US20220177996A1 - High-Hardness Steel Product and Method of Manufacturing the Same - Google Patents

High-Hardness Steel Product and Method of Manufacturing the Same Download PDF

Info

Publication number
US20220177996A1
US20220177996A1 US17/601,227 US202017601227A US2022177996A1 US 20220177996 A1 US20220177996 A1 US 20220177996A1 US 202017601227 A US202017601227 A US 202017601227A US 2022177996 A1 US2022177996 A1 US 2022177996A1
Authority
US
United States
Prior art keywords
steel product
steel
range
less
product according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US17/601,227
Other languages
English (en)
Inventor
Mikko HEMMILÄ
Tommi LIIMATAINEN
Esa Virolainen
Pasi Suikkanen
Magnus Larsson
Magnus Gladh
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SSAB Technology AB
Original Assignee
SSAB Technology AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SSAB Technology AB filed Critical SSAB Technology AB
Assigned to SSAB TECHNOLOGY AB reassignment SSAB TECHNOLOGY AB ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HEMMILA, MIKKO, LARSSON, MAGNUS, LIIMATAINEN, TOMMI, SUIKKANEN, PASI, Virolainen, Esa, Gladh, Magnus
Publication of US20220177996A1 publication Critical patent/US20220177996A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/10—Ferrous alloys, e.g. steel alloys containing cobalt
    • C22C38/105—Ferrous alloys, e.g. steel alloys containing cobalt containing Co and Ni
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/20—Ferrous alloys, e.g. steel alloys containing chromium with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Definitions

  • the present invention relates to a high-hardness steel strip product exhibiting excellent resistance to climatic corrosion, a good balance of high hardness and excellent mechanical properties such as impact strength and bendability.
  • the present invention further relates to a method of manufacturing the high-hardness steel strip product.
  • High hardness has a direct effect on wear resistance of a steel product, the higher hardness the better wear resistance.
  • high hardness it is meant that the Brinell hardness is at least 450 HBW and especially in the range of 500 HBW to 650 HBW.
  • Wear resistant steels are also known as abrasion resistant steels. They are used in applications in which high resistance against abrasive and shock wear is required. Such applications can be found in e.g. mining and earth moving industry, and waste transportation. Wear resistant steels are used for instance in gravel truck's bodies and excavator buckets, whereby longer service time of the vehicle components are achieved due to the high hardness provided by the wear resistant steels. The benefits of wear resistant steels are even more crucial when the paint layer on a machine's outer surface is frequently exposed to mechanical stresses such as impacts which can cause scratch to paint layers.
  • Such high hardness in steel product is typically obtained by martensitic microstructure produced by quench hardening steel alloy having high content of carbon (0.41-0.50 wt. %) after austenitization in the furnace.
  • steel plates are first hot-rolled, slowly cooled to room temperature from the hot-rolling heat, reheated to austenitization temperature, equalized and finally quench hardened.
  • This process is hereinafter referred to as the reheating and quenching (RHQ) process.
  • RHQ reheating and quenching
  • steels produced in this way are wear resistant steels disclosed in CN102199737 or some commercial wear resistant steels. Due to the relatively high content of carbon, which is required to achieve the desired hardness, the resulting martensite reaction causes significant internal residual stresses to the steel.
  • Stress corrosion cracking is the cracking induced from the combined influence of tensile stress and a corrosive environment. Usually, stress corrosion cracking starts as a pitting corrosion with hard-to-detect fine cracks penetrating into the material while most of the material surface appears intact. Stress corrosion cracking is classified as a catastrophic form of corrosion, as the detection of such fine cracks can be very difficult and the damage not easily predicted. There is a need of better approaches to decrease the carbon content without compromising the hardness or any of the other mechanical properties, such as impact strength, formability/bendability or resistance to stress corrosion cracking.
  • CN102392186 and CN103820717 relate to RHQ steel plates having relatively low carbon content (0.25-0.30 wt. % in CN102392186; 0.22-0.29 wt. % in CN103820717) and also relatively low manganese content.
  • a tempering step after quench hardening is required for making such RHQ steel plates, which inevitably increases the processing efforts and costs.
  • EP2695960 relates to an abrasion-resistant steel product exhibiting excellent resistance to stress corrosion cracking, which steel sheet can be made in a process where direct quenching (DQ) may be performed immediately after hot rolling, without the reheating treatment after hot rolling as in the RHQ process.
  • the steel sheet of EP2695960 has a relatively low carbon content (0.20-0.30 wt. %) and a relatively high manganese content (0.40-1.20 wt. %).
  • the base phase or main phase of the microstructure of the steel product of EP2695960 must be made of tempered martensite.
  • the area fraction of untempered martensite is restricted to 10% or less because the resistance to stress corrosion cracking is reduced in the presence of untempered martensite.
  • the steel product of EP2695960 has a surface hardness of 520 HBW or less.
  • the present invention extends the utilization of the cost-effective thermomechanically controlled processing (TMCP) in conjunction with direct quenching (DQ) to produce a high-hardness steel strip product exhibiting improved resistance to climatic corrosion, guaranteed impact strength values and excellent formability/bendability.
  • TMCP thermomechanically controlled processing
  • DQ direct quenching
  • the object of the present invention is to solve the problem of providing a high-hardness steel strip product exhibiting excellent resistance to climatic corrosion, guaranteed impact strength values and excellent formability/bendability.
  • the problem is solved by the combination of specific alloy designs with cost-efficient TMCP procedures which produces a metallographic microstructure comprising mainly martensite.
  • the present invention provides a hot-rolled steel strip product comprising a composition consisting of, in terms of weight percentages (wt. %):
  • the aforementioned composition comprises, in terms of weight percentages (wt. %):
  • the aforementioned composition comprises, in terms of weight percentages (wt. %):
  • the steel product is alloyed with the essential alloying elements Si, Cu, Ni and Cr, which provides good resistance against climatic corrosion and increases durability of a paint layer.
  • the steel product has a low content of Mn, which is important for improving impact toughness and bendability.
  • the Ca/S ratio is adjusted such that CaS cannot form thereby improving impact toughness and bendability.
  • the Ca/S ratio is preferably in the range of 1-2, more preferably 1.1-1.7, and even more preferably 1.2-1.6.
  • the level of Nb should be restricted to the lowest possible to increase formability or bendability of the steel product. Elements such as Nb may be present as residual contents that are not purposefully added.
  • residual contents are controlled quantities of alloying elements, which are not considered to be impurities.
  • a residual content as normally controlled by an industrial process does not have an essential effect upon the alloy.
  • the present invention provides a method for manufacturing hot-rolled steel strip product comprising the following steps of
  • the hot-rolling to the desired thickness at a temperature in the range of Ar 3 to 1300° C., wherein the finish rolling temperature is in the range of 800° C. to 960° C., preferably 870° C.-930° C., more preferably 885° C.-930° C.; and
  • a cooling end and coiling temperature of 450° C. or less, preferably 250° C. or less, more preferably 150° C. or less, and even more preferably 100° C. or less.
  • a step of temper annealing is performed on the direct quenched and coiled strip product at a temperature in the range of 150° C.-250° C.
  • the step of temper annealing is not required according to the present invention.
  • the steel product is a steel strip having a thickness of 10 mm or less, preferably 8 mm or less, and more preferably 7 mm or less.
  • the obtained steel product has a microstructure comprising, in terms of volume percentages (vol. %), at least 90 vol. % martensite, preferably at least 95 vol. % martensite, and more preferably at least 98 vol. % martensite, measured from 1 ⁇ 4 thickness of the steel strip product.
  • the martensitic structure may be untempered, autotempered and/or tempered.
