US20220007782A2 - Textiles and articles and processes for making the same - Google Patents

Textiles and articles and processes for making the same Download PDF

Info

Publication number
US20220007782A2
US20220007782A2 US16/945,441 US202016945441A US2022007782A2 US 20220007782 A2 US20220007782 A2 US 20220007782A2 US 202016945441 A US202016945441 A US 202016945441A US 2022007782 A2 US2022007782 A2 US 2022007782A2
Authority
US
United States
Prior art keywords
textile
polymeric composition
yarn
yarns
article
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US16/945,441
Other languages
English (en)
Other versions
US11998080B2 (en
US20210030109A1 (en
Inventor
Devon Frazier
Walter Hancock
Dave Klinger
Robert Mervar
Brian Prevo
Hilary Walker
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nike Inc
Original Assignee
Nike Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nike Inc filed Critical Nike Inc
Priority to US16/945,441 priority Critical patent/US11998080B2/en
Priority claimed from US16/945,441 external-priority patent/US11998080B2/en
Publication of US20210030109A1 publication Critical patent/US20210030109A1/en
Assigned to NIKE, INC. reassignment NIKE, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KLINGER, Dave, HANCOCK, WALTER M., PREVO, BRIAN G., FRAZIER, Devon, MERVAR, ROBERT, WALKER, HILARY
Publication of US20220007782A2 publication Critical patent/US20220007782A2/en
Application granted granted Critical
Publication of US11998080B2 publication Critical patent/US11998080B2/en
Active legal-status Critical Current
Adjusted expiration legal-status Critical

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B5/00—Footwear for sporting purposes
    • A43B5/02—Football boots or shoes, i.e. for soccer, football or rugby
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B1/00—Footwear characterised by the material
    • A43B1/0018—Footwear characterised by the material made at least partially of flexible, bellow-like shaped material
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B1/00—Footwear characterised by the material
    • A43B1/02—Footwear characterised by the material made of fibres or fabrics made therefrom
    • A43B1/028—Synthetic or artificial fibres
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B1/00—Footwear characterised by the material
    • A43B1/02—Footwear characterised by the material made of fibres or fabrics made therefrom
    • A43B1/04—Footwear characterised by the material made of fibres or fabrics made therefrom braided, knotted, knitted or crocheted
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B1/00—Footwear characterised by the material
    • A43B1/14—Footwear characterised by the material made of plastics
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B13/00—Soles; Sole-and-heel integral units
    • A43B13/02—Soles; Sole-and-heel integral units characterised by the material
    • A43B13/026—Composites, e.g. carbon fibre or aramid fibre; the sole, one or more sole layers or sole part being made of a composite
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B13/00—Soles; Sole-and-heel integral units
    • A43B13/02—Soles; Sole-and-heel integral units characterised by the material
    • A43B13/04—Plastics, rubber or vulcanised fibre
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B13/00—Soles; Sole-and-heel integral units
    • A43B13/02—Soles; Sole-and-heel integral units characterised by the material
    • A43B13/12—Soles with several layers of different materials
    • A43B13/122—Soles with several layers of different materials characterised by the outsole or external layer
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B13/00—Soles; Sole-and-heel integral units
    • A43B13/14—Soles; Sole-and-heel integral units characterised by the constructive form
    • A43B13/22—Soles made slip-preventing or wear-resisting, e.g. by impregnation or spreading a wear-resisting layer
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0205—Uppers; Boot legs characterised by the material
    • A43B23/0215—Plastics or artificial leather
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0205—Uppers; Boot legs characterised by the material
    • A43B23/0225—Composite materials, e.g. material with a matrix
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0205—Uppers; Boot legs characterised by the material
    • A43B23/0235—Different layers of different material
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0245—Uppers; Boot legs characterised by the constructive form
    • A43B23/025—Uppers; Boot legs characterised by the constructive form assembled by stitching
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0245—Uppers; Boot legs characterised by the constructive form
    • A43B23/0255—Uppers; Boot legs characterised by the constructive form assembled by gluing or thermo bonding
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0245—Uppers; Boot legs characterised by the constructive form
    • A43B23/026—Laminated layers
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B5/00—Footwear for sporting purposes
    • A43B5/001—Golf shoes
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B5/00—Footwear for sporting purposes
    • A43B5/06—Running shoes; Track shoes
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B5/00—Footwear for sporting purposes
    • A43B5/14—Shoes for cyclists
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/002—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor characterised by the choice of material
    • B29C51/004—Textile or other fibrous material made from plastics fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/12—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor of articles having inserts or reinforcements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/14—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor using multilayered preforms or sheets
    • B29C51/145—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor using multilayered preforms or sheets having at least one layer of textile or fibrous material combined with at least one plastics layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/12—Layered products comprising a layer of synthetic resin next to a fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/40—Layered products comprising a layer of synthetic resin comprising polyurethanes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/026—Knitted fabric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
    • B32B5/24—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer
    • B32B5/245—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it being a foam layer
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
    • D02G3/00—Yarns or threads, e.g. fancy yarns; Processes or apparatus for the production thereof, not otherwise provided for
    • D02G3/22—Yarns or threads characterised by constructional features, e.g. blending, filament/fibre
    • D02G3/36—Cored or coated yarns or threads
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04B—KNITTING
    • D04B1/00—Weft knitting processes for the production of fabrics or articles not dependent on the use of particular machines; Fabrics or articles defined by such processes
    • D04B1/14—Other fabrics or articles characterised primarily by the use of particular thread materials
    • D04B1/16—Other fabrics or articles characterised primarily by the use of particular thread materials synthetic threads
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
    • D06M15/21—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M15/227—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds of hydrocarbons, or reaction products thereof, e.g. afterhalogenated or sulfochlorinated
    • D06M15/233—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds of hydrocarbons, or reaction products thereof, e.g. afterhalogenated or sulfochlorinated aromatic, e.g. styrene
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/70—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment combined with mechanical treatment
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B9/00—Footwear characterised by the assembling of the individual parts
    • A43B9/02—Footwear stitched or nailed through
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2009/00—Use of rubber derived from conjugated dienes, as moulding material
    • B29K2009/06—SB polymers, i.e. butadiene-styrene polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/48—Wearing apparel
    • B29L2031/50—Footwear, e.g. shoes or parts thereof
    • B29L2031/504—Soles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/48—Wearing apparel
    • B29L2031/50—Footwear, e.g. shoes or parts thereof
    • B29L2031/505—Uppers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/536—Hardness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2437/00—Clothing
    • B32B2437/02—Gloves, shoes
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2101/00—Chemical constitution of the fibres, threads, yarns, fabrics or fibrous goods made from such materials, to be treated
    • D06M2101/16—Synthetic fibres, other than mineral fibres
    • D06M2101/30—Synthetic polymers consisting of macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M2101/32—Polyesters
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2101/00—Chemical constitution of the fibres, threads, yarns, fabrics or fibrous goods made from such materials, to be treated
    • D06M2101/16—Synthetic fibres, other than mineral fibres
    • D06M2101/30—Synthetic polymers consisting of macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M2101/34—Polyamides
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2200/00—Functionality of the treatment composition and/or properties imparted to the textile material
    • D06M2200/35—Abrasion, pilling or fibrillation resistance
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2200/00—Functionality of the treatment composition and/or properties imparted to the textile material
    • D06M2200/40—Reduced friction resistance, lubricant properties; Sizing compositions
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/02—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyamides
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/04—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyesters, e.g. polyethylene terephthalate [PET]
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/10—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyurethanes
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/04—Heat-responsive characteristics
    • D10B2401/041—Heat-responsive characteristics thermoplastic; thermosetting
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/06—Load-responsive characteristics
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/06—Load-responsive characteristics
    • D10B2401/061—Load-responsive characteristics elastic
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/06—Load-responsive characteristics
    • D10B2401/063—Load-responsive characteristics high strength
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2501/00—Wearing apparel
    • D10B2501/04—Outerwear; Protective garments
    • D10B2501/043—Footwear

Definitions

  • vulcanized rubber has been used to provide traction and abrasion resistance to articles such as apparel, footwear and sporting equipment.
  • the need to vulcanize the rubber at high temperatures and/or pressures typically makes it necessary to form a separate vulcanized rubber component which is then affixed to the article using adhesives or stitching or both, as other components of the article may not be able to withstand the temperatures and/or pressures required by the vulcanization process.
  • crosslinked polyurethanes can be used as durable covering layers, synthetic leather textiles, or laminate film layers.
  • a need remains for new materials that can provide the same types of protection as vulcanized rubber or crosslinked polyurethane in addition to traction or abrasion resistance or both, and for new ways of incorporating these materials into articles.
  • FIG. 1B is a bottom and side perspective view of the article of footwear of FIG. 1A , in accordance with aspects of the present invention.
  • FIG. 1C is a top and side perspective view of an alternative aspect of the article of footwear of FIG. 1A in accordance with aspects of the present invention.
  • FIG. 3 is a plan view of a schematic depiction of a textile having three types of textile zones, in accordance with aspects of the present invention.
  • FIGS. 4A-4J depict exemplary knit structures in accordance with aspects of the present invention.
  • FIG. 5B is a schematic representation of the interconnected courses of loops of FIG. 5A after being exposed to a thermoforming process, and showing the middle course of loops being transformed into a component including re-flowed polymeric composition which no longer has the configuration of a yarn upon thermoforming, where the two outer courses of loops remain in the configuration of yarns, in accordance with aspects of the present invention.
  • FIG. 7A shows a textile comprising coated yarns according to the present disclosure prior to thermoforming
  • FIG. 7B shows the same textile after thermoforming
  • FIG. 7C shows a textile comprising coated yarns and an additional yarn according to the present disclosure prior to thermoforming
  • FIG. 7D shows the same textile after thermoforming
  • FIG. 7E shows a textile comprising coated yarns on both a top and bottom face of the textile and incorporating coated yarns in the core of the textile prior to thermoforming
  • FIG. 7F shows the same textile after thermoforming.
  • FIGS. 8A-8M show various articles of footwear, apparel, athletic equipment, container, electronic equipment, and vision wear in accordance with the present disclosure.
  • FIGS. 8N (a)- 8 Q(e) illustrate additional details regarding different types of footwear.
  • Thermoplastic elastomers have been identified which can be incorporated into polymeric compositions that provide levels of abrasion resistance, traction, or both, making them suitable for use in articles where abrasion resistance or traction are desirable, such as articles of apparel, footwear and sporting equipment.
  • the level of abrasion resistance, traction, or both provided by these polymeric compositions are equivalent to or better than standard vulcanized rubber compositions used in the manufacture of footwear, apparel and sporting equipment.
  • Unlike vulcanized rubber due to the thermoplastic nature of these polymeric compositions, and their properties in the solid and molten state, it is possible to readily form them into coated yarns which have suitable properties for use in industrial scale knitting or weaving equipment.
  • the polymeric compositions disclosed herein retain their favorable properties after repeated cycles of melting and re-solidifying, making it possible to first use them to coat yarns, and then thermoform the yarns to create re-flowed structures which retain their abrasion resistance, traction properties, or both. Additionally, due to the compatibility of these polymeric compositions with other materials commonly used to make articles of footwear, apparel as sporting equipment such as polyurethanes, polyesters and polyamides, the thermoforming process may securely bond the polymeric composition to the other components, making it unnecessary to use adhesives or stitching to attach the textiles to the other component, thereby reducing the number of manufacturing steps and avoiding the use of toxic primers and adhesives.
  • the coated yarns disclosed herein include a core yarn and a first coating.
  • the core yarn can comprise a conventional monofilament or multifilament yarn such as a commercially available polyester or polyamide yarn having properties (such as denier and tenacity) sufficient for it to be manipulated by industrial-scale knitting equipment.
  • the first coating of the coated yarn comprises a polymeric composition which is a thermoplastic elastomeric composition. While it is possible to extrude a polymeric composition which is a thermoplastic elastomeric composition and form fibers, filaments, yarns or films directly from the polymeric composition, due to its elastomeric properties, these forms of the polymeric composition will have high levels of stretch and heat shrinkage.
  • the fibers, filaments, yarns or films may tend to stretch around machine guides rather than slide past them, and may tend to shrink at the temperatures commonly encountered in industrial-scale knitting and weaving equipment.
  • the polymeric composition as a coating onto a core yarn which is suitable to be mechanically manipulated, the resulting coated yarn retains the tenacity and stretch resistance of the core yarn, while also providing an outer surface having superior traction and abrasion resistance provided by the polymeric composition due to its elastomeric properties.
  • thermoplastic nature of the polymeric composition makes it possible to melt the composition and use it to coat the core yarn when the melting temperature of the polymeric composition is sufficiently lower than the deformation temperature of the core yarn, as well as to subsequently thermoform the textile to create a thermoformed network comprising both the core yarn and the re-flowed and re-solidified polymeric composition consolidating the core yarn.
  • the textile includes one or more second yarn in addition of the coated yarn, the thermoformed network of yarns (i.e., the core yarn and the one or more second yarn) are consolidated by the re-flowed and re-solidified polymeric composition.
  • the presence of the re-flowed and re-solidified polymeric composition can serve one or more functions within the thermoformed textile, such as controlling the level of stretch within the entire textile or just within a region of the textile, forming a skin having high abrasion-resistance and/or traction across an entire surface of the textile or just within a region of the textile, improving water resistance of an entire surface of the textile or just within a region of the textile, or bonding all of the textile or just a region of the textile to a substrate.
  • Use of the coated yarn in these textiles can also reduce the number of different materials required to form an article.
  • the coating of the coating yarn, when thermoformed, can form a skin on a surface of the textile.
  • thermoformed textiles comprising coated yarns as described herein can be used to form uppers for articles of footwear.
  • the thermoformed network of the thermoformed textile can form an externally-facing surface of an upper, such as an upper for a global football boot.
  • the thermoformed network formed by thermoforming the textiles has superior properties for ball contact, in that the properties of the thermoformed network can be equal to or superior to those of kangaroo skin leather in terms of the spin rate imparted to the ball by the upper when kicking the ball.
  • polymeric compositions having a Durometer hardness of about 65 to about 85 results in uppers with improved ball spin rates.
  • thermoformed textiles comprising coated yarns as described herein can be used to form outsoles for articles of footwear.
  • the thermoformed network of the thermoformed textile can form an externally-facing surface of an outsole, including a ground-facing surface or a ground-contacting surface of an outsole.
  • cross-linked polymeric compositions such as vulcanized rubber or cross-linked polyurethanes have been used for outsoles due to their high levels of abrasion resistance and traction.
  • the use of the textiles including coated yarns comprising polymeric coatings disclosed herein can be used to replace cross-linked polymeric compositions as outsole materials, while retaining the high levels of traction and abrasion resistance required for outsoles.
  • the present disclosure is directed to a textile comprising a first network of yarns including a first coated yarn, wherein the first coated yarn comprises a core yarn and a first coating, wherein the first coating comprises a first polymeric composition.
  • the first polymeric composition is a thermoplastic elastomeric composition, and comprises at least one thermoplastic elastomer.
  • the first network of yarns further comprises one or more second yarns.
  • the one or more second yarns can be coated yarns, or can be uncoated yarns.
  • the textile can be a knit textile, and the first network of yarns can include interconnected loops of the first coated yarn, or can include the first coated yarn inlaid in a knit structure formed of interconnecting loops of one or more second yarns.
  • the present disclosure is directed to a textile, comprising: a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to a textile, comprising: a thermoformed network of yarns, the thermoformed network comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to an upper for an article of footwear, comprising: a first textile comprising a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to an outsole for an article of footwear, comprising: a textile comprising a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to a method of making a textile, the method comprising: forming a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to a method of making an upper for an article of footwear, the method comprising: affixing a first textile to a second component, wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to a method of making an upper for an article of footwear, the method comprising: thermoforming an upper comprising a first textile, wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition within the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns.
  • the present disclosure is directed to a method of making an upper for an article of footwear, the method comprising: affixing a first textile to a second component, wherein the first textile comprises a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to a method for making an outsole for an article of footwear, the method comprising thermoforming a first textile; wherein the thermoforming comprises thermoforming the textile on a sole component, or on a molding surface, optionally wherein the molding surface is a molding surface having the dimensions of the outsole; wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition within the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between
  • the present disclosure is directed to a method of making an article, comprising: affixing a first textile to a second component, wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is directed to a method of making an article, the method comprising: thermoforming a first textile, wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition within the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns.
  • the present disclosure is directed to a method of making an article, the method comprising: affixing a first textile to a second component, wherein the first textile comprises a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition; optionally wherein the article is a component of an article of footwear, apparel or sporting equipment, or is an article of footwear, apparel or sporting equipment.
  • the present disclosure is directed to an outsole for an article of footwear, comprising:
  • thermoformed network of yarns is the thermoformed product of a first textile comprising a first network of yarns including a first coated yarn comprising the first core yarn and a first coating, the first coating comprising the first polymeric composition, the first core yarn comprising a second polymeric composition, wherein the first coating is axially centered surrounding the core yarn, a nominal average outer diameter of the coated yarn is up to about 1.0 millimeter, the first coating has an average radial coating thickness of about 50 micrometers to about 200 micrometers, and wherein, in the thermoformed network, the first polymeric composition consolidating the thermoformed network of yarns is the re-flowed and re-solidified product of the first polymeric composition of the first coating of the first coated yarn;
  • the first thermoplastic composition has a first melting temperature greater than about 110 degrees Celsius and less than about 190 degrees Celsius
  • the second polymeric composition of the core yarn has a second deformation temperature
  • the second deformation temperature is at least 50 degrees Celsius greater than the first melting temperature of the first polymeric composition
  • thermoformed network defines at least a portion of a surface of the outsole configured to be externally-facing or ground-facing or ground-contacting when the outsole is part of a finished article of footwear.
  • the present disclosure is directed to an upper for an article of footwear, comprising:
  • thermoformed network of interlooped yarns comprising a first core yarn and a first polymeric composition
  • first polymeric composition consolidates the thermoformed network of interlooped yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns
  • first polymeric composition comprises a thermoplastic elastomeric polyurethane
  • the first polymeric composition has a Durometer Hardness using a Shore A scale of from about 70 to about 80, as determined using the Durometer Hardness Test
  • thermoformed network of yarns is the thermoformed product of a first textile comprising a first network of yarns including a first coated yarn comprising the first core yarn and a first coating, the first coating comprising the first polymeric composition, the first core yarn comprising a second polymeric composition, wherein the first coating is axially centered surrounding the core yarn, a nominal average outer diameter of the coated yarn is up to about 1.0 millimeter, the first coating has an average radial coating thickness of about 50 micrometers to about 200 micrometers, and wherein, in the thermoformed network, the first polymeric composition consolidating the thermoformed network of yarns is the re-flowed and re-solidified product of the first polymeric composition of the first coating of the first coated yarn;
  • the first thermoplastic composition has a first melting temperature greater than about 110 degrees centigrade and less than about 190 degrees centigrade
  • the second polymeric composition of the core yarn has a second deformation temperature
  • the second deformation temperature is at least 50 degrees centigrade greater than the first melting temperature of the first polymeric composition
  • thermoformed network of the textile defines at least a portion of a surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear;
  • the present disclosure is directed to an outsole for an article of footwear, comprising:
  • thermoformed network of yarns comprising a first core yarn and a first polymeric composition
  • first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns
  • first polymeric composition comprises a thermoplastic elastomeric styrenic copolymer, wherein the first polymeric composition has a Durometer Hardness of from about 70 to about 80 Shore A, as determined using the Durometer Hardness Test;
  • thermoformed network of yarns is the thermoformed product of a first textile comprising a first network of yarns including a first coated yarn comprising the first core yarn and a first coating, the first coating comprising the first polymeric composition, the first core yarn comprising a second polymeric composition, wherein the first coating is axially centered surrounding the core yarn, a nominal average outer diameter of the coated yarn is up to about 1.0 millimeter, the first coating has an average radial coating thickness of about 50 micrometers to about 200 micrometers, and wherein, in the thermoformed network, the first polymeric composition consolidating the thermoformed network of yarns is the re-flowed and re-solidified product of the first polymeric composition of the first coating of the first coated yarn;
  • the first thermoplastic composition has a first melting temperature greater than about 110 degrees Celsius and less than about 190 degrees Celsius
  • the second polymeric composition of the core yarn has a second deformation temperature
  • the second deformation temperature is at least 50 degrees Celsius greater than the first melting temperature of the first polymeric composition
  • the present disclosure is directed to an upper for an article of footwear, comprising:
  • thermoformed network of yarns is the thermoformed product of a first textile comprising a first network of yarns including a first coated yarn comprising the first core yarn and a first coating, the first coating comprising the first polymeric composition, the first core yarn comprising a second polymeric composition, wherein the first coating is axially centered surrounding the core yarn, a nominal average outer diameter of the coated yarn is up to about 1.0 millimeter, the first coating has an average radial coating thickness of about 50 micrometers to about 200 micrometers, and wherein, in the thermoformed network, the first polymeric composition consolidating the thermoformed network of yarns is the re-flowed and re-solidified product of the first polymeric composition of the first coating of the first coated yarn;
  • the first thermoplastic composition has a first melting temperature greater than about 110 degrees centigrade and less than about 190 degrees centigrade
  • the second polymeric composition of the core yarn has a second deformation temperature
  • the second deformation temperature is at least 50 degrees centigrade greater than the first melting temperature of the first polymeric composition
  • thermoformed network of the textile defines at least a portion of a surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear;
  • the deformation temperature of the polymeric composition of the core yarn is at least 20 degrees Celsius higher than the melting temperature of the polymeric composition of the coating. This allows the core yarn to be coated by the coating when the coating is in a molten state.
  • the thermoplastic elastomer(s) of the polymeric composition of the coating have glass transition temperature(s) below minus 20 degrees Celsius. This allows the thermoplastic elastomer(s) present in the polymeric composition to be in their “rubbery” state, even when the article comprising the textile is used in cold environments.
  • the melting temperature of polymeric composition of the coating is at least 100 degrees Celsius. This ensures the polymeric composition will not melt when the article comprising the textile is shipped or stored under hot conditions.
  • the melting temperature of polymeric composition of the coating is at least 130 degrees Celsius. This ensures the polymeric composition will not melt when the article comprising the textile is subjected to conditions often encountered by textiles during the manufacturing processes for articles of footwear, apparel or sporting equipment, such as steaming processes.
  • the melting temperature of polymeric composition of the coating is at less than 170 degrees Celsius. This ensures the textile can be thermoformed at temperatures which do not negatively impact other textiles or components which may form part of the textile or article comprising the textile. For example, dye may migrate out of package-dyed polyester yarns when they are exposed to temperatures greater than 150 degrees Celsius for extended periods of time.
  • the enthalpy of melting of the thermoplastic elastomer(s) of the polymeric composition of the coating can be less than about 30 Joules per gram or 25 Joules per gram.
  • a lower melting enthalpy means that, during the thermoforming process, less heat and a shorter heating time is required to fully melt the polymeric composition and achieve good flow of the molten polymeric composition to better consolidate the network of yarns in the textile.
  • the recrystallization temperature of thermoplastic elastomer(s) of the polymeric composition of the coating can be above 60 degrees Celsius, or above 95 degrees Celsius.
  • a higher recrystallization temperature promotes rapid re-solidification of the polymeric composition after thermoforming, which can reduce the amount of time required to cool the textile after thermoforming, and may avoid the need to provide active cooling of the textile, thereby reducing cycle time and reducing energy consumption.
  • the present disclosure is directed to a film, fiber, filament or yarn comprising a first polymeric composition comprising at least one thermoplastic elastomer.
  • the present disclosure is also directed to process for manufacturing a film, fiber, filament or yarn, comprising using a first polymeric composition comprising at least one thermoplastic elastomer to form the film, fiber, filament or yarn.
  • the present disclosure is also directed to a textile comprising a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the present disclosure is also directed to an article comprising: a first polymeric composition, wherein the first polymeric composition is a reflowed and re-solidified product of a film, fiber, filament or yarn as described herein; and a second element selected from a second shaped component, a second film, a second fiber, a second filament, a second yarn, or a second textile.
  • the films comprising a first polymeric composition comprising at least one thermoplastic elastomer.
  • the first polymeric composition of the film can be a low processing temperature polymeric composition.
  • the film can be a multi-layered film comprising a first layer comprising the first thermoplastic elastomer.
  • the multi-layered film can be a bilayer film comprising a first layer comprising the first thermoplastic elastomer and a second layer comprising a second polymeric material.
  • the second polymeric material can be a second thermoplastic composition comprising a second thermoplastic elastomer.
  • the multi-layered film can be formed by co-extrusion or lamination.
  • the “fiber” is understood to be a fiber suitable for use in a yarn or a textile.
  • a fiber has a small diameter relative to its length, where its length is discrete, e.g., a cut or staple fiber include filaments.
  • the fiber can be a single-component fiber composed of one thermoplastic composition.
  • the fiber can be a bi-component fiber composed of two thermoplastic compositions.
  • the fiber can be a multi-component fiber composed of three or more thermoplastic compositions.
  • filaments comprising the first polymeric composition comprising at least one thermoplastic elastomer.
  • the “filament” is understood to be filament suitable for use in a yarn or a textile.
  • a filament has a small diameter relative to its length, where its length is many orders of magnitude greater than its diameter, such as a silk filament or extruded filament, or can be substantially continuous, such as an extruded filament.
  • the filament can be a single-component filament composed of one thermoplastic composition.
  • the filament can be a bi-component filament composed of two thermoplastic compositions.
  • the filament can be a multi-component fiber composed of three or more thermoplastic compositions.
  • the yarn comprises a coating of a first polymeric composition comprising at least one thermoplastic elastomer.
  • the yarns can be formed using staple fibers or continuous filaments comprising of the thermoplastic composition.
  • the fibers or filaments used to produce the yarn comprise a single polymeric composition.
  • the first polymeric composition can be a low processing temperature polymeric composition.
  • the yarn can be a coated yarn having a core, wherein the core comprises a high processing temperature polymeric composition, and the coating comprises the low processing temperature polymeric composition.
  • the yarn can comprise fibers, filaments, cores and/or coatings formed from two or more different polymeric compositions.
  • a textile comprising a first film, fiber, filament or yarn described herein.
  • the textile further includes a second yarn, where the second yarn is different from the first yarn (e.g., comprises at least one thermoplastic elastomer that differs from a thermoplastic elastomer of the first polymeric composition based on molecular weight, polymeric structure, melting temperature, melt flow index, hardness, or modulus).
  • the second yarn is substantially free of a thermoplastic elastomer.
  • the first yarn and second yarn can be used so as to form separate zones of the textile.
  • the first yarn can form a majority of a first surface of the textile
  • the second yarn can form a majority of a second surface opposing the first surface of the textile.
  • the first yarn and the second yarn can be laid down in a first zone and an adjacent second zone, wherein the first zone comprises an increased concentration of the second yarn compared to the second zone.
  • the first yarn and the second yarn can be laid down in a first zone, a second zone, and a third zone, the second zone positioned between the first and third zones, wherein the first zone comprises an increased concentration of the second yarn compared to the second zone, and wherein the third zone comprises an increased concentration of the first yarn compared to the second zone.
  • a woven textile comprising a first film, fiber, filament, or yarn as described herein.
  • the woven textile further includes a second film, fiber, filament or yarn, where the second yarn has a higher melting or deformation temperature from the first yarn.
  • the second film, fiber, filament or yarn is substantially free of a thermoplastic elastomer. The first film, fiber, filament or yarn and the second film, fiber, filament or yarn can be used to form separate zones of the woven thermoformed textile.
  • a knit or crochet textile comprising a first film, fiber, filament or yarn as described herein.
  • the knit or crochet textile can optionally further include a second film, fiber, filament or yarn, where the second film, fiber, filament or yarn has a higher melting temperature or deformation temperature from the first film, fiber, filament or yarn
  • the second film, fiber, filament or yarn is substantially free of a thermoplastic elastomer.
  • a first yarn and a second yarn can at least partly form a plurality of interconnected courses in at least one knit layer of a knit textile.
  • the knit or crochet textile can include interconnected loops comprising a second yarn and inlaid portions comprising the first film, fiber, filament or yarn, wherein the second yarn has a melting temperature or deformation temperature greater than the melting temperature of the first polymeric composition.
  • the knit textile can be a knit article having a substantially seamless configuration.
  • the entire knit article can be seamless.
  • the seamless knit article may, for example, be provided by circular knitting.
  • a circular knit article can allow a three-dimensionally preshaped article to be provided without having to be sewn up at a designated place(s). Thus, unwanted seams in the knit article can be avoided and the three-dimensionally preshaped knit article can have a particularly good fit and the additional aforementioned benefits of a seamless structure.
  • the knit textile can be a knit article formed of unitary knit construction.
  • a knit article is defined as being formed of “unitary knit construction” when formed as a one-piece element through a knitting process. That is, the knitting process substantially forms the various features and structures of the knit article without the need for significant additional manufacturing steps or processes.
  • portions of the knit article can be joined to each other (e.g., edges of the knit article being joined together, as at seam) following the knitting process, the knit article remains formed of unitary knit construction because it is formed as a one-piece knit element.
  • the knit article can further comprise other elements (e.g., a tongue, a strobel, a lace, a heel counter, logos, trademarks, placards) that can be added following the knitting process.
  • the knit textile may have one type of yarn in one area of the knit textile and another type of yarn in another area of the knit textile, e.g., a yarn comprising a first polymeric composition in one area of the knit textile and a yarn comprising a second polymeric composition, such as a thermoplastic composition, in another area of the knit textile.
  • the knit textile can incorporate yarns with different deniers, materials (e.g., cotton, elastane, polyester, rayon, wool, and nylon), and degrees of twist, for example.
  • the different types of yarns may affect the physical properties of the knit textile, including aesthetics, stretch, thickness, air permeability, and abrasion-resistance.
  • each area knit article can have specific properties that enhance the comfort, durability, and performance of the knit textile as required by its use in an article of footwear, article of apparel, or article of sporting equipment.
  • a composite element can comprise a first textile prepared as disclosed herein, along with a second textile or a film or a shaped component. That is, the composite element comprises a first textile region and a second region selected from a region comprising a second textile, a region comprising a film, a region comprising a shaped component, or combinations thereof.
  • thermoformed textile is provided according to the present disclosure.
  • a thermoformed textile is understood to be a textile comprising the first polymeric composition that has been thermoformed to have a different shape or texture or both.
  • the thermoforming can be conducted on a substantially flat surface such as a plate, or in a shaped mold, or on a shaped article such as a last.
  • the thermoformed textile is a textile in which at least a portion of the first polymeric composition present in the textile has been thermoformed (i.e., softened, molded and re-solidified, or melted, molded and re-solidified, such that at least a portion of the first network of yarns of the textile becomes a thermoformed network of yarns in which the first polymeric composition of the coated yarn consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns).
  • the first polymeric composition of a thermoformed textile has a different physical shape than before it was thermoformed and retains this second shape until the first polymeric composition is thermoformed again.
  • the thermoforming process re-flows the first polymeric composition from a first state as a first film to a second state in which the first polymeric composition penetrates into or between portions of the textile which had surrounded the first film.
  • the molten first polymeric composition may penetrate between or into second fibers, filaments or yarns of the textile, and may, when re-solidified, act as a consolidating resin for the second fibers, filaments or yarns.
  • the thermoforming process re-flows the plurality of fibers, filament, plurality of filaments, yarn, plurality of yarns, or any combination thereof, into a second state, in which the first polymeric composition no longer has a fibrous, filamentous, or yarn-like configuration.
  • thermoformed textile comprising the first polymeric composition can be a thermoformed textile wherein at least a portion of the film, plurality of fibers, filament, plurality of filaments, yarn, yarns, or any combination thereof have been at least partially melted and re-solidified into a new conformation which is different than their original (i.e., pre-thermoforming) conformation.
  • the thermoformed textile can comprise a partially re-flowed structure in which only a portion of the first polymeric composition present in the textile has been re-flowed, or an essentially completely re-flowed structure in which substantially all of the first polymeric composition present in the textile has been re-flowed.
  • the thermoformed textile can also include a second plurality of fibers including a second polymeric composition, such as a second polymeric composition comprising a second thermoplastic elastomer.
  • a second polymeric composition such as a second polymeric composition comprising a second thermoplastic elastomer.
  • zones or regions of the textile can be thermoformed into continuous, film-like layers, or thermoformed and molded to adopt desired surface topographies.
  • an upper for an article of footwear comprising a textile, wherein the textile comprises a first network of yarns including a first coated yarn, where the first coated yarn comprises a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the textile defines at least a portion of a surface of the upper configured to be externally facing when the upper is part of a finished article of footwear.
  • the textile or thermoformed textile is an outsole for an article of footwear or is a component of an article of footwear.
  • the textile or thermoformed textile is a rand or zone bridging a region between a footwear upper and the sole structure.
  • the textile or thermoformed textile is a combination upper and outsole for an article of footwear, wherein the upper includes an integrated outsole area.
  • the upper and the integrated outsole area are at least partially formed from a textile.
  • the outsole or outsole area can be configured to include a ground-facing surface but not a ground-contacting surface, and at least a portion of the textile defines at least a portion of the ground-facing surface, and wherein the at least a portion of the textile defines the at least a portion of the ground-facing surface is textured, or includes at least one traction element, or both.
  • the at least one traction element can a thermoformed traction element formed from the textile.
  • the textile or thermoformed textile as described herein can be a component of an article of apparel.
  • the textile can define an externally-facing surface of the article of apparel.
  • the textile or thermoformed textile can be used to provide abrasion resistance or traction or both to at least a portion of the article of apparel, such as, for example on an elbow area, a knee area, or both.
  • the textile or thermoformed textile can be used to provide protection to electronic components embedded in or attached to the article of apparel.
  • the textile or thermoformed textile can be used to provide protection to a wearer from hard or sharp components embedded in or attached to the article of apparel.
  • thermoformed film component as described herein can be a component of an article of footwear.
  • the thermoformed film component can be used to provide abrasion resistance or traction or both to at least a portion of the article of footwear.
  • the first polymeric composition can define an externally-facing surface of the article of footwear.
  • the thermoformed film component is a component of an upper for an article of footwear.
  • the outsole or outsole area can be configured to include a ground-facing surface but not a ground-contacting surface, and at least a portion of the first polymeric composition defines at least a portion of the ground-facing surface, and wherein the at least a portion of the first polymeric composition defines the at least a portion of the ground-facing surface is textured, or includes at least one traction element, or both.
  • the at least one traction element can a thermoformed traction element formed from the textile.
  • the present disclosure is also directed to articles comprising: a textile comprising a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition; and a second element selected from a second shaped component, a second film, a second fiber, a second filament, a second yarn, or a second textile.
  • the article is an article of footwear, which includes, but is not limited to, such articles as shoes.
  • Article of footwear is used to refer to an article intended for wear on a human foot, e.g., in some aspects, an article of footwear can be a shoe, such as an athletic shoe.
  • Articles of footwear generally include an upper and a sole structure.
  • the upper provides a covering for the foot that comfortably receives and securely positions the foot with respect to the sole structure.
  • the upper generally provides protection for the foot and may provide other attributes such as weather resistance, water resistance, contact or interaction with athletic equipment, or the like.
  • the sole structure can provide various kinds of support, cushioning and shock absorption.
  • the sole structure is secured to a lower portion of the upper and is generally positioned between the foot and the ground.
  • An upper forms a structure that that provides a covering for some or all of a wearer's foot and positions that foot relative to a sole structure of that shoe.
  • the upper forms a void on the interior of the footwear for receiving the foot.
  • the void has the general shape of the foot, and access to the void can be provided at an ankle opening.
  • the upper extends over the instep and toe areas of the foot, along medial and lateral sides of the foot, and around the heel area of the foot.
  • the upper can have any design, shape, size and/or color. For example, in certain aspects, e.g., if an article is a basketball shoe, then the upper can be a high top upper that is shaped to provide high support on an ankle.
  • the upper can be a low top upper.
  • the upper or upper component can comprise a film, fiber, filament, yarn, textile, thermoformed textile, or thermoformed film component as described herein.
  • the upper can also incorporate a closure system such as a lacing system to permit entry and removal of the foot from the void within the upper. Additionally or alternatively, the upper can also incorporate an adjustment system to adjust fit of the footwear and/or provide lock-down between the upper and the sole structure.
  • a closure and/or adjustment system such as a lacing system often is incorporated into the upper to selectively change the size of the ankle opening and to permit the wearer to modify certain dimensions of the upper, particularly girth, to accommodate feet with varying proportions.
  • the upper can include a tongue that extends under the lacing system to enhance the comfort of the footwear (e.g., to modulate pressure applied to the foot by the laces).
  • the tongue can be attached at the base of the lacing structure; can be attached at the base of the lacing structure and on the medial side of the lacing structure, or on the lateral side of the lacing structure, or on both sides; or can be integrally formed with the upper.
  • the upper can include a heel counter to limit or control movement of the heel.
  • the upper can include a toe cap to provide abrasion resistance or protection or both to the toe box portion of the upper. Abrasion resistance, traction, or both can be provided in specific regions of the upper including on portions of the medial side, the lateral side, the instep region, or any combination thereof. For example, use of materials which provide increased levels of traction are useful on athletic footwear which may come into contact with a ball during use.
  • the upper can include a heel counter; a toe cap; an abrasion resistant region on the medial side, the lateral side, or the instep; a region of increased traction on the medial side, the lateral side, or the instep; or any combination thereof.
  • a textile including a thermoformed textile, as described herein defines at least a portion of an outer surface of the upper.
  • the textile as described herein defines at least a portion of the surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear, or defines at least a portion of a surface of the upper configured to be internally-facing when the upper is part of a finished article of footwear, or forms at least a portion of an interior layer of the upper when the upper is part of a finished article of footwear, or any combination thereof.
  • the textiles can be present on a lateral side of the upper, a medial side of the upper, a heel region of the upper, a toe region of the upper, or any combination thereof.
  • the textiles when the textiles form part or all of an upper for an article of footwear, the textiles can be present in a first layer and a second layer.
  • the first layer can be an outward facing layer and the second layer can be a base layer or internal layer that is not seen when the article of footwear is being worn.
  • the first layer and second layer can independently comprise a knitted textile, a crocheted textile, a braided textile, a woven textile, a non-woven textile, or some combination thereof.
  • the outsole includes the ground-contacting portions of the article of footwear.
  • durable, wear-resistant materials are used for outsoles.
  • the outsole or outsole component can comprise a film, fiber, filament, yarn, textile, thermoformed textile, or thermoformed film component as described herein.
  • Outsoles commonly include texturing or other features such as traction elements to improve traction.
  • the outsole can optionally further comprise one or more integrally formed or removable cleats.
  • the textile defines at least a portion of an externally-facing surface of the outsole, optionally wherein the externally-facing surface is configured to be ground-facing or ground-contacting when the outsole is part of a finished article of footwear. In another aspect, the textile defines at least a portion of the medial side or lateral side of the outsole.
  • a combination upper and outsole for an article of footwear is an integrated component which serves both as the upper of the article of footwear and as the outsole of the article of footwear.
  • conventional footwear formed by first forming a separate upper and a separate outsole, and then attaching the upper and the outsole to each other.
  • at least a portion of the upper area and the outsole area of the unit are formed at the same time, for example, by thermoforming one or more components on a last.
  • the combination upper and outsole unit comprises a single textile, thermoformed textile, or thermoformed film component which forms both at least a portion of the externally-facing surface of the upper and at least a portion of the ground-facing or ground-contacting surface of the outsole.
  • certain aspects are directed to one or more textiles, thermoformed textiles, or thermoformed film components that include the films, fibers, filaments or yarns as described herein.
  • such textiles, thermoformed textiles, or thermoformed film components can form at least a portion of an article of sporting equipment or article of wear, including articles of apparel and articles of footwear.
  • the disclosed textiles, thermoformed textiles, or thermoformed film components can form at least a portion of a component of an article of footwear.
  • the disclosed textiles, thermoformed textiles, or thermoformed film components can form at least a portion of a component of an article of sporting equipment.
  • FIGS. 1A and 1B an article of footwear 100 is depicted as one exemplary article of wear. While FIGS. 1A and 1B depict an article of footwear 100 , it should be understood that other articles of wear are also contemplated by the present disclosure.
  • the article of footwear 100 of FIGS. 1A and 1B generally can include a ground-facing outsole area 110 , an ankle collar area 112 , a lateral midfoot area 114 a , and a medial midfoot area 114 b , a toe box area 116 , and a heel area 118 .
  • another textile zone such as, for example, textile zone 108
  • the textile zone 108 can include the ankle collar area 112 , the tongue area 124 , and/or the throat area 126 of the article of footwear 100 .
  • another textile such as, for example, zone 106
  • the textile zone 106 can be positioned between the textile zones 104 and 108 .
  • the textile zone 106 can include at least a portion of the lateral midfoot region 114 a and/or the medial midfoot region 114 b on the article of footwear 100 .
  • the textile zone 106 can include a combination of a first film, fiber, filament or yarn described herein from the textile zone 104 with a second film, fiber, filament or yarn, such as, for example, the second film, fiber, filament or yarn from the textile zone 108 , where the second film, fiber, filament or yarn has different properties (e.g., melting temperature, deformation temperature, etc.) compared to the first film, fiber, filament or yarn.
  • this combination of textile media present in the textile zone 106 allows the textile zone 106 to function as a flexible, pliable portion of the upper and as an abrasion-resistant or high traction zone, and optionally as a transition between the outsole functionality of the textile zone 104 and the flexible pliable functionality of the textile zone 108 , allowing for a more gradual transition from the outsole portion to flexibility of the textile 102 .
  • only textile zone 104 comprises the first polymeric composition of the disclosure.
  • only textile zone 106 comprises the first polymeric composition of the present disclosure.
  • both textile zones 104 and 106 comprise the first polymeric composition, wherein a concentration of the first polymeric composition in textile zone 104 is greater (e.g., at least 10 weight percent greater, at least 20 weight percent greater, or at least 30 weight percent greater) than in textile zone 106 .
  • textile zone 108 is substantially free of the first polymeric composition of the disclosure.
  • the textile zone 106 can exhibit rigidity or semi-rigidity to a lesser extent than the textile zone 104 , but to a greater extent than the textile zone 108 . Also, in the same or alternative aspects, the textile zone 106 can exhibit flexibility to a lesser extent than the textile zone 108 , but to a greater extent than the textile zone 104 .
  • the three textile zones 104 , 106 and 108 can be at least partly located within a midfoot region, such as lateral midfoot region 114 a and/or medial midfoot region 114 b.
  • textile zones 104 , 106 and 108 can be formed of separate textiles operably connected to each other, a single textile having two or more integrally formed textile zones can be used.
  • a single upper and outsole unit comprises two or more separately formed or integral textile zones.
  • the combination of the first film, fiber, filament or yarn described herein is present in the textile zone 104 and a second film, fiber, filament or yarn described herein is present in the textile zone 108 .
  • the process can impart one or more structural properties to these zones making them appropriate for use in the article of footwear 100 , such as abrasion resistance, improved traction, semi-rigid support, or any combination thereof, in the lateral and/or medial midfoot regions 114 a and 114 b , and/or three-dimensional shape or structure suitable for one or more portions of the article of footwear 100 .
  • the textile zone 106 extends away from the textile zone 104 towards the eyestays 120 .
  • the combination of textile media comprising the first film, fiber, filament or yarn described herein and textile media comprising the second film, fiber, filament or yarn can allow for the transferring of a force transmitted from the eyestays 120 or other lacing mechanisms into this combination of textile media present in the lateral and/or medial midfoot regions 114 a and 114 b .
  • the flexible and pliable characteristics of the second film, fiber, filament or yarn that are present in the zone 108 that is adjacent the eyestays 120 can facilitate in transferring forces transmitted from the eyestays 120 to the textile zone 106 and/or the first films, fibers, filaments or yarns described herein present in the lateral and/or medial midfoot regions 114 a and 114 b.
  • the textile zone 106 is positioned in the toe box area 116 and the heel area 118 .
  • the combination of the first film, fiber, filament or yarn described herein and the second film, fiber, filament or yarn can provide structure and/or support due to the rigidity provided by the thermoformed material.
  • the thermoformed material can provide abrasion resistance or increased traction in the toe box area 116 and/or the heel area 118 .
  • the textile zone 104 can form at least a portion of the toe box area 116 and/or the heel area 118 for increased rigidity or increased abrasion resistance or traction, since the textile zone 104 includes a greater amount, or alternative positioning (e.g., outer knit surface), of the first film, fiber, filament or yarn described herein than the textile zone 106 .
  • a force applied through one or more of the plurality of eyestays 120 a can at least partly be transferred onto the rigid or semi-rigid portions 104 b and 104 c extending through the midfoot area 115 A, and into the rigid or semi-rigid textile zone 104 a present in an outsole area, providing increased support and comfort for a wearer.
  • FIGS. 2A and 2B depict a shirt 200 as an exemplary article of apparel.
  • the shirt 200 depicted in FIGS. 2A and 2B includes at least one textile, thermoformed textile, or thermoformed film component 202 that at least partly forms a portion of the shirt 200 .
  • the textile, thermoformed textile, or thermoformed film component 202 can be a textile or thermoformed textile which includes three separate textile zones 204 , 206 a - d , and 208 , which can identify specific functional areas of the 200 .
  • these specific functional areas are at least partly associated with the targeted incorporation of specific textile media in varying amounts and combinations into these textile zones 204 , 206 a - d , and 208 .
  • the textile zone 208 can exhibit flexibility and/or pliability similar to a conventional shirt material. Further, in certain aspects, the textile zone 206 can at least partly provide a transition within the textile 202 from the more rigid or semi-rigid patch 210 present in textile zone 204 to the more flexible pliable portion present in the textile zone 208 .
  • the textile zones 206 a - d can include a combination of the first film, fiber, filament or yarn described herein present in the textile zone 204 and the second film, fiber, filament or yarn present in the textile zone 208 . While not shown in FIGS. 2A and 2B , the textile zones 206 b - d also provide a transition to a flexible pliable material, such as that present in the textile zone 208 .
  • this combination of the first film, fiber, filament or yarn described herein from textile zone 204 and the second film, fiber, filament or yarn present from textile zone 208 can provide a seamless or integrated transition from the patch 210 to the flexible pliable portion found in textile zone 208 of the shirt 200 .
  • FIG. 3 a plan view of a schematic textile 300 is provided.
  • the textile 300 can be any type of textile known to one skilled in the art.
  • a non-limiting list of textiles that are suitable for use in the articles of wear and methods disclosed herein includes knit textiles, woven textiles, non-woven textiles, crocheted textiles, and braided textiles.
  • the textile 300 of FIG. 3 includes three types of textile zones.
  • the textile 300 includes a textile zone 302 that can include the first film, fiber, filament or yarn described herein, textile zones 306 a and 306 b that can include the second film, fiber, filament or yarn, and textile zones 304 a and 304 b that can include a combination of films, fibers, or yarns compose of different thermoplastic elastomers.
  • textile 300 of FIG. 3 includes a textile zone 302 that can include the first film, fiber, filament or yarn described herein, textile zones 306 a and 306 b that can include the second film, fiber, filament or yarn, and textile zones 304 a and 304 b that can include a combination of films, fibers, or yarns compose of different thermoplastic elastomers.
  • the textile zones 304 a and 304 b can be positioned on either side of textile zone 302 , while textile zones 306 a and 306 b can be positioned on the opposite sides of the textile zones 304 and 304 b , respectively.
  • the films, fibers, filaments, yarns, and textiles described herein when exposed to a thermoforming process, can impart a structural or functional property to an article of wear or sporting equipment.
  • the combination of first films, fibers, filaments, yarns described herein and second films, fibers, filaments, or yarns can provide structural support and three-dimensional structure for a particular article of wear or sporting equipment.
  • this combination of films, fibers, filaments, yarns, and textiles can provide an integrated transition between a rigid thermoformed material and flexible pliable fibers.
  • the zones can have varying concentration of the first and second films, fibers, filaments or yarns, and thus can have varying concentrations of the first polymeric composition and the second polymeric composition in these zones.
  • concentration refers to a clustering or congregation in a specific volume.
  • concentration includes measuring the amount (e.g., the weight in grams) of a material in a specified volume (e.g., cubic centimeter).
  • a first portion of a single knit layer of a textile can have an increased concentration of a first yarn compared to a second portion of the textile by having more stitches (e.g., knit stitches, tuck stitches, and/or float stitches) of that first yarn than the second portion of equal size.
  • a first portion of a textile can include a greater concentration of an inlaid film, fiber, filament or yarn than a second portion.
  • a first portion of the textile in a non-woven textile, can have an increased concentration of a first fiber if that textile was formed with more of the first fiber (e.g., a weight in grams) than a second portion of equal size.
  • a textile, thermoformed textile, or thermoformed film component can include a first zone and a second zone, wherein the first zone comprises at least 5 weight percent, or at least 10 weight percent, or at least 20 weight percent, or at least 30 weight percent more of the first polymeric composition than the second zone.
  • FIGS. 4A-4J depict exemplary potential knitting structures that can be present in in a knit textile or knit thermoformed textile as disclosed herein.
  • FIG. 4A depicts a knit stitch (or sometimes referred to as a Jersey stitch) structure 502 formed from a back needle bed 504 .
  • the row of small circles associated with the back needle bed 504 represents needles (e.g., a needle 505 ) of the back needle bed 504 , in accordance with traditional stitch schematics.
  • a front needle bed e.g., the front needle bed 508 depicted in FIG. 4B ; that is, that the row of small circles associated with the front needle bed 508 represent needles (e.g., a needle 507 ) in the front needle bed 508 .
  • FIG. 4G depicts a knit and float stitch structure 530 , with the knit stitches formed on a front needle bed 532 .
  • FIG. 4H depicts a knit and float stitch structure 534 , with the knit stitches formed a back needle bed 536 .
  • FIG. 4I depicts a tuck and float knit structure 538 , with the tuck stitches formed by a front needle bed 540 .
  • FIG. 4J depicts a tuck and float knit structure 542 , with the tuck stitches formed by a back needle bed 544 .
  • an anchor yarn in regions of the textile 300 that include a substantial amount of the first polymeric composition described herein, e.g., the textile zone 302 , an anchor yarn can be provided in the textile 300 to help restrict the flow of the melted first polymeric composition described herein and/or to provide some flexibility to the zone once thermoformed.
  • the anchor yarn can be present in the textile 300 as many different types of knit structure, such as one or more of structures depicted in FIGS. 4E and 4G -J.
  • the stitch selection for the anchor yarn can depend upon the desired resistance to elongation of the material through which the anchor yarn extends.
  • an anchor yarn stitch which floats five needles between tuck or knit stitches would provide a greater resistance to stretch to the material through which the anchor yarn extends compared to an anchor yarn stitch which only floats 2 or 3 needles between tuck or knit stitches.
  • the differing resistance to elongation between the length of the float is a result of non-linear portions (e.g., stitch loops) that are more prone to elongation than linear segments, which results in different amounts of resistance to elongation.
  • the anchor yarn can exhibit an elongation that is less than the elongation of the low processing temperature polymeric composition, such as a yarn comprising the low processing temperature polymeric composition or a melted yarn component produced by thermoforming such a yarn.
  • the anchor yarn can exhibit an elongation that is at least about 10% less than the elongation of a yarn comprising the low processing temperature polymeric composition or a melted yarn component produced by thermoforming a yarn comprising the low processing temperature polymeric composition.
  • the anchor yarn can exhibit an elongation that at least about 25% less than the elongation of a yarn comprising the low processing temperature polymeric composition or a melted yarn component produced by thermoforming a yarn comprising the low processing temperature polymeric composition.
  • the textiles described herein which can include fibers and/or yarns comprising the film, fiber, filament or yarn described herein, can be thermoformed to impart some structure of properties to the article of wear. Further, as discussed above, the thermoforming process can cause at least a portion of the film, fiber, filament or yarn described herein present in the textile to melt or deform and subsequently solidify.
  • FIG. 5A schematically depicts a portion 700 of the textile zone 304 a of the upper knit layer of the textile 300 of FIG. 3 prior to a thermoforming process.
  • the portion 700 includes a first course 702 and a second course 704 having a first yarn 708 .
  • the portion also includes a third course 706 of a second yarn 710 that comprises the film, fiber, filament or yarn described herein.
  • the third course 706 of loops of the second yarn 710 can be interconnected, e.g., interlooped, to the first course 702 and the second course 707 having the first yarn 708 .
  • looped refers to the how a loop from one course can wrap around a loop of another course such as in a knit stitch, and also refers to how one loop can have another segment of yarn pulled through the loop (or through the loop and around the yarn forming the loop) in order to form a second loop, as in a crochet process.
  • the thermoforming process has also transformed at least a portion of the knit structure of the portion 700 of the upper knit layer of the textile 300 of FIG. 3 .
  • the courses 702 , 704 , and 706 depicted in FIG. 7A have been transformed such that the portion 700 no longer includes interconnected courses of loops of a yarn comprising the film, fiber, filament or yarn described herein and a second yarn, at least partly due to the transformation of the yarn 710 in the second course 706 to the melted yarn component 712 .
  • the thermoforming process can eliminate the interconnected loops in the portion 700 of the upper knit layer of the textile 300 of FIG.
  • At least about 80 weight percent, at least about 90 weight percent, at least about 95 weight percent, or at least 99 weight percent of the dye 716 remains within the first yarn 708 or within the thermoformed portion 700 of the upper knit layer of the textile 300 of FIG. 3 .
  • upon thermoforming there is no visible leaching of the dye into any additional materials associated with the final article of wear, which the portion 700 of upper knit layer of the textile 300 of FIG. 3 textile 300 is incorporated into.
  • FIG. 7A shows a cross-sectional view of a textile as disclosed herein, prior to thermoforming, the textile having a first side 800 , a second side 802 , and a core comprising coated yarns as disclosed herein, the coated yarns further having a core yarn 804 and a coating comprising a polymeric composition 806 .
  • FIG. 7B shows the same textile following thermoforming, where the core yarn 804 is disposed within the re-flowed and re-solidified polymeric composition 808 of the coated yarn.
  • FIG. 7C shows a cross-sectional view of a textile as disclosed herein, prior to thermoforming, the textile having a first side 800 , a second side 802 , and a core comprising coated yarns as disclosed herein and an additional second yarn 810 disposed on at least one side of the textile, the coated yarns further having a core yarn 804 and a coating comprising a polymeric composition 806 .
  • FIG. 7D shows the same textile following thermoforming, where the core yarn 804 is disposed within the re-flowed and re-solidified polymeric composition 808 of the coated yarn and the second yarn is disposed at the surface of the re-flowed and re-solidified polymeric composition.
  • FIG. 7A shows a cross-sectional view of a textile as disclosed herein, prior to thermoforming, the textile having a first side 800 , a second side 802 , and a core comprising coated yarns as disclosed herein an additional second yarn disposed on the first side and the second side of the textile 810 , the coated yarns further having a core yarn 804 and a coating comprising a polymeric composition 806 .
  • FIG. 7B shows the same textile following thermoforming, where the core yarn 804 is disposed within the re-flowed and re-solidified polymeric composition 808 of the coated yarn and the second yarn is disposed at both surfaces of the re-flowed and re-solidified polymeric composition.
  • the article can be an article of manufacture or a component of the article.
  • the article of manufacture can include footwear, apparel (e.g., shirts, jerseys, pants, shorts, gloves, glasses, socks, hats, caps, jackets, undergarments), containers (e.g., backpacks, bags), and upholstery for furniture (e.g., chairs, couches, car seats), bed coverings (e.g., sheets, blankets), table coverings, towels, flags, tents, sails, and parachutes, or components of any one of these.
  • apparel e.g., shirts, jerseys, pants, shorts, gloves, glasses, socks, hats, caps, jackets, undergarments
  • containers e.g., backpacks, bags
  • upholstery for furniture e.g., chairs, couches, car seats
  • bed coverings e.g., sheets, blankets
  • table coverings towels, flags, tents, sails, and parachutes, or components of any one of these.
  • the textile or articles including the textile can be used with or disposed items such as striking devices (e.g., bats, rackets, sticks, mallets, golf clubs, paddles, etc.), athletic equipment (e.g., golf bags, baseball and football gloves, soccer ball restriction structures), protective equipment (e.g., pads, helmets, guards, visors, masks, goggles, etc.), locomotive equipment (e.g., bicycles, motorcycles, skateboards, cars, trucks, boats, surfboards, skis, snowboards, etc.), balls or pucks for use in various sports, fishing or hunting equipment, furniture, electronic equipment, construction materials, eyewear, timepieces, jewelry, and the like.
  • striking devices e.g., bats, rackets, sticks, mallets, golf clubs, paddles, etc.
  • athletic equipment e.g., golf bags, baseball and football gloves, soccer ball restriction structures
  • protective equipment e.g., pads, helmets, guards, visors, masks, goggles, etc
  • the article can be an article of footwear.
  • the article of footwear can be designed for a variety of uses, such as sporting, athletic, military, work-related, recreational, or casual use.
  • the article of footwear is intended for outdoor use on unpaved surfaces (in part or in whole), such as on a ground surface including one or more of grass, turf, gravel, sand, dirt, clay, mud, pavement, and the like, whether as an athletic performance surface or as a general outdoor surface.
  • the article of footwear may also be desirable for indoor applications, such as indoor sports including dirt playing surfaces for example (e.g., indoor baseball fields with dirt infields).
  • the article of footwear can be designed for use in indoor or outdoor sporting activities, such as global football/soccer, golf, American football, rugby, baseball, running, track and field, cycling (e.g., road cycling and mountain biking), and the like.
  • the article of footwear can optionally include traction elements (e.g., lugs, cleats, studs, and spikes as well as tread patterns) to provide traction on soft and slippery surfaces, where components of the present disclosure can be used or applied between or among the traction elements and optionally on the sides of the traction elements but on the surface of the traction element that contacts the ground or surface.
  • traction elements e.g., lugs, cleats, studs, and spikes as well as tread patterns
  • the article can be an article of apparel (i.e., a garment).
  • the article of apparel can be an article of apparel designed for athletic or leisure activities.
  • the article of apparel can be an article of apparel designed to provide protection from the elements (e.g., wind and/or rain), or from impacts.
  • the article can be an article of sporting equipment.
  • the article of sporting equipment can be designed for use in indoor or outdoor sporting activities, such as global football/soccer, golf, American football, rugby, baseball, running, track and field, cycling (e.g., road cycling and mountain biking), and the like.
  • FIGS. 8A-8Q illustrate various articles which can comprise a textile of the present disclosure, including a thermoformed textile of the present disclosure.
  • hashed areas are positioned on various regions and structures of the articles. These hashed areas are intended to illustrate general regions and structures which can comprise a textile of the present disclosure, and are not necessarily intended to be representative of the size of the surface area of the region or surface defined by a surface of the textile.
  • the hashed areas indicate a surface of a region or a surface of a structure which can be defined by the thermoplastic network of a thermoformed textile in accordance with the present disclosure.
  • the surface defined by the thermoplastic network can have a total surface area of at least one square centimeter.
  • the surface defined by the thermoplastic network comprises a polymeric composition of a coated yarn in re-flowed and re-solidified form.
  • the cushioning element of the midsole 1014 can incorporate fluid-filled chambers, plates, moderators, and/or other elements that further attenuate forces, enhance stability, or influence motions of the foot.
  • the outsole 1012 is secured to a lower surface of the midsole 1014 and may comprise a wear-resistant elastomeric material such as a natural or synthetic rubber material.
  • the outsole can be textured to impart traction, or can include one or more traction elements.
  • the traction elements can be separate elements affixed to the outsole, or can be integrally formed with the outsole
  • the upper 1002 can be formed from various elements (e.g., lace stays, tongue, collar, medial side, lateral side, vamp, toe box, heel counter) that combine to provide a structure for securely and comfortably receiving a foot.
  • the various elements generally define a void within the upper 1002 for receiving and securing the foot relative to sole structure 1004 .
  • Surfaces of the void within upper 1002 are shaped to accommodate the foot and can extend over the instep and toe areas of the foot, along the medial and lateral sides of the foot, under the foot, and around the heel area of the foot.
  • the upper 1002 can be made of one or more materials such as films, textiles, cables, yarns, fibers, foams, natural leathers, synthetic leathers, and the like that are knitted, stitched, bonded or otherwise connected together.
  • this configuration for the sole structure 1004 and the upper 1002 provides an example of a sole structure that may be used in connection with an upper, a variety of other conventional or nonconventional configurations for the sole structure 1004 and/or the upper 1002 can also be utilized. Accordingly, the configuration and features of the sole structure 1004 and/or the upper 1002 can vary considerably.
  • the upper 1032 can be made of one or more materials such as textiles including natural and synthetic leathers, molded polymeric components, polymer foam and the like that are stitched or bonded together.
  • the primary sole components of the sole structure 1034 can include a forefoot component 1042 , a heel component 1044 , and an outsole 1046 .
  • Each of the forefoot component 1042 and the heel component 1044 can be directly or indirectly secured to a lower area of the upper 1032 .
  • the outsole 1046 may include one or both of an integrally-formed heel component and forefoot component (not shown).
  • the sole component can comprise a polymeric material that encloses a fluid, which may be a gas, liquid, or gel. During walking and running, for example, the forefoot component 1042 and the heel component 1044 may compress between the foot and the ground, thereby attenuating ground reaction forces.
  • the sole structure 1034 may include a foam material forming at least one layer or region of the sole structure, for example, a layer or region that extends between the upper 1032 and one or both of the forefoot component 1042 and the heel component 1044 , or a foam region may be located within indentations in the lower areas of the forefoot component 1042 and the heel component 1044 .
  • the sole structure 1032 may incorporate plates, moderators, lasting elements, or motion control members that further attenuate forces, enhance stability, or influence the motions of the foot, for example.
  • FIG. 8O (c) is a cross-sectional view of A-A that depicts the upper 1032 and the heel component 1044 .
  • the textile 1036 b can be disposed on the externally-facing surface of the heel component 1044 or alternatively or optionally the textile 1036 b ′ can be disposed on the internally-facing side of the heel component 1044 .
  • FIGS. 8P (a) and 8 P(b) illustrate a perspective view and a side view of an article of footwear 160 that includes traction elements 1068 .
  • the structure including the textile is represented by 1072 a and 1072 b .
  • the article of footwear 1060 includes an upper 1062 and a sole structure 1064 , where the upper 1062 is secured to the sole structure 1064 .
  • the sole structure 1064 can include one or more of a toe plate 1066 a , a mid-foot plate 1066 b , and a heel plate 1066 c .
  • the plate can include one or more traction elements 1068 , or the traction elements can be applied directly to a ground-facing surface of the article of footwear. As shown in FIGS.
  • the traction elements 1068 are cleats, but the traction elements can include lugs, cleats, studs, and spikes as well as tread patterns to provide traction on soft and slippery surfaces.
  • the cleats, studs and spikes are commonly included in footwear designed for use in sports such as global football/soccer, golf, American football, rugby, baseball, and the like, while lugs and/or exaggerated tread patterns are commonly included in footwear (not shown) including boots design for use under rugged outdoor conditions, such as trail running, hiking, and military use.
  • Footwear designed for running on paved surfaces commonly include tread patterns.
  • the sole structure 1064 is secured to the upper 1062 and extends between the foot and the ground when the article of footwear 1060 is worn.
  • FIGS. 8Q (a)- 8 Q(j) illustrate additional views of exemplary articles of athletic footwear including various configurations of upper 1076 .
  • FIG. 8Q (a) is an exploded perspective view of an exemplary article of athletic footwear showing insole 1074 , upper 1076 , optional midsole or optional lasting board 1077 , and outsole 1078 , which can take the form of a plate. Structures including the disclosed textiles are represented by 1075 a - 1075 d .
  • FIG. 8Q (b) is a top view of an exemplary article of athletic footwear indicating an opening 183 configured to receive a wearer's foot as well as an ankle collar 1081 which may include textile 1082 .
  • FIG. 8Q (d) shows a side view of an exemplary article of athletic footwear, which may optionally also include a tongue 1086 , laces 1088 , a toe cap 1089 , a heel counter 1090 , a decorative element such as a logo 1091 , and/or eyestays for the laces 1092 as well as a toe area 1093 a , a heel area 1093 b , and a vamp 1093 c .
  • the heel counter 1090 can be covered by a layer of knitted, woven, or nonwoven fabric, natural or synthetic leather, film, or other shoe upper material.
  • the eyestays 1092 are formed as one continuous piece; however, they can also comprise several separate pieces or cables individually surrounding a single eyelet or a plurality of eyelets. Structures including the disclosed textiles are represented by 1087 a - 1087 e . While not depicted, the disclosed textiles can be present on the eyestays 1092 and/or the laces 1088 .
  • the sole structure can include a sole structure, such as a midsole having a cushioning element in part or substantially all of the midsole, and the textile can be disposed on an externally-facing side of the sole structure, including on an externally-facing side of the midsole.
  • FIG. 8Q (e) is a side view of another exemplary article of athletic footwear.
  • the upper can comprise one or more containment elements 1094 such as wires, cables or molded polymeric component extending from the lace structure over portions of the medial and lateral sides of the exemplary article of athletic footwear to the top of the sole structure to provide lockdown of the foot to the sole structure, where the containment element(s) can have a textile (not shown) disposed on an externally-facing side thereon.
  • a rand (not shown) can be present across part or all of the biteline 1095 .
