US20150179482A1 - Producing method of encapsulating layer-covered semiconductor element and producing method of semiconductor device - Google Patents
Producing method of encapsulating layer-covered semiconductor element and producing method of semiconductor device Download PDFInfo
- Publication number
- US20150179482A1 US20150179482A1 US14/414,921 US201314414921A US2015179482A1 US 20150179482 A1 US20150179482 A1 US 20150179482A1 US 201314414921 A US201314414921 A US 201314414921A US 2015179482 A1 US2015179482 A1 US 2015179482A1
- Authority
- US
- United States
- Prior art keywords
- encapsulating
- layer
- encapsulating layer
- peeling
- semiconductor element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for producing an encapsulating layer-covered semiconductor element includes a disposing step of disposing a semiconductor element on a support, an encapsulating step of embedding and encapsulating the semiconductor element by an encapsulating layer in an encapsulating sheet including a peeling layer and the encapsulating layer laminated below the peeling layer and made from a thermosetting resin before complete curing, and a heating step of heating and curing the encapsulating layer after the encapsulating step. The heating step includes a first heating step in which the encapsulating sheet is heated under a normal pressure at a first temperature, a peeling step in which the peeling layer is peeled from the encapsulating layer after the first heating step, and a second heating step in which the encapsulating layer is heated at a second temperature that is higher than the first temperature after the peeling step.
Description
- The present invention relates to a method for producing an encapsulating layer-covered semiconductor element and a method for producing a semiconductor device, to be specific, to a method for producing an encapsulating layer-covered semiconductor element and a method for producing a semiconductor device using the encapsulating layer-covered semiconductor element obtained by the method for producing an encapsulating layer-covered semiconductor element.
- It has been conventionally known that a semiconductor element such as a light emitting diode is encapsulated by a resin.
- A method for producing an optical semiconductor device has been proposed (ref: for example, the following Patent Document 1). In the method, for example, an encapsulating sheet having a substrate sheet and a silicone resin layer laminated below the substrate sheet is disposed on a board mounted with a light emitting diode and next, the light emitting diode is embedded and encapsulated by the silicone resin layer. Thereafter, the encapsulating sheet is heated at 120 to 250° C., the silicone resin layer (an encapsulating layer) is cured, and subsequently, the substrate sheet is peeled from the encapsulating layer to produce the optical semiconductor device.
- Patent Document 1: Japanese Unexamined Patent Publication No. 2013-095809
- In the method described in
Patent Document 1, however, there is a disadvantage that an encapsulating layer is deformed during heating. Also, there is a disadvantage that the substrate sheet is deformed during heating, so that along with the deformation of the substrate sheet, the encapsulating layer is further deformed. - It is an object of the present invention to provide a method for producing an encapsulating layer-covered semiconductor element and a method for producing a semiconductor device that are capable of obtaining a desired encapsulating layer by preventing deformation of a peeling layer and preventing deformation of the encapsulating layer.
- In order to achieve the above-described object, a method for producing an encapsulating layer-covered semiconductor element of the present invention includes a disposing step of disposing a semiconductor element on a support, an encapsulating step of embedding and encapsulating the semiconductor element by an encapsulating layer in an encapsulating sheet including a peeling layer and the encapsulating layer laminated below the peeling layer and made from a thermosetting resin before complete curing, and a heating step of heating and curing the encapsulating layer after the encapsulating step, wherein the heating step includes a first heating step in which the encapsulating sheet is heated under a normal pressure at a first temperature, a peeling step in which the peeling layer is peeled from the encapsulating layer after the first heating step, and a second heating step in which the encapsulating layer is heated at a second temperature that is higher than the first temperature after the peeling step.
- According to this method, in the first heating step, the encapsulating sheet is heated under a normal pressure at the first temperature that is a relatively low temperature, so that the shape of the encapsulating layer is retained, while the encapsulating layer is in tight contact with the peeling layer and thus, the deformation of the encapsulating layer is capable of being suppressed.
- Also, the first heating step is performed before the peeling step, so that in the encapsulating layer that is subjected to the peeling step, the curing thereof is further progressed and thus, in the peeling step after the first heating step, a peeling of the peeling layer from the encapsulating layer is capable of being surely performed by causing an interfacial peeling on the border between the peeling layer and the encapsulating layer. As a result, a desired encapsulating layer is capable of being obtained.
- Furthermore, in the peeling step, after the peeling layer is peeled from the encapsulating layer, in the second heating step, when the encapsulating layer is heated at the second temperature that is a relatively high temperature, the peeling layer is already peeled from the encapsulating layer, so that the deformation of the peeling layer based on a difference in a linear expansion coefficient between the peeling layer and the encapsulating layer and accordingly, the deformation of the encapsulating layer is capable of being prevented.
- In the method for producing an encapsulating layer-covered semiconductor element of the present invention, it is preferable that the encapsulating layer after the first heating step has a compressive elastic modulus at 23° C. of 0.15 MPa or more.
- According to this method, the compressive elastic modulus at 23° C. of the encapsulating layer after the first heating step is 0.15 MPa or more. Thus, the peeling layer is capable of being surely peeled from the encapsulating layer in the peeling step.
- In the method for producing an encapsulating layer-covered semiconductor element of the present invention, it is preferable that the encapsulating layer in the encapsulating step is in a B-stage state of a two-step thermosetting resin composition.
- According to this method, the encapsulating layer in the encapsulating step is in a B-stage state of the two-step thermosetting resin composition, so that in the encapsulating step, the shape of the encapsulating layer is capable of being surely retained. Thus, the semiconductor element is capable of being surely embedded and encapsulated, while the shape of the encapsulating layer is retained.
- In the method for producing an encapsulating layer-covered semiconductor element of the present invention, it is preferable that the encapsulating layer contains a filler and/or a phosphor.
- According to this method, the shape retaining properties of the encapsulating layer after the first heating step is capable of being improved.
- In the method for producing an encapsulating layer-covered semiconductor element of the present invention, it is preferable that the first temperature has a temperature rising range in which the temperature rises up to the second temperature.
- According to this method, the production efficiency of the encapsulating layer-covered semiconductor element is capable of being improved.
- In the method for producing an encapsulating layer-covered semiconductor element of the present invention, it is preferable that the support is a board and in the disposing step, the semiconductor element is mounted on the board.
- According to this method, the deformation of the encapsulating layer is prevented and the encapsulating layer that is completely cured is capable of being mounted on the board, so that the encapsulating layer-covered semiconductor element having excellent reliability is capable of being produced.
- A method for producing a semiconductor device of the present invention includes the steps of producing an encapsulating layer-covered semiconductor element and mounting the encapsulating layer-covered semiconductor element on a board, wherein the encapsulating layer-covered semiconductor element is produced by the method for producing an encapsulating layer-covered semiconductor element including a disposing step of disposing a semiconductor element on a support, an encapsulating step of embedding and encapsulating the semiconductor element by an encapsulating layer in an encapsulating sheet including a peeling layer and the encapsulating layer laminated below the peeling layer and made from a thermosetting resin before complete curing, and a heating step of heating and curing the encapsulating layer after the encapsulating step, and the heating step includes a first heating step in which the encapsulating sheet is heated under a normal pressure at a first temperature, a peeling step in which the peeling layer is peeled from the encapsulating layer after the first heating step, and a second heating step in which the encapsulating layer is heated at a second temperature that is higher than the first temperature after the peeling step.
- According to this method, the encapsulating layer-covered semiconductor element including the encapsulating layer that is completely cured and in which the deformation thereof is prevented is capable of being mounted on the board, so that the semiconductor device having excellent reliability is capable of being produced.
- According to the method for producing an encapsulating layer-covered semiconductor element of the present invention, the deformation of the encapsulating layer is capable of being suppressed.
- In the method for producing a semiconductor device of the present invention, the encapsulating layer-covered semiconductor element including the encapsulating layer that is completely cured and in which the deformation thereof is prevented is capable of being mounted on the board, so that the semiconductor device having excellent reliability is capable of being produced.
-
FIG. 1 shows process drawings for producing a first embodiment of a method for producing a semiconductor device of the present invention: -
FIG. 1A illustrating a disposing step, -
FIG. 1B illustrating an encapsulating step, -
FIG. 1C illustrating a first heating step and a peeling step, and -
FIG. 1D illustrating a second heating step. -
FIG. 2 shows process drawings for producing a second embodiment of a method for producing a semiconductor device of the present invention: -
FIG. 2A illustrating an LED peeling step and -
FIG. 2B illustrating a mounting step. -
FIG. 3 shows process drawings for producing a third embodiment of a method for producing a semiconductor device of the present invention: -
FIG. 3A illustrating a disposing step, -
FIG. 3B illustrating a pressure-welding step, -
FIG. 3C illustrating a pressure exposed step, -
FIG. 3D illustrating a first heating step and a peeling step, and -
FIG. 3E illustrating a second heating step. - In
FIG. 1 , the upper side of the paper surface is referred to as an upper side (one side in a first direction, one side in a thickness direction); the lower side of the paper surface is referred to as a lower side (the other side in the first direction, the other side in the thickness direction); the left side of the paper surface is referred to as a left side (one side in a second direction perpendicular to the first direction); the right side of the paper surface is referred to as a right side (the other side in the second direction); the near side of the paper surface is referred to as a front side (one side in a third direction perpendicular to the first direction and the second direction); and the far side of the paper surface is referred to as a rear side (the other side in the third direction). To be specific, the directions described inFIG. 1 are defined as a reference. Directions in figures subsequent toFIG. 2 are in conformity with the directions inFIG. 1 . - A method for producing an
LED device 1 that is one embodiment of a method for producing an encapsulating layer-covered semiconductor element of the present invention includes a disposing step (ref:FIG. 1A ), an encapsulating step (ref:FIG. 1B ), a first heating step (ref: a solid line inFIG. 1C ), a peeling step (ref: a phantom line inFIG. 1C ), and a second heating step (ref:FIG. 1D ). Hereinafter, each of the steps is described in detail. - [Disposing Step]
- In the disposing step,
LEDs 2, as semiconductor elements, are disposed on aboard 3, as a support. To be specific, theLEDs 2 are mounted on the upper surface of theboard 3. - As shown in
FIG. 1A , theboard 3 is formed into a flat plate shape in a generally rectangular shape in plane view extending in a plane direction (a front-rear direction and a right-left direction). Theboard 3 is formed of a material that is generally used in a board of theLED device 1, such as a metal material including aluminum, a ceramic material including alumina, and a resin material including polyimide. On the upper surface of theboard 3, a conductive pattern (not shown) including an electrode (not shown) that is electrically connected to terminals (not shown) in theLEDs 2 and wires that are continuous to the electrode is formed. The conductive pattern is, for example, formed of a conductor such as gold, copper, silver, and nickel. Theboard 3 has a length of one side of, for example, 1 mm or more, and of, for example, 1000 mm or less. Theboard 3 has a thickness of, for example, 0.7 mm or more, or preferably 0.9 mm or more, and of, for example, 10 mm or less, or preferably 5 mm or less. - Each of the
LEDs 2 is formed into a flat plate shape in a generally rectangular shape in plane view and is provided with a terminal (not shown) on the upper surface or the lower surface thereof. TheLED 2 has a length of one side of, for example, 0.05 mm or more, or preferably 0.1 mm or more, and of, for example, 10 mm or less, or preferably 5 mm or less. TheLED 2 has a thickness of, for example, 5 μm or more, or preferably 10 μm or more, and of, for example, 2000 μm or less, or preferably 1000 μm or less. - As a method for mounting the
LEDs 2 on theboard 3, for example, a flip-chip mounting is used. Or, the terminals in theLEDs 2 are also capable of being wire-bonding connected to the electrode in theboard 3. - A plurality of the
LEDs 2 are mounted on theboard 3. TheLEDs 2 are mounted on the upper surface of theboard 3 at spaced intervals to each other in the plane direction. TheLEDs 2 have a gap in the front-rear direction and the right-left direction of, for example, 0.1 mm or more, or preferably 1 mm or more, and of, for example, 50 mm or less, or preferably 5 mm or less. - [Encapsulating Step]
- In the encapsulating step, as shown in
FIG. 1A , first, an encapsulatingsheet 4 is prepared and thereafter, as shown inFIG. 1B , theLEDs 2 are encapsulated by the encapsulatingsheet 4. - As shown in
FIG. 1A , the encapsulatingsheet 4 includes apeeling layer 5 and anencapsulating layer 6 that is laminated below thepeeling layer 5. - The
peeling layer 5 is a layer that supports theencapsulating layer 6 in the encapsulatingsheet 4 and that is peeled from theencapsulating layer 6 after its use. Examples of a material that forms thepeeling layer 5 include a polymer film such as a polyethylene film and a polyester film (a PET film and the like), a ceramic sheet, and a metal foil. Preferably, a polymer film is used. The surfaces (the upper surface and the lower surface) of thepeeling layer 5 can be also subjected to a release treatment such as a fluorine treatment. In the case of a polymer film, thepeeling layer 5 has a linear expansion coefficient of, for example, 70×10−6K−1 or more, or preferably 80×10−6K−1 or more, and of, for example, 140×10−6K−1 or less, or preferably 120×10−6K−1 or less. Thepeeling layer 5 has a thickness of, for example, 25 μm or more, or preferably 38 μm or more, and of, for example, 2000 μm or less, or preferably 100 μm or less. - The
encapsulating layer 6 is formed from an encapsulating resin composition containing an encapsulating resin into a sheet shape. - An example of the encapsulating resin includes a thermosetting resin that is cured by heating.
- Examples of the thermosetting resin include a silicone resin, an epoxy resin, a polyimide resin, a phenol resin, a urea resin, a melamine resin, and an unsaturated polyester resin. Preferably, a silicone resin is used.
- Examples of the thermosetting resin include a two-step thermosetting resin composition and a one-step thermosetting resin composition. Preferably, a two-step thermosetting resin composition is used.
- The two-step thermosetting resin composition has a two-step reaction mechanism in which a resin composition is brought into a B-stage state (a semi-cured state) in the first-step reaction and is brought into a C-stage state (subjected to a final curing) in the second-step reaction. On the other hand, the one-step thermosetting resin composition has a one-step reaction mechanism in which a resin composition is completely cured in the first-step reaction. The B-stage state is a state between an A-stage state in which a thermosetting resin is in a liquid state and a C-stage state in which the thermosetting resin is completely cured. Also, the B-stage state is a state in which the curing and the gelation of the thermosetting resin are slightly progressed and in which the compressive elastic modulus thereof is smaller than that in a C-stage state.
- An example of an uncured material (before the first-step curing) of the two-step thermosetting resin composition includes an uncured material of a two-step curable type silicone resin composition. Preferably, a condensation reaction and addition reaction curable type silicone resin composition is used.
- The condensation reaction and addition reaction curable type silicone resin composition is a thermosetting silicone resin composition that is capable of undergoing a condensation reaction and an addition reaction by heating. To be more specific, the condensation reaction and addition reaction curable type silicone resin composition is a thermosetting silicone resin composition that is capable of undergoing a condensation reaction to be brought into a B-stage state (a semi-cured state) by heating and next, is capable of undergoing an addition reaction (to be specific, for example, a hydrosilylation reaction) to be brought into a C-stage state (a final curing state) by further heating.
- Examples of the condensation reaction and addition reaction curable type silicone resin composition include a first condensation reaction and addition reaction curable type silicone resin composition that contains a polysiloxane containing silanol groups at both ends, an alkenyl group-containing trialkoxysilane, an organohydrogensiloxane, a condensation catalyst, and a hydrosilylation catalyst; a second condensation reaction and addition reaction curable type silicone resin composition that contains a polysiloxane containing silanol groups at both ends, an ethylenically unsaturated hydrocarbon group-containing silicon compound, an epoxy group-containing silicon compound, an organohydrogensiloxane, a condensation catalyst, and an addition catalyst; a third condensation reaction and addition reaction curable type silicone resin composition that contains a silicone oil containing silanol groups at both ends, an alkenyl group-containing dialkoxyalkylsilane, an organohydrogensiloxane, a condensation catalyst, and a hydrosilylation catalyst; a fourth condensation reaction and addition reaction curable type silicone resin composition that contains an organopolysiloxane having, in one molecule, at least two alkenylsilyl groups, an organopolysiloxane having, in one molecule, at least two hydrosilyl groups, a hydrosilylation catalyst, and a curing retarder; a fifth condensation reaction and addition reaction curable type silicone resin composition that contains a first organopolysiloxane having, in one molecule, both at least two ethylenically unsaturated hydrocarbon groups and at least two hydrosilyl groups, a second organopolysiloxane having, in one molecule, at least two hydrosilyl groups without containing an ethylenically unsaturated hydrocarbon group, a hydrosilylation catalyst, and a hydrosilylation retarder; a sixth condensation reaction and addition reaction curable type silicone resin composition that contains a first organopolysiloxane having, in one molecule, both at least two ethylenically unsaturated hydrocarbon groups and at least two silanol groups, a second organopolysiloxane having, in one molecule, at least two hydrosilyl groups without containing an ethylenically unsaturated hydrocarbon group, a hydrosilylation retarder, and a hydrosilylation catalyst; a seventh condensation reaction and addition reaction curable type silicone resin composition that contains a silicon compound, and a boron compound or an aluminum compound; and an eighth condensation reaction and addition reaction curable type silicone resin composition that contains a polyaluminosiloxane and a silane coupling agent.
- These condensation reaction and addition reaction curable type silicone resin compositions can be used alone or in combination of two or more.
- As the condensation reaction and addition reaction curable type silicone resin composition, preferably, a fourth condensation reaction and addition reaction curable type silicone resin composition is used.
- The fourth condensation reaction and addition reaction curable type silicone resin composition is described in Japanese Unexamined Patent Publication No. 2011-219597 or the like and contains, for example, a dimethylvinylsilyl-terminated polydimethylsiloxane, a trimethylsilyl-terminated dimethylsiloxane-methylhydrosiloxane copolymer, a platinum-divinyltetramethyldisiloxane complex, and a tetramethylammonium hydroxide.
- On the other hand, the one-step curable type silicone resin composition is a thermosetting silicone resin composition that has a one-step reaction mechanism and in which a silicone resin composition is subjected to a final curing in the first-step reaction.
- An example of the one-step curable type silicone resin composition includes an addition reaction curable type silicone resin composition.
- The addition reaction curable type silicone resin composition contains, for example, an ethylenically unsaturated hydrocarbon group-containing polysiloxane, which serves as a main agent, and an organohydrogensiloxane, which serves as a cross-linking agent.
- Examples of the ethylenically unsaturated hydrocarbon group-containing polysiloxane include an alkenyl group-containing polydimethylsiloxane, an alkenyl group-containing polymethylphenylsiloxane, and an alkenyl group-containing polydiphenylsiloxane.
- In the addition reaction curable type silicone resin composition, the ethylenically unsaturated hydrocarbon group-containing polysiloxane and the organohydrogensiloxane are usually provided in separate packages. To be specific, the addition reaction curable type silicone resin composition is provided as two liquids of A liquid that contains a main agent (the ethylenically unsaturated hydrocarbon group-containing polysiloxane) and B liquid that contains a cross-linking agent (the organohydrogensiloxane). A known catalyst that is necessary for the addition reaction of both components is added in the ethylenically unsaturated hydrocarbon group-containing polysiloxane.
- In the addition reaction curable type silicone resin composition, the main agent (A liquid) and the cross-linking agent (B liquid) are mixed to prepare a liquid mixture. In a step of forming the liquid mixture into the above-described shape of the
encapsulating layer 6, the ethylenically unsaturated hydrocarbon group-containing polysiloxane and the organohydrogensiloxane are subjected to an addition reaction and the addition reaction curable type silicone resin composition is cured, so that a silicone elastomer (a cured material) is formed. - The mixing ratio of the encapsulating resin with respect to 100 parts by mass of the encapsulating resin composition is, for example, 20 parts by mass or more, or preferably 50 parts by mass or more, and is, for example, 99.9 parts by mass or less, or preferably 99.5 parts by mass or less.
- A phosphor and a filler can be also contained in the encapsulating resin composition as required.
- An example of the phosphor includes a yellow phosphor that is capable of converting blue light into yellow light. An example of the phosphor includes a phosphor obtained by doping a metal atom such as cerium (Ce) or europium (Eu) into a composite metal oxide, a metal sulfide, or the like.
- To be specific, examples of the phosphor include a garnet type phosphor having a garnet type crystal structure such as Y3Al5O12:Ce (YAG (yttrium aluminum garnet):Ce), (Y, Gd)3Al5O12:Ce, Tb3Al3O12:Ce, Ca3Sc2Si3O12:Ce, and Lu2CaMg2(Si, Ge)3O12:Ce; a silicate phosphor such as (Sr, Ba)2SiO4:Eu, Ca3SiO4Cl2:Eu, Sr3SiO5:Eu, Li2SrSiO4:Eu, and Ca3Si2O7:Eu; an aluminate phosphor such as CaAl12O19:Mn and SrAl2O4:Eu; a sulfide phosphor such as ZnS:Cu,Al, CaS:Eu, CaGa2S4:Eu, and SrGa2S4:Eu; an oxynitride phosphor such as CaSi2O2N2:Eu, SrSi2O2N2:Eu, BaSi2O2N2:Eu, and Ca-α-SiAlON; a nitride phosphor such as CaAlSiN3:Eu and CaSi5N8:Eu; and a fluoride-based phosphor such as K2SiF6:Mn and K2TiF6:Mn. Preferably, a garnet type phosphor is used, or more preferably, Y3Al5O12:Ce is used. These phosphors can be used alone or in combination of two or more.
- Examples of a shape of the phosphor include a sphere shape, a plate shape, and a needle shape. Preferably, in view of fluidity, a sphere shape is used.
- The phosphor has an average value of the maximum length (in the case of a sphere shape, the average particle size) of, for example, 0.1 μm or more, or preferably 1 μm or more, and of, for example, 200 μm or less, or preferably 100 μm or less.
- The mixing ratio of the phosphor with respect to 100 parts by mass of the encapsulating resin composition is, for example, 0.1 parts by mass or more, or preferably 0.5 parts by mass or more, and is, for example, 80 parts by mass or less, or preferably 50 parts by mass or less.
- Examples of the filler include silicone microparticles, glass, alumina, silica, titania, zirconia, talc, clay, and barium sulfate. These fillers can be used alone or in combination of two or more. Preferably, silicone microparticles and silica are used.
- The mixing ratio of the filler with respect to 100 parts by mass of the encapsulating resin composition is, for example, 0.1 parts by mass or more, or preferably 0.5 parts by mass or more, and is, for example, 80 parts by mass or less, or preferably 50 parts by mass or less.
- In addition, a known additive can be added to the encapsulating resin composition at an appropriate proportion. Examples of the known additive include modifiers, surfactants, dyes, pigments, discoloration inhibitors, and ultraviolet absorbers.
- When the
encapsulating layer 6 is a two-step thermosetting resin composition, theencapsulating layer 6 is prepared from a first-step cured material of the two-step thermosetting resin composition and when theencapsulating layer 6 is a one-step thermosetting resin composition, theencapsulating layer 6 is prepared from an uncured material (before curing) of the one-step thermosetting resin composition. - Particularly preferably, the
encapsulating layer 6 is a first-step cured material of the two-step curable type silicone resin composition. That is, particularly preferably, theencapsulating layer 6 is in a B-stage state of the two-step thermosetting resin composition. - In order to form the
encapsulating layer 6, for example, the above-described encapsulating resin composition (containing a phosphor, a filler, or the like as required) is applied onto thepeeling layer 5 so as to have an appropriate thickness by, for example, an application method such as a casting, a spin coating, or a roll coating and the applied laminate is heated as required. In this way, theencapsulating layer 6 in a sheet shape is formed on thepeeling layer 5. - The
encapsulating layer 6 has a compressive elastic modulus at 23° C. of, for example, 0.15 MPa or less, preferably 0.12 MPa or less, or more preferably 0.1 MPa or less, and of, for example, 0.01 MPa or more, or preferably 0.02 MPa or more. When the compressive elastic modulus of theencapsulating layer 6 is not more than the above-described upper limit, the flexibility of theencapsulating layer 6 can be secured. On the other hand, when the compressive elastic modulus of theencapsulating layer 6 is not less than the above-described lower limit, the shape retaining properties of theencapsulating layer 6 are ensured and theLEDs 2 can be embedded by theencapsulating layer 6. - The
encapsulating layer 6 has a linear expansion coefficient of, for example, 150×10−6K−1 or more, or preferably 200×10−6K−1 or more, and of, for example, 400×10−6K−1 or less, or preferably 300×10−6K−1 or less. There may be a case where the larger a value (a difference) obtained by deducting the linear expansion coefficient of thepeeling layer 5 from that of theencapsulating layer 6 is, the more easily theencapsulating layer 6 is deformed. The linear expansion coefficient is measured by TMA (thermomechanical analysis). - As referred in
FIG. 1A , theencapsulating layer 6 is formed into a generally rectangular sheet shape in plane view. Theencapsulating layer 6 is adjusted to have a size that is capable of collectively encapsulating a plurality of theLEDs 2. Theencapsulating layer 6 has a thickness of, for example, 100 μm or more, preferably 300 μm or more, or more preferably 400 μm or more, and of, for example, 2000 μm or less, or preferably 1000 μm or less. - The
encapsulating layer 6 can be also formed of a plurality of layers. Theencapsulating layer 6 can be formed of, for example, afirst layer 61 and asecond layer 62 that is formed on the upper surface of thefirst layer 61. Thesecond layer 62 is laminated on the lower surface of thepeeling layer 5. Thefirst layer 61 and thesecond layer 62 are formed to have an appropriate thickness. - In this way, the encapsulating
sheet 4 including thepeeling layer 5 and theencapsulating layer 6 is prepared. - Thereafter, as shown in
FIG. 1B , theLEDs 2 are encapsulated by the encapsulatingsheet 4. To be specific, theLEDs 2 are embedded and encapsulated by theencapsulating layer 6 in the encapsulatingsheet 4. When theencapsulating layer 6 is formed of thefirst layer 61 and thesecond layer 62, theLEDs 2 are embedded by thefirst layer 61. - To be specific, as shown in
FIG. 1A , first, the encapsulatingsheet 4 is disposed at the upper side of theboard 3 so that theencapsulating layer 6 faces downwardly and next, as shown inFIG. 1B , theencapsulating layer 6 is pressure-welded to theboard 3 with a pressing machine or the like. - Preferably, the encapsulating
sheet 4 and theboard 3 are disposed in opposed relation to each other and then, are put into a vacuum chamber such as a vacuum pressing machine. Next, the pressure in the vacuum chamber is reduced. To be specific, the pressure in the vacuum chamber is evacuated with a vacuum pump (a pressure-reducing pump) or the like. Thereafter, the inside of the vacuum chamber is brought into a reduced pressure atmosphere and theencapsulating layer 6 is pressure-welded to theboard 3 with a pressing machine of the vacuum pressing machine or the like. The reduced pressure atmosphere is, for example, 300 Pa or less, preferably 100 Pa or less, or particularly preferably 50 Pa or less. Thereafter, theboard 3 and theencapsulating layer 6 are exposed to an atmospheric pressure atmosphere. - The temperature in the encapsulating step is adjusted to be a temperature at which the
encapsulating layer 6 is not completely cured, to be specific, a temperature at which a B-stage state is retained when theencapsulating layer 6 is in a B-stage state. The temperature in the encapsulating step is, for example, 0° C. or more, or preferably 15° C. or more, and is, for example, 30° C. or less, or preferably 25° C. or less. To be specific, the temperature in the encapsulating step is a normal temperature (to be specific, 20 to 25° C.). - In this way, the
LEDs 2 are embedded and encapsulated at a normal temperature by theencapsulating layer 6. - That is, the upper surface and the side surfaces (the left surface, the right surface, the front surface, and the rear surface) of each of the
LEDs 2 and the upper surface of theboard 3 that is exposed from theLEDs 2 are covered with theencapsulating layer 6. - [First Heating Step]
- The first heating step is a heating step of, after the encapsulating step, heating the
encapsulating sheet 4 under a normal pressure at the first temperature. - The normal pressure is a state in which the
encapsulating sheet 4 is not subjected to a fluid pressurizing or a mechanically pressurizing. To be specific, the normal pressure is a state in which theencapsulating sheet 4 is in a no-load state under a normal pressure atmosphere (an atmospheric pressure, that is, about 0.1 MPa). - In order to heat the encapsulating
sheet 4 under a normal pressure at the first temperature, for example, a normal pressure-heating device such as a heating oven (to be specific, a drying oven or the like) and a hot plate is used. Preferably, a heating oven is used. - The first temperature is selected as a fixed temperature (a constant temperature) from the above-described range.
- The first temperature and the heating duration thereof are set so that the compressive elastic modulus at 23° C. of the
encapsulating layer 6 after the first heating step is, for example, 0.15 MPa or more, or preferably 0.20 MPa or more. When the compressive elastic modulus is not less than the above-described lower limit, theencapsulating layer 6 in a cured state in which thepeeling layer 5 is capable of being surely peeled from theencapsulating layer 6 in the peeling step (to be specific, when theencapsulating layer 6 is prepared from a two-step thermosetting resin composition, theencapsulating layer 6 in a B-stage state in which the curing is slightly progressed from the B-stage state immediately after the encapsulating step) is capable of being surely prepared. - The first temperature is the temperature at which the above-described
encapsulating layer 6 is not completely cured. To be specific, the first temperature is, for example, 20° C. or more, or furthermore 25° C. or more, and is, for example, less than 75° C., or preferably less than 70° C. When the first temperature is not less than the above-described lower limit, the compressive elastic modulus at 23° C. of theencapsulating layer 6 is set within the above-described range and theencapsulating layer 6 in a cured state in which thepeeling layer 5 is capable of being surely peeled from theencapsulating layer 6 in the peeling step (to be specific, when theencapsulating layer 6 is prepared from a two-step thermosetting resin composition, theencapsulating layer 6 in a B-stage state in which the curing is slightly progressed from the B-stage state immediately after the encapsulating step) is capable of being surely prepared. When the first temperature is not more than the above-described upper limit, the deformation of thepeeling layer 5 caused by a difference in the linear expansion coefficient between thepeeling layer 5 and theencapsulating layer 6 is capable of being suppressed. - The heating duration at the first temperature is, for example, five minutes or more, preferably 10 minutes or more, more preferably one hour or more, or further more preferably 10 hours or more, and is, for example, 50 hours or less, preferably 25 hours or less, or more preferably 20 hours or less. When the heating duration at the first temperature is not less than the above-described lower limit, the compressive elastic modulus at 23° C. of the
encapsulating layer 6 is set within the above-described desired range and theencapsulating layer 6 in a cured state in which thepeeling layer 5 is capable of being surely peeled from theencapsulating layer 6 in the peeling step (to be specific, when theencapsulating layer 6 is prepared from a two-step thermosetting resin composition, theencapsulating layer 6 in a B-stage state in which the curing is slightly progressed from the B-stage state immediately after the encapsulating step) is capable of being surely prepared. On the other hand, when the heating duration at the first temperature is not more than the above-described upper limit, the duration in the first heating step is shortened and the production cost of theLED device 1 is capable of being reduced. - The compressive elastic modulus at 23° C. of the
encapsulating layer 6 after the first heating step is as described above. - By the first heating step, the curing of the
encapsulating layer 6 is slightly progressed from the B-stage state immediately after the encapsulating step, while theencapsulating layer 6 retains the state before complete curing. Among all, when theencapsulating layer 6 is in a B-stage state, by the first heating step, the curing (to be specific, an addition reaction of a condensation reaction and addition reaction curable type silicone resin composition when theencapsulating layer 6 contains the condensation reaction and addition reaction curable type silicone resin composition) is slightly progressed, while theencapsulating layer 6 retains the B-stage state. - [Peeling Step]
- As shown by the phantom line in
FIG. 1C , in the peeling step, thepeeling layer 5 is peeled from theencapsulating layer 6. When theencapsulating layer 6 is formed of thefirst layer 61 and thesecond layer 62, thepeeling layer 5 is peeled from thesecond layer 62. - A laminate made of the
LED 2, theboard 3, and the encapsulatingsheet 4 is, for example, taken out from a normal pressure-heating device and the laminate is cooled to the normal temperature. Thereafter, in the laminate, thepeeling layer 5 is peeled from theencapsulating layer 6. - [Second Heating Step]
- In the second heating step, for example, a (1) normal pressure-heating device, a (2) mechanically pressurizing-heating device, a (3) fluid pressurizing-fluid heating device, or the like is used.
- The (1) normal pressure-heating device is the same as that in the above-described normal temperature-heating device.
- Examples of the (2) mechanically pressurizing-heating device include a hot-pressing device including a flat plate provided with a heater (a mechanically pressurizing-heating device) and a pressing device-including dryer including a pressing device having a flat plate (a fluid pressurizing-heating device).
- The (3) fluid pressurizing-fluid heating device is a device that heats the
encapsulating layer 6 at the second temperature, while theencapsulating layer 6 is fluid pressurized (by a static pressure). To be specific, an autoclave or the like is used. - Preferably, in view of effectively preventing the deformation of the
encapsulating layer 6 before complete curing, a (1) normal pressure-heating device is used. In the case of the (1) normal pressure-heating device, the first heating step and the second heating step are capable of being performed with the same (1) normal pressure-heating device as that in the first heating step, that is, with the same type of the heating device as that in the first heating step, so that the device structure of the production device is capable of being simplified. - The second temperature in the second heating step is the temperature at which the
encapsulating layer 6 is completely cured. When theencapsulating layer 6 after the first heating step is in a B-stage state, the second temperature is the temperature at which theencapsulating layer 6 is brought into a C-stage state. When theencapsulating layer 6 contains a condensation reaction and addition reaction curable type silicone resin composition, the second temperature is the temperature at which the addition reaction of the condensation reaction and addition reaction curable type silicone resin composition is capable of being substantially terminated (completed). To be specific, the second temperature is, for example, 60° C. or more, preferably 75° C. or more, or more preferably 135° C. or more, and is, for example, 200° C. or less, or preferably 180° C. or less. - The heating duration at the second temperature is, for example, 10 minutes or more, or preferably 30 minutes or more, and is, for example, 20 hours or less, preferably 10 hours or less, or more preferably five hours or less.
- The
encapsulating layer 6 is completely cured by the second heating step. Theencapsulating layer 6 that is in a B-stage state in the first heating step is, for example, brought into a C-stage state by the second heating step. When theencapsulating layer 6 contains a condensation reaction and addition reaction curable type silicone resin composition, the addition reaction of the condensation reaction and addition reaction curable type silicone resin composition is substantially terminated (completed). - The
encapsulating layer 6 that is cured (completely cured) after the second heating step has a compressive elastic modulus at 23° C. of, for example, above 0.6 MPa, preferably 1.2 MPa or more, or more preferably 1.4 MPa or more, and of, for example, 15 MPa or less, or preferably 10 MPa or less. - In this way, as shown in
FIG. 1C , theLED device 1 including theboard 3, a plurality of theLEDs 2, and the encapsulatingsheet 4 is produced. - In the
LED device 1, as an encapsulating layer-covered semiconductor element, an encapsulating layer-coveredLED 11 that includes theLEDs 2 and theencapsulating layer 6 covering theLEDs 2 is made on theboard 3. That is, in theLED device 1, the encapsulating layer-coveredLED 11 is mounted on theboard 3. - [Function and Effect]
- According to this method, in the first heating step, the encapsulating
sheet 4 is heated under a normal pressure at the first temperature that is a relatively low temperature, so that the shape of theencapsulating layer 6 is retained, while theencapsulating layer 6 is in tight contact with thepeeling layer 5 and thus, the deformation of theencapsulating layer 6 is capable of being suppressed. - Also, the first heating step is performed before the peeling step, so that in the
encapsulating layer 6 that is subjected to the peeling step, the curing thereof is further progressed and thus, in the peeling step after the first heating step, a peeling of thepeeling layer 5 from theencapsulating layer 6 is capable of being surely performed by causing an interfacial peeling on the border between thepeeling layer 5 and theencapsulating layer 6. As a result, a desiredencapsulating layer 6, that is, theencapsulating layer 6 having a desired thickness and shape is capable of being obtained. - Furthermore, in the peeling step, after the
peeling layer 5 is peeled from theencapsulating layer 6, in the second heating step, when theencapsulating layer 6 is heated at the second temperature that is a relatively high temperature, thepeeling layer 5 is already peeled from theencapsulating layer 6, so that the deformation of thepeeling layer 5 based on a difference in the linear expansion coefficient between thepeeling layer 5 and theencapsulating layer 6, to be specific, a value obtained by deducting the linear expansion coefficient of theencapsulating layer 6 from that of thepeeling layer 5 is within the above-described range and thus, warping of theencapsulating layer 6 based on larger expansion of thepeeling layer 5 than that of theencapsulating layer 6, accordingly, the deformation such as the warping of theencapsulating layer 6 is capable of being prevented. - According to this method, when the compressive elastic modulus at 23° C. of the
encapsulating layer 6 after the first heating step is 0.15 MPa or more, by the first heating step, thepeeling layer 5 is capable of being surely peeled from theencapsulating layer 6 in the peeling step. - In other words, in a case where the compressive elastic modulus at 23° C. of the
encapsulating layer 6 after the first heating step is below the above-described lower limit, when theencapsulating layer 6 is subjected to the peeling step, theencapsulating layer 6 is excessively flexible, so that thepeeling layer 5 is not capable of being peeled from theencapsulating layer 6, to be specific, the interfacial peeling on the border between thepeeling layer 5 and theencapsulating layer 6 is not capable of being performed and thus, a cohesive failure may occur in theencapsulating layer 6. - On the other hand, in a case where the compressive elastic modulus at 23° C. of the
encapsulating layer 6 after the first heating step is not less than the above-described lower limit, when theencapsulating layer 6 is subjected to the second heating step, the shape of theencapsulating layer 6 is sufficiently retained, the above-described cohesive failure fails to occur in the peeling step, and theencapsulating layer 6 is hard enough to cause the interfacial peeling between thepeeling layer 5 and theencapsulating layer 6. Thus, thepeeling layer 5 is capable of being surely peeled from theencapsulating layer 6. As a result, theencapsulating layer 6 having excellent reliability is capable of being obtained. - According to this method, when the
encapsulating layer 6 in the encapsulating step is in a B-stage state of the two-step thermosetting resin composition, in the encapsulating step, the shape of theencapsulating layer 6 is capable of being surely retained. Thus, theLEDs 2 are capable of being surely embedded and encapsulated, while the shape of theencapsulating layer 6 is retained. - In this method, when the
encapsulating layer 6 contains a filler and/or a phosphor, the shape retaining properties of theencapsulating layer 6 after the first heating step are capable of being improved. - According to this method, the deformation of the
encapsulating layer 6 is prevented and theencapsulating layer 6 that is completely cured and has excellent reliability is capable of being mounted on theboard 3, so that the encapsulating layer-coveredLED 11 having excellent reliability, accordingly, theLED device 1 is capable of being produced. - In the above-described first embodiment, a plurality of the
LEDs 2 are disposed on theboard 3. Alternatively, for example, though not shown, a single piece of theLED 2 can be also disposed on theboard 3. - In the above-described first embodiment, the
LED 2 that is a light semiconductor element as a semiconductor element in the present invention is described as one example. Alternatively, for example, though not shown, the semiconductor element can also include an electronic element. - The electronic element is a semiconductor element that converts electrical energy to energy other than light, to be specific, to signal energy or the like. To be specific, examples thereof include a transistor and a diode. The size of the electronic element is appropriately selected in accordance with its use and purpose.
- In this case, the
encapsulating layer 6 contains an encapsulating resin as an essential component and a filler as an optional component. An example of the filler further includes a black pigment such as carbon black. The mixing ratio of the filler with respect to 100 parts by mass of the encapsulating resin is, for example, 5 parts by mass or more, or preferably 10 parts by mass or more, and is, for example, 99 parts by mass or less, or preferably 95 parts by mass or less. - The properties (to be specific, the compressive elastic modulus, the linear expansion coefficient, and the like) of the
encapsulating layer 6 are the same as those in the above-described first embodiment. - [First Temperature]
- In the above-described first embodiment, the first temperature is set to be a fixed temperature, but the first temperature is not limited to this and the first temperature may have, for example, a temperature range. To be specific, the first temperature may have a temperature rising range in which the temperature rises up to the second temperature.
- To be specific, the first temperature has a temperature range of, for example, 20° C. or more, or furthermore, 25° C. or more, and of, less than the second temperature. The temperature rising rate at the first temperature is, for example, 1° C./min or more, or preferably 2° C./min or more, and is, for example, 30° C./min or less, or preferably 20° C./min or less. The temperature rising duration at the first temperature is, for example, 4 minutes or more, or preferably 5 minutes or more, and is, for example, 30 minutes or less, or preferably 12 minutes or less.
- In this case, the same normal pressure-heating device is used in both the first heating step and the second heating step and the peeling step is performed at the inside of the normal pressure-heating device.
- The encapsulating
sheet 4 is, for example, set in the normal pressure-heating device in which the temperature thereof is a room temperature (about 20 to 25° C.) and subsequently, in the first heating step, the temperature is increased so that the temperature at the inside of the normal pressure-heating device reaches the second temperature. Subsequently, the peeling step is performed and thereafter, the second heating step is performed by heating the normal pressure-heating device at the second temperature. - As a result of the first temperature having a temperature rising range in which the temperature rises up to the second temperature, the production efficiency is capable of being improved.
- In the second embodiment, the same reference numerals are provided for members and steps corresponding to each of those in the first embodiment, and their detailed description is omitted.
- In the first embodiment, the support of the present invention is described as the
board 3. Alternatively, for example, as shown by the phantom lines inFIG. 1 , the support of the present invention is also capable of being described as asupport sheet 12. - The second embodiment includes a disposing step (ref:
FIG. 1A ), an encapsulating step (ref:FIG. 1B ), a first heating step (ref: the solid line inFIG. 1C ), a peeling step (ref: the phantom line inFIG. 1C ), a second heating step (ref:FIG. 1D ), and a mounting step (ref:FIGS. 2A to 2C ). Hereinafter, each of the steps is described in detail. - [Disposing Step]
- In the disposing step, as shown in
FIG. 1A , theLEDs 2 are disposed on thesupport sheet 12 as a support. - To be specific, first, the
support sheet 12 is prepared. - The
support sheet 12 is formed into the same plane shape as that of theboard 3 in the first embodiment. As shown by the phantom line inFIG. 1A , thesupport sheet 12 includes asupport board 10 and a pressure-sensitive adhesive layer 15 that is laminated on the upper surface of thesupport board 10. - The
support board 10 is formed into a plate shape extending in the plane direction. Thesupport board 10 is provided in the lower portion in thesupport sheet 12 and is formed into the generally same shape in plane view as that of thesupport sheet 12. Thesupport board 10 is made of a hard material that is incapable of stretching in the plane direction. To be specific, examples of the material include silicon oxide (silica or the like), oxide such as alumina, metal such as stainless steel, and silicon. Thesupport board 10 has a Young's modulus at 23° C. of, for example, 106 Pa or more, preferably 107 Pa or more, or more preferably 108 Pa or more, and of, for example, 1012 Pa or less. When the Young's modulus of thesupport board 10 is not less than the above-described lower limit, the hardness of thesupport board 10 is secured and theLEDs 4 are capable of being further more surely supported. The Young's modulus of thesupport board 10 is obtained from the compressive elastic modulus or the like of JIS H 7902:2008. Thesupport board 10 has a thickness of, for example, 0.1 mm or more, or preferably 0.3 mm or more, and of, for example, 5 mm or less, or preferably 2 mm or less. - The pressure-
sensitive adhesive layer 15 is formed on the entire upper surface of thesupport board 10. An example of a pressure-sensitive adhesive material that forms the pressure-sensitive adhesive layer 15 includes a pressure-sensitive adhesive such as an acrylic pressure-sensitive adhesive and a silicone pressure-sensitive adhesive. The pressure-sensitive adhesive layer 15 can be also formed of an active energy ray irradiation peeling sheet or the like (to be specific, an active energy ray irradiation peeling sheet described in Japanese Unexamined Patent Publication No. 2005-286003 or the like) in which the pressure-sensitive adhesive force is reduced by application of an active energy ray. The pressure-sensitive adhesive layer 15 has a thickness of, for example, 0.1 mm or more, or preferably 0.2 mm or more, and of, for example, 1 mm or less, or preferably 0.5 mm or less. - In order to prepare the
support sheet 12, for example, thesupport board 10 is attached to the pressure-sensitive adhesive layer 15. Also, the pressure-sensitive adhesive layer 15 can be directly laminated on thesupport board 10 by the following application method or the like. In the method, first, thesupport board 10 is prepared; next, a varnish that is prepared from the above-described pressure-sensitive adhesive material and a solvent blended as required is applied to thesupport board 10; and thereafter, the solvent is distilled off as required. - The
support sheet 12 has a thickness of, for example, 0.2 mm or more, or preferably 0.5 mm or more, and of, for example, 6 mm or less, or preferably 2.5 mm or less. - Next, a plurality of the
LEDs 2 are laminated on thesupport sheet 12. To be specific, the lower surface of each of theLEDs 2 is brought into contact with the upper surface of the pressure-sensitive adhesive layer 15. - In this way, a plurality of the
LEDs 2 are disposed on thesupport sheet 12. - [Encapsulating Step]
- In the encapsulating step, as shown in
FIG. 1A , first, the encapsulatingsheet 4 is prepared. Thereafter, as shown inFIG. 1B , theLEDs 2 are encapsulated by the encapsulatingsheet 4 in the same manner as that in the first embodiment. - [First Heating Step, Peeling Step, and Second Heating Step]
- As shown in
FIGS. 1C and 1D , a first heating step, a peeling step, and a second heating step are sequentially performed in the same manner as that in the first embodiment. - The upper limit values of the first temperature and the second temperature in the first heating step are set in view of heat resistance of the
support sheet 12. - In this way, the encapsulating layer-covered
LED 11 in which a plurality of theLEDs 2 are covered with theencapsulating layer 6 is obtained on thesupport sheet 12. - [Mounting Step]
- In the mounting step, first, as shown in
FIG. 2A , the encapsulating layer-coveredLED 11 is peeled from the upper surface of the pressure-sensitive adhesive layer 15 (an LED peeling step). To be specific, when the pressure-sensitive adhesive layer 15 is an active energy ray irradiation peeling sheet, an active energy ray is applied to the pressure-sensitive adhesive layer 15. - In this way, the encapsulating layer-covered
LED 11 that is peeled from thesupport sheet 12 is obtained. - Subsequently, as shown by a dashed line in
FIG. 2A , theencapsulating layer 6 is cut corresponding to each of theLEDs 2. To be specific, theencapsulating layer 6 is cut along the thickness direction. In this way, the encapsulating layer-coveredLEDs 11 are singulated corresponding to each of theLEDs 2. - Thereafter, after the singulated encapsulating layer-covered
LED 11 is selected in accordance with emission wavelength and luminous efficiency, as shown inFIG. 2B , the encapsulating layer-coveredLED 11 is mounted on theboard 3. To be specific, a terminal provided on the lower surface of theLED 2 is connected to an electrode in theboard 3 and the encapsulating layer-coveredLED 11 is flip-chip mounted on theboard 3. - In this way, the
LED device 1 including theboard 3, a single piece of theLED 2, and the encapsulatingsheet 4 is produced. - [Function and Effect]
- In this method, the encapsulating layer-covered
LED 11 including theencapsulating layer 6 that has excellent reliability and is completely cured and in which the deformation thereof is prevented is capable of being mounted on theboard 3, so that theLED device 1 having excellent reliability is capable of being produced. - Among all, in the second embodiment, the
LEDs 2 are disposed on the support sheet 12 (ref: the phantom line inFIG. 1A ) and theLEDs 2 are supported by thesupport sheet 12 with a smaller supporting force than that of theLEDs 2 with respect to theboard 3 in the first embodiment (ref: the solid line inFIG. 1A ). Thus, theLED 2 in the second embodiment is easily shifted (displaced) in the plane direction with respect to theLED 2 in the first embodiment. - In the second embodiment, however, in the first heating step, the encapsulating
sheet 4 is heated at a relatively low temperature, so that the displacement (chip shift) of theLED 2 is capable of being prevented. - In the third embodiment, the same reference numerals are provided for members and steps corresponding to each of those in the first embodiment, and their detailed description is omitted.
- In the first embodiment shown in
FIG. 1A , theboard 3 is formed into a flat plate shape. Alternatively, for example, as shown inFIG. 3A , aconcave portion 7 can be also formed. - The third embodiment includes a disposing step (ref:
FIG. 3A ), an encapsulating step (ref:FIGS. 3B and 3C ), a first heating step (ref: the solid line inFIG. 3D ), a peeling step (ref: the phantom line inFIG. 3D ), and a second heating step (ref:FIG. 3E ). Hereinafter, each of the steps is described in detail. - [Disposing Step]
- As shown in
FIG. 3A , theconcave portion 7 is formed so as to dent downwardly in a rectangular shape in plane view in the upper surface of theboard 3 and is surrounded by a portion other than the concave portion 7 (the circumference) of theboard 3 around theconcave portion 7 in all directions (the front-rear and the right-left directions) without any space. - The
concave portion 7 has a length of one side of, for example, 0.8 mm or more, or preferably 1 mm or more, and of, for example, 300 mm or less, or preferably 100 mm or less. - The
concave portion 7 has a depth H1 (a length, in the up-down direction, between the upper surface of a portion around the concave portion 7 (hereinafter, referred to as a circumferential upper surface 21) and the upper surface of the concave portion 7 (hereinafter, referred to as a concave upper surface 14)) of, for example, 1000 μm or less, preferably 500 μm or less, more preferably 200 μm or less, or particularly preferably 170 μm or less, and of, for example, 10 μm or more, or preferably 50 μm or more. - The depth H1 of the
concave portion 7 with respect to a thickness H2 of theboard 3 is, for example, 90% or less, or preferably 80% or less, and is, for example, 10% or more, or preferably 20% or more. - A plurality of the
LEDs 4 are disposed in theconcave portion 7. The thickness of theLED 4 with respect to the depth H1 of theconcave portion 7 is, for example, 90% or less, or preferably 80% or less. - [Encapsulating Step]
- The encapsulating step includes a pressure-welding step (ref:
FIG. 3B ) and a pressure exposed step (ref:FIG. 3C ). - (Pressure-Welding Step)
- In the pressure-welding step, first, the encapsulating
sheet 4 is prepared. As shown inFIG. 3A , a thickness H3 of theencapsulating layer 6 with respect to the depth H1 of theconcave portion 7 is, for example, 50% or more, preferably 80% or more, or more preferably 100% or more, and is, for example, 900% or less, preferably 700% or less, or more preferably 400% or less. - In the pressure-welding step, next, the prepared encapsulating
sheet 4 is disposed in opposed relation at spaced intervals to the upper side of theboard 3 and then, is put into a vacuum chamber such as a vacuum pressing machine. - Next, the pressure in the vacuum chamber is reduced. To be specific, the pressure in the vacuum chamber is evacuated with a vacuum pump (a pressure-reducing pump) or the like.
- As shown in
FIG. 3B , the inside of the vacuum chamber is brought into a reduced pressure atmosphere and theencapsulating layer 6 in the encapsulatingsheet 4 is pressure-welded to theboard 3 with a pressing machine of the vacuum pressing machine or the like. - The reduced pressure atmosphere in the pressure-welding step is, for example, 300 Pa or less, preferably 100 Pa or less, or particularly preferably 50 Pa or less.
- In the pressure-welding in the pressure-welding step, the amount (hereinafter, defined as a pushed-in amount) in which the
encapsulating layer 6 is pushed into (pressure-welded to) the side of the board 3 (the lower side) is controlled. - By controlling the pushed-in amount, the lower surface of the
encapsulating layer 6 is adjusted so as to be in tight contact with the circumferential upper surface 21 and to be separated from the concaveupper surface 14. - To be specific, the
encapsulating layer 6 is adjusted so that the pushed-in amount shown in the following formula is minus and the absolute value of the pushed-in amount is smaller than the depth H1 of theconcave portion 7. - Pushed-in amount=(height H2 of the concave
upper surface 14 with the bottom surface of theboard 3 as a reference+thickness H3 of theencapsulating layer 6 before the pressure-welding step)−height H4 of the upper surface of theencapsulating layer 6 with the bottom surface of theboard 3 after the pressure-welding step as a reference - When the pushed-in amount is plus, the
encapsulating layer 6 is excessively pressed to such a degree that the thickness (H4−H2) of theencapsulating layer 6 after the pressure-welding step becomes thinner than the thickness H3 of theencapsulating layer 6 before the pressure-welding step. In this way, theencapsulating layer 6 is brought into tight contact with the concaveupper surface 14. In contrast, when the pushed-in amount is minus, theencapsulating layer 6 is adjusted so as to be separated from the concaveupper surface 14. - When the absolute value of the pushed-in amount is larger than the depth H1 of the
concave portion 7, the lower surface of theencapsulating layer 6 is not brought into tight contact with the circumferential upper surface 21 and theconcave portion 7 is not capable of being confined by theencapsulating layer 6. In contrast, when the absolute value of the pushed-in amount is smaller than the depth H1 of theconcave portion 7, theencapsulating layer 6 is adjusted so as to be brought into tight contact with the circumferential upper surface 21. - The absolute value of the pushed-in amount (H2+H3−H4) with respect to the depth H1 of the
concave portion 7 is, for example, less than 100%, or preferably 95% or less, and is, for example, above 0%, or preferably 10% or more. - The temperature in the pressure-welding step is, for example, 0° C. or more, or preferably 15° C. or more, and is, for example, 60° C. or less, or preferably 35° C. or less.
- In the pressure-welding step, the encapsulating
sheet 4 is retained in a state of being pushed down (pushed in) as required. - The duration of retention is, for example, 5 seconds or more, or preferably 10 seconds or more, and is, for example, 10 minutes or less, or preferably 5 minutes or less.
- As shown in
FIG. 3B , by the pressure-welding step, a reduced-pressure space 8 that is, in theconcave portion 7, defined by theboard 3 and theencapsulating layer 6 and is sealed is formed. - The pressure-welding step is performed at, for example, the same temperature as that in the encapsulating step in the first embodiment or preferably at a normal temperature.
- (Pressure Exposed Step)
- As shown in
FIG. 3C , the pressure exposed step is a step of exposing theboard 3 and the encapsulatingsheet 4 to an atmospheric pressure atmosphere. - After the pressure-welding step, by the pressure exposed step, the
encapsulating layer 6 is brought into tight contact with theconcave portion 7 so as to conform to the shape thereof - To be specific, the operation of the vacuum pump is stopped and the pressure in the vacuum chamber is exposed.
- Then, by a differential pressure between a pressure in the reduced-pressure space 8 and the atmospheric pressure, the upper surface of the
encapsulating layer 6 is pressed downwardly and the lower surface of theencapsulating layer 6 is deformed so as to conform to the shape of theconcave portion 7 to be brought into tight contact with the upper surface of theconcave portion 7. - By the pressure exposed step, the
encapsulating layer 6 encapsulates theLEDs 4 so as to be in tight contact with theconcave portion 7. - [First Heating Step, Peeling Step, and Second Heating Step]
- As shown in
FIGS. 3D and 3E , a first heating step, a peeling step, and a second heating step are sequentially performed in the same manner as that in the first embodiment. - In this way, the
LED device 1 is obtained. - [Function and Effect]
- According to the method for producing the
LED device 1, in the pressure-welding step, theencapsulating layer 6 is pressure-welded so as to be separated from the concaveupper surface 14. Thus, when a member around theLEDs 2, to be specific, theLEDs 2 are wire-bonding connected to theboard 3, the stress of theencapsulating layer 6 with respect to a wire at the time of being pressure-welded thereto is capable of being reduced. - On the other hand, in the pressure-welding step, the
encapsulating layer 6 confines the circumferential upper surface 21 under a reduced pressure atmosphere, so that the reduced-pressure space 8 that is, in theconcave portion 7, defined by theboard 3 and theencapsulating layer 6 and is sealed is formed. - Thus, in the pressure exposed step, when the atmospheric pressure is exposed, the
encapsulating layer 6 fills theconcave portion 7 without any space by a differential pressure between a pressure in the reduced-pressure space 8 and the atmospheric pressure. Thus, generation of a void between theboard 3 and theencapsulating layer 6 is capable of being suppressed. - As a result, when the
LEDs 2 are wire-bonding connected to theboard 3, the deformation of the wire (not shown) is capable of being reduced and the generation of the void is capable of being suppressed. - Values in Examples and the like shown in the following can be replaced with the values (that is, the upper limit value or the lower limit value) described in the above-described embodiment.
- A plurality of LEDs were disposed on a board. Each of the LEDs had a thickness of 100 μm and the gap between the LEDs was 1.5 mm.
- [Encapsulating Step]
- An encapsulating sheet was prepared.
- To be specific, 20 g (1.4 mmol of a vinylsilyl group) of a dimethylvinylsilyl-terminated polydimethylsiloxane (a vinylsilyl group equivalent of 0.071 mmol/g); 0.40 g (1.6 mmol of a hydrosilyl group) of a trimethylsilyl-terminated dimethylsiloxane-methylhydrosiloxane copolymer (a hydrosilyl group equivalent of 4.1 mmol/g); 0.036 mL (1.9 μmol) of a xylene solution (a platinum concentration of 2 mass %) of a platinum-divinyltetramethyldisiloxane complex (a hydrosilylation catalyst); and 0.063 mL (57 μmol) of a methanol solution (10 mass %) of a tetramethylammonium hydroxide (TMAH, a curing retarder) were mixed to be stirred at 20° C. for 10 minutes and then, 30 parts by mass of silicone microparticles (Tospearl 2000B, manufactured by Momentive Performance Materials Inc.) were blended with respect to 100 parts by mass of the obtained mixture to be uniformly stirred and mixed, so that a two-step curable type silicone resin composition was obtained.
- Separately, LR7665 (a two-step curable type silicone resin composition, manufactured by Wacker Asahikasei Silicone Co., Ltd.) was applied onto a peeling layer (a thickness of 50 μm, a linear expansion coefficient: 90×10−6K−1) made of a PET film that was subjected to a release treatment, so that a second coated film having a thickness of 200 μm was prepared.
- Next, the second coated film was heated at 105° C. for 10 minutes, so that a second layer having a thickness of 200 μm was obtained.
- Next, the two-step curable type silicone resin composition was applied onto the second layer to prepare a first coated film. The obtained first coated film was heated at 135° C. for 15 minutes, so that a first layer that was made of the two-step curable type silicone resin composition in a semi-cured state (in a B-stage state) and had a thickness of 800 μm was fabricated. In this way, an encapsulating layer made of the second layer and the first layer was fabricated. That is, in this way, an encapsulating sheet including the peeling layer and the encapsulating layer (a thickness of 800 μm, a linear expansion coefficient: 260×10−6K−1) was fabricated (ref:
FIG. 1A ). - The board mounted with the LEDs and the encapsulating layer in the encapsulating sheet were disposed in opposed relation to each other in the thickness direction. The resulting laminate was put into a vacuum chamber of a vacuum pressing machine (model number: CV200, manufactured by Nichigo-Morton Co., Ltd.).
- The pressure in the vacuum chamber was evacuated with a vacuum pump (a pressure-reducing pump) (model number: E2M80, manufactured by Edwards Japan Limited) and the pressure in the vacuum chamber was reduced to be 50 Pa at a normal temperature.
- The board and the encapsulating sheet were pressure-welded to each other under a reduced pressure atmosphere with the vacuum pressing machine to be retained at 20° C. for 3 minutes. Thereafter, the vacuum pump was stopped and the pressure in the vacuum chamber was exposed.
- In this way, the LEDs were encapsulated by the encapsulating layer (ref:
FIG. 1B ). - [First Heating Step]
- The board mounted with the LEDs that were encapsulated by the encapsulating layer was set in a heating oven.
- Next, the inside of the heating oven was set to be 50° C. and the obtained laminate was heated for 12 hours.
- [Peeling Step]
- Thereafter, after the laminate was taken out from the heating oven to be cooled to 25° C., the peeling layer was peeled from the encapsulating layer.
- (Second Heating Step)
- Thereafter, the laminate was again set into the heating oven.
- Next, the temperature at the inside of the heating oven was increased to 150° C. at a temperature rising rate of 2° C./min and the laminate was heated at 150° C. for two hours. In this way, the encapsulating layer was brought into a C-stage state, that is, was completely cured.
- In this way, an LED device including the board, a plurality of the LEDs, and the encapsulating sheet was produced.
- An LED device was produced in the same manner as that in Example 1, except that the heating duration in the first heating step was changed from 12 hours to 18 hours.
- An LED device was produced in the same manner as that in Example 1, except that the heating duration in the first heating step was changed from 12 hours to 24 hours.
- An LED device was produced in the same manner as that in Example 1, except that the temperature and the duration in the first heating step were changed to 150° C. and 14 hours, respectively and the second heating step was not performed.
- An LED device was produced in the same manner as that in Example 1, except that the peeling step was performed after the second heating step.
- An LED device was produced in the same manner as that in Example 1, except that the peeling step was performed after the encapsulating step and before the first heating step.
- (Evaluation)
- (Compressive Elastic Modulus)
- The compressive elastic modulus at 23° C. of each of the encapsulating layers after the encapsulating step, after the first heating step (before the peeling step), and after the second heating step in Examples and Comparative Examples was measured. The compressive elastic modulus was measured in conformity with the description in JIS H 7902:2008.
- (Deformation of Encapsulating Layer and Peeling Layer)
- A presence or absence of deformation and a cohesive mode in each of the encapsulating layers and the peeling layers in the obtained LED devices in Examples and Comparative Examples were visually observed.
- The results are shown in Table 1.
-
TABLE 1 Comp. Ex. 1 Ex. 2 Ex. 3 Comp. Ex. 1 Ex. 2 Comp. Ex. 3 Encapsulating Compressive Elastic After Encapsulating 0.02 0.02 0.02 0.02 0.02 0.02 Layer Modulus (at 23° C.) Step [MPa] After First Heating 0.23 0.28 0.33 Unmeasurable Due 0.23*2 0.23*3 Step (Before to Less Than Lower Peeling Step) Limit of Measuring Device*1 After Second Heating 1.08 1.13 1.18 1.24 1.13 1.08 Step Presence or Absence of Deformation Absence Absence Absence Presence Presence Presence of Unevenness Due to Cohesive Failure Peeling Mode Interfacial Interfacial Interfacial Interfacial Peeling Interfacial Cohesive Failure Peeling Peeling Peeling Peeling Peeling Presence or Absence of Deformation Absence Absence Absence Absence Presence Absence Layer *1First heating step: 150° C. *2Before second heating step *3Peeling step is performed after encapsulating step and before first heating step. - While the illustrative embodiments of the present invention are provided in the above description, such is for illustrative purpose only and it is not to be construed as limiting the scope of the present invention. Modification and variation of the present invention that will be obvious to those skilled in the art is to be covered by the following claims.
- The encapsulating layer-covered semiconductor element and the semiconductor device obtained by a method for producing an encapsulating layer-covered semiconductor element and a method for producing a semiconductor device are used in various semiconductor uses.
Claims (7)
1. A method for producing an encapsulating layer-covered semiconductor element comprising:
a disposing step of disposing a semiconductor element on a support,
an encapsulating step of embedding and encapsulating the semiconductor element by an encapsulating layer in an encapsulating sheet including a peeling layer and the encapsulating layer laminated below the peeling layer and made from a thermosetting resin before complete curing, and
a heating step of heating and curing the encapsulating layer after the encapsulating step, wherein
the heating step includes
a first heating step in which the encapsulating sheet is heated under a normal pressure at a first temperature,
a peeling step in which the peeling layer is peeled from the encapsulating layer after the first heating step, and
a second heating step in which the encapsulating layer is heated at a second temperature that is higher than the first temperature after the peeling step.
2. The method for producing an encapsulating layer-covered semiconductor element according to claim 1 , wherein
the encapsulating layer after the first heating step has a compressive elastic modulus at 23° C. of 0.15 MPa or more.
3. The method for producing an encapsulating layer-covered semiconductor element according to claim 1 , wherein
the encapsulating layer in the encapsulating step is in a B-stage state of a two-step thermosetting resin composition.
4. The method for producing an encapsulating layer-covered semiconductor element according to claim 1 , wherein
the encapsulating layer contains a filler and/or a phosphor.
5. The method for producing an encapsulating layer-covered semiconductor element according to claim 1 , wherein
the first temperature has a temperature rising range in which the temperature rises up to the second temperature.
6. The method for producing an encapsulating layer-covered semiconductor element according to claim 1 , wherein
the support is a board and
in the disposing step, the semiconductor element is mounted on the board.
7. A method for producing a semiconductor device comprising the steps of:
producing an encapsulating layer-covered semiconductor element and
mounting the encapsulating layer-covered semiconductor element on a board, wherein
the encapsulating layer-covered semiconductor element is produced by a method for producing an encapsulating layer-covered semiconductor element, wherein
the method for producing an encapsulating layer-covered semiconductor element comprises:
a disposing step of disposing a semiconductor element on a support,
an encapsulating step of embedding and encapsulating the semiconductor element by an encapsulating layer in an encapsulating sheet including a peeling layer and the encapsulating layer laminated below the peeling layer and made from a thermosetting resin before complete curing, and
a heating step of heating and curing the encapsulating layer after the encapsulating step, and
the heating step includes
a first heating step in which the encapsulating sheet is heated under a normal pressure at a first temperature,
a peeling step in which the peeling layer is peeled from the encapsulating layer after the first heating step, and
a second heating step in which the encapsulating layer is heated at a second temperature that is higher than the first temperature after the peeling step.