  • the martensitic structure is not tempered. More preferably, the aforementioned microstructure comprises more than 10 vol. % untempered martensite.
  • the microstructure comprises 0-1 vol. % residual austenite, and more preferably 0-0.5 vol. % residual austenite.
  • the microstructure also comprises bainite, ferrite and/or pearlite.
  • the obtained steel product has a prior austenite grain size of 50 ⁇ m or less, preferably 30 ⁇ m or less, more preferably 20 ⁇ m or less, measured from 1 ⁇ 4 thickness of the steel strip product.
  • the aspect ratio of a prior austenite grain structure is one of the factors affecting a steel product's impact toughness and bendability.
  • the prior austenite grain structure should have an aspect ratio of at least 1.5, preferably at least 2, and more preferably at least 3.
  • the prior austenite grain structure should have an aspect ratio of 7 or less, preferably 5 or less, and more preferably 1.5 or less.
  • the obtained steel product according to the present invention has a prior austenite grain structure with an aspect ratio in the range of 1.5-7, preferably 1.5-5, and more preferably 2-5, which ensures that a good balance of excellent impact toughness and excellent bendability can be achieved.
  • the obtained steel product has a good balance of hardness and other mechanical properties such as improved resistance to climatic corrosion and excellent impact strength.
  • the steel product has at least one of the following mechanical properties: a Brinell hardness in the range of 420-580 HBW, preferably 450-550 HBW, and more preferably 470-530 HBW;
  • a corrosion index (ASTM G101-04) ⁇ 5, preferably 5.5, and more preferably ⁇ 6; a Charpy-V impact toughness of at least 34 J/cm 2 at a temperature of ⁇ 20° C. or ⁇ 40° C.
  • the steel product exhibits excellent bendability or formability.
  • the steel product has a minimum bending radius of 3.4 t or less in a measurement direction longitudinal to the rolling direction wherein the bending axis is longitudinal to rolling direction; a minimum bending radius of 2.7 t or less in a measurement direction transversal to the rolling direction wherein the bending axis is transversal to rolling direction; and wherein t is the thickness of the steel strip product.
  • the steel product has a good balance of high hardness and excellent mechanical properties such as impact strength and formability/bendability. Consequently, the steel product exhibits excellent resistance to climatic corrosion.
  • FIG. 1 illustrates the microstructures.
  • steel is defined as an iron alloy containing carbon (C).
  • climatic corrosion refers to outdoor corrosion caused by local environmental conditions. Environmental conditions are formed from weather phenomena like rain and sunshine. They are also affected by different impurities in the air like chlorides from sea water and sulfur compounds coming from volcanic activity and industry or mining.
  • Baux hardness is a designation of hardness of steel.
  • the Brinell hardness test is performed by pressing a 10 mm spherical tungsten carbide ball against a clean prepared surface using a 3000 kilogram force, producing an impression, measured and given a special numerical value.
  • corrosion index refers to the American Society for Testing and Materials (ASTM) standard G101 which is currently the only available guide to quantify the atmospheric corrosion resistance of weathering steels as a function of their composition.
  • accelerated continuous cooling refers to a process of accelerated cooling at a cooling rate down to a temperature without interruption.
  • yield strength (YS, Rp 0.2 ) refers to 0.2% offset yield strength defined as the amount of stress that will result in a plastic strain of 0.2%.
  • total elongation refers to the percentage by which the material can be stretched before it breaks; a rough indicator of formability, usually expressed as a percentage over a fixed gauge length of the measuring extensometer. Two common gauge lengths are 50 mm (A 50 ) and 80 mm (A 80 ).
  • Minimum bending radius (Ri) is used to refer to the minimum radius of bending that can be applied to a test sheet without occurrence of cracks.
  • the alloying content of steel together with the processing parameters determines the microstructure which in turn determines the mechanical properties of the steel.
  • Alloy design is one of the first issues to be considered when developing a steel product with targeted mechanical properties.
  • chemical composition according to the present invention is described in more details, wherein % of each component refers to weight percentage.
  • Carbon C is used in the range of 0.17% to 0.38%.
  • C alloying increases strength of steel by solid solution strengthening, and hence C content determines the strength level.
  • C is used in the range of 0.17% to 0.38% depending on targeted hardness. If the carbon content is less than 0.17%, it is difficult to achieve a Brinell hardness of more than 420 HBW. However, C has detrimental effects on weldability, impact toughness, formability or bendability, and resistance to stress corrosion cracking. Therefore, C content is set to not more than 0.38%.
  • C is used in the range of 0.21% to 0.35%, and more preferably 0.22% to 0.28%.
  • Silicon Si is used in an amount of 0.5% or less. Si is added to the composition to facilitate formation of a protective oxide layer under corrosive climate conditions, which provides good resistance against climatic corrosion and increases the durability of a paint layer that is easily damaged or removed from machines surfaces due to wear. Si is effective as a deoxidizing or killing agent that can remove oxygen from the melt during a steelmaking process. Si alloying enhances strength by solid solution strengthening, and enhances hardness by increasing austenite hardenability. Also the presence of Si can stabilize residual austenite. However, silicon content of higher than 0.5% may unnecessarily increase carbon equivalent (CE) value thereby weakening the weldability. Furthermore, surface quality may be deteriorated if Si is present in excess.
  • CE carbon equivalent
  • Si is an important alloying element for providing sufficient hardness and good resistance to climatic corrosion, and for increasing durability of a paint layer.
  • Si is used in the range of 0.01% to 0.5%, and more preferably 0.03% to 0.25%.
  • Manganese Mn is used in the range of 0.1% to 0.4%. Mn alloying lowers martensite start temperature (Ms) and martensite finish temperature (Mf), which can suppress autotempering of martensite during quenching. Reduced autotempering of martensite leads to higher internal stresses that enhance the risk for quench-induced cracking or distortion of shape. Although a lower degree of autotempered martensitic microstructures is beneficial to higher hardness, its negative effects on impact strength should not be underestimated.
  • Mn alloying also enhances strength by solid solution strengthening, and enhances hardness by increasing austenite hardenability. However, if the Mn content is too high, hardenability of the steel will increase at the expense of impact toughness. Excessive Mn alloying may also lead to C-Mn segregation and formation of MnS, which could induce formation of initiation sites for pitting corrosion and stress corrosion cracking.
  • Mn is used in an amount of at least 0.1% to ensure hardenability, but not more than 0.4% to avoid the harmful effects as described above and to ensure excellent mechanical properties such as impact strength and bendability.
  • a low level of Mn is used in the range of 0.15% to 0.3%.
  • Aluminum Al is used in the range of 0.015% to 0.15%. Al is effective as a deoxidizing or killing agent that can remove oxygen from the melt during a steelmaking process. Al also removes N by forming stable AlN particles and provides grain refinement, which is beneficial to high toughness, especially at low temperatures. Also Al stabilizes residual austenite. However, an excess of Al may increase non-metallic inclusions thereby deteriorating cleanliness.
  • Copper Cu is used in the range of 0.1% to 0.6%.
  • Cu is added to the composition to facilitate formation of a protective oxide layer under corrosive climate conditions, which provides good resistance against climatic corrosion and increases the durability of a paint layer that is easily damaged or removed from machines surfaces due to wear.
  • Cu may promote formation of low carbon bainitic structures, cause solid solution strengthening and contribute to precipitation strengthening.
  • Cu may also have beneficial effects of inhibiting stress corrosion cracking. When added in excessive amounts, Cu deteriorates field weldability and the heat affected zone (HAZ) toughness. Therefore, the upper limit of Cu is set to 0.6%.
  • Cu is an important alloying element for providing sufficient hardness and good resistance to climatic corrosion, and for increasing durability of a paint layer.
  • Cu is used in the range of 0.1% to 0.5%, and more preferably 0.1% to 0.35%.
  • Nickel Ni is used in in an amount of 0.8% or less. Ni is used to avoid quench induced cracking and also to improve low temperature toughness. Ni is an alloying element that improves austenite hardenability thereby increasing strength with no or marginal loss of impact toughness and/or HAZ toughness. Ni also improves surface quality thereby preventing pitting corrosion, i.e. initiation site for stress corrosion cracking. Ni is added to the composition to facilitate formation of a protective oxide layer under corrosive climate conditions, which provides good resistance against climatic corrosion and increases the durability of a paint layer that is easily damaged or removed from machines surfaces due to wear. However, nickel contents of above 0.8% would increase alloying costs too much without significant technical improvement. An excess of Ni may produce high viscosity iron oxide scales which deteriorate surface quality of the steel product. Higher Ni contents also have negative impacts on weldability due to increased CE value and cracking sensitivity coefficient.
  • Ni is an important alloying element for providing sufficient hardness and good resistance to climatic corrosion with no or marginal loss of impact toughness, and for increasing durability of a paint layer.
  • Ni is preferably used in the range of 0.2% to 0.8%.
  • Chromium Cr is used in the range of 0.1% to 1%. Cr is added to the composition to facilitate formation of a protective oxide layer under corrosive climate conditions, which provides good resistance against climatic corrosion and increases the durability of a paint layer that is easily damaged or removed from machines surfaces due to wear. Cr alloying provides better resistance against pitting corrosion thereby preventing stress corrosion cracking at an early stage. As mid-strength carbide forming element Cr increases the strength of both the base steel and weld with marginal expense of impact toughness. Cr alloying also enhances strength and hardness by increasing austenite hardenability. However, if Cr is used in an amount above 1% the HAZ toughness as well as field weldability may be adversely affected.
  • Cr is an important alloying element for providing sufficient hardness and good resistance to climatic corrosion with no or marginal loss of impact toughness, and for increasing durability of a paint layer.
  • Cr is used in the range of 0.3% to 1%, more preferably 0.35% to 1%, and even more preferably 0.35% to 0.8%.
  • Molybdenum Mo is used in the range of 0.01% to 0.3%. Mo alloying improves impact strength, low-temperature toughness and tempering resistance. The presence of Mo enhances strength and hardness by increasing austenite hardenability. Mo can be added to the composition to provide hardenability in place of Mn. In the case of B alloying, Mo is usually required to ensure the effectiveness of B. However, Mo is not an economically acceptable alloying element. If Mo is used in an amount of above 0.3% toughness may be deteriorated thereby increasing the risk of brittleness. An excessive amount of Mo may also reduce the effect of B. Furthermore, the inventors have noticed that Mo alloying retards recrystallization of austenite thereby increasing the aspect ratio of a prior austenite grain structure. Therefore, the level of Mo content should be carefully controlled to prevent excessive elongation of the prior austenite grains which may deteriorate bendability of the steel product.
  • Mo is used in the range of 0.03% to 0.3%, and more preferably 0.05% to 0.3%.
  • Niobium Nb is used in an amount of 0.005% or less. Nb forms carbides NbC and carbonitrides Nb(C,N). Nb is considered to be the major grain refining element. Nb contributes to strengthening and toughening of steels. Yet, Nb addition should be limited to 0.005% since an excess of Nb deteriorates bendability, in particular when direct quenching is applied and/or when Mo is present in the composition. Furthermore, Nb can be harmful for HAZ toughness since Nb may promote the formation of coarse upper bainite structure by forming relatively unstable TiNbN or TiNb(C,N) precipitates. The level of Nb should be restricted to the lowest possible to increase formability or bendability of the steel product.
  • Titanium Ti is used in an amount of 0.05% or less.
  • TiC precipitates are able to deeply trap a significant amount of hydrogen H, which decreases the H diffusivity in the materials and removes some of the detrimental H from the microstructure to prevent stress corrosion cracking.
  • Ti is also added to bind free N that is harmful to toughness by forming stable TiN that together with NbC can efficiently prevent austenite grain growth in the reheating stage at high temperatures.
  • TiN precipitates can further prevent grain coarsening in the HAZ during welding thereby improving toughness.
  • TiN formation suppresses BN precipitation, thereby leaving B free to make its contribution to hardenability.
  • the ratio of Ti/N is at least 3.4. However, if Ti content is too high, coarsening of TiN and precipitation hardening due to TiC develop and the low-temperature toughness may be deteriorated. Therefore, it is necessary to restrict titanium so that it is less than 0.05%.
  • Ti is used in an amount of 0.035% or less, and more preferably 0.02% or less. If the steel product has a low nitrogen content of 0.003% or less, it is unnecessary to add Ti to ensure the boron hardenability effect, and the Ti content can be as low as 0.005% or less. If the nitrogen content is more than 0.003% but no more than 0.01%, the Ti content can be more than 0.005% but no more than 0.05%.
  • Vanadium V is used in an amount of 0.2% or less. V has substantially the same but smaller effects as Nb. V 4 C 3 precipitates are able to deeply trap a significant amount of hydrogen H, which decreases the H diffusivity in the materials and removes some of the detrimental H from the microstructure to prevent HIC. V is a strong carbide and nitride former, but V(C,N) can also form and its solubility in austenite is higher than that of Nb or Ti. Thus, V alloying has potential for dispersion and precipitation strengthening, because large quantities of V are dissolved and available for precipitation in ferrite. However, an addition of more than 0.2% V has negative effects on weldability and hardenability.
  • V is used in an amount of 0.06% or less.
  • Boron B is used in the range of 0.0005% to 0.005%.
  • B is a well-established microalloying element to increase hardenability.
  • the most effective B alloying would preferably require the presence of Ti in an amount of at least 3.42 N to prevent formation of BN.
  • the Ti content can be lowered to 0.005% or less, which is beneficial to low-temperature toughness. Hardenability deteriorates if the B content exceeds 0.005%.
  • B is used in the range of 0.0008% to 0.005%.
  • Calcium Ca is used in an amount of 0.01% or less. Ca addition during a steelmaking process is for refining, deoxidation, desulphurization, and control of shape, size and distribution of oxide and sulphide inclusions. Ca is usually added to improve subsequent coating. However, an excessive amount of Ca should be avoided to achieve clean steel thereby preventing the formation of calcium sulfide (CaS) or calcium oxide (CaO) or mixture of these (CaOS) that may deteriorate the mechanical properties such as bendability and SCC resistance.
  • CaS calcium sulfide
  • CaO calcium oxide
  • CaOS mixture of these
  • Ca is used in an amount of 0.005% or less, and more preferably 0.0008% to 0.003% to ensure excellent mechanical properties such as impact strength and bendability.
  • the Ca/S ratio is adjusted such that CaS cannot form thereby improving impact toughness and bendability.
  • the inventors have noticed that, in general, during the steelmaking process the optimal Ca/S ratio is in the range of 1-2, preferably 1.1-1.7, and more preferably 1.2-1.6 for clean steel.
  • Unavoidable impurities can be phosphor P, sulfur S, nitrogen N. Their content in terms of weight percentages (wt. %) is preferably defined as follows:
  • P 0-0.025 preferably 0.001-0.025, more preferably 0.001-0.012 S 0-0.008, preferably 0-0.005, more preferably 0-0.002 N 0-0.01, preferably 0-0.005, more preferably 0-0.004
  • Austenite to martensite transformation in steels depends largely on the following factors: chemical composition and some processing parameters, mainly reheating temperature, cooling rate and cooling temperature. With regard to chemical composition, some alloying elements have a greater impact than others while others have a negligible impact. Equations describing austenite hardenability may be used to assess the impact of different alloying elements on martensite formation during cooling. One such equation is presented below. From this equation we can see that carbon has the biggest impact, Mn, Mo and Cr have an intermediate impact while Si and Ni have a lesser impact. Furthermore, the equation shows that any single element is not crucial for martensite formation and that the absence of one element may be compensated with the amount of other alloying elements and processing parameters, such as e.g. cooling rate.
  • the steel product with the targeted mechanical properties is produced in a process that determines a specific microstructure which in turn dictates the mechanical properties of the steel product.
  • the first step is to provide a steel slab by means of, for instance a process of continuous casting, also known as strand casting.
  • the steel slab is heated to the austenitizing temperature of 1200-1350° C., and thereafter subjected to a temperature equalizing step that may take 30 to 150 minutes.
  • the reheating and equalizing steps are important for controlling the austenite grain growth. An increase in the heating temperature can cause dissolution and coarsening of alloy precipitates, which may result in abnormal grain growth.
  • the final steel product has a prior austenite grain size of 50 ⁇ m or less, preferably 30 ⁇ m or less, more preferably 20 ⁇ m or less, measured from 1 ⁇ 4 thickness of the steel strip product.
  • the slab is hot rolled to the desired thickness at a temperature in the range of Ar3 to 1300° C., wherein the finish rolling temperature (FRT) is in the range of 800° C. to 960° C., preferably 870° C.-930° C., more preferably 885° C.-930° C.
  • FRT finish rolling temperature
  • the aspect ratio of a prior austenite grain structure is one of the factors affecting a steel product's impact toughness and bendability.
  • the prior austenite grain structure should have an aspect ratio of at least 1.5, preferably at least 2, and more preferably at least 3.
  • the prior austenite grain structure should have an aspect ratio of 7 or less, preferably 5 or less, and more preferably 1.5 or less.
  • a desired aspect ratio of prior austenite grains can be achieved by adjusting a number of parameters such as finish rolling temperature, strain/deformation, strain rate, and/or alloying with the elements such as Mo that retard recrystallization of austenite.
  • the obtained steel product according to the present invention has a prior austenite grain structure with an aspect ratio in the range of 1.5-7, preferably 1.5-5, and more preferably 2-5, which ensures that a good balance of excellent impact toughness and excellent bendability can be achieved.
  • the obtained steel strip product has a thickness of 10 mm or less, preferably 8 mm or less, more preferably 7 mm or less.
  • the hot-rolled steel strip product is direct quenched to a cooling end and coiling temperature of 450° C. or less, preferably 250° C. or less, more preferably 150° C. or less, and even more preferably 100° C. or less.
  • the cooling rate is at least 30° C./s.
  • the direct quenched steel strip product is coiled at temperature of 450° C. or less, preferably 250° C. or less, more preferably 150° C. or less, and even more preferably 100° C. or less.
  • the obtained steel strip product has a microstructure comprising, in terms of volume percentages (vol. %), at least 90 vol. % martensite, preferably at least 95 vol. % martensite, and more preferably at least 98 vol. % martensite, measured from 1 ⁇ 4 thickness of the steel strip product.
  • the martensitic structure may be untempered, autotempered and/or tempered.
  • the martensitic structure is not tempered. More preferably, the aforementioned microstructure comprises more than 10 vol. % untempered martensite.
  • the microstructure comprises 0-1 vol. % residual austenite, and more preferably 0-0.5 vol. % residual austenite.
  • the microstructure also comprises bainite, ferrite and/or pearlite.
  • an extra step of temper annealing is performed at a temperature in the range of 150° C.-250° C.
  • the steel strip product has a good balance of hardness and other mechanical properties such as excellent impact strength, improved resistance to climatic corrosion and excellent formability/bendability.
