US20170130123A1 - Proppant Material Incorporating Fly Ash and Method of Manufacture - Google Patents

Proppant Material Incorporating Fly Ash and Method of Manufacture Download PDF

Info

Publication number
US20170130123A1
US20170130123A1 US15/409,782 US201715409782A US2017130123A1 US 20170130123 A1 US20170130123 A1 US 20170130123A1 US 201715409782 A US201715409782 A US 201715409782A US 2017130123 A1 US2017130123 A1 US 2017130123A1
Authority
US
United States
Prior art keywords
fly ash
proppant
bauxite
granules
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/409,782
Inventor
Ralph Enderle
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Enderle Ralph Dr
Original Assignee
EPROPP LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EPROPP LLC filed Critical EPROPP LLC
Priority to US15/409,782 priority Critical patent/US20170130123A1/en
Assigned to EPROPP, LLC reassignment EPROPP, LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ENDERLE, RALPH
Priority to US15/488,631 priority patent/US20170226410A1/en
Publication of US20170130123A1 publication Critical patent/US20170130123A1/en
Assigned to Enderle, Ralph, Dr. reassignment Enderle, Ralph, Dr. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: EPROPP, LLC
Abandoned legal-status Critical Current

Abstract

A relatively low density, high strength round proppant material having (i) a round core made of a sintered mixture of fly ash and clay or, in same instances, fly ash, clay, and bauxite; and (ii) an outer shell made of sintered bauxite, and a method of making the same.

Description

    FIELD
  • Embodiments described herein generally relate to proppant materials which may be used in hydraulic fracturing operations in oil and gas wells, and methods of manufacturing the same.
  • Hydraulic fracturing is the fracturing of various rock layers by a pressurized liquid. This is useful in oil and gas operations, as the fractures created by the hydraulic fracturing can serve as enhanced flow paths to the well for oil or gas trapped in rock formations. However, once the fractures have been created, they must be “propped” open by some means because otherwise the fractures will close when the pressure from the high pressure liquid used to create the fractures is relieved.
  • Crush resistant particles, referred to as “proppant”, may be pumped into the fractures after they have been created to hold the fractures open. It is desirable that such proppant materials be both very crush resistant (so that the forces exerted on them by the fractures as they try to close do not crush them, which would permit the fractures to close) and have a relatively low specific gravity (so that they may be transported easily into the fractures by a fluid pumped into the well). These two properties often can be somewhat at odds with each other, because an increase in crush resistance typically tends to result in a material being more dense.
  • Because proppant materials typically are sold by weight rather than by volume, a proppant material having a relatively low density will actually have a lower effective cost to the user even if it is sold at the same price per pound as a more dense proppant material
  • It is also desirable that the proppant particles be relatively spherical to maximize the spaces between proppant particles and the ease with which fluids will flow through such spaces. Depending on the proppant material, crushing of proppant particles can result in the creation of many very fine particles which could block some of the spaces between the remaining larger proppant particles, reducing the ability of fluids to flow through those spaces. Accordingly, it is desirable that, when the crush strength of the proppant material is exceeded, the proppant particles break into a few relatively large fragments rather than become pulverized.
  • Depending on the application, different sizes of proppant particles may be used, although it is desirable that the proppant particles be of a relatively uniform size.
  • Bauxite is a common aluminum ore. Bauxite is composed primarily of one or more aluminum hydroxide minerals, plus various mixtures of silica (SiO2), iron oxide, titania (TiO2), aluminosilicate, and other impurities in minor amounts. Sintered bauxite has been used in the past as a proppant material because particles made essentially from bauxite, when sintered, form a relatively hard, crush resistant material. However, bauxite has a relatively high specific gravity and sintered bauxite is considered a relatively heavy-weight (i.e., higher density) ceramic proppant material. Moreover, the quality requirements for bauxite used to make a sintered bauxite proppant material are very strict. There are only a relatively few sources of bauxite that are suitable for producing a sintered bauxite proppant material because of the impurities present in most bauxites.
  • The present invention relates to lighter weight (i.e., lower density) ceramic proppant materials made containing a substantial proportion of fly ash. Fly ash comprises the fine particles that rise with the flue gases, and in industrial applications usually refers to ash particles produced during the combustion of coal. The components of fly ash vary considerably, but all fly ash includes substantial amounts of silicon dioxide (SiO2) and, in some cases, substantial amounts of calcium oxide (CaO) and/or ferric oxide (Fe2O3), which are components of many coal-bearing rock strata. Other components of the fly ash depend upon the specific coal bed makeup.
  • An advantage of using fly ash in the present application is that it has a relatively low density compared to bauxite (the specific gravity of bauxite may vary from about 2.5 to 3.5, depending on its specific composition, while the specific gravity of fly ash may vary from about 2.0 to 2.5).
  • Moreover, disposal of the fly ash has become an increasing problem with significant environmental implications, making opportunities for the recycling of fly ash desirable. Currently, most fly ash produced from coal-fired power stations is disposed of in landfills and ash ponds. The single largest recycling use at present for fly ash is to replace a portion of the Portland cement content in concrete. The present invention permits recycling of fly ash waste into a material that is useful in hydraulic fracturing operations in oil and gas wells.
  • Moreover, while the quality requirements for bauxite used to make a sintered bauxite proppant material are very strict, the bauxite used in the present invention need not be of such a high quality.
  • The proppant materials associated with this invention have relatively high crush resistance and relatively low density, and are relatively inexpensive. In addition, when a proppant particle associated with this invention fails, it tends to fracture into a relative few, large pieces rather than become pulverized.
  • DESCRIPTION OF RELATED ART
  • White fly ash has been proposed to be used to make an aggregate material for use in concrete or building materials as a component of a proppant material, past efforts to make a commercially successful ceramic proppant material containing a significant amount of fly ash have failed. The aggregate formed by sintering briquettes of fly ash containing materials and then crushing the briquettes and screening the crushed particles to obtain suitable sized particles is not be satisfactory for use as a proppant material. The shapes of the particles formed by crushing are so irregular that they are not sufficiently spherical to make a good proppant material and the irregular shapes of the particles also reduces their crush resistance.
  • A particle which is suitably crush resistant to serve as a proppant may be made by sintering spherical granules formed from a mixture of fly ash, bauxite, and clay. However, to obtain the desired degree of crush resistance, the sintering step typically must be performed at a temperature above what will typically cause such granules to become very sticky as a result of melting of some of the components of the materials in the mixture, particularly one or more of the components of (including impurities in) the fly ash. If the granules become too sticky during the sintering step, they will agglomerate, which results in a poor yield of uniformly sized particles of a specific size. Moreover, excessive stickiness will cause the granules to adhere to the kiln in which they are being sintered, reducing the yield and damaging the kiln.
  • U.S. Pat. No. 7,828,998 discloses making proppant from granules made from kaolinite, bauxite, fly ash, and combinations thereof. However, in U.S. Pat. No. 7,828,998, the granules are heated initially under reducing conditions so that at least part of the metal oxide dopant is reduced to form a metastable, transient liquid phase among the particles. This liquid phase includes at least part of the reduced metal oxide dopant, promotes sintering among the particles, and forms islands of reduced metal oxide dopant within and on the surface of the granules. Following the heating under reducing conditions, the granules are heated under oxidizing conditions such that the islands of reduced metal oxide are oxidized and/or go into solid solution within the particles, thereby creating voids within and forming a metal or metal oxide shell on the granules.
  • The present invention does not require heating the granules under reducing conditions followed by heating the granules under oxidizing conditions. Instead, the granules are treated prior to heating in a manner that obviates the stickiness problem otherwise encountered when heating the granules to the required sintering temperature.
  • Other prior art has created relatively low density proppant materials which required the use of nano-scale raw materials. The present invention does not require the use of raw materials smaller than d90<10μ (90% of the particles are less than 10μ in size), Using feedstocks with a nano-scale particle size greatly increases the cost of the feedstocks and the finished product to non-economic levels.
  • SUMMARY
  • The invention relates to a method of manufacturing a proppant material, in which the fly ash is a significant component of the final product, preferably the primary component of the proppant material. The proppant material has a core comprising fly ash, bauxite, and clay, or in some instances fly ash and clay. To prevent excessive stickiness on the surface of the granules when heated to sintering temperatures, the core granules (which contain a substantial amount of fly ash) are coated with bauxite. In certain embodiments, the core granules receive multiple coatings of bauxite, which improves adherence of the coating to the core granule as compared to a particle given a single-layer coating. In other embodiments, the core granules are coated with one or more layers of bauxite, but the application of the bauxite is in the form of a powdered bauxite slurry, in which the powdered bauxite is mixed with a carrier liquid, such as water or another suitable carrier liquid. In yet other embodiments, the powdered bauxite slurry includes both water and a binder. In some embodiments, the binder is polyvinyl alcohol (“PVA”), which acts as both an emulsifier and a binder.
  • The coated granules are then heated to a calcination temperature to remove the water and other volatile materials otherwise contained in the granules. After calcination, the granules are heated to a sintering temperature to form high strength ceramic proppant particles having a relatively low density.
  • DETAILED DESCRIPTION
  • To form a high strength proppant material having a relatively low density, a spherical granule is formed from a combination of fly ash, clay, and bauxite. While the descriptive term “spherical” is used herein, it is understood that the granules formed will not necessarily be perfect spheres, but instead will be sphere-like, i.e., well rounded with the major and minor axes of the granule be approximately the same, but not necessarily exactly the same. In other words, the “spheres” may be slightly elliptical or otherwise deviate from being perfect spheres, but will be very rounded and approximate spheres.
  • The clay acts as a plasticizer to promote formation of the desired granules and provide them with a measure of physical stability prior to the sintering of the granule. In the embodiments discussed in detail below, kaolin clay is used; but it is understood that illite or other clay materials with suitable characteristics may be used.
  • It is understood that the composition of the raw materials, including the nature and the amounts of various impurities which naturally occur in the raw materials, will affect the relative proportions of the raw materials used and may require appropriate adjustments to the times and amounts of water added to form satisfactory granules.
  • The chemical composition of different fly ashes can be substantially different. Fly ash with an excessively high iron oxide content can present economically insurmountable problems because of the degree of stickiness which results. Best results were achieved with fly ash having an iron oxide content of about 4%. Using a fly ash containing in excess of 12% iron oxide can caused insurmountable problems of sticking in the kiln. Iron content in the fly ash should be less than 12%, preferably about 7% or less, and most preferably about 4% or less.
  • The invention is suitable for making proppant materials from proppants using fly ash from the combustion of various types of coal (e.g., lignite, bituminous, and anthracite coals). Lignite fly ash typically contains a much higher proportion of CaO (and therefore smaller proportions of SiO2 and Al2O3) than bituminous or anthracite fly ash. Using lignite fly ash, the proportion of bauxite in the core granule can be reduced; in some embodiments, very strong proppant materials could be made without including any bauxite in the core particle—i.e., making the core particles of fly ash and clay. In such embodiments, bauxite is used only as a coating material. Moreover, a single, relatively light coating of bauxite may be used with core granules made using lignite fly ash (e.g., an amount of bauxite equal to about 5% or less of the total weight of the dry ingredients).
  • Prior to mixing, the fly ash, clay, and bauxite are in powdered form, as described below. In one embodiment, the specifications for the fly ash, the clay, and the bauxite are as shown in Tables 1-3 below, respectively (it is recognized that the total % may be slightly more or less than 100% —this is the result of rounding of some of the values in the table):
  • TABLE 1
    Fly Ash
    Compound %
    SiO2 66.0
    Al2O3 22.6
    Fe2O3 4.0
    TiO2 0.6
    K2O 2.5
    MgO 0.2
    Na2O 0.3
    CaO 0.3
    SO3 0.2
    LOI 5.2
  • TABLE 2
    Clay (Kaolin)
    Compound %
    SiO2 59.78
    Al2O3 25.84
    Fe2O3 1.86
    CaO 0.39
    MgO 0.54
    K2O 2.08
    Na2O 0.38
    LOI1000°C 7.28
  • TABLE 3
    Bauxite
    Compound %
    Al2O3  86 min.
    SiO2   8 max.
    Fe2O3   2 max.
    TiO2   4 max.
    K2O + Na2O 0.3 max.
    CaO + MgO 0.6 max.
  • The fly ash and the bauxite are both ground to d90<10μ. The clay is ground to d90<12μ.
  • The dry ingredients used in certain embodiments described below and their respective percentages of the total are set forth in Table 4 below:
  • TABLE 4
    Dry Ingredients
    Material Weight (g) % Core % Total
    Fly Ash 1,522 69% 62%
    Clay 326 15% 13%
    Bauxite (core) 350 16% 14%
    Bauxite (1st coating) 100 4%
    Bauxite (2nd coating) 150 6%
  • In the embodiments discussed in detail below, granulation is accomplished using an Eirich R02 mixer (with the in tool) in the embodiments discussed below. However, it is understood that other high shear granulating mixers or other granulating/pelletizing mixers or technologies may be used to form the granules, with appropriate adjustments to the times and amounts of water added to form satisfactory granules. Similarly, while the Eirich mixer also is used to coat the granules, it is understood that other mixers or equipment for powder coating or spray (with a slurry) coating the granules may be used and still be within the scope of the invention.
  • The specifications for the tools and settings on the mixer are shown in Table 5 below:
  • TABLE 5
    Mixer Specifications/Settings
    Granulation tool 1 - diameter 0.136 m
    Granulation tool 2 - diameter (Pin Type) 0.136 m
    Rotor
    V-belt setting A B C
    Rotational speed - Level 1 [rpm] 900 1500 2500
    Rotational speed - Level 2 [rpm] 1800 3000 5000
    Rim speed [m/s] A B C
    Level 1 6.41 10.68 17.80
    Level 2 12.82 21.36 35.60
  • The protocol for granulation of the raw materials involves (i) granulation of the raw ingredients plus water to form the core granules; and (ii) coating of the core granules with powdered bauxite (added either in powder form or as a powder rich slurry spray). In some embodiments, more than one coating of the core granules may be desirable to enhance adherence of the coating to the core granules.
  • By using multiple coatings, the composition of each layer coating may be varied somewhat. In some embodiments, the coating material used in successive layers may contain different amounts of bauxite to provide a transition of the composition from the core particle material to the outermost layer of the bauxite coating.
  • An additional step of finishing of the coated granules to enhance roundness also may be desirable in some embodiments.
  • Referring to the steps shown in Table 6 below and the mixer settings and times shown, such a protocol is implemented in some embodiments as discussed below.
  • TABLE 6
    Protocol for Formation of Coated Granules
    Mixing Water
    Settings Rim Speed [ms/s] Principle Addition Time
    Step Rotor Pan Rotor Pan [ccf/cf] Step Description (g) [s]
    1 C1 2 17.80 2 ccf Dry mix 0 60
    2 C1 2 17.80 2 ccf Water addition 380 15
    3 C2 2 35.60 2 ccf Water addition 60
    4 C2 2 35.60 2 ccf Microgranulation 0 120
    5 B2 2 21.36 2 ccf Growth of microgranules 0 120
    6 A2 2 12.82 2 ccf Round granules 0 30
    7 A2 2 12.82 2 ccf First powder coating 0 60
    8 A2 2 12.82 2 ccf Second powder coating 0 30
    9 A1 2 6.41 2 ccf Finishing 0 60
  • The dry, powdered raw materials (fly ash, clay, and bauxite) for the granule cores are combined in the mixer (step 1). In this embodiment, the followings amounts of the powdered raw materials were added to the mixer in step 1: fly ash—1,522 g.; clay—326 g.; and bauxite—350 g. This will result in the granule cores being about 70% fly ash, about 15% bauxite, and about 15% clay. Water is added smoothly as a spray to the powdered raw materials as they are mixed to form a cohesive material (steps 2-3). The water is preferably added in two steps to minimize dust escaping from the mixer—a small amount of water is added at first with the mixer at low speed until the raw materials have been wetted, and the remainder is added with the mixer at higher speed. After the raw materials and water have been mixed, the core granules are formed in the mixer (steps 4-6). First, microgranules are formed from the raw material and water mixture. The microgranules are then grown to e desired size. After the core granules have been grown, the granules receive one or more coatings (steps 7-8). In some embodiments, it may be desired to finish the coated granules in the mixer to further enhance roundness(step 9).
