US20190030596A1 - Mold Assemblies Used for Fabricating Downhole Tools - Google Patents
Mold Assemblies Used for Fabricating Downhole Tools Download PDFInfo
- Publication number
- US20190030596A1 US20190030596A1 US16/148,844 US201816148844A US2019030596A1 US 20190030596 A1 US20190030596 A1 US 20190030596A1 US 201816148844 A US201816148844 A US 201816148844A US 2019030596 A1 US2019030596 A1 US 2019030596A1
- Authority
- US
- United States
- Prior art keywords
- mold assembly
- cavity
- funnel
- thermal
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- A variety of downhole tools are commonly used in the exploration and production of hydrocarbons. Examples of such downhole tools include cutting tools, such as drill bits, reamers, stabilizers, and coring bits; drilling tools, such as rotary steerable devices and mud motors; and other downhole tools, such as window mills, packers, tool joints, and other wear-prone tools. Rotary drill bits are often used to drill wellbores. One type of rotary drill bit is a fixed-cutter drill bit that has a bit body comprising matrix and reinforcement materials, i.e., a “matrix drill bit” as referred to herein. Matrix drill bits usually include cutting elements or inserts positioned at selected locations on the exterior of the matrix bit body. Fluid flow passageways are formed within the matrix bit body to allow communication of drilling fluids from associated surface drilling equipment through a drill string or drill pipe attached to the matrix bit body.
- Matrix drill bits are typically manufactured by placing powder material into a mold and infiltrating the powder material with a binder material, such as a metallic alloy. The various features of the resulting matrix drill bit, such as blades, cutter pockets, and/or fluid-flow passageways, may be provided by shaping the mold cavity and/or by positioning temporary displacement materials within interior portions of the mold cavity. A preformed bit blank (or steel mandrel) may be placed within the mold cavity to provide reinforcement for the matrix bit body and to allow attachment of the resulting matrix drill bit with a drill string. A quantity of matrix reinforcement material (typically in powder form) may then be placed within the mold cavity with a quantity of the binder material.
- The mold is then placed within a furnace and the temperature of the mold is increased to a desired temperature to allow the binder (e.g., metallic alloy) to liquefy and infiltrate the matrix reinforcement material. The furnace typically maintains this desired temperature to the point that the infiltration process is deemed complete, such as when a specific location in the bit reaches a certain temperature. Once the designated process time or temperature has been reached, the mold containing the infiltrated matrix bit is removed from the furnace. As the mold is removed from the furnace, the mold begins to rapidly lose heat to its surrounding environment via heat transfer, such as radiation and/or convection in all directions.
- This heat loss continues to a large extent until the mold is moved and placed on a cooling plate and an insulation enclosure or “hot hat” is lowered around the mold. The insulation enclosure drastically reduces the rate of heat loss from the top and sides of the mold while heat is drawn from the bottom of the mold through the cooling plate. This controlled cooling of the mold and the infiltrated matrix bit contained therein can facilitate axial solidification dominating radial solidification, which is loosely termed directional solidification.
- As the molten material of the infiltrated matrix bit cools, there is a tendency for shrinkage that could result in voids forming within the bit body unless the molten material is able to continuously backfill such voids. In some cases, for instance, one or more intermediate regions within the bit body may solidify prior to adjacent regions and thereby stop the flow of molten material to locations where shrinkage porosity is developing. For instance, cooling can create stresses at the interface between the metal blank and the molten material. These stresses can cause cracking as the molten material begins to solidify. In other cases, shrinkage porosity may result in poor metallurgical bonding at the interface between the bit blank and the molten materials, which can also result in the formation of cracks within the bit body that can be difficult or impossible to inspect. When such bonding defects are present and/or detected, the drill bit is often scrapped during or following manufacturing assuming they cannot be remedied. Every effort is made to detect these defects and reject any defective drill bit components during manufacturing to help ensure that the drill bits used in a job at a well site will not prematurely fail and to minimize any risk of possible damage to the well.
- The following figures are included to illustrate certain aspects of the present disclosure, and should not be viewed as exclusive embodiments. The subject matter disclosed is capable of considerable modifications, alterations, combinations, and equivalents in form and function, without departing from the scope of this disclosure.
-
FIG. 1 is a perspective view of an exemplary fixed-cutter drill bit that may be fabricated in accordance with the principles of the present disclosure. -
FIG. 2 is a cross-sectional view of the drill bit ofFIG. 1 . -
FIG. 3 is a cross-sectional side view of an exemplary mold assembly for use in forming the drill bit ofFIG. 1 . -
FIGS. 4A-4C are progressive schematic diagrams of an exemplary method of fabricating a drill bit. -
FIGS. 5A-5D are partial cross-sectional side views of various funnels that may be used in the mold assembly ofFIG. 3 . -
FIGS. 6A and 6B are partial cross-sectional side views of other exemplary funnels that may be used in the mold assembly ofFIG. 3 . -
FIGS. 7A-7D are partial cross-sectional side views of other exemplary funnels that may be used in the mold assembly ofFIG. 3 . -
FIGS. 8A-8E are partial cross-sectional side views of other exemplary funnels that may be used in the mold assembly ofFIG. 3 . -
FIG. 9 depicts partial cross-sectional side views of an exemplary funnel taken at different angular locations shown in the center top view. -
FIG. 10 is a partial cross-sectional side view of another exemplary funnel that may be used in the mold assembly ofFIG. 3 . -
FIG. 11 is a cross-sectional side view of another exemplary mold assembly. - The present disclosure relates to tool manufacturing and, more particularly, to mold configurations for downhole tools that help control the thermal profile of the downhole tools during manufacture.
- The embodiments described herein improve directional solidification of infiltrated downhole tools by introducing alternative designs to standard mold assembly components used during the infiltration process to thereby achieve a desired thermal profile. According to the present disclosure, the mold assembly may include at least a mold that forms a bottom of the mold assembly, and a funnel that is operatively coupled to the mold. The funnel has an inner wall, an outer wall, and a cavity defined between the inner and outer walls. In some embodiments, a thermal material may be positioned within the cavity to help influence the overall thermal profile of the mold assembly and facilitate directional cooling of the molten contents within the mold assembly. Depending on the material selected, the thermal material can serve as an insulator, a heat sink, or a thermal energy source in controlling the cooling process of the infiltrated downhole tool. Among other things, this may improve quality and reduce the rejection rate of drill bit components due to defects during manufacturing.
-
FIG. 1 illustrates a perspective view of an example fixed-cutter drill bit 100 that may be fabricated in accordance with the principles of the present disclosure. It should be noted that, whileFIG. 1 depicts a fixed-cutter drill bit 100, the principles of the present disclosure are equally applicable to any type of downhole tool that may be formed or otherwise manufactured through an infiltration process. For example, suitable infiltrated downhole tools that may be manufactured in accordance with the present disclosure include, but are not limited to, oilfield drill bits or cutting tools (e.g., fixed-angle drill bits, roller-cone drill bits, coring drill bits, bi-center drill bits, impregnated drill bits, reamers, stabilizers, hole openers, cutters, cutting elements), non-retrievable drilling components, aluminum drill bit bodies associated with casing drilling of wellbores, drill-string stabilizers, cones for roller-cone drill bits, models for forging dies used to fabricate support arms for roller-cone drill bits, arms for fixed reamers, arms for expandable reamers, internal components associated with expandable reamers, sleeves attached to an uphole end of a rotary drill bit, rotary steering tools, logging-while-drilling tools, measurement-while-drilling tools, side-wall coring tools, fishing spears, washover tools, rotors, stators and/or housings for downhole drilling motors, blades and housings for downhole turbines, and other downhole tools having complex configurations and/or asymmetric geometries associated with forming a wellbore. - As illustrated in
FIG. 1 , the fixed-cutter drill bit 100 (hereafter “thedrill bit 100”) may include or otherwise define a plurality ofcutter blades 102 arranged along the circumference of abit head 104. Thebit head 104 is connected to ashank 106 to form abit body 108. Theshank 106 may be connected to thebit head 104 by welding, such as using laser arc welding that results in the formation of aweld 110 around aweld groove 112. Theshank 106 may further include or otherwise be connected to a threadedpin 114, such as an American Petroleum Institute (API) drill pipe thread. - In the depicted example, the
drill bit 100 includes fivecutter blades 102, in which multiple recesses orpockets 116 are formed.Cutting elements 118 may be fixedly installed within eachrecess 116. This can be done, for example, by brazing eachcutting element 118 into acorresponding recess 116. As thedrill bit 100 is rotated in use, thecutting elements 118 engage the rock and underlying earthen materials, to dig, scrape or grind away the material of the formation being penetrated. - During drilling operations, drilling fluid or “mud” can be pumped downhole through a drill string (not shown) coupled to the
drill bit 100 at the threadedpin 114. The drilling fluid circulates through and out of thedrill bit 100 at one ormore nozzles 120 positioned innozzle openings 122 defined in thebit head 104.Junk slots 124 are formed between each adjacent pair ofcutter blades 102. Cuttings, downhole debris, formation fluids, drilling fluid, etc., may pass through thejunk slots 124 and circulate back to the well surface within an annulus formed between exterior portions of the drill string and the inner wall of the wellbore being drilled. -
FIG. 2 is a cross-sectional side view of thedrill bit 100 ofFIG. 1 . Similar numerals fromFIG. 1 that are used inFIG. 2 refer to similar components that are not described again. As illustrated, theshank 106 may be securely attached to a metal blank (or mandrel) 202 at theweld 110 and themetal blank 202 extends into thebit body 108. Theshank 106 and themetal blank 202 are generally cylindrical structures that define correspondingfluid cavities fluid cavity 204 b of themetal blank 202 may further extend longitudinally into thebit body 108. At least one flow passageway (shown as twoflow passageways fluid cavity 204 b to exterior portions of thebit body 108. Thenozzle openings 122 may be defined at the ends of theflow passageways bit body 108. Thepockets 116 are formed in thebit body 108 and are shaped or otherwise configured to receive the cutting elements 118 (FIG. 1 ). -
FIG. 3 is a cross-sectional side view of amold assembly 300 that may be used to form thedrill bit 100 ofFIGS. 1 and 2 . While themold assembly 300 is shown and discussed as being used to help fabricate thedrill bit 100, those skilled in the art will readily appreciate thatmold assembly 300 and its several variations described herein may be used to help fabricate any of the infiltrated downhole tools mentioned above, without departing from the scope of the disclosure. As illustrated, themold assembly 300 may include several components such as amold 302, agauge ring 304, and afunnel 306. In some embodiments, thefunnel 306 may be operatively coupled to themold 302 via thegauge ring 304, such as by corresponding threaded engagements, as illustrated. In other embodiments, thegauge ring 304 may be omitted from themold assembly 300 and thefunnel 306 may instead be operatively coupled directly to themold 302, such as via a corresponding threaded engagement, without departing from the scope of the disclosure. - In some embodiments, as illustrated, the
mold assembly 300 may further include abinder bowl 308 and acap 310 placed above thefunnel 306. Themold 302, thegauge ring 304, thefunnel 306, thebinder bowl 308, and thecap 310 may each be made of or otherwise comprise graphite or alumina (Al2O3), for example, or other suitable materials. Aninfiltration chamber 312 may be defined or otherwise provided within themold assembly 300. Various techniques may be used to manufacture themold assembly 300 and its components including, but not limited to, machining graphite blanks to produce the various components and thereby define theinfiltration chamber 312 to exhibit a negative or reverse profile of desired exterior features of the drill bit 100 (FIGS. 1 and 2 ). - Materials, such as consolidated sand or graphite, may be positioned within the
mold assembly 300 at desired locations to form various features of the drill bit 100 (FIGS. 1 and 2 ). For example,consolidated sand legs flow passageways 206 a,b (FIG. 2 ) and their respective nozzle openings 122 (FIGS. 1 and 2 ). Moreover, a cylindrically-shapedconsolidated sand core 316 may be placed on thelegs 314 a,b. The number oflegs 314 a,b extending from thesand core 316 will depend upon the desired number of flow passageways andcorresponding nozzle openings 122 in thedrill bit 100. - After the desired materials, including the
sand core 316 and thelegs 314 a,b, have been installed within themold assembly 300,matrix reinforcement materials 318 may then be placed within or otherwise introduced into themold assembly 300. For some applications, two or more different types ofmatrix reinforcement materials 318 may be deposited in themold assembly 300. Suitablematrix reinforcement materials 318 include, but are not limited to, tungsten carbide, monotungsten carbide (WC), ditungsten carbide (W2C), macrocrystalline tungsten carbide, other metal carbides, metal borides, metal oxides, metal nitrides, natural and synthetic diamond, and polycrystalline diamond (PCD). Examples of other metal carbides may include, but are not limited to, titanium carbide and tantalum carbide, and various mixtures of such materials may also be used. - The
metal blank 202 may be supported at least partially by thematrix reinforcement materials 318 within theinfiltration chamber 312. More particularly, after a sufficient volume of thematrix reinforcement materials 318 has been added to themold assembly 300, themetal blank 202 may then be placed withinmold assembly 300. Themetal blank 202 may include an inside diameter 320 that is greater than anoutside diameter 322 of thesand core 316, and various fixtures (not expressly shown) may be used to position themetal blank 202 within themold assembly 300 at a desired location. Thematrix reinforcement materials 318 may then be filled to a desired level within theinfiltration chamber 312. -
Binder material 324 may then be placed on top of thematrix reinforcement materials 318, themetal blank 202, and thecore 316. Various types ofbinder materials 324 may be used and include, but are not limited to, metallic alloys of copper (Cu), nickel (Ni), manganese (Mn), lead (Pb), zinc (Zn), tin (Sn), cobalt (Co) and silver (Ag). Phosphorous (P) may sometimes also be added in small quantities to reduce the melting temperature range of infiltration materials positioned in themold assembly 300. Various mixtures of such metallic alloys may also be used as thebinder material 324. In some embodiments, thebinder material 324 may be covered with a flux layer (not expressly shown). The amount ofbinder material 324 and optional flux material added to theinfiltration chamber 312 should be at least enough to infiltrate thematrix reinforcement materials 318 during the infiltration process. In some instances, some or all of thebinder material 324 may be placed in thebinder bowl 308, which may be used to distribute thebinder material 324 into theinfiltration chamber 312 viavarious conduits 326 that extend therethrough. The cap 310 (if used) may then be placed over themold assembly 300, thereby readying themold assembly 300 for heating. - Referring now to
FIGS. 4A-4C , with continued reference toFIG. 3 , illustrated are schematic diagrams that sequentially illustrate an example method of heating and cooling themold assembly 300 ofFIG. 3 , in accordance with the principles of the present disclosure. InFIG. 4A , themold assembly 300 is depicted as being positioned within afurnace 402. The temperature of themold assembly 300 and its contents are elevated within thefurnace 402 until thebinder material 324 liquefies and is able to infiltrate thematrix reinforcement materials 318. Once a specific location in themold assembly 300 reaches a certain temperature in thefurnace 402, or themold assembly 300 is otherwise maintained at a particular temperature for a predetermined amount of time, themold assembly 300 is then removed from thefurnace 402 and immediately begins to lose heat by radiating thermal energy to its surroundings while heat is also convected away by cooler air outside thefurnace 402. In some cases, as depicted inFIG. 4B , themold assembly 300 may be transported to and set down upon athermal heat sink 404. - The radiative and convective heat losses from the
mold assembly 300 to the environment continue until aninsulation enclosure 406 is lowered around themold assembly 300. Theinsulation enclosure 406 may be a rigid shell or structure used to insulate themold assembly 300 and thereby slow the cooling process. In some cases, theinsulation enclosure 406 may include ahook 408 attached to a top surface thereof. Thehook 408 may provide an attachment location, such as for a lifting member, whereby theinsulation enclosure 406 may be grasped and/or otherwise attached to for transport. For instance, a chain orwire 410 may be coupled to thehook 408 to lift and move theinsulation enclosure 406, as illustrated. In other cases, a mandrel or other type of manipulator (not shown) may grasp onto thehook 408 to move theinsulation enclosure 406 to a desired location. - The
insulation enclosure 406 may include anouter frame 412, aninner frame 414, andinsulation material 416 arranged between the outer andinner frames outer frame 412 and theinner frame 414 may be made of rolled steel and shaped (i.e., bent, welded, etc.) into the general shape, design, and/or configuration of theinsulation enclosure 406. In other embodiments, theinner frame 414 may be a metal wire mesh that holds theinsulation material 416 between theouter frame 412 and theinner frame 414. Theinsulation material 416 may be selected from a variety of insulative materials, such as those discussed below. In at least one embodiment, theinsulation material 416 may be a ceramic fiber blanket, such as INSWOOL® or the like. - As depicted in
FIG. 4C , theinsulation enclosure 406 may enclose themold assembly 300 such that thermal energy radiating from themold assembly 300 is dramatically reduced from the top and sides of themold assembly 300 and is instead directed substantially downward and otherwise toward/into thethermal heat sink 404 or back towards themold assembly 300. In the illustrated embodiment, thethermal heat sink 404 is a cooling plate designed to circulate a fluid (e.g., water) at a reduced temperature relative to the mold assembly 300 (i.e., at or near ambient) to draw thermal energy from themold assembly 300 and into the circulating fluid, and thereby reduce the temperature of themold assembly 300. In other embodiments, however, thethermal heat sink 404 may be any type of cooling device or heat exchanger configured to encourage heat transfer from thebottom 418 of themold assembly 300 to thethermal heat sink 404. In yet other embodiments, thethermal heat sink 404 may be any stable or rigid surface that may support themold assembly 300, and preferably having a high thermal capacity, such as a concrete slab or flooring. - Once the
insulation enclosure 406 is positioned over themold assembly 300 and thethermal heat sink 404 is operational, the majority of the thermal energy is transferred away from themold assembly 300 through thebottom 418 of themold assembly 300 and into thethermal heat sink 404. This controlled cooling of themold assembly 300 and its contents allows an operator to regulate or control the thermal profile of themold assembly 300 to a certain extent and may result in directional solidification of the molten contents within themold assembly 300, where axial solidification of the molten contents dominates radial solidification. Within themold assembly 300, the face of the drill bit (i.e., the end of the drill bit that includes the cutters) may be positioned at the bottom 418 of themold assembly 300 and otherwise adjacent thethermal heat sink 404 while the shank 106 (FIG. 1 ) may be positioned adjacent the top of themold assembly 300. As a result, the drill bit 100 (FIGS. 1 and 2 ) may be cooled axially upward, from the cutters 118 (FIG. 1 ) toward the shank 106 (FIG. 1 ). - Such directional solidification (from the bottom up) may prove advantageous in reducing the occurrence of voids due to shrinkage porosity, cracks at the interface between the bit blank and the molten materials, and nozzle cracks. However, the insulating capability of the
insulation enclosure 406 may require augmentation to produce a sufficient amount of directional cooling. According to embodiments of the present disclosure, as an alternative or in addition to using theinsulation enclosure 406, the mold assembly 300 (FIG. 3 ) may be modified to help influence the overall thermal profile of the infiltrated downhole tool (e.g., thedrill bit 100 ofFIGS. 1 and 2 ) and facilitate a sufficient amount of directional cooling. More particularly, embodiments of the present disclosure provide a hybrid design for themold assembly 300 that is capable of passively producing or improving directional solidification in an infiltrated downhole tool. As described in more detail below, the hybrid configurations may be applied to one or all of the components of themold assembly 300, including themold 302, thegauge ring 304, thefunnel 306, thebinder bowl 308, and thecap 310, or any other component related thereto. - Referring now to
FIGS. 5A-5D , illustrated are partial cross-sectional side views of various funnels that may be used in an exemplary mold assembly, according to one or more embodiments. More particularly,FIGS. 5A-5D depict cross-sectional views of a portion offunnels funnel 306 ofFIG. 3 and may optionally replace thefunnel 306 in themold assembly 300 ofFIG. 3 . For simplicity,FIGS. 5A-5D depict cross-sectional views of only the right side of the funnels 500 a-d while omitting the left side. It will be appreciated, however, that each funnel 500 a-d provides a full 360° structure. - As illustrated, each funnel 500 a-500 d may include an
inner wall 502, anouter wall 504, and acavity 506 defined between the inner andouter walls inner wall 502 may help form a portion of the infiltration chamber 312 (FIG. 3 ) and otherwise face the internal components and materials of the mold assembly 300 (FIG. 3 ). Theouter wall 504, on the other hand, may form a part of the outer periphery of themold assembly 300. - In some embodiments, the inner and
outer walls cavity 506 therebetween. In such embodiments, thecavity 506 may be formed by known manufacturing techniques, such as milling or turning. As an alternate example, the funnels 500 a-d (or any of the funnels described herein) can be produced as a multi-material or hollow funnel in a multi-step process. In the first step, for instance, a blank may be formed that exhibits the shape and geometry of thecavity 506. A suitable material may be used to form the blank to either facilitate subsequent processing, such as graphite, or to provide certain thermal characteristics to promote directional solidification in the completed funnel, such as a foamed material, an insulating ceramic, a metallic shell, a conductive metallic solid, or a material that will undergo a phase change during the heating process. This blank may then be used for subsequent forming of the funnel 500 a-d, such as by sintering or casting a ceramic or metallic material around the blank. After forming the funnel 500 a-d, the blank material in thecavity 506 can either be removed via a suitable method (e.g., chemical etching, abrasive spray, machining out) to produce a hollow funnel or the blank material of thecavity 506 can be integrated as part of the final funnel and thereby provide key thermal properties. - In other embodiments, however, one or more of the funnels 500 a-d may comprise a multi-component construction. In such embodiments, for instance, the
inner wall 502 may be coupled to the outer wall 504 (or vice versa), such as via one or more threaded engagements 508 (FIG. 5A ) or the like. As will be appreciated, a multi-component construction for the funnel 500 a-d may prove advantageous in being able to more easily fabricate thecavity 506 to desired dimensions and/or geometries. More particularly, theinner wall 502 may be threaded to the outer wall 504 (e.g., at the threadedengagement 508 ofFIG. 5A ) and their combined geometry may serve to define thecavity 506. It should be noted that, while the threadedengagement 508 is depicted inFIG. 5A at a particular location on thefirst funnel 500 a, suitable threadedengagements 508 may be located at any portion of the funnels 500 a-d, without departing from the scope of the disclosure. Moreover, while not specifically depicted herein, it is contemplated to have more than one threadedengagement 508 between the inner andouter walls - The
cavity 506 may be filled at least partially with athermal material 510. In some embodiments, thethermal material 510 may be configured to provide insulation or insulative properties to the given funnel 500 a-d. In such embodiments, thethermal material 510 may prevent and otherwise retard heat transfer through the inner andouter walls thermal material 510 may provide or otherwise serve as a heat sink. In such embodiments, thethermal material 510 may comprise one or more materials configured to draw thermal energy from within the mold assembly 300 (FIG. 3 ), and thereby accelerate the cooling process of the components within themold assembly 300. - Suitable materials for the
thermal material 510 include, but are not limited to, ceramics (e.g., oxides, carbides, borides, nitrides, and silicides that may be crystalline, non-crystalline, or semi-crystalline), ceramic-fiber blankets, polymers, metals, insulating metal composites, carbon, nanocomposites, foams, fluids (e.g., air), any composite thereof, or any combination thereof. Thethermal material 510 may further include, but is not limited to, materials in the form of beads, cubes, pellets, particulates, powders, flakes, fibers, wools, woven fabrics, bulked fabrics, sheets, bricks, stones, blocks, cast shapes, molded shapes, sprayed insulation, and the like, any hybrid thereof, or any combination thereof. Accordingly, examples of suitable materials that may be used as thethermal material 510 may include, but are not limited to, ceramics, ceramic fibers, ceramic fabrics, ceramic wools, ceramic beads, ceramic blocks, ceramic powders, moldable ceramics, woven ceramics, cast ceramics, fire bricks, carbon fibers, graphite blocks, shaped graphite blocks, polymer beads, polymer fibers, polymer fabrics, nanocomposites, fluids in a jacket, metals, metal powders, intermetallic powders, metal fabrics, metal foams, metal wools, metal castings, glasses, glass beads, and the like, any composite thereof, or any combination thereof. - According to embodiments of the present disclosure, the geometry and/or configuration of the funnels 500 a-d may vary to provide varying thermal resistance or thermal properties along a height A (
FIG. 5A ) of the given funnel 500 a-d. For instance, the size, the thickness, and/or the geometry of the inner andouter walls FIG. 3 ). - In
FIG. 5A , for example, thefunnel 500 a is substantially the same size as thefunnel 306 ofFIG. 3 , but with thecavity 506 defined therein. InFIG. 5B , however, the thickness of theinner wall 502 of thefunnel 500 b may be enlarged and extended outward (radially) to provide a substantially uniform-sized cavity 506 along the height A (FIG. 5A ), which could facilitate machining of a one-piece funnel. InFIG. 5C , the size, the thickness, and/or the geometry of the inner andouter walls cavity 506. In such an embodiment, the thickness of the inner andouter walls outer walls - In
FIG. 5D , the geometry of thefunnel 500 d is altered to provide an outward and upward taper that progressively enlarges the size of thecavity 506 from the bottom 507 a of thefunnel 500 d to the top 507 b of thefunnel 500 d. More particularly, theouter wall 504 of thefunnel 500 d may be angled outward with respect to the longitudinal axis of the mold assembly 300 (FIG. 3 ) and otherwise with respect to theinner wall 502. In embodiments where thethermal material 510 comprises an insulating material, thefunnel 500 d may therefore exhibit increased thermal resistance towards the top 507 b of thefunnel 500 d. As a result, thefunnel 500 d allows an operator to vary the thermal resistance in the longitudinal direction B. - In some embodiments, as illustrated in
FIG. 5D , thecavity 506 may be sealed or capped, such as through the use of abinder bowl 511. Thebinder bowl 511 may be similar in some respects to thebinder bowl 308 ofFIG. 3 , but may exhibit thicker sidewalls as compared to thebinder bowl 308. In the illustrated embodiment, thebinder bowl 511 may be threaded to thefunnel 500 d to close off or seal the top of thecavity 506. In other embodiments, thecavity 506 may be sealed or capped with aplug 509 positioned within thecavity 506 at or near the top 507 b. As will be appreciated, thebinder bowl 308 and/or theplug 509 may be used to seal or cap any of the funnels 500 a-d, without departing from the scope of the disclosure. Such embodiments may prove useful where thethermal material 510 in thecavity 506 is a gas that acts as an insulator for the mold assembly 300 (FIG. 3 ). Suitable gases that may be sealed within thecavity 506 include, but are not limited to, air, argon, neon, helium, krypton, xenon, oxygen, carbon dioxide, methane, nitric oxide, nitrogen, nitrous oxide, or any combination thereof. - In at least one embodiment, the
cavity 506 may contain a connection to an exterior reservoir that provides heated gas to thecavity 506 to serve as a thermal energy reservoir. In this manner, a heated gas may be used to fill thecavity 506 once, or a heated gas may continuously cycle through thecavity 506 to provide a suitable thermal reservoir. In other embodiments, the gas may be omitted from thecavity 506 and a vacuum may alternatively be formed within thecavity 506 to act as an insulator. In some embodiments, thethermal material 510 may be positioned within a container (not shown) that may be filled with a gas or otherwise evacuated (i.e., a vacuum) and positioned in thecavity 506 to act as the insulator. - In some embodiments, in addition to the
thermal materials 510 mentioned above or independent thereof, a reflective coating 512 (FIG. 5B ) may be applied to a surface of one or both of the inner andouter walls reflective coating 512 is shown as being applied to the inner surface (i.e., within the cavity 506) of theouter wall 504, it will be appreciated that thereflective coating 512 may alternatively (or in addition thereto) be applied to the inner surface (i.e., within the cavity 506) of theinner wall 502. Moreover, thereflective coating 512 may be applied to any surface of the inner andouter walls - The
reflective coating 512 may be adhered to and/or sprayed onto surfaces of the inner andouter walls FIG. 3 ) back toward the molten contents. Suitable materials for thereflective coating 512 include a metal coating selected from group consisting of iron, chromium, copper, carbon steel, maraging steel, stainless steel, microalloyed steel, low alloy steel, molybdenum, nickel, platinum, silver, gold, tantalum, tungsten, titanium, aluminum, cobalt, rhenium, osmium, palladium, iridium, rhodium, ruthenium, manganese, niobium, vanadium, zirconium, hafnium, any derivative thereof, or any alloy based on these metals. A metal reflective coating may be applied via a suitable method, such as plating, spray deposition, chemical vapor deposition, plasma vapor deposition, etc. Alternatively, the coating material may be formed on a removable or thin substrate or as a thin member separately from thefunnel 500 b and then placed inside thefunnel 500 b to facilitate its formation. Another suitable material for thereflective coating 512 may be a paint (e.g., white for high reflectivity, black for high absorptivity), ceramic, or a metal oxide. In other embodiments, or in addition thereto, the inner surface of one or more of the inner andouter walls - In some embodiments, in addition to the
thermal materials 510 mentioned above or independent thereof, a thermal barrier 514 (FIG. 5C ) may be applied to a surface of one or both of the inner andouter walls thermal barrier 514 is shown as being applied to the inner surface (i.e., within the cavity 506) of theouter wall 504 inFIG. 5C , it will be appreciated that thethermal barrier 514 may alternatively (or in addition thereto) be applied to the inner surface (i.e., within the cavity 506) of theinner wall 502. Moreover, thethermal barrier 514 may be applied to any surface of the inner andouter walls FIG. 5B ), thethermal barrier 514 can be formed independent of thefunnel 500 c and then be placed inside thefunnel 500 c for use. - The
thermal barrier 514 may provide resistance to radiation heat transfer between thethermal material 510 and the exterior of the funnels 500 a-d. Suitable materials that may be used as thethermal barrier 514 include, but are not limited to, aluminum oxide, aluminum nitride, silicon carbide, silicon nitride, quartz, titanium carbide, titanium nitride, yttria-stabilized zirconia, borides, carbides, nitrides, and oxides. Thethermal barrier 514 may be applied to surfaces of the inner andouter walls thermal barrier 514 may advantageously lower the radiosity (e.g., radiant heat flux) and/or lower the heat transfer through to the funnels 500 a-d, thereby helping maintain heat within the mold assembly 300 (FIG. 3 ) and otherwise promote its ability to redirect thermal energy back at the molten contents within themold assembly 300. - Referring now to
FIGS. 6A and 6B , illustrated are partial cross-sectional side views ofexemplary funnels FIGS. 5A-5D , thefunnels 600 a,b may each be similar in some respects to thefunnel 306 ofFIG. 3 and, therefore, may replace thefunnel 306 in themold assembly 300 ofFIG. 3 . Moreover, similar to the funnels 500 a-d ofFIGS. 5A-5D , thefunnels 600 a,b may include the inner andouter wall cavity 506 defined therebetween. - The
funnels 600 a,b may comprise a two-piece construction, where the inner andouter walls inner wall 502 may also provide or include afooting 606 that extends substantially horizontal from theinner wall 502. The footing 602 may be configured to receive and support theouter wall 504. As will be appreciated, however, the footing 602 may equally extend horizontally from theouter wall 504 to support theinner wall 502, without departing from the scope of the disclosure. - In some embodiments, the inner and
outer walls outer walls outer wall 504 include, but are not limited to metals, insulating metal composites, nanocomposites, foams, a ceramic-fiber blanket, and any combination thereof since this material is not in direct contact with the matrix drill bit during the forming process. It will be appreciated that the same types of materials may be suitable for any component of themold assembly 300 ofFIG. 3 , including themold 302, thegauge ring 304, thebinder bowl 308, and thecap 310. - In other embodiments, however, the inner and
outer walls inner wall 502 may be made of graphite and theouter wall 504 may be made of alumina. In such a design, theouter wall 504 may serve as an insulating component since alumina exhibits a lower thermal conductivity than graphite. As will be appreciated, the inner andouter walls - The
cavity 506 may be characterized as a gap 602 that separates the inner andouter walls FIGS. 5A-5D ) listed above. In other embodiments, however, the gap 602 may be vacuous and otherwise left unfilled. In some embodiments, the gap 602 may provide aseparation distance 604 between the inner andouter walls separation distance 604 may be fairly small or miniscule in some embodiments, such as on the order of a few millimeters or less. In other embodiments, however, thedistance 604 may be greater than a few millimeters, without departing from the scope of the disclosure. In embodiments where the inner andouter walls separation distance 604 may prove especially advantageous in accommodating thermal expansion mismatches between the different materials. - Although not shown in
FIGS. 6A and 6B , in some embodiments, a cavity similar to thecavities 506 shown inFIGS. 5A-5D may be defined or otherwise provided within one or both of the inner andouter walls FIGS. 5A-5D ) disposed therein, as generally described above. - Referring now to
FIGS. 7A-7D , illustrated are partial cross-sectional side views of exemplary funnels 700 a-700 d, respectively, that may be used in an exemplary mold assembly, according to one or more embodiments. The funnels 700 a-d may be similar to the funnels 500 a-d ofFIGS. 5A-5D and, therefore, may be similar in some respects to thefunnel 306 ofFIG. 3 and otherwise replace thefunnel 306 in themold assembly 300 ofFIG. 3 . As illustrated, the funnels 700 a-d may include the inner andouter walls cavity 506 defined therebetween. - The
thermal material 510 disposed in the funnels 700 a-d may exhibit a high heat capacity such that thethermal material 510 is converted into and otherwise serves as a thermal mass or reservoir for the mold assembly 300 (FIG. 3 ). More particularly, whereasthermal materials 510, such as a ceramic powder, are able to provide a level of insulation for themold assembly 300,thermal materials 510, such as metals, are able to absorb thermal energy such that a thermal reservoir may be generated by thethermal materials 510 during the furnace cycle. As a result, the rate of cooling in the center regions of themold assembly 300 may be reduced axially. It will be appreciated, however, that the heat capacity and insulation properties of variousthermal materials 510 can also be employed simultaneously if benefit to the directional cooling can be obtained in such a fashion. Accordingly, in the illustrated embodiment, thethermal material 510 may be characterized as a thermal reservoir. - In some embodiments, as illustrated, the
thermal material 510 may comprise a metal, a salt, or a ceramic in the form of a plurality of cubes, pellets, particulates, flakes, and/or a powder. Generally, thethermal material 510 for the funnels 700 a-d may be any metal, salt, or ceramic that exhibits a suitable heat capacity, thermal conductivity, melting range (liquidus and solidus), and/or latent heat of fusion to provide the maximum amount of thermal resistance at, near, above, or below the liquidus and/or the solidus temperatures of thebinder material 324. Suitable metals for thethermal material 510 in the funnels 700 a-d may include a metal similar to thebinder material 324 ofFIG. 3 such as, but not limited to, copper, nickel, manganese, lead, tin, cobalt, silver, phosphorous, zinc, any alloys thereof, and any mixtures of the metallic alloys. Using athermal material 510 that is similar to thebinder material 324 may prove advantageous since they will each have the same solidus and liquidus temperatures. As a result, thethermal material 510 may be able to provide latent heat to the molten contents of the mold assembly 300 (FIG. 3 ) at essentially the same thermal points. In some embodiments, however, thethermal materials 510 may exhibit melting ranges that are sufficiently high so that they will not melt during the infiltration process and instead serve as a thermal reservoir during the cooling process. - Alternatively, a commercially pure metal may be used as a thermal reservoir if it has suitably high melting and boiling points in addition to a suitably low thermal diffusivity. Thermal diffusivity is equal to thermal conductivity divided by the product of density and specific heat. In essence, thermal diffusivity is a measure of the ability of a material to conduct heat versus its capability to retain heat. Silver, gold, and copper have very high thermal conductivities, especially in their pure (unalloyed) forms; correspondingly, they also have high thermal diffusivities (17.4, 12.8, and 11.7 m2/s, respectively). An ideal metal that could function as a suitable thermal reservoir, due to low thermal diffusivity (0.2 m2/s), while also possessing suitably high melting and boiling points, is manganese, which also has a low thermal conductivity (7.8 W/m*K). Additional suitable metals that may be used as the thermal material in the funnels 700 a-d include gadolinium, bismuth, terbium, dysprosium, cerium, samarium, scandium, erbium, and actinium (thermal diffusivity below 0.1 m2/s and thermal conductivity less than or equal to 16 W/m*K). Other suitable metals are also possible with adequately low thermal conductivities and diffusivities. Generally, suitable materials may have upper limits of thermal conductivity of 25 W/m*K, of thermal diffusivity of 0.2 m̂2/s, and of boiling point of 2200° F. Due to the propensity of many of these metals to oxidize, it is preferable to incorporate the metal in an evacuated or sealed chamber in the funnel or in proximity to a gettering agent (a material that will preferentially oxidize), or to conduct the infiltration process in a controlled atmosphere (e.g., vacuum, argon, helium, hydrogen).
- When subjected to the heat provided by the furnace 402 (
FIG. 4A ), thethermal material 510 inFIGS. 7A-7D may absorb thermal energy from thefurnace 402 and, in at least one embodiment, may become molten. Upon removing the mold assembly 300 (and the associated funnel(s) 700 a-d) from thefurnace 402, thethermal material 510 may provide heat to the molten contents within themold assembly 300, and thereby slow its cooling rate and otherwise help directional solidification. In embodiments where thethermal material 510 becomes molten, the moltenthermal material 510 may progress through a phase change from a liquid state to a solid state. As the moltenthermal material 510 cools and, therefore, proceeds through a phase change process (if applicable), latent heat involved with the phase change may be released from the moltenthermal material 510 until the molten mass solidifies. As will be appreciated, the time required for the moltenthermal material 510 to solidify may prove advantageous in providing additional time to allow thermal energy to be removed through the bottom 418 (FIGS. 4B-4C ) of themold assembly 300 via the thermal heat sink 404 (FIGS. 4B-4C ), and thereby help directionally solidify the molten contents within themold assembly 300. - Embodiments that use metal
thermal materials 510 may prove advantageous in being reusable. Once thethermal materials 510 cool, they may be subjected once again to the heat of the furnace 402 (FIG. 4A ) and serve the same purpose in another downhole tool infiltration application. In one or more embodiments, as shown inFIG. 7B , thethermal material 510 may be disposed within a container orvessel 702 that may be removably positioned within thecavity 506. In such embodiments, the vessel with thethermal material 510 disposed therein may be positioned within thecavity 506 during operation and removed once the internal components of the mold assembly 300 (FIG. 3 ) have sufficiently cooled. Accordingly, thevessel 702 may also advantageously be reusable. - In some embodiments, the
thermal material 510 may be configured to provide or extract latent heat as the result of an exothermic or endothermic chemical reaction occurring within thecavity 506. In other embodiments, thethermal material 510 may provide latent heat as the result of an allotropic phase change occurring within thecavity 506. For example, some materials used as thethermal material 510, such as iron, undergo a crystal structure change [i.e., between body-centered cubic (BCC) and face-centered cubic (FCC)] while being heated or cooled through certain temperature ranges. During the transition between crystalline structures, the ironthermal material 510 may be able to provide a specific and known energy transfer for a certain amount of time. - Referring now to
FIGS. 8A-8E , illustrated are partial cross-sectional side views of exemplary funnels 800 a-800 e, respectively, that may be used in an exemplary mold assembly, according to one or more embodiments. The funnels 800 a-e may be similar to the funnels 500 a-d ofFIGS. 5A-5D and, therefore, may be similar in some respects to thefunnel 306 ofFIG. 3 and otherwise replace thefunnel 306 in themold assembly 300 ofFIG. 3 . As illustrated, the funnels 800 a-d may include the inner andouter walls cavity 506 defined therebetween, and thethermal material 510 disposed within thecavity 506. - As indicated above, the geometry or configuration of the funnels 800 a-d described herein may vary to provide varying thermal resistance or thermal properties along a height A (
FIG. 8A ) of a given funnel 800 a-e. InFIG. 8A , for example, thecavity 506 may be shorter (e.g., its depth is shorter) along the height A such that thethermal material 510 only alters the thermal profile of thefunnel 800 a at a particular location along the height A. Thefunnel 800 b inFIG. 8B provides acavity 506 that has awidth 802 that narrows along the height A (FIG. 8A ) as it proceeds from top to bottom. In certain embodiments, this narrowing can be accomplished by a triangular cross section, thereby providing a constant change in thermal properties with respect to height A. In other embodiments, however, it may be desirable to accomplish narrowing of the cavity 506 (and modulation of its thermal properties) in a custom fashion. For example, the design shown inFIG. 8B illustrates a constant thermal property midway down thecavity 506 along the height A (FIG. 8A ) after which the thickness or depth (and thermal property) is reduced according to a cubic curve. - Along similar lines, the design in
FIG. 8C demonstrates acavity 506 that defines a bulbous central area that may be configured to provide a maximum amount ofthermal material 510 at an intermediate location along the height A (FIG. 8A ). In addition, thefunnel 800 d ofFIG. 8D modulates thermal properties by providing acavity 506 with at least one stepped inner wall that narrows along the height A (FIG. 8A ) as it proceeds from top to bottom. As will be appreciated, thecavity 506 ofFIG. 8D may alternatively narrow along the height A (FIG. 8A ) as it proceeds from bottom to top, without departing from the scope of the disclosure. Accordingly, the funnels 800 a-d and their correspondingcavities 506 may be designed so as to provide different amounts ofthermal material 510 vertically and thereby correspondingly alter the gradient of thermal energy laterally. - In
FIG. 8E , thecavity 506 forms a tortuous channel that generally follows the inner contour of thefunnel 800 e to provide thermal properties closer to the infiltrated downhole tool. As will be appreciated, when such designed channels are difficult or impossible to machine in one piece of material, thefunnel 800 e may be machined in multiple components that are attached to each other, such as via one or more threaded engagements 508 (FIG. 5A ). Alternatively, thefunnel 800 e may be formed as a multi-material or hollow funnel in the multi-step process described above that includes designing and manufacturing the blank for thecavity 506 and thereafter forming thefunnel 800 e around the blank for thecavity 506. - Referring now to
FIG. 9 , illustrated are partial cross-sectional side views of anexemplary funnel 900 taken at different angular locations, as shown in the center top view. Thefunnel 900 may be similar to or the same as any of the funnels described or shown herein. Accordingly, thefunnel 900 may include the inner andouter walls cavity 506 defined therebetween, and thethermal material 510 disposed within thecavity 506. - The
cavity 506 in thefunnel 900, however, may have an undulating or variablebottom surface 902, where thebottom surface 902 provides alternating hills and valleys (e.g., high points and low points, respectively) about the circumference of the funnel within thecavity 506. More particularly, thecavity 506 may have afirst depth 904 a at one angular location about thefunnel 900, as shown along the lines A-A, but may exhibit a second depth 904 b at a second angular location, as shown along the lines B-B. As illustrated, thefirst depth 904 a is shorter than the second depth 904 b, such that thethermal material 510 is only able to extend to thedepth 904 a in some portions of thefunnel 900 while extending to the greater depth 904 b at other portions of thefunnel 900. - Those skilled in the art will readily recognize the advantage that the undulating or variable
bottom surface 902 of thefunnel 900 may provide. For instance, the undulatingbottom surface 902 may be designed or otherwise configured to provide an operator with the ability to angularly align more or lessthermal material 510 with desired locations in the infiltrated downhole tool. In some embodiments, for example, it may be desired to include increased amounts ofthermal material 510 radially adjacent portions of the infiltrated downhole tool that exhibit higher thermal mass, such as the locations of thecutter blades 102 of the drill bit 100 (FIGS. 1 and 2 ). In such embodiments, the portions of thecavity 506 that have the second depth 904 b may be aligned with such locations where additionalthermal material 510 may be able to interact therewith. On the other hand, it may alternatively be desired to have decreased amounts ofthermal material 510 radially adjacent portions of the infiltrated downhole tool that have less thermal mass, such as the locations of thejunk slots 124 thedrill bit 100. In such embodiments, the portions of thecavity 506 that have the first andshorter depth 904 a may be aligned with such locations where lessthermal material 510 may be deposited. As will be appreciated, such embodiments may allow an operator to focus the thermal property advantages provided by thefunnel 900 in areas that are more susceptible to defects. - Referring to
FIG. 10 , illustrated is a partial cross-sectional side view of anotherexemplary funnel 1000 that that may be used in an exemplary mold assembly, according to one or more embodiments. Thefunnel 1000 may be similar to the funnels 500 a-d ofFIGS. 5A-5D and, therefore, may be similar in some respects to thefunnel 306 ofFIG. 3 and otherwise replace thefunnel 306 in themold assembly 300 ofFIG. 3 . As illustrated, thefunnel 1000 may include the inner andouter walls cavity 506 defined therebetween, and thethermal material 510 disposed within thecavity 506. - In the illustrated embodiment, the inner and
outer walls first ring 1002 a, asecond ring 1002 b, athird ring 1002 c, and afourth ring 1002 d. While four rings 1002 a-d are depicted inFIG. 10 , it will be appreciated that more or less than four rings 1002 a-d may be used, without departing from the scope of the disclosure. In some embodiments, as illustrated, the rings 1002 a-d may be threaded to each other at corresponding threadedengagements 1004. In other embodiments, however, the rings 1002 a-d may be joined via other suitable attachment or joining methods. For instance, simple attachments include locating pins with corresponding recesses, or other similar mirrored locating features/geometries, such as protrusions and channels. The rings 1002 a-d could also be attached via a sintering or brazing process, without departing from the scope of the disclosure. - In some embodiments, the materials of the rings 1002 a-d may be the same. In other embodiments, however, axially adjacent rings 1002 a-d may be made of different materials that exhibit different thermal properties. In at least one embodiment, for instance, the
fourth ring 1002 d may be made of a material that has better insulation properties or exhibits a higher heat capacity (or both) as compared to the other rings 1002 a-c. As will be appreciated by those skilled in the art, this may prove advantageous since thefourth ring 1002 d is typically radially adjacent themetal blank 202 of the drill bit 100 (FIGS. 2 and 3 ) during fabrication and, more particularly, adjacent the angled surface of themetal blank 202. The angled surface of themetal blank 202 is a region that is typically sensitive to cooling rates and, therefore, more susceptible to defects. Accordingly, thefunnel 1000 may be designed with rings 1002 a-d that vary the thermal properties of thefunnel 1000 along its axial height A so as to prevent or otherwise mitigate defects at or near the angled surface of themetal blank 202. - Furthermore, the
thermal material 510 used in thefunnel 1000 may also be composed of multiple segments (e.g., rings) as disposed within thecavity 506 in the vertical direction to provide a similar thermally graded structure. Alternatively, thecavity 506 andthermal material 510 can have different sizes in each ring segment to facilitate forming more complex internal cavities. For example, the internal wall thickness in the second andthird rings 1002 b,c could be reduced to greatly expand the width of thecavity 506 in the middle portion, similar to the design shown inFIG. 5C , thereby providing additional thermal mass in thefunnel 1000. - In any of the funnel configurations and designs described herein, conductive heat transfer may be facilitated or modulated through the given funnel by using embedded refractory particles. More particularly, the material of the funnels (i.e., the material of the inner and
outer walls - In any of the funnel configurations and designs described herein, a given funnel may provide or otherwise define a plurality of small, air filled cavities defined within the material of the inner and/or
outer walls outer surface 504, may be formed such that it is impermeable, such that the molten contents within the mold assembly 300 (FIG. 3 ) are unable to migrate into the voids formed in the funnel material. As will be appreciated, such air filled cavities may prove useful in helping to control the cooling characteristics of the given funnel. Rather than conducting the thermal energy from the molten contents within themold assembly 300 directly through the material of the given funnel, the porous, air filled cavities and associated network provide a tortuous conduction path through the material in addition to providing slower heat flux through the pores due to radiation through entrapped air or vacuum. Also, such designs with controlled porosity can be integrated in an outer sleeve, such as theouter wall 504 inFIGS. 6A and 6B , or thethermal material 510. - In any of the funnel configurations and designs described herein, the inner and
outer walls - Referring now to
FIG. 11 , illustrated is a cross-sectional side view of anotherexemplary mold assembly 1100, according to one or more embodiments. Themold assembly 1100 may be similar to themold assembly 300 ofFIG. 3 and therefore will be best understood with reference thereto, where like numerals correspond to like elements or components that will not be described again. As illustrated, themold assembly 1100 may include one or more of themold 302, thegauge ring 304, thefunnel 306, thebinder bowl 308, and thecap 310. As indicated above, the principles of the present disclosure are not only applicable to thefunnel 306 and its various configurations described herein, but are equally applicable to all components of themold assembly 1100, without departing from the scope of the disclosure. - More particularly, one or all of the components of the
mold assembly 1100 may have a cavity defined therein and filled with thethermal material 510 to alter and otherwise control the thermal properties of themold assembly 1100. As illustrated, themold 302 may provide afirst cavity 1102 a, thegauge ring 304 may provide asecond cavity 1102 b, thefunnel 306 may provide athird cavity 1102 c, thebinder bowl 308 may provide one or morefourth cavities 1102 d, includingsidewall cavities 1102 e, and thecap 310 may provide afifth cavity 1102 f. Each cavity 1102 a-f may be filled with thethermal material 510 as described herein in any of the embodiments. In some embodiments, the size, thickness, and/or configuration of any of the cavities 1102 a-f may be altered to meet desired thermal characteristics (i.e., thermal resistance) at predetermined locations about themold assembly 1100. In some embodiments, for example, the height of thegauge ring 304 may be increased, thereby increasing the size of thesecond cavity 1102 b and its thermal properties. - It will be appreciated that the various embodiments described and illustrated herein may be combined in any combination, in keeping within the scope of this disclosure. Indeed, variations in the size and configuration of any of the funnels described herein may be implemented in any of the embodiments, as generally described herein. Likewise, variations in the size and configuration of the
funnel 306 in any of the funnels described herein may be implemented according to any of the presently described embodiments. Moreover, the different types ofthermal material 510 listed or described herein may be used in any of the funnels described herein, or in any combination, without departing from the scope of the disclosure. - Embodiments disclosed herein include:
- A. A mold assembly for fabricating an infiltrated downhole tool, the mold assembly including a mold forming a bottom of the mold assembly, a funnel operatively coupled to the mold and having an inner wall, an outer wall, and a cavity defined between the inner and outer walls, and an infiltration chamber defined at least partially by the mold and the funnel, wherein the inner wall faces the infiltration chamber and the outer wall forms at least a portion of an outer periphery of the mold assembly.
- B. A method that includes placing a mold assembly within a furnace, the mold assembly including a mold forming a bottom of the mold assembly, a funnel operatively coupled to the mold, and an infiltration chamber defined at least partially by the mold and the funnel, wherein the funnel provides an inner wall, an outer wall, and a cavity defined between the inner and outer walls, and wherein the inner wall faces the infiltration chamber and the outer wall forms at least a portion of an outer periphery of the mold assembly removing the mold assembly from the furnace to cool molten contents disposed within the infiltration chamber, and varying a thermal profile of the molten contents with the funnel and thereby facilitating directional solidification of the molten contents.
- Each of embodiments A and B may have one or more of the following additional elements in any combination: Element 1: wherein the infiltrated downhole tool is selected from the group consisting of a drill bit, a cutting tool, a non-retrievable drilling component, a drill bit body associated with casing drilling of wellbores, a drill-string stabilizer, a cone for a roller-cone drill bit, a model for forging dies used to fabricate support arms for roller-cone drill bits, an arm for a fixed reamer, an arm for an expandable reamer, an internal component associated with expandable reamers, a rotary steering tool, a logging-while-drilling tool, a measurement-while-drilling tool, a side-wall coring tool, a fishing spear, a washover tool, a rotor, a stator, a blade for a downhole turbine, and a housing for a downhole turbine. Element 2: wherein the inner wall is coupled to the outer wall. Element 3: wherein the cavity is filled at least partially with a thermal material selected from the group consisting of a ceramic, a ceramic-fiber blanket, a polymer, a metal, an insulating metal composite, a carbon, a nanocomposite, a glass, a foam, a gas, any composite thereof, and any combination thereof. Element 4: wherein the thermal material is in the form of at least one of beads, cubes, pellets, particulates, a powder, flakes, fibers, wools, a woven fabric, a bulked fabric, sheets, bricks, stones, blocks, cast shapes, molded shapes, sprayed insulation, a vacuum, any hybrid thereof, and any combination thereof. Element 5: wherein the cavity is sealed and the gas is selected from the group consisting of air, argon, neon, helium, krypton, xenon, oxygen, carbon dioxide, methane, nitric oxide, nitrogen, nitrous oxide, and any combination thereof. Element 6: wherein the thermal material is segmented into multiple rings disposed within the cavity. Element 7: wherein the funnel has a top and a bottom and a height that extends between the top and the bottom, and wherein at least one of a thickness and a geometry of one or both of the inner and outer walls varies along the height to vary a thermal property of the funnel along the height. Element 8: wherein a width of the cavity narrows along at least a portion of the height. Element 9: wherein the cavity provides a tortuous conduit along at least a portion of the height. Element 10: further comprising a reflective coating disposed within the cavity and applied to or adjacent a surface of one or both of the inner and outer walls. Element 11: further comprising a thermal barrier disposed within the cavity and applied to or adjacent a surface of one or both of the inner and outer walls. Element 12: wherein the inner and outer walls are concentric cylinders and a footing extends horizontally from the inner wall to support the outer wall. Element 13: wherein the inner and outer walls are made of different materials selected from the group consisting of graphite, alumina, a ceramic, a metal, an insulating metal composite, a nanocomposite, a foam, and a ceramic-fiber blanket. Element 14: wherein the cavity is filled at least partially with a thermal material selected from the group consisting of a metal, a salt, and a ceramic in the form of at least one of beads, cubes, pellets, particulates, a powder, and flakes, fibers, wools, a woven fabric, a bulked fabric, sheets, bricks, stones, blocks, cast shapes, molded shapes, sprayed insulation, any hybrid thereof, and any combination thereof. Element 15: wherein the thermal material is disposed within a vessel that is removably positionable within the cavity. Element 16: wherein the cavity has a bottom surface that defines alternating high points and low points about a circumference of the funnel within the cavity. Element 17: wherein the inner and outer walls are segmented axially into a plurality of rings. Element 18: wherein the plurality of rings are made of at least two dissimilar materials that exhibit different thermal properties. Element 19: further comprising at least one of a gauge ring interposing the mold and the funnel, wherein the funnel is operatively coupled to the mold via the gauge ring, a binder bowl positioned above the funnel, and a cap positionable on the binder bowl. Element 20: wherein one or more of the mold, the funnel, the gauge ring, the binder bowl, and the cap are made of a material that includes embedded refractory particles. Element 21: wherein one or more of the mold, the funnel, the gauge ring, the binder bowl, and the cap are made of a material that defines a plurality of small, air filled cavities. Element 22: wherein the cavity is a first cavity and at least one of the mold, the gauge ring, the binder bowl, and the cap defines a second cavity, and wherein the second cavity is filled at least partially with a thermal material selected from the group consisting of a ceramic, a polymer, a metal, an insulating metal composite, a carbon, a nanocomposite, a glass, a foam, a gas any composite thereof, and any combination thereof.
- Element 23: wherein the cavity is filled at least partially with a thermal material, the thermal material being selected from the group consisting of a ceramic, a ceramic-fiber blanket, a polymer, a metal, an insulating metal composite, a carbon, a nanocomposite, a glass, a foam, a gas, any composite thereof, and any combination thereof, and wherein varying the thermal profile of the molten contents with the funnel comprises varying a thermal property of the mold assembly along a height of the funnel with the thermal material. Element 24: wherein the thermal material is a metal, a salt, or a ceramic in the form of at least one of beads, cubes, pellets, particulates, a powder, flakes, fibers, wools, a woven fabric, a bulked fabric, sheets, bricks, stones, blocks, cast shapes, molded shapes, sprayed insulation, any hybrid thereof, and any combination thereof, and wherein varying the thermal profile of the molten contents with the funnel comprises absorbing thermal energy with the thermal material while the mold assembly is in the furnace, and providing latent heat from the thermal material to the molten contents when the mold assembly is removed from the furnace. Element 25: wherein a reflective coating is disposed within the cavity and applied to or adjacent a surface of one or both of the inner and outer walls, the method further comprising reflecting thermal energy emitted from the molten contents back toward the molten contents with the reflective coating. Element 26: wherein a thermal barrier is disposed within the cavity and applied to or adjacent a surface of one or both of the inner and outer walls, the method further comprising increasing a thermal resistance of the funnel with the thermal barrier. Element 27: wherein the cavity is filled at least partially with a thermal material and wherein varying the thermal profile of the molten contents with the funnel comprises providing latent heat from the thermal material to the molten contents as the thermal material undergoes an exothermic chemical reaction. Element 28: wherein the cavity is filled at least partially with a thermal material and wherein varying the thermal profile of the molten contents with the funnel comprises providing latent heat as the thermal material undergoes an allotropic phase change. Element 29: wherein the mold assembly further comprises one or more of a gauge ring interposing the mold and the funnel, a binder bowl positioned above the funnel, and a cap positionable on the binder bowl, and wherein the cavity is a first cavity and at least one of the mold, the gauge ring, the binder bowl, and the cap defines a second cavity filled at least partially with a thermal material, the method further comprising varying the thermal profile of the molten contents with the thermal material disposed within the second cavity and thereby facilitating directional solidification of the molten contents.
- By way of non-limiting example, exemplary combinations applicable to A, B, and C include: Element 3 with Element 4; Element 3 with Element 5; Element 3 with Element 6; Element 7 with Element 8; Element 7 with Element 9; Element 12 with Element 13; Element 14 with Element 15; Element 17 with Element 18; Element 19 with Element 20; Element 19 with Element 21; Element 19 with Element 22; and Element 23 with Element 24.
- Therefore, the disclosed systems and methods are well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, as the teachings of the present disclosure may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular illustrative embodiments disclosed above may be altered, combined, or modified and all such variations are considered within the scope of the present disclosure. The systems and methods illustratively disclosed herein may suitably be practiced in the absence of any element that is not specifically disclosed herein and/or any optional element disclosed herein. While compositions and methods are described in terms of “comprising,” “containing,” or “including” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components and steps. All numbers and ranges disclosed above may vary by some amount. Whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range is specifically disclosed. In particular, every range of values (of the form, “from about a to about b,” or, equivalently, “from approximately a to b,” or, equivalently, “from approximately a-b”) disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee. Moreover, the indefinite articles “a” or “an,” as used in the claims, are defined herein to mean one or more than one of the element that it introduces. If there is any conflict in the usages of a word or term in this specification and one or more patent or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted.
- As used herein, the phrase “at least one of” preceding a series of items, with the terms “and” or “or” to separate any of the items, modifies the list as a whole, rather than each member of the list (i.e., each item). The phrase “at least one of” allows a meaning that includes at least one of any one of the items, and/or at least one of any combination of the items, and/or at least one of each of the items. By way of example, the phrases “at least one of A, B, and C” or “at least one of A, B, or C” each refer to only A, only B, or only C; any combination of A, B, and C; and/or at least one of each of A, B, and C.
Claims (20)