US20170275775A1 - Brochette system and method for metal plating - Google Patents
Brochette system and method for metal plating Download PDFInfo
- Publication number
- US20170275775A1 US20170275775A1 US15/080,982 US201615080982A US2017275775A1 US 20170275775 A1 US20170275775 A1 US 20170275775A1 US 201615080982 A US201615080982 A US 201615080982A US 2017275775 A1 US2017275775 A1 US 2017275775A1
- Authority
- US
- United States
- Prior art keywords
- component
- brochette
- metal plating
- spacer
- components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- Metal plating is a process of depositing a metallic material on a surface of an object. Metal plating can change the characteristics of the surface of the object, such as increasing corrosion resistance, increasing surface hardness, increasing or decreasing surface friction, increasing or decreasing surface adhesiveness, increasing aesthetic value, and the like. Many methods have been developed for metal plating, including electroplating and electroless plating. In electroplating, a substrate is provided with an ionic metal and electrons are supplied to cause a film of non-ionic metal to form on the substrate. In electroless plating, the substrate is placed in an aqueous solution where several simultaneous reactions occur without the use of external electrical power to cause a layer of metal to form on the substrate.
- Existing metal plating processes are time-consuming and hazardous. Some existing metal plating processes require significant amounts of manual labor for preparation of components to be plated and for finishing the plated components. The preparation and finishing of these components in the existing metal plating processes require manual work by a technician on each component, taking large amounts of time for the labor and exposing the technician to hazardous materials used during the preparation and finishing of the components.
- Various examples of the present disclosure provide methods of metal plating that address, among other things, the extraneous manual labor and harmful solutions needed in the finishing process of the prior art metal plating techniques.
- In one embodiment, a method of metal plating components includes placing at least one component and at least one spacer on a brochette, placing the brochette with the at least one component and the at least one spacer on a structure, and placing the structure with the brochette into a metal plating tank having a metal plating solution such that the at least one component is submersed in the metal plating solution. The at least one spacer is configured to mask a portion of the least one component. The at least one component and the at least one spacer are arranged on the brochette such that the at least one spacer prevents the portion of the at least one component from being contacted by the metal plating solution. The method further includes metal plating at least one surface of the at least one component submersed in the metal plating solution, removing the structure with the brochette from the metal plating solution, drying the at least one component on the brochette, and removing the dried at least one component and the at least one spacer from the brochette.
- In one example, the method further includes placing the structure with the brochette into a cleaning tank having a cleaning solution such that the at least one component is submersed in the cleaning solution before placing the structure into the metal plating tank. In another example, the at least one component and the at least one spacer are arranged on the brochette such that the at least one spacer prevents the portion of the at least one component from being contacted by the cleaning solution.
- In another example, the method further includes rotating the brochette with the at least one component while the at least one component is submersed in the metal plating solution. In another example, the structure comprises a brochette rotation system configured to rotate the brochette with the at least one component while the at least one component is submersed in the metal plating solution.
- In another example, the method further includes providing an electrical charge to the at least one component while the at least one component is submersed in the metal plating solution. In another example, the structure comprises at least one support hook configured to be placed on a support structure above the metal plating tank while the at least one component is submersed in the metal plating solution. In another example, providing the electrical charge to the at least one component comprises providing the electrical charge from the support structure to the structure via the at least one support hook, from the structure to the brochette via a contact point between the structure and the brochette, and from the brochette to the at least one component.
- In another example, placing the at least one component and the at least one spacer on the brochette comprises placing the at least one component and the at least one spacer between fasteners on the brochette. In another example, the method further includes applying a compressive force to the at least one component and the at least one spacer on the brochette between the fasteners.
- In another example, placing the at least one component and the at least one spacer on the brochette comprises placing the brochette through a bore of the at least one component and a bore of the at least one spacer. In another example, placing the at least one component and the at least one spacer on the brochette further comprises placing a conical section of the spacer into the bore of the at least one component.
- In another example, the at least one component comprises a plurality of components. In another example, two of the plurality of components have one or more of different sizes or different shapes. In another example, the plurality of components comprises a first component having a first surface and a second component having a second surface. In another example, placing the at least one component and the at least one spacer on the brochette comprises placing the first component and the second component on the brochette with the first surface facing the second surface. In another example, the placement of the first component and the second component on the brochette with the first surface facing the second surface is configured to prevent the first surface and the second surface from being contacted by the metal plating solution while the first and second components are submersed in the metal plating solution.
- In another embodiment, a system for holding at least one component during a metal plating process includes a brochette configured to have the at least one component placed thereon, at least one spacer configured to be placed on the brochette and to mask a portion of the least one component, and a structure configured to hold the brochette with the at least one component and the at least one spacer. The at least one spacer is configured to be arranged on the brochette such that, when the structure with the brochette is placed into a metal plating tank having a metal plating solution such that the at least one component is submersed in the metal plating solution, the at least one spacer prevents the portion of the at least one component from being contacted by the metal plating solution.
- In one example, the system further includes a brochette rotation system configured to rotate the brochette with the at least one component while the at least one component is submersed in the metal plating solution. In another example, the system further includes fasteners configured to exert a compressive force on the at least one component and the at least one spacer on the brochette when the at least one component and the at least one spacer are located between the fasteners on the brochette.
- This summary is provided to introduce a selection of concepts in a simplified form that are further described below in the Detailed Description. This summary is not intended to identify key features of the claimed subject matter, nor is it intended to be used as an aid in determining the scope of the claimed subject matter.
- The foregoing aspects and many of the attendant advantages of the disclosed subject matter will become more readily appreciated as the same become better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings, wherein:
-
FIG. 1 depicts an existing metal plating process for plating a component; -
FIGS. 2A and 2B depict a front view and a side cross-sectional view, respectively, of an embodiment of a component suitable for plating by one embodiment of a metal plating process; -
FIGS. 3A and 3B depict a front view and a side cross-sectional view, respectively, of another embodiment of a component suitable for plating by one embodiment of a metal plating process; -
FIGS. 4A and 4B depict a side view and a perspective view, respectively, of an embodiment of a spacer usable to hold and mask components in one embodiment of a metal plating system; -
FIG. 5 depicts an embodiment of a metal plating system for plating one or more components using spacers, such as, for example, the spacers depicted inFIGS. 4A and 4B ; -
FIGS. 6A and 6B depict a side view and a cross-sectional view, respectively, of an embodiment of a brochette with various embodiments of the components installed thereon using spacers, such as, for example, the spacers depicted inFIGS. 4A and 4B ; -
FIGS. 7A to 7F depict one representative embodiment of a process for metal plating components using a metal plating system, such as, for example, the system depicted inFIG. 5 ; and -
FIG. 8 depicts an embodiment of a metal plating process for plating a plurality of components in accordance with an aspect of the present disclosure. - Embodiments of systems and methods are disclosed herein for metal plating using a brochette to hold components and spacers. In some embodiments, the spacers hold the components to the brochette and mask portions of the components during the metal plating process. The systems and methods disclosed herein for metal plating provide advantages over existing metal plating processes.
- One existing
metal plating process 100 for plating a component (e.g., a bushing) is depicted inFIG. 1 . Atblock 102, the component is masked to cover a surface of the component that will not be plated. The component, for example, can include a through bore defining an interior bore surface. In one example, masking the component includes placing a masking material (e.g., masking tape) over the interior bore surface. Atblock 104, the component is blast cleaned to prepare the unmasked surfaces of the component that will be plated. Atblock 106, the component is prepared with a wire. In one example, a wire is fed through a bore in the component such that the wire touches only the masked portions of the component. Atblock 108, the component is metal plated and dried. In one example, the component is held by the wire during the metal plating and drying process and passes electrical current to the component during the plating process. - After the component has dried, the wire is then removed from the component and the component is unmasked at
block 110. In one example, uninstalling the wire includes removing the wire from a bore in the component. In another example, unmasking the component includes removing masking tape from the component. Atblock 112, the unmasked component is cleaned. Cleaning the unmasked component includes removing adhesive left on the component by the masking tape. In some examples, cleaning the unmasked component also includes removing metal plating from the surface that was not to be plated (e.g., when a gap existed in the masking tape during the plating process). Atblock 114, the metal plating on the component is brushed and polished. In some instances, the brushing and polishing is necessitated by the presence of defects in the metal plating, such as contaminants, air pockets, and the like. After the brushing and polishing, themetal plating process 100 of the component is completed and the component is ready to be used. - The
metal plating process 100 depicted inFIG. 1 has a number of deficiencies. In one example, themetal plating process 100 requires a significant amount of manual labor for each component. Each component is individually masked and cleaned prior to plating, individually plated and dried, and individually cleaned, brushed, and polished after being plated. In another example, the possibility for failure of the process is high due to the amount of manual labor required for each component. The masking process is susceptible to human error in applying the masking material (e.g., masking tape). The dipping of a component using a wire results in non-homogenous metal plating on the component. Pores can also form in the metal plating due to the presence of contaminants or air pockets formed during the plating process. The amount of manual labor can further increase the risk of exposure of a technician to hazardous materials used in themetal plating process 100, including cleaning agents used to clean the component before plating, solvents used to clean excess adhesive from the masked areas on the component, polish used to polish the plated regions of the component, and the like. - Embodiments of metal plating processes, systems, and apparatuses are described herein that address some of the deficiencies of the
metal plating process 100 depicted inFIG. 1 . Specifically, embodiments of the metal plating processes, systems, and apparatuses described herein are capable of achieving one or more of the following: metal plating multiple components at one time, increasing homogeneity of metal plating applied to components, reducing the number of defective components by reducing the opportunity for human error in the metal plating process. -
FIGS. 2A and 2B illustrate an embodiment of acomponent 120 suitable for plating in a metal plating process. Thecomponent 120 includes abore 122. Thecomponent 120 also includesouter surfaces 124 a-d that are to be plated in a metal plating process and anouter surface 128 that is not to be plated during the metal plating process. Thebore 122 of thecomponent 120 includes aninner bore surface 126 that is also not to be plated during the metal plating process. In some examples, thecomponent 120 is made from a metal or metal alloy, such as iron, steel, and the like. As can be seen inFIG. 2B , thebore 122 runs through thecomponent 120 from theouter surface 124 a to theouter surface 128, and thus, can be referred to as a through bore. -
FIGS. 3A and 3B illustrate an embodiment of acomponent 130 for plating in a metal plating process. Thecomponent 130 includes abore 132. Thecomponent 130 also includes anouter surface 134 that is to be plated in a metal plating process. Thebore 132 of thecomponent 130 includes aninner surface 136 that is not to be plated during the metal plating process. In some examples, thecomponent 130 is made from a metal or metal alloy, such as iron, steel, and the like. As can be seen inFIG. 3B , thebore 132 runs through thecomponent 130 from one side to the other to give the component 130 a tube-like structure. - The embodiments of
components components - Referring now to
FIGS. 4A and 4B there is depicted an embodiment of aspacer 140. Thespacer 140 is suitable for holding and masking one or more components in one representative embodiment of a metal plating system described below, for example, inFIG. 5 . Thespacer 140 includes two opposing conical sections 142 a-b. The conical sections 142 a-b extend from acentral portion 144 to respective ends 146 a-b of thespacer 140. Thespacer 140 also includes a throughbore 148 extending between the ends 146 a-b of thespacer 140. Various dimensions of the spacer 140 (e.g., a diameter of thecentral portion 144, a slope of the conical sections 142 a-b, a diameter of the ends 146 a-b, a diameter of thebore 148, a distance between the ends 146 a-b, etc.) may be selected based on one or more dimensions of components (e.g., a diameter of thebore 122 incomponent 120, a diameter of thebore 132 incomponent 130, etc.). In some embodiments, thespacer 140 is made from a material, such as stainless steel, that does not adhere well to metal plating. In these embodiments, thespacer 140 can be used in a metal plating process, cleaned to remove any metal plating residue after the metal plating process, and used in a subsequent metal plating process. In other embodiments, thespacer 140 is made from a material, such as silicone, plastic, etc., that adhere to metal plating. In these embodiments, thespacer 140 can be used in a metal plating process and then discarded. -
FIG. 5 depicts an embodiment of ametal plating system 150 for metal plating a plurality of components, such as, for example,components spacers 140, in accordance with an aspect of the present disclosure. Thesystem 150 includes astructure 152 configured to hold a number of brochettes 154 a-e. The brochettes 154 a-e include first ends 156 a-e, respectively, and second ends 158 a-e, respectively. Each of the first ends 156 a-e and second ends 158 a-e is configured to be placed in thestructure 152 such that the brochettes 154 a-e are held by thestructure 152 and permitted to rotate. In some embodiments, one or more of the first ends 156 a-e and second ends 158 a-e are configured to make an electrical connection with thestructure 152 when the brochettes 154 a-e are placed in thestructure 152. - The brochettes 154 a-e are configured to carry a plurality of components, shown as components 160 a-e, respectively. In one embodiment, one or more of the brochettes 154 a-e carries components 160 a-e having different shapes or sizes. As described in greater detail below with respect to
FIGS. 6A and 6B , in one embodiment, the components 160 a-e are held on the brochettes 154a -e using spacers 140 that are configured to mask portions of the components 160 a-e that are not to be plated during the metal plating process. - The
system 150 also includes a brochette rotation system configured to rotate one or more of the brochettes either individually or at the same time. In one embodiment, the brochette rotation system includes a source ofmotion 162 and a transmission comprising a plurality of motion transfer mechanisms 164 a-f. In the embodiment shown inFIG. 5 , the source ofmotion 162 includes a motor, such as a turbine, configured to produce a rotary driving force. In one embodiment, the motor is driven by pressurized air that is provided via avalve 166 andair lines 168. In other embodiments, the source ofmotion 162 may include but is not limited to a hydraulic-powered rotation mechanism, a manual rotation mechanism (e.g., a rotating handle), an electrical motor, or any other means for producing a rotary driving force. In the embodiment shown inFIG. 5 , the motion transfer mechanisms 164 a-f include gears that are configured to be rotationally driven by the source ofmotion 162. In other embodiments, the source ofmotion 162 may produce a linear output that causes rotation of the gears via a transmission device, such as a rack and pinion system, a Scottish yoke, among others. - Rotation of the motion transfer mechanisms 164 a-f causes the brochettes 154 a-e to rotate via direct or indirect coupling. In one embodiment the first ends 156 a-e of the brochettes 154 a-e are configured to be coupled to the motion transfer mechanisms 164 a-f such that rotation of the motion transfer mechanisms 164 a-f causes the brochettes 154 a-e to rotate. In other embodiments, motion transfer mechanisms 164 a-f in the brochette rotation system are replaced by another motion transfer mechanism or mechanisms, such as a chain and sprocket system, a rack and pinion system, and the like. In the case of the rack and pinion system, the source of
motion 162 may generate linear motion to drive the rack and the pinion or pinions convert the linear motion of the rack to rotary motion of the brochettes 154 a-e. - In some embodiments, the
system 150 includes additional features, such as support hooks 170. In use, the support hooks 170 in one example are placed on a support structure over a tank (e.g., a cleaning solution tank or a metal plating solution tank) such that the brochettes 154 a-e are suspended in the tank. In this example, when the brochettes 154 a-e are suspended in a tank containing solution, the source ofmotion 162 can be operated to rotate the brochettes 154 a-e and the components 160 a-e via an associated transmission, such as the motion transfer mechanisms 164 a-f, within the solution contained in the tank. In some embodiments, the support hooks 170 are made of an electrically-conductive material that conducts electricity from a support structure over a tank to the brochettes 154 a-e to provide an electrical charge during the metal plating process. - Referring now to
FIGS. 6A and 6B , side and cross-sectional views of an embodiment of thebrochette 154 a is depicted withcomponents spacers brochette 154 a includes a threaded rod withfirst end 156 a andsecond end 158 a. From left to right in the depiction shown inFIGS. 6A and 6B , the following components are installed on thebrochette 154 a: afastener 180, thespacer 140 through thebore 148, thecomponent 120 through thebore 122,component 120′ through thebore 122′, thespacer 140 through thebore 148, thespacer 140′ through thebore 148′, thecomponent 130 through thebore 132, thespacer 140′ through thebore 148′, thecomponent 130′ through thebore 132′, thespacer 140′ through thebore 148′, and thefastener 180′. - The
spacers 140 in some embodiments are configured to engage thebores components spacers 140′ are configured to engage thebores components spacers bores fasteners components spacer spacers bores fasteners bores components brochette 154 a is submersed in the solution. This arrangement allows for such solution to contact and/or plate theouter surfaces 124 a-d, 124 a′-d′, 134, and 134′ of thecomponents brochette 154 a is submersed in the solution but prevents plating at the location of inner bore surfaces. - In the embodiment shown in
FIGS. 6A and 6B , there is no spacer between thecomponent 120 and thecomponent 120′. Thecomponent 120 and thecomponent 120′ are placed on the brochette 154 withouter surfaces outer surfaces outer surfaces fasteners outer surfaces bores brochette 154 a is submersed in the solution. The arrangement shown inFIGS. 6A and 6B allows thebrochette 154 a to be submersed in metal plating solution during a metal plating process without plating theinner surfaces components outer surfaces components components - In the embodiment shown in
FIGS. 6A and 6B , there are twospacers component 120′ and thecomponent 130. In some embodiments, the use of two spacers between components enables components of different sizes and/or shapes, such as thecomponent 120′ and thecomponent 130, to be placed on the same brochette. This ability increases the number of components that can be held on a brochette during a single metal plating process. - One representative process for metal plating components using a metal plating system, such as, for example, the system shown in
FIG. 5 , will now be described with reference toFIGS. 7A to 7F . InFIG. 7A ,components 202 andspacers 204 are installed on abrochette 200. Thespacers 204 are configured to mask portions of thecomponents 202 that are not to be plated during the plating process. In some examples, thecomponents 202 and/or thespacers 204 have different sizes and/or shapes. In these examples, at least some of thespacers 204 have different sizes or shapes to mask the portions of thecomponents 202 that are not to be plated. InFIG. 7B , thebrochette 200 with the installedcomponents 202 andspacers 204 is placed into astructure 206. Thestructure 206 includes abrochette rotation system 208 configured to selectively rotate thebrochette 200 and, optionally, other brochettes placed in thestructure 206. - An assembly composed of the
structure 206 and thebrochette 200 is then placed in acleaning solution tank 210 that holds cleaningsolution 212, as shown inFIG. 7C . As shown inFIG. 7C , thebrochette 200, thecomponents 202, and thespacers 204 are submersed in thecleaning solution 212. Thespacers 204 are configured to mask portions of thecomponents 202 such that the portions of thecomponents 202 are not contacted by thecleaning solution 212 when thebrochette 200, thecomponents 202, and thespacers 204 are submersed in thecleaning solution 212. In one embodiment, thecomponents 202 and thespacers 204 are located on thebrochette 200 between fasteners that exert a compressive force to prevent the portions of thecomponents 202 from being contacted by thecleaning solution 212. - As shown in
FIG. 7C , thestructure 206 includes support hooks 213 that are configured to be placed on a support structure 214 (e.g., a bar or a pipe) located above thecleaning solution tank 210. In one embodiment, thesupport structure 214 is located at a position above thecleaning solution tank 210 such that all of the brochettes on thestructure 206 are submersed in thecleaning solution 212 when the support hooks 213 of thestructure 206 are placed on thesupport structure 214. In one embodiment, thecleaning solution 212 is configured to remove contaminants and debris from surfaces of thecomponents 202 that will be plated. The cleaning solution in one embodiment is capable of removing contaminants and debris from surfaces of thecomponents 202 that will be plated without movement of thecomponents 202 in thecleaning solution 212. In this embodiment, thebrochette 200 is not rotated by thebrochette rotation system 208 while thebrochette 200 is submersed in thecleaning solution 212. - After the
components 202 have been cleaned in thecleaning solution 212, thecomponents 202 are ready to be plated.FIG. 7D illustrates thestructure 206 supporting thebrochette 200 placed in ametal plating tank 216 that holds ametal plating solution 218. As shown inFIG. 7D , thebrochette 200, thecomponents 202, and thespacers 204 are submersed in themetal plating solution 218. Thespacers 204 are configured to mask portions of thecomponents 202 such that the portions of thecomponents 202 are not contacted by themetal plating solution 218 when thebrochette 200, thecomponents 202, and thespacers 204 are submersed in themetal plating solution 218. In one embodiment, thecomponents 202 and thespacers 204 are located on thebrochette 200 between fasteners that exert a compressive force to prevent the portions of thecomponents 202 from being contacted by themetal plating solution 218. - As shown in
FIG. 7D , the support hooks 213 on thestructure 206 are configured to be placed on a support structure 220 (e.g., a bar or a pipe) located above the metalplating solution tank 216. In one embodiment, thesupport structure 220 is located at a position above the metalplating solution tank 216 such that all of the brochettes on thestructure 206 are submersed in themetal plating solution 218 when the support hooks 213 of thestructure 206 are placed on thesupport structure 220. Themetal plating solution 218 is configured to plate surfaces of thecomponents 202. In one embodiment, thecomponents 202 are plated by themetal plating solution 218 in response to an electrical charge being provided to thecomponents 202. In one embodiment, the support hooks 213 are electrically conductive and an electrical charge is provided to thecomponents 202 from thesupport structure 220 to thecomponents 202 via the support hooks 213, thestructure 206, and thebrochette 200. In this and other embodiments, portions of thestructure 206 can be covered by a dielectric material, electrical insulation, etc., as long as an electrical conductive path between the support hooks and the brochette is not interrupted. - In one embodiment, the
brochette rotation system 208 is configured to rotate thebrochette 200 while thebrochette 200 is submersed in themetal plating solution 218. In some embodiments, rotating thebrochette 200 while thebrochette 200 is submersed in themetal plating solution 218 results in more even metal plating on thecomponents 202 than if thebrochette 200 remained stationary. In one embodiment, pressurized air can be advantageously used to power thebrochette rotation system 208 because pressurized air will not harm themetal plating solution 218 if pressurized air is inadvertently released into themetal plating solution 218. In addition, powering thebrochette rotation system 208 with an electrical motor may introduce an electrical charge into themetal plating solution 218 that causes uneven application of metal plating to thecomponents 202. However, while an electric motor may not be the preferred source of motion in thebrochette rotation system 208, an electric motor may be used in thebrochette rotation system 208 as a source of motion. - After the
components 202 have been metal plated, as shown inFIG. 7D , thestructure 206 is removed from themetal plating tank 216 and thecomponents 202 are dried. The components may be left on thebrochette 200 during the drying process, either with thebrochette 200 placed in the structure or with thebrochette 200 removed from the structure. After thecomponents 202 are dried, thecomponents 202 and thespacers 204 can be removed from thebrochette 200, as shown inFIG. 7E . In one example, removing thecomponents 202 and thespacers 204 from thebrochette 200 includes loosing fasteners from thebrochette 200 and sliding thecomponents 202 and thespacers 204 off of thebrochette 200. -
FIG. 7F depicts thecomponents 202 and thespacers 204 removed from thebrochette 200. In some embodiments, thecomponents 202 removed from thebrochette 200 are plated on the surfaces that were to be plated and not plated on the surfaces that were not to be plated. In some embodiments, thecomponents 202 do not require post-plating cleaning because no adhesive masking materials were used to mask thecomponents 202. In embodiments that employed brochette rotation during plating, polishing may also be avoided as rotation of thecomponents 202 during the plating inFIG. 7D can result in plating that does not need to be polished. -
FIG. 8 depicts an embodiment of ametal plating process 230 in accordance with an aspect of the present disclosure. Atblock 232, components are installed on a brochette using spacers that are configured to mask a portion of the components. In some embodiments, the components have different sizes and/or shapes. In some embodiments, the spacers have different sizes and/or shapes. In some embodiments, the components and the spacers are installed on the brochette between fasteners that are configured to exert a compressive force on the components and spacers. One example of installing components on a brochette is depicted inFIG. 7A . - At
block 234, the components are cleaned. In some embodiments, the components are cleaned by submersing the brochette with the components and spacers in a cleaning solution. The components and spacers are installed on the brochette such that portions of the components that will not be plated are not exposed to the cleaning solution. In one example, the cleaning solution is an electrolytic cleaning solution. One example of cleaning components on a brochette is depicted inFIG. 7C . - At block 236, the cleaned components are metal plated and dried. In some embodiments, the components are cleaned by submersing the brochette with the components and spacers in a metal plating solution. The components and spacers are installed on the brochette such that portions of the components that will not be plated are not exposed to the metal plating solution. In one example, the metal plating solution is an aqueous solution with cadmium for cadmium plating. In some embodiments, the components are metal plated by passing an electrical charge to the components while the components are submersed in the metal plating solution. In some embodiments, the brochette with the components is rotated by a brochette rotation system while the components are submersed in the metal plating solution. One example of metal plating components on a brochette is depicted in
FIG. 7D . - At
block 237, the plated and dried components and the spacers are uninstalled (e.g., removed) from the brochette. In one example, the metal plating process is complete when the plated and dried components are removed from the brochette. In this example, no polishing or adhesive cleaning is required after the plated and dried components are removed from the brochette. One example of uninstalling components from a brochette is depicted inFIG. 7E . - The
method 230 depicted inFIG. 8 has a number of advantages over themethod 100 depicted inFIG. 1 , some of which will now be explained. In one example, the brochette used in themethod 230 can hold a larger number of components than the wires used in themethod 100, resulting in greater volume of components plated in each metal plating process. In another example, themethod 230 eliminates the time and expense of masking components that is done in themethod 100. In another example, themethod 230 eliminates the time and expense of unmasking the components inmethod 100, as well as the risk to technicians from using a solvent to remove adhesive left on the component from the masking tape in themethod 100. In another example, the rotation of the brochette while in themetal plating solution 218 results in more even metal plating on the components than the wire dipping process used in themethod 100. Such even metal plating from themethod 230, in some embodiments, eliminates the time and expense of brushing and polishing done inmethod 100, as well as the risk to technicians from using a polish to polish the component in themethod 100. In another example, the brochette and spacers used in themethod 230 allow for treatment of components of different sizes on the same brochette at the same time. In another example, the success rate of plating components (i.e., the percentage of components that are plated without a defect) is greater using themethod 230 than themethod 100. Themethod 230 may have other advantages over themethod 100 not explicitly discussed herein. - It should be noted that for purposes of this disclosure, terminology such as “upper,” “lower,” “vertical,” “horizontal,” “inwardly,” “outwardly,” “inner,” “outer,” “front,” “rear,” etc., should be construed as descriptive and not limiting the scope of the claimed subject matter. Further, the use of “including,” “comprising,” or “having” and variations thereof herein is meant to encompass the items listed thereafter and equivalents thereof as well as additional items. Unless limited otherwise, the terms “connected,” “coupled,” and “mounted” and variations thereof herein are used broadly and encompass direct and indirect connections, couplings, and mountings.
- The principles, representative embodiments, and modes of operation of the present disclosure have been described in the foregoing description. However, aspects of the present disclosure which are intended to be protected are not to be construed as limited to the particular embodiments disclosed. Further, the embodiments described herein are to be regarded as illustrative rather than restrictive. It will be appreciated that variations and changes may be made by others, and equivalents employed, without departing from the spirit of the present disclosure. Accordingly, it is expressly intended that all such variations, changes, and equivalents fall within the spirit and scope of the present disclosure, as claimed.
Claims (20)