US20150104346A1 - Laser sintering powder, method for producing structure, apparatus for producing structure - Google Patents
Laser sintering powder, method for producing structure, apparatus for producing structure Download PDFInfo
- Publication number
- US20150104346A1 US20150104346A1 US14/511,444 US201414511444A US2015104346A1 US 20150104346 A1 US20150104346 A1 US 20150104346A1 US 201414511444 A US201414511444 A US 201414511444A US 2015104346 A1 US2015104346 A1 US 2015104346A1
- Authority
- US
- United States
- Prior art keywords
- powder
- metal particles
- laser sintering
- layer
- powder layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A laser sintering powder to be sintered by irradiation with a laser light is provided. The sintering powder includes a plurality of metal particles and a binder which binds the metal particles to one another. The binder is sublimated by the irradiation with the laser light. The average particle diameter of the metal particles is 5 μm or more and 10 μm or less, and the average particle diameter of the laser sintering powder is 30 μm or more and 50 μm or less. Further, after a powder layer is formed using the laser sintering powder, this powder layer may be compressed in the thickness direction before or after irradiation with the laser light.
Description
- 1. Technical Field
- The present invention relates to a laser sintering powder, a method for producing a structure, and an apparatus for producing a structure.
- 2. Related Art
- A production method for forming a structure by irradiating a metal powder with a laser light is known. This method is suitable for the production of small amounts of various structures because the structure is formed by controlling a laser light using a computer. One such production method is disclosed in JP-T-2001-504897. According to this method, first, a metal powder is spread on a flat plate. Subsequently, a leveling plate is moved along the surface of the metal powder layer to level the metal powder to a given uniform thickness. Subsequently, a protection gas is flowed over the metal powder layer to create a protection gas atmosphere. Subsequently, a laser light is formed into a beam and scanned across the metal powder layer to draw a given image. In a region irradiated with the laser light, the metal powder is sintered and bound.
- The steps of spreading the metal powder, leveling the metal powder, and drawing by irradiating the metal powder with the laser light are then repeated as desired. By doing this, the layers of the sintered metal powder are bound to one another, whereby a three-dimensional structure is formed.
- Unfortunately, fine metal powder is easily stirred up in the air. Therefore, a metal powder which can be used for laser sintering has an average particle diameter of 30 μm or more. When a plurality of metal powder particles overlap with one another, the metal powder particles on the surface are easily heated by irradiation with the laser light, and the metal powder particles hidden behind the other particles are hardly heated. Due to this, a structure results that includes a completely sintered layer and an incompletely sintered layer stacked on one another in the stacking direction. When the completely sintered layer and the incompletely sintered layer are alternately disposed, the outer appearance of the surface is not glossy. Therefore, it is necessary to polish the surface to achieve the desired glossiness. Thus, although a minute structure can be obtained by laser sintering, the minute structure may have a surface which a polishing tool or a polishing cloth cannot reach, and therefore, it is difficult to make the surface glossy. Therefore, in the production of a structure by irradiating a metal powder with a laser light, a laser sintering powder capable of producing a structure having a glossy surface, a method for producing a structure, and an apparatus for producing a structure have been demanded.
- An advantage of some aspects of the invention is to solve the problem described above, and the invention can be implemented as the following aspects or application examples.
- This application example is directed to a laser sintering powder, which is sintered by irradiation with a laser light, and includes a plurality of metal particles and a binder which binds the metal particles to one another, wherein the binder contains a material which is decomposed and vaporized by the laser light.
- According to this application example, the laser sintering powder is configured such that the metal particles are bound to one another by the binder. The size of the metal particles is smaller than that of the laser sintering powder. The laser sintering powder is placed to a given thickness. Then, when the laser sintering powder is irradiated with the laser light, the binder is decomposed and vaporized, and therefore, in the laser sintering powder, the metal particles are separated from one another. The metal particles irradiated with the laser light are heated. At this time, a large energy is applied to the laser sintering powder in a shallow region, and a small energy is applied to the laser sintering powder in a deep region. The heat capacity of the metal particles can be decreased when the size of the metal particles is small as compared with the case where the size of the metal particles is large. Therefore, the temperature of the metal particles can be easily increased. Accordingly, the temperature of the metal particles located in a deep region can be increased, and thus, the metal particles can be reliably sintered even in a deep region.
- In the laser sintering, a step of placing the laser sintering powder to a given thickness and a step of drawing with the laser light may be alternately repeated. In the case where the diameter of the metal particles is large and there is a difference in heating of the metal particles by the laser light in the depth direction as in the related art, a laminate in which a completely sintered layer and an incompletely sintered layer are stacked is formed. According to the laser sintering powder of this application example, a difference in heating of the metal particles by the laser light in the depth direction is prevented from occurring. Therefore, a structure formed by irradiating the laser sintering powder with the laser light can be configured such that a surface where the metal particles are stacked has few irregularities. As a result, a structure obtained by laser sintering can be configured to have a glossy surface.
- This application example is directed to the laser sintering powder according to the application example described above, wherein the average particle diameter of the metal particles is 5 μm or more and 10 μm or less, and the average particle diameter of the laser sintering powder is 30 μm or more and 50 μm or less.
- According to this application example, the average particle diameter of the laser sintering powder is 30 μm or more and 50 μm or less. When the laser sintering powder is placed to a given thickness and a given pattern is drawn thereon with the laser light, the laser sintering powder having an average particle diameter of 30 μm or more and 50 μm or less is hardly stirred up. Therefore, the laser sintering powder can be irradiated with the laser light in a state where the laser sintering powder is statically stable. Further, since the average particle diameter of the metal particles is 5 μm or more and 10 μm or less, the heat capacity of the metal particles is decreased so that the temperature when heating can be easily increased. As a result, the metal can be sintered to an accurate thickness with good quality, and thus, a structure can be formed with good quality.
- This application example is directed to the laser sintering powder according to the application example described above, wherein the average particle diameter of the laser sintering powder is 3 times or more and 10 times or less larger than the average particle diameter of the metal particles.
- According to this application example, the balance of particle diameter between the laser sintering powder and the metal particles is optimized, and thus, both the fluidity of the laser sintering powder and the sinterability of the metal particles can be achieved. Further, when a powder layer formed using the laser sintering powder is compressed in the thickness direction, it becomes easy to moderately crush the laser sintering powder, and also it becomes easy to rearrange the metal particles more densely, and thus, the volume reduction when sintering the metal particles can be further reduced.
- This application example is directed to the laser sintering powder according to the application example described above, wherein the metal particles contain any one of iron, nickel, and cobalt as a principal component and are produced by an atomization method.
- According to this application example, the principal component of the metal particles is mainly any of iron, nickel, and cobalt, and therefore, a metal obtained by sintering the laser sintering powder can be any of iron, an iron alloy, nickel, a nickel alloy, cobalt, and a cobalt alloy.
- This application example is directed to the laser sintering powder according to the application example described above, wherein the metal particles contain iron as a principal component, and at least one of nickel, chromium, molybdenum, and carbon.
- According to this application example, the principal component of the metal particles is iron, and further at least one of nickel, chromium, molybdenum, and carbon is contained in the metal particles, and therefore, a metal obtained by sintering the laser sintering powder can have corrosion resistance and mechanical rigidity.
- This application example is directed to the laser sintering powder according to the application example described above, wherein the binder is PVA.
- According to this application example, the binder is PVA. PVA can bind the metal particles to one another, and therefore, the laser sintering powder can be produced by binding the metal particles to one another by PVA. PVA can be sublimated by the irradiation with the laser, and therefore, the metal obtained by sintering the laser sintering powder can be made not to contain the binder.
- This application example is directed to a laser sintering powder, which is sintered by irradiation with a laser light, and including granulated particles obtained by granulating a plurality of metal particles produced by an atomization method by a spray drying method, wherein the granulated particles have pores therein.
- According to this application example, the laser sintering powder includes granulated particles having pores therein. In such granulated particles, the densification of an outer shell portion relatively proceeds, and thus, the granulated particles have a relatively large mechanical strength as compared with particles having no pores therein. Therefore, such granulated particles have excellent fluidity. Further, when a powder layer formed using the laser sintering powder is compressed in the thickness direction, the powder layer is easily crushed, and thus, the powder layer is easily compressed. Accordingly, the laser sintering powder achieves both fluidity and easy compressibility.
- This application example is directed to a method for producing a structure including forming a powder layer composed of a laser sintering powder in which a plurality of metal particles are bound to one another by a binder, and sintering the metal particles by emitting a laser light to the powder layer to draw a given pattern and vaporizing the binder, wherein a structure in which the metal particles are sintered is formed by alternately repeating the forming of a powder layer so as to overlap with the powder layer having the pattern drawn thereon and the sintering.
- According to this application example, a powder layer composed of the laser sintering powder is formed. Then, the laser light is emitted to the powder layer, whereby a given pattern is drawn. In a region irradiated with the laser light, the binder is vaporized, and the metal particles are sintered. In the laser sintering powder of this application example, the average particle diameter of the metal particles is smaller than the average particle diameter of the laser sintering powder. The heat capacity of the metal particles is decreased as the size of the metal particles is decreased, and therefore, the metal particles are easily sintered. Accordingly, the temperature of the metal particles located in a deep region of the powder layer can be increased, and thus, the metal particles can be more reliably sintered even in a deep region. Therefore, a structure formed by the method of this application example can be configured such that a surface where the metal particles are stacked has few irregularities. As a result, a structure obtained by laser sintering can be configured to have a glossy surface.
- This application example is directed to the method for producing a structure according to the application example described above, wherein the metal particles irradiated with the laser light are sintered by heating to a temperature at which the metal particles do not melt.
- According to this application example, the metal particles are heated to a sintering temperature. If a metal is heated until it melts, the melting metal flows in the direction where the gravitational force or surface tension acts. Therefore, in the case where the metal is heated to a sintering temperature, the metal can be more accurately formed into a shape as it is drawn as compared with the case where the metal is heated until it melts.
- This application example is directed to the method for producing a structure according to the application example described above, wherein the method further includes compressing the powder layer in the thickness direction.
- According to this application example, the powder layer is crushed in the thickness direction and consolidated, and therefore, even when the metal particles are sintered, a difference in thickness between the sintered layer and the powder layer can be made sufficiently small. Moreover, when a new powder layer is formed thereon, a powder layer having a uniform thickness can be formed regardless of the condition of the underlayer. Accordingly, even in the case where the volume of the powder layer is greatly reduced accompanying the sintering of the metal particles, the shape of the structure to be produced can be prevented from being largely deviated from the design value, and thus, the dimensional accuracy of the structure can be further enhanced.
- This application example is directed to an apparatus for producing a structure including a powder layer forming unit which forms a powder layer using a laser sintering powder in which a plurality of metal particles are bound to one another by a binder, and a laser light source which emits a laser light to the powder layer.
- According to this application example, a powder layer composed of the laser sintering powder is formed. Then, the laser light is emitted to the powder layer, whereby a given pattern is drawn. In a region irradiated with the laser light, the binder is vaporized, and the metal particles are sintered. In the laser sintering powder of this application example, the average particle diameter of the metal particles is smaller than the average particle diameter of the laser sintering powder. The heat capacity of the metal particles is decreased as the size of the metal particles is decreased, and therefore, the metal particles are easily sintered. Accordingly, the temperature of the metal particles located in a deep region of the powder layer can be increased, and thus, the metal particles can be more reliably sintered even in a deep region. Therefore, a structure formed by the apparatus of this application example can be configured such that a surface where the metal particles are stacked has few irregularities. As a result, a structure obtained by laser sintering can be configured to have a glossy surface.
- This application example is directed to the apparatus for producing a structure according to the application example described above, wherein the apparatus further includes a compressing unit which compresses the powder layer in the thickness direction.
- According to this application example, the powder layer is crushed in the thickness direction and consolidated, and therefore, even when the metal particles are sintered, a difference in thickness between the sintered layer and the powder layer can be made sufficiently small. Moreover, when a new powder layer is formed thereon, a powder layer having a uniform thickness can be formed regardless of the condition of the underlayer. Accordingly, even in the case where the volume of the powder layer is greatly reduced accompanying the sintering of the metal particles, the shape of the structure to be produced can be prevented from being largely deviated from the design value, and thus, the dimensional accuracy of the structure can be further enhanced.
- This application example is directed to the apparatus for producing a structure according to the application example described above, wherein the compressing unit includes a roller capable of coming in contact with the powder layer.
- According to this application example, a possibility that the roller carelessly scrapes off the powder layer is low, and therefore, the powder layer is easily crushed to a desired thickness. Further, the structure of the roller is simple and also small, and therefore, the operation of the apparatus for producing a structure is hardly inhibited.
- Embodiments of the invention will be described with reference to the accompanying drawings, wherein like numbers reference like elements.
-
FIG. 1 is a schematic perspective view showing the structure of a laser sintering powder. -
FIGS. 2A to 2E are schematic views for explaining the sintering of the laser sintering powder. -
FIG. 3 is a schematic view showing the structure of a spray drying apparatus for producing the laser sintering powder. -
FIG. 4 is a schematic view showing the structure of a laser sintering apparatus to which a first embodiment of an apparatus for producing a structure according to the invention is applied. -
FIGS. 5A to 5F are schematic views for explaining a method for forming a structure using a laser sintering powder (a first embodiment of the method for producing a structure according to the invention). -
FIGS. 6A to 6D are schematic views for explaining the method for forming a structure using a laser sintering powder (the first embodiment of the method for producing a structure according to the invention). -
FIG. 7 is a schematic view showing the structure of a laser sintering apparatus to which a second embodiment and a third embodiment of the apparatus for producing a structure according to the invention are applied. -
FIGS. 8A to 8F are schematic views for explaining a method for forming a structure using a laser sintering powder (a second embodiment of the method for producing a structure according to the invention). -
FIGS. 9A to 9E are schematic views for explaining the method for forming a structure using a laser sintering powder (the second embodiment of the method for producing a structure according to the invention). -
FIGS. 10A to 10F are schematic views for explaining a method for forming a structure using a laser sintering powder (a third embodiment of the method for producing a structure according to the invention). -
FIGS. 11A to 11E are schematic views for explaining a method for forming a structure using a laser sintering powder (the third embodiment of the method for producing a structure according to the invention). -
FIG. 12 is a table showing an example in which metal particles containing iron, nickel, and chromium were sintered. -
FIG. 13 is a table showing examples in which metal particles containing iron, nickel, and chromium were sintered. -
FIGS. 14A-E are tables showing examples in which various types of metal particles containing iron as a principal component were sintered. -
FIGS. 15A-E are tables showing examples in which various types of metal particles containing iron as a principal component were sintered. -
FIGS. 16A-D are tables showing examples in which various types of metal particles containing iron as a principal component were sintered. -
FIGS. 17A-D are tables showing examples in which various types of metal particles containing cobalt as a principal component were sintered. -
FIGS. 18A-D are tables showing examples in which various types of metal particles containing cobalt as a principal component were sintered. -
FIGS. 19A-E are tables showing examples in which various types of metal particles containing nickel as a principal component were sintered. -
FIG. 20 is a table showing an example in which metal particles containing nickel as a principal component were sintered. -
FIGS. 21A-F are tables showing examples in which metal particles of SUS316L were sintered. -
FIGS. 22A-F are tables showing examples in which metal particles of SUS316L were used and sintering was performed by adding a powder layer compressing step which was performed before a laser sintering step (light exposure). -
FIG. 23A-F are tables showing examples in which metal particles of SUS316L were used and sintering was performed by adding a powder layer compressing step which was performed after a laser sintering step (light exposure). -
FIG. 24A-F are tables showing examples in which metal particles of SUS316L were used, and also a spray drying method or a tumbling granulation method was used as the granulation method, and sintering was performed by adding a powder layer compressing step. - Hereinafter, the laser sintering powder, the method for producing a structure, and the apparatus for producing a structure according to the invention will be described in detail based on preferred embodiments shown in the accompanying drawings. That is, in the embodiments, a characteristic laser sintering powder, the production of the laser sintering powder, an example of producing a structure using the laser sintering powder, and an example of an apparatus for producing a structure using the laser sintering powder will be described with reference to
FIGS. 1 to 6D . Incidentally, the scales of the respective members in the respective drawings have been appropriately changed so that the respective members have a recognizable size in the respective drawings. - First, an embodiment of the laser sintering powder according to the invention will be described with reference to
FIG. 1 .FIG. 1 is a schematic perspective view showing the structure of the laser sintering powder. As shown inFIG. 1 , alaser sintering powder 1 is formed by binding a plurality ofmetal particles 2. - The average particle diameter (a particle diameter at 50% accumulation in a cumulative particle size distribution on a mass basis) of the
metal particles 2 is not particularly limited, but is preferably 5 μm or more and 10 μm or less. As the particle diameter is smaller, the surface roughness of a structure to be produce can be made smaller. However, if the average particle diameter thereof is less than the above lower limit, depending on the constituent material of themetal particles 2, themetal particles 2 are liable to be stirred up in the air, and therefore, it may become difficult to handle themetal particles 2. Further, if the average particle diameter thereof exceeds the above upper limit, depending on the constituent material of themetal particles 2, the sinterability of themetal particles 2 is sometimes deteriorated, and therefore, it may take a longtime to produce a structure. The average particle diameter of a metal powder and the average particle of a granulated powder can be measured by any of a variety of particle diameter measurement methods such as a dynamic light scattering method, a laser diffraction method, a centrifugal sedimentation method, an FFF (Field Flow Fractionation) method, and an electrical sensing zone method. - The constituent material of the
metal particles 2 is not particularly limited as long as it is a metal material, but preferably contains a powder produced by an atomization method using any of iron, nickel, and cobalt as a principal component. According to this, the metal obtained by sintering thelaser sintering powder 1 can be any of iron, an iron alloy, nickel, a nickel alloy, cobalt, and a cobalt alloy. When themetal particles 2 contain iron as a principal component, themetal particles 2 preferably contain one element or two or more elements in combination selected from nickel, chromium, molybdenum, and carbon. Further, when themetal particles 2 contain nickel as a principal component, themetal particles 2 preferably contain one element or two or more elements in combination selected from chromium, molybdenum, and carbon. According to this, the metal obtained by sintering thelaser sintering powder 1 can have corrosion resistance and mechanical rigidity. - Examples of the atomization method include a water atomization method, a gas atomization method, and a spinning water atomization method, and the
metal particles 2 may be produced by any method among them. - The shape of the
metal particles 2 is not particularly limited, and may be a sphere such as a true sphere or an ellipse, a polyhedron such as a cube or a rectangular parallelepiped, a column such as a circular column or a prismatic column, a conic solid such as a cone or a pyramid, or another irregular shape. - However, as described in detail later, in the case where a step of compressing a powder layer formed using the
laser sintering powder 1 in the thickness direction is performed, the aspect ratio of themetal particles 2 is preferably within a predetermined range. Specifically, the average of the aspect ratio of themetal particles 2 defined by S/L wherein S (μm) represents the minor axis of each particle, and L (μm) represents the major axis thereof is preferably 0.3 or more and 0.9 or less, and more preferably 0.4 or more and 0.8 or less. Themetal particles 2 having such an aspect ratio have a shape with a certain anisotropy. Therefore, when themetal particles 2 are adhered to one another through abinder 3, themetal particles 2 are easily caught on one another so as to easily exhibit the property of maintaining the adhered state. Then, when a step of compressing a powder layer produced using thelaser sintering powder 1 in the thickness direction is performed, a given frictional resistance can be ensured between themetal particles 2, and thus, the compressed powder layer can be prevented from being crushed at once. Accordingly, such a configuration contributes to the shape retainability of the powder layer after compressing. - Here, the “major axis” is the maximum length in the projected image of the
metal particle 2, and the “minor axis” is the maximum length in the direction perpendicular to the major axis. Further, the average of the aspect ratio is obtained as an average of the aspect ratio measured for 100 ormore metal particles 2. - Further, from the viewpoint of frictional resistance between the
metal particles 2, as the atomization method when producing themetal particles 2, a water atomization method or a spinning water atomization method, in which a liquid is used as a medium for atomizing a molten metal, is preferably used. In either of these atomization methods, water is used as the medium for atomizing a molten metal, and therefore, the collision energy when atomizing a molten metal is high, and also the cooling rate when cooling the atomized molten metal is high. Due to this, as compared with a method using a gas as a medium for atomizing a molten metal like a gas atomization method, fine irregularities are more easily formed on the surface of eachmetal particle 2 to be produced, and thus, the frictional resistance between themetal particles 2 can be relatively increased in this respect. - The surface of each
metal particle 2 is covered with thebinder 3. Themetal particles 2 are adhered to one another by thebinder 3. The material of thebinder 3 may be any material as long as it is easily vaporized by sublimation or decomposition through heating, and a variety of resin materials can be used. For example, as the material of thebinder 3, PVA (polyvinyl alcohol), PVP (polyvinylpyrrolidone) or the like can be used. In this embodiment, for example, PVA is used as the material of thebinder 3. The amount of the binder is appropriately adjusted according to the type of the metal particles or the like, but is set to, for example, 0.1 parts by mass or more and 5.0 parts by mass or less with respect to 100 parts by mass of the metal particles. - In the
binder 3, other than the material which is easily vaporized by sublimation or decomposition through heating, a material which is not vaporized may be contained as long as the amount thereof is small so that it does not inhibit the sintering of themetal particles 2. In this case, the amount of the material which is not vaporized is preferably 10% by mass or less, and more preferably 5% by mass or less of the amount of thebinder 3. - Further, in the
binder 3, multiple types of materials which are easily vaporized by sublimation or decomposition through heating and have sublimation temperatures or decomposition temperatures different from one another may be contained. By incorporating such multiple types of materials, when thebinder 3 is heated, the multiple types of materials are sequentially sublimated or decomposed with a given time lag. Due to this, during the process of heating thebinder 3, a time for which thebinder 3 exists without vaporizing can be secured longer, and thus, a time for which themetal particles 2 are adhered to one another can be ensured longer. As a result, when the powder layer is formed using thelaser sintering powder 1 as described below, the shape retainability can be further enhanced, and thus, the dimensional accuracy of a structure to be produced in the end can be further enhanced. - For example, in the case where two types of materials whose sublimation temperatures or decomposition temperatures are different from one another are contained in the
binder 3, a difference in sublimation temperature or decomposition temperature is preferably 3° C. or more and 100° C. or less, and more preferably 5° C. or more and 70° C. or less. By setting the difference in sublimation temperature or decomposition temperature within the above range, the shape retainability of the powder layer can be sufficiently enhanced. - The average particle diameter (a particle diameter at 50% accumulation in a cumulative particle size distribution on a mass basis) of the
laser sintering powder 1 is not particularly limited, but is preferably 30 μm or more and 50 μm or less, and more preferably 30 μm or more and 40 μm or less. If the average particle diameter of thelaser sintering powder 1 is less than the above lower limit, thelaser sintering powder 1 is stirred up when it is irradiated with the laser light, and therefore, it becomes difficult to form a structure. If the average particle diameter of thelaser sintering powder 1 is larger than the above upper limit, the size of spaces in thelaser sintering powder 1 is increased, and therefore, a possibility that air bubbles are formed in the structure is increased. - On the other hand, the average particle diameter of the
laser sintering powder 1 is preferably 3 times or more and 10 times or less larger than the average particle diameter of themetal particles 2. By setting the average particle diameter of thelaser sintering powder 1 within the above range, the balance of the particle diameter between thelaser sintering powder 1 and themetal particles 2 is optimized, and thus, both the fluidity of thelaser sintering powder 1 and the sinterability of themetal particles 2 can be achieved. Further, as described in detail below, when a powder layer formed using thelaser sintering powder 1 is compressed in the thickness direction, it becomes easy to moderately crush thelaser sintering powder 1, and also it becomes easy to rearrange the metal particles more densely, and thus, the volume reduction when sintering themetal particles 2 can be further reduced. - In
FIG. 1 , in order to make thelaser sintering powder 1 easy to understand, three aggregates of thelaser sintering powder 1 are illustrated apart from one another. When thelaser sintering powder 1 is used, a large number of aggregates of thelaser sintering powder 1 are spread out in layers. -
FIGS. 2A to 2E are schematic views for explaining the sintering of the laser sintering powder. As shown inFIG. 2A , a large number of aggregates of thelaser sintering powder 1 are spread out in layers. In the drawing, the aggregates of thelaser sintering powder 1 are arranged in three layers, however, the number of layers of the aggregates of thelaser sintering powder 1 to be stacked is not particularly limited. In order to control the arrangement of themetal particles 2 after sintering with good quality, it is preferred to arrange the aggregates of thelaser sintering powder 1 in one layer. - As shown in
FIG. 2B , subsequently, thelaser sintering powder 1 is irradiated with alaser light 4. By thelaser light 4, thebinder 3 is heated and sublimated. As a result, the binding force between themetal particles 2 by thebinder 3 is decreased so that themetal particles 2 easily move. As shown inFIG. 2C , the fluidity of themetal particles 2 is further increased by heating. Then, themetal particles 2 move to occupy the spaces in thelaser sintering powder 1. As a result, as shown inFIG. 2D , themetal particles 2 are arranged in lines (layers). Themetal particles 2 are heated in a state where theadjacent metal particles 2 come closer to one another, whereby a metal bond is formed. When the irradiation with thelaser light 4 is stopped, themetal particles 2 in lines (layers) are cooled. At this time, a metal bond is formed between themetal particles 2, and therefore, a metal block is formed. Then, in the formed structure, themetal particles 2 are densely arranged as shown inFIG. 2E , and therefore, also the side surfaces on the left and right sides in the drawing can be made glossy. -
FIG. 3 is a schematic view showing the structure of a spray drying apparatus for producing a laser sintering powder. As shown inFIG. 3 , aspray drying apparatus 5 includes afirst vessel 6. In thefirst vessel 6, adisk rotating unit 7, a startingmaterial dropping unit 8, and a hotair blowing unit 9 are provided on aceiling 6 a. Thedisk rotating unit 7 includes amotor 10, and a conicalrotary plate 11 is attached to arotating shaft 10 a of themotor 10. Therotary plate 11 is rotated by themotor 10. - The starting
material dropping unit 8 includes asecond vessel 12. In thesecond vessel 12,metal particles 2, abinder 3, and a solvent 13 for dissolving thebinder 3 are placed. The solvent 13 is not particularly limited and may be any as long as it is a medium which dissolves thebinder 3, has a low viscosity, and is readily dried. As the solvent 13, for example, water, methyl alcohol, ethyl alcohol, MEK (methyl ethyl ketone), or the like can be used. In this embodiment, for example, water is used as the solvent 13. The material of themetal particles 2 is prepared in accordance with the composition of a structure to be produced. For example, when the material of the structure is stainless steel SUS301, the material of themetal particles 2 is an alloy containing iron, chromium, and nickel. - The starting
material dropping unit 8 includes amotor 14 on the side of theceiling 6 a, and animpeller 15 is attached to arotating shaft 14 a of themotor 14. Theimpeller 15 is rotated by themotor 14. Theimpeller 15 has a function of stirring themetal particles 2, thebinder 3, and the solvent 13. By theimpeller 15, themetal particles 2 are uniformly dispersed and thebinder 3 is uniformly dissolved in the solvent 13. - An
ejection port 16 is disposed on the lower side of thesecond vessel 12 in the drawing. From theejection port 16,liquid droplets 17 composed of themetal particles 2, thebinder 3, and the solvent 13 are dropped. The ejection port is provided with anelectromagnetic valve 16 a. Theelectromagnetic valve 16 a can adjust the size of theliquid droplets 17 and the ejection frequency. - The hot
air blowing unit 9 includes amotor 18 on the side of theceiling 6 a, and animpeller 21 is attached to arotating shaft 18 a of themotor 18. Theimpeller 21 is rotated by themotor 18. Aheater 22 is disposed between themotor 18 and theimpeller 21. Theheater 22 heats the air flowing aroundheater 22. According to this, the hotair blowing unit 9 causes ahot air 23 to flow downward in the drawing. - The gravitational force acts on the
liquid droplets 17 ejected from theejection port 16. The rotatingrotary plate 11 is disposed on the gravitational acceleration direction of theejection port 16. Theliquid droplets 17 hit therotary plate 11 and break up into smallliquid droplets 24. The smallliquid droplets 24 move through the air. Around therotary plate 11, thehot air 23 flows. The solvent 13 in the smallliquid droplets 24 is heated by thehot air 23 and released in the air. By doing this, the smallliquid droplets 24 are dried and formed into alaser sintering powder 1. The driedlaser sintering powder 1 moves downward in the drawing by the gravitational force and is accumulated. According to the procedure described above, thelaser sintering powder 1 is produced. - The thus produced
laser sintering powder 1 includes many particles (granulated particles) having pores therein. In such particles having pores therein, the densification of an outer shell portion relatively proceeds, and thus, the particles have a relatively large mechanical strength as compared with particles having no pores therein. Therefore, thelaser sintering powder 1 including such particles having pores therein has excellent fluidity. Further, since the particles have pores therein, as described in detail below, when a powder layer formed using thelaser sintering powder 1 is compressed in the thickness direction, the particles are easily crushed, and thus, the powder layer is easily compressed. Due to this, the powder layer can be more uniformly compressed in the compressing step. Therefore, by incorporating such particles having pores therein, thelaser sintering powder 1 can achieve both fluidity and easy compressibility. - In the
metal particles 2 having an aspect ratio within the range as described above, a given frictional resistance is ensured between themetal particles 2 as described above, and therefore, an outer shell portion can be rapidly formed during the granulation, and also the densification of the formed outer shell portion easily proceeds. Accordingly, themetal particles 2 having an aspect ratio within the range as described above are useful when forming the particles having pores therein. - The size or the like of the pores contained in the particles is not particularly limited, however, the size thereof is preferably about 1% by volume or more and 50% by volume or less, and more preferably about 5% by volume or more and 30% by volume or less of the
laser sintering powder 1. By setting the size of the pores within such a range, thelaser sintering powder 1 can particularly achieve both fluidity and easy compressibility. That is, if the size of the pores is less than the above lower limit, the easy compressibility may be deteriorated, and if the size of the pores exceeds the above upper limit, the mechanical strength of the outer shell portion is decreased, and thus, the fluidity may be deteriorated. - The method for producing the
laser sintering powder 1 is not limited to the above-described spray drying method, and for example, any of a variety of granulation methods such as a tumbling granulation method, a fluidized bed granulation method, and a tumbling fluidized bed granulation method may be used. However, according to the spray drying method, alaser sintering powder 1 including many (preferably 30% by number or more) particles having pores therein as described above is obtained. - The
laser sintering powder 1 may be a mixed powder obtained by mixing an arbitrary powder in the granulated powder produced as described above. The arbitrary powder is not particularly limited in terms of constituent material or mixing amount thereof as long as it does not inhibit the sintering of themetal particles 2. - Next, a laser sintering apparatus to which a first embodiment of the apparatus for producing a structure according to the invention is applied will be described.
-
FIG. 4 is a schematic view showing the structure of a laser sintering apparatus to which a first embodiment of the apparatus for producing a structure according to the invention is applied. Alaser sintering apparatus 25 includes anXYZ stage 26. TheXYZ stage 26 is a device which moves a table 27 in three axial directions perpendicular to one another. Specifically, theXYZ stage 26 includes anXY stage 28 and alifting device 29. TheXY stage 28 moves the table 27 in the horizontal direction. Further, the liftingdevice 29 is provided on theXY stage 28 and lifts and lowers the table 27. TheXY stage 28 includes a biaxial linear motion mechanism, and thelifting device 29 includes a uniaxial linear motion mechanism. According to this, theXYZ stage 26 can move the table 27 in the three axial directions perpendicular to one another. - A bottomed rectangular
cylindrical vessel 30 is disposed on the table 27, and thelaser sintering powder 1 is spread in thevessel 30. Apowder supply device 31 which supplies thelaser sintering powder 1 into thevessel 30 is disposed on the upper side of thevessel 30 in the drawing. Thepowder supply device 31 includes arail 32 which extends transversely in the drawing. Further, a movingstage 33 which moves along therail 32 is provided. Ahopper 34 which stores thelaser sintering powder 1 is mounted on the movingstage 33. The outer appearance of thehopper 34 has a triangular prism shape, and adischarge port 34 a is provided on the side facing a bottom 30 a of thevessel 30. - The
discharge port 34 a is provided with anelectromagnetic valve 35. Theelectromagnetic valve 35 opens and closes thedischarge port 34 a. When theelectromagnetic valve 35 opens thedischarge port 34 a, thelaser sintering powder 1 flows from thedischarge port 34 a to the bottom 30 a of thevessel 30. A levelingplate 36 is attached to thedischarge port 34 a. The levelingplate 36 is also called “squeegee”. Theelectromagnetic valve 35 opens thedischarge port 34 a, and the movingstage 33 moves thehopper 34 and the levelingplate 36. By doing this, thelaser sintering powder 1 is supplied to the bottom 30 a, and the levelingplate 36 can level the surface of thelaser sintering powder 1 flat. A mechanism for moving a cylindrical roller while rotating the roller may be provided in place of the levelingplate 36. Then, by rotating the roller, the surface of thelaser sintering powder 1 may be leveled flat. By the movingstage 33, thehopper 34, the levelingplate 36, and the like as described above constitute a powder layer forming unit of thelaser sintering apparatus 25. - A
laser irradiation unit 37 is disposed on the upper side of thepowder supply device 31 in the drawing. Thelaser irradiation unit 37 includes alaser light source 38. Thelaser light source 38 may be any as long as it can emit alaser light 4 having a light intensity capable of sintering themetal particles 2, and a laser light source such as a carbon dioxide laser, an argon laser, or a YAG (yttrium aluminum garnet) laser can be used. In this embodiment, for example, as thelaser light source 38, a carbon dioxide laser is used. - The
laser light 4 emitted from thelaser light source 38 is incident on ascanner 41. Thescanner 41 includes amirror 41 a, and thescanner 41 oscillates themirror 41 a. Thelaser light 4 incident on thescanner 41 is reflected by themirror 41 a. Then, themirror 41 a is oscillated, and thus, thelaser light 4 is scanned by thescanner 41. - The
laser light 4 reflected by themirror 41 a is incident on a condensinglens 42. The condensinglens 42 is a cylindrical lens, and condenses thelaser light 4 to be scanned on the surface of thelaser sintering powder 1. The condensinglens 42 may be a single lens or a combination lens. - A hot
air blowing unit 43 is provided on the right side of thelaser irradiation unit 37 in the drawing. The hotair blowing unit 43 includes a heater and heats a gas. The hotair blowing unit 43 also includes a motor and an impeller, and the motor rotates the impeller to blow the air. The hotair blowing unit 43 includes anair blowing tube 44 on the side of thevessel 30. Theair blowing tube 44 are provided withejection ports 44 a at equal intervals. The hotair blowing unit 43 sends ahot air 23 to theair blowing tube 44. Then, thehot air 23 is blown on thelaser sintering powder 1 from theejection ports 44 a of theair blowing tube 44. - The
laser sintering apparatus 25 includes a control section 45 (e.g., CPU or processor). Thecontrol section 45 is electrically or optically connected to theXYZ stage 26, the movingstage 33, theelectromagnetic valve 35, thelaser light source 38, and the hotair blowing unit 43. Thecontrol section 45 controls each member and forms a structure from thelaser sintering powder 1. - The
laser sintering apparatus 25 includes achamber 46, and in thechamber 46, theXYZ stage 26, thevessel 30, thepowder supply device 31, thelaser irradiation unit 37, and the hotair blowing unit 43 are disposed. An inertgas supply section 48 which supplies aninert gas 47 is disposed on thechamber 46. Thechamber 46 is filled with theinert gas 47. The type of theinert gas 47 is not particularly limited, however, in this embodiment, for example, argon gas is used as theinert gas 47. That is, thehot air 23 to be blown from the hotair blowing unit 43 is composed of heated argon gas. Further, nitrogen gas may be used as theinert gas 47. According to this, themetal particles 2 can be prevented from oxidizing. - Next, a first embodiment of the method for producing a structure according to the invention will be described.
-
FIGS. 5A to 5F andFIGS. 6A to 6D are schematic views for explaining a method for forming a structure using a laser sintering powder (a first embodiment of the method for producing a structure according to the invention), respectively. Hereinafter, with reference toFIGS. 5A to 5F andFIGS. 6A to 6D , the method for forming a structure will be described. In this method, thelaser sintering apparatus 25 described above is used. - As shown in
FIG. 5A , thelaser sintering powder 1 is placed in thehopper 34 of thelaser sintering apparatus 25. At this time, theelectromagnetic valve 35 is closed to close thedischarge port 34 a. By doing this, thelaser sintering powder 1 is held in thehopper 34. Then, the distance between the bottom 30 a of thevessel 30 and the leveling plate is set to the average particle diameter of thelaser sintering powder 1. Subsequently, as shown inFIG. 5B , theelectromagnetic valve 35 is opened to open thedischarge port 34 a. By doing this, thelaser sintering powder 1 is supplied to the bottom 30 a of thevessel 30 from thedischarge port 34 a. The movingstage 33 moves thehopper 34 and the levelingplate 36 while opening thedischarge port 34 a. By doing this, thelaser sintering powder 1 is supplied to the bottom 30 a. Further, thelaser sintering powder 1 is spread on the bottom 30 a of thevessel 30 sequentially, and also the surface of thelaser sintering powder 1 is leveled. By doing this, apowder layer 1 a which is the first layer of thelaser sintering powder 1 is formed. That is, by the powder layer forming unit constituted by the movingstage 33, thehopper 34, the levelingplate 36, and the like, the first layer of thepowder layer 1 a is formed. The thickness of the first layer of thepowder layer 1 a may be different from the average particle diameter of thelaser sintering powder 1, but is preferably set to the same length as the average particle diameter. By doing this, in the first layer of thepowder layer 1 a, thelaser sintering powder 1 is spread such that the powder particles do not overlap with one another in the thickness direction. Subsequently, by closing theelectromagnetic valve 35 to close thedischarge port 34 a, thelaser sintering powder 1 is made not to flow out from thedischarge port 34 a. - Subsequently, as shown in
FIG. 5C , thehot air 23 is blown on the first layer of thepowder layer 1 a. By doing this, the first layer of thepowder layer 1 a is heated. The temperature of the heated first layer of thepowder layer 1 a is lower than the temperature at which themetal particles 2 are sintered. Subsequently, thelaser light 4 is irradiated such that the light is condensed on the first layer of thepowder layer 1 a. The laser light is scanned by thescanner 41, and also the first layer of thepowder layer 1 a is moved in the horizontal direction by theXY stage 28. By doing this, a given pattern is drawn on the first layer of thepowder layer 1 a. - The
laser sintering powder 1 irradiated with the laser light is sintered at a temperature at which thelaser sintering powder 1 does not melt. If the metal is heated until it melts, the melting metal flows in the direction where the gravitational force or surface tension acts. Therefore, the metal is not heated until it melts, but heated to a sintering temperature, whereby a structure of the metal can be accurately formed into a shape as it is drawn. - As a result, as shown in
FIG. 5D , asintered layer 1 b in which themetal particles 2 are sintered is formed in a region of the first layer of thepowder layer 1 a irradiated with thelaser light 4. Thereafter, by the liftingdevice 29, thevessel 30 is lowered. Then, the distance between thesintered layer 1 b and the levelingplate 36 is set to the average particle diameter of thelaser sintering powder 1. - Subsequently, as shown in
FIG. 5E , by the movingstage 33, thehopper 34 and the levelingplate 36 are moved to the left side in the drawing. When the amount of thelaser sintering powder 1 in thehopper 34 becomes small, thelaser sintering powder 1 is replenished at this time. Then, as shown inFIG. 5F , theelectromagnetic valve 35 is opened to open thedischarge port 34 a. By doing this, thelaser sintering powder 1 is supplied so as to overlap with the first layer of thepowder layer 1 a and thesintered layer 1 b from thedischarge port 34 a. By the movingstage 33, thehopper 34 and the levelingplate 36 are moved while opening thedischarge port 34 a. By doing this, thelaser sintering powder 1 is supplied to the bottom 30 a and is spread on the bottom 30 a of thevessel 30 sequentially, and also the surface of thelaser sintering powder 1 is leveled. By doing this, apowder layer 1 a which is the second layer of thelaser sintering powder 1 is formed so as to overlap with the first layer of thepowder layer 1 a and thesintered layer 1 b. Also at this time, the thickness of the second layer of thepowder layer 1 a may be different from the average particle diameter of thelaser sintering powder 1, but is preferably set to the same length as the average particle diameter. By doing this, in the second layer of thepowder layer 1 a, thelaser sintering powder 1 is spread such that the powder particles do not overlap with one another in the thickness direction. Subsequently, by closing theelectromagnetic valve 35 to close thedischarge port 34 a, thelaser sintering powder 1 is made not to flow out from thedischarge port 34 a. - Subsequently, as shown in
FIG. 6A , thehot air 23 is blown on the second layer of thepowder layer 1 a. By doing this, the second layer of thepowder layer 1 a is heated. Subsequently, thelaser light 4 is irradiated such that the light is condensed on the uppermost (second)powder layer 1 a. Thelaser light 4 is scanned by thescanner 41, and also the second layer of thepowder layer 1 a is moved in the horizontal direction by theXY stage 28. By doing this, a given pattern is drawn on the second layer of thepowder layer 1 a. As a result, as shown inFIG. 6B , asintered layer 1 b in which themetal particles 2 are sintered is formed in a region of the second layer of thepowder layer 1 a irradiated with thelaser light 4. Thesintered layer 1 b is formed so as to be connected to thesintered layer 1 b located below. Thereafter, by the liftingdevice 29, thevessel 30 is lowered. Then, the distance between thesintered layer 1 b and the levelingplate 36 is set to the average particle diameter of thelaser sintering powder 1. Also at this time, the distance between thesintered layer 1 b and the levelingplate 36 may be different from the average particle diameter of thelaser sintering powder 1. - Thereafter, the step of forming the
powder layer 1 a so as to overlap with thesintered layer 1 b formed by drawing and the step of emitting thelaser light 4 to thepowder layer 1 a are alternately repeated. As a result, as shown inFIG. 6C , in thevessel 30, astructure 49 in which a number ofsintered layers 1 b sintered in a given pattern are stacked is formed. Then, as shown inFIG. 6D , thestructure 49 is taken out from thevessel 30, and thelaser sintering powder 1 adhered to thestructure 49 is removed, whereby the production of thestructure 49 is completed. - The
structure 49 produced using the above production method can be used for various purposes. For example, it can be used as a metal piece to be attached to the teeth for an orthodontic treatment in humans. This metal piece is a component whose variety is wide because it is designed to fit the shape of the teeth to which the metal piece is to be attached. Also in this case, thestructure 49 can be produced to fit a required shape. - Further, in addition to this, the
structure 49 can be applied to all sorts of constituent parts including: parts for transportation machinery such as parts for automobiles, parts for railcars, parts for ships, and parts for airplanes; parts for electronic devices such as parts for personal computers and parts for mobile phone terminals; and parts for machines such as machine tools and semiconductor production apparatuses. - Next, a second embodiment of the method for producing a structure according to the invention will be described.
- Hereinafter, a second embodiment will be described, however, in the following description, different points from the first embodiment will be mainly described, and the description of the same matter will be omitted. Further, in the drawings, the same components as in the above-described embodiment will be given the same reference numerals.
-
FIGS. 8A to 8F andFIGS. 9A to 9E are schematic views for explaining a method for forming a structure using a laser sintering powder (a second embodiment of the method for producing a structure according to the invention), respectively. Hereinafter, with reference toFIGS. 8A to 8F andFIGS. 9A to 9E , the method for forming a structure will be described. In this method, a laser sintering apparatus 25 (a second embodiment of the apparatus for producing a structure according to the invention) shown inFIG. 7 is used. - First, the
laser sintering apparatus 25 shown inFIG. 7 will be described. InFIG. 7 , in thelaser sintering apparatus 25, only a portion around therail 32 is extracted and shown. - The
laser sintering apparatus 25 shown inFIG. 7 is the same as thelaser sintering apparatus 25 shown inFIG. 4 except that a compressing unit which compresses thepowder layer 1 a in the thickness direction is added. - That is, the
laser sintering apparatus 25 shown inFIG. 7 further includes a compressing mechanism (compressing unit) 39, which is disposed on the movingstage 33 that moves along therail 32, and is capable of coming into contact with thepowder layer 1 a and compressing thepowder layer 1 a in the thickness direction. When the movingstage 33 moves along therail 32, thecompressing mechanism 39 can move with the movement of the movingstage 33. - The
compressing mechanism 39 includes arotating shaft 391 in parallel with the surface of thepowder layer 1 a, aroller 392 rotatably provided around therotating shaft 391, and alifting device 393 capable of moving therotating shaft 391 and theroller 392 in the vertical direction inFIG. 7 . There is a low possibility that theroller 392 carelessly scrapes off thepowder layer 1 a, and therefore, thepowder layer 1 a is easily crushed to a desired thickness. Further, the structure of the roller is simple and also small, and therefore, even if the roller is disposed on the movingstage 33, the driving of the movingstage 33 is hardly inhibited. - In the
roller 392, a portion which comes in contact with thepowder layer 1 a may be formed from a material which prevents the adhesion to thepowder layer 1 a as desired. Further, the portion which comes in contact with thepowder layer 1 a may be subjected to a surface treatment with a material which prevents the adhesion to thepowder layer 1 a, or an adhesion preventive layer may be deposited thereon as desired. - Further, the
compressing mechanism 39 is electrically or optically connected to thecontrol section 45 through a wiring (not shown). According to this, the operation of thecompressing mechanism 39 can be controlled by thecontrol section 45. - The structure of the
compressing mechanism 39 is not limited to the above-described structure, and for example, in place of theroller 392, an arbitrary member capable of compressing thepowder layer 1 a in the thickness direction such as a flat plate which compresses thepowder layer 1 a in the thickness direction can be used. - Next, a method for forming a structure shown in FIGS. 8A to 8F and
FIGS. 9A to 9E will be described. - First, as shown in
FIG. 8A , thelaser sintering powder 1 is placed in thehopper 34 of thelaser sintering apparatus 25. Subsequently, thelaser sintering powder 1 is supplied to the bottom 30 a of thevessel 30 from thedischarge port 34 a. As the movingstage 33 moves, the surface of the suppliedlaser sintering powder 1 is leveled, and therefore, as shown inFIG. 8B , the first layer of thepowder layer 1 a having a substantially uniform thickness is formed (a powder layer forming step). - Subsequently, the leveled surface of the first layer of the
powder layer 1 a is compressed in the thickness direction by the compressing mechanism 39 (a powder layer compressing step). By doing this, as shown inFIG. 8C , the first layer of thepowder layer 1 a is crushed in the thickness direction to reduce the volume, and therefore is consolidated. That is, by moving theroller 392 along the surface of the first layer of thepowder layer 1 a while rotating theroller 392, the first layer of thepowder layer 1 a is crushed in the thickness direction by theroller 392. At this time, by appropriately adjusting the distance between the bottom 30 a of thevessel 30 and theroller 392 by thelifting device 393, the degree of consolidation can be controlled. A guide to the degree of consolidation can be exemplified as follows: for example, in the case where thesintered layer 1 b is formed by sintering themetal particles 2, the first layer of thepowder layer 1 a is consolidated to a thickness equivalent to the thickness of thesintered layer 1 b. - Subsequently, as shown in
FIG. 8D , thehot air 23 is blown on the first layer of thepowder layer 1 a. By doing this, the first layer of thepowder layer 1 a is heated. Subsequently, thelaser light 4 is irradiated such that the light is condensed on the first layer of thepowder layer 1 a (a laser sintering step). By doing this, a given pattern is drawn on the first layer of thepowder layer 1 a. As a result, as shown inFIG. 8E , asintered layer 1 b in which themetal particles 2 are sintered is formed in a region of the first layer of thepowder layer 1 a irradiated with thelaser light 4. - Subsequently, as shown in
FIG. 8F , apowder layer 1 a which is the second layer of thelaser sintering powder 1 is formed so as to overlap with the first layer of thepowder layer 1 a and thesintered layer 1 b (a powder layer forming step). - Subsequently, the leveled surface of the second layer of the
powder layer 1 a is compressed in the thickness direction by the compressing mechanism 39 (a powder layer compressing step). By doing this, as shown inFIG. 9A , the second layer of thepowder layer 1 a is crushed in the thickness direction to reduce the volume, and therefore is consolidated. Also in this case, a guide to the degree of consolidation can be exemplified as follows: when thesintered layer 1 b is formed by sintering themetal particles 2, the second layer of thepowder layer 1 a is consolidated to a thickness equivalent to the thickness of thesintered layer 1 b. - Subsequently, as shown in
FIG. 9B , thehot air 23 is blown on the second layer of thepowder layer 1 a. By doing this, the second layer of thepowder layer 1 a is heated. Subsequently, thelaser light 4 is irradiated such that the light is condensed on the second layer of thepowder layer 1 a (a laser sintering step). By doing this, a given pattern is drawn on the second layer of thepowder layer 1 a. As a result, as shown inFIG. 9C , asintered layer 1 b in which themetal particles 2 are sintered is formed in a region of the second layer of thepowder layer 1 a irradiated with thelaser light 4. - Thereafter, the step of forming the
powder layer 1 a so as to overlap with thesintered layer 1 b formed by drawing, the step of compressing thepowder layer 1 a in the thickness direction, and the step of emitting thelaser light 4 to thepowder layer 1 a are repeated in this order. As a result, as shown inFIG. 9D , in thevessel 30, astructure 49 in which a number ofsintered layers 1 b sintered in a given pattern are stacked is formed. Then, as shown inFIG. 9E , thestructure 49 is taken out from thevessel 30, and thelaser sintering powder 1 adhered to thestructure 49 is removed, whereby the production of thestructure 49 is completed. - In the
structure 49 obtained by the production method as described above, therespective powder layers 1 a are compressed individually, and therefore, when themetal particles 2 are sintered by irradiating thepowder layer 1 a with thelaser light 4, the volume reduction accompanying the sintering can be minimized. - Specifically, when the
metal particles 2 are sintered in a state where thepowder layer 1 a is not compressed, depending on the particle diameter of thelaser sintering powder 1 or the particle diameter of themetal particles 2, the volume of thepowder layer 1 a in the sintered region is relatively greatly reduced accompanying the sintering of themetal particles 2 in some cases. When such a great volume reduction is caused, a large difference in volume between thesintered layer 1 b formed by the sintering of themetal particles 2 and thepowder layer 1 a adjacent thereto occurs so that the thickness is different between thesintered layer 1 b and thepowder layer 1 a. In such a case, when the step of forming thepowder layer 1 a and the step of emitting thelaser light 4 are repeated, this thickness difference is accumulated, and therefore, when anew powder layer 1 a is formed, the thickness of thenew powder layer 1 a to be formed may vary depending on the condition of the underlayer, that is, whether the underlayer is thepowder layer 1 a or thesintered layer 1 b. As a result, the thickness of thenew powder layer 1 a becomes non-uniform, and thus, it becomes difficult to produce thestructure 49 having a desired shape. Further, when the volume of thepowder layer 1 a in the sintered region is relatively greatly reduced accompanying the sintering of themetal particles 2, it may become difficult to irradiate a region hidden behind thepowder layer 1 a whose volume is not reduced with thelaser light 4. - On the other hand, by adding the step of compressing the
powder layer 1 a in the thickness direction as in this embodiment, spaces for causing the volume reduction accompanying the sintering of themetal particles 2 can be crushed in advance. By doing this, even if themetal particles 2 are sintered, the volume reduction accompanying the sintering can be minimized. As a result, a difference in thickness between thesintered layer 1 b and thepowder layer 1 a can be made sufficiently small, and therefore, when anew powder layer 1 a is formed thereon, apowder layer 1 a having a uniform thickness can be formed regardless of the condition of the underlayer. Further, the volume reduction accompanying the sintering of themetal particles 2 can be made sufficiently small, and therefore, the inhibition of the irradiation with thelaser light 4 by thepowder layer 1 a can be prevented. - In this manner, according to this embodiment, even in the case where the volume of the
powder layer 1 a is greatly reduced accompanying the sintering of themetal particles 2, the shape of thestructure 49 to be produced can be prevented from being largely deviated from the design value, and thus, the dimensional accuracy of thestructure 49 can be further enhanced. - Incidentally, also in the second embodiment as described above, the same effects and advantages as those in the first embodiment can be obtained.
- Next, a third embodiment of the method for producing a structure according to the invention will be described.
- Hereinafter, a third embodiment will be described, however, in the following description, different points from the second embodiment will be mainly described, and the description of the same matter will be omitted. Further, in the drawings, the same components as in the above-described embodiments will be given the same reference numerals.
-
FIGS. 10A to 10F andFIGS. 11A to 11E are schematic views for explaining a method for forming a structure using a laser sintering powder (a third embodiment of the method for producing a structure according to the invention), respectively. Hereinafter, with reference toFIGS. 10A to 10F andFIGS. 11A to 11E , the method for forming a structure will be described. Also in this method, thelaser sintering apparatus 25 shown inFIG. 7 is used. - The third embodiment is the same as the second embodiment except that the timing of the step of compressing the
powder layer 1 a in the thickness direction is different. - Specifically, first, as shown in
FIG. 10A , thelaser sintering powder 1 is placed in thehopper 34 of thelaser sintering apparatus 25. Subsequently, thelaser sintering powder 1 is supplied to the bottom 30 a of thevessel 30 from thedischarge port 34 a. As the movingstage 33 moves, the surface of the suppliedlaser sintering powder 1 is leveled, and therefore, as shown inFIG. 10B , the first layer of thepowder layer 1 a having a substantially uniform thickness is formed (a powder layer forming step). - Subsequently, as shown in
FIG. 10C , thehot air 23 is blown on the first layer of thepowder layer 1 a. By doing this, the first layer of thepowder layer 1 a is heated. Subsequently, thelaser light 4 is irradiated such that the light is condensed on the first layer of thepowder layer 1 a (a laser sintering step). By doing this, a given pattern is drawn on the first layer of thepowder layer 1 a. As a result, as shown inFIG. 10D , asintered layer 1 b in which themetal particles 2 are sintered is formed in a region of the first layer of thepowder layer 1 a irradiated with thelaser light 4. - Subsequently, the surface of the first layer of the
powder layer 1 a is compressed in the thickness direction by the compressing mechanism 39 (a powder layer compressing step). By doing this, as shown inFIG. 10E , the first layer of thepowder layer 1 a is crushed in the thickness direction to reduce the volume, and therefore is consolidated. That is, by moving theroller 392 along the surface of the first layer of thepowder layer 1 a while rotating theroller 392, the first layer of thepowder layer 1 a is crushed in the thickness direction by theroller 392. At this time, in the case where thesintered layer 1 b is present in the moving path of theroller 392, the distance between the bottom 30 a of thevessel 30 and theroller 392 depends on thesintered layer 1 b and cannot be made smaller than the thickness of thesintered layer 1 b. Therefore, the first layer of thepowder layer 1 a is consolidated to a thickness equivalent to the thickness of thesintered layer 1 b. Incidentally, also in the case where thesintered layer 1 b is not present in the moving path of theroller 392, when the first layer of thepowder layer 1 a is consolidated, it is preferred to consolidate the first layer of thepowder layer 1 a to a thickness equivalent to the thickness of thesintered layer 1 b. By doing this, when the second layer of thepowder layer 1 a is formed so as to overlap with the first layer of thepowder layer 1 a and thesintered layer 1 b, thepowder layer 1 a having a uniform thickness is easily formed. - Subsequently, as shown in
FIG. 10F , apowder layer 1 a which is the second layer of thelaser sintering powder 1 is formed so as to overlap with the first layer of thepowder layer 1 a and thesintered layer 1 b (a powder layer forming step). - Subsequently, as shown in
FIG. 11A , thehot air 23 is blown on the second layer of thepowder layer 1 a. By doing this, the second layer of thepowder layer 1 a is heated. Subsequently, thelaser light 4 is irradiated such that the light is condensed on the second layer of thepowder layer 1 a (a laser sintering step). By doing this, a given pattern is drawn on the second layer of thepowder layer 1 a. As a result, as shown inFIG. 11B , asintered layer 1 b in which themetal particles 2 are sintered is formed in a region of the second layer of thepowder layer 1 a irradiated with thelaser light 4. - Subsequently, the surface of the second layer of the
powder layer 1 a is compressed in the thickness direction by the compressing mechanism 39 (a powder layer compressing step). By doing this, as shown inFIG. 11C , the second layer of thepowder layer 1 a is crushed in the thickness direction to reduce the volume, and therefore is consolidated. Also at this time, in the case where thesintered layer 1 b is present in the moving path of theroller 392, the second layer of thepowder layer 1 a is consolidated to a thickness equivalent to the thickness of thesintered layer 1 b. - Thereafter, the step of forming the
powder layer 1 a so as to overlap with thesintered layer 1 b formed by drawing, the step of emitting thelaser light 4 to thepowder layer 1 a, and the step of compressing thepowder layer 1 a in the thickness direction are repeated in this order. As a result, as shown inFIG. 11D , in thevessel 30, astructure 49 in which a number ofsintered layers 1 b sintered in a given pattern are stacked is formed. Then, as shown inFIG. 11E , thestructure 49 is taken out from thevessel 30, and thelaser sintering powder 1 adhered to thestructure 49 is removed, whereby the production of thestructure 49 is completed. - In the
structure 49 obtained by the production method as described above, therespective powder layers 1 a are compressed individually after thesintered layer 1 b is formed by irradiating thepowder layer 1 a with thelaser light 4, and therefore, the surface levels of thepowder layer 1 a and thesintered layer 1 b are easily equalized. Therefore, when anew powder layer 1 a is formed on the surface of thepowder layer 1 a and thesintered layer 1 b, apowder layer 1 a having a uniform thickness can be formed. As a result, astructure 49 having a desired shape can be produced. - Incidentally, also in the third embodiment as described above, the same effects and advantages as those in the first and second embodiments can be obtained.
- Next, specific examples of the invention will be described.
-
FIGS. 12 and 13 are tables showing examples in which metal particles of SUS301 were sintered. InFIG. 12 , as themetal particles 2, particles of an alloy containing iron, nickel, and chromium were formed and used. Themetal particles 2 were produced by a water atomization method. Then, by changing the production conditions, themetal particles 2 having a different average particle diameter were obtained. As the binder, PVA was used, and as the solvent, ion exchanged water was used. - A mixture of the
metal particles 2, the binder, and the solvent was placed in the second vessel of the spray drying apparatus shown inFIG. 3 . Then, from theejection port 16, liquid droplets composed of themetal particles 2, the binder, and the solvent were dropped. The liquid droplets were broken up into small liquid droplets by the rotary plate. The small liquid droplets were dried by hot air, whereby a laser sintering powder 1 (granulated powder) was obtained. Then, by changing the size of the liquid droplets and the rotation speed of the rotary plate, various types oflaser sintering powders 1 having a different average particle diameter were obtained. - The average particle diameter of the
metal particles 2 and the average particle diameter of thelaser sintering powder 1 were each obtained as a particle diameter at 50% accumulation in a cumulative particle size distribution on a mass basis using a laser diffraction particle size distribution analyzer (Microtrack HRA9320-X100, manufactured by Nikkiso Co., Ltd.). - In
FIG. 13 , as shown in Examples 1 to 36,laser sintering powders 1 having an average particle diameter of 25 to 55 μm were formed by performing granulation using themetal particles 2 having an average particle diameter of 3 to 13 In Example 1, alaser sintering powder 1 having an average particle diameter of 30 μm was formed by performing granulation using themetal particles 2 having an average particle diameter of 5.1 Then, thelaser sintering powder 1 was sintered, whereby astructure 49 was formed. - As shown in Examples 1 to 15, when the average particle diameter of the
metal particles 2 was from 5 to 10 μm, and the average particle diameter of thelaser sintering powder 1 was from 30 to 50 μm, the surface of the formed structure was glossy, and good results were obtained. - As shown in Examples 16 to 20, when the average particle diameter of the
metal particles 2 was from 5 to 10 μm, and the average particle diameter of thelaser sintering powder 1 exceeded 50 μm, the surface of the formed structure was not glossy, and bad results were obtained. As shown in Examples 21 to 25, when the average particle diameter of themetal particles 2 was from 5 to 10 μm, and the average particle diameter of thelaser sintering powder 1 was less than 30 μm, themetal particles 2 moved when thelaser light 4 was irradiated, and the structures had a poor shape. Accordingly, bad results were obtained under the conditions of Examples 21 to 25. - As shown in Examples 26 to 34, when the average particle diameter of the
metal particles 2 exceeded 10 μm, and the average particle diameter of thelaser sintering powder 1 was from 30 to 50 μm, the surface of the formed structure was not glossy, and bad results were obtained. As shown in Examples 35 and 36, when the average particle diameter of themetal particles 2 was less than 5 μm, a variation in the particle diameter of thelaser sintering powder 1 was large, and a normallaser sintering powder 1 could not be granulated. -
FIGS. 14A to 16D are tables showing examples in which various types of metal particles containing iron as a principal component were sintered. InFIGS. 14A to 16D , as shown in Examples 37 to 48, when the average particle diameter of themetal particles 2 was from 5 to 10 μm, and the average particle diameter of thelaser sintering powder 1 was from 30 to 50 μm, the surface of the formed structure was glossy, and good results were obtained. As shown in Example 49, when the average particle diameter of themetal particles 2 exceeded 10 μm, and the average particle diameter of thelaser sintering powder 1 exceeded 50 μm, the surface of the formed structure was not glossy, and bad results were obtained. In the same manner, as shown in Example 50, even if the average particle diameter of themetal particles 2 was from 5 to 10 μm, when the average particle diameter of thelaser sintering powder 1 exceeded 50 μm, the surface of the formed structure was not glossy, and bad results were obtained. -
FIGS. 17A-D and 18A-D are tables showing examples in which various types of metal particles containing cobalt as a principal component were sintered. InFIGS. 17A-D and 18A-D, as shown in Examples 51 to 58, when the average particle diameter of themetal particles 2 was from 5 to 10 μm, and the average particle diameter of thelaser sintering powder 1 was from 30 to 50 μm, the surface of the formed structure was glossy, and good results were obtained. -
FIGS. 19A-E and 20 are tables showing examples in which various types of metal particles containing nickel as a principal component were sintered. InFIGS. 19A-E and 20, as shown in Examples 59 to 64, when the average particle diameter of themetal particles 2 was from 5 to 10 μm, and the average particle diameter of thelaser sintering powder 1 was from 30 to 50 μm, the surface of the formed structure was glossy, and good results were obtained. -
FIGS. 21A-F are tables showing examples in which metal particles of SUS316L were sintered. InFIGS. 21A-F , as themetal particles 2, particles of an alloy containing iron, nickel, and chromium were formed and used. The metal particles were produced by a water atomization method or a gas atomization method. Then, by changing the production conditions, themetal particles 2 having a different average particle diameter were obtained by a water atomization method and a gas atomization method, respectively. As the binder, PVP was used, and as the solvent, ion exchanged water was used. - In
FIGS. 21A-F , as shown in Examples 65 to 70, when the average particle diameter of thelaser sintering powder 1 was 3 times or more and 10 times or less larger than the average particle diameter of themetal particles 2, the surface of the formed structure was glossy, and good results were obtained. - Further, it was confirmed that in the case where the
metal particles 2 produced by the water atomization method were used, the dimensional accuracy of the formed structure was higher (the deviation from the design value was smaller) as compared with the case where themetal particles 2 produced by the gas atomization method were used. Incidentally, this dimensional accuracy was evaluated by comparing the degree of deviation of the actual value of the height (thickness) of thestructure 49 from the design value thereof. - In Examples 65 and 70, when the aspect ratios of the
metal particles 2 were compared, the average of the aspect ratio (minor axis S/major axis L) of themetal particles 2 produced by the water atomization method was about 0.54 to 0.75, however, the average of the aspect ratio of themetal particles 2 produced by the gas atomization method was 0.86 to 0.94, which was slightly high. -
FIGS. 22A-F are tables showing examples in which metal particles of SUS316L were used and sintering was performed by adding a powder layer compressing step which was performed before a laser sintering step (light exposure). Also inFIGS. 22A-F , themetal particles 2 were produced by a water atomization method or a gas atomization method. Then, by changing the production conditions, themetal particles 2 having a different average particle diameter were obtained by a water atomization method and a gas atomization method, respectively. As the binder, PVP was used, and as the solvent, ion exchanged water was used. - In
FIGS. 22A-F , as shown in Examples 71 to 76, it was confirmed that in the case where themetal particles 2 produced by the water atomization method were used, the dimensional accuracy of the formed structure was higher (the deviation from the design value was smaller) as compared with the case where themetal particles 2 produced by the gas atomization method were used. - Further, by comparing
FIGS. 21A-F withFIGS. 22A-F , it was confirmed that by providing the powder layer compressing step before the laser sintering step (light exposure), the dimensional accuracy of the producedstructure 49 was increased as compared with the case where the powder layer compressing step was not provided. -
FIGS. 23A-F are tables showing examples in which metal particles of SUS316L were used and sintering was performed by adding a powder layer compressing step which was performed after a laser sintering step (light exposure). Also inFIGS. 23A-F , themetal particles 2 were produced by a water atomization method or a gas atomization method. Then, by changing the production conditions, themetal particles 2 having a different average particle diameter were obtained by a water atomization method and a gas atomization method, respectively. As the binder, PVP was used, and as the solvent, ion exchanged water was used. - In
FIGS. 23A-F , as shown in Examples 77 to 82, it was confirmed that in the case where themetal particles 2 produced by the water atomization method were used, the dimensional accuracy of the formed structure was higher (the deviation from the design value was smaller) as compared with the case where themetal particles 2 produced by the gas atomization method were used. - Further, by comparing
FIGS. 21A-F withFIGS. 23A-F , it was also confirmed that in the case where the powder layer compressing step was provided after the laser sintering step (light exposure), the dimensional accuracy of the producedstructure 49 was increased as compared with the case where the powder layer compressing step was not provided. -
FIGS. 24A-F are tables showing examples in which metal particles of SUS316L were used, and also a spray drying method or a tumbling granulation method was used as the granulation method, and sintering was performed by adding a powder layer compressing step. InFIGS. 24A-F , themetal particles 2 were produced by a water atomization method. Then, by changing the production conditions, themetal particles 2 having a different average particle diameter were obtained. As the binder, PVA was used, and as the solvent, ion exchanged water was used. - In
FIGS. 24A-F , as shown in Examples 83 to 88, it was confirmed that when thelaser sintering powder 1 produced by a spray drying method was used, the dimensional accuracy of the formed structure was higher as compared with the case where thelaser sintering powder 1 produced by a tumbling granulation method was used. - Incidentally, the cross sections of the laser sintering powders 1 produced in Examples 83 to 85 were observed with an electron microscope, and it was confirmed that 50% by number or more of the particles have pores therein. Then, the volume ratio of the pores was calculated for 100 particles among them, and it was about 5 to 50% by volume.
- On the other hand, the cross sections of the laser sintering powders 1 produced in Examples 86 to 88 were observed with an electron microscope, and it was found that there were few particles confirmed to have pores therein (20% by number or less).
- As described above, according to this embodiment, the following effects are obtained.
- (1) According to this embodiment, the
laser sintering powder 1 is configured such that a plurality of themetal particles 2 are bound to one another by thebinder 3. Thelaser sintering powder 1 is placed to a given thickness. Then, when thelaser sintering powder 1 is irradiated with thelaser light 4, themetal particles 2 irradiated with thelaser light 4 are heated, and thebinder 3 is decomposed and vaporized. At this time, a large energy is applied to a shallow region of thelaser sintering powder 1, and a small energy is applied to a deep region thereof. The heat capacity of themetal particles 2 can be decreased when the size of themetal particles 2 is small. Therefore, the temperature of themetal particles 2 can be easily increased. Accordingly, since the temperature of themetal particles 2 located in a deep region can be increased, themetal particles 2 can be reliably sintered even in a deep region. - (2) According to this embodiment, a step of placing the
laser sintering powder 1 to a given thickness as thepowder layer 1 a and a step of drawing a given pattern with thelaser light 4 are alternately repeated. In the case where there is a difference in heating of themetal particles 2 by thelaser light 4 in the depth direction, a laminate in which a completely sintered layer and an incompletely sintered layer are stacked is formed. According to thelaser sintering powder 1 of this embodiment, since the particle diameter of themetal particles 2 is small, a difference in heating of themetal particles 2 by thelaser light 4 in the depth direction is prevented from occurring. As a result, thestructure 49 obtained by laser sintering can be configured such that the side surfaces on the left and right sides in the drawing can also be made glossy. Further, thestructure 49 formed by irradiating thelaser sintering powder 1 with thelaser light 4 has a low degree of anisotropy of the strength in the thickness direction. Further, thestructure 49 obtained by laser sintering can be configured such that interlayer peeling hardly occurs. - (3) According to this embodiment, the average particle diameter of the
laser sintering powder 1 is 30 μm or more and 50 μm or less. When the laser sintering powder is placed to a given thickness and a given pattern is drawn with thelaser light 4, thelaser sintering powder 1 having an average particle diameter of 30 μm or more and 50 μm or less is hardly stirred up. Therefore, the metal with an accurate thickness can be sintered, and thus, thestructure 49 can be accurately formed. - (4) According to this embodiment, the average particle diameter of the
metal particles 2 is 5 μm or more and 10 μm or less, and therefore, the heat capacity of themetal particles 2 is decreased so that the temperature when heating can be easily increased. As a result, themetal particles 2 can be sintered with good quality, and therefore, thestructure 49 can be formed with good quality. - (5) According to this embodiment, the
metal particles 2 are heated to a sintering temperature without melting. If a metal is heated until it melts, the melting metal flows in the direction where the gravitational force acts. By heating the metal not until it melts, but until the sintering temperature is reached, the metal can be accurately formed into a shape as it is drawn. Accordingly, thestructure 49 can be accurately shaped. - (6) According to this embodiment, the
metal particles 2 are arranged in lines (layers) in the thickness direction. Therefore, the surface roughness of the side surfaces of thestructure 49 can be made small. - The present embodiments are not limited to the details described above, and various alterations or improvements can be made by a person with an ordinary skill in the art within the technical ideas of the present invention. Hereinafter some modification examples will be described.
- In the embodiments described above, the
powder layer 1 a is sintered by irradiating thepowder layer 1 a with thelaser light 4. However, thesintered layer 1 b may be further heated. By doing this, astructure 49 having high peeling resistance strength can be obtained. - In the embodiments described above, the
structure 49 is formed by stacking thesintered layers 1 b. However, thestructure 49 may be further subjected to a heat treatment. This can enhance the performance of thestructure 49. In addition, as a post-treatment, a surface treatment may be performed. - In the embodiments described above, the
scanner 41 scans thelaser light 4. However, theXY stage 28 may scan thevessel 30. Then, thescanner 41 is excluded and themirror 41 a may be fixed. By doing this, the production of thelaser sintering apparatus 25 can be facilitated. - In the embodiments described above, the
laser sintering apparatus 25 is provided with the hotair blowing unit 43. However, when themetal particles 2 can be sintered by thelaser light 4 without blowing thehot air 23 on thelaser sintering powder 1, the hotair blowing unit 43 may be an air blowing unit which does not include a heating section, or the hotair blowing unit 43 and theair blowing tube 44 may not be provided. According to this, the production of thelaser sintering apparatus 25 can be facilitated by decreasing the constituent elements thereof. - In the embodiments described above, the powder layer compressing step is performed before or after the laser sintering step, however, the powder layer compressing step may be performed both before and after the laser sintering step. According to this, the dimensional accuracy of the
structure 49 to be produced can be further more enhanced. - The entire disclosures of Japanese Patent Application Nos. 2013-213468 filed Oct. 11, 2013 and 2014-167738 filed Aug. 20, 2014 are expressly incorporated by reference herein.
Claims (12)
1. A laser sintering powder which is sintered by irradiation with a laser light, comprising:
a plurality of metal particles; and
a binder which binds the metal particles to one another, wherein
the binder contains a material which is decomposed and vaporized by the laser light.
2. The laser sintering powder according to claim 1 , wherein an average particle diameter of the metal particles is 5 μm or more and 10 μm or less, and an average particle diameter of the laser sintering powder is 30 μm or more and 50 μm or less.
3. The laser sintering powder according to claim 1 , wherein an average particle diameter of the laser sintering powder is 3 times or more and 10 times or less larger than an average particle diameter of the metal particles.
4. The laser sintering powder according to claim 1 , wherein the metal particles contain any one of iron, nickel, and cobalt as a principal component and are produced by an atomization method.
5. The laser sintering powder according to claim 4 , wherein the metal particles contain iron as a principal component, and at least one of nickel, chromium, molybdenum, and carbon.
6. The laser sintering powder according to claim 1 , wherein the binder is polyvinyl alcohol.
7. A method for producing a structure, comprising:
forming a powder layer composed of a laser sintering powder in which a plurality of metal particles are bound to one another by a binder; and
sintering the metal particles by emitting a laser light to the powder layer to draw a given pattern and vaporizing the binder, wherein
a structure in which the metal particles are sintered is formed by alternately repeating the forming of a powder layer so as to overlap with the powder layer having the pattern drawn thereon and the sintering.
8. The method for producing a structure according to claim 7 , wherein the metal particles irradiated with the laser light are sintered by heating to a temperature at which the metal particles do not melt.
9. The method for producing a structure according to claim 7 , further comprising compressing the powder layer in a thickness direction.
10. An apparatus for producing a structure, comprising:
a powder layer forming unit which forms a powder layer using a laser sintering powder in which a plurality of metal particles are bound to one another by a binder; and
a laser light source which emits a laser light to the powder layer.
11. The apparatus for producing a structure according to claim 10 , further comprising a compressing unit which compresses the powder layer in a thickness direction.
12. The apparatus for producing a structure according to claim 11 , wherein the compressing unit includes a roller selectively coming in contact with the powder layer.