US20130308888A1 - Outer ring for rocking bearing, retainer for rocking bearing, rocking bearing, and air disk brake system - Google Patents
Outer ring for rocking bearing, retainer for rocking bearing, rocking bearing, and air disk brake system Download PDFInfo
- Publication number
- US20130308888A1 US20130308888A1 US13/673,048 US201213673048A US2013308888A1 US 20130308888 A1 US20130308888 A1 US 20130308888A1 US 201213673048 A US201213673048 A US 201213673048A US 2013308888 A1 US2013308888 A1 US 2013308888A1
- Authority
- US
- United States
- Prior art keywords
- retainer
- rocking bearing
- outer ring
- parts
- rollers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An outer ring for rocking bearing (11 a) includes a raceway surface (12 a) on the inner diameter side and has flange parts (13 a) and (13 b) provided by bending axial both ends to the inner diameter side. The flange parts (13 a) and (13 b) are provided with bent parts (17 a) and (17 b) axially bent toward the raceway surface (12 a) side so as to enfold a retainer arranged on the inner diameter side. Thus, the retainer can be enfolded by the bent parts (17 a) and (17 b). Therefore, even when the retainer comes to be moved to the inner diameter side of the outer ring for rocking bearing (11 a), the retainer is caught by the bent parts (17 a) and (17 b), so that the movement of the retainer to the inner diameter side is restricted and rollers and the retainer can be prevented from dropping off.
Description
- The present invention relate to an outer ring for a rocking bearing, a retainer for a rocking bearing, a rocking bearing, and an air disk brake system.
- An air disk brake system using compressed air is employed in a large-sized commercial motor vehicle such as a track and a bus. Here, a brief description will be made of a constitution of a general air disk brake system.
FIG. 40 is a schematic sectional view showing the constitution of the general air disk brake system. Referring toFIG. 40 , an airdisk brake system 101 includes a brake cylinder (not shown) having anactuator rod 102, alever 103 connected to one end of theactuator rod 102, arotation member 104 connected to the other end of thelever 103, a rocking bearing 105 rotatably supporting therotation member 104, aconnection part 107 provided at an eccentric position with respect to therotation member 104, atraverse 106 having one end connected to theconnection part 107, right and left brake pads (not shown) working with thetraverse 106, and a rotor (not shown) arranged between the right and left brake pads. According to the airdisk brake system 101, the rotor is sandwiched by the right and left brake pads by use of the compressed air supplied from the brake cylinder through thelever 103 and the like. - In addition, such air disk brake system is disclosed in Japanese National Publication PCT application No. 8-504250 and WO2006/002905A1.
- A brief description will be made of a constitution of the rocking bearing in the above air disk brake system. The rocking bearing has an outer ring for the rocking bearing, a plurality of rollers, and a retainer to retain the rollers. The outer ring for the rocking bearing is not in the form of a ring, and it is provided by splitting a cylindrical member at two circumferential points. The retainer also has a configuration provided by splitting a cylindrical member at two circumferential points and following the outline of the outer ring for the rocking bearing. When the rocking bearing having the above constitution is assembled, the rollers are incorporated in pockets of the retainer first, and the retainer having the rollers is arranged on the inner diameter side of the outer ring for the rocking bearing.
- Here, after the rocking bearing has been assembled, the movement of the retainer toward the inner diameter side is not restricted. Thus, when the assembled rocking bearing is mounted on the air disk brake system having the above constitution, the retainer could be moved toward the inner diameter side and drop out of the outer ring for the rocking bearing.
- It is an object of the present invention to provide an outer ring for a rocking bearing in which rollers and a retainer are prevented from dropping off.
- It is another object of the present invention to provide a rocking bearing having high assembling properties.
- It is still another object of the present invention to provide an air disk brake system having high productivity.
- An outer ring for a rocking bearing according to the present invention includes a raceway surface on the inner diameter side and has a flange part provided by bending axial each end to the inner diameter side. Here, at least one the flange part is provided with a bent part axially bent toward the raceway surface side so as to enfold a retainer arranged on the inner diameter side.
- In this constitution, at the time of assembling of the rocking bearing assembling, when the retainer having the rollers is arranged on the inner diameter surface of the outer ring for the rocking bearing, the retainer can be enfolded by the bent part. Thus, even when the retainer comes to be moved toward the inner diameter side of the outer ring for the rocking bearing, the retainer is caught by the bent part, so that the movement of the retainer toward the inner diameter side can be restricted. Thus, the rollers and retainer can be prevented from dropping out of the outer ring for the rocking bearing.
- Preferably, the bent part is provided so as to be continued in a circumferential direction of the flange part. Thus, since the retainer can be enfolded over the wide range in the circumferential direction, the retainer and the roller can be prevented from dropping off more surely.
- Further preferably, the bent part is provided along each flange part. Thus, the retainer can be held by the bent part provided on each flange part. Thus, the rollers and retainer can be prevented from dropping out of the outer ring for the rocking bearing more surely.
- Further preferably, a material containing 0.15 to 1.1% by weight of carbon is subjected to a carbonitriding treatment to produce the outer ring for the rocking bearing. Thus, high-strength outer ring for the rocking bearing can be produced at low cost. Since the outer ring for the rocking bearing has high load capacity, it is hardly damaged. In addition, since the strength of the bent part is also high, the retainer and the rollers can be prevented from dropping off more surely.
- In addition, the material of the outer ring for the rocking bearing may contain 0.5 to 1.1% by weight of carbon. According to the above constitution, processability is improved, and its outline configuration can be formed with high accuracy by a pressing process. In addition, even when the carbonitriding treatment is not performed, hardness required for the outer ring for the rocking bearing can be provided. Thus, the outer ring for the rocking bearing can be prevented from being deformed at the time of heat treatment. Therefore, the outer ring for the rocking bearing is high in accuracy, low in cost, and high in load capacity.
- Further preferably, the outer ring for the rocking bearing containing 0.5 to 1.1% by weight of carbon is subject to a bright quenching treatment. In addition, the outer ring for the rocking bearing containing 0.5 to 1.1% by weight of carbon may be subject to a high-frequency quenching treatment. The above heat treatments can be performed at low cost.
- According to another aspect of the present invention, a rocking bearing includes a plurality of rollers arranged on the raceway surface, a retainer containing pockets to hold the rollers and a pair of connection parts positioned on axial each end of the pockets and continued in a circumferential direction, and any one of the outer rings for the rocking bearing described above.
- According to the rocking bearing, the rollers and the retainer are prevented from dropping out of the outer ring for the rocking bearing. In addition, at the time of assembling, since the retainer and the outer ring for the rocking bearing are prevented from being separated or shifted, a mounting defect can be also prevented. Therefore, the assembling properties can be improved.
- Preferably, an engagement part engaging with the bent part is provided at the connection part. Thus, when the bent part engages with the engagement part, the retainer and the roller can be more surely prevented from dropping off, and the assembling properties an be further improved.
- Further preferably, the outer ring for the rocking bearing and/or the roller have a nitride enrichment layer, and an austenite grain size number exceeding 10, and contains 11% to 25% by volume of retained austenite, and 0.1% to 0.7% by weight of nitrogen.
- When the roller bearing such as the rocking bearing is reduced in size, the problem is that an applied load per unit area is increased and the life is shortened. Therefore, it is inevitable that the life is shortened when the roller bearing is reduced in size.
- Here, when the austenite grain of the above bearing member is miniaturized such that its grain size number exceeds 10, the rolling fatigue life can be considerably elongated. When the austenite grain size number is not more than 10, since the rolling fatigue life is not sufficiently elongated, the number should be more than 10. In general, it is to be not less than 11. In addition, an average grain size may be not more than 6 μm. A finer austenite grain size is better, but it is difficult get the grain size number exceeding 13 in general. The above austenite grain size may be found by a normal method defined in JIS or may be calculated by finding an average grain size corresponding to the grain size number by a section method.
- In addition, the austenite grain is not changed even in a surface layer having a nitrogen enrichment layer, and in the inner side thereof. Therefore, the grain size number is to be within the above range at the surface layer and its inner side. Here, the austenite grain is the phase-transformed austenite grain during the quenching treatment, which means that it remains as a past history even after transformed to martensite.
- In addition, when the retained austenite is less than 11% by volume, the surface damage life is considerably lowered, and when the retained austenite is more than 25% by volume, an aging length change deteriorates because there is no difference from the retained austenite volume when the normal carbonitriding treatment is performed.
- The retained austenite volume is a value at a surface layer of 50 μm from a rolling surface after ground, and can be measured by comparing the diffraction intensity of martensite α (211) with that of retained austenite γ (220). As another example, it can be measured by finding magnetization force by a magnetic scale, using the fact that an austenite phase is a nonmagnetic body and a ferrite phase is a ferromagnetic body. Or, it can be easily measured by use of a commercially available measurement device.
- The nitrogen enrichment layer is a layer in which a nitrogen content is increased, and formed in a surface layer by the carbonitriding treatment or the nitriding treatment. When the nitrogen content of the nitrogen enrichment layer is less than 0.1% by weight, there is no effect, and the surface damage life is shortened especially. Meanwhile, the nitrogen content is more than 0.7% by weight, a void is generated and hardness is not provided because of too many retained austenite, whereby the life is shortened. The nitrogen content of the nitrogen enrichment layer is a value at 50 μm of the surface layer from the rolling surface after ground, and it can be measured by EPMA (Electron Probe Micro-Analysis wavelength-dispersive X-ray microanalyzer).
- As described above, according to this constitution, the rocking bearing containing the above outer ring for the rocking bearing and the rollers can have a long life.
- Further preferably, a snap fitting allowable configuration part to allow snap fitting is provided in the retainer and/or the bent part so that the retainer is retained by the bent part after passing through the bent part.
- According to this constitution, when the retainer is held by the bent part of the outer ring for the rocking bearing through the bent part, the retainer is snap-fit in the outer ring for the rocking bearing by the snap fitting allowable configuration provided at the retainer and/or the bent part, and the retainer can be held by the bent part of the outer ring for the rocking bearing. Since the bent part holds the retainer so as to enfold it, the retainer can be prevented from being separated from the outer ring for the rocking bearing. In addition, since the snap fitting allowable configuration part uses elastic deformation of the retainer and the outer ring for the rocking bearing, when the retainer is assembled in the outer ring for the rocking bearing, it can be easily fit in without needing strong force. In addition, at the time of assembling, the retainer and the outer ring for the rocking bearing can be prevented from being damaged. Therefore, the assembling properties of the rocking bearing are improved.
- Further preferably, the snap fitting allowable configuration includes a fitting click axially projecting from the end face of the connection part. Thus, the snap fitting can be implemented by use of the fitting click projecting in the axial direction.
- Further preferably, a corner part of the fitting click is chamfered on the outer diameter side. Thus, the snap fitting can be implemented by use of the chamfered part of the fitting click. Thus, the snap fitting can be implemented smoothly. Therefore, the assembling properties can be further improved.
- Further preferably, a corner part of the bent part is chamfered on the inner diameter side. Thus, the snap fitting is implemented by use of the chamfered part of the bent part. Thus, the snap fitting can be implemented smoothly. Therefore, the assembling properties can be further improved.
- Further preferably, the fitting click is provided at a circumferential position provided with the pocket. The circumferential position of the pocket is not connected in the axial direction. Thus, the retainer can be easily elastically deformed in the axial direction at the circumferential position of the fitting click. Therefore, the assembling properties can be further improved.
- Further preferably, the fitting click is provided at each connection part, and the circumferential position of the fitting click provided at one connection part is different from the circumferential position of the fitting click provided at the other connection part. Thus, the circumferential positions of the elastic deformation can be differentiated between the fitting click provided at the one connection part and the fitting click provided at the other connection part. Therefore, the retainer can be easily elastically deformed in the axial direction, so that the assembling properties are further improved.
- Further preferably, the snap fitting allowable configuration is provided at the connection part, and contains a slit recessed in a radial direction. Thus, the snap fitting can be implemented by use of the slit recessed in the radial direction.
- Further preferably, the outer ring for the rocking bearing satisfies a relation 0.2W2<W1<0.8W2 wherein W1 represents an axial length of the slit, and W2 represents an axial length of the connection part, and a relation 0.2H2<H1<0.8H2 wherein H1 represents an radial length of the slit, and H2 represent an radial length of the connection part. Thus, the elastic deformation can be appropriately implemented at the time of snap fitting. That is, when the length dimensional relation of the slit is within the above range, the retainer can be elastically deformed by appropriate force and the snap fitting can be implemented without damaging the retainer.
- Further preferably, a projection part is provided at a predetermined position of an axial end face of the connection part, and a click part is provided at the outer ring for the rocking bearing to limit the movement amount of the retainer by abutting on the projection part after the retainer is moved a predetermined amount in a circumferential direction with respect to the outer ring for the rocking bearing.
- According to the above constitution, even when the retainer is moved in the circumferential direction, the projection part provided at the predetermined position of the connection part abuts on the click part provided at the outer ring for the rocking bearing. Then, the retainer cannot be moved in the circumferential direction any more. Thus, the circumferential movement of the retainer can be restricted. In addition, according to the rocking bearing having the above constitution, when the projection part is provided at the optional position, the circumferential movement amount of the retainer can be optionally determined. Thus, the retainer can be moved beyond the circumferential end of the outer ring for the rocking bearing. In addition, it is not necessary provide a new member. Therefore, the range of movement of the retainer can be increased in the inexpensive constitution. In addition, according to the rocking bearing, since the retainer is prevented from dropping off, the assembling properties can be improved.
- Further preferably, the predetermined position of the projection part is on the circumferential inner side of the pocket arranged circumferential outermost side, and the movement of the retainer is limited after a part of the retainer projects from the circumferential one end side of the outer ring for the rocking bearing. Thus, even when the predetermined position of the projection part is on the circumferential inner side than the pocket arranged on the circumferential outermost side, the circumferential movement of the retainer is limited and restricted under the condition that the circumferential end of the retainer projects from the one end of the outer ring for the rocking bearing. Therefore, the movement range of the retainer can be further increased.
- Further preferably, a circumferential length of the retainer projecting from the outer ring for the rocking bearing is not more than a circumferential length from the one end side of the retainer to the pocket arranged on the circumferential outermost side of the one end side thereof. Thus, the roller housed in the pocket arranged on the outermost side can be prevented from dropping off. Therefore, the assembling properties of the rocking bearing can be further improved.
- Further preferably, the click part and the projection part are provided axial each end. Thus, since the projection part engages with the click part on axial each side, the assembling properties can be further improved.
- In addition, a rocking bearing includes any one of the outer rings for the rocking bearing described above, a plurality of rollers arranged on the raceway surface, a retainer for the rocking bearing having a pair of connection parts extending in a circumferential direction, and a plurality of column parts connecting the pair of connection parts to each other to form a plurality of pockets to hold the rollers between the adjacent column parts, and the radial outermost part of the column part is arranged apart from a pitch circle formed by connecting rotation centers of the rollers.
- According to the retainer for the rocking bearing, the distance between the adjacent rollers is smallest on a pitch circle. Therefore, when the column part is provided apart from the pitch circle, the distance between the adjacent rollers can be small. As a result, the number of the rollers can be increased in the retainer for the rocking bearing, so that the rocking bearing is high in load capacity.
- Preferably, the rocking bearing satisfies a relation B2<0.98<B4 wherein B2 represent an outer diameter of the column part, and B4 represents a diameter of the pitch circle. Thus, when the column part is arranged on the inner side of the pitch circle, the roller in the pocket can be prevented from dropping off toward the radial inner side. In addition, the roller can be prevented from dropping off toward the radial outer side by the outer rings for the rocking bearing in general.
- Further preferably, the rocking bearing satisfies:
-
- wherein n represents the number of rollers housed in the pockets, l represents a length of the pitch circle overlapping with the roller, and L represents a circumferential length of the pitch circle between the rotation centers of the rollers housed in the pockets positioned at circumferential both ends.
- The formula 1 designates an occupancy of the roller on a circumference of the pitch circle. Referring to the formula 1, when the occupancy of the roller is not more than 0.9, the distance between the adjacent rollers is too long and sufficient load capacity cannot be provided. Meanwhile, when the distance between the adjacent rollers is small, the rollers could be in contact with each other at the time of rocking. This causes oil film cutting and heat generation on the roller surface. Thus, the occupancy needs to be less than 1.0.
- Further preferably, the retainer for the rocking bearing is formed of a material containing polyamide 46, and 5% to 20% by weight of a fiber filler material. The resin retainer produced of a resin material by projection part molding has high degree of freedom in configuration. In addition, when the fiber filler material such as carbon fiber and glass fiber is contained, the strength required for the retainer can be provided.
- In addition, when the content of the fiber filler material is less than 5% by weight, it is hard to get strength required for the retainer for the rocking bearing. Meanwhile, when it is more than 20% by weight, fluidity of the resin material at the time of molding deteriorates. This could cause a problem such as gas burning and lack of filling in producing the retainer having many pockets and thin column parts. Furthermore, when a filling pressure is increased to solve the problem, a burr could be generated. Therefore, the content of the fiver filler material is to be within the above range.
- A retainer for a rocking bearing according to the present invention includes a pair of connection parts extending in a circumferential direction, and a plurality of column parts connecting the pair of connection parts to each other to form a plurality of pockets to hold rollers between the adjacent column parts. The radial outermost part of the column part is arranged apart from a pitch circle formed by connecting rotation centers of the rollers.
- A rocking bearing includes any one of the outer rings for the rocking bearing described above, a plurality of rollers arranged on the raceway surface, and a retainer for the rocking bearing having a pair of connection parts extending in a circumferential direction and a plurality of column parts connecting the pair of connection parts to form a plurality of pockets to hold the rollers between the adjacent column parts, and satisfying a relation {θ/(n−1)}°<a0<90° wherein n represents the number of rollers housed in the pockets, a0 represent an angle formed between opposed wall surfaces of the adjacent column parts, and θ represents a center angle formed between rotation centers of the rollers housed in the pockets positioned at circumferential both ends.
- When the angle a0 formed between the opposed wall surfaces of the adjacent column parts is decreased in the retainer for the rocking bearing, the number of pockets formed at the same time in one die is reduced. Therefore, the larger angle a0 is desirable in view of molding improvement, and a lower limit value of the angle a0 is set to {θ/(n−1)}°
- Meanwhile, when the angle a0 is increased, the roller could not be appropriately held by the pocket. More specifically, when a0≧90°, component force F1 acting in a parallel direction to the wall surface and component force F2 acting in a vertical direction to the wall surface of the force pressing the wall surface of the column part by the roller have a relation: F1≧F2. In this case, the roller could be brought on the column part and in contact with the adjacent roller. This causes the oil film cutting and heat generation on the roller surface. Therefore, the smaller angle a0 is desirable in view of appropriate roller retention, so that the upper limit value of the angle a0 is set to 90°.
- Thus, the rocking bearing can be high in productivity and load capacity.
- A retainer for a rocking bearing according to the present invention includes a pair of connection parts extending in a circumferential direction, and a plurality of column parts connecting the pair of connection parts to each other to form a plurality of pockets to hold the rollers between the adjacent column parts, and satisfies a relation {θ/(n−1)}°<a0<90° wherein n represents the number of rollers housed in the pockets, ao represents an angle formed between opposed wall surfaces of the adjacent column parts, and θ represents a center angle formed between rotation centers of the rollers housed in the pockets positioned at circumferential both ends.
- A rocking bearing includes an outer ring for the rocking bearing containing a raceway surface on the inner diameter side and having a flange part provided by bending axial each end to the inner diameter side, a plurality of rollers arranged on the raceway surface and any one of the retainers for the rocking bearing described above.
- According to a still another aspect of the present invention, an air disk brake system includes any one of the rocking bearing described above.
- Since the above air disk brake system contains the rocking bearing having preferable assembling properties, its productivity can be improved.
-
FIG. 1 is a perspective view showing an outer ring for a rocking bearing according to one embodiment of the present invention; -
FIG. 2 is a perspective view showing a retainer contained in a rocking bearing according to one embodiment of the present invention; -
FIG. 3 is a perspective view showing the retainer having rollers in pockets on the lower side; -
FIG. 4 is a perspective view showing the retainer having the rollers in the pockets on the upper side; -
FIG. 5 is a perspective view showing a rocking bearing according to one embodiment of the present invention; -
FIG. 6 is a sectional view showing the rocking bearing shown inFIG. 5 when cut by a plane containing an engagement part; -
FIG. 7 is a sectional view showing the rocking bearing shown inFIG. 5 viewed in an axial direction; -
FIG. 8 is an enlarged view showing a part VIII inFIG. 7 ; -
FIG. 9 is a further enlarged view ofFIG. 8 ; -
FIG. 10 is a view showing a retainer for the rocking bearing according to another embodiment of the present invention; -
FIG. 11 is a sectional view showing a rocking bearing including an outer ring for the rocking bearing according to another embodiment of the present invention when cut by a plane containing an engagement part; -
FIG. 12 is a sectional view showing a rocking bearing including an outer ring for the rocking bearing according to still another embodiment of the present invention when cut by a plane containing an engagement part; -
FIG. 13 is a sectional view showing a state before a roller and a retainer are assembled in an outer ring for the rocking bearing; -
FIG. 14 is a sectional view showing a state after the roller and the retainer have been assembled in the outer ring for the rocking bearing; -
FIG. 15 is an enlarged view showing a part of a rocking bearing according to still another embodiment of the present invention; -
FIG. 16 is a view showing a retainer provided in a rocking bearing according to still another embodiment of the present invention; -
FIG. 17 is a sectional view showing a rocking bearing according to still another embodiment of the present invention; -
FIG. 18 is a sectional view showing a rocking bearing according to still another embodiment of the present invention; -
FIG. 19 is an enlarged view showing a part of the rocking bearing shown inFIG. 17 ; -
FIG. 20 is an enlarged view showing a part of a rocking bearing according to still another embodiment of the present invention; -
FIG. 21 is an enlarged view showing a part of a rocking bearing according to still another embodiment of the present invention; -
FIG. 22 is an enlarged view showing a part of a rocking bearing according to still another embodiment of the present invention; -
FIG. 23 is a view showing a rocking bearing according to still another embodiment of the present invention taken in an axial direction when a click part does not abut on a projection part; -
FIG. 24 is a view showing the rocking bearing according to still another embodiment of the present invention taken in the axial direction when the click part abuts on the projection part; -
FIG. 25 is a perspective view showing an outer ring for the rocking bearing provided in a rocking bearing according to still another embodiment of the present invention; -
FIG. 26 is a view showing the rocking bearing containing the outer ring for the rocking bearing shown inFIG. 25 taken in the axial direction when a click part does not abut on a projection part; -
FIG. 27 is a view showing the rocking bearing containing the outer ring for the rocking bearing shown inFIG. 25 taken in the axial direction when the click part abuts on the projection part; -
FIG. 28 is a flowchart showing representative production steps of the outer ring for the rocking bearing; -
FIG. 29 is a view explaining a two-stage heat treatment method; -
FIG. 30 is a view explaining a variation of the two-stage heat treatment method; -
FIG. 31 is a view showing microstructure, austenite grains especially in a bearing component subjected to a heat treatment pattern shown inFIG. 29 ; -
FIG. 32 is a view showing microstructure, austenite grains especially in a conventional bearing component; -
FIG. 33 is a schematic diagram of the microstructure shown inFIG. 31 in which an illustrated austenite grain boundary is shown; -
FIG. 34 is a schematic diagram of the microstructure shown inFIG. 32 in which an illustrated austenite grain boundary is shown; -
FIG. 35 is a sectional view showing structures (dimensions) of samples 1 to 6; -
FIG. 36 is a sectional view showing structures (dimensions) of samples 7 to 11; -
FIG. 37 is a front view showing an essential part of a peeling life test machine; -
FIG. 38 is a sectional view taken along line XXXVIII-XXXVIII inFIG. 37 ; -
FIG. 39 is a schematic sectional view showing a part of an air disk brake system according to one embodiment of the present invention; and -
FIG. 40 is a schematic sectional view showing a part of a conventional air disk brake system. - Embodiments of the present invention will be described with reference to the drawings hereinafter.
FIG. 1 is a perspective view showing an outer ring a the rocking bearing (referred to as the “outer ring” hereinafter) according to one embodiment of the present invention. A constitution of anouter ring 11 a will be described with reference toFIG. 1 . Theouter ring 11 a has a configuration provided by splitting a cylindrical member at two circumferential certain points. A raceway surface 12 on which rollers roll is provided on the inner diameter side of theouter ring 11 a. -
Projection parts outer ring 11 a. Although a retainer arranged on the inner diameter side of theouter ring 11 a can be moved in a circumferential direction, its circumferential movement is restricted at the one end by theprojection parts - In addition, a tongue-shaped
protrusion part 15 a bent toward the outer diameter side is provided between theprojection parts protrusion part 16 a is also provided at the circumferential other end of theouter ring 11 a. By use of theprotrusion parts outer ring 11 a is mounted on a housing (not shown) and fixed so that the circumferential movement of theouter ring 11 a is restricted. - The
outer ring 11 a hasflange parts flange parts outer ring 11 a. - Here, the
flange parts parts raceway surface 12 a in the axial direction so as to hold the retainer arranged on the inner diameter side, respectively. Thebent parts - Next, a description will be made of a constitution of the retainer provided in the rocking bearing according to one embodiment of the present invention and arranged on the inner diameter side of the
outer ring 11 a.FIG. 2 is a perspective view showing the retainer to be arranged on the inner diameter side of theouter ring 11 a.FIGS. 3 and 4 are perspective views showing states in whichrollers 20 a are housed inpockets 22 a of aretainer 21 a shown inFIG. 2 .FIG. 3 shows a state in which therollers 20 a are provided on the lower side, andFIG. 4 shows a state in which therollers 20 a are provided on the upper side. Referring toFIGS. 1 to 4 , theretainer 21 a has a configuration provided by splitting a cylindrical member at two circumferential certain points similar to the above-describedouter ring 11 a and follows the configuration of theouter ring 11 a. - The
retainer 21 a includespockets 22 a to hold therollers 20 a, and a pair ofconnection parts pockets 22 a and continued in the circumferential direction, that is, extending in the circumferential direction. Eachpocket 22 a holds the oneroller 20 a. A distance between thepocket 22 a positioned on the outermost side in the circumferential direction and each of circumferential ends 25 a and 25 b of theretainer 21 a is set so as to be larger than a distance between thepockets 22 a. In addition, a rotation member (not shown) contained in an air disk brake system is arranged on the inner diameter side of theretainer 21 a. - The pair of
connection parts column parts 24 a positioned between thepockets 22 a and extending in the axial direction. Thecolumn part 24 a is provided on the inner diameter side rather than a PCD (Pitch Circle Diameter) of theroller 20 a held in thepocket 22 a. Thus, the number of therollers 20 a that can be held by theretainer 21 a can be increased. In this case, load capacity of the rocking bearing containingsuch retainer 21 a can be increased. In addition, after the rocking bearing has been assembled, theraceway surface 12 a and thecolumn part 24 a hold theroller 20 a so as to sandwich it, to restrict the radial movement of theroller 20 a. - The pair of
connection parts engagement parts 26 a to engage with thebent parts engagement parts 26 a project from theconnection parts engagement part 26 a is not continued along theconnection parts engagement parts 26 a are provided at certain circumferential points of theconnection parts -
FIG. 5 is a perspective view showing a rocking bearing 30 a according to one embodiment of the present invention.FIG. 6 is a sectional view showing the rocking bearing 30 a shown inFIG. 5 cut by a plane containing the engagement part. A description will be made of a constitution of the rocking bearing 30 a according to one embodiment of the present invention with reference toFIGS. 1 to 6 . The rockingbearing 30 a includes theouter ring 11 a, the plurality ofrollers 20 a, and theretainer 21 a to retain therollers 20 a. The rockingbearing 30 a is assembled such that theretainer 21 a holding therollers 20 a is arranged on the inner diameter side of theouter ring 11 a. - Here, at the time of assembling, the
retainer 21 a is arranged on the inner diameter side of theouter ring 11 such that thebent parts engagement parts 26 a. In this constitution, theretainer 21 a can be held and enfolded by thebent parts engagement parts 26 a in theouter ring 11 a. Thus, even when theretainer 21 a comes to be moved toward the inner diameter side of theouter ring 11 a, that is, toward a direction shown by arrows A inFIGS. 5 and 6 , theengagement parts 26 a of theretainer 21 a are caught by thebent parts retainer 21 a toward the inner diameter side can be restricted. Therefore, therollers 20 a and theretainer 21 a can be prevented from dropping out of theouter ring 11 a. In this case, since theretainer 21 a is held in such a manner that thebent parts engagement parts 26 a, therollers 20 a and theretainer 21 a can be surely prevented from dropping out of theouter ring 11 a. In addition, therollers 20 a and theretainer 21 a are not separated and not shifted from each other. According to the rocking bearing 30 a, when it is mounted on the air disk brake system that will be described below, a mounting defect is hardly generated. In addition, at the time of assembling, therollers 20 a and the retainer 21 are assembled as shown inFIG. 4 , and then theouter ring 11 a is assembled from the upper side inFIG. 4 to be fit in. Thus, the assembling operation can be performed easily without dispersing therollers 20 a. - Furthermore, since the
bent parts bent parts engagement parts 26 a regardless of the circumferential positions of theengagement parts 26 a. Therefore, theretainer 21 a and therollers 20 a are more surely prevented from dropping off. Here, theengagement part 26 a may be continued in the circumferential direction. In this case, theretainer 21 a can be held by thebent parts retainer 21 a can be held more stably, and therollers 20 a and theretainer 21 a can be further prevented from dropping off. - In addition, the
bent parts retainer 21 a is held by thebent parts rollers 20 a and theretainer 21 a can be prevented from dropping off. - In addition, since the
bent parts flange parts retainer 21 a can be held so as to be enfolded by bothflange parts rollers 20 a and theretainer 21 a can be prevented from dropping off more surely. - Here, recently, the rocking bearing employed in the air disk brake system comes to be strongly required to be miniaturized and have high load capacity as the air disk brake system is reduced in size and increased in power. Thus, as a method for increasing the load capacity of the rocking bearing, a method for increasing a roller diameter or increasing the number of rollers is generally used. However, the increase in roller diameter is contrary to the demand for miniaturization of the rocking bearing.
- Meanwhile, when the retainer is produced with a resin material by injection molding, a pocket is formed by punching out a mold toward the radial outer side of the retainer. At this time, various efforts have been made to improve molding properties such that the plurality of adjacent pockets are formed at the same time with one mold. However, when the number of pockets to hold the rollers is increased, the molding properties are lowered because the number of molds is increased and the mold becomes large and its structure becomes complicated. In addition, when the number of pockets formed at the same time is increased forcedly to punch out the mold, the retainer could be damaged.
- Therefore, the
column part 24 a and the like preferably has the following relations when thecolumn part 24 a is provided.FIG. 7 is a sectional view when the rocking bearing 30 a is cut by a plane perpendicular to the axial direction.FIG. 8 is an enlarged view showing a part VIII inFIG. 7 .FIG. 9 is an enlarged view ofFIG. 8 . - Referring to
FIGS. 7 and 8 , arotation member 31 a is arranged on the inner diameter side of the rocking bearing 30 a. Here, it is preferable to have relations B3≦B1 and B2<0.98×B4 wherein B1 represents an inner diameter of thecolumn part 24 a, B2 represents an outer diameter thereof, B3 represents a diameter of therotation member 31 a, and B4 represents apitch circle 32 a. In this constitution, the number ofrollers 20 a contained in theretainer 21 a can be increased. Therefore, the load capacity of the rocking bearing 30 a can be high. - In addition, referring to
FIGS. 7 to 9 , a wall surface of thecolumn part 24 a for guiding the rotation of theroller 20 a (referred to as the “guide surface” hereinafter) is a flat surface (its cross sectional configuration is a straight line). Thus, dimensions are set to satisfy {θ/(n−1)}°<a1<90° wherein n represents the number of therollers 20 a housed in thepockets 22 a, a1 represents an angle formed between opposed wall surfaces of theadjacent column parts 24 a, and θ represents a center angle between rotation centers of therollers 20 a housed in thepockets 22 a positioned at circumferential both ends. - As the angle a1 formed between the opposed wall surfaces (designating the “guide surface”) of the
adjacent column parts 24 a is decreased, the number ofpockets 22 a that can be formed at the same time by the one mold is decreased. Therefore, it is preferable that the angle a1 is large in view of the improvement of the molding properties, so that a lower limit value of the angle a1 is set to {θ/(n−1)}°. - Meanwhile, when the angle a1 is increased, the
roller 20 a could not be held appropriately in thepocket 22 a. More specifically, force F applied from theroller 20 a to the wall surface of thecolumn part 24 a can be decomposed into force F1 acting in a parallel direction to the wall surface of thecolumn part 24 a and force F2 acting in a vertical direction to the wall surface of thecolumn part 24 a. Thus, the forces F1 and F2 have a relation F1≧F2 when a1≧90°. In this case, theroller 20 a could be brought on thecolumn part 24 a and in contact with theadjacent roller 20 a at the time of rocking. This causes oil film cutting and heat generation on the surface of theroller 20 a. Therefore, in order to hold theroller 20 a appropriately, the angle a1 is preferably small and its upper limit value of the angle a1 is set to 90°. - In addition, although the retainer contained in the rocking bearing has the column part on the inner diameter side than the pitch circle in the above embodiment, the column part may be provided on the upper side of the pitch circle or on the outer diameter side of the pitch circle. In addition, the present invention may be applied to a retainer having no connection part.
- For example, a description will be made of a retainer 21 b for the rocking bearing (referred to as the “retainer 21 b” hereinafter) according to another embodiment of the present invention with reference to
FIG. 10 . In addition, since a basic constitution of the retainer 21 b is the same as that of theretainer 21 a, a description of the common part is omitted and a different part will be mainly described. - The retainer 21 b has
pockets 22 b, a pair ofconnection parts column parts 24 b connecting the pair of connection parts to each other. In addition, thecolumn part 24 b extends in the radial direction across apitch circle 32 b. Thus, dimensions are set to satisfy {θ/(n−1)}°<a2<90° wherein n represents the number of rollers, θ represents the center angle, and a2 represents an angle formed between opposed wall surfaces of theadjacent column part 24 b. - Thus, when the angle formed between the opposed wall surfaces of the adjacent column parts is set within the above range, the effect of the present invention can be achieved regardless of the arranged position of the column part.
- In addition, the
retainer 21 a and the like is preferably formed of a resin in view of mass productivity. For example, theretainer 21 a is formed of a resin material in which fiber filler material is contained in polyamide 46 by injection molding. A specific example of the fiber filler material includes carbon fiber and glass fiber. - In addition, a content of the fiber filler material in polyamide 46 is within a range of 5% to 20% by weight. When the content of the fiber filler material is less than 5% by weight, it is difficult to provide strength required for the
retainer 21 a. Meanwhile, when it is more than 20% by weight, the fluidity of the resin material at the time of molding deteriorates. This causes the problem such as gas burn and filling shortage in molding theretainer 21 a havingmany pockets 22 a and a thin column part. Furthermore, when a filling pressure is increased in order to solve the above problem, a burr could be generated. Therefore, it is preferable that the content of the fiber filler material is within the above-described range. - In addition, referring to
FIG. 8 , dimensions are set to satisfy the following formula 2 wherein n represents the number ofrollers 20 a housed in thepockets 22 a, l represents a length of a part of thepitch circle 32 a overlapping with theroller 20 a, and L represents a circumferential length of thepitch circle 32 a between the rotation centers of therollers 20 a housed in thepockets 22 a positioned at circumferential both ends. -
- The formula 2 shows an occupancy of the
rollers 20 a on the circumference of thepitch circle 32 a. Referring to the formula 2, when the occupancy of therollers 20 a is 0.9 or less, the distance between theadjacent rollers 20 a becomes too large, so that sufficient load capacity cannot be obtained. Meanwhile, when the distance between theadjacent rollers 20 a is small, therollers 20 a could be in contact with each other at the time of rocking. This causes oil film cutting and heat generation on the surface of theroller 20 a. Thus, the occupancy of therollers 20 a needs to be less than 1.0. - In addition, although the bent parts are provided at both flange parts and the engagement parts are provided at both connection parts in the above embodiment, the bent part and the engagement part engaging with it may be only provided at one flange part and one connection part, respectively.
FIG. 11 is a sectional view showing a part of a rockingbearing 30 c in this case, and corresponds toFIG. 6 . Referring toFIG. 11 , abent part 17 d bent toward araceway surface 12 c in the axial direction is provided only on the side of oneflange part 13 d, in anouter ring 11 c contained in the rockingbearing 30 c. Theother flange part 13 c just projects toward the inner diameter side. Anengagement part 26 d projecting in the axial direction is provided at oneconnection part 23 d of aretainer 21 c. Theother connection part 23 c does not have the engagement part. In this constitution also, thebent part 17 d of theouter ring 11 e engages with theengagement part 26 d of theretainer 21 c, and theretainer 21 c can be held so as to be enfolded. Therefore,rollers 20 c and theretainer 21 c can be prevented from dropping out of theouter ring 11 c. - In addition, although the retainer includes the engagement part in the above embodiment, it may not include the engagement part.
FIG. 12 is a sectional view showing a part of a rockingbearing 30 e in this case and corresponds toFIG. 6 . Referring toFIG. 12 ,bent parts raceway surface 12 e in the axial direction are provided at bothflange parts outer ring 11 e contained in the rockingbearing 30 e. In addition, the engagement part projecting in the axial direction is not provided at bothconnection parts retainer 21 e. In this constitution also, theretainer 21 e can be held such that theconnection parts retainer 21 e are enfolded by thebent parts outer ring 11 e. Thus,rollers 20 e and theretainer 21 e can be prevented from dropping out of theouter ring 11 e. In this case also, the bent part may be provided only at one of the flange parts. - Here, although the
retainer 21 a is held by thebent parts outer ring 11 a, a snap fitting allowable configuration may be provided at theretainer 21 a and/or thebent parts retainer 21 a can be held by thebent parts bent parts engagement parts connection parts retainer 21 a in the axial direction. Theengagement parts bent parts engagement parts bent parts - Here, a description will be made of an assembling method of a rocking bearing 30 g.
FIG. 13 is a sectional view showing anouter ring 11 g, aroller 20 g, and aretainer 21 g before assembled. In addition,FIG. 14 is a sectional view showing theouter ring 11 g, theroller 20 g and theretainer 21 g after assembled. In addition, since basic constitutions of the rocking bearing 30 g, theouter ring 11 g, theretainer 21 g and the like are the same as those of the rocking bearing 30 a and the like, their description will be omitted. Referring toFIGS. 13 and 14 , chamferedparts 28 g are provided at outer-diameter corners ofengagement parts connection parts retainer 21 g. In addition, chamferedparts 28 h are also provided at corners of thebent parts - First, the plurality of
rollers 20 g are put in pockets 22 g of theretainer 21 g as shown inFIG. 4 . Then, theouter ring 11 g is moved in a direction shown by an arrow A shown inFIG. 13 . Thus, thebent parts engagement parts retainer 21 g passes through thebent parts bent parts engagement parts retainer 21 g is held by thebent parts retainer 21 g in which therollers 20 g are incorporated may be moved from a direction opposite to the arrow A. - Since the
retainer 21 g is held in theouter ring 11 g so as to be enfolded by thebent parts retainer 21 g is prevented from moving in the direction of the arrow A inFIGS. 13 and 14 , so that theretainer 21 g does not drop out of theouter ring 11 g. Since this snap fitting uses the elastic deformation of thebent parts outer ring 11 g and theengagement parts retainer 21 g, strong force is not necessarily applied at the time of assembling, so that the assembling can be easily performed. In addition, theouter ring 11 g and theretainer 21 g can be prevented from being damaged at the time of assembling. Therefore, the assembling properties of the rocking bearing 30 g can be improved. - Since the chamfered
parts engagement parts bent parts parts 28 g provided at theengagement parts chamfered part 28 h provided at thebent parts engagement parts bent parts engagement parts chamfered part 28 i having a large sloped surface as shown inFIG. 15 . - Here, it is preferable that the
engagement parts connection parts retainer 21 g can be easily elastically deformed in the axial direction in the circumferential positions of theengagement parts - In addition, although the engagement parts as the fitting clicks are provided at the circumferential same position, in both connection parts in the above embodiment, as another example, the circumferential position of the engagement part as the fitting click provided in one connection part may be different from the circumferential position of the engagement part as the fitting click provided in the other connection part.
-
FIG. 16 is a view showing a retainer taken from the inner diameter side in the above case. Referring toFIG. 16 , aretainer 21 i has the same constitution as that of the above retainer basically, and includespockets 22 i, a pair ofconnection parts column parts 24 i. Here, the pair ofconnection parts engagement parts engagement part 26 i as the fitting click provided in oneconnection part 23 i is different from the circumferential position of theengagement part 26 j as the fitting click provided in theother connection part 23 j. - Thus, when the snap fitting is performed, the
engagement part 26 i as the fitting click provided in the oneconnection part 23 i and theengagement part 26 j as the fitting click provided in theother connection part 23 j are not elastically deformed at the same circumferential position. Therefore, theretainer 21 i can be elastically deformed in the axial direction at the circumferential different positions of theengagement parts - Especially, when the axial projection amount of the
engagement parts retainer 21 i, in the case where theengagement parts engagement parts 25 i and 26 j as fitting clicks is increased at the time of assembling, which could cause the damage of theengagement parts engagement parts - In addition, although the snap fitting allowable configuration includes the engagement part as the fitting click projecting from the end face of the connection part of the retainer in the above embodiment, as another example, the snap fitting allowable configuration may be provided at the connection part of the retainer and have a slit recessed in the radial direction.
-
FIG. 17 is a sectional view showing a rocking bearing in this case and corresponds toFIG. 6 . Referring toFIG. 17 , a rockingbearing 30 k has the same configuration as that of the above rocking bearing basically, and includes an outer ring ilk, aroller 20 k, and aretainer 21 k to hold theroller 20 k. Here, aslit 28 k allowing the axial elastic deformation of aconnection part 23 k is provided at the oneconnection part 23 k of a pair ofconnection parts 23 k and 23 l of theretainer 21 k. Theslit 28 k is recessed from anouter diameter surface 29 k of theconnection part 23 k in the radial direction, that is, toward the inner diameter side so as to be continued along theconnection part 23 k. In addition, theslit 23 k has a roughly V-shaped section. Here, the snap fitting allowable configuration includes theslit 28 k. Theretainer 21 k can be elastically deformed so that theconnection part 23 k is shrunk in the axial direction by use of theslit 28 k. Therefore, theconnection part 23 k snap-fit in thebent part 17 k, whereby theretainer 21 k can be held by thebent part 17 k of the outer ring ilk. Therefore, similar to the above rocking bearing, its assembling properties can be improved. - In addition, although the
slit 28 k is provided only oneconnection part 23 k in the above embodiment, as another case, slits 28 k and 28 l may be provided at bothconnection parts 23 k and 23 l, respectively as shown inFIG. 18 . In other words, the snap fitting allowable configuration may include theslits 28 k and 28 l provided at theconnection parts 23 k and 23 l, respectively. Furthermore, theslits 28 k and 28 l may be partially provided in the circumferential direction and they may not be necessarily continued in the circumferential direction. - Here, it is preferable that dimensions of the
slit 28 k have the following relation.FIG. 19 is an enlarged view showing theslit 28 k in the rockingbearing 30 k shown inFIG. 17 . Referring toFIG. 19 , the dimension are set to have a relation 0.2W2<W1<0.8W2 wherein W1 represents an axial length of the of theslit 28 k, and W2 represents an axial length of theconnection part 23 k. In addition, the dimension are set to have a relation 0.2H2<H1<0.8H2 wherein H1 represents a radial length of theslit 28 k, and H2 represents a radial length of theconnection part 23 k. Here, the axial length W1 of theslit 28 k designates a length of theslit 28 k on the side of theouter diameter surface 29 k, and the length W2 of theconnection part 23 k designates an axial length from anend face 27 k of theconnection part 23 k to a wall surface 21 of the pocket. In addition, the radial length H1 of theslit 28 k designates a length from theouter diameter surface 29 k to a radial most recessed part of theslit 28 k, and the radial length H2 of theconnection part 23 k designates a length from theouter diameter surface 29 k to an inner diameter surface 29 l of theconnection part 23 k. - Thus, the
connection part 23 k can be appropriately elastically deformed. That is, when 0.2W2<W1 and 0.2H2<H1, theconnection part 23 k can be elastically deformed and the snap fitting can be implemented appropriately. In addition, when W1<0.8W2 and H1<0.8H2, theconnection part 23 k can be prevented from being damaged at the time of snap fitting. - In addition, although the slit has the roughly V-shaped section in the above embodiment, it may have another configuration.
FIG. 20 is an enlarged sectional view showing a part of a rocking bearing in this case, and corresponds toFIG. 19 . Referring toFIG. 20 , a rockingbearing 30 m has the same constitution as that of the above rocking bearing basically, and includes anouter ring 11 m, aroller 20 m, and aretainer 21 m holding theroller 20 m. Aconnection part 23 m of theretainer 21 m is provided with aslit 28 m. Side wall surfaces 25 m and 25 n of theslit 28 m are roughly parallel to anend face 27 m of theconnection part 23 m, and abottom part 26 m recessed toward the inner diameter side has R section. The slit may be theslit 28 m having the above configuration. - Similar to the above, the dimensions have a relation 0.2W2<W1<0.8W2 wherein W1 represents an axial length of the
slit 28 m, and W2 represents an axial length of theconnection part 23 m. In addition, dimensions have a relation 0.2H2<H1<0.8H2 wherein H1 represents a radial length of theslit 28 m, and H2 represents a radial length of theconnection part 23 m. Thus, similar to the rocking bearing shown inFIGS. 17 to 19 , theconnection part 23 m can be appropriately elastically deformed. Here, the axial length W1 of theslit 28 m designates a length between the side wall surfaces 25 m and 25 n of theslit 28 m, and the length W2 of theconnection part 23 m designates an axial length from anend face 27 m of theconnection part 23 m to awall surface 27 n of a pocket. In addition, the radial length H1 of theslit 28 m designates a length from theouter diameter surface 29 m to abottom part 26 m, and the radial length H2 of theconnection part 23 m designates a length from theouter diameter surface 29 m to aninner diameter surface 29 n of theconnection part 23 m. - In addition, in this case also, the slit having the same configuration may be provided at each connection part. In addition, the present invention is not limited to the configurations shown in
FIGS. 17 to 20 , and may be applied to other various configurations. - Furthermore, as shown in
FIG. 21 , the snap fitting allowable configuration may include anend face 28 p of aconnection part 23 p sloped so that its axial length is increased from the outer diameter side to the inner diameter side in aretainer 21 p contained in a rockingbearing 30 p. In this case also, theconnection part 23 p can snap-fit in thebent part 17 p. - Here, for example, the above snap fitting allowable configurations may be combined such that the slit is provided at one connection part and the fitting click is provided at the other connection part in the retainer. In this case, for example, when the slit recessed from the inner diameter surface toward the outer diameter side is provided at the connection part having the
end face 28 p shown inFIG. 21 , the snap fitting can be more easily implemented. - In addition, as shown in
FIG. 22 , the snap fitting allowable configuration may be provided in abent part 17 q. Thebent part 17 q provided at the flange part of anouter ring 11 q in a rockingbearing 30 q is folded back in the axial direction. In this case, the snap fitting can be implemented between thebent part 17 q and theconnection part 23 q by elastically deforming thebent part 17 q in the axial direction. - In addition, as the retainer arranged on the inner diameter side of the outer ring can be circumferentially moved in the above rocking bearing, it is necessary to provide movement restricting means in order to prevent the retainer from dropping out of the outer ring. According to a conventional example, a projection part projecting toward the inner diameter side is provided at a circumferential end of an outer ring and the projection part abuts on a circumferential end of a retainer to restrict the circumferential movement of the retainer. However, according to the movement restricting means, the circumferential movable range of the retainer cannot be provided enough. Meanwhile, according to Japanese Unexamined Patent Publication No. 2003-214330, a control lever is provided in a rocking bearing as a new member, a raceway ring and a retainer are connected so as not to be separated, and both ends of the control lever are fit in a rotation member and a fix member, to restrict the circumferential movement of the retainer. However, according to the Japanese Unexamined Patent Publication No. 2003-214330, since it is necessary to provide the control lever, this is not preferable in view of the aim to reduce cost and the number of components.
- Here, for example, in the rocking bearing 30 a containing the
outer ring 11 a shown inFIG. 1 , a click part to abut on and engage with a projection part provided in a retainer that will be described later in the circumferential direction may be provided at axial both ends of theouter ring 11 a in which theflange parts connection parts - The above will be described with reference to
FIGS. 23 and 24 .FIGS. 23 and 24 are views showing the rocking bearing 30 a taken from the axial direction, in whichFIG. 23 shows a state in which aclick part 18 a does not abut on aprojection part 18 b, andFIG. 24 shows a state in which theclick part 18 a abuts on theprojection part 18 b. In addition, theflange parts FIGS. 23 and 24 in view of easy understanding In addition, since the basic constitutions of the rocking bearing 30 a, theouter ring 11 a, theretainer 21 a are the same as those described above, their description will be omitted. - Referring to
FIGS. 23 , 24, and 1, theclick part 18 a is provided at the end opposite to the circumferential end in which theprojection parts click part 18 a may be provided at the position closer to the end in theflange parts projection part 18 b is provided at the position closer to theend 25 a of theends projection part 18 b is provided circumferential peripheral inner side than thepocket 22 a arranged circumferential outermost side. In addition, although theprojection part 18 b is combined with theengagement part 26 a here, theprojection part 18 b and theengagement part 26 a may be provided separately. - The
retainer 21 a is moved within a predetermined range in the circumferential direction in theouter ring 11 a. Theretainer 21 a is moved around arotation center 33 a in the circumferential direction, that is, a direction shown by an arrow E inFIG. 23 and its opposite direction. Here, when theretainer 21 a is moved in the circumferential direction, and theprojection part 18 b provided at the predetermined position of theconnection part click part 18 a provided in theouter ring 11 a, theretainer 21 a cannot be moved in the circumferential direction any more. - Thus, the circumferential movement of the
retainer 21 a can be restricted. In other words, after theretainer 21 a is circumferentially moved in theouter ring 11 a by the predetermined amount, theclick part 18 a abuts on theprojection part 18 b to limit the movement amount of theretainer 21 a. According to the rocking bearing 30 a having the above constitution, the circumferential movement amount of theretainer 21 a can be optionally determined by the position of theprojection part 18 b. In this case, since theretainer 21 a can be moved until theprojection part 18 b abuts on theclick part 18 a, its movement range can be largely provided. In addition, according to the rocking bearing 30 a containing theouter ring 11 a and theretainer 21 a, since it is not likely that theretainer 21 a drops off, its assembling properties is improved. According to the rocking bearing 30 a, since it is not necessary to provide a new member, its cost can be low. - In addition, since the predetermined position of the
projection part 18 b is on the circumferential inner side than thepocket 22 a arranged in the circumferential outermost side, and the movement of theretainer 21 a is limited at the position in which a part of theretainer 21 a projects from the circumferential one end of theouter ring 11 a, the movement range of theretainer 21 a can be further increased within a rolling range of theroller 20 a held in thepocket 22 a. - The circumferential length of the
retainer 21 a projecting from theouter ring 11 a may be not more than the circumferential length from the oneend 25 a of theretainer 21 a to thepocket 22 a positioned on the circumferential outermost side on the oneend 25 a side. More specifically, a length F is to be not more than a length G inFIGS. 23 and 24 . Thus, the movement range of theretainer 21 a can be further increased. In addition, even when theprojection part 18 b abuts on theclick part 18 a, theroller 20 a housed in thepocket 22 a positioned on the circumferential outermost side does not drop off. Therefore, theroller 20 a housed in thepocket 22 a arranged on the circumferential outermost side can be prevented from dropping off. According to such rocking bearing 30 a, its assembling properties can be further improved. - In addition, the predetermined position of the
projection part 18 b may be on the circumferential outer side than thepocket 22 a provided on the outermost side on the side of theengagement part end 25 a. In this case also, the movement range of theretainer 21 a can be largely provided. - In addition, the
click part 18 a and theprojection part 18 b abutting thereon may be provided only axial one side. In this case also, the circumferential movement of theretainer 21 a can be restricted. - Here, although the click part is provided at the circumferential end of the outer ring in the above embodiment, the click part may be provided at a predetermined position close to the circumferential end of the outer ring.
FIGS. 25 , 26, and 27 show an outer ring and a rocking bearing in this case, and correspond toFIGS. 1 , 23, and 24, respectively. Referring toFIGS. 25 to 27 , a constitution of anouter ring 11 r is basically the same as that of theouter ring 11 a shown inFIG. 1 , and theouter ring 11 r has araceway surface 12 r,flange parts projection parts protrusions bent parts retainer 21 r is circumferentially moved around arotation center 33 r. Here, aclick part 18 r is provided at a predetermined position close to its circumferential end. In addition, theclick part 18 r is provided on the side of theraceway surface 12 r of theflange parts retainer 21 r can be largely provided. - The above outer ring is produced by the following production method. As a starting material, carbon steel containing 0.5 to 1.1% by weight of carbon is used. More specifically, SK5, SUJ2, and SAE1070 containing 0.5 to 1.1% by weight of carbon (all of them comply with JIS) may be used.
-
FIG. 28 is a flowchart showing representative production steps of the outer ring. Referring toFIG. 28 , a steel plate of the above starting material is punched out (FIG. 28(A) ). Then, the flange part is formed by a bending process, whereby an outline configuration of the outer ring is formed (FIG. 28(B) ). This bending step is implemented by a pressing process. In this case, since the above material having the above carbon content is used, that is, since the material containing 1.1% or less by weight of carbon is used, its processability is preferable, so that the outline configuration of the outer ring can be formed with high accuracy. In addition, since the bending process is performed by the pressing process, the outline configuration of the outer ring can be formed at low cost. - Then, a heat treatment is performed (
FIG. 28(C) ). Here, a bright quenching treatment or high-frequency quenching treatment is performed as the heat treatment. In this case, since the material containing 0.5% or more of carbon is used, hardness required for the outer ring, that is, hardness of Hv653 or more can be provided by the bright quenching treatment or the high-frequency quenching treatment. Accordingly, a carburized quenching treatment is not needed. Therefore, the outer ring is not likely to be prevented from being deformed and the outline configuration of the outer ring can be maintained with high accuracy. - Here, the bright quenching treatment means a quenching treatment in which the steel is heated in a protective atmosphere or vacuum while its surface is prevented from being oxidized. This quenching treatment is low in facility cost. Therefore, the production cost can be low.
- The high-frequency quenching treatment is a method for producing a hardened layer by heating a steel surface rapidly by use of induction heating and then cooling rapidly. This quenching treatment is also low in facility cost. Therefore, production cost can be also low. In addition, since a gas is not needed in the heat treatment step, it has an advantage of being environment-friendly. Furthermore, the quenching treatment can be partially performed.
- Furthermore, it is preferable to perform a tempering treatment after the above quenching treatment to reduce a residual stress and internal distortion generated in the quenching treatment, and to improve the toughness and stabilize the dimension.
- In addition, after the heat treatment, a polishing process for polishing the object is performed and then a cleaning process is performed, whereby a final product is provided. In addition, the rollers and the retainer are assembled in the above outer ring produced as described above, whereby the rocking bearing is completed.
- As described above, the outline configuration can be formed by the pressing process with high accuracy. In addition, the hardness required for the outer ring can be provided by the bright quenching treatment or the high-frequency quenching treatment as the heat treatment. Thus, the deformation can be prevented at the time of heat treatment. Therefore, the outer ring is high in accuracy, low in cost, and high in load capacity. Furthermore, since not only the raceway surface but also the bent part can be high in hardness, the bent part is prevented from being damaged. Therefore, the retainer and the roller can be more surely prevented from dropping off.
- In addition, the above outer ring may be produced by the following production method. As a starting material, carbon steel containing 0.15% to 1.1% by weight of carbon is used. More specifically, SCM415 and S50C containing 0.15% to 0.5% by weight of carbon (both comply with JIS) or SAE1070 and SK5 containing 0.5% to 1.1% by weight of carbon (both comply with JIS) may be used.
- Referring to
FIG. 28 again, the steel plate of the starting material is punched out (FIG. 28(A) ). Then, the flange part is bent by the bending process, whereby the outline of the outer ring is formed (FIG. 28(B) ). Then, the above heat treatment is performed (FIG. 28(C) ). Then, the polishing process is performed and the cleaning process is performed, whereby the final product is completed. - Here, as the heat treatment, carbonitriding treatment is performed. When the carbonitriding treatment is performed on the material containing 0.15 to 1.1% by weight of carbon, the outer ring having the required hardness can be produced at low cost. That is, since the outer ring has high load capacity, it is hardly damaged. In addition, since the strength of the bent part can be high, the retainer and the roller can be more surely prevented from dropping off.
- As another heat treatment, a carburizing treatment may be performed. The carburizing treatment is a heat treatment using a phenomenon in which carbon is soluble in high-temperature steel, by which while the carbon content is low inside the steel, the carbon content is high in a surface layer (hardened layer). Thus, the carburized material has a hard surface but its inside is soft and high in toughness. In addition, according to such quenching treatment, its facility cost is low.
- Furthermore, it is preferable to perform a tempering treatment after the above quenching treatment to reduce the residual stress and internal distortion generated in the quenching treatment, and to improve the toughness and stabilize the dimension.
- In addition, the outer ring and/or the roller may have a nitrogen enrichment layer, and an austenite grain size number of 10 or more, and contains 11% to 25% by volume of retained austenite and 0.1% to 0.7% by weight of nitrogen. In this constitution, the rocking bearing features a long life.
- When a low-temperature secondary quenching treatment as the heat treatment to be described below is performed on the outer ring and/or the roller in the rocking bearing, the outer ring and/or the roller can have an austenite grain size number in the nitrogen enrichment layer that exceeds 10, and contains 11% to 25% by volume of retained austenite and 0.1% to 0.7% by weight of nitrogen.
- Next, a description will be made of the heat treatment including the carbonitriding treatment performed on the outer ring and/or the roller. In addition, a roller bearing having a roller (outer ring), a roller shaft (inner ring), and rollers as bearing components, is used in a working example.
FIG. 29 is a view showing one example of a two-stage heat treatment to obtain the above bearing components. In addition,FIG. 30 is a view showing a variation of the two-stage heat treatment shown inFIG. 29 . Thus,FIG. 29 shows a heat treatment pattern in which a primary quenching treatment and a secondary quenching treatment are performed, andFIG. 30 shows a heat treatment pattern in which a material is cooled below the transformation temperature of A1 during the quenching treatment and then heated again to be quenched at a final stage. In either case, the above bearing components can be produced. In these drawings, carbon and nitrogen are diffused and carbon is sufficiently dissolved in a steel base in a treatment T1, and then the steel base is cooled below the transformation temperature A1. Then, in a treatment T2, the steel is heated again to the temperature lower than that in the treatment T1, and then subjected to an oil quenching treatment. In addition, the heat treatment methods shown inFIGS. 29 and 30 are called the two-stage heat treatment collectively. - According to the above heat treatment, while the surface layer is carbonitrided, cracking strength can be improved and an aging length change rate can be reduced as compared with the general quenching treatment in which the quenching treatment is performed one time after the carbonitriding treatment. Through the above heat treatment method, a microstructure in which the austenite grain size can be less than half the conventional one can be provided. According to the bearing component subjected to the above heat treatment, rolling fatigue characteristics has a long life, the cracking strength is improved and the aging length change rate can be reduced.
-
FIGS. 31 and 32 show the microstructures of the austenite grains of the bearing components.FIG. 31 shows a bearing component subjected to the above heat treatment, andFIG. 32 shows a conventional bearing component. More specifically,FIG. 31 shows the austenite grain size of bearing steel subjected to the heat treatment pattern shown inFIG. 30 . In addition, for comparison,FIG. 32 shows the austenite grain size of the bearing steel subjected to a conventional heat treatment method. In addition,FIGS. 33 and 34 are views showing illustrated austenite grain boundaries ofFIGS. 31 and 32 , respectively. According to the structure of the austenite grain size, the austenite grain size number according to JIS standard is 10 or less in the case of the conventional treatment, and the number is 12 in the case of the above two-stage heat treatment. In addition, an average grain size inFIG. 31 measured by a section method is 5.6 μm. - The working example will be described hereinafter. A roll, a roll shaft, and a roller were produced by the three kinds of heat treatments such as a standard heat treatment, a carbonitriding treatment, and a two-stage heat treatment. The standard heat treatment, the carbonitriding treatment, and the two-stage heat treatment are the following heat treatments.
- The standard heat treatment: After a heat treatment at a heating temperature of 840° C. for a retention time of 20 minutes in a RX gas atmosphere, a quenching treatment was performed and then a tempering treatment was performed at 180° C. for 90 minutes.
- Carbonitriding treatment: After a heat treatment at a heating temperature of 850° C. for a retention time of 150 minutes in a RX-ammonia mixture gas atmosphere, a quenching treatment was performed from a temperature of 850° C. and then a tempering treatment was performed at 180° C. for 90 minutes.
- Two-stage heat treatment: A carbonitriding treatment was performed at a carbonitriding treatment temperature of 850° C. for a retention time of 150 minutes. The carbonitriding treatment was performed in a RX-ammonia mixture gas atmosphere. Then, based on the heat treatment pattern shown in
FIG. 29 , the primary quenching was performed at the carbonitriding treatment temperature of 850° C., and the secondary quenching was performed at a temperature of 800° C. lower than the carbonitriding treatment temperature, for 20 minutes, and a tempering treatment was performed at 180° C. for 90 minutes. - Table 1 shows qualities of the members provided by the above heat treatments.
-
TABLE 1 RETAINED AUSTENITE AUSTENITE NITROGEN HEAT TREATMENT GRAIN SIDE VOLUME CONTENT METHOD (JIS) (% BY VOLUME) (% BY WEIGHT) STANDARD HEAT 9 7 0 TREATMENT CARBONITRIDING 8 29 0.31 TRATMENT TWO-STAGE HEAT 12 21 0.30 TREATMENT - A description will be made of methods for examining material qualities.
- Austenite grain size: The austenite grain size was measured based on an austenite grain size testing method for steel of JIS G 0551.
- Retained austenite volume: The retained austenite volume was measured by comparing the diffraction intensity of martensite α (211) with that of retained austenite γ (220). As the retained austenite volume, the value at a surface layer of 50 μm from a rolling surface after ground was used.
- Nitrogen content: The nitrogen content was measured by use of EPMA. As the nitrogen content, a value at a surface layer of 50 μm from the rolling surface after ground was used.
- Next, the test result shown in Table 1 will be described.
- Austenite grain size: The grain size number of the member through the two-stage heat treatment is as fine as 12, which is considerably miniaturized. The grain size numbers of the member through the standard heat treatment and the member through the carbonitriding treatment are 9 and 8, respectively and the austenite grains are larger than that of the member through the two-stage heat treatment.
- Retained austenite volume: The retained austenite volume of the member through the two-stage heat treatment is 21% by volume and austenite exists appropriately. Meanwhile, the retained austenite volume of the member through the standard heat treatment is 7% by volume which is less than that of the member through the two-stage heat treatment. In addition, the retained austenite volume of the member through the carbonitriding treatment is 29% by volume which is more than that of the member through the two-stage heat treatment. As a result, it can be understood that the member through the two-stage heat treatment is intermediate in retained austenite volume between the member through the standard heat treatment and the member through the carbonitriding treatment.
- Nitrogen content: The nitrogen content of the member through the two-stage heat treatment is 0.30%. The nitrogen content of the member through the standard heat treatment is 0% because the carbonitriding treatment is not performed. In addition, the nitrogen content of the member through the carbonitriding treatment is 0.31%. The nitrogen content of the member through the two-stage heat treatment is a little less than that of the member through the carbonitriding treatment. This is attributed to the fact that the secondary quenching treatment was performed at 800° C. lower than the carbonitriding treatment temperature after the carbonitriding treatment in the two-stage heat treatment.
- Then, roller bearings are made up of various combinations of the roll, the roll shaft, and the rollers produced by the above three kinds of heat treatments, as samples 1 to 11.
FIG. 35 is a sectional view showing the structures (dimensions) of the samples 1 to 6.FIG. 36 is a sectional view showing the structures (dimensions) of the samples 7 to 11. As shown inFIG. 35 , according to the samples 1 to 6, aroll 62 androller 64 are 6.9 mm in width, and aroll shaft 63 is 17.3 mm in width. Meanwhile, as shown inFIG. 36 , according to the samples 7 to 11, theroll 62 and theroller 64 are 5.5 mm in width, and theroll shaft 63 is 15.9 mm in width. That is, the samples 7 to 11 are reduced in size by about 20% as compared with the samples 1 to 6. - Then, a peeling life test was performed on the samples 1 to 11 by the following method.
FIG. 37 is a front view showing an essential part of a peelinglife test machine 65, andFIG. 38 is a sectional view taken along a line XXXVIII-XXXVIII inFIG. 37 . As shown inFIGS. 37 and 38 , aroller bearing 61 is arranged so that a drivingroll 66 of the peelinglife test machine 65 is brought in contact with theroll 62 to fix theroller shaft 63. Thus, under the condition that a radial load was applied from the drivingroll 66 of the peelinglife test machine 65, the drivingroll 66 was rotated in a direction shown by an arrow inFIG. 37 to rotate theroll 62. A time (life) to occurrence of peeling in any one of theroll 62, theroll shaft 63, and theroller 64 was measured. In addition, the load applied from the drivingroll 66 to theroller bearing 61 was set to 2.58 kN, and the rotation speed of theroll 62 was set to 7000 r/min. In addition, as lubricant oil between theroller 64, and theroll 62 and theroll shaft 63, 10W-30 engine oil was used and the temperature of the lubricant oil was set to 100° C. - Tables 2 and 3 show the combinations of the members of the samples and the peeling lives of the samples. The samples 6, 9 10 and 11 were subjected to the two-stage heat treatment. In addition, the peeling lives of the samples are shown assuming that the peeling life of the sample 1 is set to 1.
-
TABLE 2 SAMPLE NO. 1 2 3 4 5 6 SAMPLE 6.9 (mm) WIDTH OUTER RING STANDRAD HEAT CARBONITRIDING STANDRAD TWO-STAGE (ROLL) TREATMENT TREATMENT HEAT HEAT TREATMENT TREATMENT ROLLER STANDRAD CARBONITRIDING TREATMENT TWO-STAGE HEAT (ROLLING HEAT TREATMENT BODY) TREATMENT INNER RING STANDRAD HEAT CARBONITRIDING TWO-STAGE HEAT (ROLL TREATMENT TREATMENT TREATMENT SHAFT) LOAD 2.58 (kN) DAMAGED SHAFT AND SHAFT SHAFT SHAFT SHAFT SHAFT MEMBER ROLLER PEELING 1 1.3 1.7 1.9 2.8 3.5 LIFE -
TABLE 3 SAMPLE NO. 7 8 9 10 11 SAMPLE 5.5 (mm) WIDTH OUTER RING STANDRAD CARBONITRIDING TREATMENT (ROLL) HEAT TREATMENT ROLLER CARBONITRIDING TWO-STAGE CARBONITRIDING TWO-STAGE (ROLLING TREATMENT HEAT TREATMENT HEAT BODY) TREATMENT TREATMENT INNER RING CARBONITRIDING TREATMENT TWO-STAGE HEAT TREATMENT (ROLL SHAFT) LOAD 2.58 (kN) DAMAGED OUTER RING SHAFT SHAFT SHAFT SHAFT MEMBER PEELING LIFE 0.8 1.1 1.2 1.5 1.7 - As shown in Table 2, according to the sample 6 in which all of the
roll 62, theroll shaft 63, and theroller 64 were subjected to the two-stage heat treatment, the peeling life is 3.5 times as long as the sample 1 in which all of the members were subjected to the standard heat treatment. In addition, as shown in Table 3, even when the bearing is reduced in size, the sample 9 in which theroll 62 and theroll shaft 63 were subjected to the carbonitriding treatment and theroller 64 was subjected to the two-stage heat treatment has a peeling life that is 1.2 times as long as the sample 1. In addition, the sample 10 in which theroll 62 and theroller 64 were subjected to the carbonitriding treatment, and theroll shaft 63 was subjected to the two-stage heat treatment has a peeling life that is 1.5 times as long as the sample 1. Furthermore, thesample 11 in which theroll 62 was subjected to the carbonitriding treatment, and theroller 64 and theroll shaft 63 were subjected to the two-stage heat treatment has a peeling life that is 1.7 times as long as the sample 1. As a result, it can be understood that each of theroll 62, theroll shaft 63, and theroller 64 has the nitrogen enrichment layer, and when theroll 62 and/or theroller 64 are subjected to the two-stage heat treatment, the life can be elongated while the bearing can be reduced in size. - Therefore, the rocking bearing composed of the outer ring and the roller having the same constitutions as above has a longer peeling life. Therefore, the long life can be achieved.
- Next, a brief description will be made of a constitution of the air disk brake system having the above-described rocking bearing.
FIG. 39 is a schematic sectional view showing a part of the air disk brake system according to one embodiment of the present invention. Referring toFIG. 39 , an airdisk brake system 71 includes abrake cylinder 79 having anactuator rod 72, alever 73 connected to one end of theactuator rod 72, arotation member 74 connected to the other end of thelever 73, a rockingbearing 75 rotatably supporting therotation member 74, aconnection part 80 provided at an eccentric position with respect to therotation member 74, atransmission part 76 having one end connected to theconnection part 80, right and leftbrake pads transmission part 76, and arotor 78 arranged between the right and leftbrake pads - The
actuator rod 72 pushes thelever 73 in a direction shown by an arrow C inFIG. 39 by the action of compressed air in thebrake cylinder 79. Thus, therotation member 74 is rotated and thetransmission part 76 connected to theconnection part 80 is pressed in a direction shown by an arrow D inFIG. 39 . Then, when thetransmission part 76 is moved, the right and leftbrake pads rotor 78. In addition, when the load from therotation member 74 is removed, thetransmission part 76 receives force applied from aspring 81 in a direction opposite to the direction shown by the arrow D, and thetransmission part 76 is returned to the original position. Thus, thebrake pads rotor 78. Thus, the airdisk brake system 71 are constituted. - Here, the rocking
bearing 75 rotatably supporting therotation member 74 has the same constitution as the above shown inFIG. 5 . According the rockingbearing 75, after assembled by arranging a retainer holding rollers, on the inner diameter side of an outer ring, the retainer is held so as to be enfolded by a bent part, so that the roller and the retainer can be prevented from dropping out of the outer ring. In addition, at the time of assembling, the roller and the retainer can be prevented from being separated and shifted. Therefore, the assembling properties of the rockingbearing 75 are improved. - Since the air
disk brake system 71 contains the rockingbearing 75 having preferable assembling properties, its productivity can be improved. - Furthermore, the air
disk brake system 71 may have any one of the above-described rocking bearings. - In addition, although the outer ring is formed into the final outline configuration by punching out the steel plate in the above embodiments, it may be produced by a cutting process.
- Although the embodiments of the present invention have been described with reference to the drawings in the above, the present invention is not limited to the above-illustrated embodiments. Various kinds of modifications and variations may be added to the illustrated embodiments within the same or equal scope of the present invention.
- The outer ring according to the present invention can be effectively used in the rocking bearing requiring preferable assembling properties.
- The rocking bearing according to the present invention can be effectively used when preferable assembling properties are required.
- The air disk brake system according to the present invention can be effectively used when productivity is required to be improved.
Claims (5)
1-34. (canceled)
35. A retainer for rocking bearing comprising:
a pair of connection parts extending in a circumferential direction; and
a plurality of column parts connecting said pair of connection parts to each other to form a plurality of pockets to hold rollers between said adjacent column parts, wherein
the radial outermost part of said column part is arranged apart from a pitch circle formed by connecting rotation centers of said rollers.
36. A rocking bearing comprising:
an outer ring for rocking bearing containing a raceway surface on the inner diameter side and having a flange part provided by bending axial each end to the inner diameter side;
a plurality of rollers arranged on said raceway surface; and
the retainer for rocking bearing according to claim 35 .
37. A retainer for rocking bearing comprising:
a pair of connection parts extending in a circumferential direction; and
a plurality of column parts connecting said pair of connection parts to each other to form a plurality of pockets to hold the rollers between said adjacent column parts, and satisfying a relation:
{θ/(n−1)}°<a 0<90°
{θ/(n−1)}°<a 0<90°
wherein n represents the number of rollers housed in said pockets, a0 represents an angle formed between opposed wall surfaces of said adjacent column parts, and θ represents a center angle formed between rotation centers of the rollers housed in said pockets positioned at circumferential both ends.
38. A rocking bearing comprising:
an outer ring for rocking bearing containing a raceway surface on the inner diameter side and having a flange part provided by bending axial each end to the inner diameter side;
a plurality of rollers arranged on said raceway surface; and
the retainer for rocking bearing according to claim 37 .