US20170210952A1 - Improved binder compositions and uses thereof - Google Patents

Improved binder compositions and uses thereof Download PDF

Info

Publication number
US20170210952A1
US20170210952A1 US15/326,532 US201515326532A US2017210952A1 US 20170210952 A1 US20170210952 A1 US 20170210952A1 US 201515326532 A US201515326532 A US 201515326532A US 2017210952 A1 US2017210952 A1 US 2017210952A1
Authority
US
United States
Prior art keywords
binder composition
dmh
acid
curable binder
aqueous curable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/326,532
Other languages
English (en)
Inventor
Carl Hampson
Ferdous Khan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Knauf Insulation SPRL
Knauf Insulation Inc
Original Assignee
Knauf Insulation SPRL
Knauf Insulation Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=51494741&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20170210952(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Knauf Insulation SPRL, Knauf Insulation Inc filed Critical Knauf Insulation SPRL
Publication of US20170210952A1 publication Critical patent/US20170210952A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J101/00—Adhesives based on cellulose, modified cellulose, or cellulose derivatives
    • C09J101/08—Cellulose derivatives
    • C09J101/26—Cellulose ethers
    • C09J101/28—Alkyl ethers
    • C09J101/284—Alkyl ethers with hydroxylated hydrocarbon radicals
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J101/00—Adhesives based on cellulose, modified cellulose, or cellulose derivatives
    • C09J101/08—Cellulose derivatives
    • C09J101/26—Cellulose ethers
    • C09J101/28—Alkyl ethers
    • C09J101/286—Alkyl ethers substituted with acid radicals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B27—WORKING OR PRESERVING WOOD OR SIMILAR MATERIAL; NAILING OR STAPLING MACHINES IN GENERAL
    • B27K—PROCESSES, APPARATUS OR SELECTION OF SUBSTANCES FOR IMPREGNATING, STAINING, DYEING, BLEACHING OF WOOD OR SIMILAR MATERIALS, OR TREATING OF WOOD OR SIMILAR MATERIALS WITH PERMEANT LIQUIDS, NOT OTHERWISE PROVIDED FOR; CHEMICAL OR PHYSICAL TREATMENT OF CORK, CANE, REED, STRAW OR SIMILAR MATERIALS
    • B27K3/00—Impregnating wood, e.g. impregnation pretreatment, for example puncturing; Wood impregnation aids not directly involved in the impregnation process
    • B27K3/02—Processes; Apparatus
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B27—WORKING OR PRESERVING WOOD OR SIMILAR MATERIAL; NAILING OR STAPLING MACHINES IN GENERAL
    • B27N—MANUFACTURE BY DRY PROCESSES OF ARTICLES, WITH OR WITHOUT ORGANIC BINDING AGENTS, MADE FROM PARTICLES OR FIBRES CONSISTING OF WOOD OR OTHER LIGNOCELLULOSIC OR LIKE ORGANIC MATERIAL
    • B27N3/00—Manufacture of substantially flat articles, e.g. boards, from particles or fibres
    • B27N3/002—Manufacture of substantially flat articles, e.g. boards, from particles or fibres characterised by the type of binder
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L3/00—Compositions of starch, amylose or amylopectin or of their derivatives or degradation products
    • C08L3/02—Starch; Degradation products thereof, e.g. dextrin
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J101/00—Adhesives based on cellulose, modified cellulose, or cellulose derivatives
    • C09J101/08—Cellulose derivatives
    • C09J101/26—Cellulose ethers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J103/00—Adhesives based on starch, amylose or amylopectin or on their derivatives or degradation products
    • C09J103/02—Starch; Degradation products thereof, e.g. dextrin
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J105/00—Adhesives based on polysaccharides or on their derivatives, not provided for in groups C09J101/00 or C09J103/00
    • C09J105/08—Chitin; Chondroitin sulfate; Hyaluronic acid; Derivatives thereof
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
    • C09J11/02—Non-macromolecular additives
    • C09J11/04—Non-macromolecular additives inorganic
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
    • C09J11/02—Non-macromolecular additives
    • C09J11/06—Non-macromolecular additives organic
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
    • C09J11/08—Macromolecular additives
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J131/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an acyloxy radical of a saturated carboxylic acid, of carbonic acid, or of a haloformic acid; Adhesives based on derivatives of such polymers
    • C09J131/02—Homopolymers or copolymers of esters of monocarboxylic acids
    • C09J131/04—Homopolymers or copolymers of vinyl acetate
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J179/00—Adhesives based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen, with or without oxygen, or carbon only, not provided for in groups C09J161/00 - C09J177/00
    • C09J179/02—Polyamines