  • The protocol described in Table 6 is suitable for making proppants in the range of 20-50 mesh, but with appropriate modifications can be used to make proppant materials in the range of 16-30 mesh, 40-70 mesh, or even smaller than 40-70 mesh; pretty much any commercially desired size range is feasible. The moisture content after granulation in this particular embodiment is in the range of 13-15 Ma. %. It is understood that the targeted residual moisture content may vary depending on the composition of feedstocks used, including the relative proportions of the feedstocks and their individual specifications (e.g., constituent components and impurities, particle size, etc.). Generally, the residual moisture content should be in the range of 10-25 Ma. %, and preferably in the range of 10-20 Ma. %. By relatively small changes in the moisture content, temperature, and the time allotted to growth of the microgranules, different particle size distributions can be achieved.
  • For up-scaling of the process, it is helpful to properly control the rim speed. Especially during the first part of the granulation process, its essential to use a higher rim speed to form microgranules with a good particle size distribution. These microgranules can then be grown to very round granules later using a lower rim speed. Rim speed during the different steps is shown in Table 6.
  • After creating microgranules with a good size distribution, the rim speed of the rotor should be decreased to ensure proper growth of the granules. The speed of the rotor still needs a relatively high value to ensure good distribution. If the speed is too low, large lumps can be formed on the granules which can result in a bad distribution and a poor yield. Growth of the granules continues until the granules have reached the desired size. At this point, the granules are the proper size, but are not very well rounded.
  • To better round the granules, the rotor speed is reduced and the granules are rounded for a relatively brief period of time. The time should be as short as possible, but as long as necessary to get reasonably round granules. If the time is too long, the granules will start to grow again at the low rotor speed.
  • The first coating step ensures that the size of the granules remains the same. In this embodiment, because the core granules are going to be coated twice, about 100 g. of powdered bauxite (about 4% of the total dry ingredient weight) is added to the mixer to stop the growth of the granules and to permit further rounding of the granules in the mixer. After 60 seconds of rounding, the coated granules are well rounded and there is good adhesion of the coating material on the granules.
  • In the second powder coating step, about 150 g. of powdered bauxite (about 6% of the total dry ingredient weight) is added to the mixer. The differences in the composition of the core granule, the first layer of powder coating, and the second layer of powder coating can provide a good transition in the composition of the materials in the layers, which promotes good adhesion of the coating to the core. In other embodiments, more layers or layers having varying compositions may be used, but two layers of bauxite powder coating provides a significant improvement over a single layer of coating in the adhesion of the coating to the core granule.
  • In some embodiments in which the core granules are coated twice (i.e., two layers of coating), the granules receive a first coating of powdered bauxite equal to about 2%-10%, preferably 3%-6%, more preferably 4%-5% of the total weight of the dry ingredients to stop the growth of the granules and to permit further rounding of the granules in the mixer for extended time. The granules then receive a second coating of powdered bauxite equal to about 4% -15%, preferably 5%-10%, more preferably 6%-8% of the total weight of the dry ingredients.
  • As noted above, the coating step in some embodiments may be accomplished by spraying the granules with a slurry rich in powdered bauxite rather than adding the powdered bauxite in dry form. In some embodiments using a bauxite rich slurry to coot the granules, PVA or another suitable binder is included in the slurry (the PVA acting as both an emulsifier and a binder). If the coating is applied as a slurry rather than as a powder, the weight of the powdered bauxite in the slurry is added to the dry ingredient weight for purposes of determining the total dry ingredient weight referred to herein.
  • After the bauxite coating or coatings have been added to the core, the granules may be sieved.
  • The green strength of the coated granules is very good—it is not difficult to sieve and calcinate the green material using standard methods. The granules are then calcinated in suitable kiln, such as a rotary kiln, at a temperature of about 900° C.-1150° C., preferred 950° C.- 1150° C., more preferred 1050° C.-1080° C. for about 2-60 minutes, preferably 10-30 minutes, or most preferably 15-20 minutes. The temperature of a rotary kiln typically is somewhat higher than the actual sintering temperature in the sintering bed inside the kiln tube (which may be read by a thermocouple), so the kiln temperature may be on the order of about 1050° C.-1350° C., depending on the kiln. Calcination of the material at too high a temperature could result in the crystalline water and other volatile materials being released too fast, which could lead to cracks in the green material which in turn would weaken the structure of the proppant material and limit its maximum strength.
  • The calcined granules are then sintered in a suitable kiln, such as a rotary kiln, at a temperature of at least 1200° C. (again, the kiln temperature may be somewhat higher that the sintering temperature in the sintering bed). By using this method of manufacture, in which the core granule is formed from a mixture of fly ash, bauxite, and clay, and subsequently is coated with bauxite, the maximum sintering temperature can be increased to about 1240° C.-1280° C. without significant sticking of the granules to each other during sintering (again, the kiln temperature may be somewhat higher that the sintering temperature in the sintering bed, which may be on the order of about 1380° C., depending on the kiln).
  • It is understood that the calcination and the sintering steps described above may be performed in separate kilns or in different sections of the same kiln as the material passes through the kiln.
  • For proppant made using lignite fly ash, the sintering temperature may be lower. For example, if lignite fly ash is used, a combination calcination/sintering step may be used at a temperature of about 1080° C.-1100° C.
  • If a rotary kiln is used, there may be a small amount of sticking to the kiln tube, but it should not be excessive.
  • Crush Testing of the proppant material produced in the manner described above indicated a compressive strength in excess of 10,000 psi. Compressive strength of the proppant material is dependant to a large degree on particle size. The embodiment described above achieved a compressive strength in excessive of 11,000 psi for 20/40 mesh proppant material, while a 30/50 mesh proppant material embodying the invention achieved a compressive strength over 13,000 psi.

Claims (20)

What is claimed is:
1. A round proppant material comprising:
a core comprising fly ash, bauxite, and clay wherein the fly ash is the primary component by weight; and
a coating comprising bauxite surrounding the core.
2. The proppant of claim 2, wherein the core comprises about 70% fly ash, about 15% bauxite, and about 15% clay.
3. The proppant of claim 2, wherein an iron oxide content of the fly ash is 12% or less.
4. The proppant of claim 2, wherein an iron oxide content of the fly ash is about 7% or less.
5. The proppant of claim 2, wherein an iron oxide content of the fly ash is about 4% or less.
6. The proppant of claim 2, wherein the clay comprises kaolin clay.
7. The proppant of claim 2, wherein the coating comprises more than one layer of coating.
8. A round proppant material comprising:
a core comprising lignite fly ash and clay wherein the fly ash is the primary component by weight; and
a coating comprising bauxite surrounding said core.
9. The proppant of claim 8, wherein an iron oxide content of the fly ash is 12% or less.
10. The proppant of claim 8, wherein an iron oxide content of the fly ash is about 7% or less.
11. The proppant of claim 8, wherein an iron oxide content of the fly ash is about 4% or less.
12. The proppant of claim 8, wherein the clay comprises kaolin clay.
13. The proppant of claim 8, wherein the coating content of the proppant is about 5% or less.
14. A method for manufacturing a round proppant material comprising the steps of:
forming round granules comprising lignite fly ash and clay wherein the fly ash is the primary component by weight;
coating the round granules with a coating comprising bauxite to form coated round granules;
heating the coated round granules to a temperature of at least 1080° C.
15. The method of claim 14, wherein the coated round granules are heated to a temperature in a range between 1080° C. and 1100° C.
16. The method of claim 14, wherein the heating step comprises:
calcining said coated round granules at a temperature in a range between 900° C. and 1150° C.; and
sintering said coated round granules at a temperature of at least about 1200° C.
17. The method of claim 14 in which said coating comprising bauxite is applied in more than one layer.
18. The method of claim 14 in which said coating is applied in powder form.
19. The method of claim 14 in which said coating is applied in the form of a slurry containing powdered bauxite.
20. The method of claim 14 in which said coating is applied in the form of a slurry comprising powdered bauxite and a binder.
US15/409,782 2013-08-20 2017-01-19 Proppant Material Incorporating Fly Ash and Method of Manufacture Abandoned US20170130123A1 (en)