US20220362774A1 - Microfluidic chips with one or more vias - Google Patents
Microfluidic chips with one or more vias Download PDFInfo
- Publication number
- US20220362774A1 US20220362774A1 US17/813,954 US202217813954A US2022362774A1 US 20220362774 A1 US20220362774 A1 US 20220362774A1 US 202217813954 A US202217813954 A US 202217813954A US 2022362774 A1 US2022362774 A1 US 2022362774A1
- Authority
- US
- United States
- Prior art keywords
- vias
- device layer
- microfluidic
- equal
- silicon device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Microfluidic chips that can comprise thin substrates and/or a high density of vias are described herein. An apparatus comprises: a silicon device layer comprising a plurality of vias, the plurality of vias comprising greater than or equal to about 100 vias per square centimeter of a surface of the silicon device layer and less than or equal to about 100,000 vias per square centimeter of the surface of the silicon device layer, and the plurality of vias extending through the silicon device layer; and a sealing layer bonded to the silicon device layer, wherein the sealing layer has greater rigidity than the silicon device layer. In some embodiments, the silicon device layer has a thickness between about 7 micrometers and about 500 micrometers while a via of the plurality of vias has a diameter between about 5 micrometers and about 5 millimeters.
Description
- The subject disclosure relates to microfluidic chips, and more specifically, to microfluidic chips that can comprise thin substrates and/or a high density of vias.
- Extensive and growing interest in lab-on-a-chip (“LOC”) technologies is evident from the tens of thousands of currently available in literature from close-system microfluidic publications alone. Such a broad interest in microfluidic technologies is representative of their many advantages over traditional laboratory methods, such as the ability to carry out separation and detection with high resolution and sensitivity, need for only very small quantities of sample and reagent, small footprint of the analytical devices these chips contain, low cost of manufacture, and short time of analysis.
- With such great potential benefits, a number of material options and techniques have been explored to integrate microfluidic features and devices to separate, detect, and manipulate biological analytes. For microfluidic applications requiring high-density parallelization, biological samples and other fluids introduced into a silicon chip must have exit points, or fluidic outlets, at a high packing density to collect material. When fluidic vias are integrated at low density, structured glass (glass with holes) can be bonded to silicon as a last process step or defined in thermoplastics; however, at high density, wherein hundreds or thousands of vias are required at small sizes (e.g., 50 micrometers (μm) diameters or less), these standard options are no longer possible, either physically (e.g., in silicon due difficulties of etching through the thickness of a standard 200 millimeter (mm) or 300 mm wafer) or practically from a cost perspective (e.g., due to structured glass manufacturing limitations). Therefore, a method of manufacturer is required that can accomplish this feat to enable applications that require a high density of vias (e.g., nanoscale deterministic lateral displacement (“nanoDLD”) arrays) for separating particles (e.g., exosomes).
- A key challenge for LOC manufacturing in silicon, when high-density vias are implemented into a design, is to make the vias fluidically accessible and eliminate downstream wets processing common in semiconductor manufacturing, such as wet cleans. Wet processes can wick these fluids into the microfluidic device through capillary action, rendering the device unusable.
- The following presents a summary to provide a basic understanding of one or more embodiments of the invention. This summary is not intended to identify key or critical elements, or delineate any scope of the particular embodiments or any scope of the claims. Its sole purpose is to present concepts in a simplified form as a prelude to the more detailed description that is presented later. In one or more embodiments described herein, apparatuses, methods, and/or systems regarding microfluidic chips with high via density are described.
- According to an embodiment, an apparatus is provided. The apparatus can comprise a silicon device layer, which can comprise a plurality of vias. The plurality of vias can comprise greater than or equal to about 100 vias per square centimeter of a surface of the silicon device layer and less than or equal to about 100,000 vias per square centimeter of the surface of the silicon device layer. Also, the plurality of vias can extend through the silicon device layer. The apparatus can also comprise a sealing layer bonded to the silicon device layer, which can have greater rigidity than the silicon device layer.
- According to an optional embodiment, the apparatus can further comprise a microfluidic element that can be located on a second surface of the silicon device layer. The microfluidic element can be in fluid communication with a via of the plurality of vias. Also, the microfluidic element can be encapsulated by a combination of the silicon device layer and the sealing layer.
- According to another embodiment, a method is provided. The method can comprise defining a microfluidic element on a first surface of a device layer. The method can also comprise bonding a sealing layer to the first surface of the device layer. A combination of the sealing layer and the device layer can encapsulate the microfluidic element. The method can further comprise forming, after the bonding, a via within the device layer. The via can extend from a second surface of the device layer to a first surface of the device layer. Also, the second surface can be located on an opposite side of the device layer than the first surface. In one or more embodiments, the method can further comprise thinning the device layer after the bonding and before the forming of the via.
- According to another embodiment, an apparatus is provided. The apparatus can comprise a silicon device layer comprising a via and a microfluidic device. The via can extend through the silicon device layer and can be in fluid communication with the microfluidic device. Also, the silicon device layer can have a thickness greater than or equal to about 7 micrometers and less than or equal to about 500 micrometers. The apparatus can also comprise a sealing layer bonded to the silicon device layer. The sealing layer can have greater rigidity than the silicon device layer.
- According to an optional embodiment, the via can be comprised within a plurality of vias. The plurality of vias can comprise greater than or equal to about 100 vias and less than or equal to about 100,000 vias per square centimeter of a surface of the silicon device layer opposite to the sealing layer.
- Thus, various embodiments described herein can provide a manufacturable structure and approach to create LOC technologies with high-density microfluidic vias. It is useful, for example, for LOC technologies that require high-throughput sample preparation. Also, one or more methods described herein can provide a means of protecting sealed microfluidic features from downstream wets processing (e.g., by opening vias last to make microfluidic features accessible using a final dry process).
-
FIG. 1 illustrates a diagram of an example, non-limiting microfluidic chip that can comprise a high density of vias in accordance with one or more embodiments described herein. -
FIG. 2 illustrates a photo of an example, non-limiting wafer containing microfluidic chips that can comprise a high density of vias in accordance with one or more embodiments described herein. -
FIG. 3 illustrates another photo of an example, non-limiting microfluidic chip that can comprise a high density of vias in accordance with one or more embodiments described herein. -
FIG. 4 illustrates a flow diagram of an example, non-limiting method that can facilitate manufacturing a microfluidic chip that can comprise a high density of vias in accordance with one or more embodiments described herein. -
FIG. 5 illustrates a diagram of an example, non-limiting microfluidic chip at a first stage of manufacturing in accordance with one or more embodiments described herein. -
FIG. 6 illustrates a diagram of an example, non-limiting microfluidic chip at a second stage of manufacturing in accordance with one or more embodiments described herein. -
FIG. 7 illustrates a diagram of an example, non-limiting microfluidic chip at a third stage of manufacturing in accordance with one or more embodiments described herein. -
FIG. 8 illustrates a diagram of an example, non-limiting microfluidic chip at a fourth stage of manufacturing in accordance with one or more embodiments described herein. -
FIG. 9 illustrates a diagram of an example, non-limiting microfluidic chip at a fifth stage of manufacturing in accordance with one or more embodiments described herein. -
FIG. 10 illustrates a diagram of an example, non-limiting microfluidic chip that can comprise a high density of vias in accordance with one or more embodiments described herein. - The following detailed description is merely illustrative and is not intended to limit embodiments and/or application or uses of embodiments. Furthermore, there is no intention to be bound by any expressed or implied information presented in the preceding Background or Summary sections, or in the Detailed Description section.
- One or more embodiments are now described with reference to the drawings, wherein like referenced numerals are used to refer to like elements throughout. In the following description, for purposes of explanation, numerous specific details are set forth in order to provide a more thorough understanding of the one or more embodiments. It is evident, however, in various cases, that the one or more embodiments can be practiced without these specific details.
-
FIG. 1 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 in accordance with one or more embodiments described herein. Themicrofluidic chip 100 can comprise one ormore vias 102, asealing layer 104, one ormore buses 106, one or moremicrofluidic elements 108, and/or adevice layer 110. In one or more embodiments, themicrofluidic chip 100 can comprise a high density ofvias 102 within thedevice layer 110. In some embodiments, themicrofluidic chip 100 can comprise athin device layer 110 and/or one ormore vias 102 in fluid communication with the one or moremicrofluidic elements 108, which can be characterized by one or more dimensions that are greater than or equal to 1 nanometer and less than or equal to 10 millimeters. Thesealing layer 104 and/or thedevice layer 110 can respectively comprise silicon (e.g., silicon compositions), glass, a combination thereof, and/or the like. - Silicon is a well-established material in fabrication methods that can utilize subtractive (e.g. wet or dry etching) or additive methods (e.g. metal or chemical vapor deposition) to create microfluidic structures with nanoscale placement and features. High elastic modulus (e.g., characterized by 130-180 gigapascals (GPa)) can form rigid well-defined structures. Silanol group (—Si—OH) surface chemistry is well developed (e.g., surface modification with silanes). Further, silicon's ability to scale and integrate to provide complex functionality can be very high. However, silicon is not transparent to visible light, so typical fluorescence detection or fluid imaging is challenging; although this can be overcome by bonding a transparent material to the surface of silicon, such as a polymer or glass. Also, silicon's high elastic modulus can make silicon difficult to be made into active fluidic components such as valves and pumps.
- Glass fabrication methods exist that can utilize subtractive or additive methods to create microfluidic structures albeit not at the precision and scale of silicon. Glass can have low background fluorescence, and like silicon, can have silanol-based surface modification chemistries readily available. Also, glass can be compatible with biological samples, can have relatively low nonspecific adsorption, and can be gas impermeable. However, compared to silicon, glass fabrication methods are not nearly as broad or precise (e.g., nanoscale features for microfluidics that are possible in silicon can be difficult to implement in glass). Glass can also have a large, composition-dependent elastic modulus (e.g., hybrid devices can be required for active components such as valves and pumps).
- Other materials that conventionally comprise microfluidic chip technologies can include ceramics, elastomers, thermoplastics, and/or paper. However, one or more embodiments of the
microfluidic chips 100 described herein can comprise silicon and/or glass materials due at least in part to one or more structural and/or manufacturing difficulties ceramics, elastomers, thermoplastics, and/or paper can exhibit in microfluidic platforms. For example, low-temperature cofired ceramics (“LTCC”) can be fabricated into complex three-dimensional devices, wherein each layer can be inspected for quality control before assembling. Electrodes can be deposited using expansion matched metal pastes (e.g., for added functionality for detection and separation). Also, organically modified ceramics can provide an optically transparent, UV-curable material. However, high-density ceramic electronics and multiplexed or integrated ceramic architectures can be difficult to implement. Further, features such as electrodes and channels can typically be 10's to 100's of microns in size and. not adaptable to certain types of microfluidic elements such as smaller pillar arrays or nanochannels. Also, ceramics can have a high elastic modulus, thereby rendering ceramics difficult to be made into active fluidic components such as valves and pumps. Moreover, ceramics can be difficult to hybridize with other materials. - Regarding elastomers, polydimethylsiloxane (“PDMS”) can be low in cost and is perhaps the most common microfluidic substrate. Elastomers can be easy to fabricate using a number of processes, including conventional machining and photolithography, and elastomers can be cast, stamped, and cured on molds. Elastomers can have low elastic modulus (e.g., 300-500 kilopascals (kPa)), thereby making them useful for making values and pumps. PDMS can be gas permeable and thereby useful for oxygen and/or carbon dioxide transport in cellular studies. Also, elastomers can be transparent in the visible range, so typical fluorescence detection or fluid imaging can be employed. However, since PDMS can be gas permeable, it can cause problematic bubble formation. Also, PDMS can be a hydrophobic material and thereby susceptible to nonspecific adsorption and permeation by hydrophobic molecules. Other example elastomers can include, but are not limited to: thermoset polyester (“TPE”), polyfluoropolyether diol methacrylate (“PFPE-DMA”), and/or polystyrene (“PS”).
- Further, thermoplastics can be highly moldable and manufacturable given they are durable, amenable to micromachining, hot embossing, and injection molding processes. Thermoplastics can be optically clear, resistant to permeation of small molecules, and stiffer than elastomers. Also, thermoplastics can be thermally, and/or laser, bonded to seal two layers together. For example, cyclic-olefin copolymer (“COC”) can be suitable for use with most solvents and aqueous solutions and can have low background fluorescence. Further, thermoplastics can have low manufacturing costs. However, COC can be hydrophobic, and thereby require surface modification to reduce nonspecific adsorption. Also, thermoplastics can typically require another medium (e.g., a master mold) to replicate many devices (e.g. silicon master).
- Moreover, paper can be extremely cheap and readily available, can be disposed of by burning or natural degradation, and can be easily patterned and functionalized. Porous paper can allow for a combination of flow, filtering, and separation. Also, paper can be biologically compatible and chemically modified through composition or formulation changes or by implementing surface chemistry. However, paper can rely on passive capillary action for operation, and thereby paper system may not be amenable to more complex functionality or material hybridization.
- Considerations regarding the selection of materials comprising the
sealing layer 104 and/or thedevice layer 110 can include, but are not limited to: the required function of the layers, the degree ofmicrofluidic element 108 integration needed on the layers, and/or the final application of themicrofluidic chip 100. In one or more embodiments, the choice of silicon and/or silicon-glass systems are most attractive in LOC applications requiring high-density device integration, parallelization, multi-functional or multi-device arrangements (separation and detection, for example) or in application requiring embedded microelectronics. For example, thesealing layer 104 can comprise glass and thedevice layer 110 can comprise silicon (e.g., a crystalline silicon such as a silicon wafer). In an embodiment in which thedevice layer 110 comprises silicon, high pressures can be applied to themicrofluidic element 108 as a driving force to operate themicrofluidic chip 100 without deforming the structures. - The
sealing layer 104 can be bonded to thedevice layer 110. Thesealing layer 104 can have greater rigidity that thedevice layer 110, thereby providing enhanced rigidity to thedevice layer 110 during manufacturing of themicrofluidic chip 100. Further, thesealing layer 104 can encapsulate the one or moremicrofluidic elements 108 and/or the one ormore buses 106; thereby protected the one or moremicrofluidic elements 108 and/or the one ormore buses 106 during manufacturing of themicrofluidic chip 100. Thesealing layer 104 can have a thickness greater than or equal to 100 μm and less than or equal to 2.5 mm. Thedevice layer 110 can have a thickness greater than or equal to 7 μm and less than or equal to 500 μm. In one or more embodiments, thesealing layer 104 can be thicker than thedevice layer 110. - The one or more buses 106 (e.g., fluid buses) can be embedded, subtractively patterned, and/or otherwise etched into the
device layer 110. The one ormore buses 106 can serve as channels that guide and/or transport fluid through themicrofluidic chip 100 with low fluidic resistance. For example, the one ormore buses 106 can form a bus network that can carry fluid to and/or from the one or moremicrofluidic elements 108. Themicrofluidic elements 108 can be embedded within thedevice layer 110 and/or be located on a top surface of thedevice layer 110, which is bonded to thesealing layer 104. Themicrofluidic elements 108 can comprise one or more devices that can utilize deterministic displacement arrays and/or deterministic lateral displacement technologies (“DLD”), such as condenser arrays (e.g., microscale condenser arrays and/or nanoscale condenser arrays) and/or nanoDLD arrays. Further examplemicrofluidic elements 108 can include, but are not limited to: microscale and/or nanoscale pillars, channels, biosensors, fluid mixing features, fluidic bus networks, fluidic inlets, and/or fluidic outlets. - One or more of the
buses 106 and/or themicrofluidic elements 108 can be in fluid communication with the one ormore vias 102. The one ormore vias 102 can traverse through thedevice layer 110. For example, the one ormore vias 102 can extend from a first side of thedevice layer 110 to a second side of the device layer 110 (e.g., wherein thesealing layer 104 can be boned to the second side of the device layer 110). - In one or more embodiments, the
microfluidic chip 100 can have a high density ofvias 102 traversing thedevice layer 110. For example, themicrofluidic chip 100 can comprise hundreds to tens of thousands ofvias 102 per square centimeter of thedevice layer 110. For instance, themicrofluidic chip 100 can comprise greater than or equal to 100vias 102 per square centimeter of thedevice layer 110 and less than or equal to 100,000vias 102 per square centimeter of thedevice layer 110. Additionally, the one ormore vias 102 can have diameters greater than or equal to 5 μm and less than or equal to 5 mm. Moreover,respective vias 102 of the one ormore vias 102 can share a common diameter or can have different diameters. One of ordinary skill in the art will recognize that althoughFIG. 1 shows a particular number ofvias 102,buses 106, and/ormicrofluidic elements 108, the architecture of themicrofluidic chip 100 is not so limited. For example, themicrofluidic chip 100 can comprise fewer oradditional vias 102,buses 106, and/ormicrofluidic elements 108 than those depicted inFIG. 1 . -
FIG. 2 illustrates a photo of an example,non-limiting wafer 200 that can comprise one or more microfluidic chips 100 (e.g., including a device layer 110 (e.g., comprising silicon) and/or sealing layer 104 (e.g., comprising glass)) in accordance with one or more embodiments described herein. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity. Thewafer 200 can have a thickness greater than or equal to 300 μm and less than or equal to 2.5 mm. Also, thewafer 200 can comprise greater than or equal to 1microfluidic chips 100 and less than or equal to 32,000microfluidic chips 100. For example, thewafer 200 can have a thickness of 200 mm and comprise 32microfluidic chips 100. Further,wafer 200 ofFIG. 2 can comprise one or moremicrofluidic chips 100 that can have one ormore vias 102 having a common diameter of 50 μm and/or a density of 1,000vias 102 per square centimeter. Additionally, thewafer 200 can comprise one or more chip boarders (not shown) etched into thewafer 200 to facilitate separation of one or more of the microfluidic chips 100 (e.g., via chip dicing). The one or more chip boarders can help prevent damage to thethin device layer 110 at the edges of the subjectmicrofluidic chip 100 being separated. -
FIG. 3 illustrates a scanning electron micrograph (“SEM”) of an exemplarymicrofluidic chip 100 of thewafer 200 shown inFIG. 2 . Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 3 depicts a cross-section of themicrofluidic chip 100. As shown inFIG. 3 , the exemplarymicrofluidic chip 100 can comprise aglass sealing layer 104 having a thickness of 700 μm, and asilicon device layer 110 of 90 μm. - Conventional methods of manufacturing are unable to produce the
microfluidic chip 100 due at least to the following considerations. First, the one ormore vias 102 described herein can require much thinner substrates (e.g., device layer 110) to etch completely through the wafers (e.g., wafer 200) to create fluidically accessible holes. The one ormore vias 102 can have aspect ratios greater than 1:10 (diameter: depth), which can be challenging to create using the conventional standard for via creation of reactive-ion etch (“RIE”). Second, etching completely through a wafer (e.g., wafer 200) can also be problematic as many of these RIE chambers have inductively coupled wafer chucks and use vacuum systems that will be damaged or error out during processing if thedevice layer 110 is etched through completely. Third, thethin device layer 110 can imply the need for a carrier wafer of some kind to support thethin device layer 110, which can be extremely brittle when thinned to, for example, 50 μm thickness (e.g., which can facilitate 5 μm diameter vias 102). Thin wafers (e.g., thin device layers 110) can also be desired to reduce RIE process time to create thevias 102. Fourth, thin device layers 110 cannot be de-bonded from the carrier after polishing as the silicon is too brittle and amicrofluidic sealing layer 104 can still be required. This presents a fifth challenge of preventing fluidic wicking or capillary wetting of microfluidic features due to post via 102 wet processing common in semiconductor manufacturing. Standard thru-silicon via (“TSV”) technology can use a fill material, such as copper, to plug thevias 102, which does not translate to microfluidic devices. Collectively, these challenges call for a via-last structure and method that can protect sealed microfluidic features from downstream wets processing (e.g. chemical mechanical polishing (CMP) and cleans) and that can provide apermanent sealing layer 104 for support. -
FIG. 4 illustrates a flow diagram of an example,non-limiting method 400 that can facilitate manufacturing themicrofluidic chip 100 in accordance with one or more embodiments described herein. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity. - At 402, the
method 400 can comprise defining one or moremicrofluidic elements 108 and/or one ormore buses 106 onto the surface of adevice layer 110. For example, the one or moremicrofluidic elements 108 and/or the one ormore buses 106 can be defined on a first lithography layer and patterned unto the surface of thedevice layer 110. Depending on the minimum feature size of themicrofluidic elements 108 and/orbuses 106, a number of lithography options can be employed during themethod 400, including but not limited to: various wavelength optical lithography (mid-ultraviolet (“UV”), deep-UV, 193 nm (e.g. argon fluoride laser)), immersion lithography, e-beam lithography, imprint lithography, interference lithography, x-ray lithography, a combination thereof, and/or the like. -
FIG. 5 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 being manufactured in accordance withmethod 400. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 5 can show a cross-section of themicrofluidic chip 100 after completion of the defining at 402. As shown inFIG. 5 , the defining at 402 can comprising defining one or moremicrofluidic elements 108 and/or one ormore buses 106 onto afirst surface 502 of thedevice layer 110. - Referring again to
FIG. 4 , at 404 themethod 400 can optionally comprise deepening the one ormore buses 106.Respective buses 106 can be deepened in their entirety at 404, or only a portion of arespective bus 106 can be deepened. The deepening at 404 can be facilitated by a second lithography layer, which can be used in conjunction with an etch process (e.g., RIE, tetramethylammonium hydroxide (“TMAH”) etching, potassium hydroxide (“KOH”) etching, a combination thereof, and/or the like). The deepening at 404 can be omitted for sufficiently smallmicrofluidic chips 100 or those whosemicrofluidic elements 108 are very fluidically restrictive. Essentially, parallel device arrays or othermicrofluidic elements 108 can drop most of the fluidic resistance to avoid one or more discrepancies in fluidic rate conditions in the one or more buses 106 (e.g., the plurality ofbuses 106 can comparably have very high fluidic conductance). -
FIG. 6 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 being manufactured in accordance withmethod 400. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 6 can show a cross-section of themicrofluidic chip 100 after completion of the deepening at 404. - Referring again to
FIG. 4 , at 406 themethod 400 can comprise bonding asealing layer 104 to the surface of thedevice layer 110. For example, thesealing layer 104 can be permanently bonded to thedevice layer 110. Thesealing layer 104 can be anodically bonded glass (e.g. Borofloat 33), a thermally bonded silicon wafer, and/or other substrates. Glass and other transparent substrate options offer the advantage of transparency for applications that require some kind of in situ analysis, such as fluorescence microscopy. Sealing thedevice layer 110 can serve at least two purposes: 1) it can prevent downstream damage, wetting, and process contamination from impacting themicrofluidic chip 100 features, and 2) it can act as a support for a thinneddevice layer 110 when polished subsequently in themethod 400. -
FIG. 7 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 being manufactured in accordance withmethod 400. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 7 can show a cross-section of themicrofluidic chip 100 after completion of the bonding at 406. - Referring again to
FIG. 4 , at 408 themethod 400 can comprise reducing the thickness of thedevice layer 110 to a final thickness. The thinning at 408 can be facilitated using a chemical-mechanical planarization (“CMP”) or a wet process (e.g., TMAH and/or KOH etching). Thedevice layer 110 can be thinned to a thickness of 7-500 μm post subsequent to the bonding at 406. By thinning thedevice layer 110, scaledfluidic vias 102 with diameters ranging from 5 μm to 100 μm can be possible to fabricate in up to 300mm wafers 200 with a starting nominal thickness of 775 μm, which can mate with themicrofluidic elements 108 and/orbuses 106 to input and extract a sample from various access points on themicrofluidic chip 100. -
FIG. 8 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 being manufactured in accordance withmethod 400. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 8 can show a cross-section of themicrofluidic chip 100 after completion of the reducing at 408. As shown inFIGS. 7 and 8 , “T1” can represent the thickness of thedevice layer 110 prior to the thinning at 408, and “T2” can represent the thickness of thedevice layer 110 subsequent to the thinning at 408; wherein T1 can be greater than T2. - Referring again to
FIG. 4 , at 410 themethod 400 can comprise forming one ormore vias 102 in thedevice layer 110. The one ormore vias 102 can extend completely through thedevice layer 110. Front-to-back alignment of the one ormore vias 102 can be performed using an optical and/or infrared (“IR”) camera to ensure alignment accuracy of a third lithography layer needed to align thevias 102 patterned on the back side of the device layer 110 (e.g., the side opposite to a side comprising the one or more microfluidic elements 108) with the front sidemicrofluidic elements 108, which reside in the device layer 110 (e.g., comprised of silicon) at the interface of thesealing layer 104 anddevice layer 110. The third lithography layer can be used to pattern the one ormore vias 102 in a hard mask, such as silicon oxide and/or silicon nitride, followed by removal of the resist and cleaning of thedevice layer 110, after which the one ormore vias 102 can be defined by a RIE process. Alternatively, the third lithography layer can be used as the etch mask itself and can be removed with an oxygen plasma after the one ormore vias 102 have been opened. The first approach of defining the one ormore vias 102 in a hard mask has the advantage of being able to more thoroughly clean the bonded layer pair (e.g., thedevice layer 110 bonded to the sealing layer 104) before the final via 102 opening RIE process. Wherein multiplemicrofluidic chips 100 are formed on awafer 200, themicrofluidic chips 100 can then be diced employing a standard dicing process and bonding film of sufficient tack to prevent fluid from entering thevias 102. -
FIG. 9 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 being manufactured in accordance withmethod 400. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 9 can show a cross-section of themicrofluidic chip 100 after completion of the forming of thevias 102 at 410. As shown inFIG. 9 , once formed the one ormore vias 102 can extend from asecond surface 902 of thedevice layer 110 to thefirst surface 502 of thedevice layer 110. - In one or more embodiments, the
microfluidic chip 100 can further comprise one or moresacrificial plugs 1002. Themethod 400 can comprise inserting thesacrificial plugs 1002 into thedevice layer 110 after defining the one or more buses 106 (e.g., at 402 and/or 404) and prior to bonding thedevice layer 110 to the sealing layer 104 (e.g., at 406). Thesacrificial plugs 1002 can be patterned using a resist material. The one or moresacrificial plugs 1002 can perform the function of ensuring uniformity of RIE breakthrough to the one or moremicrofluidic elements 108, ensuring that the one or moremicrofluidic elements 108 are not themselves etched by the forming of the one ormore vias 102. This may be particularly useful in cases where the one ormore vias 102 have different dimensions and thus etch at different rates. Thesacrificial plugs 1002 can be extracted using a downstream oxygen plasma (e.g., before or after themicrofluidic chip 100 is diced). -
FIG. 10 illustrates a diagram of an example, non-limitingmicrofluidic chip 100 being manufactured in accordance withmethod 400. Repetitive description of like elements employed in other embodiments described herein is omitted for sake of brevity.FIG. 7 can show a cross-section of themicrofluidic chip 100 after completion of the forming of thevias 102 at 410, wherein one or moresacrificial plugs 1002 were inserted into thedevice layer 110. - Thus,
method 400 can facilitate manufacturing one or moremicrofluidic chips 100 described herein by forming the one ormore vias 102 as a last step. Unlike conventional TSV technology, thefluidic vias 102 ofmicrofluid chip 100 can be open structures, which makes chips that implement them vulnerable to destruction by capillary action of wets processing common in semiconductor manufacturing. However,method 400 avoids destruction of themicrofluidic chip 100 by using a final RIE process (dry) to open thevias 102. Additionally, by thinning the device layer 110 (e.g., silicon) prior to forming the one ormore vias 102, themethod 400 can avoid conventional requirements of ultra-deep silicon etching that would otherwise be required to create thefluidic vias 102 and is problematic to implement in a practical process flow. Moreover, whilemethod 400 is described herein with regard to amicrofluidic chip 100 comprising a high density ofvias 102,method 400 can also applicable to the manufacturing ofmicrofluidic chips 100 only afew vias 102. - In addition, the term “or” is intended to mean an inclusive “or” rather than an exclusive “or.” That is, unless specified otherwise, or clear from context, “X employs A or B” is intended to mean any of the natural inclusive permutations. That is, if X employs A; X employs B; or X employs both A and B, then “X employs A or B” is satisfied under any of the foregoing instances. Moreover, articles “a” and “an” as used in the subject specification and annexed drawings should generally be construed to mean “one or more” unless specified otherwise or clear from context to be directed to a singular form. As used herein, the terms “example” and/or “exemplary” are utilized to mean serving as an example, instance, or illustration. For the avoidance of doubt, the subject matter disclosed herein is not limited by such examples. In addition, any aspect or design described herein as an “example” and/or “exemplary” is not necessarily to be construed as preferred or advantageous over other aspects or designs, nor is it meant to preclude equivalent exemplary structures and techniques known to those of ordinary skill in the art.
- What has been described above include mere examples of systems, computer program products and computer-implemented methods. It is, of course, not possible to describe every conceivable combination of components, products and/or computer-implemented methods for purposes of describing this disclosure, but one of ordinary skill in the art can recognize that many further combinations and permutations of this disclosure are possible. Furthermore, to the extent that the terms “includes,” “has,” “possesses,” and the like are used in the detailed description, claims, appendices and drawings such terms are intended to be inclusive in a manner similar to the term “comprising” as “comprising” is interpreted when employed as a transitional word in a claim. The descriptions of the various embodiments have been presented for purposes of illustration, but are not intended to be exhaustive or limited to the embodiments disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the described embodiments. The terminology used herein was chosen to best explain the principles of the embodiments, the practical application or technical improvement over technologies found in the marketplace, or to enable others of ordinary skill in the art to understand the embodiments disclosed herein.
Claims (16)
1. An apparatus, comprising:
a silicon device layer comprising a plurality of vias, the plurality of vias comprising greater than or equal to about 100 vias per square centimeter of a surface of the silicon device layer and less than or equal to about 100,000 vias per square centimeter of the surface of the silicon device layer, and the plurality of vias extending through the silicon device layer; and
a sealing layer bonded to the silicon device layer, wherein the sealing layer has greater rigidity than the silicon device layer.
2. The apparatus of claim 1 , wherein the sealing layer is selected from a group consisting of silicon and glass.
3. The apparatus of claim 2 , wherein the silicon device layer has a thickness greater than or equal to about 7 micrometers and less than or equal to about 500 micrometers.
4. The apparatus of claim 2 , wherein a via of the plurality of vias has a diameter greater than or equal to about 5 micrometers and less than or equal to about 5 millimeters.
5. The apparatus of claim 1 , further comprising a microfluidic element located on a second surface of the silicon device layer.
6. The apparatus of claim 5 , wherein the microfluidic element is in fluid communication with a via of the plurality of vias.
7. The apparatus of claim 6 , wherein the microfluidic element is encapsulated by a combination of the silicon device layer and the sealing layer.
8. The apparatus of claim 5 , wherein the microfluidic element is selected from a group consisting of a deterministic displacement array and a condenser array.
9. The apparatus of claim 8 , further comprising a fluidic bus embedded within the surface of the silicon device layer and in fluid communication with the microfluidic element.
10. The apparatus of claim 1 , wherein the sealing layer is thicker than the silicon device layer.
11. An apparatus, comprising:
a silicon device layer comprising a via and a microfluidic device, the via extending through the silicon device layer and in fluid communication with the microfluidic device, wherein the silicon device layer has a thickness greater than or equal to about 7 micrometers and less than or equal to about 500 micrometers; and
a sealing layer bonded to the silicon device layer, wherein the sealing layer has greater rigidity than the silicon device layer.
12. The apparatus of claim 11 , wherein the sealing layer has a second thickness greater than or equal to about 100 micrometers and less than or equal to about 2.5 millimeters.
13. The apparatus of claim 11 , wherein the sealing layer is selected from a group consisting of silicon and glass.
14. The apparatus of claim 11 , wherein the via has a diameter greater than or equal to about 5 micrometers and less than or equal to about 5 millimeters.
15. The apparatus of claim 11 , wherein the via is comprised within a plurality of vias.
16. The apparatus of claim 15 , wherein the plurality of vias comprise greater than or equal to about 100 vias and less than or equal to about 100,000 vias per square centimeter of a surface of the silicon device layer opposite to the sealing layer.