Definitions

  • the present invention relates to new improved binder compositions, more specifically curable binder compositions for use in manufacturing products from a collection of non or loosely assembled matter.
  • these binder compositions may be employed to fabricate fiber products which may be made from woven or nonwoven fibers.
  • the binder compositions are used to bind glass fibers to make fiberglass.
  • the binder compositions are used to bind mineral wool fibers, such as glass wool or stone wool in a matted layer, such as an insulating product.
  • the binders are used to make cellulosic compositions.
  • the binders may be used to bind cellulosic matter to fabricate, for example, wood fiber board or particle board which has desirable physical properties (e.g., mechanical strength).
  • the invention further extends to a product made from loosely assembled matter bound by a binder of the invention.
  • curable binder compositions involve sustainable materials and is based on polyester chemistry, more particularly curable aqueous binder compositions comprising a polyacid component or anhydride or salt derivatives thereof, and a polyhydroxy component, possibly together with a silicon containing compound.
  • curable aqueous binder compositions comprising a polyacid component or anhydride or salt derivatives thereof, and a polyhydroxy component, possibly together with a silicon containing compound.
  • Another such composition involves the condensation of ammonium salt of inorganic acids or of polycarboxylic acids or an amine, preferably a polyamine, with reducing sugars as thermosets.
  • binder chemistries show a relatively high binder weight loss upon exposure to heat. Some also show undesirable degradation in humid environments which may negatively affect the bond strength properties of the products containing same. There further is an ongoing interest in improving the bond strength of the employed binder compositions, hence providing improved final products, showing improved properties, and/or final products with reduced binder content, at more advantageous costs.
  • the present invention seeks to provide binders which generate or promote cohesion and are capable of holding a collection of matter together such that the matter adheres in a manner to resist separation.
  • An objective of the present invention is to provide binders showing improved bond strength, as compared to close prior art binder compositions, more particularly such binder compositions based on polyester chemistry or the condensation of ammonium salt of inorganic acid or ammonium salt of polycarboxylic acids or amine with reducing sugars as thermosets.
  • Another objective of the present invention is to provide cost-effective binder compositions for large volume applications.
  • Another objective is to provide a binder composition based on renewable and/or sustainable resources.
  • the invention seeks to provide binder compositions that rapidly cure into strong binders.
  • Yet another purpose of the invention is to provide an assembly of matter bonded with the invention binder.
  • the present invention now provides an aqueous curable binder composition comprising the starting materials required for forming a thermoset resin upon curing and a matrix polymer.
  • the matrix polymer may be of natural and/or synthetic origin. These polymers may act as an active filling agent in the binder formulation, and may form intra- and inter-molecular chain interactions.
  • Naturally derived polymers may advantageously be selected from polysaccharides, such as chitosan, cellulose and its derivatives, such as cellulose ether and ester derivatives.
  • the cellulose ether derivatives can be prepared by carboxymethylation, carboxyethylation and carboxypropylation.
  • cellulose ether derivatives are: nanocellulose, carboxymethyl cellulose (CMC), sodium carboxymethyl cellulose (NaCMC), hydroxypropyl cellulose (HPC), hydroxyethyl cellulose (HEC), hydroxypropylmethyl cellulose (HPMC), methyl cellulose (MC), ethyl cellulose (EC), trityl cellulose, and so on.
  • the preferred cellulose ester derivatives include acetates, butyrates, benzoates, phthalates and anthranilic acid esters of cellulose, preferably, cellulose acetate phthalate (CAP), cellulose acetate butyrate (CAB), cellulose acetate trimelitate (CAT), hydroxylpropylmethyl cellulose phthalate (HPMCP), succinoyl cellulose, cellulose fuoroate, cellulose carbanilate, and mixtures thereof.
  • CAP cellulose acetate phthalate
  • CAB cellulose acetate butyrate
  • CAT cellulose acetate trimelitate
  • HPPMCP hydroxylpropylmethyl cellulose phthalate
  • succinoyl cellulose succinoyl cellulose
  • cellulose fuoroate cellulose carbanilate
  • mixtures thereof cationic cellulose derivatives may be used.
  • binder compositions may comprise other polysaccharides such as alginates, starch, chitin and chitosan, agarose, hyaluronic acid, and their derivatives or copolymers (e.g., graft-copolymer, block copolymer, random copolymers), or mixtures thereof.
  • polysaccharides such as alginates, starch, chitin and chitosan, agarose, hyaluronic acid, and their derivatives or copolymers (e.g., graft-copolymer, block copolymer, random copolymers), or mixtures thereof.
  • Chitosan is a polysaccharide derived from crustacean shells, like shrimp shells. Chitosan may have different molecular weights and deacetylation degrees. Preferred are molecular weights between 500 Daltons and 2. 10 6 Daltons, more preferably between 60 ⁇ 10 3 and 2 ⁇ 10 5 Da.
  • Synthetically derived polymers may include polyacrylates, polymethacrylates, polyacrylamides, polymethacrylamides, polyurethanes, polyesters, polyvinyls and/or their copolymers, aliphatic isocyanate oligomers, azetidinium groups containing polymer (azetidinium polymer) or mixtures thereof.
  • the binder formulation may comprise polyacrylate, polymethacrylate or polyacrylamide or mixtures thereof, which may be formed from polymerisation of one or more, typically two or three, monomers, which may be present in differing amounts.
  • the one of the monomers is a substituted alkyl methacrylate or acrylate monomer.
  • the alkyl group of the substituted alkyl function may have from 1 to 10, preferably 1 to 4 carbon atoms and the substituent group may be an alkoxy group with 1 to 4 carbon atoms, such as a methoxy group, or a dialkylamino group, such as dimethylamino.
  • acrylate monomers are: 2-methoxyacrylate (MEA), 3,5,5-trimethylhexyl acrylate (TMHA), ethylene glycol acrylate (EGA), 2-ethoxyethyl acrylate (EOEA), ethylene glycol diacrylate (EGDA), ethyl 2-ethylacrylate (EEA), (ethyl-cyano)acrylate (ECA), ethyl 2-propyl acrylate (EPA), ethyl 2-(trimethylsilylmethyl)acrylate (ETMSMA), butyl acrylate (BA), butylcyclohexyl acrylate (BCHA), benzyl 2-propyl acrylate (BPA), carboxyethyl acrylate (CEA), 2-(diethylamino)ethyl acrylate (DEAEA), 2-(diethylamino)propyl acrylate (DEAPA).
  • MEA 2-methoxyacrylate
  • TMHA 3,5,5-trimethylhe
  • methylmethacrylate MMA
  • 2-hydroxyethyl methacrylate HEMA
  • 2-methoxymethacrylate MEMA
  • 2-(diethylamino) ethyl methacrylate DEAEMA
  • 2-aminoethyl methacrylate AEMA
  • benzyl methacrylate BMA
  • 2-butoxyethyl methacrylate BEMA
  • 2-(tert-butylamino)ethyl methacrylate TAAEMA
  • CHMA cyclohexyl methacrylate
  • EGMA ethylene glycol methacrylate
  • DIPAEMA 2-(diisopropylamino)ethyl methacrylate
  • Preferred acrylamide/methacrylamide monomers are: alkylacrylamide (AAAm), butylacrylamide (BAAm), diethylacrylamide(DEAAm), N,N-dimethyl acrylamide (DMAAm), ethylacrylamide (EAAm), hydroxyethyl acrylamide (HEAAm), hydroxymethyl acrylamide (HMAAm), N-isopropyl acrylamide (NIPAAm), N,N-diethylmethacrylamide (DEMAAm), N-diphenyl methacrylamide (DPMAAm).
  • Preferred polymers comprise two or more monomers and typically a mixture of MEMA or MEA, and DEAEMA or vise versa, in the range between 5:95 and 95:5 percent by weight, advantageously from 10:90 to 90:10, preferably from 20:80 to 80:20, more preferably from 30:70 to 70:30.
  • further monomers may be present, such as acrylic acid (AA) or methacrylic acid (MAA) in a weight ratio of 1 to 10 percent, preferably about 5 percent by weight.
  • a suitable polymer includes MEMA, DEAEMA and AA in a ratio of 55:40:5 to 75:20:5.
  • Such polymers may comprise one or more monomers which include an aryl group, such as styrene (St) and optionally a dialkylacrylamide group (alkyl representing 1 to 4 carbon atoms), such as dimethylacrylamide (DMAA); and diethylacrylamide (DEAA).
  • St styrene
  • DMAA dimethylacrylamide
  • DEAA diethylacrylamide
  • the polymers comprise two monomers selected from styrene and a dialkylacrylamide.
  • Preferred polymers comprise, or consist of the following monomers: St:DMAA and St:DEAA and which may be present in the range of ratios between 40:60 and 95:5.
  • Additional polymers which may be used in binder formulations of the invention may comprise MEA (2-methoxyacrylate) and a dialkylacrylamide group (alkyl representing 1 to 4 carbon atoms), such as dimethylacrylamide (DMAA); and diethylacrylamide (DEAA).
  • Preferred polymers comprise or consist of MEA:DMAA and MEA:DEAA, which may be present in the ratios between 30-80:70-20 respectively.
  • the binder composition may comprise a polyurethane matrix polymer which provides bond strength and faster curing.
  • Polyurethane polymers may be formed by polymerising a polydiol with a diisocyanate and optionally with an extender molecule, such as a diol.
  • the extender molecules have the effect of modifying the physical character of the polymers, for example, polymer shape, viscosity and polymer state.
  • the polydiol may be selected from the group consisting of but not limited to, poly(polypropylene glycol)-poly(ethylene glycol) (PPG-PEG), polyethylene glycol (PEG), poly(caprolactone)-diol (PCL-diol), poly(lactic acid)-diol (PLA-diol), poly(glycolic acid)-diol (PGA-diol), poly(tetramethylene glycol) (PTMG) also known as poly(butylene glycol), poly[1,6-hexanediol/neopentyl glycol-alt-(adipic acid)]diol (PHNAD), poly[1,6-hexanediol/neopentyl glycol/diethylene glycol-alt-(adipic acid)]diol (PHNDGAD), poly(dimethyl siloxane)-diol (PDMS).
  • PPG-PEG
  • the diisocyanate may be selected from the group consisting of but not limited to methylene diphenyl diisocyanate (MDI), 1,4-phenylene diisocyanate (PDI), 1,1′-methylenebis(4-isocyanatocyclohexane) (HMDI), 2,4-toluene diisocyanate (TDI), hexamethylene diisocyanate (HDI), 1,3-bis(isocynanatomethyl) cyclohexane (BICH).
  • MDI methylene diphenyl diisocyanate
  • PDI 1,4-phenylene diisocyanate
  • HMDI 1,1′-methylenebis(4-isocyanatocyclohexane)
  • TDI 2,
  • the diisocyanate is present in an amount of 45-55% by weight of the polymer.
  • Suitable extenders include 1,4-butanediol (BD), ethylene glycol (EG), 2,2,3,3,4,4,5,5-octafluoro-1,6-hexanediol (OFHD); and 3-dimethylamino-1,2-propanediol (DMAPD).
  • the extender may be present in an amount of 10-30 mol % of the polymer, typically 10-25%.
  • the binder composition may comprise polyesters, copolymers or mixtures (blends) thereof.
  • polyesters are: polyglycolide or polyglycolic acid (PGA), polylactic acid (PLA), polycaprolactone (PCL), polyhydroxyalkanoate (PHA), polyhydroxybutyrate (PHB), polyethylene adipate (PEA), polybutylene succinate (PBS), poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polytrimethylene terephthalate (PTT), polyethylene naphthalate (PEN), vectran, and/or their copolymers such as PCL-PLA, PCL-PGA, PLA-PGA, PCL-PLA-PCL, PIBVE-b-PCL, and others.
  • the binder composition of the invention may comprise vinyl polymers and amic acid based polymers, such as poly(pyromellitic dianhydride-co-4,4′oxodianiline) amic acid.
  • these may include polyethylene, polypropylene, polybutadiene, polyvinyl chloride (PVC), polyvinyl acetate (PVAc), polyvinyl alcohol (PVA), partially hydrolized polyvinyl acetate, polyacrylonitrile (PAN), polyvinyl butyral (PVB), and polyvinyl toluene (PVT) and/or their copolymers such as PVA-b-PS, PS-b-PMMA, PS-b-PAN, PVA-PGMA, or mixtures thereof.
  • PVC polyvinyl chloride
  • PVAc polyvinyl acetate
  • PVA polyvinyl alcohol
  • PVB partially hydrolized polyvinyl acetate
  • PAN polyacrylonitrile
  • PVB polyvinyl buty
  • the above said polymers may be incorporated into the binder formulation in homogeneous (aqueous solution) or heterogeneous (emulsion) systems.
  • the solution or emulsion polymers may be present in the composition in an amount ranging from 0.5% up to 50% by weight based on total solids.
  • the binder composition may comprise an azetidinium polymer.
  • azetidinium polymer Such material is known per se and may be obtained by the reaction of a polyamidoamine and a halohydrin.
  • An azetidinium polymer is made up of at least two monomeric units containing a substituted or unsubstituted four membered nitrogen containing heterocycle.
  • the azetidinium polymer may be a homopolymer or a copolymer comprising one or more non-azetidinium monomer units incorporated into the polymer structure.
  • a preferred polyazetidinium suitable for use in accordance with the invention shows the formula
  • R 1 may be C 1 -C 25 alkanediyl, preferably C 1 -C 10 alkanediyl or C 1 -C 5 alkanediyl, possibly substituted with a hydroxyl group, carboxyl functional group or an amine,
  • Carbohydrate based binders or binder compositions may comprise polymer micro- and/or nano-particles.
  • Preferred micro- and/or nano-particles derived from natural polymers are selected from polysaccharides, such as chitin and chitosan, cellulose and its derivatives, such as cellulose ether and ester derivatives, alginates, starch, agarose, hyaluronic acid, and their derivatives or copolymers, and mixtures thereof.
  • Preferable nano materials are nanocelluloses such as cellulose nanocrystals or cellulose nanowhiskers or nanofibres and/or mixtures thereof.
  • Synthetically derived polymer micro- and/or nano-particles particularly suitable for carbohydrate based binders are advantageously selected from polyacrylates, polymethacrylates, polyacrylamides, polymethacrylamides, polyurethanes, polyesters, and aliphatic isocyanate oligomers, or copolymers and/or mixtures thereof.
  • the weight ratio of the matrix polymer may make up from about 1 to 20% dry weight of the binder composition, preferably from about 2 to 18% dry weight, more preferably from 5 to 15% dry weight of the composition.
  • the said matrix polymers may show a molecular weight ranging from 500 Daltons (Da) to 2 ⁇ 10 6 Da, preferably from 1 ⁇ 10 3 -5 ⁇ 10 5 Da, more preferably 5 ⁇ 10 4 Da-3 ⁇ 10 5 Da.
  • One or more pre-formed polymers, or monomers, possibly together with initiator, may be emulsion dispersed or solubilised in the binder composition.
  • the starting materials are selected from compounds bearing hydroxide functional groups and compounds bearing carboxylic acid functional groups, or anhydride or salt derivatives thereof, such that upon curing under appropriate curing conditions the desired polyester resin is obtained.
  • polyester based resins are well known in the technical field.
  • the hydroxide functional compound may be selected from carbohydrates, such as dextrose, and the compound bearing carboxylic acid functional groups, or anhydride or salt derivatives thereof, may be selected from polycarboxylic acid, anhydride or salt thereof.
  • the polycarboxylic acid may advantageously be selected from monomeric and polymeric polycarboxylic acids.
  • a monomeric polycarboxylic acid may be a dicarboxylic acid, including, but not limited to, unsaturated aliphatic dicarboxylic acids, saturated aliphatic dicarboxylic acids, aromatic dicarboxylic acids, unsaturated cyclic dicarboxylic acids, saturated cyclic dicarboxylic acids, hydroxy-substituted derivatives thereof, and the like.
  • the polycarboxylic acid(s) itself may be a tricarboxylic acid, including, but not limited to, unsaturated aliphatic tricarboxylic acids, saturated aliphatic tricarboxylic acids, aromatic tricarboxylic acids, unsaturated cyclic tricarboxylic acids, saturated cyclic tricarboxylic acids, hydroxy-substituted derivatives thereof, and the like. It is appreciated that any such polycarboxylic acids may be optionally substituted, such as with hydroxy, halo, alkyl, alkoxy, and the like. In one variation, the polycarboxylic acid is the saturated aliphatic tricarboxylic acid, citric acid.
  • polycarboxylic acids include, but are not limited to, aconitic acid, adipic acid, azelaic acid, butane tetracarboxylic acid dihydride, butane tricarboxylic acid, chlorendic acid, citraconic acid, dicyclopentadiene-maleic acid adducts, diethylenetriamine pentaacetic acid, adducts of dipentene and maleic acid, ethylenediamine tetraacetic acid (EDTA), fully maleated rosin, maleated tall-oil fatty acids, fumaric acid, glutaric acid, isophthalic acid, itaconic acid, maleated rosin oxidized with potassium peroxide to alcohol then carboxylic acid, maleic acid, malic acid, mesaconic acid, bisphenol A or bisphenol F reacted via the KOLBE-Schmidt reaction with carbon dioxide to introduce 3-4 carboxyl groups, oxalic acid, phthalic acid
  • a polymeric polycarboxylic acid may be an acid, for example, polyacrylic acid, polymethacrylic acid, polymaleic acid, and like polymeric polycarboxylic acids, copolymers thereof, anhydrides thereof, and mixtures thereof.
  • polyacrylic acids include AQUASET-529 (Rohm & Haas, Philadelphia, Pa., USA), CRITERION 2000 (Kemira, Helsinki, Finland, Europe), NF1 (H.B. Fuller, St. Paul, Minn., USA), and SOKALAN (BASF, Ludwigshafen, Germany, Europe).
  • SOKALAN this is a water-soluble polyacrylic copolymer of acrylic acid and maleic acid, having a molecular weight of approximately 4000.
  • AQUASET-529 is a composition containing polyacrylic acid cross-linked with glycerol, also containing sodium hypophosphite as a catalyst.
  • CRITERION 2000 is an acidic solution of a partial salt of polyacrylic acid, having a molecular weight of approximately 2000.
  • NF1 this is a copolymer containing carboxylic acid functionality and hydroxy functionality, as well as units with neither functionality; NF1 also contains chain transfer agents, such as sodium hypophosphite or organophosphate catalysts.
  • the polymeric polycarboxylic acid comprises an organic polymer or oligomer containing more than one pendant carboxy group.
  • the polymeric polycarboxylic acid may be a homopolymer or copolymer prepared from unsaturated carboxylic acids including, but not necessarily limited to, acrylic acid, methacrylic acid, crotonic acid, isocrotonic acid, maleic acid, cinnamic acid, 2-methylmaleic acid, itaconic acid, 2-methylitaconic acid, ⁇ , ⁇ -methyleneglutaric acid, and the like.
  • the polymeric polycarboxylic acid may be prepared from unsaturated anhydrides including, but not necessarily limited to, maleic anhydride, itaconic anhydride, acrylic anhydride, methacrylic anhydride, and the like, as well as mixtures thereof. Methods for polymerizing these acids and anhydrides are well-known in the chemical art.
  • the polymeric polycarboxylic acid may additionally comprise a copolymer of one or more of the aforementioned unsaturated carboxylic acids or anhydrides and one or more vinyl compounds including, but not necessarily limited to, styrene, a-methylstyrene, acrylonitrile, methacrylonitrile, methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, methyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, glycidyl methacrylate, vinyl methyl ether, vinyl acetate, and the like.
  • Methods for preparing these copolymers are well-known in the art.
  • the polymeric polycarboxylic acids may comprise homopolymers and copolymers of polyacrylic acid.
  • the molecular weight of the polymeric polycarboxylic acid, and in particular polyacrylic acid polymer may be is less than 10000 Da, less than 5000 Da, or about 3000 Da or less.
  • the molecular weight may be 2000 Da.
  • the carbohydrate may include one or more reactants having one or more reducing sugars.
  • any carbohydrate reactant should be sufficiently nonvolatile to maximize its ability to remain available for reaction with the amine reactant.
  • the carbohydrate reactant may be a monosaccharide in its aldose or ketose form, including a triose, a tetrose, a pentose, a hexose, or a heptose; or a polysaccharide; or combinations thereof.
  • a carbohydrate reactant may be a reducing sugar, or one that yields one or more reducing sugars in situ under thermal curing conditions.
  • an aldotriose sugar or a ketotriose sugar may be utilized, such as glyceraldehyde and dihydroxyacetone, respectively.
  • aldotetrose sugars such as erythrose and threose
  • ketotetrose sugars such as erythrulose
  • aldopentose sugars such as ribose, arabinose, xylose, and lyxose
  • ketopentose sugars such as ribulose, arabulose, xylulose, and lyxulose
  • aldohexose sugars such as glucose (i.e., dextrose), mannose, galactose, allose, altrose, talose, gulose, and idose
  • ketohexose sugars such as fructose, psicose, sorbose and tagatose
  • a ketoheptose sugar such as sedoheptulose may be utilized.
  • Other stereoisomers of such carbohydrate reactants not known to occur naturally are also contemplated to be useful in preparing the binder compositions as described herein.
  • a polysaccharide serves as the carbohydrate, or is used in combination with monosaccharides, sucrose, lactose, maltose, starch, and cellulose may be utilized.
  • the carbohydrate component may advantageously comprise oligomers or polymers that result from the hydrolysis of a polysaccharide, such as starch, cellulose or molasses.
  • a polysaccharide such as starch, cellulose or molasses.
  • Such hydrolysates are capable of generating reducing sugars in situ and/or already comprise reducing sugars and further may contribute to the effect of the matrix polymer.
  • Preferred are hydrolysates that show a DE (dextrose equivalent) of 25 to 90, preferably 35 to 85, or 45 to 85, most preferably 55 to 80.
  • the carbohydrate compound may advantageously be selected from the carbohydrates mentioned here above.
  • dextrose is the most preferred.
  • the nitrogen containing compound may advantageously be selected from ammonium salt of inorganic acids or organic acids and amine compounds.
  • the inorganic acid part of ammonium salt may advantageously be selected from phosphoric, sulphuric, nitric and carbonic acid. Ammonium sulphate and ammonium phosphate are preferred.
  • the organic acid may be selected from the polycarboxylic acids mentioned here above.
  • the amine compound may advantageously be selected from polyamine functional compounds comprising primary and/or secondary amine functional groups.
  • the polyamine is a primary polyamine.
  • the polyamine may be a molecule having the formula of H 2 N-Q-NH 2 , wherein Q is an alkyl, cycloalkyl, heteroalkyl, or cycloheteroalkyl, each of which may be optionally substituted.
  • Q is an alkyl selected from a group consisting of C 2 -C 24 .
  • Q is an alkyl selected from a group consisting of C 2 -C 8 .
  • Q is an alkyl selected from a group consisting of C 3 -C 7 .
  • Q is a C 6 alkyl.
  • Q is selected from the group consisting of a cyclohexyl, cyclopentyl or cyclobutyl.
  • Q is a benzyl.
  • the polyamine is selected from a group consisting of a di-amine, tri-amine, tetra-amine, and penta-amine.
  • the polyamine is a diamine selected from a group consisting of 1,6-diaminohexane and 1,5-diamino-2-methylpentane.
  • the di-amine is 1,6-diaminohexane.
  • the polyamine is a tri-amine selected from a group consisting of diethylenetriamine, 1-piperazineethaneamine, and bis(hexamethylene)triamine.
  • the polyamine is a tetra-amine such as triethylenetetramine.
  • the polyamine is a penta-amine, such as tetraethylenepentamine.
  • the polyamine is selected from polyethyleneimine (PEI), polyninyl amine, polyether amine, polylysine.
  • polyethylenimines As is known to the skilled person, several different types of polyethylenimines are available, such as linear polyethylenimines, branched polyethylenimines and dendrimer type polyethylenimine; all are suitable in the binder compositions of the invention.
  • polyetheramines may show a linear form and branched forms, and all are believed to be suitable for the generation of binder compositions and, hence, binders of the invention.
  • the dry weight ratio of carbohydrate to ammonium salt of inorganic or polycarboxylic acid ranges from about 2 to about 15, preferably from about 2.5 to about 13.
  • the matrix polymer may make up from about 1 to 20% dry weight of the binder composition, preferably from about 2 to 18% dry weight, more preferably from 5 to 15% dry weight of the composition.
  • binder compositions of the invention and binders produced therefrom are essentially formaldehyde-free (that is comprising less than about 1 ppm formaldehyde based on the weight of the composition) and do not liberate substantial formaldehyde. They furthermore are based on natural, hence renewable, resources.
  • the invention compositions may obviously further comprise coupling agents, dyes, antifungal agents, antibacterial agents, hydrophobes and other additives known in the art for such binder applications, as may be appropriate.
  • Silicon-containing coupling agents are typically present in such binders, generally in the range from about 0.1 to about 1% by weight based on the weight of the solids in the binder composition.
  • These additives are obviously selected such as not to antagonise the adhesive properties of the binder nor the mechanical and other desired properties of the final product comprising such binder composition or binder produced therefrom, and advantageously comply with stringent environmental and health related requirements.
  • curing generates highly crosslinked high molecular weight polymers. These may be analysed by techniques generally known in the art, including determination of molecular weight, and other known techniques.
  • binder composition is not particularly restricted and generally includes any composition which is capable of binding loosely assembled matter, either as such or upon curing.
  • aqueous is not particularly limited and generally relates to a solution and/or dispersion which is based on water as a solvent. Said term further includes compositions or mixtures which contain water and one or more additional solvents.
  • An “aqueous binder composition” of the invention may be a solution or partial solution of one or more of said binder components or may be a dispersion, such as an emulsion or suspension.
  • the solid content of the invention aqueous binder composition may range from 5 to 95 w%, advantageously from 8 to 90 w%, preferably from 10 to 85 w%, based on the weight of the total aqueous binder composition. More specifically, when used as a binder for mineral wool insulation, the solid content of the aqueous binder composition may be in the range from 5 to 25 w%, preferably from 8 to 20 w%, more preferably from 10 to 20 w% or even 12 to 18 w%, based on the weight of the total aqueous binder composition.
  • the solid content of the aqueous binder composition may range from 50 to 95 w%, preferably 50 to 90 w%, more preferably 55 to 85 w% or even 60 to 80 w%, based upon the weight of the total aqueous binder composition.
  • Binder compositions of the invention may further comprise nano-particles derived from inorganic materials such as metal-oxides, preferably MgO, CaO, Al 2 O 3 and CaCO 4 .
  • nanoclays may be incorporated in the binder formulations. Such nanoclays include, without being limited to, montmorillonite, bentonite, kaolinite, hectorite, and halloysite and other organically-modified nanoclays, and/or mixtures thereof.
  • Such inorganic materials may be present in an amount ranging from 0.1 to 10 w%, preferably 0.1 to 5 w%, of solid content of the total composition.
  • binder compositions may be transported separately and combined shortly before use in the relevant manufacturing plant. It is also possible to transport the binder composition as such.
  • the binders of the invention may be used to bond a collection of non or loosely assembled matter.
  • the collection of matter includes any collection of matter which comprises fibers selected from mineral fibers, including but not limited to slag wool fibers, stone wool fibers, glass fibers, aramid fibers, ceramic fibers, metal fibers, carbon fibers, polyimide fibers, polyester fibers, rayon fibers, and cellulosic fibers. Further examples of collection of matter include particulates such as coal, sand, cellulosic fibers, wood shavings, saw dust, wood pulp, ground wood, wood chips, wood strands, wood layers, other natural fibers, such as jute, flax, hemp, straw, wood veneers, facings and other particles, woven or non-woven materials. According to a specific embodiment of the invention, the collection of matter is selected from wood particles and mineral fibers.
  • the binder composition of the invention may be used to make insulation products, comprising mineral fibers.
  • the fibers are bonded together such that they become organized in a fiberglass mat which may then be processed into an insulation product.
  • the fibers are generally present in an amount ranging from 70 to 99%.
  • the binder may be used to bond cellulosic particles, such as cellulosic fibers, wood shavings, wood pulp and other materials commonly used to manufacture composite wood boards, including fiber boards, particle boards, oriented strand boards etc.
  • cellulosic particles such as cellulosic fibers, wood shavings, wood pulp and other materials commonly used to manufacture composite wood boards, including fiber boards, particle boards, oriented strand boards etc.
  • Such wood boards show nominal thicknesses ranging from 6 to 30 mm and a modulus of Elasticity of at least about 1000 N/mm 2 , bending strength of at least about 5 N/mm 2 and/or an internal bond strength of at least 0.10 N/mm 2 .
  • the binder content in the final wood board may range from about 5 to 30% wt with respect to the total weight of the wood board notably from 9 to 20%.
  • the aqueous binder composition may be applied in a manner known per se onto the fiber or particular material.
  • the binder composition may preferably be applied by spray application. Other techniques include roll application or mixing and/or tumbling the collection of matter with the binder composition.
  • As water evaporates the binder composition forms a gel that bonds the particulate material together when arranged into a desirable assembly as detailed further herein below.
  • the reactive binder components are caused to react to form essentially water insoluble macromolecular binder intermingled with matrix polymer. Curing thus imparts increased adhesion, durability and water resistance as compared to uncured binder. Curing may be effected at temperatures between ambient (from about 10 to 25° C.) and up to 280 ° C.
  • the invention covers a process for the preparation of a bonded assembly of fibrous materials or particulate materials by application of binder, curing and water evaporation.
  • the obtained product may then be further processed in suitable process steps to make intermediate or final products, including but not limited to insulation products.
  • a process for the manufacturing of an assembly of fibers or cellulosic particles may comprise the successive or concomitant application of the relevant components of the binder composition described here above or the application of an aqueous binder composition as previously described onto a collection of fibers or particles; the gathering of the coated fibers or particles in an assembly; and curing whereby the carbohydrate and ammonium salt components are caused to react to form a macromolecular binder, and evaporating water.
  • Curing may be effected at a temperature ranging from 90-200° C., preferably higher than 140° C., more preferably lower than 190° C., typically between 160 and 180° C. In the manufacture of wood boards, curing is performed while the material is subjected to pressing
  • FIGS. 1-3 show the cure rate of several binder compositions
  • FIG. 4 shows the bond strength before and after weathering for dextrose/ammonium sulphate/polymer based binder compositions
  • FIG. 5 shows the bond strength before and after weathering for dextrose/citric acid/polymer based binder compositions
  • FIGS. 6 and 7 show the bond strength before and after weathering for dextrose/diammonium phosphate/polymer based binder compositions.
  • the required amount of matrix polymer was dissolved in water.
  • the required amount of dextrose monohydrate (DMH) was dissolved in water separately, followed by addition of ammonium sulphate (AmSO4), diammonium phosphate (DAP) or citric acid monohydrate (CAMH) with constant stirring, as the case may be.
  • AmSO4 ammonium sulphate
  • DAP diammonium phosphate
  • APH citric acid monohydrate
  • a 50 ⁇ L sample of binder solution was dispensed onto a spot of a WhatmanTM glass microfiber filter surface. Samples were kept on the top shelf in an oven, avoiding high moisture content inside the oven during curing. For each binder solution, samples were cured for different time periods ranging from 1 minute up to 20 minutes, at different temperatures. After curing, each glass filter sample was cut and fully immersed in 50 mL cold water in a 150 mL glass beaker, and then sonicated for 15 minutes at room temperature. The extract solution was filtered and the absorbance of the extract was determined with a spectrophotometer at 470 nm. The absorbance was plotted as a function of cure time. The results of various binder compositions are presented in FIGS. 1-3 .
  • the matrix polymer addition to DMH/AmSO4 binder compositions shows no significant effect on the cure rate.
  • the addition of matrix polymer to CAMH based binder compositions ( FIG. 2 ) and DAP based binder compositions ( FIG. 3 ) accelerated curing as demonstrated in FIGS. 2 and 3 .
  • PF phenol formaldehyde
  • A4 size glass fiber veils were placed into a muffle furnace oven for 30 minutes at 600° C. in order to burnout the PF binder, and were then allowed to cool for 30 minutes. The obtained veil samples were weighted.
  • binder solution samples were poured into dip trays, and the obtained veil samples carefully fully immersed into the relevant binder solutions.
  • the impregnated veils were cured at desired temperature for desired periods of time. Binder content was then measured and bond strength determined as follows.
  • the bond strength of the relevant cured binder impregnated veils was determined by means of a testometric machine (M350-10CT). For each test a cured binder impregnated A4 veil was cut into 8 equal strips. Each strip was tested separately using a 50 Kg load cell (DBBMTCL-50 kg) at an automated test speed of 10 mm/min controlled by winTest Analysis software. Glass veil tensile plates were attached to the testometric machine in order to ensure a 100 mm gap between plates. Samples were placed vertically in the grippers; and the force was tarred to zero. Various parameters such as maximum load at peak, stress at peak and modulus (stiffness) were evaluated by the software, and data presented as an average of 8 samples with standard deviation. The average maximum load at peak or stress at peak defined as the bond strength.
  • Cured binder impregnated veils were placed in an autoclave (J8341, Vessel: PVO2626 with associated safety valve, door interlock and integrated pipework) system. Samples were treated at 90% humidity and at a temperature ranging from 40° C. to 110° C. (full cycle), at a pressure of up to 2.62 bar, for 3 hours. The samples were dried completely in order to ensure no moisture remains onto the veils. The autoclave treated samples were tested for bond strength by means of testometric machine (M350-10CT) described here above, and the results were compared with those of untreated samples.
  • M350-10CT testometric machine
  • FIG. 4 the results for the following binder compositions are shown: DMH/AmSO4/CS, DMH/AmSO4/NaCMC and DMH/AmSO4/PVA.
  • the bond strength was found to be ⁇ 66N for DMH/AmSO4 (85/15), when CS was added into the binder composition, the bond strength increased significantly. More specifically, the bond strength increased to 96N for DMH/AmSO4/CS (74/13/13) which is 45% higher bond strength as compared to that of DMH/AmSO4(85/15) binder ( FIG. 4 a ).
  • FIG. 5 shows the bond strength results of various DMH/CAMH/NaCMC binder compositions impregnated into glass fiber veils.
  • NaCMC 50% was added into the citric acid based composition
  • the bond strength increased by ⁇ 23% ( FIG. 5 ).
  • Increase of the NaCMC concentration in the binder composition does not significantly affect the bond strength.
  • FIG. 6 shows the bond strength before and after extreme weather treatment.
  • the study was performed with 7% DAP, and the ratio of DMH/polymer was varied.
  • Results indicate the bond strength of DMH/DAP (93/7) is increased by addition of CMC or CS matrix polymer. When adding more matrix polymer into the binder composition (93/7), the bond strength remains essentially steady within the range.
  • FIG. 7 shows the bond strength of DMH/DAP/Polymer compositions before and after full cycle autoclaving: (a) DMH/DAP/NaCMC, (b) DMH/DAP/PVA and (c) DMH/DAP/CS.
  • the values presented in each graph are the average values of the corresponding compositions.
  • the DAP concentration was kept constant (12-13%). Results indicate that both NaCMC and CS significantly increase the bond strength as well as improved the weather stability as compared to that of DMH/DAP (87/13).
  • Binder solutions were prepared as described above and weighted samples showing a solids content of 2-5% were poured into aluminium petri dishes and kept in an oven for 2 hours at 140° C. The theoretical and experimental values were determined and the weight loss was calculated. The results obtained for various compositions are shown in Table 1 below. As can be seen, the binder weight loss is significantly reduced with addition of matrix polymer in the compositions.
  • Binder Weight Formulations Loss (%) 85% DMH + 15% AmSO4 31.52 80% DMH + 15% AmSO4 + 5% NaCMC 22.76 75% DMH + 15% AmSO4 + 10% NaCMC 16.67 70% DMH + 15% AmSO4 + 15% NaCMC 8.46 80% DMH + 15% AmSO4 + 5% CS 26.76 80% DMH + 15% AmSO4 + 5% PVA 21.65 85% DMH + 15% CAMH 32.75 80.75% DMH + 14.25% CAMH + 5% NaCMC 23.98 80.75% DMH + 14.25% CAMH + 5% PVA 24.72 78.2% DMH + 13.8% CAMH + 8% NaCMC 23.59 78.2% DMH + 13.8% CAMH + 8% PVA 24.68 85% DMH + 15% CAMH 32.75 87% DMH + 13% DAP 32.44 80% DMH + 12% DAP + 8% NaC
  • binder solutions 100 g were prepared with desired solid content. Glass microfiber filter GFA were completely immerged and kept for 10 seconds in the relevant binder solutions, and then removed.
  • the binder impregnated GFA samples were cured at desired temperatures, e.g. at 180-190° C. for 10 minutes, and the weight was measured (4 decimal point). Thereafter, the cured GFA samples were fully immerged into a beaker filled with 200 mL water. The samples were maintained for 1 hour under water by means of a glass rod. After 1 hour, the GFA samples were withdrawn and the surface water was absorbed by absorbent paper. The weight of the wet GFA sample was measured. The percentage of water absorption was determined for each sample in three replicates according to the following relationship.
  • Table 2 represents water absorption (%) for various compositions of DMH/AmSO4/Polymer, DMH/CAMH/Polymer and DMH/DAP/Polymer, with and without additive (silicone). It can be seen that water absorption is about 247% for standard known DMH/AmSO4 (85/15) binder. With the addition of matrix polymer such as NaCMC and CS the water absorption is significantly reduced, depending on the type and ratio of the matrix polymer used in the formulation. The addition of silicone (1% or 1.5%) in the composition further reduces water absorption significantly.
  • matrix polymer such as NaCMC and CS
  • Binder solutions comprising 2% solids were prepared according to the method disclosed above and showed the compositions indicated in the tables below. Bond strength of weathered and unweathered veils impregnated with the relevant binder compositions and cured for 8 minutes at 200° C. were measured as disclosed above. The results are summarized in the tables below, averaged over 8 replicates.
  • binder compositions comprising 2% solids.
  • the compositions are shown in the tables below and comprise a polyazetidinium (CA1025) as polymer matrix. Bond strength of weathered and unweathered veils impregnated with the relevant binder compositions and cured for 8 minutes at 200° C. were measured as disclosed above. The results are summarized in Table 6 below, averaged over 8 replicates.
  • Aspect 4 The aqueous curable binder composition of aspect 4 wherein the polycarboxylic acid component is a monomeric polycarboxylic acid, such as dicarboxylic acid, including, but not limited to, unsaturated aliphatic dicarboxylic acids, saturated aliphatic dicarboxylic acids, aromatic dicarboxylic acids, unsaturated cyclic dicarboxylic acids, saturated cyclic dicarboxylic acids, hydroxy-substituted derivatives thereof, or, tricarboxylic acid, including, but not limited to, unsaturated aliphatic tricarboxylic acids, saturated aliphatic tricarboxylic acids, aromatic tricarboxylic acids, unsaturated cyclic tricarboxylic acids, saturated cyclic tricarboxylic acids, hydroxy-substituted derivatives thereof, preferably citric acid, and mixtures thereof.
  • dicarboxylic acid including, but not limited to, unsaturated aliphatic dicarboxylic
  • Aspect 9 The aqueous curable binder composition of any of aspects 7 or 8 wherein the nitrogen containing component is an ammonium salt of an inorganic acid, selected from phosphoric, sulphuric, nitric and carbonic acid, preferably ammonium sulphate or ammonium phosphate.
  • the nitrogen containing component is an ammonium salt of an inorganic acid, selected from phosphoric, sulphuric, nitric and carbonic acid, preferably ammonium sulphate or ammonium phosphate.
  • Aspect 10 The aqueous curable binder composition of any of aspects 7 or 8 wherein the nitrogen containing component is selected from polyamine functional compounds comprising primary and/or secondary and/or tertialy and/or quaternary amine functional groups.
  • Aspect 11 The aqueous curable binder composition of any of aspect 10 wherein the polyamine functional compound has the formula of H 2 N-Q-NH 2 , wherein Q is an alkyl, cycloalkyl, heteroalkyl, or cycloheteroalkyl, each of which optionally substituted.
  • Aspect 12 The aqueous curable binder composition of aspect 11 wherein the polyamine functional compound is selected from di-amine, tri-amine, tetra-amine, and penta-amine, more specifically 1,6-diaminohexane and 1,5-diamino-2-methylpentane, diethylenetriamine, 1-piperazine-ethaneamine, and bis(hexamethylene)triamine, triethylenetetramine, tetraethylenepentamine, polyethyleneimine (PEI), polyninyl amine, polyether amine, polylysine.
  • the polyamine functional compound is selected from di-amine, tri-amine, tetra-amine, and penta-amine, more specifically 1,6-diaminohexane and 1,5-diamino-2-methylpentane, diethylenetriamine, 1-piperazine-ethaneamine, and bis(hexamethylene)triamine, triethylenetetramine, tetraethylenepentamine, polyethyleneimine
  • Aspect 13 The aqueous curable binder composition of any of the preceding aspects wherein the matrix polymer is selected from naturally derived polymers, such as polysaccharides, such as cellulose, starch, alginate, hyaluronic acid, and their derivatives, carboxymethyl cellulose (CMC), hydroxypropyl cellulose (HPC), 2-hydroxyethyl cellulose (HEC), synthetically derived polymers, such as polyvinyls (PVA, PVAc, PAN), polyacrylics, polyacrylate, polymethacrylate, polyacrylamide, polymethacrylamides, polyurethanes, polyesters, aliphatic isocyanate oligomers, polyazetidinium, copolymers thereof and mixtures thereof.
  • naturally derived polymers such as polysaccharides, such as cellulose, starch, alginate, hyaluronic acid, and their derivatives, carboxymethyl cellulose (CMC), hydroxypropyl cellulose (HPC), 2-hydroxye
  • Aspect 14 The aqueous curable binder composition of aspect 13 wherein the matrix polymer is selected from cellulose derivatives, such as carboxymethyl cellulose (CMC), hydroxypropyl cellulose (HPC), 2-hydroxyethyl cellulose (HEC); polyvinyl acetate (PVAc), aliphatic isocyanate oligomers, or mixtures thereof.
  • CMC carboxymethyl cellulose
  • HPC hydroxypropyl cellulose
  • HEC 2-hydroxyethyl cellulose
  • PVAc polyvinyl acetate
  • aliphatic isocyanate oligomers or mixtures thereof.
  • Aspect 15 The aqueous curable binder composition of any of the preceding aspects wherein the matrix polymer shows a molecular weight ranging from 500 Daltons (Da) to 2 ⁇ 10 6 Da, preferably from 1 ⁇ 10 3 -5 ⁇ 10 5 Da, more preferably from 5 ⁇ 10 4 Da-3 ⁇ 10 5 Da.
  • Aspect 17 The aqueous curable binder composition of aspect 16 wherein the matrix polymer makes up from about 1 to 20% of the dry weight of the binder composition, preferably from about 2 to 18% dry weight, more preferably from 5 to 15% dry weight of the composition.
  • Aspect 18 The aqueous curable binder composition of any of the preceding aspects further comprising dyes, antifungal agents, antibacterial agents, hydrophobes, silicone containing coupling agents and/or other additives known in the art for such binder compositions.
  • Aspect 19 The aqueous binder composition of any of the preceding aspects wherein a component is selected micro-/or nano-particles derived from natural or synthetic polymers of their combination such as nanocelluloses, or from inorganic materials such as MgO, CaO, Al 2 O 3 and CaCO 4 , or nanoclays such as montmorillonite, bentonite, kaolinite, hectorite, and halloysite and other organically-modified nanoclays, and/or mixtures thereof.
  • a component is selected micro-/or nano-particles derived from natural or synthetic polymers of their combination such as nanocelluloses, or from inorganic materials such as MgO, CaO, Al 2 O 3 and CaCO 4 , or nanoclays such as montmorillonite, bentonite, kaolinite, hectorite, and halloysite and other organically-modified nanoclays, and/or mixtures thereof.
  • Aspect 20 An assembly of fibers or particles bonded with an aqueous curable binder composition according to any of the preceding aspects or with a binder resulting from the curing of any of the curable binder compositions of the preceding aspects.
  • Aspect 21 The assembly of fibers according to aspect 20 being an insulation product, such as a mineral wool mat or other.
  • Aspect 22 The assembly of particles according to aspect 20 being a composite wood board, such as wood fiber board, wood particle board, plywood or similar board.
  • a process for the manufacturing of an assembly of fibers or particles according to any of aspects 20-22 characterized in that it comprises the successive or concomitant application of the relevant components of the aqueous curable binder composition of any of aspects 1-19, or the application of an aqueous binder composition according to any of aspects 1 to 19 onto a collection of fibers or particles; the gathering of the coated fibers or particles in an assembly; and curing, whereby the components of the aqueous curable binder composition are caused to react to form a macromolecular binder, and evaporating water.
  • Aspect 24 The process according to aspect 23 characterized in that curing is performed at a temperature ranging from 120° C.-200° C., preferably higher than 140° C., more preferably lower than 190° C., typically between 160 and 180° C.
  • Aspect 25 The process according to any of aspects 23-24 characterized in that the aqueous binder composition is applied by spraying onto the collection of fibers or particles.
  • Aspect 26 The process of any of aspects 23 to 25 wherein the assembly is a wood fiber board or wood particle board or similar wood board, subjected to pressing during curing.
US15/326,532 2014-07-17 2015-07-17 Improved binder compositions and uses thereof Abandoned US20170210952A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
GBGB1412709.6A GB201412709D0 (en) 2014-07-17 2014-07-17 Improved binder compositions and uses thereof
GB1412709.6 2014-07-17
PCT/EP2015/066455 WO2016009062A1 (en) 2014-07-17 2015-07-17 Improved binder compositions and uses thereof

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2015/066455 A-371-Of-International WO2016009062A1 (en) 2014-07-17 2015-07-17 Improved binder compositions and uses thereof

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US202015931565A Continuation 2014-07-17 2020-05-13

Publications (1)

Publication Number Publication Date
US20170210952A1 true US20170210952A1 (en) 2017-07-27

Family

ID=51494741

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/326,532 Abandoned US20170210952A1 (en) 2014-07-17 2015-07-17 Improved binder compositions and uses thereof
US17/498,146 Pending US20220098452A1 (en) 2014-07-17 2021-10-11 Binder compositions and uses thereof

Family Applications After (1)

Application Number Title Priority Date Filing Date
US17/498,146 Pending US20220098452A1 (en) 2014-07-17 2021-10-11 Binder compositions and uses thereof

Country Status (14)

Country Link
US (2) US20170210952A1 (ko)
EP (1) EP3169741B1 (ko)
JP (1) JP2017531048A (ko)
KR (1) KR102542973B1 (ko)
CN (2) CN112662339A (ko)
AU (1) AU2015289030B2 (ko)
CA (1) CA2954960C (ko)
DK (1) DK3169741T3 (ko)
GB (1) GB201412709D0 (ko)
MX (1) MX2017000726A (ko)
PL (1) PL3169741T3 (ko)
RU (1) RU2694345C2 (ko)
SI (1) SI3169741T1 (ko)
WO (1) WO2016009062A1 (ko)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019121713A1 (en) * 2017-12-19 2019-06-27 Knauf Insulation Sprl Mineral fiber based composites
US10988588B2 (en) 2016-01-28 2021-04-27 Ursa Insulation, S.A. Curable resin for mineral wool
US11111372B2 (en) 2017-10-09 2021-09-07 Owens Corning Intellectual Capital, Llc Aqueous binder compositions
US11136451B2 (en) 2017-10-09 2021-10-05 Owens Corning Intellectual Capital, Llc Aqueous binder compositions
US11248108B2 (en) * 2017-01-31 2022-02-15 Knauf Insulation Sprl Binder compositions and uses thereof
CN114921071A (zh) * 2022-03-13 2022-08-19 宁波大学 一种抗菌纳米纤维素/phbv复合材料及其制备方法
WO2023114146A3 (en) * 2021-12-14 2023-08-03 Sanford, L.P. Kits and molds for preparing cured articles
US11813833B2 (en) 2019-12-09 2023-11-14 Owens Corning Intellectual Capital, Llc Fiberglass insulation product
US11976168B2 (en) * 2020-12-23 2024-05-07 Basf Se Binder composition comprising poly(amino acid)s for fiber composite articles

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB201519187D0 (en) * 2015-10-30 2015-12-16 Knauf Insulation Ltd Improved binder compositions and uses thereof
GB201609616D0 (en) * 2016-06-02 2016-07-20 Knauf Insulation Ltd Method of manufacturing composite products
KR101922644B1 (ko) 2017-04-13 2018-11-27 씨제이제일제당 주식회사 바인더 조성물, 물품 및 물품 제조방법
US11214714B2 (en) * 2018-05-08 2022-01-04 Iowa State University Research Foundation, Inc. Thermoplastic poly acrylated glycerol adhesives useful in cellulosic products
CN108729308B (zh) * 2018-06-11 2020-02-11 杭州西红柿环保科技有限公司 一种纸浆模塑产品及其制备方法
CN109207070B (zh) * 2018-11-07 2020-12-04 深圳市浩力新材料技术有限公司 一种高耐水性的丙烯酸酯胶黏剂及其制备方法
CN110394869B (zh) * 2019-05-23 2020-11-20 山东省工艺美术研究所 一种桃木除胶除虫防裂防变形的木材处理技术工艺
EP4010425A4 (en) * 2019-07-29 2023-09-20 LRBG Chemicals Inc. BINDER FOR INSULATING AND NON-WOVEN MATS
WO2022096518A1 (en) 2020-11-05 2022-05-12 Covestro (Netherlands) B.V. Compositions suitable for enhancing the flexural properties of objects containing vegetable fibers
CA3203217A1 (en) * 2020-12-23 2022-06-30 Gereon Antonius SOMMER Binder composition comprising polyamine(s) and hydroxyacetone for composite articles
CA3203220A1 (en) 2020-12-23 2022-06-30 Gereon Antonius SOMMER Binder composition comprising amino acid polymer(s) as well as carbohydrates for composite articles
CN117529393A (zh) 2021-06-07 2024-02-06 巴斯夫欧洲公司 生产木质纤维素复合材料的方法、相应的木质纤维素复合材料及其用途
CN113351610A (zh) * 2021-06-24 2021-09-07 扬州杰嘉工业固废处置有限公司 工业废盐渣固化成型及填埋处置方法
KR102561168B1 (ko) * 2021-08-27 2023-07-31 벽산페인트 주식회사 친환경 단열재용 바인더 조성물 및 그의 제조방법
WO2024008939A1 (en) 2022-07-08 2024-01-11 Covestro (Netherlands) B.V. Compositions for fibreboards with enhanced properties upon fast-curing at low temperature
WO2024008938A1 (en) 2022-07-08 2024-01-11 Covestro (Netherlands) B.V. Compositions for fibreboards with enhanced properties upon fast-curing at low temperature
WO2024008940A1 (en) 2022-07-08 2024-01-11 Covestro (Netherlands) B.V. Compositions for fibreboards with enhanced properties upon fast-curing at low temperature
WO2024038152A1 (en) 2022-08-19 2024-02-22 Covestro (Netherlands) B.V. Compositions for fibreboards with enhanced properties upon fast-curing at low temperature
WO2024038153A1 (en) 2022-08-19 2024-02-22 Covestro (Netherlands) B.V. Compositions for fibreboards with enhanced properties upon fast-curing at low temperature
WO2024074400A1 (en) 2022-10-05 2024-04-11 Basf Se Foam based on polylysine
WO2024074399A1 (en) 2022-10-05 2024-04-11 Basf Se In-situ foam based on polylysine
WO2024088944A1 (en) 2022-10-28 2024-05-02 Basf Se Process of producing a lignocellulosic composite and corresponding binder composition, lignocellulosic composite, kit and use
ES2955862A1 (es) * 2023-06-06 2023-12-07 Parrotecnic S L Composicion liquida en forma de dispersion acuosa de polimerizado, uso de dicha composicion como agente ligante y agente de revestimiento con dicho agente ligante

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5905115A (en) * 1996-10-29 1999-05-18 Cooperatieve Weiproduktenfabriek "Borculo" W. A. Sugar amines and sugar amides and use as glues
US7026390B2 (en) * 2002-12-19 2006-04-11 Owens Corning Fiberglas Technology, Inc. Extended binder compositions
US20090275699A1 (en) * 2008-05-05 2009-11-05 Mingfu Zhang Starch containing formaldehyde-free thermoset binders for fiber products
US20100087571A1 (en) * 2007-01-25 2010-04-08 Roger Jackson Composite wood board
US20110040010A1 (en) * 2009-08-11 2011-02-17 Kiarash Alavi Shooshtari Curable fiberglass binder comprising salt of inorganic acid
US20120135152A1 (en) * 2010-11-30 2012-05-31 William Christopher Finch Stable reactive thermosetting formulations of reducing sugars and amines
US20120156954A1 (en) * 2009-08-11 2012-06-21 Bernhard Eckert Curable fiberglass binder
FR2982268A1 (fr) * 2011-11-07 2013-05-10 Knauf Insulation Liants et materiaux qui en decoulent
US20140033950A1 (en) * 2012-08-03 2014-02-06 Ecosynthetix Ltd. Bio-based binder and fiberglass insulation
EP2730689A1 (en) * 2012-11-13 2014-05-14 Johns Manville Viscosity modified formaldehyde-free binder compositions
US20150159000A1 (en) * 2013-12-11 2015-06-11 Rohm And Haas Company Aqueous compositions of polyaldehydes from the oxidation of polysaccharides and their thermosets
US9242899B2 (en) * 2012-06-29 2016-01-26 Ursa Insulation, S.A. Formaldehyde-free binder and use for mineral wool insulation products
US10047210B2 (en) * 2011-04-07 2018-08-14 Owens Corning Intellectual Capital, Llc Bio-based binders including carbohydrates and a pre-reacted product of an alcohol or polyol and a monomeric or polymeric polycarboxylic acid

Family Cites Families (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3554788A (en) * 1968-10-09 1971-01-12 Johnson & Johnson Water dispersible nonwoven fabric
US5346541A (en) * 1992-11-18 1994-09-13 Net/Tech International, Inc. Water dispersible formulations and materials and methods for influencing their water dispersibility
DE69718850T2 (de) * 1996-06-28 2003-10-09 Dow Agrosciences Llc Heterocyclische N-Acetonylbenzamide und ihre Verwendung als Fungizide
ES2189225T3 (es) 1997-07-17 2003-07-01 Henkel Kgaa Aglomerados para la obtencion de un sistema de agente aglutinante acuoso.
US5895804A (en) 1997-10-27 1999-04-20 National Starch And Chemical Investment Holding Corporation Thermosetting polysaccharides
US6818694B2 (en) 2002-10-10 2004-11-16 Johns Manville International, Inc. Filler extended fiberglass binder
US20040254285A1 (en) 2003-06-12 2004-12-16 Rodrigues Klein A. Fiberglass nonwoven binder
DE102004011231A1 (de) * 2004-01-27 2005-08-11 Wtb Biotech Gmbh Mehrkomponenten-Bindemittel und dessen Verwendung
WO2005061647A1 (de) 2003-12-19 2005-07-07 Wtb Biotech Gmbh Mehrkomponenten-bindemittel und deren verwendung
US20050215153A1 (en) 2004-03-23 2005-09-29 Cossement Marc R Dextrin binder composition for heat resistant non-wovens
ES2732298T3 (es) 2005-07-26 2019-11-21 Knauf Insulation Gmbh Un método de fabricación de productos de aislamiento de fibra de vidrio
US9217065B2 (en) 2006-06-16 2015-12-22 Georgia-Pacific Chemicals Llc Binder compositions for making fiberglass products
WO2008127936A2 (en) * 2007-04-13 2008-10-23 Knauf Insulation Gmbh Composite maillard-resole binders
GB0715100D0 (en) * 2007-08-03 2007-09-12 Knauf Insulation Ltd Binders
DE102007060494A1 (de) 2007-12-14 2009-06-18 Johns Manville Europe Gmbh Trägereinlage, Verfahren zu deren Herstellung und deren Verwendung
DE102008059128A1 (de) 2008-11-26 2010-05-27 Johns Manville Europe Gmbh Binderverfestigtes, textiles Flächengebilde, Verfahren zu dessen Herstellung und dessen Verwendung
EP2223940B1 (en) * 2009-02-27 2019-06-05 Rohm and Haas Company Polymer modified carbohydrate curable binder composition
EP2223941B1 (en) * 2009-02-27 2018-10-17 Rohm and Haas Company Rapid cure carbohydrate composition
EP2230222A1 (en) 2009-03-19 2010-09-22 Rockwool International A/S Aqueous binder composition for mineral fibres
EP2464772B2 (en) 2009-08-11 2020-12-02 Johns Manville Curable fiberglass binder comprising amine salt of inorganic acid
FI20096036A0 (fi) 2009-10-08 2009-10-08 Upm Kymmene Wood Oy Bioliima ja puulevy
CA2777078C (en) 2009-10-09 2017-11-21 Owens Corning Intellectual Capital, Llc Bio-based binders for insulation and non-woven mats
WO2011138458A1 (en) 2010-05-07 2011-11-10 Knauf Insulation Carbohydrate polyamine binders and materials made therewith
US8845851B2 (en) 2010-05-26 2014-09-30 Solenis Technologies, L.P. Protein adhesive formulations with amine-epichlorohydrin and isocyanate additives
JP5879521B2 (ja) 2011-03-31 2016-03-08 パナソニックＩｐマネジメント株式会社 接着用組成物
FR2976582B1 (fr) 2011-06-17 2014-12-26 Saint Gobain Isover Composition d'encollage pour laine minerale a faible emission de composes organiques volatils, et produits isolants obtenus.
FR2978768B1 (fr) 2011-08-05 2014-11-28 Saint Gobain Isover Composition d'encollage pour laine minerale a base de saccharide reducteur et de saccharide hydrogene, et produits isolants obtenus
EP2669349B1 (en) 2012-05-29 2014-06-04 Rohm and Haas Company Aqueous amine-carbohydrate thermosets having reduced weight loss upon cure and improved early dry strength
US10208414B2 (en) * 2012-11-13 2019-02-19 Johns Manville Soy protein and carbohydrate containing binder compositions
EP2928936B1 (en) * 2012-12-05 2022-04-13 Knauf Insulation SPRL Binder
EP3221412A4 (en) 2014-11-19 2018-07-18 Dow Global Technologies LLC Binder composition and paint formulation made thereof

Patent Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5905115A (en) * 1996-10-29 1999-05-18 Cooperatieve Weiproduktenfabriek "Borculo" W. A. Sugar amines and sugar amides and use as glues
US7026390B2 (en) * 2002-12-19 2006-04-11 Owens Corning Fiberglas Technology, Inc. Extended binder compositions
US20100087571A1 (en) * 2007-01-25 2010-04-08 Roger Jackson Composite wood board
US20090275699A1 (en) * 2008-05-05 2009-11-05 Mingfu Zhang Starch containing formaldehyde-free thermoset binders for fiber products
US20120156954A1 (en) * 2009-08-11 2012-06-21 Bernhard Eckert Curable fiberglass binder
US20110040010A1 (en) * 2009-08-11 2011-02-17 Kiarash Alavi Shooshtari Curable fiberglass binder comprising salt of inorganic acid
US20120135152A1 (en) * 2010-11-30 2012-05-31 William Christopher Finch Stable reactive thermosetting formulations of reducing sugars and amines
US10047210B2 (en) * 2011-04-07 2018-08-14 Owens Corning Intellectual Capital, Llc Bio-based binders including carbohydrates and a pre-reacted product of an alcohol or polyol and a monomeric or polymeric polycarboxylic acid
FR2982268A1 (fr) * 2011-11-07 2013-05-10 Knauf Insulation Liants et materiaux qui en decoulent
US9242899B2 (en) * 2012-06-29 2016-01-26 Ursa Insulation, S.A. Formaldehyde-free binder and use for mineral wool insulation products
US20140033950A1 (en) * 2012-08-03 2014-02-06 Ecosynthetix Ltd. Bio-based binder and fiberglass insulation
EP2730689A1 (en) * 2012-11-13 2014-05-14 Johns Manville Viscosity modified formaldehyde-free binder compositions
US20140134909A1 (en) * 2012-11-13 2014-05-15 Johns Manville Viscosity modified formaldehyde-free binder compositions
US20150159000A1 (en) * 2013-12-11 2015-06-11 Rohm And Haas Company Aqueous compositions of polyaldehydes from the oxidation of polysaccharides and their thermosets

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10988588B2 (en) 2016-01-28 2021-04-27 Ursa Insulation, S.A. Curable resin for mineral wool
US11248108B2 (en) * 2017-01-31 2022-02-15 Knauf Insulation Sprl Binder compositions and uses thereof
US11111372B2 (en) 2017-10-09 2021-09-07 Owens Corning Intellectual Capital, Llc Aqueous binder compositions
US11136451B2 (en) 2017-10-09 2021-10-05 Owens Corning Intellectual Capital, Llc Aqueous binder compositions
WO2019121713A1 (en) * 2017-12-19 2019-06-27 Knauf Insulation Sprl Mineral fiber based composites
US11795278B2 (en) 2017-12-19 2023-10-24 Knauf Insulation Sprl Mineral fiber based composites
US11813833B2 (en) 2019-12-09 2023-11-14 Owens Corning Intellectual Capital, Llc Fiberglass insulation product
US11976168B2 (en) * 2020-12-23 2024-05-07 Basf Se Binder composition comprising poly(amino acid)s for fiber composite articles
WO2023114146A3 (en) * 2021-12-14 2023-08-03 Sanford, L.P. Kits and molds for preparing cured articles
CN114921071A (zh) * 2022-03-13 2022-08-19 宁波大学 一种抗菌纳米纤维素/phbv复合材料及其制备方法

Also Published As

Publication number Publication date
MX2017000726A (es) 2017-05-01
JP2017531048A (ja) 2017-10-19
RU2694345C2 (ru) 2019-07-11
CA2954960C (en) 2022-12-06
CN112662339A (zh) 2021-04-16
DK3169741T3 (da) 2023-01-09
RU2017105098A3 (ko) 2019-01-28
AU2015289030B2 (en) 2018-09-13
CN106536660A (zh) 2017-03-22
KR102542973B1 (ko) 2023-06-14
EP3169741A1 (en) 2017-05-24
AU2015289030A1 (en) 2017-02-02
SI3169741T1 (sl) 2023-03-31
PL3169741T3 (pl) 2023-06-19
WO2016009062A1 (en) 2016-01-21
EP3169741B1 (en) 2022-11-02
CA2954960A1 (en) 2016-01-21
KR20170052566A (ko) 2017-05-12
GB201412709D0 (en) 2014-09-03
US20220098452A1 (en) 2022-03-31
RU2017105098A (ru) 2018-08-17

Similar Documents

Publication Publication Date Title
US20220098452A1 (en) Binder compositions and uses thereof
JP2017531048A5 (ko)
AU2019203797B2 (en) Improved binder compositions and uses thereof
JP2017528551A5 (ko)
ES2704135T3 (es) Composición de carbohidratos de curado rápido
US11879063B2 (en) Binder compositions and uses thereof
BRPI1107078A2 (pt) composição de aglutinante de termocura aquosa, estável, e, método para usar a composição de aglutinante de termocura aquosa estável
EP3034555B1 (en) Curable formaldehyde-free resin dispersion and improved mineral wool products produced therewith
US10988588B2 (en) Curable resin for mineral wool

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STCV Information on status: appeal procedure

Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED

STCV Information on status: appeal procedure

Free format text: ON APPEAL -- AWAITING DECISION BY THE BOARD OF APPEALS

STCV Information on status: appeal procedure

Free format text: BOARD OF APPEALS DECISION RENDERED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION