US20150211177A1 - Press Belt in a Paper-Making Machine - Google Patents

Press Belt in a Paper-Making Machine Download PDF

Info

Publication number
US20150211177A1
US20150211177A1 US14/425,650 US201314425650A US2015211177A1 US 20150211177 A1 US20150211177 A1 US 20150211177A1 US 201314425650 A US201314425650 A US 201314425650A US 2015211177 A1 US2015211177 A1 US 2015211177A1
Authority
US
United States
Prior art keywords
press belt
press
silicon dioxide
cross
plastic matrix
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/425,650
Other languages
English (en)
Inventor
Delphine Delmas
Uwe Matuschczyk
Hermann Reichert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Voith Patent GmbH
Original Assignee
Voith Patent GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Voith Patent GmbH filed Critical Voith Patent GmbH
Assigned to VOITH PATENT GMBH reassignment VOITH PATENT GMBH ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: REICHERT, HERMANN, DELMAS, DELPHINE, MATUSCHCZYK, UWE
Publication of US20150211177A1 publication Critical patent/US20150211177A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21F—PAPER-MAKING MACHINES; METHODS OF PRODUCING PAPER THEREON
    • D21F1/00—Wet end of machines for making continuous webs of paper
    • D21F1/0027—Screen-cloths
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21F—PAPER-MAKING MACHINES; METHODS OF PRODUCING PAPER THEREON
    • D21F3/00—Press section of machines for making continuous webs of paper
    • D21F3/02—Wet presses
    • D21F3/0209—Wet presses with extended press nip
    • D21F3/0218—Shoe presses
    • D21F3/0227—Belts or sleeves therefor
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21F—PAPER-MAKING MACHINES; METHODS OF PRODUCING PAPER THEREON
    • D21F3/00—Press section of machines for making continuous webs of paper
    • D21F3/02—Wet presses
    • D21F3/0209—Wet presses with extended press nip
    • D21F3/0218—Shoe presses
    • D21F3/0227—Belts or sleeves therefor
    • D21F3/0236—Belts or sleeves therefor manufacturing methods
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21F—PAPER-MAKING MACHINES; METHODS OF PRODUCING PAPER THEREON
    • D21F7/00—Other details of machines for making continuous webs of paper
    • D21F7/08—Felts
    • D21F7/086—Substantially impermeable for transferring fibrous webs
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21G—CALENDERS; ACCESSORIES FOR PAPER-MAKING MACHINES
    • D21G1/00—Calenders; Smoothing apparatus
    • D21G1/0066—Calenders; Smoothing apparatus using a special calendering belt

Definitions

  • the invention relates to a press belt for a shoe-press device, having the features of the preamble of claim 1 .
  • the invention furthermore relates to a method for manufacturing a plastic matrix for a press belt of a shoe-press device, having the features of the preamble of claim 12 .
  • Press belts which may be configured, for example, as a closed sleeve of a shoe-press roller or as a transfer belt which is routed as a continuously revolving belt between the fibrous web and the sleeve of the counter roller, are exposed to high mechanical, thermal and also chemical stresses.
  • Press belts of this type typically are composed of a polyurethane matrix which is fiber-reinforced.
  • the polyurethane matrix here may be configured so as to be single-layered or multi-layered, such that the press belt may display a plurality of plies or layers, respectively.
  • the outer surface of the respective press belt may be provided with a structure, such as grooves, blind holes, or similar, in order for dewatering in the press to be optimized.
  • fissures may develop in the press belts, wherein further growth of the fissures may arise, likewise on account of the high mechanical stress.
  • This occurrence of fissure growth may increasingly arise also in press belts having grooves or blind holes.
  • structural and/or functional failure of the press belt may be incurred.
  • the press belts are also exposed to enormous mechanical-cum-dynamic stresses, such that the press belts additionally are subjected to high abrasion.
  • the press belts are exposed to intense chemical stresses in the paper-making machine. In this way, the press belts may be in contact with, for example, water, oil, acids, bases, solvents, or similar, and are at least partially corroded by these media.
  • a press sleeve is thus disclosed in DE19702138 A1, the hardness and resistance to wear of said press sleeve having been increased by additives from rock flour, ceramic, or carbon. It is proposed in DE4411620 A1 to provide only an outer layer of the press sleeve with additives which increase resistance to wear.
  • US2005287373 and US20060118261 disclose press belts which display polydimethyl siloxane.
  • the paper-making machine belts of WO2005090429 and of US2008081179 display nanoparticles, in order to improve resilience in relation to fissure growth, hardness or resilience to abrasion, for example.
  • Paper-making machine belts which display silicon dioxide microparticles are described in EP2330249.
  • the present invention focuses on the object of providing for a press belt of a shoe-press device, and for a method for manufacturing a plastic matrix for a press belt of this type, an improved or at least an alternative embodiment which is distinguished, in particular, by higher resilience to abrasion, a tendency toward fissure formation and toward fissure growth which is lower or at least not worse, and/or by a lower sensitivity in relation to media which are present in a paper-making machine.
  • a press belt for a shoe-press device for dewatering or smoothing a fibrous web, in particular a paper, cardboard, or tissue web is proposed, in which the press belt displays a fiber-reinforced plastic matrix.
  • the fiber-reinforced plastic matrix here may at least in a part-region display a polyurethane material, and polydimethyl siloxane and silicon dioxide microparticles as additives.
  • chemical resistance in relation to the media present in the paper-making machine can be increased on account of the combination of the additives polydimethyl siloxane and silicon microparticles.
  • resilience to abrasion can be improved, and the tendency toward fissure formation and toward fissure growth can be held low.
  • the swelling behavior of the press belt is not or only slightly modified.
  • a balanced stress profile can be created only by way of the combination of additives, such that both resistance to chemicals and the tendency toward fissure formation and toward fissure growth, and resilience to abrasion, are improved in a mutually balanced ratio, without any deterioration of one of these properties or in the further required properties, such as the swelling behavior, for example, occurring.
  • a press belt is to be understood a belt or a sleeve which, together with a fibrous web, is routed through a shoe-press nip which is formed between a static press element, the so-called press shoe, and a cylindrical counter roller.
  • the press shoe is supported on a fixed yoke and is hydraulically pressed against the counter roller.
  • one or a plurality of continuously revolving felts and/or further continuously revolving press belts may be routed through the press nip.
  • the press belt may be implemented as a press sleeve of the shoe-press roller, i.e. as a closed sleeve said press belt is held by two lateral tension disks and rotates about the fixed press shoe.
  • oil for lubricating is applied to the inner side of the press belt.
  • the press belt may be routed over the press shoe and a plurality of guide rollers, as is the case in open shoe presses.
  • the surface of press sleeves may be provided with grooves and/or blind holes.
  • the press belt may also be implemented as a transfer belt which, in order to convey the fibrous web through the shoe-press nip, is routed as a continuously revolving belt between the fibrous web and the sleeve of the counter roller. After the shoe-press nip, the fibrous web is then taken off the press belt with the aid of a suction roller, transferred to another clothing, and supplied to the downstream machine group. It is thus advantageous for the surface of the transfer belt to have adequate adhesion in relation to the fibrous web in order to reliably guide the latter, and for the surface of the transfer belt to have good smoothness and a low tendency toward marking. On the other hand, it is likewise advantageous for the fibrous web to be capable of being easily taken off again.
  • a fiber-reinforced plastic matrix is to be understood as a plastic matrix in which one-, two-, or three-dimensional fiber structures are embedded.
  • the term one-dimensional fiber structure here comprises fibers, endless fibers, yarns, fiber bundles, fiber strands, filaments, filament bundles, rovings, or hybrid forms.
  • the term two-dimensional fiber structure comprises woven fabrics, knitted fabrics, warp-knitted fabrics, non-woven fabrics, cross-laid structures, unidirectionally deposited fiber layers, multiaxial cross-laid structures, mats, knitted goods, woven spacer fabrics, braided hoses, embroideries, sewn goods, peel plies, or hybrid forms.
  • the term three-dimensional fiber structure is to be understood as being substantially a plurality of two-dimensional fiber structures which are layered so as to be on top of one another.
  • the two-dimensional fiber structures here may be configured in different manners. In this way it is conceivable, for example, that a unidirectional fiber layer is followed by a non-woven fabric as the next layer, while a woven fabric may complete the three-dimensional fiber structure.
  • unidirectional two-dimensional fiber structures may also be exclusively used for constructing a three-dimensional fiber structure.
  • the unidirectional two-dimensional fiber structures here may be identically oriented or be variably oriented with respect to their direction. In the event of the latter, a multiaxial cross-laid structure is present.
  • Materials which may be employed for fiber structures are glass fibers, carbon fibers, plastic fibers, aramid fibers, PBO fibers, polyethylene fibers, polyester fibers, polyamide fibers, natural fibers, basalt fibers, quartz fibers, aluminum oxide fibers, silicon carbide fibers, or hybrid forms.
  • Additives are to be understood as materials which are added to the plastic matrix in order to modify the properties of the latter in the desired way and manner.
  • additives are added to the plastic matrix in order to, for example, influence in a targeted manner resilience to abrasion, a low tendency toward fissure formation, a low fissure growth, high resilience in relation to media present in the paper-making machine, such as, for example, water, oil, acids, bases, solvents, or similar, desired surface properties, such as, for example the adhesive capability in relation to a fibrous web, hardness, or similar.
  • desired surface properties such as, for example the adhesive capability in relation to a fibrous web, hardness, or similar.
  • properties which are achieved by way of the fiber reinforcement may be influenced by the additives.
  • pigments, microfibers such as, for example, carbon fibers, glass fibers, or similar, powdered glass, carbon black, clay, montmorillonite, saponite, hectorite, mica, vermiculite, bentonite, nontronite, beidellite, volkonskoite, manadiite, kenyaite, smectite, bederite, silicon carbide, silicic acid salt, metal oxides, or arbitrary mixtures of the aforementioned compounds can be used as further addivitives.
  • a fibrous web is to be understood as a cross-laid structure or a random structure of fibers, respectively, comprising wood fibers, plastic fibers, glass fibers, carbon fibers, additives, auxiliaries, or similar.
  • the fibrous web may be configured as a paper, cardboard, or tissue web, for example, which is substantially composed of wood fibers, with small amounts of other fibers or also additives and auxiliaries being present.
  • At least one further part-region of the fiber-reinforced plastic matrix may be configured as foam.
  • a further part-region of the fiber-reinforced plastic matrix may be configured as foam.
  • higher elasticity and softness of the press belt may advantageously be established.
  • the compressive force may be adjusted in a more exact manner.
  • Foam here is to be understood as bubbles which are separated by walls. If the foam has open pores, the walls are at least in part breached, while in a closed foam the individual bubbles are closed off by the walls.
  • the part-region which displays at least polyurethane, and polydimethyl siloxane and silicon dioxide microparticles as additives, or the further part-region which is configured as foam, may comprise a layer of the press belt, a surface layer of the press belt, a peripheral region of the press belt, or an inner layer of the press belt, for example.
  • the press belt may thus be equipped with the desired surface property but, on account of layers of the press belt which lie on the inside and which are configured in various manners, may be equipped with further advantageous properties.
  • a surface layer which is designed in such a manner, abrasion resistance, an advantageous fissure behavior, and high resilience in relation to the media present in the paper-making machine may be achieved, for example, while sufficiently high elasticity and tear strength can be established by way of inner layers.
  • An inner layer for example configured from a foam, may positively influence elastic behavior and softness of the press belt, without the demanded high resilience of the surface of the press belt deteriorating.
  • a layer or a ply, respectively, of the press belt here is understood to be a region which is delimitable in the direction of thickness in relation to other layers or plies. Delimiting may be performed, for example, by the fiber reinforcement, by the construction of the plastic matrix, by the additive proportions and/or by mechanical properties.
  • the employed polydimethyl siloxane may display a viscosity of 100 to 100,000 mPa*s.
  • Polydimethyl siloxane having a viscosity of 500 to 50,000 mPa*s, optionally of 1000 to 10,000 mPa*s, in particular of 1500 to 5000 mPa*s, and of 2000 to 3000 mPa*s, for example, may also be employed. This relates to a temperature of 25° C.
  • the at least one part-region furthermore may display 0.1 to 10% by weight polydimethyl siloxane. It is also conceivable that the at least one part-region displays 0.1 to 8% by weight, in particular 0.1 to 5% by weight, optionally 0.1 to 3% by weight, and 0.2 to 1.5% by weight polydimethyl siloxane, for example.
  • the silicon dioxide microparticles may display a mean particle size of 2 to 800 ⁇ m. It is also conceivable for the silicon dioxide microparticles which display a mean particle size of 5 to 500 ⁇ m, in particular of 5 to 50 ⁇ m, for example of 10 to 30 ⁇ m, and optionally of 10 to 20 ⁇ m, to be employed.
  • the at least one part-region may display 0.01 to 10% by weight silicon dioxide microparticles. It is also conceivable for the at least one part-region to display 0.01 to 5% by weight, in particular 0.05 to 3% by weight, optionally 0.05 to 0.5% by weight, and for example 0.05 to 2% by weight silicon dioxide microparticles.
  • silicon dioxide nanoparticles having a mean particle size of 10 to 80 nm may be employed in the at least one part-region. It is also conceivable for silicon dioxide nanoparticles which have a mean particle size of 12 to 60 nm, in particular of 14 to 40 nm, for example of 16 to 30 nm, and optionally of 18 to 25 nm, to be employed.
  • the tendency toward fissure formation may be advantageously reduced. Possibly, the tendency toward fissure growth likewise may be reduced.
  • Employing silicon dioxide nanoparticles alone does in turn improve the tendency toward fissure formation, but leads to a deterioration in the resilience to abrasion. By combining the additives, resilience to abrasion of the at least one part-region is increased.
  • the at least one part-region may display 0.01 to 10% by weight silicon dioxide nanoparticles.
  • the at least one polyurethane material may be manufactured from a polyurethane polymer and a cross-linking agent.
  • the polyurethane polymer here may be configured as an MDI prepolymer and/or as a PPDI prepolymer having polyether and/or polycarbonates and/or polycaprolactones as a polyol component.
  • the desired durability and resilience in relation to the wear of the press belt may be advantageously established.
  • a plastic matrix of this type is distinguished by high resilience in relation to media present in the paper-making machine.
  • the cross-linking agent may contain at least one polyether polyol. It is also conceivable for linear polyether polyol, and also linear polypropylene etherpolyol, for example, to be employed.
  • the properties of the plastic matrix with respect to elasticity, hardness, and resilience to media present in the paper-making machine may be advantageously influenced.
  • a method for manufacturing a plastic matrix for a press belt of a shoe-press device for dewatering or smoothing a fibrous web, in particular a paper, cardboard, or tissue web as described above is proposed.
  • the plastic matrix is manufactured from at least one polyurethane prepolymer, at least one cross-linking agent, polydimethyl siloxane, and silicon dioxide microparticles.
  • press belts which display the abovementioned advantages may be advantageously manufactured.
  • silicon dioxide nanoparticles having at least part of the cross-linking agent are mixed to form a nanoparticles mixture which contains 20 to 60% by weight silicon dioxide nanoparticles. It is also conceivable for the nanoparticles mixture to contain 25 to 55% by weight, for example 30 to 50% by weight, in particular 35 to 45% by weight, and optionally 38 to 42% by weight silicon dioxide nanoparticles.
  • the nanoparticles mixture in the downstream method steps may replace the cross-linking agent entirely or by 5 to 40%. Furthermore, it is also conceivable for the nanoparticles mixture to replace the cross-linking agent by 6 to 35%, in particular by 7 to 30%, for example by 9 to 30%, and optionally by 10 to 25%.
  • dispersibility of the reactants of the plastic matrix likewise may be further enhanced. Furthermore, better mixing of the individual reactants of the plastic matrix is also possible on account thereof.
  • the silicon dioxide microparticles can be mixed with the polydimethyl siloxane and, if applicable, with further additives, to form an additive mixture.
  • the latter may subsequently be mixed with at least part of the cross-linking agent. It is conceivable here for silicon dioxide nanoparticles to have already been previously mixed into the cross-linking agent.
  • a homogenous mixture of the reactants of the plastic matrix may advantageously be achieved and both dispersibility and the mixing behavior may be improved.
  • the mean particle size may be determined, for example, by way of laser scattered light methods or by means of dynamic image analysis. By means of dynamic image analysis, particle sizes from 1 ⁇ m to 30 mm may be determined.
  • the laser scattered light methods allow an analysis of particle sizes from 0.3 nm to 1 ⁇ m.
  • the mean particle size is defined according to the measuring method employed according to the respective size range
  • FIG. 1 shows a view of a shoe press having a press sleeve according to one exemplary embodiment of the present invention
  • FIG. 2 shows a view of a press section of a paper-making machine, comprising a shoe press and a conveyor belt, according to one exemplary embodiment of the present invention.
  • FIG. 1 a shoe press 10 which comprises a shoe roller 12 and a counter roller 14 is illustrated. While the counter roller 14 is composed of a rotating roller which is designed in a cylindrical manner, the shoe roller 12 is assembled from a shoe 16 , a static yoke 18 carrying said shoe 16 , and a press sleeve 20 .
  • the shoe 16 here is supported by the yoke 18 and by way of hydraulic press elements (not illustrated) pressed onto the press sleeve 20 revolving around said shoe 16 .
  • a comparatively long press nip 22 results.
  • the shoe press 10 is particularly suitable for dewatering fibrous webs 24 .
  • a fibrous web 24 having one or two press films 26 , 26 ′ is routed through the press nip 22 , wherein the fluid which, on account of the pressure exerted in the press nip 22 on the fibrous web 24 , leaks from the fibrous web 24 and which, apart from water, contains dissolved and undissolved compounds, such as, for example, fibers, fiber fragments, additives and/or auxiliaries, is temporarily received by the press felt or felts 26 , 26 ′, respectively, and by depressions (not illustrated) which are provided in the press sleeve surface.
  • FIG. 2 a detail of a press section of a paper-making machine 30 which comprises a shoe press 10 is shown.
  • the shoe press 10 here comprises a shoe roller 12 which comprises a press sleeve 20 and a press element or shoe 16 , respectively, and a counter roller 14 , wherein a press nip is configured between the shoe 16 and the counter roller 14 .
  • this part of the paper-making machine comprises two suction rollers 28 , 28 ′ and two deflection rollers 30 , 30 ′.
  • a felt 26 which is guided by the suction rollers 28 , 28 ′ and which receives the fibrous web 24 on the suction roller 28 , is routed through the press nip.
  • a routed conveyor belt or transfer belt 32 is routed through the press nip by the deflection rollers 30 , 30 ′ below the felt 26 which guides the fibrous web 24 , wherein the transfer belt 32 in the press nip takes over the fibrous web 24 from the felt 26 and conveys away said fibrous web 24 from the press nip via the deflection roller 30 ′.
  • fluid leaks from the fibrous web 24 which fluid apart from water contains dissolved and undissolved compounds, for example fibers, fiber fragments, additives and/or auxiliaries, and is temporarily received by the felt 26 and by depressions which are provided in the press sleeve surface.
  • the fluid which has been received by the press sleeve is thrown off by the press sleeve 20 , before the press sleeve 20 again enters into the press nip.
  • water which has been received by the felt 26 is removed after leaving the press nip by suction elements which are provided on the suction roller 28 ′.
  • resilience to abrasion is significantly improved, in particular post water storage, on account of adding polydimethyl siloxane—silicon dioxide microparticles.
  • the tendency toward fissure formation here is substantially unchanged.
  • resilience to abrasion can be improved while the tendency toward fissure growth remains almost unchanged.
  • An MDI-polyether-prepolymer having an NCO content of approx. 6% is employed.
  • MCDEA and PTHF200 are used as a cross-linking agent, and cross-linking is performed at a temperature of 90° C.
  • the prepolymer, the MCDEA and the PTHF200 are separately degassed, using a vacuum evaporator. Polydimethyl siloxane-SiO 2 microparticles are added to the cross-linking agent. Then all components are mixed in a vortex mixer. The mixture is poured into steel molds and tempered.
  • Resilience to abrasion determination was performed according to DIN 5316 and ISO 4649. To this end, a specimen piece having a diameter of 16 mm was impinged with a testing force of 10 N. The grinding length was 40 m at an angular speed of 40 revolutions per min.
  • Fissure growth determination is performed in a flexural fatigue machine. To this end, the specimen is flexed 1,000,000 times at a frequency of 7.5 Hz, at an angle of +/ ⁇ 40°. A section in the specimen displays a width of 6 mm and a depth of 2.5 mm.

Landscapes

  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Paper (AREA)
US14/425,650 2012-09-04 2013-08-29 Press Belt in a Paper-Making Machine Abandoned US20150211177A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
DE102012215612.7 2012-09-04
DE102012215612 2012-09-04
PCT/EP2013/067858 WO2014037268A1 (fr) 2012-09-04 2013-08-29 Bande de pressage dans une machine à papier

Publications (1)

Publication Number Publication Date
US20150211177A1 true US20150211177A1 (en) 2015-07-30

Family

ID=49080881

Family Applications (1)

Application Number Title Priority Date Filing Date
US14/425,650 Abandoned US20150211177A1 (en) 2012-09-04 2013-08-29 Press Belt in a Paper-Making Machine

Country Status (5)

Country Link
US (1) US20150211177A1 (fr)
EP (1) EP2893079A1 (fr)
CN (1) CN104603358A (fr)
CA (1) CA2883016A1 (fr)
WO (1) WO2014037268A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10731294B2 (en) * 2015-04-07 2020-08-04 Yamauchi Corporation Shoe press belt

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FI20216016A1 (en) * 2021-09-30 2023-03-31 Valmet Technologies Oy Band

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050208288A1 (en) * 2004-03-16 2005-09-22 Cheng-Kuang Li Belts and roll coverings having a nanocomposite coating
US20050287373A1 (en) * 2004-06-25 2005-12-29 Ichikawa Co., Ltd. Papermaking machine belt
US20060118261A1 (en) * 2004-11-16 2006-06-08 Ichikawa Co., Ltd. Shoe press belt
US20100130701A1 (en) * 2007-07-05 2010-05-27 Tamfelt Pmc Oy Shoe press belt
US20110127000A1 (en) * 2009-11-27 2011-06-02 Ichikawa Co., Ltd. Process belt for papermaking and method for making the same

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4830905A (en) * 1988-08-22 1989-05-16 Appleton Mills Papermaker's felt incorporating a closed cell polymeric foam layer
JP3831851B2 (ja) * 1999-09-29 2006-10-11 イチカワ株式会社 シュープレス用ベルト
US20040014383A1 (en) * 2002-07-19 2004-01-22 Atsushi Ishino Belt for papermaking machine and manufacturing method therefor
JP4133433B2 (ja) * 2003-02-26 2008-08-13 イチカワ株式会社 抄紙用プレスフェルト
US7156956B2 (en) * 2003-08-11 2007-01-02 Albany International Corp. Paper industry process belt with a surface structure composed of a porous membrane
JP2006144139A (ja) * 2004-11-16 2006-06-08 Ichikawa Co Ltd シュープレス用ベルト
DE102007019960A1 (de) * 2007-04-27 2008-11-06 Voith Patent Gmbh Verbesserungen bei Transferbändern, Hintergrund der Erfindung

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050208288A1 (en) * 2004-03-16 2005-09-22 Cheng-Kuang Li Belts and roll coverings having a nanocomposite coating
US20050287373A1 (en) * 2004-06-25 2005-12-29 Ichikawa Co., Ltd. Papermaking machine belt
US20060118261A1 (en) * 2004-11-16 2006-06-08 Ichikawa Co., Ltd. Shoe press belt
US20100130701A1 (en) * 2007-07-05 2010-05-27 Tamfelt Pmc Oy Shoe press belt
US20110127000A1 (en) * 2009-11-27 2011-06-02 Ichikawa Co., Ltd. Process belt for papermaking and method for making the same

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10731294B2 (en) * 2015-04-07 2020-08-04 Yamauchi Corporation Shoe press belt

Also Published As

Publication number Publication date
EP2893079A1 (fr) 2015-07-15
CA2883016A1 (fr) 2014-03-13
WO2014037268A1 (fr) 2014-03-13
CN104603358A (zh) 2015-05-06

Similar Documents

Publication Publication Date Title
RU2404221C2 (ru) Ремни с полиуретановым покрытием и покрытия валов, содержащие нанонаполнители
US9777433B2 (en) Shoe press belt
KR101340402B1 (ko) 습지 반송용 벨트
CN102094351B (zh) 抄纸用操作带及其制造方法
US7909965B2 (en) Shoe press belt
JP6985490B2 (ja) プレススリーブおよびその使用
JP7174103B2 (ja) ポリマー構成要素の改良された耐摩耗性のための組成物及び方法
CA2732288C (fr) Toile pour machines a papier et procede de fabrication connexe
US8282785B2 (en) Roll cover and a covered roll
EP2711457A1 (fr) Bande pour transférer une bande de papier humide
US20150211177A1 (en) Press Belt in a Paper-Making Machine
CN103243603B (zh) 造纸靴形压榨带
JP5539656B2 (ja) 製紙用プレスフェルト及びその製造方法
US20050081570A1 (en) Paper machine belt
EP3098347B1 (fr) Courroie de transfert d'une bande de papier humide
JP2022501528A (ja) プレスカバー、プレスカバーの使用、ならびにプレスロール、シュープレス、およびプレスカバーにおける補強繊維の使用
JP4673359B2 (ja) 製紙用ドライヤーカンバス
JP5755696B2 (ja) 製紙用プレスフェルト及びその製造方法
JP2022169404A (ja) 製紙用ベルトおよび製紙用ベルトの製造方法
JP2010159810A (ja) ロール材用フェルト
UA30872U (uk) Спосіб виготовлення нетканого голкопробивного матеріалу
JP2014125712A (ja) 製紙用フェルト及びその製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: VOITH PATENT GMBH, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DELMAS, DELPHINE;MATUSCHCZYK, UWE;REICHERT, HERMANN;SIGNING DATES FROM 20150130 TO 20150202;REEL/FRAME:035094/0036

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION