US20150262602A1 - Perpendicular magnetic recording medium - Google Patents
Perpendicular magnetic recording medium Download PDFInfo
- Publication number
- US20150262602A1 US20150262602A1 US14/724,557 US201514724557A US2015262602A1 US 20150262602 A1 US20150262602 A1 US 20150262602A1 US 201514724557 A US201514724557 A US 201514724557A US 2015262602 A1 US2015262602 A1 US 2015262602A1
- Authority
- US
- United States
- Prior art keywords
- layer
- magnetic
- magnetic recording
- split
- recording layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application is a divisional of Ser. No. 13/062,640 filed May 5, 2011, which is the National Stage of International Application No. PCT/JP2009/066200 filed Sep. 16, 2009, which claims priority to Japanese Patent Application No. 2008-236271 filed Sep. 16, 2008 and Japanese Patent Application No. 2008-249266 filed Sep. 26, 2008, the contents of all of which are incorporated herein by reference in their entirety.
- The present invention relates to a perpendicular magnetic recording medium to be mounted on an HDD (hard disk drive) or the like of a perpendicular magnetic recording type.
- With an increase in capacity of information processing in recent years, various information recording technologies have been developed. In particular, the surface recording density of an HDD using a magnetic recording technology is continuously increasing at an annual rate of approximately 100%. In recent years, an information recording capacity exceeding 200 gigabytes per perpendicular magnetic recording medium with a 2.5-inch diameter for use in an HDD or the like has been demanded. To fulfill such a demand, an information recording density exceeding 400 gigabits per square inch is desired to be achieved.
- To achieve a high recording density in a magnetic recording medium for use in an HDD or the like, a perpendicular magnetic recording type has been proposed in recent years. In a perpendicular magnetic recording medium for use in the perpendicular magnetic recording type, the axis of easy magnetization of a magnetic recording layer is adjusted so as to be oriented in a direction perpendicular to the base surface. In the perpendicular magnetic recording type, compared with a conventional in-plane recording type, it is possible to more suppress a so-called thermal fluctuation phenomenon, in which thermal stability of a recording signal is impaired because of a superparamagnetic phenomenon to cause the recording signal to be lost, and therefore the perpendicular magnetic recording type is suitable for increasing the recording density.
- As a magnetic recording medium for use in the perpendicular magnetic recording type, a CoCrPt—SiO2 perpendicular magnetic recording medium (refer to Non-Patent Document 1) has been proposed because of high thermal stability and excellent recording characteristic. This is to configure a granular structure in a magnetic recording layer in which a non-magnetic grain boundary part with segregation of SiO2 is formed between magnetic particles in which a crystal with an hcp structure (a hexagonal close-packed crystal lattice) of Co continuously grows in a columnar shape, thereby achieving finer magnetic particles and an improvement of a coercive force Hc together. It is known that an oxide is used for the non-magnetic grain boundary (a non-magnetic portion between magnetic particles), and, for example, using any one of SiO2, Cr2O3, TiO, TiO2, and Ta2O5 has been proposed (Patent Document 1).
- The magnetostatic characteristic and electromagnetic conversion characteristic of a magnetic layer having the granular structure can be adjusted by changing kinds of oxides that form the grain boundary or changing oxide contents. Both high coercive force and low noise are important, but they have a tradeoff relationship that, as one of them increases, the other decreases. Therefore, conventionally, the magnetic recording layer is divided into plural layers so that they take different roles. For example, by providing a layer that contains a smaller amount of oxide to achieve improvement in coercive force Hc and a layer that contains a larger amount of oxide to achieve improvement in SNR (Signal to Noise Ratio), the advantages of both the oxides can be obtained.
- However, when an intense magnetic field is applied to the magnetic recording layer, leak field to an adjacent track becomes large, so that WATE (wide Area Track Erasure), namely, a phenomenon, that recorded information within the range of several micrometers from a track to write on is lost, is problematic. As means for reducing WATE, it is important to set a reversed magnetic domain nucleation field Hn of the magnetic recording layer at a negative value, and increase the absolute value thereof. In order to obtain a high (large in absolute value) Hn, a CGC (Coupled Granular Continuous) medium in which a thin film having a high perpendicular magnetic anisotropy is formed above or below the magnetic recording layer having a granular structure was devised (Patent Document 2).
- The CGC medium shown in Patent Document 2 has a structure in which a CoB magnetic film and a Pd non-magnetic thin film are stacked one on top of another, and uses their exchange coupling to obtain a high Hn. However, in the CGC medium, the exchange coupling cannot be obtained unless the magnetic film is a thin film, and it is required to stack CoB films and Pd films alternately three times because only one for each layer is less effective. Therefore, in recent years, it is often found that an auxiliary recording layer which is a single layer having high perpendicular magnetic anisotropy and which is magnetically approximately continuous in an in-plane direction of a main surface of a base is formed on the magnetic recording layer.
- As the coercive force Hc of the magnetic recording layer is more improved, a higher recording density can be achieved but writing by the magnetic head tends to be more difficult. Then, an auxiliary recording layer improves saturated magnetization Ms and also contributes to improving easy writing, namely, an overwrite characteristic. In other words, objects of disposing the auxiliary recording layer on the magnetic recording layer are to improve the reversed magnetic domain nucleation filed Hn to reduce noise, and to improve the saturated magnetization Ms to improve the overwrite characteristic. Note that the auxiliary recording layer may be referred to as a continuous layer or cap layer.
-
- [Non-Patent Document 1] T. Oikawa et. al., IEEE Trans. Magn., vol. 38, 1976-1978 (2002)
-
- [Patent Document 1] Japanese Unexamined Patent Application Publication No. 2006-024346
- [Patent Document 2] Japanese Unexamined Patent Application Publication No. 2003-346315
- In the magnetic recording medium with such increased recording density as described above, a further improvement in recording density is demanded for the future. Important factors for increasing recording density of the perpendicular magnetic recording medium include an improvement in magnetostatic characteristic, such as a coercive force Hc and a reversed magnetic domain nucleation magnetic field Hc; and an improvement in electromagnetic conversion characteristic, such as an overwrite characteristic, an SNR (Signal to Noise Ratio), and narrowing of a track width. Of them, the improvement in coercive force Hc and the improvement in SNR are important for reading and writing accurately at high speed even at a recording bit of a small area.
- The improvement in SNR is achieved mainly by reducing noise in a magnetization transition region of the magnetic recording layer. Effective factors for reducing noise include an improvement in crystalline orientation of the magnetic recording layer, making particle diameters of magnetic particles finer, and isolation of the magnetic particles. Of them, when isolation of magnetic particles is promoted, magnetic interaction between adjacent magnetic particles is interrupted. Therefore, noise can be greatly reduced and the SNR can be significantly improved. In the perpendicular magnetic recording medium of the above granular structure, magnetic particles are isolated and refined by using an oxide to form a grain boundary, thereby improving the SNR.
- However, as described above, simply increasing the amount of oxide in the magnetic recording layer in order to promote isolation of magnetic particles causes reduction in coercive force Hc, resulting in deterioration in recording and reproducing characteristic. Therefore, both the characteristics of a high coercive force and a high SNR are obtained by configuring the magnetic recording layer to have plural layers, one of which is a layer having high coercive force Hc and the other of which is a layer having a high SNR, but noise due to a layer having a high coercive force Hc becomes a problem. Therefore, conventionally, the noise is suppressed by thinning the film thickness of the layer having a high coercive force. However, it is necessary to secure a minimum required coercive force, and accordingly it is inevitable to allow a certain amount of noise.
- Further, the auxiliary recording layer described above does not have a granular structure but has a structure that is magnetically approximately continuous in an in-plane direction. This makes it possible for the auxiliary recording layer to improve the overwrite characteristic but causes increase in noise. In particular, the auxiliary recording layer is positioned at an upper portion of the medium, and therefore has a large effect on the increase in noise. However, without the auxiliary recording layer, the OW characteristic enormously lowers, and a recent magnetic recording layer having a high coercive force can no longer be written. This makes it inevitable to allow a certain amount of noise.
- Therefore, in the above techniques, it is inevitable to allow the noise to increase to a certain degree in order to secure a high coercive force Hc, and accordingly the improvement in SNR has reached a limit. Therefore, in order to achieve a higher recording density of the magnetic recording medium, it is a problem to be solved to establish a new technique that can improve the SNR further while securing high coercive force Hc.
- In view of such a problem to be solved, an object of the present invention is to provide a perpendicular magnetic recording medium the SNR of which is further improved while a high coercive force Hc thereof is secured so that a higher recording density can be achieved.
- In order to solve the above problem, the inventors of the present invention have conducted careful examination and have focused on reducing the noise due to the magnetic recording layer. That is, the inventors have thought that there is a possibility that a magnetized state of the magnetic recording layer may affect noise generation. Then, they have accumulated their studies, and have found that the above problem to be solved is solved by configuring the magnetic recording layer to have two layers, a first magnetic layer and a second magnetic layer, and interposing therebetween a non-magnetic split layer containing Ru so that the direction of magnetization of the magnetic recording layer, in particular the first magnetic layer is controlled to reduce the noise, and they have completed the present invention.
- That is, in order to solve the above problem, a representative configuration of a perpendicular magnetic recording medium according to the present invention is characterized by including, on a base, at least a first magnetic layer having a granular structure in which a non-magnetic grain boundary portion is formed between crystal particles grown in a columnar shape; a non-magnetic split layer containing Ru disposed on the first magnetic layer; and a second magnetic layer that is disposed on the split layer and that has a granular structure in which a non-magnetic grain boundary portion is formed between crystal particles grown in a columnar shape, wherein the first magnetic layer and the second magnetic layer contain oxides which form the gain boundary portion, and when an oxide content of the first magnetic layer is represented by A and an oxide content of the second magnetic layer is represented by B, a relationship between the oxide contents A/B is in the range of 0.5<A/B<1.0.
- According to the above configuration, since the split layer containing Ru is interposed between the first magnetic layer and the second magnetic layer, antiferro-magnetic exchange coupling (AFC), which is a magnetic interaction, can be generated between the magnetic recording layers. This makes it possible to arrange the direction of magnetization of the first magnetic layer and the direction of magnetization of the second magnetic layer in an antiparallel manner to each other (so as to be opposite to each other), thereby causing them to interact so as to fix the directions of magnetization thereof.
- Furthermore, since the relationship between the oxide contents A/B is in the range of 0.5<A/B<1.0, the oxide contents of the first magnetic layer and the second magnetic layer can be set properly so that the first magnetic layer becomes a layer having a reduced amount of grain boundary portion and having a high coercive force Hc, and the second magnetic layer becomes a layer having a large amount of grain boundary portion and having a high SNR. Therefore, it becomes possible to further improve the SNR of the perpendicular magnetic recording medium while keeping a high coercive force Hc thereof. In addition, since the first magnetic layer has a high coercive force Hc, the first magnetic layer can act as a pin layer that fixes the direction of magnetization of the second magnetic layer.
- It is preferred that the split layer described above have a film thickness in the range of 2 Å to 10 Å. The split layer the film thickness of which is set in such a range can interrupt magnetism between the first magnetic layer and the second magnetic layer to generate AFC.
- Note that, if the film thickness of the split layer is set at 10 Å or more, the exchange coupling generated between the magnetic recording layers is weakened, and therefore it becomes impossible to obtain a desired SNR. Furthermore, if the film thickness is as thick as 10 Å or more, the magnetic recording layers on and just below the split layer are magnetically completely separated from each other and inheritance of crystal orientation from one to the other is completely lost. On the other hand, if the film thickness of the split layer is 2 Å or less, the magnetism between the first magnetic layer and the second magnetic layer cannot be interrupted, and therefore it becomes impossible to generate AFC. In addition, the split layer having a film thickness in a range of 2 Å or less cannot form a coating film. Note that, here, the coating film may not necessarily be continuous, for example, the film may deposit in an island shape as long as it can fulfill its function.
- It is preferred that the split layer described above is composed of Ru or a Ru alloy. Because Ru has a crystalline form (hcp) similar to Co that composes the magnetic particles, and therefore Ru does not easily disturb epitaxial growth of Co crystal particles even if it is interposed between the magnetic recording layers.
- It is preferred that the Ru alloy is selected from a group consisting of RuO, RuCo, RuCr, RuSiO2, RuTiO2, RuCr2O3, RuWO3, and RuTa2O5. These Ru alloys, among various Ru alloys, are most effective in securing a high coercive force Hc and improving the SNR.
- In particular, when the Ru alloy is RuO or when it contains an oxide, the split layer contains oxygen atoms. Thereby, in a portion of the split layer positioned on the grain boundary with the granular structure in the first magnetic layer, the oxygen atoms contained in the split layer have a high affinity with oxygen atoms contained in the grain boundary in the first magnetic layer, so that the portion inherits the grain boundary structure of the magnetic layer as a Ru oxide. Also, when the split layer contains an oxide, the oxide becomes high in affinity with the grain boundary of the first magnetic layer, and similarly inherits the grain boundary structure of the first magnetic layer. Therefore, in both the cases, it is possible to grow Co crystal particles in the second magnetic layer, without the split layer interfering with the inheritance of the grain boundary structure of the first magnetic layer.
- Note that, as a specific means for causing the split layer to contain Ru and oxygen, the split layer can be composed of RU and an oxide. By sputtering using a target containing RU and an oxide, oxygen dissociated from the oxide is caused to be contained in the film, which results in achievement of a similar effect to oxygen addition.
- It is particularly preferred that the oxide contained in the split layer is WO3, TiO2, or RuO. These oxides can improve the electromagnetic conversion characteristic (SNR). Among them, WO3 can obtain a high effect. This is because WO3 is an unstable oxide, and therefore exhibits the effect of oxygen addition more effectively by dissociating a large amount of oxygen during sputtering.
- Then, the inventors have accumulated further studies, and have found that the above problem can be solved by connecting the first magnetic recording layer and the auxiliary recording layer by magnetic interaction, unlike the conventional manner in which the layers are respectively continuous with a main recording layer having a high SNR, and they have completed the present invention.
- That is, in order to solve the above problem, a representative configuration of a perpendicular magnetic recording medium according to the present invention is characterized by including, on a base, at least a first magnetic layer having a granular structure in which a non-magnetic grain boundary portion is formed between crystal particles grown in a columnar shape; a first split layer disposed on the first magnetic layer; a second magnetic layer that is disposed on the first split layer and that has a granular structure in which a non-magnetic grain boundary portion is formed between crystal particles grown in a columnar shape; a second split layer that is disposed on the second magnetic layer; and a third magnetic layer that is disposed on the second split layer and that is magnetically approximately continuous in an in-plane direction of a main surface of the base.
- The first or second split layer is interposed between the first magnetic layer (first magnetic recording layer) and the second magnetic layer (second magnetic recording layer) or between the second magnetic layer and the third magnetic layer (auxiliary recording layer), so that magnetic interaction can be caused to occur therebetween, and can be controlled. That is, by changing the film thicknesses of the split layers, antiferro-magnetic exchange coupling (AFC) is generated between the magnetic layers, or ferromagnetic exchange coupling (FC) is adjusted therebetween. By adjusting a coupling state or strength between the magnetic layers on and just below the split layer in this manner, fluctuation in magnetic axis can be reduced, or noise can be reduced.
- In particular, the first split layer that is set to be relatively thicker (for example, 0.6 nm to 1.2 nm) can interrupt the magnetism between the first and second magnetic layers to generate AFC. Furthermore, in the first magnetic layer, by making the film thickness thereof thin, a height to width ratio of granular magnetic particles is also shortened, and therefore a diamagnetic field occurring inside the magnet is made intense. This makes an externally-directed magnetic moment of the first magnetic layer smaller, which can result in a magnetic layer that exerts a high coercive force but is reduced in noise.
- On the other hand, the second split layer is set to be relatively thinner (for example, 0.2 nm to 0.6 nm). The second split layer is thinner than the first split layer, and the film thickness of the second split layer is in the range that does not cause AFC. This makes it possible to adjust the strength of exchange coupling between the first and second magnetic layers properly without interrupting the magnetism between them. This makes it possible to reduce the noise thought to be due to the third magnetic layer to improve the SNR. This is thought to be because exchange coupling between the auxiliary recording layer and the magnetic recording layer are moderately adjusted by providing the second split layer between the second magnetic layer and the third magnetic layer.
- The first or second split layer may be composed of Ru or a Ru alloy. Since Ru has a crystalline form (hcp) similar to Co composing magnetic particles, Ru does not easily disturb epitaxial growth of Co crystal particles even if it is interposed between the magnetic layers.
- The first or second spit layer may further contain oxygen or an oxide. In a portion of the split layer positioned above the grain boundary of the granular magnetic layer, by causing the split layer to contain Ru and oxygen, the oxygen atoms contained in the split layer inherits the grain boundary structure of the magnetic layer as a Ru oxide, since it has a high affinity for oxygen atoms contained in the grain boundary of the magnetic layer. Alternatively, when the split layer contains an oxide, the oxide has a high affinity for the grain boundary of the magnetic layer, and similarly inherits the grain boundary structure of the magnetic layer. Therefore, the split layer can cause Co in an upper layer to grow without disturbing the grain boundary structure of the magnetic layer.
- The first or second spit layer may be RuO, RuWO3, or RuTiO2. There are various possible oxides, but in particular use of oxides of Ru, W (tungsten), Ti (titanium), can improve an electromagnetic conversion characteristic (SNR). Among them, WO3 can obtain a high effect. This is because WO3 is an unstable oxide, and therefore WO3 dissociates a lot of oxygen during sputtering, and exhibits the effect of oxygen addition more effectively.
- The thickness of the first or second split layer may be in the range of 2 Å to 10 Å. This is because, if the film thickness of the split layer is 10 Å or more, the magnetic layers on and just below the split layer are magnetically completely split to lose the inheritance of crystal orientation. Furthermore, if the film thickness becomes 10 Å or more, the exchange coupling occurring between the magnetic layers is weakened, and therefore it becomes impossible to obtain a desired SNR. On the other hand, that is also because, if the film thickness is 2 Å or less, the split layer cannot form a coating film.
- The thickness of the first magnetic layer may be 5 nm or less. In this case, it is preferred that the first magnetic layer be a layer having a reduced amount of grain boundary portion and having a high coercive force Hc, and the second magnetic layer be a layer having a large amount of grain boundary portion and having a high SNR. This enhances the diamagnetic field of the first magnetic layer so that the magnetic field generated from the first magnetic layer can be reduced. Therefore, the noise generated from the first magnetic layer does not reach the magnetic head, and thus the coercive force Hc of the first magnetic layer can be increased by reducing the amount of oxide thereof so that the first magnetic layer can act as a pin layer that fixes the direction of magnetization of the second magnetic layer.
- It is preferred that the film thickness of the first magnetic layer is in a range of 0.7 nm to 3.0 nm. This enhances the diamagnetic field of the first magnetic layer so that the noise due to the first magnetic layer can be reduced. Since the coercive force Hc can be increased by reducing the oxide in the first magnetic layer so that the first magnetic layer acts as a pin layer that fixes the direction of magnetization of the second magnetic layer, a high coercive force Hc can be achieved.
- The oxide content of the first magnetic layer may be 5 mol % or more. This is because, when the oxide content is 5 mol % or more, a high coercive force Hc and a high SNR can be obtained.
- The second magnetic layer may contain 5 mol % or more of oxide constituting the grain boundary. This is because, when the oxide is 5 mol % or more, a high magnetostatic characteristic and a high electromagnetic conversion characteristic can be obtained, and besides, though the characteristic of the third magnetic layer decreases considerably when the oxide content is in such a range, the characteristic can be improved by providing the split layer described above.
- The second magnetic layer may contain two or more kinds of oxides. This makes it possible to obtain the characteristics of the plural oxides to achieve further refinement and isolation of the magnetic particles in the second magnetic layer to reduce the noise and improve the SNR, so that a perpendicular magnetic recording medium that can achieve a higher recording density can be obtained.
- The second magnetic layer may contain one or plural oxides selected from a group consisting of SiO2, TiO2, and CoO. SiO2 has the characteristic of promoting refinement and isolation of magnetic particles, and TiO2 has the characteristic of improving the electromagnetic conversion characteristic (in particular, SNR). By segregating these oxides in combination to the grain boundary of the second magnetic layer, the perpendicular magnetic recording medium can enjoy the advantages of both the oxides.
- According to the present invention, it is possible to provide a perpendicular magnetic recording medium the SNR of which is further improved while a coercive force Hc thereof is secured so that a higher recording density can be achieved.
-
FIG. 1 is a diagram for describing the structure of a perpendicular magnetic recording medium according to an embodiment of the present invention. -
FIG. 2 is a diagram for describing a model of a magnetic coupling composed of a first magnetic recording layer, a split layer, and a second magnetic recording layer. -
FIG. 3 is a graph showing a relationship between the film thickness of the split layer and SNR. -
FIG. 4 is a graph showing a relationship between the composition of the split layer, the SNR, and a track width. -
FIG. 5 is a graph showing a relationship between the relationship A/B between the oxide contents of the first and second magnetic recording layers, the SNR, and a coercive force Hc. -
FIG. 6 is a graph showing the relationship between the film thickness of the first magnetic recording layer and the coercive force Hc. -
FIG. 7 is a diagram for describing the structure of a perpendicular magnetic recording medium. -
FIG. 8 is a diagram for describing a model of two antiferro-magnetic exchange couplings composed of a first magnetic recording layer, a first split layer, a second magnetic recording layer, a second split layer, and an auxiliary recording layer. -
FIG. 9 is a diagram including a table and a graph, showing examples and comparative examples different in that a non-magnetic split layer is provided or not. -
FIG. 10 is a diagram including a table and graph, showing a result of comparison between examples different in composition of the split layer. -
FIG. 11 shows TEM photographs of the auxiliary recording layers of an example and a comparative example. -
- 100 . . . perpendicular magnetic recording medium
- 110 . . . disk base
- 112 . . . adhesion layer
- 114 . . . soft magnetic layer
- 114 a . . . first soft magnetic layer
- 114 b . . . spacer layer
- 114 c . . . second soft magnetic layer
- 116 . . . preliminary ground layer
- 118 . . . ground layer
- 118 a . . . first ground layer
- 118 b . . . second ground layer
- 120 . . . non-magnetic granular layer
- 122 . . . magnetic recording layer
- 122 a . . . first magnetic recording layer
- 122 b . . . split layer (first split layer)
- 122 c . . . second magnetic recording layer
- 124 . . . second split layer
- 126 . . . auxiliary recording layer
- 128 . . . medium protective layer
- 130 . . . lubricating layer
- In the following, with reference to the attached drawings, preferred embodiments of the present invention will be described in detail. The dimensions, materials, and others such as specific numerical values shown in the embodiments are merely examples so as to facilitate understanding of the invention, and are not meant to restrict the present invention unless otherwise specified. Note that, in the specification and drawings, components having substantially the same functions and structures are provided with the same reference numerals and are not redundantly described, and components not directly relating to the present invention are not shown in the drawings.
- In a first embodiment, first, an embodiment of a perpendicular magnetic recording medium according to the present invention will be described, and then a first magnetic layer, a second magnetic layer, and a split layer disposed between the first magnetic layer and the second magnetic layer will be described in detail.
- [Perpendicular Magnetic Recording Medium]
-
FIG. 1 is a diagram for describing the structure of a perpendicularmagnetic recording medium 100 according to this embodiment. The perpendicularmagnetic recording medium 100 shown inFIG. 1 includes adisk base 110, anadhesion layer 112, a first softmagnetic layer 114 a, aspacer layer 114 b, a second softmagnetic layer 114 c, apreliminary ground layer 116, afirst ground layer 118 a, asecond ground layer 118 b, a non-magneticgranular layer 120, a firstmagnetic recording layer 122 a (first magnetic layer), asplit layer 122 b, a secondmagnetic recording layer 122 c (second magnetic layer), anauxiliary recording layer 126, amedium protecting layer 128, and alubricating layer 130. Note that the first softmagnetic layer 114 a, thespacer layer 114 b, the second softmagnetic layer 114 c together constitute a softmagnetic layer 114. Thefirst ground layer 118 a and thesecond ground layer 118 b together constitute aground layer 118. The first magnetic recording layer 112 a, thesplit layer 122 b, and the secondmagnetic recording layer 122 c together constitute amagnetic recording layer 122. - As the
disk base 110, a glass disk formed by molding an amorphous aluminosilicate glass in a disk form by direct pressing can be used. Note that the type, size, thickness, and others of the glass disk are not particularly restrictive. As a material of the glass disk, for example, an aluminosilicate glass, a soda lime glass, a soda aluminosilicate glass, an aluminoborosilicate glass, a borosilicate glass, a quartz glass, a chain silicate glass, or a glass ceramic, such as a crystallized glass, is used. On this glass disk, grinding, polishing, and chemical strengthening are sequentially performed, and the smoothnon-magnetic disk base 110 formed of the chemically-strengthened glass disk can be obtained. - On the
disk base 110, theadhesion layer 112 to theauxiliary recording layer 126 are sequentially formed by DC magnetron sputtering, and the mediumprotective layer 128 can be formed by CVD. Then, thelubricating layer 130 can be formed by dip coating. Note that it is also preferred to use an inline-type film forming method in view of high productivity. The structure of each layer is described below. - The
adhesion layer 112 is formed in contact with thedisk base 110, including a function of increasing delamination strength between the softmagnetic layer 114 formed on the adhesion layer and thedisk base 110 and a function of refining and homogenizing crystal grains of each layer formed on the softmagnetic layer 114. When thedisk base 110 is made of an amorphous glass, it is preferred that theadhesion layer 112 be an amorphous alloy film so as to adapt to the surface of the amorphous glass. - As the
adhesion layer 112, for example, it can be selected from a group of a CrTi-type amorphous layer, a CoW-type amorphous layer, a CrW-type amorphous layer, a CrTa-type amorphous layer, and a CrNb-type amorphous layer. Theadhesion layer 112 may be a monolayer formed of a single material, or may be formed by laminating a plurality of layers. - The soft
magnetic layer 114 is a layer for temporarily forming a magnetic path at recording time in order to let a magnetic flux pass through the recording layer in a perpendicular direction in the perpendicular magnetic recording type. The softmagnetic layer 114 can be configured to include AFC by interposing thenon-magnetic spacer layer 114 b between the first softmagnetic layer 114 a and the second softmagnetic layer 114 c. With this, the magnetizing direction of the softmagnetic layer 114 can be aligned with high accuracy along the magnetic path (a magnetic circuit). With this, perpendicular components in the magnetizing direction are extremely decreased, thereby reducing noise occurring from the softmagnetic layer 114. As the compositions of the first softmagnetic layer 114 a and the second softmagnetic layer 114 c, a cobalt-type alloy, such as a CoTaZr; a Co—Fe-type alloy, such as CoCrFeB or CoFeTaZr; or a Ni—Fe-type alloy, such as a [Ni—Fe/Sn]n multilayered structure can be used. - The
preliminary ground layer 116 is a non-magnetic alloy layer, including an operation of protecting the softmagnetic layer 114 and a function of orienting an axis of easy magnetization of a hexagonal close-packed structure (hcp structure) contained in theground layer 118 formed on thepreliminary ground layer 116 in a direction perpendicular to the disk. It is preferred that thepreliminary ground layer 116 have a (111) plane of a face-centered cubic structure (fcc structure) parallel to a main surface of thedisk base 110. Thepreliminary ground layer 116 may also be configured to have these crystal structures and an amorphous structure in a mixed manner. As a material of thepreliminary ground layer 116, it can be selected from a group of Ni, Cu, Pt, Pd, Zr, Hf, Nb, and Ta. Further, an alloy that contains these metals as a main component and that contains any one of Ti, V, Cr, Mo, and W as an additive element may be selected. For example, as an alloy having an fcc structure, NiW, CuW, or CuCr can be preferred to be selected. - The
ground layer 118 has an hcp structure, and has an operation of growing a crystal with an hcp structure of Co in themagnetic recording layer 122 as a granular structure. Therefore, the orientation of themagnetic recording layer 122 can be more improved as the crystalline orientation of theground layer 118 becomes higher, that is, as a (0001) surface of the crystal of theground layer 118 becomes more parallel to the main surface of adisk base 110. A typical material of theground layer 118 is Ru, though the material can be selected from RuCr and RuCo instead. Because Ru has an hcp structure and has crystal lattice spacing close to that of Co, themagnetic recording layer 122 containing Co as a main component can be well oriented. - When Ru is used for the
ground layer 118, by changing gas pressure at sputtering, a two-layer structure made of Ru can be formed. Specifically, Ar gas pressure is set at a predetermine pressure, namely, a low pressure when thefirst ground layer 118 a on the bottom side is formed, and the Ar gas pressure is set at a pressure higher than when thefirst ground layer 118 a on the bottom side is formed, namely, a high pressure when thesecond ground layer 118 b on the top side is formed. This makes it possible for thefirst ground layer 118 a to improve in crystalline orientation of themagnetic recording layer 122 and for thesecond ground layer 118 b to refine a particle diameter of a magnetic particle of themagnetic recording layer 122. - Further, as the gas pressure increases, an average free path of plasma ions to be sputtered becomes shorter, and thus a film formation speed becomes slower and a coating film becomes rougher, and therefore it is possible to promote separation and refinement of the crystal particles of Ru, and also it becomes possible to refine the crystal particles of Co.
- Furthermore, a small amount of oxygen may be contained in Ru of the
ground layer 118. This makes it possible to promote further separation and refinement of the crystal particles of Ru, and to achieve further isolation and refinement of themagnetic recording layer 122. Note that although oxygen may be caused to be contained by reactive sputter, it is preferred that a target containing oxygen be used at film formation by sputtering. - The non-magnetic
granular layer 120 is a non-magnetic layer having a granular structure. On the hcp crystal structure of theground layer 118, the non-magnetic granular layer is formed, on which a granular layer of the firstmagnetic recording layer 122 a (or the magnetic recording layer 122) is grown. With this, the magnetic granular layer has an operation of separating the magnetic granular layer from a stage of initial growth (start-up). This makes it possible to promote isolation of the magnetic particles of themagnetic recording layer 122. The composition of the non-magneticgranular layer 120 can have a granular structure by subjecting a non-magnetic substance to segregation between non-magnetic crystal particles made of a Co-type alloy to form a grain boundary. - In this embodiment, CoCr—SiO2 is used for this non-magnetic
granular layer 120. This causes the non-magneticgranular layer 120 to have a granular structure because SiO2 (non-magnetic substance) is subjected to segregation between the Co-type alloys (non-magnetic crystal particles) to form a grain boundary. Note that CoCr—SiO2 is merely an example, and is not meant to be restrictive. Alternatively, CoCrRuSiO2 can be preferred to be used, and, in place of Ru, Rh (rhodium), Pd (palladium), Ag (silver), Os (osmium), Ir (iridium), or Au (gold) can also be used. Still further, the non-magnetic substance can be any non-magnetic substance that can form a grain boundary portion around magnetic particles so as to suppress or interrupt an exchange interaction operation between the magnetic particles (magnetic grains), and that does not allow solid solution with cobalt (Co). Examples can include silicon oxide (SiOx), chromium (Cr), chromium oxide (Cr2O2), titanium oxide (TiO2), zircon oxide (ZrO2), and tantalum oxide (Ta2O5). - In this embodiment, the non-magnetic
granular layer 120 is provided on the ground layer 188 (the second ground layer 188 b). This is not meant to be restrictive, and the perpendicularmagnetic recording medium 100 can be configured without the non-magneticgranular layer 120. - The
magnetic recording layer 122 has a granular structure in a columnar shape in which a non-magnetic substance is subjected to segregation around magnetic particles of a hard magnetic substance selected from a group consisting of a Co-type alloy, a Fe-type alloy, and a Ni-type alloy to form a ground boundary. By providing the non-magneticgranular layer 120, these magnetic particles can epitaxially grow continuously from the granular structure. - The
magnetic recording layer 122 comprises the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c, different in composition and film thickness from each other in this embodiment, and thesplit layer 122 b provided therebetween. This makes it possible for fine crystal particles of the secondmagnetic recording layer 122 c to grow continuously from crystal particles of the firstmagnetic recording layer 122 a, so that refinement of the secondmagnetic recording layer 122 c serving as a main recording layer can be achieved and the SNR can be improved. - In this embodiment, CoCrPt—Cr2O3 is used for the first magnetic recording layer 112 a. CoCrPt—Cr2O3 forms a granular structure in which Cr and Cr2O3 (oxides), which are non-magnetic substances, are subjected to segregation around magnetic particles (grains) made of CoCrPt to form a ground boundary and the magnetic particles are grown in a columnar shape. The magnetic particles are epitaxially grown continuously from the granular structure of the non-magnetic granular layer.
- The
split layer 122 b is a non-magnetic thin film composed of Ru, which is interposed between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c to split ferromagnetic continuity between these magnetic recording layers 122. Therefore, antiferro-magnetic exchange coupling (AFC) is generated between these magnetic recording layers 122. This makes the direction of magnetization antiparallel between the magnetic recording layers 122 (the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c) on and just below thesplit layer 122 b, which can reduce noise. - Further, CoCrPt—SiO2—TiO2 is used for the second
magnetic recording layer 122 c. Also in the secondmagnetic recording layer 122 c, a granular structure is formed in which Cr, SiO2 and TiO2 (composite oxide), which are non-magnetic substances, are subjected to segregation around magnetic particles (grains) made of CoCrPt to form a ground boundary and the magnetic particles are grown in a columnar shape. - Note that the substances for use in the first
magnetic recording layer 122 a and the secondmagnetic recording layer 122 c described above are merely examples, and are not meant to be restrictive. In this embodiment, the materials (targets) of the firstmagnetic recoding layer 122 a and the secondmagnetic recording layer 122 c are different from each other, but not limited to this, and the materials thereof may be of the same composition or type as each other. A non-magnetic substance for forming a non-magnetic region may be, for example, an oxide such as a silicon oxide (SiOx), chromium (Cr), chromium oxide (CrxOY), titanium oxide (TiO2), zircon oxide (ZrO2), tantalum oxide (Ta2O5), cobalt oxide (CoO2 or Co2O4), iron oxide (Fe2O3), or boron oxide (B2O2). Also, a nitride, such as BN, and a carbide, such as B4C2, can be suitably used. - Furthermore, in this embodiment, one type of non-magnetic substance (oxide) is used in the first
magnetic recording layer 122 a, and two types thereof are used in the secondmagnetic recording layer 122 c, but this is not meant to be restrictive, and it is also possible to use two or more types of non-magnetic substances in combination in either or both of the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c. Here, although the types of non-magnetic substances contained are not limited, it is preferred that SiO2 and TiO2 are particularly contained in this embodiment. Therefore, unlike this embodiment, when themagnetic recording layer 122 is composed of a single layer, it is preferred that thismagnetic recording layer 122 be made of CoCrPt—SiO2—TiO2. - The
auxiliary recording layer 126 is a magnetic layer magnetically approximately continuing in an in-plane direction of the main surface of the base. Theauxiliary recording layer 126 is required to be adjacent or close to themagnetic recording layer 122 so as to have a magnetic interaction therewith. A material of theauxiliary recording layer 126 may be, for example, CoCrPt or CoCrPtB, or can be composed of any of these materials containing a slight amount of oxide. Theauxiliary recording layer 126 is aimed at adjusting a reversed magnetic domain nucleation magnetic field Hn and adjusting the coercive force Hc, thereby achieving improvement in resistance to heat fluctuations, OW characteristic, and SNR. To achieve this aim, it is desired that theauxiliary recording layer 126 have high perpendicular magnetic anisotropy Ku and saturation magnetization Ms. Note that, though theauxiliary recording layer 126 is disposed above themagnetic recording layer 122 in this embodiment, it may be disposed therebelow. - Note that “magnetically continuing” means that magnetization continues. “Approximately continuing” means that the
auxiliary recording layer 126 is not necessarily a single magnet when observed as a whole and the magnetism may be discontinued due to the grain boundary of the crystal particles and others. In the grain boundary, the crystal may be not only discontinuous but also Cr may be subjected to segregation. Furthermore, a slight amount of oxide may be contained for segregation. However, even when a grain boundary containing an oxide is formed in theauxiliary recording layer 126, it is preferred that the area (amount of oxide content) of the grain boundary is smaller than that of the ground boundary of themagnetic recording layer 122. Though the function and operation of theauxiliary recording layer 126 are not necessarily clear, it is thought that theauxiliary recording layer 126 has a magnetic interaction (performs exchange coupling) with the granular magnetic particles of themagnetic recording layer 122, thereby adjusting Hn and Hc and improving resistance to heat fluctuations and the SNR. It is also thought that, because the area of the crystal particles connected to the granular magnetic particles (crystal particles having a magnetic interaction) is larger than the cross-section of the granular magnetic particles, theauxiliary recording layer 126 receives more magnetic fluxes from a magnetic head to become prone to magnetization reversal, thereby improving an overall OW characteristic. - The medium
protective layer 128 can be formed by forming a film of carbon by CVD with vacuum being kept. The mediumprotective layer 128 is a layer for protecting the perpendicularmagnetic recording medium 100 from an impact of the magnetic head. In general, a carbon film formed by CVD has a film hardness improved as compared with those formed by sputtering, and therefore the perpendicularmagnetic recording medium 100 can be effectively protected from an impact from the magnetic head. - The
lubricating layer 130 can be formed by dip coating with the use of PFPE (perfluoropolyether). PFPE has a long-chain-shaped molecular structure, and combines with N atoms on the surface of the mediumprotective layer 128 with high affinity. With this operation of thelubricating layer 130, even when the magnetic head comes into contact with the surface of the perpendicularmagnetic recording medium 100, damage and loss of the mediumprotective layer 128 can be prevented. - According to the above manufacturing process, the perpendicular
magnetic recording medium 100 can be obtained. Next, the magnetic recording layer 122 (the firstmagnetic recording layer 122 a, the secondmagnetic recording layer 122 c, and thesplit layer 122 b provided therebetween), which is a feature of the present invention, will be described in further detail. - As described above, the
split layer 122 b is a non-magnetic layer provided between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c. This splits ferromagnetic continuity between these magnetic recording layers 122, and antiferro-magnetic exchange coupling (AFC) is generated between the magnetic recording layers 122 as a magnetic effect. -
FIG. 2 is a diagram for describing a model of a magnetic coupling composed of the firstmagnetic recording layer 122 a, thesplit layer 122 b, and the secondmagnetic recording layer 122 c. As shown inFIG. 2 , by providing thesplit layer 122 b between the first magnetic recording layer 112 a and the secondmagnetic recording layer 122 c, antiferro-magnetic exchange coupling (AFC) is caused therebetween, the directions of magnetization of the first magnetic recording layer 112 a and the secondmagnetic recording layer 122 c are made antiparallel, which interacts so as to fix the directions of magnetization. Therefore, noise can be reduced. - Furthermore, as shown in
FIG. 2 , it is preferred that the thickness of the firstmagnetic recording layer 122 a is smaller than that of the secondmagnetic recording layer 122 c, and it is more preferred that the film thickness of the firstmagnetic recording layer 122 a is in the range of 0.7 nm to 3.0 nm. - Without the
split layer 122 b, the firstmagnetic recording layer 122 a would be a magnet continuous with the secondmagnetic recording layer 122 c, but here, since thesplit layer 122 b splits them, the firstmagnetic recording layer 122 a constitutes an individual short magnet. Then, by further reducing the film thickness of the firstmagnetic recording layer 122 a, a height to width ratio of the granular magnetic particles is reduced (in the perpendicular magnetic recording medium, a direction along the film thickness corresponds to a longitudinal direction of an axis of easy magnetization), and thus a diamagnetic field occurring inside the magnet becomes intense. Therefore, a magnetic field generated outward from the firstmagnetic recording layer 122 a becomes too weak to be easily sensed by the magnetic head. That is, by adjusting the film thickness of the firstmagnetic recording layer 122 a to set the magnetic moment (strength of a magnet) such that the magnetic field does not easily reach the magnetic head and such that the firstmagnetic recording layer 122 a magnetically interacts with the secondmagnetic recording layer 122 c, themagnetic recording layer 122 that exerts a high coercive force but is reduced in noise can be obtained. - Furthermore, since noise generated from the first
magnetic recording layer 122 a does not reach the magnetic head, the amount of oxide of the firstmagnetic recording layer 122 a can be reduced to increase the coercive force Hc, and besides, the firstmagnetic recording layer 122 a can be caused to act as a pin layer that fixes the direction of magnetization of the secondmagnetic recording layer 122 c. - It is preferred that the
split layer 122 b have a film thickness in the range of 2 Å to 10 Å (0.2 nm to 1 nm). This makes it possible to interrupt magnetism between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c to generate AFC. Here, if the film thickness of thesplit layer 122 b is set at 10 Å or more, the exchange coupling generated between the magnetic recording layers 122 is weakened, and therefore it becomes impossible to obtain a desired SNR, and besides, the magnetic recording layers 122 on and just below thesplit layer 122 b are magnetically completely separated from each other and inheritance of crystal orientation from one to the other is lost. On the other hand, if the film thickness of thesplit layer 122 b is 2 Å or less, the magnetism between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c cannot be interrupt, and therefore it becomes impossible to generate AFC, and besides, thesplit layer 122 b cannot form a coating film. Note that, because the strength of exchange coupling of AFC attenuates while fluctuating according to the thickness of the intervening splitlayer 122 b, it is preferred that the film thickness is set so as to obtain the peak of the fluctuation. - Furthermore, in terms of the crystal structure, the first
magnetic recording layer 122 a and the secondmagnetic recording layer 122 c have similar granular structures, and therefore the inheritance of the crystalline orientation between them is not blocked. Because thesplit layer 122 b does not contain so much as oxygen as the magnetic recording layers 122 (the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c), no grain boundary is formed in thesplit layer 122 b, but it is thought that thesplit layer 122 b does not disturb crystal growth, since thesplit layer 122 b is an extremely thin film with a thickness of 1 nm or less and Ru constituting thesplit layer 122 b has an hcp structure as described later. - Hereinabove, the advantages of the film configuration of the
magnetic recording layer 122 have been described. Next, the compositions of the firstmagnetic recording layer 122 a, the secondmagnetic recording layer 122 c, and thesplit layer 122 b will be described in detail. - The first
magnetic recording layer 122 a and the secondmagnetic recording layer 122 c are layers each of which has a granular structure in which a non-magnetic grain boundary portion is formed between crystal particles grown in a columnar shape, and they contain oxides as a substance to form the grain boundary portion. Here, when an oxide content of the firstmagnetic recording layer 122 a is represented by A, and an oxide content of the secondmagnetic recording layer 122 c is represented by B, it is preferred that a relationship between the oxide contents A/B is in the range of 0.5<A/B<1.0. - This makes it possible to further improve the SNR of the perpendicular magnetic recording medium while keeping a high coercive force Hc thereof, since the first
magnetic recording layer 122 a becomes a layer having a small amount of grain boundary portion and having a high coercive force Hc, and the secondmagnetic recording layer 122 c becomes a layer having a large amount of grain boundary portion and having a high SNR. In addition, since the firstmagnetic recording layer 122 a has a high coercive force, the firstmagnetic recording layer 122 a can act as a pin layer that fixes the direction of magnetization of the secondmagnetic recording layer 122 c. - Note that it is preferred that an amount of oxide contained in the first
magnetic recording layer 122 a is 5 mol % or more, because this makes it possible to obtain a high coercive force Hc and a high SNR. - It is also preferred that two or more kinds of oxides are contained in the second
magnetic recording layer 122 c. This makes it possible to obtain plural oxide characteristics, thereby achieving further refinement and isolation of the magnetic particles of the secondmagnetic recording layer 122 c to reduce noise and improve the SNR, so that a higher recording density of the perpendicularmagnetic recording medium 100 can be achieved. - Above all, it is preferred that one or plural oxides contained in the second
magnetic recording layer 122 c are selected from a group consisting of SiO2, TiO2, and CoO. SiO2 has the characteristic of promoting refinement and isolation of magnetic particles, and TiO2 has the characteristic of achieving improvement in electromagnetic conversion characteristic (in particular, SNR). Therefore, by causing these oxides in combination to segregate to the grain boundary of the secondmagnetic recording layer 122 c, the perpendicularmagnetic recording medium 100 can enjoy the advantages of both the oxides. - It is preferred that the
split layer 122 b is composed of Ru or a Ru alloy. Because Ru is close in lattice constant to Co constituting the magnetic particles, and Ru has a similar crystalline structure (hcp) to Co constituting the magnetic particles, the split layer composed of Ru does not easily disturb epitaxial growth of Co crystal particles even if it is interposed between the magnetic recording layers 122. - Note that it is preferred that the Ru alloy is selected from a group consisting of RuO, RuCo, RuCr, RuSiO2, RuTiO2, RuCr2O3, RuWO3, and RuTa 2O5. This is because these Ru alloys are most effective in securing a high coercive force Hc and improving the SNR.
- The
adhesion layer 112 to theauxiliary recording layer 126 were sequentially formed on thedisk base 110 in an Ar atmosphere by DC magnetron sputtering using an apparatus for film formation that was subjected to vacuuming. Theadhesion layer 112 was composed of CrTi. Regarding the softmagnetic layer 114, the respective compositions of the first softmagnetic layer 114 a and the second softmagnetic layer 114 c were CoCrTaZr, and the composition of thespacer layer 114 b was Ru. The composition of thepreliminary ground layer 116 was a NiW alloy having an fcc structure. As thefirst ground layer 118 a, a Ru film was formed under an Ar atmosphere at a predetermined pressure (low pressure: for example, 0.6 to 0.7 Pa). As thesecond ground layer 118 b, a Ru film containing oxygen was formed under an Ar atmosphere at a higher pressure than the predetermined pressure (high pressure: for example, 4.5 to 7 Pa) by using a target containing oxygen. The composition of the non-magneticgranular layer 120 was non-magnetic CoCr—SiO2. The secondmagnetic recording layer 122 c was caused to contain SiO2 and TiO2 as an example of a composite oxide (plural kinds of oxides) at the grain boundary portion to form the hcp crystal structure of CoCrPt—SiO2—TiO2. Regarding the firstmagnetic recording layer 122 a and thesplit layer 122 b, the following examples and comparative examples that were different in film thickness and composition thereof were produced. The composition of theauxiliary recording layer 126 was CoCrPtB. Themedium protecting layer 128 was formed by CVD method using C2H4 and CN, and thelubricating layer 130 was formed by dip coating using PFPE. -
FIG. 3 is a graph showing the relationship between the film thickness of thesplit layer 122 b and the SNR. The composition of thesplit layer 122 b was Ru in all the cases. InFIG. 3 , the name of a substance attached to each line represents the composition of the firstmagnetic recording layer 122 a. - As shown in
FIG. 3 , in each line, as the film thickness of thesplit layer 122 b increases from a state where thesplit layer 122 b is not provided, that is, 0 nm, the SNR remarkably increases. Then, once the film thickness of thesplit layer 122 b exceeds 1 nm (10 Å), the SNR starts to decrease. When the film thickness reaches 3 nm, the SNR becomes a value lower than in the case where thesplit layer 122 b is not provided. - Because a desired SNR to achieve a higher recording density of the perpendicular
magnetic recording medium 100 is 17.5 dB or more, it can be understood fromFIG. 3 that it is preferred that the film thickness of thesplit layer 122 b is in the range of 0.2 nm to 1.0 nm (2 Å to 10 Å). From this, it is thought that antiferro-magnetic exchange coupling (AFC), which was magnetic interaction, was generated between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c, and the direction of magnetization of the firstmagnetic recording layer 122 a and the direction of magnetization of the secondmagnetic recording layer 122 c were arranged antiparallel to each other and fixed to reduce noise and consequently improve the SNR. - Incidentally, it is thought that the reason why improvement in SNR to a desired value could not be achieved when the thickness of the
split layer 122 b was less than 0.2 nm was because thesplit layer 122 b could not interrupt the magnetism between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c, and could not generate AFC. Also, it is considered that the reason why a desired SNR could not be obtained when the film thickness of thesplit layer 122 b was more than 1.0 nm was because AFC generated between the magnetic recording layers 122 became weak, so that the function of arranging the directions of magnetization of the magnetic recording layers 122 (the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c) or fixing them was reduced and the desired SNR could not be obtained. - Furthermore, in
FIG. 3 , focusing on the oxide contained in the firstmagnetic recording layer 122 a, the four lines can be roughly classified into one line containing SiO2 (4 mol %) and TiO2 (4 mol %) as oxides and the other three lines containing Cr2O3. Then, from comparison between the line containing SiO2 and TiO2 and the lines containing Cr2O3, it can be seen that all the lines show almost the same tendency to improve the SNR when thesplit layer 122 b is provided and reduce the SNR when the film thickness of thesplit layer 122 b becomes excessively thick. From this, it can be understood that the SNR can be improved regardless of the kind of oxide by optimizing the film thickness of thesplit layer 122 b. - Furthermore, focusing on only the lines containing Cr2O3, it can be seen that, as the oxide content of the first
magnetic recording layer 122 a increases from 5 mol % to 7 mol % and further to 9 mol %, the SNR further improves. From this, it is thought that, since the oxide content of the firstmagnetic recording layer 122 a increased, the amount of a substance that formed the grain boundary of the magnetic particles in a columnar shape, namely, a grain boundary portion, in the firstmagnetic recording layer 122 a increased, and consequently the column of the magnetic particles became thinner. -
FIG. 4 is a graph showing the relationship between the composition of thesplit layer 122 b, the SNR, and the track width. Here, the composition of thesplit layer 122 b is Ru in an example 1, RuCo in an example 2, RuCr in an example 3, RuSiO2 in an example 4, Co—Cr in a comparative example 1, and Ni—Cu in a comparative example 2. RuCo, RuCr, and RuSiO2 are Ru alloys. The film thickness of thesplit layer 122 b is 7 Å in all the cases. Note that the track width mentioned above is not an actual track width of the perpendicularmagnetic recording medium 100 but a track width that a track profile obtained in a recordable width test shows a predetermined ratio. - As shown in
FIG. 4 , the examples and the comparative examples exceed the SNR value of 17.5 dB desired for achievement of a high recording density. However, in comparison between the examples and the comparative examples, it can be seen that the examples in which thesplit layer 122 b is composed of Ru or a Ru alloy achieve higher SNRs than the comparative examples. Therefore, it can be seen that it is preferred that Ru or a Ru alloy is used for thesplit layer 122 b in order to achieve a higher recording density. - The track widths of the examples are also narrower than those of the comparative examples. From this, it can also be seen that using Ru or a Ru alloy for the split layer makes it possible to make the track width narrower so that a higher recording density can be achieved.
-
FIG. 5 is a graph showing the relationship between the relationship A/B between the oxide contents of the magnetic recording layers 122, the SNR, and the coercive force Hc. Note that a higher absolute value of the coercive force Hc is better, and therefore the absolute value of the coercive force Hc is shown in the graph. The composition of thesplit layer 122 b was Ru and the film thickness thereof was 7 Å in all the cases. - As shown in
FIG. 5 , as A/B increases, the SNR further improves, but the coercive force Hc decreases. This proves once again that the coercive force Hc and the SNR are in a trade-off relationship. However, by setting A/B in the range of 0.5<A/B<1.0, the two requirements for achievement of a high recording density which are the SNR of 17.5 dB or more and the coercive force Hc of 4800 Oe or more can be satisfied. Therefore, it becomes possible to further improve the SNR while securing a high coercive force Hc so that a higher recording density can be achieved. -
FIG. 6 is a graph showing the relationship between the film thickness of the firstmagnetic recording layer 122 a and the coercive force Hc. InFIG. 6 , also, the coercive force Hc is shown as the absolute value thereof in the graph. InFIG. 6 , the name of a substance attached to each line represents the composition of the firstmagnetic recording layer 122 a. The composition of thesplit layer 122 b was Ru in all the cases, and the film thickness thereof was 7 Å. - As shown in
FIG. 6 , in all the lines, as the film thickness of the firstmagnetic recording layer 122 a increases, the coercive force Hc further improves. Then, the coercive force Hc starts to decrease when the film thickness of the firstmagnetic recording layer 122 a exceeds about 3 nm, and the coercive force Hc becomes lower than in a case where the firstmagnetic recording layer 122 a is not provided, when the film thickness reaches about 4 nm. - Since the coercive force Hc required for a perpendicular magnetic recording medium is 4800 Oe or more, it can be seen from
FIG. 6 that it is preferred that the film thickness of the firstmagnetic recording layer 122 a is in the range of 0.7 nm to 3.0 nm. This makes it possible to achieve a higher recording density of the perpendicularmagnetic recording medium 100 while securing a high coercive force Hc. Since the firstmagnetic recording layer 122 a has a high coercive force Hc, the firstmagnetic recording layer 122 a can act as a pin layer that fixes the direction of magnetization of the secondmagnetic recording layer 122 c. - Furthermore, focusing on the oxide contained in the first
magnetic recording layer 122 c inFIG. 6 , the five lines can be roughly classified into one line containing TiO2 (9 mol %) as an oxide, another line containing SiO2 (4 mol %) and TiO2 (4 mol %), and the other three lines containing Cr2O3. Then, from comparison between the above lines, it can be seen that all the lines show a tendency to improve the coercive force Hc further as the film thickness of the firstmagnetic recording layer 122 a increases, and start to reduce the coercive force Hc when the film thickness becomes excessively thick. This shows that a high coercive force Hc can be secured regardless of the kind of oxide by optimizing the film thickness of the firstmagnetic recording layer 122 a. - As described above, according to the present invention, since the
magnetic recording layer 122 is composed of the firstmagnetic recording layer 122 a, thesplit layer 122 b, and the secondmagnetic recording layer 122 c, and the film thickness and composition of each layer are optimized, the SNR can be further improved while a high coercive force Hc is secured. This makes it possible to achieve a higher recording density of the perpendicularmagnetic recording medium 100. - A second embodiment of the perpendicular magnetic recording medium according to the present invention will be described. Components overlapping with the first embodiment are denoted by the same reference numerals and not repeatedly described.
- In the first embodiment, the structure in which the
split layer 122 b is provided between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c has been described. On the other hand, in the second embodiment, a structure in which asecond split layer 124 is additionally provided between the secondmagnetic recording layer 122 c and theauxiliary recording layer 126 will be described. In the following description, thesplit layer 122 b described in the first embodiment is referred to as “first split layer 122 b”. -
FIG. 7 is a diagram for describing the structure of a perpendicularmagnetic recording medium 100 according to the second embodiment. The perpendicularmagnetic recording medium 100 according to the second embodiment has the same structure as the first embodiment except for themagnetic recording layer 122 and thesecond split layer 124. Themagnetic recording layer 122 is composed of the firstmagnetic recording layer 122 a (first magnetic layer), thefirst split layer 122 b, and the secondmagnetic recording layer 122 c (second magnetic layer), and thesecond split layer 124 and the auxiliary recording layer 126 (third magnetic layer) are formed on themagnetic recording layer 122 in this order. - The
first split layer 122 b is a non-magnetic thin film, and interposed between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c so that magnetic continuity is split between these magnetic layers. Thesplit layer 122 b can be composed of Ru or a Ru alloy, and additionally can contain oxygen or an oxide. Thesplit layer 122 b is configured to have a predetermined film thickness to generate antiferro-magnetic exchange coupling (AFC) between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c. Since this makes the directions of magnetization of the magnetic layers on and just below thefirst split layer 122 b antiparallel to each other, so that the directions of magnetization interact with each other so as to fix the directions of magnetization, fluctuation of the axis of magnetization is reduced, and noise is reduced. - In terms of crystalline structure, the
split layer 122 b is an extremely thin film, and therefore does not disturb the inheritance of the crystal orientation between the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c. Since thefirst split layer 122 b does not contain as much oxygen as the magnetic recording layer, no grain boundary is formed in thefirst split layer 122 b, but it is thought that thefirst split layer 122 b does not disturb crystal growth, since thefirst split layer 122 b is an extremely thin film with a thickness of 1 nm or less and Ru has a hcp structure. - The
second split layer 124 is a non-magnetic layer provided between the magnetic recording layer 122 (the secondmagnetic recording layer 122 c) and theauxiliary recording layer 126. Thesecond split layer 124 can be composed of Ru or a Ru alloy, and additionally can contain oxygen or an oxide. Thesecond split layer 124 is configured to have a predetermined film thickness to generate ferromagnetic exchange coupling (FC) between the secondmagnetic recording layer 122 c and theauxiliary recording layer 126. - Providing the
second split layer 124 thus configured makes it possible to reduce noise thought to be due to theauxiliary recording layer 126 to improve the SNR. It is thought that this is because theauxiliary recording layer 126 can adjust a fine structure inherited from themagnetic recording layer 122 as the effect of crystal structure when theauxiliary recording layer 126 makes crystal growth. In a portion of thesecond split layer 124 positioned on the magnetic particles of themagnetic recording layer 122, Ru causes Co of theauxiliary recording layer 126 to inherit the crystal structure of Co of themagnetic recording layer 122. In a portion of thesecond split layer 124 positioned on the grain boundary of themagnetic recording layer 122, because oxygen and Ru forming the grain boundary are substantially different in lattice constant from each other, inheritance of the crystalline orientation does not occur, but RU and oxygen freely migrate to form a coating film (crystal). Since theauxiliary recording layer 126 is formed on the crystal of Ru, separation of the Co particles of theauxiliary recording layer 126 is further promoted to achieve noise reduction. Therefore, the crystalline orientation of theauxiliary recording layer 126 is improved as a whole. - Even if the split layers (the
first split layer 122 b, the second split layer 124) are composed of only Ru, improvement in OW characteristic or the like can be observed. Ru is preferred, since Ru is close in lattice constant to Co constituting the magnetic particles, and therefore does not easily disturb epitaxial growth of Co crystal particles even if it is interposed between the magnetic layers. However, remarkable improvement in SNR can be observed when the Ru contains oxygen. It is thought that this is because oxygen atoms contained in the split layer has a high affinity for oxygen atoms contained in the grain boundary in the magnetic recording layer, and selectively segregate. Particularly in thesecond split layer 124, it is thought that by causing thesecond split layer 124 to contain a lower percent of oxygen than the percentage of oxide contained in themagnetic recording layer 122, the second split layer is allowed to act as a magnetic and structural bridge between the grain boundary of themagnetic recording layer 122 containing a large amount of oxygen and theauxiliary recording layer 126 containing no oxygen. - Oxygen contained in Ru in the split layer includes either one or both of oxygen atoms as a single body and oxygen atoms as an oxide. Ru is caused to contain a slight amount of oxygen by a method of causing a target to contain oxygen in advance or by reactive sputtering that oxygen is added to atmosphere gas during sputtering. The reactive sputtering is a method of forming a compound film or mixed film of the atoms of a target and the atoms of active gas by adding the active gas to atmosphere gas supplied into a chamber where sputtering is performed. Therefore, by adding oxygen gas as active gas during sputtering of the split layer, the split layer can be caused to contain oxygen.
- However, regarding the reactive sputtering, because a small amount of oxygen gas is added to the atmosphere gas, it is very difficult to adjust the amount of oxygen contained in the split layer to a desired amount. It is also difficult to adjust the active gas so as to distribute evenly in the atmosphere gas, and therefore distribution of oxygen becomes uneven in the split layer. Furthermore, it is difficult to completely evacuate the oxygen gas mixed in the split layer during formation of the split layer, the oxygen gas remaining in the chamber enters a chamber where the layers following the split layer are formed. Therefore, it is preferred that the split layer is subjected to the sputtering using a target made of Ru and an oxide, because oxygen can be caused to be contained evenly in the whole of the film.
- As a specific example, the composition of the split layer may be RuO, RuWO3, or RuTiO2. As described above, it is preferred that the split layer is caused to contain oxygen by causing a target for sputtering to contain an oxide. There are various possible oxides, but in particular, by using an oxide of W, Ti, or Ru, the electromagnetic conversion characteristic (SNR) can be improved. Of them, WO3 can obtain a high effect. This is because WO3 is an unstable oxide, and therefore oxygen is dissociated during sputtering, and the oxygen dissociated also exhibits the effect of oxygen addition. That is, using WO3 produces both the effect of oxygen addition and the effect of oxide addition, and therefore WO3 is preferred. Other examples of the oxide can include silicon oxide (SiOx), chromium (Cr), chromium oxide (CrxOY), titanium oxide (TiO2), zircon oxide (ZrO2), tantalum oxide (Ta2O5), iron oxide (Fe2O3), boron oxide (B2O3), and the like. It is also preferred to use a nitride such as BN or a carbide such as B4O3.
- Incidentally, it is preferred that the
second split layer 124 is non-magnetic, but may be slightly magnetized. RuCo50 can be involved as a specific example. In particular, RuCo50 is superior in improving the SNR because Co can inherit the crystal orientation from the magnetic recording layer toward the auxiliary recording layer. - The thicknesses of the split layers (the
first split layer 122 b, the second split layer 124) may be in a range of 2 Å to 10 Å, respectively. In particular, by setting the thicknesses in the range of 7 Å to 9 Å, strong exchange coupling can be obtained. If the respective film thicknesses of the split layers are set at 10 Å or more, the magnetic layers on and just below the respective split layers are magnetically completely split from each other and inheritance of crystal orientation from one to the other is completely lost. Furthermore, if the film thicknesses become 10 Å or more, the exchange coupling generated between the magnetic layers is weakened, and therefore it becomes impossible to obtain a desired SNR. On the other hand, if the film thicknesses are 2 Å or less, there is a possibility that the split layers cannot form a coating film. The strength of exchange coupling attenuates while fluctuating between FC and AFC according to the thicknesses of the intervening split layers, it is preferred that the film thickness of thesplit layer 122 b is set so as to obtain the peak of AFC, and the film thickness of thesecond split layer 124 is set so as to obtain the peak of FC. The film thicknesses that generate these peaks are obtained by experiment according to the upper and lower magnetic recording layers and the material of the split layers. -
FIG. 8 is a diagram for describing a model of two magnetic couplings composed of the firstmagnetic recording layer 122 a, thefirst split layer 122 b, the secondmagnetic recording layer 122 c, thesecond split layer 124, and theauxiliary recording layer 126. As shown inFIG. 8 , the directions of magnetization of the firstmagnetic recording layer 122 a and the secondmagnetic recording layer 122 c are made antiparallel to each other by AFC coupling, the directions of magnetization of the secondmagnetic recording layer 122 c and theauxiliary recording layer 126 are made parallel to each other by FC coupling, and in both the cases, the action to fix the directions of magnetization mutually occurs. Therefore, the fluctuation of the axis of magnetization is reduced, and accordingly noise is reduced. - Without the
first split layer 122 b, the firstmagnetic recording layer 122 a would be a magnet continuous with the secondmagnetic recording layer 122 c, but here, since thefirst split layer 122 b splits them, the firstmagnetic recording layer 122 a constitutes an individual short magnet. Then, by further reducing the film thickness of the firstmagnetic recording layer 122 a, a height to width ratio of the granular magnetic particles is reduced (in the perpendicular magnetic recording medium, a direction along the film thickness corresponds to an axial direction of an axis of easy magnetization), and thus a diamagnetic field occurring inside the magnet becomes intense. Therefore, even though the firstmagnetic recording layer 122 a is hard magnetic, a magnetic moment generated therefrom outwardly becomes small to such an extent that the magnetic head cannot easily sense it. That is, by adjusting the film thickness of the firstmagnetic recording layer 122 a, the magnetic moment (strength of a magnet) of the firstmagnetic recording layer 122 a is set such that the magnetic flux does not easily reach the magnetic head and such that the firstmagnetic recording layer 122 a magnetically interacts with the secondmagnetic recording layer 122 c, so that themagnetic recording layer 122 that exerts high a coercive force but is reduced in noise can be obtained. - The thickness of the first
magnetic recording layer 122 a may be 5 nm or less. In this case, it is preferred that the firstmagnetic recording layer 122 a is a layer having a small amount of grain boundary portion and having a high coercive force Hc, and the secondmagnetic recording layer 122 c is a layer having a large amount of grain boundary portion (a large amount of oxide) and having a high SNR. This enhances the diamagnetic field of the firstmagnetic recording layer 122 a so that the magnetic moment generated from the firstmagnetic recording layer 122 a can be reduced. Therefore, the noise from the firstmagnetic recording layer 122 a does not reach the magnetic head, and thus the amount of oxide of the firstmagnetic recording layer 122 a can be reduced to increase the coercive force Hc, so that the firstmagnetic recording layer 122 a can act as a pin layer that fixes the direction of magnetization of the secondmagnetic recording layer 122 c. - The
magnetic recording layer 122 may include two or more kinds of oxides. This makes it possible to obtain characteristics of a plurality of oxides, and therefore it becomes possible to obtain a perpendicular magnetic recording medium that achieves further refinement and isolation of the magnetic particles of themagnetic recording layer 122 to reduce noise and improve the SNR so that a high recording density is achieved. - The
magnetic recording layer 122 may include SiO2 and TiO2 as oxides. SiO2 has a characteristic of promoting refinement and isolation of magnetic particles, and TiO2 has a characteristic of improving an electromagnetic conversion characteristic (particularly, SNR). By causing these oxides in combination to segregate to the grain boundary of themagnetic recording layer 122, both their advantages can be gained. - The
magnetic recording layer 122 may include 5 mol % or more of oxide constituting a grain boundary portion. This is because, when 5 mol % or more of oxide is included, high magnetostatic characteristic and electromagnetic conversion characteristic can be obtained, and the characteristic of theauxiliary recording layer 126 is lowered, which cannot be ignored, when the oxide is in such a range, but the characteristic can be improved by providing the abovesecond split layer 124. - The
adhesion layer 112 to theauxiliary recording layer 126 were sequentially formed on thedisk base 110 in an Ar atmosphere by DC magnetron sputtering using an apparatus for film formation that was subjected to vacuuming. Theadhesion layer 112 was composed of CrTi. Regarding the softmagnetic layer 114, the compositions of the first softmagnetic layer 114 a and the second softmagnetic layer 114 c were CoCrTaZr, and the composition of thespacer layer 114 b was Ru. The composition of thepreliminary ground layer 116 was a NiW alloy having an fcc structure. As thefirst ground layer 118 a, a Ru film was formed under an Ar atmosphere at a predetermined pressure (low pressure: for example, 0.6 to 0.7 Pa). As thesecond ground layer 118 b, a Ru film containing oxygen was formed under an Ar atmosphere at a higher pressure than the predetermined pressure (high pressure: for example, 4.5 to 7 Pa) by using a target containing oxygen. The composition of the non-magneticgranular layer 120 was non-magnetic CoCr—SiO2. As the firstmagnetic recording layer 122 a, a film having an hcp crystal structure of CoCrPt—Cr2O3 containing Cr2O3 as an example of an oxide in the grain boundary portion was formed. As the secondmagnetic recording layer 122 c, a film having an hcp crystal structure of CoCrPt—SiO2—TiO2 containing SiO2 and TiO2 as an example of a composite oxide (plural kinds of oxides) in the grain boundary portion was formed. Regarding thefirst split layer 122 b and thesecond split layer 124, the film thicknesses thereof were set at 8 Å and 4 Å, respectively, and the following examples and comparative examples thereof different in composition were produced and compared. The composition of theauxiliary recording layer 126 was CoCrPtB. Themedium protecting layer 128 was formed by CVD method using C2H4 and CN, and thelubricating layer 130 was formed by dip coating using PFPE. -
FIG. 9 is a diagram including a table and a graph, showing examples and comparative examples different in that a split layer is provided or not. An example 11 is an example in which thefirst split layer 122 b and thesecond split layer 124 were provided and the secondmagnetic recording layer 122 c contained plural oxides in combination, an example 12 is an example in which CoO was further added to the secondmagnetic recording layer 122 c as an oxide in the example 12, and an example 13 is a case where the oxide was a single material. A comparative example 11 is an example in which thefirst split layer 122 b and thesecond split layer 124 were not provided, a comparative example 12 is an example in which only thesecond split layer 124 was provided, and a comparative example 13 is an example in which only thefirst split layer 122 b was provided. Regarding each of the examples and comparative examples, the coercive force Hc and the reversed magnetic domain nucleation magnetic field Hn as magnetostatic characteristic, and the SNR as electromagnetic conversion characteristic were measured. Higher absolute values of the coercive force Hc and the reversed magnetic domain nucleation magnetic field Hn are better, and therefore the absolute values thereof are coaxially shown in the graph. - As can be seen in
FIG. 9 , the coercive forces Hc and the reversed magnetic domain nucleation magnetic fields Hn of the examples are improved as compared with those of the comparative examples, in particular, the SNRs thereof are remarkably improved. In comparison among the comparative example 11 to the comparative example 13, the comparative example 12 proves that thesecond split layer 124 improves the SNR, and the comparative example 13 proves that thefirst split layer 122 b also slightly improves the SNR. However, by providing both the split layers like the examples, significant improvement in performance can be achieved. - Comparison between the example 11 and the example 13 reveals that it is more effective to mix plural oxides as the oxide in the second
magnetic recording layer 122 c. The example 12 reveals that the Hc, Hn, and SNR are further increased by adding CoO. -
FIG. 10 is a diagram a table and a graph, showing a result of comparison between examples different in composition of thesecond split layer 124. The example 12 is an example in which thesecond split layer 124 was composed of RuWO2, an example 14 is an example in which thesecond split layer 124 was composed of Ru—SiO2, an example 15 is an example in which thesecond split layer 124 was formed by Ru+O2 exposure, and an example 16 is an example in which thesecond split layer 124 was composed of only Ru. - In
FIG. 10 , it can be seen that the SNRs of the examples 12 to 15 containing oxygen were improved as compared with the example 16 composed of only Ru. Among them, the SNR of the example 12 in which the split layer was composed of RuWO3 was improved the most. - As described above, according to the present invention, the SNR of the magnetic recording layer can be further improved. This makes it possible to achieve a higher recording density of the perpendicular
magnetic recording medium 100. -
FIG. 11 shows TEM photographs of the auxiliary recording layers 126 of the example 11 (a case where thesecond split layer 124 was provided) and the comparative example 11 (a case where thesecond split layer 124 was not provided). Referring toFIG. 4 , it can be seen that the fine structure of theauxiliary recording layer 126 is fuzzy in the comparative example 11, but separation of particles is clearly promoted in the example 11. That is, it can be said that separation of crystal particles is promoted in a magnetic layer disposed on a split layer. This can support that noise reduction of theauxiliary recording layer 126 can be achieved by thesplit layer 124. - As described above, according to the perpendicular
magnetic recording medium 100 according to the first embodiment, the noise thought to be due to the auxiliary recording layer is reduced so that improvement in SNR can be achieved. This makes it possible to achieve a higher recording density of the perpendicularmagnetic recording medium 100. - Hereinabove, the preferred embodiments of the present invention have been described with reference to the appended drawings. Needless to say, however, the present invention is not restricted by these embodiments. It is clear that the person skilled in the art can conceive various modifications or variations within the scope of claims for patent, and it should be understood that these modifications belong to the technical scope of the present invention.
- The present invention can be utilized as a perpendicular magnetic recording medium to be mounted on an HDD or the like of a perpendicular magnetic recording type.
Claims (11)