  • the steel strip product has a high Brinell hardness in the range of 420-580 HBW, preferably 450-550 HBW, and more preferably 470-530 HBW.
  • the steel strip product has a corrosion index (ASTM G101-04) of at least 5, preferably at least 5.5, and more preferably at least 6, which indicates improved resistance against climatic corrosion.
  • the durability of a paint layer is increased and the repainting interval can be 1.5-2 times longer by using the steel product of the invention.
  • the corrosion index (ASTM G101-04) is used for estimating long term atmospheric corrosion of low alloy steels in various environments.
  • the corrosion index (ASTM G101-04) equation is formed with a statistical method from long term outdoor corrosion exposure tests, which equation is represented as follows.
  • the steel strip product with high hardness has a Charpy-V impact toughness of at least 34 J/cm 2 at a temperature of ⁇ 20° C. or ⁇ 40° C. thereby fulfilling the conventional impact strength requirements.
  • the steel strip product exhibits excellent bendability or formability.
  • the steel product has a minimum bending radius of 3.4 t or less in a measurement direction longitudinal to the rolling direction wherein the bending axis is longitudinal to rolling direction; a minimum bending radius of 2.7 t or less in a measurement direction transversal to the rolling direction wherein the bending axis is transversal to rolling direction; and wherein t is the thickness of the steel strip product.
  • Microstructure Microstructure can be characterized from SEM micrographs and the volume fraction can be determined using point counting or image analysis method.
  • the microstructures of the tested inventive examples no. 1-4 all have a main phase of at least 90 vol. % martensite.
  • FIG. 1 is an SEM image on the RD-ND plane from 1 ⁇ 4 thickness of the steel strip no. 1, where the prior austenite grain boundaries are visualized.
  • the prior austenite grain structure of the steel strip no. 1 has an aspect ratio of 3.4.
  • Brinell hardness HBW The Brinell hardness test is performed by pressing a 10 mm spherical tungsten carbide ball against a clean prepared surface using a 3000 kilogram force, producing an impression, measured and given a special numerical value. The measurement is done perpendicular to the upper surface of the steel sheet at 10-15% depth from the steel surface.
  • each one of the inventive examples no. 1-4 exhibits a Brinell harness in the range of 475-491 HBW.
  • the comparative example no. 5 exhibits a Brinell harness of 486 HBW while the comparative example no. 6 exhibits a Brinell harness of 469 HBW.
  • Corrosion index (ASTM G101-04) The corrosion index (ASTM G101-04) is calculated based on the American Society for Testing and Materials (ASTM) standard G101. As shown in Table 3, each one of the inventive examples no. 1-4 has a corrosion index (ASTM G101-04) of at least 5.28. On the other hand, the comparative examples no. 5 and 6 have a much lower corrosion index (ASTM G101-04) of 3.4 and 1.04 respectively.
  • the impact toughness values at ⁇ 20° C. or ⁇ 40° C. were obtained by Charpy V-notch tests according to the ASME (American Society of Mechanical Engineers) Standards.
  • the inventive examples no. 1 and 2 have a Charpy-V impact toughness of 63 J/cm 2 and 45 J/cm 2 respectively at a temperature of ⁇ 20° C. (Table 3).
  • Each one of the inventive examples no. 1-4 has a Charpy-V impact toughness in the range of 38-120 J/cm 2 at a temperature of ⁇ 40° C. if the measurement direction is longitudinal to the rolling direction.
  • the 1-4 has a Charpy-V impact toughness in the range of 58-105 J/cm 2 at a temperature of ⁇ 40° C. if the measurement direction is transversal to the rolling direction.
  • the impact toughness of the inventive examples no. 1-4 is improved compared to the comparative example no. 6.
  • the comparative example no. 5 has a better Charpy-V impact toughness values than the inventive examples no. 1 and 2 at the expense of bendability.
  • Elongation Elongation was determined according ASTM E8 standard using transverse specimens of a produced batch of 2000 ton of plates.
  • the mean value of total elongation (A 50 ) of the inventive examples no. 1 and 2 is 11.6 and 11.3 respectively (Table 3), which is better than the comparative examples no. 5 and 6 having a mean A 50 value of 10.1 and 9.1 respectively.
  • the comparative examples no. 5 and 6 have better A 50 values than the inventive examples no. 3 and 4 at the expense of Charpy-V impact toughness.
  • the bend test consists of subjecting a test piece to plastic deformation by three-point bending, with one single stroke, until a specified angle 90° of the bend is reached after unloading.
  • the inspection and assessment of the bends is a continuous process during the whole test series. This is to be able to decide if the punch radius (R) should be increased, maintained or decreased.
  • the limit of bendability (R/t) for a material can be identified in a test series if a minimum of 3 m bending length, without any defects, is fulfilled with the same punch radius (R) both longitudinally and transversally. Cracks, surface necking marks and flat bends (significant necking) are registered as defects.
  • each one of the inventive examples no. 1-4 has a minimum bending radius of 3.3 t or less in a measurement direction longitudinal to the rolling direction; a minimum bending radius of 2.6 t or less in a measurement direction transversal to the rolling direction; and wherein t is the thickness of the steel strip product (Table 3).
  • the comparative example no. 5 exhibits lower bendability with a minimum bending radius of 3.7 tin a measurement direction longitudinal to the rolling direction and a minimum bending radius of 2.2 tin a measurement direction transversal to the rolling direction.
  • Yield strength Yield strength was determined according ASTM E8 standard using transverse specimens of a produced batch of 2000 ton of plates.
  • Each one of the inventive examples no. 1-4 has a mean value of yield strength (Rp 0.2 ) in the range of 1302 MPa to 1399 MPa, measured in the longitudinal direction (Table 3).
  • the comparative examples no. 5 and 6 have a mean value of yield strength (Rp 0.2 ) of 1262 MPa and 1338 MPa respectively, measured in the longitudinal direction (Table 3).
  • Tensile strength was determined according ASTM E8 standard using transverse specimens of a produced batch of 2000 ton of plates.
  • Each one of the inventive examples no. 1-4 has a mean value of ultimate tensile strength (Rm) in the range of 1509 MPa to 1566 MPa, measured in the longitudinal direction (Table 3).
  • the comparative examples no. 5 and 6 have a mean value of ultimate tensile strength (Rm) of 1550 MPa and 1552 MPa respectively, measured in the longitudinal direction (Table 3).
US17/601,227 2019-04-05 2020-04-02 High-Hardness Steel Product and Method of Manufacturing the Same Pending US20220177996A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
EP19167552.9A EP3719148B1 (en) 2019-04-05 2019-04-05 High-hardness steel product and method of manufacturing the same
EP19167552.9 2019-04-05
EP19185759.8 2019-07-11
EP19185759.8A EP3719149B1 (en) 2019-04-05 2019-07-11 High-hardness steel product and method of manufacturing the same
PCT/EP2020/059424 WO2020201438A1 (en) 2019-04-05 2020-04-02 High-hardness steel product and method of manufacturing the same

Publications (1)

Publication Number Publication Date
US20220177996A1 true US20220177996A1 (en) 2022-06-09

Family

ID=66101932

Family Applications (2)

Application Number Title Priority Date Filing Date
US17/601,234 Pending US20220177997A1 (en) 2019-04-05 2020-04-02 High-Hardness Steel Product and Method of Manufacturing the Same
US17/601,227 Pending US20220177996A1 (en) 2019-04-05 2020-04-02 High-Hardness Steel Product and Method of Manufacturing the Same

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US17/601,234 Pending US20220177997A1 (en) 2019-04-05 2020-04-02 High-Hardness Steel Product and Method of Manufacturing the Same

Country Status (10)

Country Link
US (2) US20220177997A1 (pl)
EP (2) EP3719148B1 (pl)
JP (1) JP2022528420A (pl)
KR (1) KR20210149123A (pl)
CN (2) CN113785078B (pl)
BR (2) BR112021019860A2 (pl)
CA (2) CA3135144A1 (pl)
PL (1) PL3719148T3 (pl)
SI (1) SI3719148T1 (pl)
WO (2) WO2020201437A1 (pl)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020086971A1 (en) 2018-10-26 2020-04-30 Oerlikon Metco (Us) Inc. Corrosion and wear resistant nickel based alloys
WO2023067544A1 (en) * 2021-10-20 2023-04-27 Tata Steel Limited High hardness low alloyed hot rolled steel and method of manufacturing thereof
WO2023080629A1 (ko) 2021-11-02 2023-05-11 주식회사 엘지에너지솔루션 이차전지용 양극활물질
EP4180544A1 (en) * 2021-11-11 2023-05-17 SSAB Technology AB A hot-rolled steel strip product and method for its production
CN114774772B (zh) * 2022-03-07 2023-10-31 江阴兴澄特种钢铁有限公司 一种耐腐蚀500hb马氏体耐磨钢板及其生产方法
CN115058572B (zh) * 2022-06-13 2023-07-04 北京科技大学 一种添加中间层的不锈钢/碳钢层状复合板及其制备方法

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101270439A (zh) * 2007-03-23 2008-09-24 宝山钢铁股份有限公司 一种高强度热轧防弹钢板及其制造方法
JP5145804B2 (ja) * 2007-07-26 2013-02-20 Ｊｆｅスチール株式会社 耐低温焼戻し脆化割れ特性に優れた耐磨耗鋼板
CN101660108A (zh) * 2009-10-16 2010-03-03 江苏省沙钢钢铁研究院有限公司 非调质针状组织高强度低屈强比耐候钢及其生产方法
WO2011099408A1 (ja) * 2010-02-15 2011-08-18 新日本製鐵株式会社 厚鋼板の製造方法
CN102199737B (zh) 2010-03-26 2012-09-19 宝山钢铁股份有限公司 一种600hb级耐磨钢板及其制造方法
ES2691209T3 (es) * 2010-06-03 2018-11-26 Nippon Steel & Sumitomo Metal Corporation Proceso para fabricar un tubo de acero para airbag
MX341765B (es) 2011-03-29 2016-09-02 Jfe Steel Corp Placa de acero o lamina de acero resistente a la abrasion excelente en resistencia al agrietamiento por corrosion y esfuerzo y metodo para la fabricacion de la misma.
FI20115702L (fi) * 2011-07-01 2013-01-02 Rautaruukki Oyj Menetelmä suurlujuuksisen rakenneteräksen valmistamiseksi ja suurlujuuksinen rakenneteräs
CN102392186B (zh) 2011-11-07 2012-11-07 南京钢铁股份有限公司 一种hb500级低锰耐磨钢板的制造方法
AU2013204206B2 (en) * 2012-10-19 2016-09-15 Bluescope Steel Limited Steel Plate
US9803256B2 (en) * 2013-03-14 2017-10-31 Tenaris Coiled Tubes, Llc High performance material for coiled tubing applications and the method of producing the same
FI20135775L (fi) * 2013-07-16 2014-09-03 Rautaruukki Oyj Menetelmä valmistaa galvannealed-käsitelty teräsnauhatuote kuumapuristusmuovaukseen, menetelmä valmistaa kuumapuristettu teräskomponentti, ja galvannealed-käsitelty teräsnauhatuote
EP2789699B1 (en) * 2013-08-30 2016-12-28 Rautaruukki Oy A high-hardness hot-rolled steel product, and a method of manufacturing the same
WO2015110585A1 (en) * 2014-01-24 2015-07-30 Rautaruukki Oyj Hot-rolled ultrahigh strength steel strip product
CN103820717A (zh) 2014-01-28 2014-05-28 莱芜钢铁集团有限公司 钢板及其制备方法
JP6394378B2 (ja) * 2014-12-26 2018-09-26 新日鐵住金株式会社 耐摩耗鋼板およびその製造方法
EP3390040B2 (en) * 2015-12-15 2023-08-30 Tata Steel IJmuiden B.V. High strength hot dip galvanised steel strip
US10174398B2 (en) * 2016-02-22 2019-01-08 Nucor Corporation Weathering steel
WO2017183059A1 (ja) * 2016-04-19 2017-10-26 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
JP6119934B1 (ja) * 2016-04-19 2017-04-26 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
US20190368014A1 (en) * 2017-01-26 2019-12-05 Ssab Technology Ab Quench hardened steel
BR112019017699B1 (pt) * 2017-03-13 2023-03-14 Jfe Steel Corporation Placa de aço resistente à abrasão e método para fabricar a mesma

Also Published As

Publication number Publication date
EP3719148B1 (en) 2023-01-25
CA3135141A1 (en) 2020-10-08
WO2020201438A1 (en) 2020-10-08
PL3719148T3 (pl) 2023-05-08
BR112021019865A2 (pt) 2021-12-07
CN113785078A (zh) 2021-12-10
CN113785079B (zh) 2024-04-05
EP3719148A1 (en) 2020-10-07
CA3135144A1 (en) 2020-10-08
CN113785078B (zh) 2023-10-27
KR20210149123A (ko) 2021-12-08
EP3719149B1 (en) 2023-03-22
US20220177997A1 (en) 2022-06-09
WO2020201437A1 (en) 2020-10-08
CN113785079A (zh) 2021-12-10
BR112021019860A2 (pt) 2021-12-07
SI3719148T1 (sl) 2023-06-30
EP3719149A1 (en) 2020-10-07
JP2022528420A (ja) 2022-06-10

Similar Documents

Publication Publication Date Title
US20220177996A1 (en) High-Hardness Steel Product and Method of Manufacturing the Same
EP2157203B1 (en) High-strength steel sheet superior in formability
US11111553B2 (en) High-strength steel sheet and method for producing the same
US10196705B2 (en) Martensitic steel with delayed fracture resistance and manufacturing method
US9028626B2 (en) Method for manufacturing high strength galvanized steel sheet with excellent formability
EP2546375B1 (en) High-strength pressed member and method for producing same
US20180044759A1 (en) High-strength air-hardening multi-phase steel comprising outstanding processing properties and method for the production of a steel strip from said steel
CN110621794B (zh) 具有优异延展性和可拉伸翻边性的高强度钢片
US20210269892A1 (en) High-strength steel sheet having excellent impact resistant property and method for manufacturing thereof
US20210054473A1 (en) Steel composition in accordance with api 5l psl-2 specification for x-65 grade having enhanced hydrogen induced cracking (hic) resistance, and method of manufacturing the steel thereof
US20220186335A1 (en) Ultra-high strength steel sheet having excellent shear workability and method for manufacturing same
US20220042131A1 (en) Pressure vessel steel having excellent hydrogen induced cracking resistance, and manufacturing method therefor
KR20220088903A (ko) 강판 및 도금 강판
KR101889189B1 (ko) 수소유기균열 저항성이 우수한 인장강도 450MPa급 후육 강재 및 그 제조방법
CN113166898A (zh) 具有优异的氢致开裂抗力的压力容器用钢板和制造其的方法
US11981975B2 (en) High-strength steel sheet having excellent impact resistant property and method for manufacturing thereof
EP4180544A1 (en) A hot-rolled steel strip product and method for its production
US20230416860A1 (en) High yield ratio and high strength steel sheet having excellent thermal stability, and manufacturing method therefor

Legal Events

Date Code Title Description
AS Assignment

Owner name: SSAB TECHNOLOGY AB, SWEDEN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HEMMILA, MIKKO;LIIMATAINEN, TOMMI;VIROLAINEN, ESA;AND OTHERS;SIGNING DATES FROM 20211108 TO 20211109;REEL/FRAME:058134/0784

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION