US20090087335A1 - Fire resistant steel and method of production of same - Google Patents

Fire resistant steel and method of production of same Download PDF

Info

Publication number
US20090087335A1
US20090087335A1 US11/919,781 US91978106A US2009087335A1 US 20090087335 A1 US20090087335 A1 US 20090087335A1 US 91978106 A US91978106 A US 91978106A US 2009087335 A1 US2009087335 A1 US 2009087335A1
Authority
US
United States
Prior art keywords
less
steel
fire resistant
yield strength
strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/919,781
Other languages
English (en)
Inventor
Teruhisa Okumura
Kohichi Yamamoto
Suguru Yoshida
Hiroshi Kita
Hirokazu Sugiyama
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Assigned to NIPPON STEEL CORPORATION reassignment NIPPON STEEL CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: OKUMURA, TERUHISA, YOSHIDA, SUGURU, YAMAMOTO, KOHICHI, KITA, HIROSHI, SUGIYAMA, HIROKAZU
Publication of US20090087335A1 publication Critical patent/US20090087335A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper

Definitions

  • N forms B nitrides and assists the formation of ferrite, so the content of N was limited to 0.006% or less.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Steel (AREA)
  • Metal Rolling (AREA)
US11/919,781 2005-05-02 2006-04-28 Fire resistant steel and method of production of same Abandoned US20090087335A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2005134297 2005-05-02
JP2006118826A JP5098210B2 (ja) 2005-05-02 2006-04-24 耐火用鋼材およびその製造方法
PCT/JP2006/309347 WO2006118339A1 (ja) 2005-05-02 2006-04-28 耐火用鋼材およびその製造方法

Publications (1)

Publication Number Publication Date
US20090087335A1 true US20090087335A1 (en) 2009-04-02

Family

ID=37308117

Family Applications (1)

Application Number Title Priority Date Filing Date
US11/919,781 Abandoned US20090087335A1 (en) 2005-05-02 2006-04-28 Fire resistant steel and method of production of same

Country Status (6)

Country Link
US (1) US20090087335A1 (ko)
EP (1) EP1878810B1 (ko)
JP (1) JP5098210B2 (ko)
KR (2) KR20100046068A (ko)
CN (1) CN101171354B (ko)
WO (1) WO2006118339A1 (ko)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100065168A1 (en) * 2006-09-04 2010-03-18 Suguru Yoshida Fire resistant steel excellent in high temperature strength, toughness, and reheating embrittlement resistance and process for production of the same
EP2143813A4 (en) * 2007-04-06 2015-09-30 Nippon Steel & Sumitomo Metal Corp STEEL MATERIAL HAVING EXCELLENT HIGH TEMPERATURE RESISTANCE AND TENACITY, AND PRODUCTION PROCESS

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102251178B (zh) * 2011-06-21 2012-12-05 北京科技大学 一种在热扰动下保持恒定硬度的低合金钢的制备方法
JP6295632B2 (ja) * 2013-12-16 2018-03-20 新日鐵住金株式会社 靭性に優れた高強度ｈ形鋼
CN104046902B (zh) * 2014-06-30 2016-09-28 莱芜钢铁集团有限公司 一种低钼高钛590MPa级建筑用耐火钢板及其制造方法
CN105112783A (zh) * 2015-09-15 2015-12-02 攀钢集团攀枝花钢铁研究院有限公司 一种焊接结构用钢及其制备方法
WO2020158823A1 (ja) * 2019-01-31 2020-08-06 Ｊｆｅスチール株式会社 突起付きｈ形鋼およびその製造方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6290784B1 (en) * 1998-11-10 2001-09-18 Kawasaki Steel Corporation Hot rolled steel sheet having an ultrafine grain structure and process for producing steel sheet
US20020192012A1 (en) * 2000-04-24 2002-12-19 Tatsumi Kimura Linear shape steel excellent in joint fatigue characteristics and production method therefor

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06104854B2 (ja) * 1989-02-04 1994-12-21 新日本製鐵株式会社 耐火性に優れた建築用低降伏比熱延鋼板の製造方法
JPH07100816B2 (ja) * 1989-05-08 1995-11-01 新日本製鐵株式会社 耐火性に優れた建築用低降伏比冷延鋼板の製造方法
JP4819233B2 (ja) * 2000-08-30 2011-11-24 新日本製鐵株式会社 成形性に優れたアルミニウム合金板
JP4362219B2 (ja) * 2000-10-11 2009-11-11 新日本製鐵株式会社 高温強度に優れた鋼およびその製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6290784B1 (en) * 1998-11-10 2001-09-18 Kawasaki Steel Corporation Hot rolled steel sheet having an ultrafine grain structure and process for producing steel sheet
US20020192012A1 (en) * 2000-04-24 2002-12-19 Tatsumi Kimura Linear shape steel excellent in joint fatigue characteristics and production method therefor

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100065168A1 (en) * 2006-09-04 2010-03-18 Suguru Yoshida Fire resistant steel excellent in high temperature strength, toughness, and reheating embrittlement resistance and process for production of the same
US8097096B2 (en) 2006-09-04 2012-01-17 Nippon Steel Corporation Fire resistant steel excellent in high temperature strength, toughness, and reheating embrittlement resistance and process for production of the same
EP2143813A4 (en) * 2007-04-06 2015-09-30 Nippon Steel & Sumitomo Metal Corp STEEL MATERIAL HAVING EXCELLENT HIGH TEMPERATURE RESISTANCE AND TENACITY, AND PRODUCTION PROCESS

Also Published As

Publication number Publication date
CN101171354A (zh) 2008-04-30
WO2006118339A1 (ja) 2006-11-09
EP1878810A4 (en) 2010-02-17
JP5098210B2 (ja) 2012-12-12
CN101171354B (zh) 2011-04-20
EP1878810A1 (en) 2008-01-16
KR20070116686A (ko) 2007-12-10
JP2006336105A (ja) 2006-12-14
EP1878810B1 (en) 2014-01-15
KR20100046068A (ko) 2010-05-04

Similar Documents

Publication Publication Date Title
US9023158B2 (en) Steel material superior in high temperature characteristics and toughness and method of production of same
US8048367B2 (en) High strength thick-gauge steel plate superior in weldability and having tensile strength of 780 MPA or more and method of production of same
US20060016526A1 (en) High-strength steel for welded structures excellent in high temperature strength and method of production of the same
EP2143814A1 (en) Steel material having excellent high-temperature strength and toughness, and method for production thereof
EP1878810B1 (en) Heat-resistant steel product and method for production thereof
WO2006022053A1 (ja) 溶接性および靭性に優れた引張り強さ５５０MPa級以上の高張力鋼材およびその製造方法
US8097096B2 (en) Fire resistant steel excellent in high temperature strength, toughness, and reheating embrittlement resistance and process for production of the same
US20090020190A1 (en) Fire Resistant High Strength Rolled Steel Material and Method of Production of The Same
KR100559095B1 (ko) 고강도 압연 ｈ 형 강의 제조방법
KR102089167B1 (ko) 형강 및 그 제조 방법
JP2776174B2 (ja) 高張力・高靱性微細ベイナイト鋼の製造法
JP3397271B2 (ja) 耐火用圧延形鋼およびその製造方法
JPH10204572A (ja) ７００℃耐火圧延形鋼およびその製造方法
JP5223295B2 (ja) 耐再熱脆化特性に優れた耐火ｈ形鋼及びその製造方法
JP3472017B2 (ja) 耐火圧延形鋼およびその製造方法
JP3426425B2 (ja) 耐火圧延形鋼用鋳片およびそれを素材とする耐火用圧延形鋼の製造方法
JP7297096B2 (ja) 形鋼およびその製造方法
KR101467030B1 (ko) 고강도 강판 제조 방법
JPH08283902A (ja) 耐火用圧延形鋼およびその製造方法
JPH0790473A (ja) 耐火用含酸化物鋳片及びその鋳片による耐火用圧延形鋼の製造方法
JPH10204573A (ja) ７００℃耐火圧延形鋼およびその製造方法
JP2006348378A (ja) 耐火性に優れた高強度極厚ｈ形鋼およびその製造方法
JPH0739606B2 (ja) 耐火性及び靱性の優れた圧延形鋼の製造方法
JPH06235021A (ja) 超音波探傷試験における内部特性の優れた耐火形鋼の製造方法
JPH08283901A (ja) 耐火用圧延形鋼およびその製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: NIPPON STEEL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:OKUMURA, TERUHISA;YAMAMOTO, KOHICHI;YOSHIDA, SUGURU;AND OTHERS;REEL/FRAME:020145/0733;SIGNING DATES FROM 20070913 TO 20070927

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION