US20130323069A1 - Turbine Blade for Industrial Gas Turbine and Industrial Gas Turbine - Google Patents
Turbine Blade for Industrial Gas Turbine and Industrial Gas Turbine Download PDFInfo
- Publication number
- US20130323069A1 US20130323069A1 US13/904,097 US201313904097A US2013323069A1 US 20130323069 A1 US20130323069 A1 US 20130323069A1 US 201313904097 A US201313904097 A US 201313904097A US 2013323069 A1 US2013323069 A1 US 2013323069A1
- Authority
- US
- United States
- Prior art keywords
- barrier layer
- substrate
- diffusion barrier
- gas turbine
- blade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present application claims priority from Japanese Patent application serial No. 2012-122810, filed on May 30, 2012, the content of which is hereby incorporated by reference into this application.
- 1. Field of the Invention
- The present invention relates to a long-life turbine blade for industrial gas turbine including a blade substrate of a low-Re (low-rhenium) single crystal alloy, the blade substrate having a thermal barrier coating (TBC) thereon, and an industrial gas turbine including the turbine blade.
- 2. Description of Related Art
- Recently, combustion gas temperature of a gas turbine has been increased to improve efficiency. Along with this, each of alloy members such as a turbine blade and a turbine nozzle has had the thermal barrier coating (TBC).
- The TBC includes a top coat as a thermal barrier formed of an oxide having a low coefficient of thermal conductivity. Such an oxide typically includes yttria stabilized zirconia (YSZ) that contains yttria added thereto to stabilize the crystal structure thereof. The TBC also includes a bond coat for securing certain oxidation resistance and corrosion resistance, the bond coat including MCrAlY alloy (M is at least one of Ni, Co and Fe) or aluminide such as Ni—Al or Ni—Al—Pt.
- The bond coat includes a thermal grown oxide (TGO) formed on a surface of the blade to protect the substrate from oxidizing and corrosive environment. Since alumina is preferred as the TGO, the bond coat generally has a high Al concentration compared with the substrate. Thus, Al may diffuse from the bond coat to the substrate during high temperature service, causing formation of a secondary reaction zone (SRZ) in the substrate which may reduce strength of the substrate. To solve this problem, Japanese Unexamined Patent
- Application Publication No. 2007-186788 (Patent Document 1) discloses a diffusion barrier layer including an alloy layer containing Ru or Re which suppresses diffusion of any element between the substrate and the bond coat. Japanese Unexamined Patent Application Publication No. 2008-156697 (Patent Document 2) discloses an example of a diffusion barrier layer including an intermetallic compound containing Re, Cr and Ni.
- Japanese Patent No. 3559670 (Patent Document 3) discloses a high-strength Ni-base superalloy for directional solidification having a predetermined composition which is free from occurrence of solidification cracking during casting, has grain boundary strength enough to secure reliability during service, and has excellent high-temperature strength.
- The diffusion barrier layer corresponds to an equilibrium phase in a phase diagram for a substrate-bond coat system. In other words, the diffusion barrier layer must be thermodynamically stable. The alloy layer containing Ru or Re described in
Patent Document 1, however, is increasingly decomposed at high temperature through a reaction of the substrate and the bond coat, and is thus failed to maintain the above-described effects. - In contrast, the o phase of the intermetallic compound containing Re, Cr and Ni described in
Patent Document 2 is an equilibrium phase between the substrate and the bond coat, and is thus thermodynamically stable, thereby the diffusion barrier layer can maintain its function for a long time. - The industrial gas turbine (hereinafter, abbreviated as “gas turbine”) is now necessary to be improved in efficiency in light of a reduction in carbon dioxide emissions . Increasing combustion gas temperature is an effective way to improve efficiency. Hence, heatproof temperature of a substrate for a turbine blade and a turbine nozzle must be increased, and a casting-solidification-controlled single-crystal material is a most promising material for the substrate.
- Furthermore, some turbine blade or turbine nozzle has the thermal barrier coating (TBC) combined with high-performance cooling, which may allow the cooling air content to be reduced, and allows surplus air to be used for combustion, and thereby helps to improve efficiency. As described above, blade substrate temperature is designed to be an upper limit of the heatproof temperature of the single crystal material in this approach. As a result, temperature of the TBC bond layer also increases, which accelerates counter diffusion at an interface between the bond layer and the substrate. Consequently, a recrystallized layer due to the counter diffusion is formed in a surface of the substrate (particularly, the single crystal material), and oxidation resistance of the bond layer is reduced after long service. Hence, the diffusion barrier layer is necessary at the interface between the bond layer and the substrate.
- In addition, the gas turbine blade has a unique issue, i.e. , has differences from an aircraft turbine blade that often includes a single crystal blade, as described below. The heatproof temperature is designed with reference to 50,000 to 100,000 hour creep rupture strength for the gas turbine blade, while being designed with reference to a shorter period, i.e., thousands of hours creep rupture strength for the aircraft turbine blade. Furthermore, the gas turbine blade has a dimension about 10 to 20 times as large as that of the aircraft turbine blade. Based on such differences, first, a single-crystal gas turbine blade assumed to have a long life is essentially subjected to solution heat treatment and aging at accurate temperature, and is essentially not subjected to post-forming high-temperature heat treatment to prevent recrystallization of a structure maintaining certain material strength.
- Hence, for example, while
Patent Document 2 exemplifies formation of the barrier layer at high temperature (solution heat treatment temperature), such a process cannot be applied to the single-crystal gas turbine blade due to a possibility of recrystallization at a blade forming portion. In some exemplary case, the barrier layer is formed at a relatively low temperature (aging temperature) . In such a case, however, the barrier layer has turned out to be somewhat brittle as a result of investigations of the inventors. - Second, the gas turbine blade has a dimension about 10 to 20 times as large as that of the aircraft turbine blade. A large blade further has a significant issue, i.e., yield in a precision casting process of the blade.
- Third, such a difference in blade size is also associated with a deposition process of TBC. For the large gas turbine blade, the bond-layer metal and the top-layer ceramics are each preferably deposited by thermal spray in light of cost. A physical evaporation process which allows a large number of blades to be processed in one batch is costly promising for the small aircraft turbine blade. In the thermal spray process, blast treatment is usually performed as pretreatment before thermal spray operation of the bond coat to improve adhesion of the bond coat to a substrate, in which hard particles such as alumina particles are bombarded to a surface of the substrate to roughen and clean the surface.
- As known from the above results, the gas turbine blade is required to be long in life compared with the aircraft turbine blade. The gas turbine blade therefore must be a single-crystal blade having a predetermined alloy component. In addition, the barrier layer must be deposited at low temperature. The barrier layer deposited at low temperature is slightly brittle, and thus may be damaged to lose its functions by the blast treatment in the thermal spray process required for TBC operation of the large blade.
- An object of the invention is to provide a long-life turbine blade for industrial gas turbine having a thermal barrier coating formed by a thermal spray process without loss of a function of a diffusion barrier layer, and provide an industrial gas turbine including the turbine blade.
- To solve the above-described problem, a turbine blade for industrial gas turbine of the present invention is characterized by including a blade substrate formed of a single crystal alloy containing C: 0.06 to 0.08%, B: 0.016 to 0.035%, Hf: 0.2 to 0.3%, Cr: 6.9 to 7.3%, Mo: 0.7 to 1.0%, W: 7.0 to 9.0%, Re: 1.2 to 1.6%, Ta: 8.5 to 9.5%, Nb: 0.6 to 1.0%, Al: 4.9 to 5.2%, Co: 0.8 to 1.2%, and the remainder substantially consisting of Ni with reference to mass, and including a diffusion barrier layer, a metal layer, a bond coat, and a top coat, in which the diffusion barrier layer, the metal layer, the bond coat and the top coat are stacked in this order on a surface of the blade substrate, and the metal layer has a thickness of 5 to 30 μm.
- According to the present invention, a long-life turbine blade for industrial gas turbine having a thermal barrier coating formed by a thermal spray process without loss of a function of the diffusion barrier layer, and an industrial gas turbine including the turbine blade can be provided.
-
FIG. 1 is a schematic cross-sectional diagram showing a conventional heat-resistant alloy member; -
FIG. 2 is a schematic cross-sectional diagram showing a heat-resistant alloy member including a diffusion barrier layer; -
FIG. 3 is a flowchart showing a method of manufacturing the heat-resistant alloy member including the diffusion barrier layer; -
FIG. 4 is an SEM image of a cross-section showing a state after being subjected to a thermal spray of a heat-resistant alloy member including a diffusion barrier layer and a metal layer that is an Example; -
FIG. 5 is an SEM image of a cross-section showing a state after being subjected to a thermal spray of a heat-resistant alloy member including a diffusion barrier layer that is a comparative example; -
FIG. 6 is an SEM image of a cross-section showing a state after being subjected to high-temperature exposure at 1100° C. for 600 hr of the heat-resistant alloy member including the diffusion barrier layer and the metal layer that is the Example; -
FIG. 7 is an SEM image of a cross-section showing a state after being subjected to high-temperature exposure at 1100° C. for 600 hr of a conventional heat-resistant alloy member; -
FIG. 8 is a side view showing an industrial gas turbine including a turbine blade for industrial gas turbine of an Example; and -
FIG. 9 is an enlarged partial cross-sectional view showing a detail of a portion A inFIG. 8 . - The blade material of the present invention preferably includes the high-strength Ni-base superalloy for directional solidification according to
Patent Document 3 which contains grain-boundary strengthening elements such as C, B or Hf added thereto, has a large allowable crystal orientation difference of a particular crystal having an orientation different from that of the single crystal, and allows a large blade to be improved in yield in a precision casting process. In particular, a single-crystal heat-resistant alloy is practically suitable for a material composing a large single-crystal blade, the alloy containing C: 0.06 to 0.08%, B: 0.016 to 0.035%, Hf: 0.2 to 0.3%, Cr: 6.9 to 7.3%, Mo: 0.7 to 1.0%, W: 7.0 to 9.0%, Re: 1.2 to 1.6%, Ta: 8.5 to 9.5%, Nb: 0.6 to 1.0%, Al: 4.9 to 5.2%, Co: 0.8 to 1.2%, and the remainder substantially consisting of Ni with reference to mass. In other words, the remainder consists of Ni and inevitable impurities. - In this specification, for example, “0.06% or more and 0.08% or less” may be described as “0.06 to 0.08%”. The same holds true for other numerical ranges.
- Hereinafter, description is made with reference to drawings.
-
FIG. 1 shows a schematic cross-sectional diagram of a conventional heat-resistant alloy member. - The heat-resistant alloy member shown in this drawing includes a
substrate 5, and includes abond coat 3 and atop coat 4 provided in this order on a surface of thesubstrate 5. - The
substrate 5 secures certain strength of the heat-resistant alloy member. Thesubstrate 5 is subjected to high stress at high temperature and to repeated stress associated with start and stop. Thus, a material selected for thesubstrate 5 has high high-temperature creep strength and high fatigue strength. - A single-crystal alloy material having the above-described alloy composition is used for the
substrate 5 for the turbine blade for industrial gas turbine. - The
bond coat 3 protects thesubstrate 5 from corrosion and oxidation, and secures certain adhesion of thesubstrate 5 to thetop coat 4. - MCrAlY (M is at least one metal selected from a group consisting of Ni, Co and Fe) which exhibits excellent corrosion resistance and oxidation resistance is generally used for the
bond coat 3. For example, CoNiCrAlY (Co—32Ni-21Cr—8Al—0.5Y) and NiCoCrAlY (Ni—17Cr—23Co—12.5Al—0.5Y) are widely known as the MCrAlY. - The
top coat 4 is disposed on the surface of the heat-resistant alloy member to serve as a thermal barrier, and causes a temperature gradient between a hot combustion gas and thesubstrate 5 to prevent increase in surface temperature of thesubstrate 5. - A material having a low coefficient of thermal conductivity is used for the
top coat 4, for example, yttria stabilized zirconia (YSZ: containing Y2O3 in a range of 6 to 8 mass percent). A large number of pores are provided in the inside of thetop coat 4, thereby the coefficient of thermal conductivity of thetop coat 4 can be decreased to about 1/10 of that of the Ni-base alloy, i.e., about 0.5 to 2 W/m·K. - A method of manufacturing the heat-resistant alloy member shown in
FIG. 1 is now described. - First, a surface of the
substrate 5 is subjected to blast treatment as a pretreatment. The blast treatment is a process where nonmetallic particles such as silica sand or metal particles are blasted to thesubstrate 5 at high speed to roughen and clean the surface of thesubstrate 5. In the thermal spray, the blast treatment is a step of securing certain adhesion between thesubstrate 5 and thebond coat 3. - After the blast treatment, the
bond coat 3 for oxidation resistance and corrosion resistance is deposited by a low pressure plasma spray (LPPS) or a high velocity oxy-fuel frame-spraying (HVOF). - The thickness of the
bond coat 3 is usually about 100 to 200 micrometers, though not limited to. - After the deposition of the
bond coat 3, thetop coat 4 as a thermal barrier is usually formed by an air plasma spray (APS). - The
top coat 4 is usually deposited to a thickness of 250 to 300 μm. - The conventional heat-resistant alloy member shown in
FIG. 1 is manufactured through the above steps. -
FIG. 2 is a schematic cross-sectional diagram showing a configuration of a heat-resistant alloy member including a diffusion barrier layer as an Example. - The heat-resistant alloy member shown in this drawing includes a
substrate 5, and includes adiffusion barrier layer 1, ametal layer 2, abond coat 3 and atop coat 4 provided in this order on a surface of thesubstrate 5. - The
substrate 5, thebond coat 3 and thetop coat 4 are the same as those inFIG. 1 . - The
diffusion barrier layer 1 is provided to prevent diffusion of atoms between thesubstrate 5 and thebond coat 3. - In high-temperature environment, Al largely diffuses from the
bond coat 3 into thesubstrate 5, causing formation of a secondary reaction zone (SRZ) in thesubstrate 5, so that the structure of thesubstrate 5 varies. As a result, strength of thesubstrate 5 is reduced. On the other hand, elements such as Co, Mo, W, Ta, Nb, Ti, B and C diffuse into thebond coat 3 from thesubstrate 5, so that the composition of thebond coat 3 varies. As a result, corrosion resistance and oxidation resistance of thebond coat 3 are degraded. - The
diffusion barrier layer 1 prevents diffusion of any element between thesubstrate 5 and thebond coat 3, thereby suppresses a reduction in strength of thesubstrate 5, and helps to maintain the certain corrosion resistance and oxidation resistance of thebond coat 3. - The
diffusion barrier layer 1 is required to have a small diffusion coefficient. In general, metal has a diffusion coefficient that is in inverse proportion to the melting point of the metal. Hence, a metal having a high melting point is preferably selected for thediffusion barrier layer 1. For example, the metal is Ru or Re. Furthermore, thediffusion barrier layer 1 is required to be stable without being decomposed at high temperature for a long time, and is preferably an equilibrium phase in a phase diagram for a system of asubstrate 5 andbond coat 3. Examples of the equilibrium phase include the a phase as the intermetallic compound containing Re, Cr and Ni. - The
metal layer 2 is intended to prevent thediffusion barrier layer 1 from being broken by shock during the blast treatment. - Metals having higher toughness than the
diffusion barrier layer 1 are each selected as a compositional metal of themetal layer 2. For example, the metals of themetal layer 2 are Ni, Cr, Co, Fe, Pt, Pd and Ir. Each of such metals absorbs the shock during the blast treatment through deformation of the metal itself. In particular, Ni or Co is preferred. Consequently, fracture of the brittlediffusion barrier layer 1 can be prevented, and thus thediffusion barrier layer 1 can maintain its function. - Although the
metal layer 2 gradually reacts with thebond coat 3 at high temperature, the reaction does not significantly vary the composition of thebond coat 3 since Ni, Cr, Co and Fe are originally contained in thebond coat 3. Hence, the corrosion resistance and the oxidation resistance of thebond coat 3 are not adversely affected thereby. Pt, Pd and Ir are known as elements that improve corrosion resistance and oxidation resistance of any of alloys such as MCrAlY being widely used for thebond coat 3. - A method of manufacturing the heat-resistant alloy member of the invention is now described.
-
FIG. 3 is a flowchart showing the method of manufacturing the heat-resistant alloy member including the diffusion barrier layer as an Example. - The surface of the
substrate 5 is subjected to pretreatment to improve adhesion of thediffusion barrier layer 1 to be provided on the surface of thesubstrate 5. That is, the pretreatment is removal of surface oxides and degreasing. Although the method is not limited, the surface oxides may be removed typically by blast treatment, polishing with waterproof abrasive paper, or pickling with hydrochloric acid or other acids. The degreasing is usually performed using an organic solvent such as acetone, benzene or alcohol. - After the pretreatment, the
diffusion barrier layer 1 is deposited on the surface of the substrate 5 (S1). Although thediffusion barrier layer 1 may be deposited by any of various processes without limitation, thediffusion barrier layer 1 is readily deposited by a combined process of plating and heat treatment. The process is industrially advantageous. - The plating allows thickness control on the order of micrometers. In addition, the plating readily meets a member having a complicated shape since it is a process using a liquid. Such advantages are preferred for deposition operation on the member having a complicated shape such as a turbine blade.
- A layer deposited by the thermal spray has a thickness of at least several tens of micrometers. In other words, the thermal spray has a limit in control of the thickness. On the other hand, electron beam physical vapor deposition (EB-PVD) requires a sophisticated vacuum apparatus. In EB-PVD, the vacuum apparatus must be evacuated after the member is placed therein, and a long time is required for such evacuation. As a result, EB-PVD is low in operation efficiency compared with the plating requiring no special apparatus.
- For example, in the case where the intermetallic compound containing Re, Cr and Ni is deposited as the
diffusion barrier layer 1 by plating, a Re—Cr—Ni layer is plated in an appropriate thickness on the surface of thesubstrate 5, and then the plated Re—Cr—Ni layer is subjected to heat treatment to improve adhesion between the relevant layers. The heat treatment releases stress that has occurred within each layer during plating. In addition, the layers are bonded at an interface therebetween through diffusion, leading to improvement in adhesion. - Although the heat treatment is usually performed in a vacuum or an atmosphere of an inert gas such as argon or nitrogen, the heat treatment is not limited thereto, and also includes heat treatment industrially referred to as a diffusion coating.
- The diffusion coating is also called “cementation” which is a general term of various types of heat treatment that allows another metal or nonmetal element to diffuse into a surface of a member, and is performed while the member is placed in a liquid or gas, or the member is buried in a solid such as metal or alloy powder. Aluminizing or chromizing is industrially widely practiced, which allows diffusion of Al or Cr, respectively, into the surface.
- If the diffusion coating is performed as post-plating heat treatment, the composition of the
diffusion barrier layer 1 can be appropriately adjusted. Thediffusion barrier layer 1 containing Re, Cr and Ni may be formed through the chromizing after deposition of a Re—Ni layer by the plating. - After the deposition of the
diffusion barrier layer 1, themetal layer 2 is deposited on the surface of the diffusion barrier layer 1 (S2). Themetal layer 2 is preferably deposited by the plating due to the above-described reason, though not limited. Themetal layer 2 has a thickness of 5 to 30 μm. - If the
metal layer 2 has the thickness of less than 5 μm, thediffusion barrier layer 1 may be insufficiently protected from the shock by the blast. If the thickness is more than 30 μm, the bond coat may greatly vary in composition during a reaction with themetal layer 2, leading to degradation in corrosion resistance, oxidation resistance etc. of the bond coat. - After the
metal layer 2 is deposited, the heat-resistant alloy member may be manufactured by the same steps as those in the method of manufacturing the conventional heat-resistant alloy member shown inFIG. 1 . That is, the blast treatment (S3) and the thermal spray of thebond coat 3 and the top coat 4 (S4) are performed in order under conditions being industrially generally used, so that the heat-resistant alloy member including thediffusion barrier layer 1 is manufactured (S5). - Examples are now described.
- In the gas turbine member, a single-crystal heat-resistant alloy having a composition of Ni—7Cr—1Co—0.8Mo—8.8W—1.4Re—0.8Nb—8.9Ta—5.1Al—0.25Hf—0.07C—0.02B was casted into a rod, and the rod was mechanically processed into a diameter of one inch and a thickness of 3 mm, so that the
substrate 5 was prepared. The composition of the alloy was within a particularly preferable composition range of the invention. - The surface of the
substrate 5 was polished with #600 SiC waterproof abrasive paper, and then thesubstrate 5 was ultrasonically cleaned in acetone for degreasing. Thediffusion barrier layer 1 was then deposited by an electroplating. - In this Example, electrolytic Ni plating was performed to precipitate a Ni layer on the surface of the
substrate 5, and then the Ni layer was washed with distilled water, and then electrolytic Re plating was successively performed to precipitate a Re layer. Then, electrolytic Ni plating layers and electrolytic Re plating layers were alternately stacked in this order, and eventually three Ni/Re layers in total were formed. Each of the deposited Ni/Re layers had a thickness of about 2 μm. - Then, the Ni/Re layer was subjected to chromizing as heat treatment. The plated
substrate 5 was buried in a mixed powder of Cr and alumina while being placed in an alumina crucible. - The ratio of Cr to alumina in the mixed powder was ⅓ in mass ratio. The heat treatment, however, may be performed using a mixed powder having any other mixing ratio. The alumina crucible was placed in a vacuum heater, and the atmospheric gas was then exhausted to 10−3 Pa, and then heating was started.
- After the chromizing, the test piece was washed and degreased again, and then electrolytic Ni was deposited by 30 μm as the
metal layer 2 by the plating. Then, the electrolytic Ni was subjected to the blast treatment using alumina particles having a particle size of 24 as the pretreatment before the thermal spray. - Commercially available thermal spray powder of CoNiCrAlY having a composition of Co—32Ni-21Cr—8Al—0.5Y was thermally sprayed by about 150 μm as the
bond coat 3 by high velocity oxy-fuel frame-spraying (HVOF). - Commercially available yttria stabilized zirconia (YSZ) was also deposited by about 300 μm as the
top coat 4 by air plasma spray (APS). -
FIG. 4 shows a cross-sectional scanning microscopic photograph of a region near thediffusion barrier layer 1 and themetal layer 2 in the above-described Example. - In this drawing, the
diffusion barrier layer 1, themetal layer 2, and thebond coat 3 are disposed in this order on the surface of thesubstrate 5. - It is observed that the Ni layer as the
metal layer 2 is deformed by the blast treatment, resulting in formation of surface irregularity preferable for adhesion to thebond coat 3. On the other hand, defects such as deformation and cracks are not observed in thediffusion barrier layer 1, which reveals that themetal layer 2 absorbs the shock by the blast. Themetal layer 2 effectively protects thediffusion barrier layer 1. - A test piece was produced as a comparative example in the following manner:
- The
diffusion barrier layer 1 was deposited on the surface of thesubstrate 5 by the same process as above, and thediffusion barrier layer 1 was then subjected to the blast treatment without providing themetal layer 2, and thebond coat 3 and thetop coat 4 were then formed in order thereon by the thermal spray. -
FIG. 5 shows a scanning microscopic photograph of a heat-resistant alloy member of the above-described comparative example. This test piece has a surface coated withresin 11 for observation. - As shown in this drawing, it was observed in the cross-section observation was performed after the blast treatment that the
diffusion barrier layer 1 had incomplete portions over a wide area and a large number of cracks. This reveals that one of the three layers stacked as thediffusion barrier layer 1 was completely lost by the blast . Thediffusion barrier layer 1 was damaged to lose its functions by the blast treatment. - To confirm the effects of the invention, each test piece was subjected to a high-temperature exposure test at 1100° C. for evaluation.
- A test piece having a structure without the
diffusion barrier layer 1 and themetal layer 2 as shown inFIG. 1 was produced in addition to the test pieces as shown inFIGS. 4 and 5 . The blast treatment and the deposition of each of thebond coat 3 and thetop coat 4 were performed under the same conditions as those in the Example shown inFIG. 4 . -
FIG. 6 shows a scanning microscopic photograph of a cross section of the test piece of the Example shown inFIG. 4 after the exposure at 1100° C. for 600 hr. As seen in this drawing, thesubstrate 5 in the Example does not have the secondary reaction zone (SRZ) that may degrade mechanical properties of thesubstrate 5, revealing that thediffusion barrier layer 1 effectively suppresses diffusion of any element between thesubstrate 5 and thebond coat 3. - In contrast, in the case of the test piece having the conventional structure without the
diffusion barrier layer 1 as shown inFIG. 7 , the surface layer of thesubstrate 5 noticeably had SRZ, in which an acicular topologically close-packed (TCP) phase was precipitated due to counter diffusion of some element between thesubstrate 5 and thebond coat 3, after the exposure at 1100° C. for 600 hr, thus inevitably leading to a reduction in strength of thesubstrate 5. - As described above, the heat-resistant alloy member of the Example as shown in
FIG. 2 has thediffusion barrier layer 1 that effectively operates to suppress the counter diffusion, which resultantly prevents the formation of the SRZ. Consequently, the heat-resistant alloy member of the Example can meet the increased combustion temperature. - The same coating as that in the Example 1 was formed on a surface of a first
stage turbine blade 23 formed of a single-crystal heat-resistant alloy having the same composition as that of the Example 1, the surface being to be exposed to combustion gas, so that a turbine blade for industrial gas turbine was produced. -
FIG. 8 shows an outline of an industrial gas turbine including the turbine blade for industrial gas turbine of the Example 1. - In this drawing, the gas turbine includes a
compressor 11, acombustor 12, a turbine unit 13 (including a turbine blade and a turbine nozzle), and anexhaust outlet 14. -
FIG. 9 shows a portion A inFIG. 8 in an enlarged manner, which is a cross-sectional diagram showing a detail of theturbine unit 13 including the turbine blade and the turbine nozzle. - In this drawing, the turbine unit includes a
first stage shroud 21, a second stage shroud 22, a first-stage turbine blade 23, a second-stage turbine blade 24, adisc 25, a first-stage turbine nozzle 26, a second-stage turbine nozzle 27, and acombustor transition piece 28. - The industrial gas turbine of this Example had the single-crystal coating blade having excellent heat resistance, thereby enabling an increase in combustion gas temperature, and consequently a gas turbine at a level of generation efficiency of 40% was achieved.
- Although the present invention has been described with the specific Examples hereinbefore, the invention is not limited thereto, and various modifications or alterations thereof may be made within the scope without departing from the gist thereof.
Claims (4)