  • thermoforming processes include the selective thermoforming of only a portion of an article, e.g., by masking portions of the article not desired to be exposed to the thermoforming process, or using tooling which contacts or covers only a portion of an article.
  • Such conventional methods result in time and energy intensive manufacturing processes, as multiple steps are required to mask and unmask portions of the article before and after the thermoforming process, or multiple sets of tooling are required.
  • Other conventional thermoforming processes include the thermoforming of article components prior to assembly into an article. This conventional process is also a time and resource intensive process, as multiple steps and machinery are required to individually form the article components prior to assembling the article.
  • an article formed from several individual components results in multiple seams where the individual components interface, thereby providing weaknesses in the article, less natural feel for a wearer, and/or actual discomfort or injury for a wearer.
  • the manufacturing processes disclosed herein solve one or more of the foregoing problems.
  • the manufacturing processes disclosed herein utilize one or more of the films, textiles, yarns and fibers disclosed herein.
  • the specific and selective incorporation of the film, fiber, filament, yarn, or textile as described herein into an article provides a way to program structural features into an article that can be formed upon thermoforming.
  • the article can comprise a textile comprising the film, fiber, filament or yarn as described herein, e.g., a textile comprising at least one plurality of fibers or yarn comprising a film, fiber, filament or yarn as described herein in at least a portion of the textile.
  • the article can comprise a first shaped article comprising a film, fibers, filaments, textile, yarn as described herein, and a second shaped component, film, textile, yarn or plurality of fibers, e.g., a knit upper for an article of footwear and a film as described herein.
  • the article can comprise an aggregation of components at least a portion of which comprise a film, fiber, filament or yarn as described herein and a second fiber, upon which the disclosed thermoforming process has been applied.
  • such structural features are built into the article depending upon the location in the article of the film, fiber, filament or yarn as described herein, upon thermoforming these structural features become integrated with each other, allowing for a more natural feel for the wearer or user.
  • a knit program for electronic knitting equipment can used to determine the location of structural features.
  • the manufacturing processes is not limited to the use of the textiles disclosed herein.
  • a process to form structural features in a disclosed article can utilize a film as described herein with a textile is also contemplated as a process to program structural features into a disclosed article.
  • a process to effectively program structural features into a disclosed article can utilize a shaped component comprising a film, fiber, filament or yarn as described herein with a textile.
  • use of the articles described herein in the manufacturing processes described herein also allows for several different structural or other advantageous features to be provided in the article without the need to combine individual components into the final article, since such features can be built into the article at the textile level using the film, fiber, filament or yarn as described herein.
  • thermoforming process occurs at a temperature above the melting temperature of the thermoplastic elastomer present in the films, fibers, yarns and textiles described herein.
  • thermoforming generates a “consolidated” textile.
  • a consolidated textile comprises a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the first polymeric composition surrounds external surfaces of at least a portion of the yarn or yarns forming the textile, the first polymeric composition occupies spaces between the yarns, and the first polymeric composition forms attachments between the yarns, such that the stretch of the textile is reduced.
  • the reduction in stretch can be along just one axis of the consolidated textile (e.g., an x axis, a y axis, or a bias axis at a 45 degree angle to the x and y axes) or along more than one axis of the consolidated textile.
  • the first polymeric composition can comprise a processing agent in order to improve productivity.
  • the processing agent can be montane wax or a fatty acid ester (C5-C9) with pentaerythritol.
  • the coated yarn can be prepared by compounding in a conventional extruder the first polymeric composition, and optionally also including one or more additives, and then coating the compounded first polymeric composition on the surface of the core yarn.
  • the process for preparing the coated yarn comprises the steps of: 1) preparing formed thermoplastic pellets; and 2) producing coated yarn.
  • the formed thermoplastic pellets can be prepared by the method disclosed herein, prepared by similar methods as known to the skilled artisan, or obtained from a commercially available source.
  • the step of preparing formed thermoplastic pellets comprises the steps of: 1) mixing thermoplastic elastomer with various additives, e.g., a thickener and/or a processing aid, and feeding the mixture into the hopper of a conventional compounding extruder; 2) melting, kneading and compounding the mixture in the cylinder of the compounding extruder at a temperature of about 150-250 degrees Celsius and a pressure of about 50-150 kgf; 3) cutting the compounded thermoplastic elastomer, discharged through the dice of the compounding extruder, in cooling water to form pellets; and 4) drying the formed thermoplastic elastomer pellets at a temperature of 60-80 degrees Celsius for about 4-6 hours and aging the dried pellets at a temperature of 30-50 degrees Celsius for about 7 days or more.
  • additives e.g., a thickener and/or a processing aid
  • the coated yarn can have a thermal shrinkage of from 0 to 20 percent, optionally of from 0 to 15 percent, or of from 0 to 10 percent, measured as described in the Property Analysis and Characterization Procedures.
  • the coated yarn can have a tenacity of from about 1 gram per denier to about 10 grams per denier, optionally of about 2 grams per denier to about 8 grams per denier, or of about 2.5 grams per denier to about 5 grams per denier, measured as described in the Property Analysis and Characterization Procedures.
  • the coated yarn can have a strain at break of from 0 to 20 percent, optionally of from 0 to 15 percent, or of 0 to 10 percent, measured as described in the Property Analysis and Characterization Procedures.
  • thermal shrinkage, tenacity, and strain at break relate to the suitability of yarns for commercial knitting machines.
  • coated yarns having the disclosed properties are suitable for commercial knitting.
  • the step of producing the coated yarn can comprise the following steps: 1) mixing the formed thermoplastic elastomer pellets with a master batch corresponding to a desired color and feeding the mixture into the hopper of a yarn coating extruder; 2) melting the mixture of the formed thermoplastic elastomer pellets and the master batch in the cylinder of the yarn coating extruder at a temperature of about 150-250 degrees Celsius. and a pressure of about 50-150 kgf; 3) coating the compounded thermoplastic elastomer and master batch on the surface of yarn passing through a nipple and a dice to produce coated yarn; and 4) winding the coated yarn around a bobbin using a winding machine.
  • the yarn is a coated yarn comprising a core yarn comprising a second polymeric composition and a coating layer disposed on the core yarn, the coating layer comprising the first polymeric composition, wherein the first polymeric composition has a first melting temperature, wherein the second polymeric composition is a second thermoplastic composition having a second deformation temperature, and the second deformation temperature is at least 20 degrees Celsius greater than the first melting temperature of the first polymeric composition, wherein the second polymeric composition is a first thermoset composition, and wherein the difference between the second deformation temperature and the first melting temperature is at least 20 degrees Celsius, at least 50 degrees Celsius, at least 75 degrees Celsius, or at least 100 degrees Celsius.
  • thermoforming process occurs at a temperature above the first melting temperature of the first polymeric composition but below the deformation temperature of the second polymeric composition.
  • the core yarn i.e., the second polymeric composition
  • the core yarn does not deform or soften during the coating process.
  • a method for making an article comprising affixing a first textile to a second component, wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • a method for making an article comprising affixing a first textile to a second component, wherein the first textile comprises a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • the method for making the article further includes the process of making a textile as disclosed herein. Also disclosed are articles made by the disclosed methods and processes.
  • a method for making an upper for an article of footwear comprising affixing a first textile to a second component, wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • thermoforming an upper comprising a first textile wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition with n the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns.
  • a method for making an upper for an article of footwear comprising affixing a first textile to a second component, wherein the first textile comprises a thermoformed network of yarns comprising a first core yarn and a first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • uppers made by the disclosed methods and processes.
  • more than one coating can be applied to the yarns disclosed herein.
  • disclosed herein are yarns containing an optional second coating and/or an optional third coating.
  • the first coating is applied to the entirety of the core yarn and the second and/or third coatings are applied on top of the first coating.
  • the first coating is applied to only a portion of the core yarn and the second and/or third coatings are applied to portions of the core yarn uncoated by the first coating.
  • the second coating and/or the third coating when the second coating and/or the third coating is polymeric, the second coating and/or third coating displays melting characteristics similar to those of the first coating.
  • the second coating and/or the third coating melts at a lower temperature than the T m of the first coating.
  • a process for making a midsole-outsole unit for an article of footwear includes affixing a midsole cushioning element and an outsole component for an article of footwear to each other, wherein the first polymeric composition defines at least a portion of an outer surface of the outsole configured to be ground-facing or ground-contacting.
  • a process for manufacturing an upper for an article of footwear involves affixing an upper and an outsole to each other to form the article of footwear, wherein the first polymeric composition defines at least a portion of an outer surface of the upper.
  • a process for manufacturing an outsole for an article of footwear involves affixing an upper and an outsole to each other to form the article of footwear, wherein the first polymeric composition defines at least a portion of an outer surface of the outsole configured to be ground-facing or ground-contacting.
  • a process for manufacturing a midsole-outsole unit for an article of footwear comprising a midsole cushioning element and an outsole element.
  • the method involves affixing an upper and an outsole to each other to form the article of footwear, wherein the first polymeric composition defines at least a portion of an outer surface of the midsole-outsole unit configured to be ground-facing or ground-contacting.
  • a process for making an upper for an article of apparel includes weaving a first course that includes interlacing a first yarn and a second yarn.
  • the first and/or second yarn includes a film, fiber, filament or yarn as described herein.
  • at least a portion of the first yarn is a warp yarn; and wherein at least a portion of the second yarn is a weft yarn.
  • at least a portion of the first yarn is a weft yarn; and wherein at least a portion of the second yarn is a warp yarn.
  • the first network of yarns includes interlaced sets of yarns comprising the first coated yarn in a warp direction, or in a weft direction, or in both the warp and weft directions.
  • a process for manufacturing an upper for a shoe includes receiving an upper that includes a first yarn and a second yarn.
  • the first and/or second yarn includes a film, fiber, filament or yarn as described herein.
  • at least one of the first yarn and the second yarn form a plurality of interconnected loops.
  • the process also includes placing the upper on a last. Further, the process includes heating the entire upper, while on the last, to a temperature that is above the melting temperature of the thermoplastic elastomer present in the film, fiber, filament or yarn described herein. Subsequent to the heating the entire upper, cooling the entire upper, while on the last, to a temperature below the melting temperature of the thermoplastic elastomer, to thereby form a thermoformed upper.
  • a process for manufacturing an upper for a shoe includes receiving an upper including one or more first film, fiber, filament or yarns as described herein and one or more second films, fibers, or yarns.
  • the upper includes a ground-facing outsole area, and wherein at least a portion of the one or more first fibers is present on the ground-facing outsole area.
  • the process further includes placing the upper on a last such that at least a portion of the ground-facing outsole area covers at least a portion of a bottom of the last.
  • the process also includes heating the entire upper, while on the last, to a temperature that is above the melting temperature of the thermoplastic elastomer present in the film fibers, or yarn described herein. Subsequent to the heating the entire upper, cooling the entire upper, while on the last, to a temperature below the melting temperature of the thermoplastic elastomer, to thereby form a thermoformed upper.
  • a process for making a knit upper for an article of footwear includes knitting a first course that includes loops of a first yarn and a second yarn.
  • the first yarn included a film, fibers, filaments, or yarn as described herein.
  • the process further includes knitting a second course that comprises loops of the first yarn and the second yarn. At least a portion of the first course and at least a portion of the second course form a plurality of interconnected loops.
  • the article or textile can be combined with additional materials in forming the upper for the article of footwear.
  • the textile can be combined or layered with one or more of an ankle collar lining, ankle collar foam, upper lining, or upper foam layer.
  • one or more of these additional materials can be secured to the textile, e.g., by knitting, stitching, or adhesion, prior to thermoforming the textile.
  • the film, fiber, filament, yarn, textile, or footwear component comprising the first polymeric composition disclosed herein can be thermoformed on a molding surface such as a last.
  • the article is a component footwear that includes an upper or a component of an upper, (e.g., is a textile that will become part of an upper, is an upper, or is an upper and outsole unit)
  • the article in order to prepare the article for the thermoforming process, the article is placed on a last such that the article wraps over a portion of the last, or last enters the inside of the upper.
  • the article can wrap around the last to cover all of or a portion of: a bottom portion of the last, a forefoot portion of the last, a heel portion of the last, or any combination thereof.
  • the last can be formed of a polymeric material such as a high processing temperature polymer composition.
  • the last can be formed of a polymeric material having a melting temperature T m or a degradation temperature greater than 250 degrees Celsius or greater than 300 degrees Celsius such as, for example, a silicone polymer.
  • T m melting temperature
  • T m degradation temperature
  • the last can be made of other types of material as long as such a material would not be deformed or melt during the thermoforming process or otherwise adversely affect the thermoforming of the upper.
  • a first layer can be placed on a molding surface, such as a last, before the article, such as an article of footwear or component of an article of footwear.
  • a first layer such as a liner
  • a film, fiber, filament, yarn or textile according to this disclosure is then placed such it covers at least a portion of the liner.
  • at least a portion of the film, fiber, filament or yarn as described herein is covering at least a portion of the liner.
  • an outer layer can be optionally positioned on at least a portion of the article that is positioned on a molding surface and covering at least a portion of the article.
  • the outer layer which can comprise a film, fiber, filament, yarn or textile comprising the first polymeric composition, can be optionally placed over at least a portion of a textile or an article, such as an upper, that is positioned on a molding surface, such as a last.
  • a textile zone which is associated with the ground-facing outsole portion of the upper can cover all or at least a portion of the bottom portion of the last, or at least a portion of a textile or article in contact with the last.
  • a textile zone associated with the upper can cover all or at least a portion of the upper region of the last or can cover all or at least a portion of a textile or upper in contact with the last.
  • at least a portion of the film, fiber, filament, yarn, textile or component comprising the first polymeric composition as described herein is in contact with at least a portion of the outer layer, or forms at least a portion of the outer layer.
  • a shaped component such as a heel counter or a toe cap
  • a shaped component can be optionally placed on an outer surface of an upper or a combination upper and outsole unit.
  • a shaped component such as a heel counter or a toe cap
  • the film, fiber, filament or yarn as described herein can melt and flow.
  • it can be desirable to mask regions of the article or restrict or direct the flow of the melted film, fiber, filament or yarn as described herein, or both.
  • a protective sheath can be applied over the article positioned on a molding surface.
  • a protective sheath can be positioned over an upper positioned on a last.
  • the protective sheath can be formed of a polymeric material having a melting temperature greater than that of the second polymeric composition.
  • the protective sheath can be formed of an elastomeric polymeric material having a melting temperature T m or a degradation temperature greater than 250 degrees Celsius or greater than 300 degrees Celsius such as, for example, a silicone polymer.
  • the protective sheath can be made of other types of material as long as such a material would not be deformed or melt during the thermoforming process or otherwise adversely affect the thermoforming of the upper.
  • the protective sheath can apply a compressive force to the outer surface of the article being thermoformed, which can aid in restricting and/or directing the flow of the melted first polymeric composition as described herein.
  • a vacuum can be drawn on the combination of the molding surface and the article positioned on the molding surface, and optionally, when present the protective sheath positioned on the article.
  • a bag under vacuum can be compressed on the outside of the article or protective sheath to apply a compressive force to the article or the article and the protective sheath to ensure the article is in flush contact with the molding surface, or is in flush contact with the molding surface and the protective sheath.
  • a protective sheath or a vacuum bag can be used to form a texture on the reflowed first polymeric composition during the thermoforming process.
  • the thermoforming process includes increasing the temperature of the first polymeric composition, e.g., the film, fiber, filament, yarn, textile, to a temperature that can cause at least a portion of the first polymeric composition as described herein present to melt and flow, or to deform. Further, the thermoforming process includes the subsequent decreasing of the temperature of the first polymeric composition to solidify the re-flowed first polymeric composition as described herein into the desired conformation and/or shape, such as an article of footwear.
  • the first polymeric composition e.g., the film, fiber, filament, yarn, textile
  • the thermoforming process includes the subsequent decreasing of the temperature of the first polymeric composition to solidify the re-flowed first polymeric composition as described herein into the desired conformation and/or shape, such as an article of footwear.
  • the thermoforming process does not deform or alter the shaped components, textiles, fibers and/or yarn comprising the second polymeric composition with a deformation temperature greater than the melting temperature of the first polymeric composition present in the film, fiber, filament or yarn.
  • the thermoforming can increase the temperature of the un-masked materials, or only the first polymeric composition, to a temperature of from about 90 degrees Celsius to about 240 degrees Celsius. In aspects, the thermoforming can increase the temperature of the un-masked materials, or only the first polymeric composition, to a temperature of from about 90 degrees Celsius to about 200 degrees Celsius. In one aspect, the thermoforming can increase the temperature of the un-masked materials, or only the first polymeric composition, to a temperature of from about 110 degrees Celsius to about 180 degrees Celsius.
  • the temperature of the un-masked materials, or only the first polymeric composition can be increased for about 10 seconds to about 5 minutes. In aspects, the temperature of the un-masked materials, or only the first polymeric composition, can be increased for about 30 seconds to about 5 minutes. In one aspect, the temperature of the un-masked materials, or only the first polymeric composition, can be increased for about 30 seconds to about 3 minutes.
  • the thermoforming can expose the materials on the mold surface to a pressure of about 50 kPa to about 300 kPa. In aspects, the thermoforming can expose the materials on the mold surface to a pressure of about 50 kPa to about 250 kPa. In one aspect, the thermoforming can expose the materials on the mold surface to a pressure of about from about 100 kPa to about 300 kPa.
  • the un-masked materials, or only the first polymeric composition can be exposed the thermoforming under the above conditions multiple times in a row prior to undergoing the cooling step.
  • the un-masked materials, or only the first polymeric composition can be exposed to the temperatures described above under the above conditions 2 to 10 times in a row prior to undergoing the cooling step.
  • the un-masked materials, or only the first polymeric composition can be exposed the temperatures described above under the above conditions twice in a row prior to undergoing the cooling step.
  • the temperature of the un-masked materials, or only the first polymeric composition is decreased to a temperature below the melting temperature T m of the first polymeric composition present in the film, fiber, filament or yarn as described herein for a duration of time sufficient for the yarner-flowed first polymeric composition to solidify.
  • the un-masked materials or only the first polymeric composition can be heated using a thermal energy source, including, but not limited to, conventional heaters, such as convection heating, a conventional oven, air-circulating oven or forced hot air oven, steam, targeted microwave heat, ultraviolet radiation, infrared heating, and combinations of any of the foregoing.
  • heat can be applied using hotplates, heat presses, or high tonnage presses with rigid clamshell molds.
  • the thermal energy source can further comprise a plurality of thermal energy sources such as a plurality of similar sources, e.g., a plurality of heating coils or infrared emitters.
  • a plurality of thermal energy sources can comprise a plurality of one or more different thermal energy sources, e.g., a plurality of heating coils and a plurality of infrared emitters that can be used simultaneously or sequentially, or alternatively, used in a mode where only one of the plurality of thermal energy sources is used at any given time.
  • the materials when in the cooling zone, can be exposed to a temperature of about from about ⁇ 10 degrees Celsius to about 10 degrees Celsius.
  • the materials can be exposed to one or more of the cooling zone temperatures or ranges discussed above for about 10 seconds to about 5 minutes.
  • the materials can be exposed to one or more of the cooling zone temperatures or ranges discussed above for about 10 seconds to about 3 minutes.
  • the materials can be exposed to one or more of the cooling zone temperatures or ranges discussed above for about 10 seconds to about 2.5 minutes.
  • the textile can be prepared in a number of different ways.
  • the textile can be prepared as a large piece (e.g., as a rolled good) from which one or more pieces of are cut out.
  • the textile can be formed into a single piece (e.g., knit into a single element having roughly the desired size and shape).
  • the textile e.g., a large piece ora single element
  • the textile can be thermoformed before cutting out smaller pieces from a larger piece, or before trimming a single element.
  • the textile can be cut or trimmed (e.g., cutting a large piece into a smaller piece, or trimming excess material from a single element) and then thermoformed.
  • the textile can be pressed against the molding surface with a force greater than atmospheric pressure during the thermoforming process. In another aspect, no additional pressure beyond atmospheric pressure may be applied to the textile during the thermoforming process.
  • textiles and shaped components can include the selective incorporation of films, fibers, filaments, and yarns as described alone or in combination with other materials (e.g., second films, fibers, filaments, or yarns that do not fall under the films, fibers, filaments, and yarns described herein).
  • the films, fibers and filaments, described herein can be used to form yarns which in turn can be used to form textiles, including knit, woven, crocheted, or braided textiles, in accordance with the present disclosure.
  • the films, fibers, filaments, and yarns described herein can also be used to form non-woven textiles in accordance with the present disclosure.
  • the first network of yarns includes entangled or bonded yarns comprising the first coated yarn.
  • the entangled or bonded yarns can be mechanically entangled yarns, thermally bonded yarns, yarns bonded by a solvent treatment, chemically bonded yarns, or any combination thereof.
  • the yarns and/or fibers described herein can be used to provide a specific functionality.
  • a yarn as described herein can be thermoformed to form a film having water-proof or water-resistant properties.
  • coated yarns described herein can have a break strength of from about 0.6 to about 0.9 kilograms of applied force, or of from about 0.7 to about 0.9 kilograms of applied force, or of about 0.8 to about 0.9 kilograms of applied force, or greater than 0.9 kilograms of applied force.
  • the yarns described herein can be produced from films, fibers, or filaments composed of only a single thermoplastic elastomer.
  • the fibers can be composed of a blend of two or more different thermoplastic elastomers.
  • the yarn is a coated yarn, wherein a core yarn comprises a second polymeric composition and a coating layer disposed on the core yarn, the coating layer comprising the first polymeric composition, wherein the first polymeric composition has a first melting temperature.
  • the second polymeric composition is a second thermoplastic composition having a second deformation temperature, and the second deformation temperature is at least 20 degrees Celsius greater, at least 50 degrees Celsius greater, at least 75 degrees Celsius greater, or at least 100 degrees Celsius greater than the first melting temperature of the first polymeric composition.
  • the second polymeric composition is a second thermoplastic composition having a second melting or deformation temperature, and the second deformation temperature is at about 20 degrees Celsius greater, about 50 degrees Celsius greater, about 75 degrees Celsius greater, or about 100 degrees Celsius greater than the first melting temperature of the first polymeric composition.
  • the first polymeric composition includes a polymeric component.
  • the first polymeric composition can include a single polymeric component (e.g., a single thermoplastic elastomer).
  • the first polymeric composition can include two or polymeric components (e.g., two or more different thermoplastic elastomers).
  • the second polymeric composition is a first thermoset composition. In one aspect, the second polymeric composition comprises a second thermoset composition.
  • the core yarn can be any material which retains its strength at the temperature at which the first polymeric material is extruded during the coating process.
  • the core yarn can be natural fibers or regenerated fibers or filaments, or synthetic fibers or filaments. In one aspect, the core yarn can be composed of a cotton, silk, wool, rayon, nylon, elastane, polyester, polyamide, polyurethane, or polyolefin. In one aspect, the core yarn is composed of polyethylene terephthalate (PET).
  • PET polyethylene terephthalate
  • the second polymeric composition has a deformation temperature greater than 200 degrees Celsius, greater than 220 degrees Celsius, greater than 240 degrees Celsius, or between about 200 degrees Celsius to about 300 degrees Celsius.
  • the core yarn is a staple yarn, a multi-filament yarn or a mono-filament yarn. In one aspect the core yarn is polytwisted. In one aspect, the core yarn has a linear density of about 100 denier to about 300 denier, or of about 100 to about 250 denier, or about 100 to about 200 denier, or about 100 to 150 denier, or about 150 to 300 denier, or about 200 to 300 denier, or about 250 to 300 denier. In one aspect, the core yarn has a thickness of about 60 microns to 200 microns, about 60 to 160 microns, about 60 to 120 microns, about 60 to 100 microns, about 100 to 200 microns, or about 140 to 200 microns.
  • the core yarn is polyethylene terephthalate having a thickness of about 100 denier to about 200 denier, about 125 denier to about 175 denier, or about 150 denier to 160 denier. In one aspect, the core yarn is polyethylene terephthalate having a percent elongation of about 20 percent to about 30 percent, about 22 percent to about 30 percent, about 24 percent to about 30 percent, about 20 percent to about 28 percent, or about 20 percent to about 26 percent.
  • the core yarn is polyethylene terephthalate having a tenacity of about 1 gram per denier to about 10 grams per denier, about 3 grams to about 10 grams per denier, about 5 grams to about 10 grams per denier, about 1 gram to about 7 grams per denier, or about 1 gram to about 5 grams per denier.
  • the coating has a nominal average outer diameter of about 0.1 millimeters to about 1.00 millimeter, or about 0.1 millimeters to about 0.80 millimeters, or about 0.1 millimeters to about 0.60 millimeters.
  • the coating on the yarn has an average radial coating thickness of about 50 micrometers to about 200 micrometers, or about 50 micrometers to about 150 micrometers, or about 50 micrometers to about 125 micrometers.
  • the core yarn has a thickness of about 100 denier to about 200 denier, about 125 denier to about 175 denier, or about 150 denier to 160 denier, and the coating has a nominal average outer diameter of about 0.10 millimeters to about 0.50 millimeters, or of about 0.10 millimeters to about 0.25 millimeters, or of about 0.10 millimeters to about 0.20 millimeters.
  • the core yarn is polyethylene terephthalate having a thickness of about 100 denier to about 200 denier, about 125 denier to about 175 denier, or about 150 denier to about 160 denier, and the coating has a nominal average outer diameter of about 0.10 millimeters to about 0.50 millimeters, or of about 0.10 millimeters to about 0.25 millimeters, or of about 0.10 millimeters to about 0.20 millimeters.
  • thermoplastic composition and the lubricating composition are miscible when the thermoplastic composition is reflowed and resolidified in the presence of the lubricating composition.
  • the reflowed and resolidified composition can comprise the lubricating composition.
  • the core yarn has a percent elongation of about 8 percent to about 30 percent, about 10 percent to about 30 percent, about 15 percent to about 30 percent, about 20 percent to about 30 percent, about 10 percent to about 25 percent, or about 10 percent to about 20 percent.
  • the core yarn has a tenacity of about 1 gram per denier to about 10 grams per denier, about 2 grams per denier to about 8 grams per denier, about 4 grams per denier to about 8 grams per denier, or about 2 grams per denier to about 6 grams per denier.
  • the yarn can be used as an inlaid that is incorporated into a textile (e.g., knit, woven etc.).
  • the core yarn has a thickness of about 200 denier to about 300 denier, about 225 denier to about 275 denier, or about 250 denier to 260 denier.
  • the core yarn is polyethylene terephthalate having a thickness of about 200 denier to about 300 denier, about 225 denier to about 275 denier, or about 250 denier to 260 denier.
  • the coating has a nominal average outer diameter of up to about 3.0 millimeters, of up to about 2.5 millimeters, of up to about 2 millimeters, of up to about 1.5 millimeters, of up to about 1.0 millimeter, or of up to about 0.5 millimeters.
  • the core yarn has a thickness of about 200 denier to about 300 denier, about 225 denier to about 275 denier, or about 250 denier to about 260 denier
  • the coating has a nominal average outer diameter of about 0.5 millimeters to about 3.0 millimeters, or of about 1.0 millimeter to about 2.5 millimeters, or of about 1.5 millimeters to about 2.0 millimeters.
  • the core yarn is polyethylene terephthalate having a thickness of about 200 denier to about 300 denier, about 225 denier to about 275 denier, or about 250 denier to about 260 denier, and the coating has a nominal average outer diameter of about 0.5 millimeters to about 3.0 millimeters , or of about 1.0 millimeter to about 2.5 millimeters, or of about 1.5 millimeters to about 2.0 millimeters.
  • the films, fibers, filaments, and yarns described herein have several unique properties that make them suitable for the production of articles such as textiles and the like.
  • the films, fibers, filaments, and yards have improved resistance to abrasion.
  • textiles and articles produced from or incorporating the films, fibers, filaments, and yarns described herein have improved resistance to abrasion.
  • the outer sole will have improved durability as the outer sole is less likely to lose mass over time.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has an Akron abrasion of less than 0.50 cubic centimeters, optionally less than 0.40 cubic centimeters, less than 0.30 cubic centimeters, less than 0.20 cubic centimeters, or less than 0.10 cubic centimeters as determined using the Akron Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has an Akron abrasion of about 0.05 cubic centimeters to about 0.5 cubic centimeters, about 0.10 cubic centimeters to about 0.45 cubic centimeters, or about 0.05 to about 0.20 cubic centimeters as determined using the Akron Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has an Akron abrasion of less than 500 milligrams, optionally less than 400 milligrams, less than 300 milligrams, less than 200 milligrams, or less than 100 milligrams as determined using the Akron Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has an Akron abrasion of about 50 milligrams to about 500 milligrams, about 100 milligrams to about 400 milligrams, or about 100 milligrams to about 150 milligrams as determined using the Akron Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has a DIN abrasion of less than 0.30 cubic centimeters, optionally less than 0.20 cubic centimeters, less than 0.10 cubic centimeters, less than 0.05 cubic centimeters, or less than 0.07 cubic centimeters as determined using the DIN Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has a DIN abrasion of about 0.01 cubic centimeters to about 0.30 cubic centimeters, about 0.05 cubic centimeters to about 0.20 cubic centimeters, or about 0.05 cubic centimeters to about 0.10 cubic centimeters as determined using the DIN Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, and yarn has a DIN abrasion of less than 300 milligrams, optionally less than 200 milligrams, less than 100 milligrams, less than 50 milligrams, or less than 30 milligrams as determined using the DIN Abrasion Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has a DIN abrasion of about 10 milligrams to about 300 milligrams, about 50 milligrams to about 250 milligrams, or about 50 milligrams to about 100 milligrams as determined using the DIN Abrasion Test.
  • the films, fibers, and yarns described herein when incorporated into a textile or article the product has improved traction properties.
  • the coefficient of friction of the films, fibers or yarns can be used to measure traction properties on various surfaces.
  • the first polymeric composition of the film, fibers, filaments, yarn, and polymeric has a wet dynamic COF of greater than 0.25, optionally of greater than 0.30, greater than 0.35, greater than 0.40, or greater than 0.50, as determined using the Coefficient of Friction Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has a wet dynamic COF of greater than 0.15, optionally of greater than 0.2, greater than 0.25, or greater than 0.3, using the Coefficient of Friction Test.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile when thermoformed, has a melting temperature from about 100 degrees Celsius to about 210 degrees Celsius, optionally from about 110 degrees Celsius to about 195 degrees Celsius, from about 120 degrees Celsius to about 180 degrees Celsius, or from about 120 degrees Celsius to about 170 degrees Celsius.
  • the first polymeric composition has a melting temperature greater than about 120 degrees Celsius and less than about 170 degrees Celsius, and optionally greater than about 130 degrees Celsius, and less than about 160 degrees Celsius.
  • the melting temperature when the melting temperature is greater than 100 degrees Celsius, the integrity of articles formed from or incorporating the first polymeric composition is preserved if the articles briefly encounter similar temperatures, for example, during shipping or storage.
  • the melting temperature when the melting temperature is greater than 100 degrees Celsius, or greater than 120 degrees Celsius, articles formed from or incorporating the first polymeric composition can be steamed without melting or uncontrollably fusing any polyester components incorporated in the articles for purposes such as fill, zonal surface, or comfort features, as well as stretch yarn used for snugness and fit features.
  • the melting temperature when the melting temperature is greater than 120 degrees Celsius, materials incorporating the first or second polymeric composition disclosed herein are unlikely to soften and/or become tacky during use on a hot paved surface, a court surface, an artificial or natural soccer pitch, or a similar playing surface, track, or field.
  • the higher the melting temperature of the first or second polymeric composition and the greater its enthalpy of melting the greater the ability of an article of footwear or athletic equipment incorporating or constructed from the first or second polymeric composition to withstand contact heating excursions, frictional surface heating events, or environmental heating excursions.
  • such heat excursions may arise when the articles contact hot ground, court, or turf surfaces, or from frictional heating that comes from rubbing or abrasion when the articles contact another surface such as the ground, another shoe, a ball, or the like.
  • polymer coated yarns when the melting temperature is less than about 210 degrees Celsius, or less than about 200 degrees Celsius, or less than about 190 degrees Celsius, or less than about 180 degrees Celsius, or less than about 175 degrees Celsius, but greater than about 120 degrees Celsius, or greater than about 110 degrees Celsius, or greater than about 103 degrees Celsius, polymer coated yarns can be melted for the purposes of molding and/or thermoforming a given region of textiles knitted therefrom in order to impart desirable design and aesthetic features in a short period of time.
  • a melting temperature lower than 140 degrees Celsius can prevent or mitigate the risk dye migration from polyester yarns incorporated in the footwear or other articles.
  • dye migration from package-dyed polyester yarns or filaments is a diffusion-limited process and short periods of exposure to temperatures greater than 140 degrees Celsius, such as during thermoforming, do not extensively damage, discolor, or otherwise render the appearance of the footwear or other articles unacceptable.
  • the melting temperature of the polymer coating is greater than about 210 degrees Celsius, thermal damage and dye migration may occur.
  • a high melting enthalpy indicates a longer heating time is required to ensure a polymer is fully melted and will flow well.
  • a low melting enthalpy requires less heating time to ensure full melting and good flow.
  • high cooling exotherms indicate rapid transitions from molten to solid.
  • higher recrystallization temperatures indicate polymers are capable of solidifying at higher temperatures.
  • high-temperature solidification can be beneficial for thermoforming.
  • recrystallization above 95 degrees Celsius can promote rapid setting after thermoforming, reduce cycle time, reduce cooling demands, and improve stability of shoe components during assembly and use.
  • viscosity of the coating compositions disclosed herein can affect the properties and processing of the coating compositions.
  • high viscosities at low shear rates e.g., less than 1 reciprocal second
  • low viscosities at higher shear rates e.g., greater than 10 reciprocal seconds
  • the ability to flow and deform adequately to coat core yarn substrate becomes challenging.
  • materials that exhibit high shear thinning indices can be challenging to extrude and may melt fracture if coated or extruded at a velocity that is too high.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has a melt flow index of at least 0.2 grams per 10 minutes, optionally at least 2, at least 5, at least 10, at least 15, at least 20, at least 25, at least 30, at least 40, or at least 50 grams per 10 minutes, as determined using the Method to Determine the Melt Flow Index (ASTM D1238-13) at 160 degrees Celsius using a weight of 2.16 kg.
  • the first polymeric composition of the film, fibers, filaments, yarn, and textile has a durometer Shore A hardness of about 50 to about 90 Shore A, optionally from about 55 to about 85 Shore A, from about 60 to about 80 Shore A, from about 60 to about 70 Shore A, or from about 67 to about 77 shore A.
  • the first polymeric composition of the film, fibers, filaments, yarn, or textile have two or more of the first properties, or optionally three or more, four or more, five or more, six or more, seven or more, or all ten first properties provided above.
  • the textile described herein can exhibit a modulus of from about 1 megapascal to about 500 megapascals.
  • the coated yarns can exhibit a modulus of from about 5 megapascals to about 150 megapascals, or of from about 20 megapascals to about 130 megapascals, or of from about 30 megapascals to about 120 megapascals, or of from about 40 megapascals to about 110 megapascals.
  • modulus refers to a respective testing method described below in the Property Analysis And Characterization Procedures section.
  • a material having a high modulus is relatively stiffer than a material having a low modulus, which is more flexible.
  • thermoplastic polymeric compositions having a lower modulus will be more flexible than articles comprising thermoplastic polymeric compositions having a high modulus.
  • the first polymeric composition of the film, fibers, filaments, and yarn when thermoformed, has a stress at break greater than 7 megapascals, optionally greater than 8 megapascals, as determined using Method to Determine the Modulus, Tenacity, and Elongation (yarn) at 25 degrees Celsius. In one aspect, when thermoformed, the first polymeric composition of the film, fibers, filaments, and yarn has a tensile stress at 300 percent modulus greater than 2 megapascals, optionally greater than 2.5 megapascals, or greater than 3 megapascals as determined using Method to Determine the Modulus, Tenacity, and Elongation (yarn) at 25 degrees Celsius.
  • the textiles described herein or articles comprising the textiles described herein can be subjected to Akron Abrasion testing as described in the Property Analysis and Characterization Procedures.
  • the textiles or articles after 300 cycles of Akron Abrasion testing, the textiles or articles have a mass loss of from 0 to 0.05 weight percent, optionally from 0 to 0.04 weight percent, or from 0 to 0.03 weight percent, or from 0 to 0.02 weight percent after 300 cycles.
  • the textiles or articles after 3000 cycles of Akron Abrasion testing, have a mass loss of from 0 to 0.2 weight percent, or of from 0 to 0.15 weight percent, or of from 0 to 0.1 weight percent, or of from 0 to 0.05 weight percent.
  • a textile-ball impact test or a boot-ball impact test can be performed as described in the Property Analysis and Characterization Procedures.
  • the textile or an upper comprising the textile produces a ball spin rate of from about 220 revolutions per minute to about 240 revolutions per minute, or of about 220 revolutions per minute to about 230 revolutions per minute.
  • the revolutions per minute can be right-handed (positive, or clockwise) or left-handed (negative, or counterclockwise).
  • a higher number of revolutions per minute is desirable for generating a ball path with suitable curvature for avoiding opposing players on, for example, a soccer (football) field.
  • thermoformed knitted or woven textiles comprising the first polymer composition possesses desirable performance properties.
  • the disclosed thermoformed knitted or woven textiles outperform traditional materials included in uppers for articles of footwear such as Kangaroo leather and Duragon skin (a trade name referring to a preformed, polyurethane laminated skin on a polyester textile).
  • the thermoformed knit textiles showed similar dry and wet coefficients of friction (e.g., boot-to-ball interaction) as the laminated Duragon skin; however, the knitted textile as described herein can be produced in a streamlined, more integrated, lower waste manner of construction.
  • thermoformed textiles and/or footwear uppers containing the coated yarns disclosed herein exhibit higher wet and dry COF values overall, and a lower degree of difference between dry COF and wet COF than DURAGON skin.
  • the first polymeric composition has one or more properties selected from:
  • the films, fibers, and yarns described herein can exhibit a tenacity greater than 1 gram/denier. In one aspect, the films, fibers, and yarns described herein can exhibit a tenacity of from about 1 gram/denier to about 5 grams/denier. In one or more aspects, the films, fibers, and yarns described herein can exhibit a tenacity of from about 1.5 grams/denier to about 4.5 grams/denier. In one aspect, the films, fibers, and yarns described herein can exhibit a tenacity of from about 2 grams/denier to about 4.5 grams/denier. “Tenacity” as used herein refers to a property of a fiber or yarn, and is determined using the respective testing method and sampling procedure described below in the Property Analysis and Characterization Procedures section.
  • a free-standing shrinkage of a yarn at 50 degrees Celsius is one property that can be predictive of a suitable yarn for use on a commercial knitting machine.
  • a films, fibers, filaments, and yarns described herein can exhibit a free-standing shrinkage when heated from 20 degrees Celsius to 70 degrees Celsius of less than 15 percent.
  • the films, fibers, and yarns described herein can exhibit free-standing shrinkage when heated from 20 degrees Celsius to 70 degrees Celsius of about 0 percent to about 60 percent, about 0 percent to about 30 percent, or about 0 percent to about 15 percent.
  • the term “free-standing shrinkage” as used herein refers to a property of a yarn and a respective testing method described below in the Property Analysis and Characterization Procedures section.
  • the free-standing shrinkage of a yarn at 70 degrees Celsius can be a useful indicator of the ability of a yarn to be exposed to certain environmental conditions without any substantial changes to the physical structure of the yarn.
  • a yarn comprising the low processing temperature polymeric composition can exhibit a free-standing shrinkage when heated from 20 degrees Celsius to 70 degrees Celsius of from about 0% to about 60%.
  • a yarn comprising the low processing temperature polymeric composition can exhibit a free-standing shrinkage when heated from 20 degrees Celsius to 70 degrees Celsius of from about 0% to about 30%.
  • a yarn comprising the low processing temperature polymeric composition can exhibit a free-standing shrinkage when heated from 20 degrees Celsius to 70 degrees Celsius of from about 0% to about 20%.
  • the melted yarn component formed from the coated fibers as described herein during the thermoforming process can be integrally connected to the non-altered structure (e.g., a yarn or fiber), which can provide three-dimensional structure and/or other properties targeted to specific spots on an article of wear.
  • the non-altered structure e.g., a yarn or fiber
  • the elastomer plaque can have a toughness of from 850 kilogram ⁇ millimeters to 2200 kilogram ⁇ millimeters, or of from about 850 kilogram ⁇ millimeters to about 2000 kilogram ⁇ millimeters, or of from about 900 kilogram ⁇ millimeters to about 1750 kilogram ⁇ millimeters, or of from about 1000 kilogram ⁇ millimeters to about 1500 kilogram ⁇ millimeters, or of from about 1500 kilogram ⁇ millimeters to about 2000 kilogram ⁇ millimeters.
  • the thermoplastic elastomer can be a block co-polymer having repeating blocks of polymeric units of the same chemical structure (segments) which are relatively harder (hard segments), and repeating blocks of polymeric segments which are relatively softer (soft segments).
  • block co-polymers including block co-polymers having repeating hard segments and soft segments, physical crosslinks can be present within the blocks or between the blocks or both within and between the blocks.
  • hard segments include isocyanate segments and polyamide segments.
  • Particular examples of soft segments include polyether segments and polyester segments.
  • the polymeric segment can be referred to as being a particular type of polymeric segment such as, for example, an isocyanate segment, a polyamide segment, a polyether segment, a polyester segment, and the like. It is understood that the chemical structure of the segment is derived from the described chemical structure. For example, an isocyanate segment is a polymerized unit including an isocyanate functional group. When referring to a block of polymeric segments of a particular chemical structure, the block can contain up to 10 mol percent of segments of other chemical structures.
  • a polyether segment is understood to include up to 10 mol percent of non-polyether segments.
  • the thermoplastic elastomer can include one or more of a thermoplastic copolyester elastomer, a thermoplastic polyether block amide elastomer, a thermoplastic polyurethane elastomer, a polyolefin based-copolymer elastomer, a thermoplastic styrenic copolymer elastomer, a thermoplastic ionomer elastomer, or any combination thereof.
  • the first polymeric composition comprises a thermoplastic elastomeric styrenic copolymer.
  • the thermoplastic elastomeric styrenic copolymer can be a styrene butadiene styrene (SBS) block copolymer, a styrene ethylene/butylene styrene (SEBS) resin, a styrene acrylonitrile (SAN) resin, or any combination thereof.
  • the first polymeric composition comprises a thermoplastic elastomeric polyester polyurethane, a thermoplastic polyether polyurethane, or any combination thereof.
  • the thermoplastic elastomeric polyester polyurethane can be an aromatic polyester, an aliphatic composition, or a combination thereof.
  • the first polymeric composition comprising the thermoplastic elastomer has a melting temperature greater than about 110 degrees Celsius and less than about 170 degrees Celsius. In another aspect, the first polymeric composition comprising the thermoplastic elastomer has a melting temperature of about 110 degrees Celsius to about 170 degrees Celsius, about 115 degrees Celsius to about 160 degrees Celsius, about 120 degrees Celsius to about 150 degrees Celsius, about 125 degrees Celsius to about 140 degrees Celsius, about 110 degrees Celsius to about 150 degrees Celsius, or about 110 degrees Celsius to about 125 degrees Celsius.
  • the glass transition temperature of the thermoplastic elastomer is selected such that articles incorporating the coated yarns disclosed herein, wherein the coated yarns comprise a coating material comprising the thermoplastic elastomer, the thermoplastic material is above its glass transition temperature during normal wear when incorporated into an article of footwear (i.e., is more rubbery and less brittle).
  • the thermoplastic elastomer comprises: (a) a plurality of first segments; (b) a plurality of second segments; and, optionally, (c) a plurality of third segments.
  • the thermoplastic elastomer is a block copolymer.
  • the thermoplastic elastomer is a segmented copolymer.
  • the thermoplastic elastomer is a random copolymer.
  • the thermoplastic elastomer is a condensation copolymer.
  • thermoplastic elastomer can have a weight average molecular weight of about 50,000 Daltons to about 1,000,000 Daltons; about 50,000 Daltons to about 500,000 Daltons; about 75,000 Daltons to about 300,000 Daltons; about 100,000 Daltons to about 200,000 Daltons.
  • thermoplastic elastomer can have a ratio of first segments to second segments from about 1:1 to about 1:2 based on the weight of each of the first segments and the second segments; or of about 1:1 to about 1:1.5 based on the weight of each of the first segments and the second segments.
  • thermoplastic elastomer can have a ratio of first segments to third segments from about 1:1 to about 1:5 based on the weight of each of the first segments and the third segments; about 1:1 to about 1:3 based on the weight of each of the first segments and the third segments; about 1:1 to about 1:2 based on the weight of each of the first segments and the third segments; about 1:1 to about 1:3 based on the weight of each of the first segments and the third segments.
  • thermoplastic elastomer can have first segments derived from a first component having a number-average molecular weight of about 250 Daltons to about 6000 Daltons; about 400 Daltons to about 6,000 Daltons; about 350 Daltons to about 5,000 Daltons; or about 500 Daltons to about 3,000 Daltons.
  • the thermoplastic elastomer can comprise phase separated domains.
  • a plurality of first segments can phase-separate into domains comprising primarily the first segments.
  • a plurality of second segments derived from segments having a different chemical structure can phase-separate into domains comprising primarily the second segments.
  • the first segments can comprise hard segments, and the second segments can comprise soft segments.
  • the thermoplastic elastomer can comprise phase-separated domains comprising a plurality of first copolyester units.
  • the first polymeric composition prior to thermoforming, has a glass transition temperature glass transition temperature of from about 20 degrees Celsius to about ⁇ 60 degrees Celsius. In one aspect, prior to thermoforming, the first polymeric composition has a Taber Abrasion Resistance of from about 10 milligrams to about 40 milligrams as determined by ASTM D3389. In one aspect, prior to thermoforming, the first polymeric composition has a Durometer Hardness (Shore A) of from about 60 to about 90 as determined by ASTM D2240. In one aspect, prior to thermoforming, the first polymeric composition has a specific gravity of from about 0.80 g/cm 3 to about 1.30 g/cm 3 as determined by ASTM D792.
  • the first polymeric composition prior to thermoforming, has a melt flow index of about 2 grams/10 minutes to about 50 grams/10 minutes at 160 degrees Celsius using a test weight of 2.16 kilograms. In one aspect, prior to thermoforming, the first polymeric composition has a melt flow rate greater than about 2 grams/10minutes at 190 degrees Celsius or 200 degrees Celsius when using a test weight of 10 kilograms. In one aspect, prior to thermoforming, the first polymeric composition has a modulus of about 1 megapascal to about 500 megapascals.
  • the thermoplastic elastomer is a thermoplastic polyurethane elastomer.
  • the thermoplastic polyurethane elastomer can be a thermoplastic block polyurethane co-polymer.
  • the thermoplastic polyurethane co-polymer can be a copolymer comprising hard segments and soft segments, including blocks of hard segments and blocks of soft segments.
  • the hard segments can comprise or consist of isocyanate segments.
  • the soft segments can comprise or consist of polyether segments, or polyester segments, or a combination of polyether segments and polyester segments.
  • thermoplastic material or the polymeric component of the thermoplastic material, can comprise or consist essentially of an elastomeric thermoplastic polyurethane hard segments and soft segments, such as an elastomeric thermoplastic polyurethane having repeating blocks of hard segments and repeating blocks of soft segments.
  • thermoplastic polyurethane elastomer can be produced by polymerizing one or more isocyanates with one or more polyols to produce copolymer chains having carbamate linkages (—N(CO)O—) as illustrated below in Formula 1, where the isocyanate(s) each preferably include two or more isocyanate (—NCO) groups per molecule, such as 2, 3, or 4 isocyanate groups per molecule (although, single-functional isocyanates can also be optionally included, e.g., as chain terminating units).
  • each R 1 and R 2 independently is an aliphatic or aromatic segment.
  • each R 2 can be a hydrophilic segment.
  • any of the functional groups or chemical compounds described herein can be substituted or unsubstituted.
  • a “substituted” group or chemical compound, such as an alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkenyl, aryl, heteroaryl, alkoxyl, ester, ether, or carboxylic ester refers to an alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkenyl, aryl, heteroaryl, alkoxyl, ester, ether, or carboxylic ester group, has at least one hydrogen radical that is substituted with a non-hydrogen radical (i.e., a substituent).
  • non-hydrogen radicals include, but are not limited to, alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkynyl, ether, aryl, heteroaryl, heterocycloalkyl, hydroxyl, oxy (or oxo), alkoxyl, ester, thioester, acyl, carboxyl, cyano, nitro, amino, amido, sulfur, and halo.
  • substituents can be bound to the same carbon or two or more different carbon atoms.
  • the isocyanates can also be chain extended with one or more chain extenders to bridge two or more isocyanates. This can produce polyurethane copolymer chains as illustrated below in Formula 2, wherein R 3 includes the chain extender. As with each R 1 and R 3 , each R 3 independently is an aliphatic or aromatic segment.
  • Each segment R 1 , or the first segment, in Formulas 1 and 2 can independently include a linear or branched C 3-30 segment, based on the particular isocyanate(s) used, and can be aliphatic, aromatic, or include a combination of aliphatic portions(s) and aromatic portion(s).
  • aliphatic refers to a saturated or unsaturated organic molecule that does not include a cyclically conjugated ring system having delocalized pi electrons.
  • aromatic refers to a cyclically conjugated ring system having delocalized pi electrons, which exhibits greater stability than a hypothetical ring system having localized pi electrons.
  • Each segment R 1 can be present in an amount of 5 percent to 85 percent by weight, from 5 percent to 70 percent by weight, or from 10 percent to 50 percent by weight, based on the total weight of the reactant monomers.
  • each segment R 1 can include a linear aliphatic group, a branched aliphatic group, a cycloaliphatic group, or combinations thereof.
  • each segment R 1 can include a linear or branched C 3-20 alkylene segment (e.g., C 4-15 alkylene or C 6-10 alkylene), one or more C 3-8 cycloalkylene segments (e.g., cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, or cyclooctyl), and combinations thereof.
  • suitable aliphatic diisocyanates for producing the polyurethane copolymer chains include hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), butylenediisocyanate (BDI), bisisocyanatocyclohexylmethane (HMDI), 2,2,4-trimethylhexamethylene diisocyanate (TMDI), bisisocyanatomethylcyclohexane, bisisocyanatomethyltricyclodecane, norbornane diisocyanate (NDI), cyclohexane diisocyanate (CHDI), 4,4′-dicyclohexylmethane diisocyanate (H12MDI), diisocyanatododecane, lysine diisocyanate, and combinations thereof.
  • HDI hexamethylene diisocyanate
  • IPDI isophorone diisocyanate
  • BDI butylenediisocyan
  • each segment R 1 can include one or more aromatic groups, such as phenyl, naphthyl, tetrahydronaphthyl, phenanthrenyl, biphenylenyl, indanyl, indenyl, anthracenyl, and fluorenyl.
  • aromatic groups such as phenyl, naphthyl, tetrahydronaphthyl, phenanthrenyl, biphenylenyl, indanyl, indenyl, anthracenyl, and fluorenyl.
  • an aromatic group can be an unsubstituted aromatic group or a substituted aromatic group, and can also include heteroaromatic groups.
  • Heteroaromatic refers to monocyclic or polycyclic (e.g., fused bicyclic and fused tricyclic) aromatic ring systems, where one to four ring atoms are selected from oxygen, nitrogen, or sulfur, and the remaining ring atoms are carbon, and where the ring system is joined to the remainder of the molecule by any of the ring atoms.
  • heteroaryl groups examples include pyridyl, pyrazinyl, pyrimidinyl, pyrrolyl, pyrazolyl, imidazolyl, thiazolyl, tetrazolyl, oxazolyl, isooxazolyl, thiadiazolyl, oxadiazolyl, furanyl, quinolinyl, isoquinolinyl, benzoxazolyl, benzimidazolyl, and benzothiazolyl.
  • Suitable aromatic diisocyanates for producing the polyurethane copolymer chains include toluene diisocyanate (TDI), TDI adducts with trimethyloylpropane (TMP), methylene diphenyl diisocyanate (MDI), xylene diisocyanate (XDI), tetramethylxylylene diisocyanate (TMXDI), hydrogenated xylene diisocyanate (HXDI), naphthalene 1,5-diisocyanate (NDI), 1,5-tetrahydronaphthalene diisocyanate, para-phenylene diisocyanate (PPDI), 3,3′-dimethyldipheny1-4,4′-diisocyanate (DDDI), 4,4′-dibenzyl diisocyanate (DBDI), 4-chloro-1,3-phenylene diisocyanate, and combinations thereof.
  • the copolymer chains are substantially free of
  • the polyurethane copolymer chains are produced from diisocyanates including HMDI, TDI, MDI, H 12 aliphatics, and combinations thereof.
  • the coated fiber as described herein of the present disclosure can comprise one or more polyurethane copolymer chains are produced from diisocynates including HMDI, TDI, MDI, H 12 aliphatics, and combinations thereof.
  • polyurethane chains which are crosslinked e.g., partially crosslinked polyurethane copolymers which retain thermoplastic properties
  • polyurethane copolymers which retain thermoplastic properties can be crosslinked.
  • suitable triisocyanates for producing the polyurethane copolymer chains include TDI, HDI, and IPDI adducts with trimethyloylpropane (TMP), uretdiones (i.e., dimerized isocyanates), polymeric MDI, and combinations thereof.
  • Segment R 3 in Formula 2 can include a linear or branched C 2 -C 10 segment, based on the particular chain extender polyol used, and can be, for example, aliphatic, aromatic, or polyether.
  • suitable chain extender polyols for producing the polyurethane copolymer chains include ethylene glycol, lower oligomers of ethylene glycol (e.g., diethylene glycol, triethylene glycol, and tetraethylene glycol), 1,2-propylene glycol, 1,3-propylene glycol, lower oligomers of propylene glycol (e.g., dipropylene glycol, tripropylene glycol, and tetrapropylene glycol), 1,4-butylene glycol, 2,3-butylene glycol, 1,6-hexanediol, 1,8-octanediol, neopentyl glycol, 1,4-cyclohexanedimethanol, 2-ethyl-1,6-hex
  • Segment R 2 in Formula 1 and 2 can include a polyether group, a polyester group, a polycarbonate group, an aliphatic group, or an aromatic group. Each segment R 2 can be present in an amount of 5 percent to 85 percent by weight, from 5 percent to 70 percent by weight, or from 10 percent to 50 percent by weight, based on the total weight of the reactant monomers.
  • the thermoplastic polyurethane elastomer can be a thermoplastic polyurethane having relatively high degree of hydrophilicity.
  • the thermoplastic polyurethane can be a thermoplastic polyether polyurethane in which segment R 2 in Formulas 1 and 2 includes a polyether group, a polyester group, a polycarbonate group, an aliphatic group, or an aromatic group, wherein the aliphatic group or aromatic group is substituted with one or more pendant group having relatively greater degree of hydrophilicity (i.e., relatively “hydrophilic” groups).
  • the relatively “hydrophilic” groups can be selected from the group consisting of hydroxyl, polyether, polyester, polylactone (e.g., polyvinylpyrrolidone (PVP)), amino, carboxylate, sulfonate, phosphate, ammonium (e.g., tertiary and quaternary ammonium), zwitterion (e.g., a betaine, such as poly(carboxybetaine (pCB) and ammonium phosphonates such as phosphatidylcholine), and combinations thereof.
  • this relatively hydrophilic group or segment of R 2 can form portions of the polyurethane backbone, or can be grafted to the polyurethane backbone as a pendant group.
  • the pendant hydrophilic group or segment can be bonded to the aliphatic group or aromatic group through a linker.
  • Each segment R 2 can be present in an amount of 5 percent to 85 percent by weight, from 5 percent to 70 percent by weight, or from 10 percent to 50 percent by weight, based on the total weight of the reactant monomers.
  • At least one R 2 segment of the thermoplastic polyurethane elastomer includes a polyether segment (i.e., a segment having one or more ether groups).
  • Suitable polyethers include, but are not limited to polyethylene oxide (PEO), polypropylene oxide (PPO), polytetrahydrofuran (PTHF), polytetramethylene oxide (P T m O), and combinations thereof.
  • PEO polyethylene oxide
  • PPO polypropylene oxide
  • PTHF polytetrahydrofuran
  • P T m O polytetramethylene oxide
  • alkyl refers to straight chained and branched saturated hydrocarbon groups containing one to thirty carbon atoms, for example, one to twenty carbon atoms, or one to ten carbon atoms.
  • C n means the alkyl group has “n” carbon atoms.
  • C 4 alkyl refers to an alkyl group that has 4 carbon atoms.
  • C 1-7 alkyl refers to an alkyl group having a number of carbon atoms encompassing the entire range (i.e., 1 to 7 carbon atoms), as well as all subgroups (e.g., 1-6, 2-7, 1-5, 3-6, 1, 2, 3, 4, 5, 6, and 7 carbon atoms).
  • alkyl groups include, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl (2-methylpropyl), t-butyl (1,1- dimethylethyl), 3,3-dimethylpentyl, and 2-ethylhexyl.
  • an alkyl group can be an unsubstituted alkyl group or a substituted alkyl group.
  • the at least one R 2 segment includes a polyester segment.
  • the polyester segment can be derived from the polyesterification of one or more dihydric alcohols (e.g., ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol, 2-methylpentanediol-1,5,diethylene glycol, 1,5-pentanediol, 1,5-hexanediol, 1,2-dodecanediol, cyclohexanedimethanol, and combinations thereof) with one or more dicarboxylic acids (e.g., adipic acid, succinic acid, sebacic acid, suberic acid, methyladipic acid, glutaric acid, pimelic acid, azelaic acid, thiodipropionic acid and citraconic acid and combinations thereof).
  • dihydric alcohols e.g., ethylene glycol, 1,3-prop
  • the polyester also can be derived from polycarbonate prepolymers, such as poly(hexamethylene carbonate) glycol, poly(propylene carbonate) glycol, poly(tetramethylene carbonate)glycol, and poly(nonanemethylene carbonate) glycol.
  • Suitable polyesters can include, for example, polyethylene adipate (PEA), poly(1,4-butylene adipate), poly(tetramethylene adipate), poly(hexamethylene adipate), polycaprolactone, polyhexamethylene carbonate, poly(propylene carbonate), poly(tetramethylene carbonate), poly(nonanemethylene carbonate), and combinations thereof.
  • At least one R 2 segment includes a polycarbonate segment.
  • the polycarbonate segment can be derived from the reaction of one or more dihydric alcohols (e.g., ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol, 2-methylpentanediol-1,5, diethylene glycol, 1,5-pentanediol, 1,5-hexanediol, 1,2-dodecanediol, cyclohexanedimethanol, and combinations thereof) with ethylene carbonate.
  • dihydric alcohols e.g., ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol, 2-methylpentanediol-1,5, diethylene glycol, 1,5-pentanediol, 1,5-hexanedi
  • the one or more relatively hydrophilic group can be selected from the group consisting of hydroxyl, polyether, polyester, polylactone (e.g., polyvinylpyrrolidone), amino, carboxylate, sulfonate, phosphate, ammonium (e.g., tertiary and quaternary ammonium), zwitterion (e.g., a betaine, such as poly(carboxybetaine (pCB) and ammonium phosphonates such as phosphatidylcholine), and combinations thereof.
  • polylactone e.g., polyvinylpyrrolidone
  • amino carboxylate
  • sulfonate phosphate
  • ammonium e.g., tertiary and quaternary ammonium
  • zwitterion e.g., a betaine, such as poly(carboxybetaine (pCB) and ammonium phosphonates such as phosphatidylcholine
  • the aliphatic group is linear and can include, for example, a C 1-20 alkylene chain or a C 1-20 alkenylene chain (e.g., methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, decylene, undecylene, dodecylene, tridecylene, ethenylene, propenylene, butenylene, pentenylene, hexenylene, heptenylene, octenylene, nonenylene, decenylene, undecenylene, dodecenylene, tridecenylene).
  • a C 1-20 alkylene chain or a C 1-20 alkenylene chain e.g., methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, decy
  • alkylene refers to a bivalent hydrocarbon.
  • C n means the alkylene group has “n” carbon atoms.
  • C 1-6 alkylene refers to an alkylene group having, e.g., 1, 2, 3, 4, 5, or 6 carbon atoms.
  • alkenylene refers to a bivalent hydrocarbon having at least one double bond.
  • Suitable aromatic groups include, but are not limited to, phenyl, naphthyl, tetrahydronaphthyl, phenanthrenyl, biphenylenyl, indanyl, indenyl, anthracenyl, fluorenylpyridyl, pyrazinyl, pyrimidinyl, pyrrolyl, pyrazolyl, imidazolyl, thiazolyl, tetrazolyl, oxazolyl, isooxazolyl, thiadiazolyl, oxadiazolyl, furanyl, quinolinyl, isoquinolinyl, benzoxazolyl, benzimidazolyl, and benzothiazolyl groups, and combinations thereof.
  • the pendant hydrophilic group includes one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) sulfonate groups. In some cases, the pendant hydrophilic group includes one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) phosphate groups. In some examples, the pendant hydrophilic group includes one or more ammonium groups (e.g., tertiary and/or quaternary ammonium). In other examples, the pendant hydrophilic group includes one or more zwitterionic groups (e.g., a betaine, such as poly(carboxybetaine (pCB) and ammonium phosphonate groups such as a phosphatidylcholine group).
  • a betaine such as poly(carboxybetaine (pCB) and ammonium phosphonate groups such as a phosphatidylcholine group.
  • the pendant “hydrophilic” group is at least one polyether group, such as two polyether groups. In other cases, the pendant hydrophilic group is at least one polyester. In various cases, the pendant hydrophilic group is polylactone group (e.g., polyvinylpyrrolidone). Each carbon atom of the pendant hydrophilic group can optionally be substituted with, e.g., a C 1-6 alkyl group. In some of these aspects, the aliphatic and aromatic groups can be graft polymeric groups, wherein the pendant groups are homopolymeric groups (e.g., polyether groups, polyester groups, polyvinylpyrrolidone groups).
  • the pendant hydrophilic group is a polyether group (e.g., a polyethylene oxide group, a polyethylene glycol group), a polyvinylpyrrolidone group, a polyacrylic acid group, or combinations thereof.
  • a polyether group e.g., a polyethylene oxide group, a polyethylene glycol group
  • a polyvinylpyrrolidone group e.g., a polyacrylic acid group, or combinations thereof.
  • thermoplastic polyurethane elastomer can be physically crosslinked through e.g., nonpolar or polar interactions between the urethane or carbamate groups on the polymers (the hard segments.
  • component R 1 in Formula 1, and components R 1 and R 3 in Formula 2 forms the portion of the polymer often referred to as the “hard segment”
  • component R 2 forms the portion of the polymer often referred to as the “soft segment”.
  • the soft segment can be covalently bonded to the hard segment.
  • thermoplastic polyurethane elastomer having physically crosslinked hard and soft segments can be a hydrophilic thermoplastic polyurethane elastomer (i.e., a thermoplastic polyurethane elastomer including hydrophilic groups as disclosed herein).
  • the thermoplastic polyurethane elastomer is an aromatic polyester thermoplastic elastomeric polyurethane or an aliphatic polyester thermoplastic elastomeric polyurethane having the following properties: (1) a glass transition temperature glass transition temperature of from about 20 degrees Celsius to about ⁇ 60 degrees Celsius; (2) a Taber Abrasion Resistance of from about 10 milligrams to about 40 milligrams as determined by ASTM D3389; (3) a Durometer Hardness (Shore A) of from about 60 to about 90 as determined by ASTM D2240; (4) a specific gravity of from about 0.80 g/cm 3 to about 1.30 g/cm 3 as determined by ASTM D792; (5) a melt flow index of about 2 grams/10 minutes to about 50 grams/10 minutes at 160 degrees Celsius using a test weight of 2.16 kilograms; (6) a melt flow rate greater than about 2 grams/10 minutes at 190 degrees Celsius or 200 degrees Celsius when using a test weight of 10 kilograms; and (7) a modulus
  • thermoplastic polyurethane elastomers having greater hydrophilicity suitable for the present use include, but are not limited to those under the tradename “TECOPHILIC”, such as TG-500, TG-2000, SP-80A-150, SP-93A-100, SP-60D-60 (Lubrizol, Countryside, Ill.), “ESTANE” (e.g., 58238, T470A; Lubrizol, Countryside, Ill.), and “ELASTOLLAN” (e.g., 9339, B70A; BASF).
  • TECOPHILIC such as TG-500, TG-2000, SP-80A-150, SP-93A-100, SP-60D-60 (Lubrizol, Countryside, Ill.), “ESTANE” (e.g., 58238, T470A; Lubrizol, Countryside, Ill.), and “ELASTOLLAN” (e.g., 9339, B70A; BASF).
  • the thermoplastic elastomer is a thermoplastic elastomeric styrenic copolymer.
  • these copolymers include, but are not limited to, styrene butadiene styrene (SBS) block copolymer, a styrene ethylene/butylene styrene (SEBS) resin, a polyacetal resin (POM) a styrene acrylonitrile resin (SAN), or a blend, alloy, or compound thereof.
  • SBS styrene butadiene styrene
  • SEBS styrene ethylene/butylene styrene
  • POM polyacetal resin
  • SAN styrene acrylonitrile resin
  • thermoplastic elastomeric styrenic copolymers include MONOPRENE IN5074, SP066070, and SP16975 (Teknor Apex, Pawtucket, R.I., USA), which are styrene ethylene/butylene styrene (SEBS) resins.
  • SEBS styrene ethylene/butylene styrene
  • blends, alloys, and compounds should be melt compatible or can be compatibilized with additives, oils, or grafted chemical moieties in order to achieve miscibility.
  • thermoplastic elastomeric styrenic copolymer includes at least one block as illustrated below in Formula 3:
  • SEBS polymers have a density from about 0.88 grams per cubic centimeter to about 0.92 grams per cubic centimeter. In a further aspect, SEBS polymers can be as much as 15 to 25 percent less dense than cross-linked rubbers, cross-linked polyurethanes, and thermoplastic polyurethane materials. In a further aspect, a less dense coating composition offers weight savings and per part cost savings for the same material of volume employed while achieving similar performance.
  • the films, fibers, and yarns described herein can further comprise an additive.
  • the additive can be incorporated directly into the films, fibers, and yarns, or alternatively, applied thereto.
  • Additives that can be used include, but are not limited to, dyes, pigments, colorants, ultraviolet light absorbers, hindered amine light stabilizers, antioxidants, processing aids or agents, plasticizers, lubricants, emulsifiers, pigments, dyes, optical brighteners, rheology additives, catalysts, heat stabilizers, flow-control agents, slip agents, lubricating agents, crosslinking agents, crosslinking boosters, halogen scavengers, smoke inhibitors, flameproofing agents, antistatic agents, fillers, or mixtures of two or more of the foregoing.
  • an additive can be present in an amount of from about 0.01 weight percent to about 10 weight percent, about 0.025 weight percent to about 5 weight percent, or about 0.1 weight percent to 3 weight percent, where the weight percent is based upon the sum of the material components in the film, fiber, filament or yarn.
  • thermoplastic elastomer(s) can be mixed together with the other components of the thermoplastic elastomer(s) in a continuous mixer or a batch mixer, e.g., in an intermeshing rotor mixer, such as an Intermix mixer, a twin screw extruder, in a tangential rotor mixer such as a Banbury mixer, using a two-roll mill, or some combinations of these to make a composition comprising a thermoplastic polymer and an additive.
  • the mixer can blend the components together via a single step or multiple steps, and can mix the components via dispersive mixing or distributive mixing to form the resulting thermoplastic composition. This step is often referred to as “compounding.”
  • first, second, third, etc. can be used herein to describe various elements, components, regions, layers and/or sections. These elements, components, regions, layers and/or sections should not be limited by these terms. These terms can be only used to distinguish one element, component, region, layer or section from another region, layer or section. Terms such as “first,” “second,” and other numerical terms do not imply a sequence or order unless clearly indicated by the context. Thus, a first element, component, region, layer or section discussed below could be termed a second element, component, region, layer or section without departing from the teachings of the example configurations.
  • ratios, concentrations, amounts, and other numerical data can be expressed herein in a range format. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the disclosure, e.g. the phrase “x to y” includes the range from ‘x’ to ‘y’ as well as the range greater than ‘x’ and less than ‘y’. The range can also be expressed as an upper limit, e.g. ‘about x, y, z, or less’ and should be interpreted to include the specific ranges of ‘about x’, ‘about y’, and ‘about z’ as well as the ranges of ‘less than x’, less than y’, and ‘less than z’.
  • the phrase ‘about x, y, z, or greater’ should be interpreted to include the specific ranges of ‘about x’, ‘about y’, and ‘about z’ as well as the ranges of ‘greater than x’, greater than y’, and ‘greater than z’.
  • the phrase “about ‘x’ to ‘y’”, where ‘x’ and ‘y’ are numerical values, includes “about ‘x’ to about ‘y’”.
  • the terms “about,” “approximate,” “at or about,” and “substantially” mean that the amount or value in question can be the exact value or a value that provides equivalent results or effects as recited in the claims or taught herein. That is, it is understood that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but can be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art such that equivalent results or effects are obtained. In some circumstances, the value that provides equivalent results or effects cannot be reasonably determined.
  • references to “a” chemical compound” refers to one or more molecules of the chemical compound, rather than being limited to a single molecule of the chemical compound. Furthermore, the one or more molecules can or cannot be identical, so long as they fall under the category of the chemical compound. Thus, for example, “a polyamide” is interpreted to include one or more polymer molecules of the polyamide, where the polymer molecules can or cannot be identical (e.g., different molecular weights and/or isomers).
  • At least one and “one or more of” an element are used interchangeably, and have the same meaning that includes a single element and a plurality of the elements, and can also be represented by the suffix “(s)” at the end of the element.
  • at least one polyamide”, “one or more polyamides”, and “polyamide(s)” can be used interchangeably and have the same meaning.
  • the terms “optional” or “optionally” means that the subsequently described component, event or circumstance can or cannot occur, and that the description includes instances where said component, event or circumstance occurs and instances where it does not.
  • receiving such as for “receiving an upper for an article of footwear”, when recited in the claims, is not intended to require any particular delivery or receipt of the received item. Rather, the term “receiving” is merely used to recite items that will be referred to in subsequent elements of the claim(s), for purposes of clarity and ease of readability.
  • weight percent and “wt percent,” which can be used interchangeably, indicate the percent by weight of a given component based on the total weight of the composition, unless otherwise specified. That is, unless otherwise specified, all wt percent values are based on the total weight of the composition. It should be understood that the sum of wt percent values for all components in a disclosed composition or formulation are equal to 100.
  • temperatures referred to herein are determined at standard atmospheric pressure (i.e., 1 ATM).
  • the coefficient of friction (COF) is then calculated from the ratio of the two forces. Dry COF is determined by testing a dry sample against a dry testing surface, and wet COF is determined by testing a sample wetted with water by soaking it in room temperature water for 10 minutes against a test surface wetted with room temperature water.
  • the static and dynamic coefficient of friction (COF) of a sample prepared using the Component Sampling Procedure or the Textile Sampling Procedure described below against a sample from a panel of a “MERLIN” soccer ball (Nike Inc., Beaverton, Oreg., USA) is determined using a modified version of test method ASTM D1894.
  • ASTM D1894 the sample is cut to size and mounted on an acrylic substrate, and the ball material is cut to size and mounted on the sled. Once the ball material has been mounted on the sled, the sled has a contact footprint of 3.9 inches by 1 inch, and a weight of approximately 1.7 kilograms.
  • the sample and ball material are positioned with the outer surface of the ball material contacting the surface of the sample which is intended form the outer surface of an article of footwear, and the sled is pulled across the sample. Dry samples and dry ball material are used to determine the static or dynamic dry COF. To determine the static or dynamic wet COF, the sample and the ball material are both soaked in room temperature water for 10 minutes immediately prior to testing. Each measurement is repeated at least 3 times, and the results of the runs are averaged.
  • Each article of footwear can be tested on one of two surfaces in wet and dry conditions: (1) quarry tile, and (2) smooth concrete. Footwear tested using the Whole Footwear Coefficient of Friction Test when new can subsequently be subjected to abrasion using the Whole Footwear Abrasion Test and then re-tested using the Whole Footwear Coefficient of Friction Test to simulate the traction and slip resistance of the footwear on surfaces after the equivalent of many days or miles worth of simulated wear. Coefficient of friction is calculated from the applied force to laterally translate the outsole of the shoe across the substrate divided by the applied normal force loaded on the sample as specified in the test method.
  • Biomechanical abrasion testing is performed on outsoles of whole articles of footwear using the SATRA TM362 testing method.
  • a walking action over a real wear surface is simulated.
  • Sample footwear is mounted on a mechanical leg and a flooring mechanism rotates to simulate turns during walking with the forepart of the sole in contact with the walking surface.
  • the force applied by the footwear on the sample flooring surface follows a distinct profile that can be adjusted by adding or subtracting weights.
  • a standard load of 180 pounds is used, and the speed can be adjusted to replicate normal walking, running, and/or sprinting.
  • the walking surface is a textured concrete slab. Samples are conditioned for 24 hours in a climate controlled lab and inserted into the machine. Each sample is tested for 48 hours of simulated foot strikes, or about 96,000 steps, which approximates 100 miles of walking. Mass loss is recorded at 24 hours and at 48 hours of testing.
  • the melting temperature and/or glass transition temperature are determined for a sample prepared according to Material Sampling Procedure described below, using a commercially available Differential Scanning Calorimeter (“DSC”) in accordance with ASTM D3418-97. Briefly, a 10-60 milligram sample is placed into an aluminum DSC pan and then the lid is sealed with a crimper press. The DSC is configured to scan from ⁇ 100 degrees Celsius to 225 degrees Celsius with a 20 degree Celsius/minute heating rate, hold at 225 degrees Celsius for 2 minutes, and then cool down to 25 degrees Celsius at a rate of ⁇ 20 degrees Celsius/minute. The DSC curve created from this scan is then analyzed using standard techniques to determine the glass transition temperature and the melting temperature. Melting enthalpy is calculated by integrating the melting endotherm and normalizing by the mass of the sample. Crystallization enthalpy upon cooling is calculated by integrating the cooling endotherm and normalizing by the mass of the sample.
  • DSC Differential Scanning Calorimeter
  • the Vicat softening temperature is determined for a sample prepared according to Material Sampling Procedure or the Component Sampling Procedure described below, according to the test method detailed in ASTM Tm D1525-09 Standard Test Method for Vicat Softening Temperature of Plastics, preferably using Load A and Rate A. Briefly, the Vicat softening temperature is the temperature at which a flat-ended needle penetrates the specimen to the depth of 1 millimeter under a specific load. The temperature reflects the point of softening expected when a material is used in an elevated temperature application. It is taken as the temperature at which the specimen is penetrated to a depth of 1 millimeter by a flat-ended needle with a 1 square millimeter2 circular or square cross-section.
  • the test involves placing a test specimen in the testing apparatus so that the penetrating needle rests on its surface at least 1 millimeter from the edge. A load is applied to the specimen per the requirements of the Vicat A or Vicat B test. The specimen is then lowered into an oil bath at 23° C. degrees Celsius. The bath is raised at a rate of 50 degrees Celsius or 120 degrees Celsius per hour until the needle penetrates 1 millimeter. The test specimen must be between 3 and 6.5 millimeter thick and at least 10 millimeter in width and length. No more than three layers can be stacked to achieve minimum thickness.
  • melt flow index is determined for a sample prepared according to the Material Sampling Procedure described below according to the test method detailed in ASTM D1238-13 Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer, using Procedure A described therein. Briefly, the melt flow index measures the rate of extrusion of thermoplastics through an orifice at a prescribed temperature and load. In the test method, approximately 7 grams of the material is loaded into the barrel of the melt flow apparatus, which has been heated to a temperature specified for the material. A weight specified for the material is applied to a plunger and the molten material is forced through the die. A timed extrudate is collected and weighed.
  • melt flow index values are calculated in g/10 min for a given applied load and applied temperature. As described in ASTM D1238-13, melt flow index can be determined at 160 degrees Celsius using a weight of 2.16 kg, or at 200 degrees Celsius using a weight of 10 kg.
  • the test is conducted using 2 millimeter plaques or films prepared according to the Plaque or Film Sampling Procedure described below. A circular die is used to cut 50 millimeter specimen discs of from the plaque or film. Test specimens are mounted on a 50 millimeter diameter aluminum parallel plate on an ARES-G2 (displacement controlled) rheometer. The top plate is lowered so that the test specimens are in contact with both disc surfaces under a defined normal force load and the stage is heated to 210 degrees Celsius. Samples are equilibrated until molten, for a defined dwell time of minutes, and oscillatory shear frequency sweeps are applied at low strain amplitudes to gather rate-dependent data. The ratio of the applied shear stress required to generate the oscillatory motion at a given shear frequency rate yields the measured viscosity value. Shear rate-dependent viscosity data can be gathered from 0.1 reciprocal seconds to 1000 reciprocal seconds.
  • the modulus for sample prepared according to the Plaque or Film Sampling Procedure described below is determined according to the test method detailed in ASTM D412-98 Standard Test Methods for Vulcanized Rubber and Thermoplastic Rubbers and Thermoplastic Elastomers-Tension, with the following modifications.
  • the sample dimension is the ASTM D412-98 Die C, and the sample thickness used is 2.0 millimeters plus or minus 0.5 millimeters.
  • the grip type used is a pneumatic grip with a metal serrated grip face. The grip distance used is 75 millimeters.
  • the loading rate used is 500 millimeters/minute.
  • the modulus (initial) is calculated by taking the slope of the stress (MPa) versus the strain in the initial linear region. This test can also be used to determine other tensile properties such as break strength, strain to break, load at 100 percent strain, toughness, stiffness, tear strength, and the like.
  • Yarn Denier and Thickness Test To determine denier, a sample of yarn is prepared according to the Yarn Sampling Procedure described below. A known length of the yarn sample and its corresponding weight are measured. This is converted to grams per 9000 meters of yarn. To determine the thickness of a coated yarn, the yarn is first cut with a razor and observed under a microscope, where coating thickness relative to core yarn diameter is determined to scale.
  • the modulus for a yarn is determined for a sample prepared according to the Yarn Sampling Procedure described above, and tested according to the test method detailed in EN ISO 2062 (Textiles-Yarns from Packages)—Determination of Single-End Breaking Force and Elongation at Break Using Constant Rate of Extension (CRE) Tester. The following modifications to the test method are used. 5 test specimens are prepared with a sample length of 600 millimeters. The equipment used is an Instron Universal Testing System. Instron Pneumatic cord and Thread Grips or similar pneumatic grips are installed, with a grip distance of 250 millimeters.
  • Grip distance is set to 145+1 millimeter and gauge length is set at 250+2 millimeters when using Instron Pneumatic Cord and Thread Grips.
  • the pre-loading is set to 5 grams and the loading rate used is 250 millimeters/minute.
  • the modulus (initial) is calculated by taking the slope of the stress (MPa) versus the strain in the initial linear region. Maximum tensile force value is recorded.
  • Tenacity and elongation of the yarn sample are determined according to the test method detailed in EN ISO 2062 with the pre-load set to 5 grams. Elongation is recorded at the maximum tensile force value applied prior to breaking. Tenacity can be calculated as the ratio of load required to break the specimen to the linear density of the specimen.
  • Durometer Hardness Test The hardness of a material is determined for a sample prepared according to the Material Sampling Procedure, the Component Sampling Procedure, the Plaque or Film Sampling Procedure, or the Textile Sampling Procedure described below, according to the test method detailed in ASTM D-2240 Durometer Hardness, using a Shore A scale.
  • the specific gravity for a sample prepared according to the Material Sampling Procedure, the Component Sampling Procedure, the Plaque or Film Sampling Procedure, the Yarn Sampling Procedure, or the Textile Sampling Procedure described below is determined according to the test method detailed in ASTM D792 using volume displacement.
  • the free-standing shrinkage of yarns can be determined by the following method.
  • a yarn sample is prepared according to the Yarn Sampling Procedure described below, and is cut to a length of approximately 30 millimeters with minimal tension at approximately room temperature (e.g., 20 degrees Celsius).
  • the cut sample is placed in a 50 degrees Celsius or 70 degrees Celsius oven for 90 seconds.
  • the sample is removed from the oven and measured.
  • the percentage of shrink is calculated using the pre-and post-oven measurements of the sample, by dividing the post-oven measurement by the pre-oven measurement, and multiplying by 100.
  • the cold Ross flex test is determined using a sample prepared according to the Plaque or Film Sampling Procedure described below according the following test method. The purpose of this test is to evaluate the resistance to cracking of a sample under repeated flexing to 60 degrees in a cold environment.
  • the plaque sample is sized to fit inside the flex tester machine. Each material is tested as five separate samples.
  • the flex tester machine is capable of flexing samples to 60 degrees at a rate of 100 ⁇ 5 cycles per minute.
  • the mandrel diameter of the machine is 10 millimeters. Suitable machines for this test include the Emerson AR-6, the Satra S T m 141F, the Gotech GT-7006, and the Shin II Scientific SI-LTCO (DaeSung Scientific).
  • the sample(s) are inserted into the machine according to the specific parameters of the flex machine used.
  • the machine is placed in a freezer set to ⁇ 6 degrees Celsius for the test.
  • the motor is turned on to begin flexing with the flexing cycles counted until the sample cracks. Cracking of the sample means that the surface of the material is physically split. Visible creases of lines that do not actually penetrate the surface are not cracks.
  • the sample is measured to a point where it has cracked but not yet broken in two.
  • the Bally Flex test which is based on standard methods including ISO 5402, ISO 32100, SATRA TM55, DIN 53351, and BS-3144, is conducted as follows, using samples prepared according to the Component Sampling Procedure, the Plaque or Film Sampling Procedure, or the Textile Sampling Procedure described below. A minimum of 6 samples are required for this test method. Samples are 60 millimeters ⁇ 75 millimeters and can be hand cut or die cut. Each sample is folded and inserted into the testing equipment such that it protrudes from the bottom clamp a distance equal to the sample thickness. The folded front edge of the sample is perpendicular to the base of the testing machine. The samples are then repeatedly flexed. Samples are visually inspected during the test period.
  • the wet Bally Flex test is designed to assess the ability of a sample textile, film, or other specimen to resist water penetration from repeated flexing and is conducted as follows using samples prepared according to the Component Sampling Procedure, the Plaque or Film Sampling Procedure, or the Textile Sampling Procedure described below. At a minimum, 4 samples are required. Specimens are 60 millimeters ⁇ 75 millimeters and can be hand cut or die cut. 1 gram of sodium chloride is dissolved in 1 liter of distilled water and stirred to create a sodium chloride solution. The sodium chloride solution is poured into a water tank and placed into the testing machine.
  • a Gotech GT-7071-DWN instrument (Gotech Testing Machines, Taichung City, Taiwan) or similar instrument can be used for analysis. Specimens are folded into a U shape and clamped into the instrument such that the side of the specimens to be tested for water penetration faces outward. The samples are then repeatedly flexed. If a specimen remains intact through at least 5000 cycles of flexing, it can be considered “water resistant.” If a sample remains intact for at least 15,000 cycles of flexing, it can be considered “waterproof.” If a specimen leaks, triggering a sensor, before all cycles have been conducted, the specimen is said to fail.
  • Abrasion resistance including abrasion resistance simulating footwear upper scuffing
  • Stoll abrasion test can be measured using the Stoll abrasion test, using samples prepared according to the Component Sampling Procedure, the Plaque or Film Sampling Procedure, or the Textile Sampling Procedure described below.
  • the minimum number of samples for Stoll abrasion testing is 3. Samples used herein were hand cut or die cut into circles having a 112 millimeter diameter.
  • the Stoll abrasion test is described more fully in ASTM D3886 and can be performed on the Atlas Universal Wear Tester. In the Stoll abrasion test, an abrading medium is moved over the stationary, mounted test sample and the visual appearance of the sample is monitored.
  • the Stoll abrasion test is performed under pressure to simulate wear under normal usage.
  • Abrasion resistance including abrasion resistance simulating footwear sole structure scuffing of ground-contacting areas can be measured using the Akron abrasion test, using samples prepared according to the Component Sampling Procedure, the Plaque or Film Sampling Procedure, or the Textile Sampling Procedure described below.
  • a sample strip is cut from a sample, wherein the strip is approximately 2-3 millimeters thick, 0.5 inches (127 millimeters) wide, and 8 inches (2032 millimeters) long.
  • the strip is mounted to the perimeter of a rubber wheel, and the wheel is mounted so the strip is pushed against an abrasive grit surface at a slight angle (approximately 15 degrees) and under a known force (approximately 6 pounds or 2.72 kilograms).
  • the strip is run for a number of cycles to prepare the surface, cleaned with a brush and vacuum, and weighed.
  • the strip is then mounted against the abrasive wheel and run for about 3000 additional cycles, then cleaned and weighed again. Mass loss can be adjusted based on the density of the material. The measured mass and volume losses represent the abrasion level of resistance.
  • Abrasion loss is tested on cylindrical samples with a diameter of 16 ⁇ 0.2 millimeters and a minimum thickness of 6 millimeters cut using a ASTM standard hole drill.
  • the abrasion loss is measured using Method B of ASTM D 5963-97a on a Gotech GT-7012-D abrasion test machine.
  • the tests are performed as 22 degrees Celsius with an abrasion path of 40 meters.
  • the Standard Rubber #1 used in the tests has a density of 1.336 grams per cubic centimeter (g/cm 3 ). The smaller the abrasion loss volume, the better the abrasion resistance.
  • Test specimens for softer materials are cut to the same size, with length direction marked on the test specimens.
  • Backing paper is prepared from white or off-white paper towels, coffee filters, or similar thin, absorbent papers. Backing paper is also cut into 220 millimeter diameter circles.
  • One backing paper is prepared per test specimen and backing paper is not reused.
  • the backing paper and a specimen are placed in a sample fixture, which is in turn placed in a spray testing device.
  • the sample length direction should be parallel with the water flow direction.
  • a funnel is adjusted to a height of 6 inches (152.4 millimeters) between a spray nozzle and the test specimen. The spray nozzle must be over the center of the test specimen. 250 ⁇ 2 milliliters of distilled water are added to the funnel, which causes water to spray onto the test specimen.
  • the top surface is evaluated for water repellency.
  • the sample fixture is removed from the support base and the backing paper is evaluated to determine if water penetrated through the sample. Water penetration is reported after visual assessment and samples are rated as “pass” or “fail” according to the degree of wetting. If no sticking or wetting of the top surface is observed, if slight random sticking or wetting of the top surface is observed, or if wetting of the top surface is observed at spray points, the sample is considered to pass. Further wetting beyond the spray points and/or including the back surface indicates the sample has failed the water penetration test.
  • Test samples of textiles are prepared according to the Component Sampling Procedure or the Textile Sampling Procedure described below.
  • a 10 inch by 8 inch test sample of the textile is mounted on the outer surface on a metal cylinder having a 10 inch circumference.
  • the test sample and cylinder are mounted on the swinging arm of a robot, the swinging arm is swung at a rate of 50 miles per hour, and impacts the equator of a stationary ball.
  • the ball used is a regulation size Nike “MERLIN” soccer ball inflated to 0.80 bar.
  • a high speed video camera is used to record the ball position immediately following the impact. Using the position in space and rotation of the ball across multiple frames of the images recorded by the high-speed video camera, software is then used to calculate the velocity and spin rate of the ball immediately after impact. Each measurement is repeated at least 3 times, and the results of the runs are averaged.
  • a whole men's size 10.5 football boot, or the upper of a men's size 10.5 football boot, is mounted on the swinging arm of a robot, and positioned so the ball impacts the boot on the medial side of the vamp, on or near the laces (when the boot includes a lacing structure), and the upper impacts the equator of the ball when the singing arm of the robot is swung at a rate of 50 miles per hour.
  • the ball used is a regulation size Nike “MERLIN” soccer ball inflated to 0.80 bar.
  • a high speed video camera is used to record the ball position immediately following the impact. Using the position in space and rotation of the ball across multiple frames of the images recorded by the high-speed video camera, software is then used to calculate the velocity and spin rate of the ball immediately after impact. Each measurement is repeated at least 3 times, and the results of the runs are averaged.
  • the Material Sampling Procedure can be used to obtain a neat sample of a polymeric composition or of a polymer, or, in some instances, a sample of a material used to form a polymeric composition or a polymer.
  • the material is provided in media form, such as flakes, granules, powders, pellets, and the like. If a source of the polymeric material or polymer is not available in a neat form, the sample can be cut from a component or element containing the polymeric material or polymer, such as a composite element or a sole structure, thereby isolating a sample of the material.
  • Plaque or Film Sampling Procedure A sample of a polymeric composition or a polymer is prepared. A portion of the polymer or polymeric composition is then be molded into a film or plaque sized to fit the testing apparatus. For example, when using a Ross flexing tester, the plaque or film sample is sized to fit inside the Ross flexing tester used, the sample having dimensions of about 15 centimeters (cm) by 2.5 centimeters (cm) and a thickness of about 1 millimeter (mm) to about 4 millimeters (mm) by thermoforming the polymeric composition or polymer in a mold.
  • the sample can be prepared by melting the polymer, charging the molten polymer into a mold, re-solidifying the polymer in the shape of the mold, and removing the solidified molded sample from the mold.
  • the sample of the polymer can be melted and then extruded into a film which is cut to size.
  • the sample can be prepared by blending together the ingredients of the polymeric composition, melting the thermoplastic ingredients of the polymeric composition, charging the molten polymeric composition into a mold, re-solidifying the polymeric composition in the shape of the mold, and removing the solidified molded sample from the mold.
  • the sample of the polymer material can be prepared by mixing and melting the ingredients of the polymeric composition, and then the molten polymeric composition can be extruded into a film which is cut to size.
  • the film is extruded as a web or sheet having a substantially constant film thickness for the film (within ⁇ 10 percent of the average film thickness) and cooled to solidify the resulting web or sheet.
  • a sample having a surface area of 4 square centimeters is then cut from the resulting web or sheet.
  • the film can be cut from a substrate of a footwear component, or from a backing substrate of a co-extruded sheet or web, thereby isolating the film. In either case, a sample having a surface area of 4 square centimeters is then cut from the resulting isolated film.
  • This procedure can be used to obtain a sample of a material from a component of an article of footwear, an article of footwear, a component of an article of apparel, an article of apparel, a component of an article of sporting equipment, or an article of sporting equipment, including a sample of a polymeric composition or of a textile, or a portion of a textile, such as thermoformed network.
  • a sample including the material in a non-wet state e.g., at 25 degrees Celsius and 20 percent relative humidity
  • the procedure can include separating the additional materials from the material to be tested.
  • the opposite surface can be skinned, abraded, scraped, or otherwise cleaned to remove any adhesives, yarns, fibers, foams, and the like which are affixed to the material to be tested.
  • the resulting sample includes the material and may include any additional materials bonded to the material.
  • the sample is taken at a location along the article or component that provides a substantially constant material thickness for the material as present on the article or component (within plus or minus 10 percent of the average material thickness), such as, for an article of footwear, in a forefoot region, midfoot region, or a heel region of a ground-facing surface.
  • a sample having a surface area of 4 square centimeters (cm 2 ) is used.
  • the sample is cut into a size and shape (e.g., a dogbone-shaped sample) to fit into the testing apparatus.
  • sample sizes with smaller cross-sectional surface areas can be taken and the area-specific measurements are adjusted accordingly.
  • Yarn Sampling Procedure Yarn to be tested is stored at room temperature (20 degrees Celsius to 24 degrees Celsius) for 24 hours prior to testing. The first 3 meters of material are discarded. A sample yarn is cut to a length of approximately 30 millimeters with minimal tension at approximately room temperature (e.g., 20 degrees Celsius).
  • a textile to be tested is stored at room temperature (20 degrees Celsius to 24 degrees Celsius) for 24 hours prior to testing.
  • the textile sample is cut to size as dictated by the test method to be used, with minimal tension at approximately room temperature (e.g., 20 degrees Celsius).
  • Aspect 2 The textile of Aspect 1, wherein the textile is a knit or crochet textile, and the first network of yarns includes connected loops of the first coated yarn.
  • Aspect 3 The textile of Aspect 1, wherein the textile is a woven textile, and the first network of yarns includes interlaced sets of yarns comprising the first coated yarn in a warp direction, or in a weft direction, or in both the warp and weft directions.
  • Aspect 4 The textile of Aspect 1, wherein the textile is a non-woven textile, and the first network of yarns includes entangled or bonded yarns comprising the first coated yarn.
  • Aspect 5 The textile of Aspect 4, wherein the entangled or bonded yarns comprise mechanically entangled yarns, thermally bonded yarns, yarns bonded by a solvent treatment, chemically bonded yarns, or any combination thereof.
  • Aspect 6 The textile of any of Aspects 1-5, wherein the first core yarn comprises a second polymeric composition, and wherein the first polymeric composition of the first coating has a first melting temperature.
  • Aspect 7 The textile of Aspect 6, wherein the second polymeric composition is a second thermoplastic composition having a second deformation temperature, and the second deformation temperature is at least 20 degrees Celsius (C) greater, or optionally at least 50 degrees C. greater, or optionally at least 100 degrees C. greater than the first melting temperature of the first thermoplastic composition.
  • C degrees Celsius
  • Aspect 8 The textile of Aspect 6 or 7, wherein the second polymeric composition is a second thermoset composition.
  • Aspect 9 The textile of any of Aspects 1-8, wherein the first core yarn comprises a first core yarn composition comprising a polyester or a polyamide.
  • Aspect 10 The textile of any of Aspects 1-9, wherein the first core yarn has a linear density from about 100 denier to about 300 denier, or has a diameter of from about 60 to 200 microns.
  • Aspect 11 The textile of any of Aspects 1-10, wherein the first coating is axially centered surrounding the core yarn, and the first coating thickness leads to a nominal average outer diameter of the coated yarn of up to about 1.0 millimeter.
  • Aspect 12 The textile of any of Aspects 1-11, wherein the first coating is axially centered surrounding the first core yarn, and the first coating thickness leads to a nominal average outer diameter of the coated yarn of about 0.1 millimeters to about 0.6 millimeters.
  • Aspect 13 The textile of any of Aspects 1-12, wherein the first coating has an average radial coating thickness of about 50 micrometers to about 200 micrometers.
  • Aspect 14 The textile of any of Aspects 1-13, wherein the first polymeric composition has a melting temperature greater than about 110 degrees C. and less than about 190 degrees C.
  • Aspect 15 The textile of any of Aspects 1-13, wherein the first polymeric composition has a melting temperature greater than about 120 degrees C. and less than about 170 degrees C., and optionally greater than about 130 degrees C., and less than about 160 degrees C.
  • Aspect 16 The textile of any of Aspects 1-15, wherein the first polymeric composition has a glass transition temperature glass transition temperature of less than 20 degrees C.
  • Aspect 17 The textile of any of Aspects 1-16, wherein the first polymeric composition has a glass transition temperature glass transition temperature of from about 20 degrees C. to about ⁇ 60 degrees C.
  • Aspect 18 The textile of any of Aspects 1-17, wherein the first polymeric composition has a Taber Abrasion Resistance of from about 10 milligrams to about 40 milligrams as determined by ASTM D3389.
  • Aspect 19 The textile of any of Aspects 1-18, wherein the first polymeric composition has a Durometer Hardness (Shore A) of from about 60 to about 90, from about 60 to about 90, or from about 65 to about 85, or from about 70 to about 80 as determined by ASTM D2240.
  • Durometer Hardness Shore A
  • Aspect 20 The textile of any of Aspects 1-19, wherein the first polymeric composition has a specific gravity of from about 0.80 grams per cubic centimeter to about 1.30 grams per cubic centimeter, or from about 1.0 grams per cubic centimeter to about 1.2 grams per cubic centimeter as determined by ASTM D792.
  • Aspect 21 The textile of any of Aspects 1-20, wherein the first polymeric composition has a melt flow index of about 2 grams/10 minutes to about 50 grams/10 minutes at 160 degrees C. using a test weight of 2.16 kilograms as determined using ASTM D1238-13.
  • Aspect 22 The textile of any of Aspects 1-21, wherein the first polymeric composition has a melt flow index greater than about 2 grams/10minutes at 190 degrees C. or 200 degrees C. when using a test weight of 10 kilograms as determined using ASTM D1238-13.
  • Aspect 23 The textile of any of Aspects 1-22, wherein the first polymeric composition has a modulus of about 1 megapascal to about 500 megapascals as determined using the Plaque Modulus Test.
  • Aspect 24 The textile of any of Aspects 1-23, wherein the first polymeric composition comprises a polymeric component consisting of all the polymers present in the polymeric composition; optionally wherein and the polymeric component comprises two or more polymers, wherein the two or more polymers differ from each other in chemical structure of individual segments of each of the two or more polymers, or in molecular weight of each of the two or more polymers, or in both.
  • Aspect 25 The textile of any of Aspects 1-24, wherein the first polymeric composition comprises a thermoplastic elastomeric styrenic copolymer, a thermoplastic elastomeric polyurethane, or a combination thereof; optionally wherein the polymeric component of the first polymeric composition consists of the thermoplastic elastomeric styrenic copolymer, the thermoplastic elastomeric polyurethane, or the combination thereof.
  • thermoplastic elastomeric styrenic copolymer comprises a styrene butadiene styrene (SBS) block copolymer, a styrene ethylene/butylene styrene (SEBS) copolymer, a styrene acrylonitrile copolymer (SAN), or any combination thereof.
  • SBS styrene butadiene styrene
  • SEBS styrene ethylene/butylene styrene
  • SAN styrene acrylonitrile copolymer
  • thermoplastic elastomeric polyurethane comprises a thermoplastic elastomeric polyester polyurethane, a thermoplastic polyether polyurethane, or any combination thereof.
  • thermoplastic elastomeric polyurethane comprises an aromatic polyester thermoplastic elastomeric polyurethane.
  • thermoplastic elastomeric polyurethane comprises an aliphatic polyester thermoplastic elastomeric polyurethane.
  • Aspect 30 The textile of any of Aspects 1-29, wherein the textile further comprises a lubricating composition.
  • Aspect 31 The textile of Aspect 30, wherein the lubricating composition is from about 0.1 weight percent to about 3 weight percent of the textile.
  • Aspect 32 The textile of Aspect 30 or 31, wherein the lubricating composition comprises mineral oil, silicone oil, or a combination thereof.
  • Aspect 33 The textile of any of Aspects 1-32, wherein the first coated yarn has a stress at break greater than 7 megapascals, optionally greater than 8 megapascals, or greater than 8 megapascals as determined using ASTM DE-412 at 25 degrees C.
  • Aspect 34 The textile of any of Aspects 1-33, wherein the first coated yarn has a tensile stress at 300 percent modulus greater than 2 megapascals, optionally greater than 2.5 megapascals, or greater than 3 megapascals as determined using ASTM DE-412 at 25 degrees C.
  • Aspect 35 The textile of any of Aspects 1-34, wherein the first coated yarn has an elongation at break greater than 450 percent, optionally greater than 500 percent, or greater than 550 percent as determined using the Yarn Modulus, Tenacity and Elongation Test.
  • Aspect 36 The textile of any of Aspects 1-35, wherein the first coated yarn has a tenacity of about 1 gram per denier to about 10 grams per denier as determined using the Yarn Modulus, Tenacity and Elongation Test.
  • a textile comprising:
  • thermoformed network of yarns comprising a first core yarn and a first polymeric composition
  • first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • thermoformed network of yarns is the thermoformed product of a first textile comprising a first network of yarns including a first coated yarn comprising the first core yarn and a first coating, the first coating including the first polymeric composition, wherein, in the thermoformed network, the first polymeric composition consolidating the thermoformed network of yarns is the re-flowed and re-solidified product of the first polymeric composition of the first coating of the first coated yarn.
  • Aspect 40 The textile of any of Aspects 37 to 39, wherein, when the textile has a mass loss of less than 0.05 weight percent after 300 cycles as determined by the Akron Abrasion Test.
  • Aspect 41 The textile of any of Aspects 37 to 39, wherein the textile has a mass loss of less than 0.20 weight percent after 3,000 cycles as determined by the Akron Abrasion Test.
  • Aspect 42 The textile of any of Aspects 37 to 41, wherein the textile passes at least 1,200 cycles, or optionally at least 1,300 cycles, or at least 1,600 cycles of the Stoll Abrasion Test.
  • Aspect 43 The textile of any of Aspects 37 to 42, wherein the textile passes at least at least 75 cycles, or at least 100 cycles, or at least 125 cycles of the Bally Flex Test.
  • Aspect 44 The textile of any of Aspects 37 to 43, wherein the textile passes at least 3,000 cycles, or at least 5,000 cycles, or at least 7,000 cycles of the Wet Bally Flex Test.
  • Aspect 45 The textile of any of Aspects 37 to 44, wherein the textile produces a ball spin rate of at least 220 revolutions per minute, or a ball spin rate of about 220 revolutions per minute to about 240 revolutions per minute, as determined using the Textile-Ball Impact Test.
  • Aspect 46 The textile of any of Aspects 37 to 45, wherein the first polymeric composition has an abrasion loss of less than 0.50 cubic centimeters, optionally less than 0.40 cubic centimeters, less than 0.30 cubic centimeters, less than 0.20 cubic centimeters, or less than 0.10 cubic centimeters as determined using the Akron Abrasion Test.
  • Aspect 48 The textile of any of Aspects 37 to 47, wherein the first polymeric composition has a dry dynamic coefficient of friction of at least 1.0 as determined against dry smooth concrete using the Sample Coefficient of Friction Test.
  • Aspect 49 The textile of any of Aspects 37 to 48, wherein the first polymeric composition has a wet dynamic coefficient of friction of at least 0.5 as determined against wet smooth concrete using the Sample Coefficient of Friction Test.
  • Aspect 50 The textile of any of Aspects 37 to 49, wherein the difference between the dry dynamic coefficient of friction and the wet coefficient of the first polymeric composition as determine against smooth concrete is less than 40 percent, optionally less than 30 percent, or less than 20 percent as determined using the Sample Coefficient of Friction Test.
  • thermoformed network of the textile has a dry dynamic coefficient of friction of at least 0.8 as determined against dry smooth concrete using the Sample Coefficient of Friction Test.
  • Aspect 52 The textile of any of Aspects 37 to 51, wherein the first thermoformed network of the textile has a wet dynamic coefficient of friction of at least 0.5 as determined against wet smooth concrete using the Sample Coefficient of Friction Test.
  • Aspect 53 The textile of any of Aspects 37 to 52, wherein the difference between the dry dynamic coefficient of friction and the wet coefficient of the thermoformed network of the textile as determine against smooth concrete is less than 50 percent, optionally less than 40 percent, or less than 30 percent as determined using the Sample Coefficient of Friction Test.
  • Aspect 54 The textile of any of Aspects 37 to 53, wherein the difference between the static coefficient of friction of the dry surface and the wet surface of the textile is less than 40 percent, optionally less than 30 percent, or less than 20 percent as determined using the Sample Coefficient of Friction Test.
  • thermoformed network of the textile has a dry dynamic coefficient of friction of at least 1.0 as determined using the Textile-Ball Coefficient of Friction Test.
  • Aspect 56 The textile of any of Aspects 37 to 55, wherein the first thermoformed network of the textile has a wet dynamic coefficient of friction of at least 0.5 as determined using the Textile-Ball Coefficient of Friction Test.
  • Aspect 57 The textile of any of Aspects 37 to 56, wherein the difference between the dry dynamic coefficient of friction and the wet dynamic coefficient of friction is less than 40 percent, optionally less than 30 percent, or less than 20 percent as determined using the Textile-Ball Coefficient of Friction Test.
  • thermoformed network of the textile has a dry static coefficient of friction of at least 1.2 as determined using the Textile-Ball Coefficient of Friction Test.
  • thermoformed network of the textile has a wet static coefficient of friction of at least 0.9 as determined using the Textile-Ball Coefficient of Friction Test.
  • Aspect 60 The textile of any of Aspects 37 to 59, wherein the difference between the dry static coefficient of friction and the wet static coefficient of friction of the thermoformed network of the textile is less than 40 percent, optionally less than 30 percent, or less than 20 percent as determined using the Textile-Ball Coefficient of Friction Test.
  • Aspect 61 An article comprising the textile according to any one of Aspects 1 to 60.
  • Aspect 62 The article of Aspect 61, wherein the article is a component of an article of apparel, footwear, or sporting equipment, or is an article of apparel, footwear, or sporting equipment.
  • An upper for an article of footwear comprising:
  • Aspect 64 The upper of Aspect 63, wherein the textile defines at least a portion of a surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear.
  • Aspect 65 The upper of Aspect 63, wherein the textile defines at least a portion of the surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear, or defines at least a portion of a surface of the upper configured to be internally-facing when the upper is part of a finished article of footwear, or forms at least a portion of an interior layer of the upper when the upper is part of a finished article of footwear, or any combination thereof.
  • Aspect 66 The upper of any of Aspects 63 to 65, wherein the textile is a textile according to any one of Aspects 1 to 36.
  • An upper for an article of footwear comprising:
  • thermoformed network of yarns comprising a first core yarn and a first polymeric composition
  • first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns
  • first polymeric composition is a thermoplastic elastomeric composition
  • Aspect 68 The upper of Aspect 67, wherein the textile defines at least a portion of a surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear.
  • Aspect 69 The upper of Aspect 67, wherein the textile defines at least a portion of the surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear, or defines at least a portion of a surface of the upper configured to be internally-facing when the upper is part of a finished article of footwear, or forms at least a portion of an interior layer of the upper when the upper is part of a finished article of footwear, or any combination thereof.
  • Aspect 71 The upper of any of Aspects 67 to 70, wherein the textile comprises the textile of any of Aspects 1 to 60.
  • Aspect 72 The upper of any of Aspects 67-71, wherein the textile defines at least a portion of a surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear,
  • Aspect 73 The upper of any of Aspects 67-71, wherein the textile defines from about 15 percent to about 100 percent, or from about 15 percent to about 35 percent, or from about 40 percent to about 70 percent, or from about 75 percent to about 100 percent of the total surface area of the upper configured to be externally-facing when the upper is part of a finished article of footwear.
  • thermoformed network of the thermoformed textile defines at least a portion of a surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear
  • thermoformed network includes an externally-facing side
  • the externally-facing side of the thermoformed network defines at least a portion of the surface of the upper configured to be externally-facing when the upper is part of a finished article of footwear, and about 15 percent to 100 percent, or about 15 percent to 35 percent, or about 40 percent to 70 percent, or about 75 percent to 100 percent of a total surface area of the externally-facing side of the thermoformed network comprises the first polymeric composition.
  • Aspect 76 The upper of any of Aspects 67-75, wherein the first polymeric composition comprises about 15 percent to 95 percent by weight, or about 15 percent to 35 percent by weight, or about 40 percent to 70 percent by weight, or about 75 percent to 95 percent by weight of the textile, based on a total weight of the textile present in the upper.
  • Aspect 77 The upper of any of Aspects 67-76, wherein the textile produces a ball spin rate of at least 210 revolutions per minute, or a ball spin rate of about 210 revolutions per minute to about 230 revolutions per minute, as determined using the Upper-Ball Impact Test.
  • An outsole for an article of footwear comprising:
  • thermoformed network of yarns comprising a first core yarn and a first polymeric composition
  • first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns
  • first polymeric composition is a thermoplastic elastomeric composition
  • thermoformed network defines at least a portion of an externally-facing surface of the outsole, optionally wherein the externally-facing surface is configured to be ground-facing or ground-contacting when the outsole is part of a finished article of footwear.
  • thermoformed textile defines at least a portion of a heel region, a toe region, or a midfoot region, or any combination thereof, of the outsole.
  • thermoformed network of the textile when new, has a dry dynamic coefficient of friction of greater than 1.0 as determined against smooth concrete using the Whole Footwear Coefficient of Friction Test.
  • Aspect 82 The outsole of any of Aspects 78 to 81, wherein the thermoformed network of the textile, when new, has a wet dynamic coefficient of friction of greater than 0.5 as determined against smooth concrete using the Whole Footwear Coefficient of Friction Test.
  • Aspect 83 The outsole of any of Aspects 78 to 82, wherein the difference between the dry dynamic coefficient of friction and the wet dynamic coefficient of friction of the thermoformed network of the textile, when new, is less than 40 percent, optionally less than 30 percent, or less than 20 percent as determined against smooth concrete using the Whole Footwear Coefficient of Friction Test.
  • thermoformed network of the textile after being abraded according to the Whole Footwear Abrasion Test, has a dry dynamic coefficient of friction of greater than 0.9 as determined against smooth concrete using the Whole Footwear Coefficient of Friction Test.
  • thermoformed network of the textile after being abraded according to the Whole Footwear Abrasion Test, has a wet dynamic coefficient of friction of greater than 0.5 as determined against smooth concrete using the Whole Footwear Coefficient of Friction Test.
  • Aspect 86 The outsole of any of Aspects 78 to 85, wherein the difference between the dry dynamic coefficient of friction and the wet dynamic coefficient of friction of the thermoformed network of the textile, after being abraded according to the Whole Footwear Abrasion Test, is less than 40 percent, optionally less than 30 percent, or less than 20 percent as determined against smooth concrete using the Whole Footwear Coefficient of Friction Test.
  • thermoformed network defines at least a portion of a surface of the outsole configured to be ground-contacting when the outsole is part of a finished article of footwear, and the thermoformed network further comprises a layer of a third polymeric composition, wherein the third polymeric composition is a thermoplastic elastomeric composition comprising a thermoplastic elastomeric styrenic copolymer; wherein a first side of the layer defines the surface of the outsole configured to be ground-contacting when the outsole is part of a finished article of footwear, and a second side of the yarn opposite the first side is thermally bonded to a first side of the textile via the first polymeric composition of the textile.
  • Aspect 88 The outsole of Aspect 87, wherein the layer of the third polymeric composition is an extruded layer or an injection molded layer or a film layer.
  • thermoplastic elastomeric styrenic copolymer of the first polymeric composition and the thermoplastic elastomeric styrenic copolymer of the third polymeric component each have the same chemical structure, or the first polymeric composition and the third polymeric composition each have melting temperatures within about 10 degrees C. of each other, or both.
  • Aspect 90 The outsole of any of Aspects 87-89, wherein the layer of the third polymeric composition has a thickness of from about 0.1 millimeter to about 5 millimeters.
  • Aspect 91 The outsole of any of Aspects 78-90, wherein the textile comprises the textile of any of Aspects 1 to 60.
  • a method of making a textile comprising:
  • first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • Aspect 93 The method of Aspect 92, wherein the textile is a textile according to any one of Aspects 1-36.
  • a method of making a textile comprising:
  • thermoforming a first textile comprising a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; thereby forming a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns.
  • Aspect 95 The method of Aspect 94, wherein the first textile is a textile according to any one of Aspects 1 to 60.
  • a method of making an upper for an article of footwear comprising:
  • the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • a method of making an upper for an article of footwear comprising:
  • thermoforming an upper comprising a first textile wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition within the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns.
  • a method of making an upper for an article of footwear comprising:
  • the first textile comprises a thermoformed network of yarns comprising a first core yarn and a first polymeric composition
  • the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns, and wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • Aspect 100 The method of any of Aspects 97 to 99, wherein the first textile is a textile according to any one of Aspects 1 to 60.
  • Aspect 101 An upper made according to the method of any one of Aspects 97 to 100.
  • thermoforming comprises thermoforming the textile on a sole component, or on a molding surface, optionally wherein the molding surface is a molding surface having the dimensions of the outsole; wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition within the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in
  • Aspect 103 The method of Aspect 102, wherein the first textile has a first side and a second side, wherein the method further comprises thermally bonding a layer comprising a third polymeric composition to the first side or the second side of the first textile, wherein the third polymeric composition of the layer defines a surface of the outsole configured to be externally-facing or ground-facing or ground-contacting when the outsole is in a finished article of footwear.
  • Aspect 104 The method of Aspect 103, wherein the method comprises thermally bonding a sheet comprising the third polymeric composition to the first textile before, during or after the step of thermoforming the first textile.
  • Aspect 105 The method of Aspect 103, wherein the method comprises extruding or injection molding the third polymeric composition on the first side or the second side of the first textile before, during or after thermoforming the first textile.
  • Aspect 106 The method of any one of Aspects 102-105, wherein the first textile is a textile according to any one of Aspects 1 to 60.
  • Aspect 107 An outsole made according to the method of any one of Aspects 102 to 106.
  • a method of making an article comprising:
  • the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition.
  • a method of making an article comprising:
  • thermoforming a first textile wherein the first textile comprises a first network of yarns including a first coated yarn, the first coated yarn comprising a first core yarn and a first coating including a first polymeric composition disposed on at least a portion of an outer surface of the first core yarn, wherein the first polymeric composition is a thermoplastic elastomeric composition; and wherein the thermoforming comprises melting, reflowing, and re-solidifying the first polymeric composition within the first textile, forming a thermoformed textile comprising a thermoformed network of yarns comprising the first core yarn and the first polymeric composition, wherein the first polymeric composition consolidates the thermoformed network of yarns by surrounding at least a portion of the first core yarn and occupying at least a portion of spaces between yarns in the thermoformed network of yarns,
  • Aspect 110 A method of making an article, the method comprising:
  • Aspect 111 The method of any one of Aspects 108 to 110, wherein the first textile is a textile according to any one of Aspects 1 to 60.
  • Aspect 112. An article made by the method of any one of Aspects 108 to 111.
  • Thermoplastic polyurethane elastomers and thermoplastic styrenic copolymer elastomers were evaluated as candidates for the preparation of coated yarns, textiles and other articles as described herein. Several properties were determined for each polymer, and the results are summarized in Tables 1 and 2. The hardness of the polymers was determined using the Durometer Hardness Test, the specific gravity was determined using the Specific Gravity Test, the DIN abrasion loss was determined using the DIN Abrasion Test, and the coefficients of friction were determined using the Sample Coefficient of Friction Test as disclosed herein.
  • Coated yarns coated with polymeric compositions including polymers under investigation were made and their properties were investigated.
  • a comparison of hardness values, glass transition temperature, melting temperature, tensile strength, and elongation at break is provided in Table 3, where the hardness of the polymer was determined using the Durometer Hardness Test, the glass transition temperatures and the melting temperatures of the polymers were determined using the Melting and Glass Transition Temperature Test, and the yarn tensile strength and elongation were determined using the Yarn Modulus, Tenacity, and Elongation Test disclosed herein:
  • Estane 58238, Estane T470A-3, and Monprene SP66070 are particularly well-suited for high flow rate extrusion on fast moving fibers (e.g. core yarn).
  • Cross-linked rubber materials are known to exhibit reduced material or mass loss during abrasion testing, while thermoplastic materials have typically not been able to match the balance of traction and abrasion loss provided by cross-linked rubbers. However, the polymers tested showed good traction performance relative to known rubber outsole formulations. Results obtained in accordance with the Durometer Hardness Test, the Specific Gravity Test, the DIN Abrasion Test, and the Sample Coefficient of Friction Test described herein can be seen in Tables 7. Table 8 presents the results of whole shoe tests using outsoles comprising thermoformed textiles as described herein, obtained in accordance with the Whole Footwear Coefficient of Friction Test and the Whole Footwear Abrasion Test disclosed herein. Table 9 shows hardness and Akron abrasion loss results for thermoformed textiles described herein when used as outsoles, as obtained using the Durometer Hardness Test and the Akron Abrasion Test as disclosed herein.
  • thermoformed knit textiles were tested for abrasion mass loss and traction using the Akron Abrasion Test and the Sample Coefficient of Friciton Test as described herein. Traction properties of the thermoformed knit textiles were comparable to polymer test plaques and to rubber outsole materials, indicating that the thermoformed knit textiles were successfully thermoformed to form thermoformed networks (Table 9). Additionally, Akron abrasion material losses measured for the thermoformed knit textiles were comparable to the rubber control references. Mass loss measured for Akron abrasion test strips 0.5 inches wide and 8 inches long were comparable to much larger outsole areas of whole shoe mass as described in Table 8. Thus, test strips and whole shoe performance are consistent and thermoformed knit textiles were shown to be acceptable as outsole materials as they did not lose material out of scale with representative rubbers and further, the thermoformed knit textiles exhibited sufficient traction properties to perform as outsoles.
  • the first swatch used UNIFI polyethylene terephthalate (polyester) yarn (158 denier, tenacity of 7.131 grams per denier, 23.42 percent elongation) as the core yarn, and was coated with a polymeric composition consisting essentially of Estane 58238 at a thickness of about 0.4 millimeters.
  • the second swatch used the same UNIFI polyethylene terephthalate yarn core yarn, but was coated with a polymeric composition consisting essentially of Monprene TPE SP66070 at a thickness of about 0.4 millimeters.
  • the flat knit textile swatches were thermoformed either without texture or with a herringbone texture prior to testing.
  • the edge-2 knit structure is a double-bed knit structure with tuck knit stitches connecting the two faces of the knit textile.
  • One face of the textile is exclusively uncoated polyester yarn and the other is exclusively the coated yarn under evaluation, with the tuck stitches connecting the two exterior facing knit surfaces.
  • Tuck stitches are constructed from the same coated yarns as the outer face yarn.
  • thermoformed textiles knitted from the coated yarn with a coating consisting essentially of the SEBS-based Monprene demonstrated a high dynamic coefficient of friction on concrete and court (Table 10).
  • the thermoformed textiles including the Monprene coated yarn demonstrated higher coefficients of friction when thermoformed flat on smooth concrete and court.
  • the thermoformed textiles including the Monprene coated yarn demonstrated good coefficients of friction when tested dry and when wet.
  • thermoformed textiles knitted from the coated yarn with a coating consisting essentially of the Estane demonstrated higher coefficients of friction when thermoformed flat and tested on smooth concrete and court; the herringbone texture demonstrated a greater coefficient of friction when tested on rough concrete. (Table 10).
  • the thermoformed textiles including the Estane coated yarn demonstrated a good coefficient of friction when tested dry and wet (with some exceptions).
  • thermoformed 1 ⁇ 2 knit textiles exhibited less volumetric loss on abrasion testing than the thermoformed 1 ⁇ 1 knit textiles.
  • the thermoformed textiles including the Estane coated yarn exhibited less volumetric loss than the thermoformed textiles including the Monprene coated yarn.
  • Coated and uncoated yarns were knit into edge-2 1 ⁇ 2 or 1 ⁇ 1 swatches and lightly pressed in a t-shirt press at 20 pounds per square inch and 150 degrees Celsius for 20 seconds to avoid fraying.
  • the swatches were cut into outsole shapes and placed into a rubber-phylon mold having the cavity size of a standard rubber mold but coated for heating and cooling cycles similar to a phylon mold.
  • the empty mold was preheated to the melting temperature of the polymer plus 15 degrees Celsius as measured by a thermocouple.
  • the cut outsole shapes were placed into the mold with uncoated polyester yarn side up and pressed for 45 seconds, then cooled for at least 60 seconds, or 90 seconds if time allowed.
  • edge-2 1 ⁇ 1 swatches were not large enough material to fill the mold.
  • silicone, rubber, or other material was added to fill the mold.
  • Tested temperatures, polymers present in the yarn coating, and times are provided in Table 12:
  • thermoforming process When a regular thermoforming process was used, this was conducted on a DMT Press with a total heating time of 35 to 45 seconds and a pressure of 30 bar. The process was stopped when the thermocouple reached 130 degrees Celsius or 150 degrees Celsius depending on the end point.
  • thermocouple When a flat molding process was used, this was conducted on a Kukdong heat press with a total heating time of from 30 seconds to 60 seconds or until the textile reached 150 degrees Celsius as measured by thermocouple. Temperature was held for 0 to 10 seconds as needed. The heating pressure was 0.1 megapascals and the heat press set point was 190 degrees Celsius. Heating was stopped when the thermocouple reached 150 degrees Celsius, with some samples receiving an additional dwell time of 10 seconds as indicated. Cold pressing at 20 degrees Celsius was then carried out at 0.1 megapascals for 30 seconds.
  • IR heating and/or thermoforming coated yarns were knitted into an exemplary upper and the upper was placed in a Flash Activator with the surface of the upper to be heated facing the heating elements.
  • the surface of a knit upper configured to be externally-facing was placed facing the heating elements, while in other experiments, the surface of the knit upper configured to be internally-facing was placed facing the heating elements.
  • the knit textile can be laid flat, heated, and then formed, or heated on a last in three dimensions and formed. The knit textile was exposed to IR flash heat for about 23 seconds, which was sufficient for the local temperature of the irradiated surface to reach 160 degrees Celsius or more.
  • the upper and last were then removed from the Flash Activator and temperature was measured with a heat gun while moving the upper to a vacuum machine in order to verify the temperature was greater than the melting point of the polymeric composition of the yarn coating.
  • the knit upper was then positioned on a vacuum stage so that the newly thermoformed surface of the textile of the upper contacted the desired template master pattern for forming.
  • a textured embossing pad (rubber, plastic, or silicone) was placed face down on the thermoformed surface of the upper such that the thermoformed surface is in contact with the silicone pad molding pattern.
  • the embossing pad can be at room temperature or heated to 120 to 200 degrees Celsius depending on the length of time needed to maintain a higher temperature on the molten polymeric composition of the coating.
  • the embossing pad and knit textile of the upper were pressed in a vacuum machine for 60 seconds. The vacuum was released and discharged to reveal the surface of the thermoformed network of the thermoformed knit textile.
  • abrasion mass losses for unthermoformed knit textiles and thermoformed knit textiles which were thermoformed in a flat configuration as determined after 300 and 3000 cycles of abrasion testing using the Akron Abrasion Test.
  • the knit textiles were knit using the UNIFI polyester core yarn described above coated with a polymeric composition comprising a thermoplastic styrene copolymer elastomer (Monprene 66070) or a thermoplastic polyurethane elastomer (Estane 58238).
  • the knit structure of the knit textile included either 1 end (1 ⁇ 1) or 2 ends (1 ⁇ 2) of the coated yarn and 1 end of the uncoated UNIFI polyester yarn knit on the surface of the knit textile which was tested.
  • the knit structures are those described above.
  • thermoformed knit textiles showed performance equal to or superior to conventional rubber, and showed similar performance regardless of whether 1 or 2 ends were used at the top knit surface.
  • Durability and weatherization were assessed as a function of knit structure and processing conditions using the Stoll Abrasion Test, Bally Flex Test, Wet Bally Flex Test, and Water Resistance Test as described herein.
  • a knit textile was produced using yarns coated with a polymeric composition comprising a thermoplastic elastomer (Estane T470A-3) (WC2 yarns), and thermoformed by heating in a press manufactured by Kukdong Machinery (Busan, Korea) under flat molding conditions to 150 degrees Celsius. For some samples, the textile was held in the press for an additional 10 seconds of dwell time after reaching the temperature of 150 degrees Celsius.
  • “Knit A” samples were knit samples having a knit structure in which, when thermoformed, 75-100 percent of the total surface area of the thermoformed network was defined by the re-flowed and re-solidified polymeric composition.
  • “Knit B” samples were knit samples having a knit structure in which, when thermoformed, 40-70 percent of the total surface area of the thermoformed network was defined by the re-flowed and re-solidified polymeric composition.
  • “Knit C” samples were knit samples having a knit structure in which, when thermoformed, 15-35 percent of the total surface area of the thermoformed network was defined by the re-flowed and re-solidified polymeric composition. Performance of the Wet Bally Flex Test and Water Resistance Test were performed on textile samples having at least 90 percent of their surface area covered by thermoformed network in order to minimize water transmission through the sample.
  • thermoformed textiles and uppers for articles of footwear including the thermoformed textiles were manufactured, where the region of the textile or upper tested included a thermoformed network comprising a polymeric as disclosed herein.
  • “Knit A”, “Knit B”, and “Knit C” are as described above.
  • coated yarns wherein the coating included a polymeric composition comprising a thermoplastic polyurethane elastomer (Estane T470A-3).
  • the coated yarn included a 0.4 millimeter coating of the polymeric composition on a 150-600 denier multifilament polyester yarn. Dry and wet coefficients of friction are presented in Table 15:
  • Thermoformed knit samples showed similar dry and wet coefficients of friction (e.g., boot-to-ball interaction) as the laminated Duragon skin. but in a streamlined, more integrated, lower waste manner of construction.
  • Kangaroo leather displays little change between wet COF and dry COF, but both wet and dry COF are low for this material overall.
  • DURAGON skin displays higher wet COF and dry COF but also a large difference between these two values.
  • Thermoformed textiles and/or footwear uppers containing the coated yarns disclosed herein exhibit higher wet and dry COF values overall, and a lower degree of difference between dry COF and wet COF than DURAGON skin.
  • thermoformed uppers knit with yarns coated with a thermoplastic composition comprising a thermoplastic polyurethane elastomer having a durometer of about 65 to 85 Shore A created higher levels of ball spin. as compared to thermoformed knit uppers knit using a yarn coated with a thermoplastic composition comprising a thermoplastic polyurethane elastomer having a durometer of about 90 Shore A, and commercially available uppers formed of DURAGON skin.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • General Health & Medical Sciences (AREA)
  • Physical Education & Sports Medicine (AREA)
  • Composite Materials (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Footwear And Its Accessory, Manufacturing Method And Apparatuses (AREA)
US16/945,441 2020-07-31 Textiles and articles and processes for making the same Active 2042-03-23 US11998080B2 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US16/945,441 US11998080B2 (en) 2020-07-31 Textiles and articles and processes for making the same

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201962882008P 2019-08-02 2019-08-02
US16/945,441 US11998080B2 (en) 2020-07-31 Textiles and articles and processes for making the same

Publications (3)

Publication Number Publication Date
US20210030109A1 US20210030109A1 (en) 2021-02-04
US20220007782A2 true US20220007782A2 (en) 2022-01-13
US11998080B2 US11998080B2 (en) 2024-06-04

Family

ID=

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI820958B (zh) * 2022-10-07 2023-11-01 峻典股份有限公司 自動化鞋墊素材模外加熱並同時有多組模具換料流程方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190116927A1 (en) * 2017-10-19 2019-04-25 Nike, Inc. Materials, methods of making, methods of use, and articles incorporating the materials

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190116927A1 (en) * 2017-10-19 2019-04-25 Nike, Inc. Materials, methods of making, methods of use, and articles incorporating the materials

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI820958B (zh) * 2022-10-07 2023-11-01 峻典股份有限公司 自動化鞋墊素材模外加熱並同時有多組模具換料流程方法

Also Published As

Publication number Publication date
EP3817613B1 (de) 2021-10-20
US20210030108A1 (en) 2021-02-04
CN114451633A (zh) 2022-05-10
CN114451628A (zh) 2022-05-10
CN114468459A (zh) 2022-05-13
EP3833208A1 (de) 2021-06-16
EP3793390B1 (de) 2021-07-21
WO2021026031A1 (en) 2021-02-11
CN114302986A (zh) 2022-04-08
WO2021026030A1 (en) 2021-02-11
US20230130760A1 (en) 2023-04-27
US20210030109A1 (en) 2021-02-04
EP4039118A1 (de) 2022-08-10
US11564443B2 (en) 2023-01-31
WO2021026032A1 (en) 2021-02-11
EP3939463A1 (de) 2022-01-19
WO2021026033A1 (en) 2021-02-11
CN114126442A (zh) 2022-03-01
EP4241601A2 (de) 2023-09-13
EP3793390A1 (de) 2021-03-24
CN114080169A (zh) 2022-02-22
EP3855969B1 (de) 2023-10-04
CN114302986B (zh) 2024-05-10
US20210030117A1 (en) 2021-02-04
US20210030115A1 (en) 2021-02-04
EP3855969A1 (de) 2021-08-04
CN114072022A (zh) 2022-02-18
EP3833208B1 (de) 2022-04-27
CN114304810A (zh) 2022-04-12
EP3817613A1 (de) 2021-05-12
EP4241601A3 (de) 2023-10-25

Similar Documents

Publication Publication Date Title
US11564443B2 (en) Textiles and articles and processes for making the same
CN113576109B (zh) 针织纺织品和鞋面及其制作方法
EP4007504B1 (de) Sohlenstrukturen mit verbundelementen und daraus hergestelltes schuhwerk
US20230087149A1 (en) Knitted components and articles for improved ball control and durability
US11998080B2 (en) Textiles and articles and processes for making the same
US20230129224A1 (en) Articles of footwear with knitted components and methods of manufacturing the same
TWI838655B (zh) 具有一第一表面及一相對的第二表面的針織部件、包括針織部件的鞋類製品及服飾製品、針織部件的製造方法、及鞋類鞋面的針織製品
KR20240044534A (ko) 편직 구성요소를 포함한 신발류 물품 및 그 제조 방법
CN117957345A (zh) 具有针织部件的鞋类制品及其制造方法
TW202404493A (zh) 具有針織部件的鞋類製品及其製造方法

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

AS Assignment

Owner name: NIKE, INC., OREGON

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FRAZIER, DEVON;HANCOCK, WALTER M.;KLINGER, DAVE;AND OTHERS;SIGNING DATES FROM 20210226 TO 20210312;REEL/FRAME:058171/0444

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: AWAITING TC RESP., ISSUE FEE NOT PAID

ZAAB Notice of allowance mailed

Free format text: ORIGINAL CODE: MN/=.

STPP Information on status: patent application and granting procedure in general

Free format text: NOTICE OF ALLOWANCE MAILED -- APPLICATION RECEIVED IN OFFICE OF PUBLICATIONS

STPP Information on status: patent application and granting procedure in general

Free format text: AWAITING TC RESP., ISSUE FEE NOT PAID

STPP Information on status: patent application and granting procedure in general

Free format text: NOTICE OF ALLOWANCE MAILED -- APPLICATION RECEIVED IN OFFICE OF PUBLICATIONS

STPP Information on status: patent application and granting procedure in general

Free format text: AWAITING TC RESP, ISSUE FEE PAYMENT RECEIVED

STPP Information on status: patent application and granting procedure in general

Free format text: AWAITING TC RESP, ISSUE FEE PAYMENT VERIFIED

STPP Information on status: patent application and granting procedure in general

Free format text: PUBLICATIONS -- ISSUE FEE PAYMENT VERIFIED

STCF Information on status: patent grant

Free format text: PATENTED CASE