism shaped, rod-shaped, or otherwise including one or more vertices along the perimeter.
  • the shaped abrasive particles may have a variable cross-sectional area along a length of the particle, such as those described in U.S. PAP 2019/0249051.
  • the shaped abrasive particles may be dog-bone shaped, or otherwise have a cross sectional area that varies from a first end to a second end.
  • the shaped abrasive particles may have a tetrahedron shape, such as those described in WO 2018/207145, published on Nov. 15, 2018, or those of U.S. Pat. No. 9,573,250, issued on Feb. 21, 2017.
  • the shaped abrasive particles may also have a concave or convex portion, or may be defined as having one or more acute interior angles, such as those described in U.S. Pat. No. 10,301,518, issued on May 28, 2019.
  • the shaped abrasive particles may also include shape-on-shape particles, such as a plate on plate shaped particle as described in U.S. Pat. No. 8,728,185, issued on May 20, 2014.
  • the shaped abrasive particles may also include shaped abrasive particles that have an irregular polygonal shape, as described in U.S. Provisional Patent Application 62/924,956, filed on Oct. 23, 2019.
  • the shaped abrasive particles may also be shaped to be self-standing abrasive particles, such that cutting portions are more likely to embed in a make coat, for example, in an orientation away from the backing, such as those described in PCT Application with Ser. No. IB 2019/060457, filed on Dec. 4, 2019.
  • the shaped abrasive particles can also be aggregate particles.
  • the aggregate particles may include shaped abrasive particles in a vitreous bond matrix as described, for example, in U.S. PAP 2018/081246, published on May 3, 2018.
  • the aggregate particles may also include shaped abrasive particles in a silicate binder, as described in WO 2019/167022, published on Sep. 6, 2019.
  • the aggregate particles may also include frustro-pyrimidal shaped particles in a vitreous bond matrix, as described in US PAP 2019/0283216, published on Sep. 19, 2019.
  • the aggregate may also include a mixture of crushed and shaped particles, as described in PCT Publication IB/2019/058349, filed on Oct. 1, 2019.
  • the abrasive grain may have a surface treatment thereon.
  • the surface treatment may increase adhesion to the binder, alter the abrading characteristics of the abrasive particle, or the like.
  • Examples of surface treatments include coupling agents, halide salts, metal oxides including silica, refractory metal nitrides, and refractory metal carbides.
  • the abrasive layer may also comprise diluent particles, typically on the same order of magnitude as the abrasive particles.
  • diluent particles include gypsum, marble, limestone, flint, silica, glass bubbles, glass beads, and aluminum silicate.
  • Abrasive articles and vibratory finishing systems described herein may be suitable for a variety of workpieces having material and may have any form.
  • materials include metal, metal alloys, exotic metal alloys, ceramics, painted surfaces, plastics, polymeric coatings, stone, polycrystalline silicon, wood, marble, and combinations thereof.
  • workpieces include molded and/or shaped articles (e.g., optical lenses, automotive body panels, boat hulls, counters, and sinks), wafers, sheets, and blocks.
  • the force at the abrading interface can range from about 0.1 kg to over 1000 kg. Generally, this range is between 1 kg to 500 kg of force at the abrading interface.
  • a liquid present during abrading can be water and/or an organic compound. Examples of typical organic compounds include lubricants, oils, emulsified organic compounds, cutting fluids, surfactants (e.g., soaps, organosulfates, sulfonates, organophosphonates, organophosphates), and combinations thereof. These liquids may also contain other additives such as defoamers, degreasers, corrosion inhibitors, and combinations thereof.
  • An abrading system includes a first vibratory structure comprising a first plurality of protrusions, a second vibratory structure comprising a second plurality of protrusions, an abrasive article contacting the first film, and a stroke plate coupled to the second film.
  • the stroke plate When the stroke plate is activated, the first and second plurality of protrusions are configured to interlock and slip with respect to each other in a first direction.
  • the abrading system may be implemented such that the abrasive article is a rolled sheet of abrasive fed through the abrading system in a feeding direction.
  • the feeding direction is perpendicular to the first direction.
  • the abrading system may be implemented such that the abrasive article is a coated abrasive article, a bonded abrasive article or a nonwoven abrasive article.
  • the abrading system may be implemented such that the abrasive article includes abrasive particles.
  • the abrasive particles include crushed, formed, or shaped abrasive particles.
  • the abrading system may be implemented such that the first plurality of protrusions include a shaped protrusion repeating along a surface of the first vibratory structure.
  • the abrading system may be implemented such that the shaped protrusion repeats along the surface of the first vibratory structure at regular intervals.
  • the abrading system may be implemented such that the regular intervals include a space length between adjacent protrusions that is greater than a protrusion width.
  • the abrading system may be implemented such that a sum of the regular interval and the protrusion width is less than or equal to twice a height of the shaped protrusion.
  • the abrading system may be implemented such that the shaped protrusion is a rectangular shaped protrusion.
  • the abrading system may be implemented such that the shaped protrusion includes a triangular shaped protrusion.
  • the abrading system may be implemented such that the shaped protrusion has a rounded corner.
  • the abrading system may be implemented such that the first and second vibratory structures include microreplicated film.
  • the abrading system may be implemented such that the microreplicated film includes a resin.
  • the abrading system may be implemented such that the microreplicated film includes a polyolefin.
  • the abrading system may be implemented such that it includes a compressible pad between the stroke plate and the second vibratory structure.
  • a robotic repair system includes an abrading system with a vibration source, a first structure, with a first interlocking feature, coupled to the vibration source, and a second structure, with a second interlocking feature interlocked to the first locking feature.
  • the first and second structures are configured to, when interlocked, slip in a first direction.
  • An abrasive article contacts the second structure on a second side opposite a first side that contacts the first structure.
  • the abrading system also includes a robotic repair unit configured to move the abrading system into position over a workpiece and a mount that couples the abrading system to the robotic repair unit.
  • the robotic repair system may be implemented such that the abrasive article is an abrasive belt.
  • the abrading system also includes a belt feeder that feeds the belt in between the second structure and the workpiece, in a feed direction. The feed direction is different from the first direction.
  • the robotic repair system may be implemented such that the feed direction is perpendicular to the first direction.
  • the robotic repair system may be implemented such that, during an abrasive operation, a surface area of the abrasive belt contacts the workpiece.
  • the surface area of the abrasive article includes a dimension of the second structure and a width of the abrasive belt.
  • the robotic repair system may be implemented such that the abrasive belt is fed from a first belt roll to a second belt roll.
  • the robotic repair system may be implemented such that it also includes a cushion in between the vibration source and the first structure.
  • the robotic repair system may be implemented such that the vibration source is a stroke plate.
  • the robotic repair system may be implemented such that the abrasive article is an abrasive pad coupled to the second structure.
  • the robotic repair system may be implemented such that the abrasive article includes abrasive particles.
  • the abrasive particles include crushed, formed or shaped abrasive particles.
  • the robotic repair system may be implemented such that the abrasive article is a coated, bonded or nonwoven abrasive article.
  • the robotic repair system may be implemented such that the first and second interlocking features are micro-replicated features.
  • the robotic repair system may be implemented such that the first and second interlocking features each include a plurality of protrusions extending from a base surface.
  • the robotic repair system may be implemented such that, when in an interlocking position, a plurality of spaces are present between the first and second interlocking features.
  • the robotic repair system may be implemented such that the plurality protrusions include a repeating shape.
  • the robotic repair system may be implemented such that the repeating shape is rectangular or triangular.
  • the robotic repair system may be implemented such that the repeating shape is a polygon adjacent a space.
  • the robotic repair system may be implemented such that the length of the repeating shape is less than or equal to twice a height of the repeating shape.
  • a method of abrading a surface that includes coupling an abrasive article to an abrading system.
  • the abrading system includes a vibration source and a first structure coupled to the vibration source.
  • the first structure includes a first plurality of protrusions extending from a first base.
  • the abrading system also includes a second structure comprising a second plurality of protrusions, extending from a second base. The second plurality of protrusions interlock with the first plurality of protrusions.
  • the abrasive article is coupled to the second structure.
  • the method also includes actuating the abrading system. Actuating the abrading system causes the first and second plurality of protrusions to slip with respect to each other in a first direction.
  • the method may be implemented such that it also includes causing the abrasive article to move with respect to the workpiece in a feed direction.
  • the method may be implemented such that the workpiece remains stationary, the abrasive article is physically attached to the second structure, and causing the abrasive article to move includes moving the abrading system using a robotic repair unit.
  • the method may be implemented such that the workpiece remains stationary, the abrasive article is an abrasive belt.
  • Causing the abrasive article to move includes feeding the abrasive belt, under tension, from a feed roll to a rolling roll.
  • the method may be implemented such that a feeding direction is opposite the first direction.
  • the first and second plurality of protrusions substantially prohibit slippage in the feeding direction.
  • the method may be implemented such that the first plurality of protrusions are micro-replicated.
  • the method may be implemented such that the first plurality of protrusions are machined into the first structure.
  • the method may be implemented such that the first plurality of protrusions are formed of the same material as the first base.
  • the method may be implemented such that the first plurality of protrusions are integral to the first base.
  • the method may be implemented such that the first plurality of protrusions have a first protrusion height, the second plurality of protrusions have a second protrusion height, and the first and second protrusions heights are the same.
  • the method may be implemented such that the first and second plurality of protrusions interlock such that gaps are present between adjacent protrusions.
  • the method may be implemented such that the first plurality of protrusions are polygonal in shape.
  • the method may be implemented such that the polygonal shape is substantially rectangular or substantially triangular.
  • the method may be implemented such that the vibration source is a stroke plate.
  • the method may be implemented such that a cushion is present between the vibration source and the first structure.
  • An abrasive article that includes a substrate longer in a first direction than a second direction.
  • the abrasive article also includes a plurality of protrusions on the substrate.
  • the protrusions extend in the second direction.
  • the protrusions are in a repeating pattern on the substrate.
  • the abrasive article may be implemented such that the substrate has a first side, comprising the protrusions, and a second side.
  • the second side includes a plurality of abrasive particles configured to contact a work surface.
  • the abrasive article may be implemented such that the substrate has a first side, comprising the protrusions, and a second side.
  • the second side contacts a cushion.
  • the abrasive article may be implemented such that the abrasive article is a coated abrasive article, a bonded abrasive article or a nonwoven abrasive article.
  • the abrasive article may be implemented such that the abrasive article includes abrasive particles.
  • the abrasive particles include crushed, formed, or shaped abrasive particles.
  • the abrasive article may be implemented such that the repeating pattern includes a space length between adjacent protrusions that is greater than a protrusion width.
  • the abrasive article may be implemented such that a length of a first edge of a first protrusion and a corresponding first edge of a second protrusion is less than or equal to twice a height of the shaped protrusion.
  • the abrasive article may be implemented such that abrasive article is rolled around a core.
  • the abrasive article may be implemented such that the abrasive article is on the core side.
  • the abrasive article may be implemented such that the protrusions are on the core side.
  • FIGS. 7 A- 7 C illustrate experimental results discussed in the Examples herein.
  • An abrasive was obtained from 3M company, model 373L, 30 mic.
  • the workpiece was an SUS 304.
  • the machine illustrated in FIGS. 5 A- 5 C was used, and the abrasive article was handfed through the machine.
  • the pad size was 25 mm ⁇ 50 mm ⁇ 10 mm in height.
  • a sponge was used as the pad to provide cushion.
  • a load of 15.7N was applied.
  • FIG. 7 A illustrates the cut rate comparing a pad as described above, labeled as “Example A” compared to a traditional pad.
  • FIG. 7 B illustrates the pad of Example A after a grinding operation with vibratory scratching
  • FIG. 7 C illustrates the pad of Example A with feeding scratch only. More abrading is illustrated when the vibrations are observed.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Polishing Bodies And Polishing Tools (AREA)
  • Grinding And Polishing Of Tertiary Curved Surfaces And Surfaces With Complex Shapes (AREA)
  • Finish Polishing, Edge Sharpening, And Grinding By Specific Grinding Devices (AREA)
US18/040,712 2020-08-10 2021-07-19 Abrasive system and method of using the same Pending US20230364744A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US18/040,712 US20230364744A1 (en) 2020-08-10 2021-07-19 Abrasive system and method of using the same

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US202062706322P 2020-08-10 2020-08-10
US18/040,712 US20230364744A1 (en) 2020-08-10 2021-07-19 Abrasive system and method of using the same
PCT/IB2021/056504 WO2022034397A1 (fr) 2020-08-10 2021-07-19 Système d'abrasion et son procédé d'utilisation

Publications (1)

Publication Number Publication Date
US20230364744A1 true US20230364744A1 (en) 2023-11-16

Family

ID=77021688

Family Applications (1)

Application Number Title Priority Date Filing Date
US18/040,712 Pending US20230364744A1 (en) 2020-08-10 2021-07-19 Abrasive system and method of using the same

Country Status (4)

Country Link
US (1) US20230364744A1 (fr)
EP (1) EP4192650A1 (fr)
JP (1) JP2023537084A (fr)
WO (1) WO2022034397A1 (fr)

Family Cites Families (48)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4314827A (en) 1979-06-29 1982-02-09 Minnesota Mining And Manufacturing Company Non-fused aluminum oxide-based abrasive mineral
US4623364A (en) 1984-03-23 1986-11-18 Norton Company Abrasive material and method for preparing the same
CA1254238A (fr) 1985-04-30 1989-05-16 Alvin P. Gerk Procede sol-gel pour l'obtention de grains d'abrasif et de produits abrasifs ceramiques durables a base d'alumine
US4652275A (en) 1985-08-07 1987-03-24 Minnesota Mining And Manufacturing Company Erodable agglomerates and abrasive products containing the same
US4770671A (en) 1985-12-30 1988-09-13 Minnesota Mining And Manufacturing Company Abrasive grits formed of ceramic containing oxides of aluminum and yttrium, method of making and using the same and products made therewith
US4799939A (en) 1987-02-26 1989-01-24 Minnesota Mining And Manufacturing Company Erodable agglomerates and abrasive products containing the same
US4881951A (en) 1987-05-27 1989-11-21 Minnesota Mining And Manufacturing Co. Abrasive grits formed of ceramic containing oxides of aluminum and rare earth metal, method of making and products made therewith
US5152917B1 (en) 1991-02-06 1998-01-13 Minnesota Mining & Mfg Structured abrasive article
US5366523A (en) 1992-07-23 1994-11-22 Minnesota Mining And Manufacturing Company Abrasive article containing shaped abrasive particles
US5201916A (en) 1992-07-23 1993-04-13 Minnesota Mining And Manufacturing Company Shaped abrasive particles and method of making same
US5213591A (en) 1992-07-28 1993-05-25 Ahmet Celikkaya Abrasive grain, method of making same and abrasive products
US5435816A (en) 1993-01-14 1995-07-25 Minnesota Mining And Manufacturing Company Method of making an abrasive article
CA2113318A1 (fr) * 1993-01-28 1994-07-29 Robert J. Jantschek Accessoire abrasif pour appareil d'abrasion rotatif
WO1995007797A1 (fr) 1993-09-13 1995-03-23 Minnesota Mining And Manufacturing Company Article abrasif, son procede de fabrication, son procede d'utilisation pour la finition, et outil de production
US5975987A (en) 1995-10-05 1999-11-02 3M Innovative Properties Company Method and apparatus for knurling a workpiece, method of molding an article with such workpiece, and such molded article
US5946991A (en) 1997-09-03 1999-09-07 3M Innovative Properties Company Method for knurling a workpiece
US8123828B2 (en) 2007-12-27 2012-02-28 3M Innovative Properties Company Method of making abrasive shards, shaped abrasive particles with an opening, or dish-shaped abrasive particles
WO2009085841A2 (fr) 2007-12-27 2009-07-09 3M Innovative Properties Company Particules abrasives formées fracturées, article abrasif les utilisant, et leur procédé de fabrication
US10137556B2 (en) 2009-06-22 2018-11-27 3M Innovative Properties Company Shaped abrasive particles with low roundness factor
US8142532B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with an opening
US8142891B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Dish-shaped abrasive particles with a recessed surface
RU2506152C2 (ru) 2008-12-17 2014-02-10 3М Инновейтив Пропертиз Компани Фасонные абразивные частицы с канавками
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
EP2507013B1 (fr) 2009-12-02 2019-12-25 3M Innovative Properties Company Particules abrasives façonnées à effilement double
CN102858496B (zh) 2010-04-27 2016-04-27 3M创新有限公司 陶瓷成形磨粒及其制备方法以及包含陶瓷成形磨粒的磨具制品
DE102010038351B4 (de) 2010-07-23 2020-09-03 Robert Bosch Gmbh Verfahren und Vorrichtung zum Betreiben eines hybriden Antriebssystems
CN103025490B (zh) 2010-08-04 2016-05-11 3M创新有限公司 相交平板成形磨粒
WO2013151745A1 (fr) 2012-04-04 2013-10-10 3M Innovative Properties Company Particules abrasives, procédé de fabrication de particules abrasives et articles abrasifs
PL2914402T3 (pl) 2012-10-31 2021-09-27 3M Innovative Properties Company Ukształtowane cząstki ścierne oraz wyroby ścierne obejmujące sposoby ich wytwarzania
EP2981378B1 (fr) 2013-04-05 2021-06-30 3M Innovative Properties Company Particules abrasives frittées, leur procédé de fabrication et articles abrasifs les comprenant
KR20160148590A (ko) 2014-04-21 2016-12-26 쓰리엠 이노베이티브 프로퍼티즈 컴파니 연마 입자 및 이를 포함하는 연마 용품
WO2016085791A1 (fr) * 2014-11-26 2016-06-02 3M Innovative Properties Company Articles abrasifs, ensembles et procédés avec matériau de saisie
WO2016194269A1 (fr) 2015-05-29 2016-12-08 パナソニック液晶ディスプレイ株式会社 Dispositif d'affichage à cristaux liquides
EP3904002B1 (fr) 2016-04-01 2023-01-25 3M Innovative Properties Company Articles abrasifs comprenant des particules abrasives de forme allongée
WO2018017695A1 (fr) 2016-07-20 2018-01-25 3M Innovative Properties Company Agglomérat abrasif vitrifié façonné, articles abrasifs et procédé d'abrasion
BE1024462B1 (nl) 2016-08-01 2018-03-05 Atlas Copco Airpower Naamloze Vennootschap Vloeistofgeïnjecteerd compressor- of expanderelement en werkwijze voor het regelen van de vloeistofinjectie van een compressor- of expanderinrichting
EP3491091A4 (fr) 2016-08-01 2020-07-22 3M Innovative Properties Company Particules abrasives profilées à extrémités pointues
EP3516006A4 (fr) 2016-09-21 2020-03-18 3M Innovative Properties Company Particule abrasive présentant des caractéristiques de rétention améliorées
JP2020519468A (ja) 2017-05-12 2020-07-02 スリーエム イノベイティブ プロパティズ カンパニー 研磨物品中の四面体研磨粒子
JP7086550B2 (ja) 2017-09-19 2022-06-20 東洋アルミニウム株式会社 太陽電池モジュールの設置方法
US10911849B2 (en) 2017-09-20 2021-02-02 Mitek Corp., Inc. Direct fire small ceiling speaker system
US20200233905A1 (en) 2017-09-24 2020-07-23 Domo, Inc. Systems and Methods for Data Analysis and Visualization Spanning Multiple Datasets
US20200283502A1 (en) 2017-09-25 2020-09-10 Pepticom Ltd. Positive allosteric modulators of gaba a receptor
CN113174235A (zh) 2017-10-02 2021-07-27 3M创新有限公司 细长磨料颗粒、其制备方法以及包含细长磨料颗粒的磨料制品
CN112055737B (zh) 2018-03-01 2022-04-12 3M创新有限公司 具有成型磨料颗粒的成型硅质磨料团聚物、磨料制品及相关方法
WO2019207423A1 (fr) 2018-04-24 2019-10-31 3M Innovative Properties Company Article abrasif doté de particules abrasives façonnées dotées d'angles de coupe prédéterminés
US20210046612A1 (en) 2018-04-24 2021-02-18 3M Innovative Properties Company Method of making a coated abrasive article
EP3790439A1 (fr) 2018-05-10 2021-03-17 3M Innovative Properties Company Composition anti-rayures et article de nettoyage abrasif

Also Published As

Publication number Publication date
EP4192650A1 (fr) 2023-06-14
WO2022034397A1 (fr) 2022-02-17
JP2023537084A (ja) 2023-08-30

Similar Documents

Publication Publication Date Title
US7410413B2 (en) Structured abrasive article and method of making and using the same
US8425278B2 (en) Structured abrasive article and method of using the same
US11097398B2 (en) Abrasive article and method of making the same
US20220339761A1 (en) Coated abrasive articles and method of making the same
US8444458B2 (en) Plasma treated abrasive article and method of making same
US20230226664A1 (en) Composite abrasive article, and method of making and using the same
KR100494605B1 (ko) 유리상에 투명한 표면 마무리 상태를 제공하기 위한 연마용품
EP2176031B1 (fr) Abrasif structuré ayant une couche de recouvrement et procédé de fabrication et d'utilisation de celui-ci
US7258705B2 (en) Abrasive article and methods of making same
US20070066186A1 (en) Flexible abrasive article and methods of making and using the same
KR20060101791A (ko) 유리를 연삭하는 방법
EP2598291A1 (fr) Manique abrasive hybride et procédé d'abrasion d'une surface
WO2014197551A2 (fr) Procédé de formation d'un évidement dans un substrat, meule abrasive, et couvercle
US20230364744A1 (en) Abrasive system and method of using the same
EP3204190B1 (fr) Article abrasif texturé et procédés associés
US20190264082A1 (en) Structured abrasive article including features with improved structural integrity
CN213136220U (zh) 研磨工具和包括该研磨工具的组件
US12128526B2 (en) Conformable abrasive article
US20230166384A1 (en) Abrasive body and method of making the same
US20210114171A1 (en) Conformable abrasive article
CN112428098A (zh) 研磨工具、包括该研磨工具的组件和抛光基板的方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: 3M INNOVATIVE PROPERTIES COMPANY, MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SATO, TSUKIO;REEL/FRAME:062601/0885

Effective date: 20220303

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION