US20090068446A1 - Layered structures with integral brazing materials - Google Patents

Layered structures with integral brazing materials Download PDF

Info

Publication number
US20090068446A1
US20090068446A1 US11/799,012 US79901207A US2009068446A1 US 20090068446 A1 US20090068446 A1 US 20090068446A1 US 79901207 A US79901207 A US 79901207A US 2009068446 A1 US2009068446 A1 US 2009068446A1
Authority
US
United States
Prior art keywords
brazing
major surface
layered structure
brazing layer
cover plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/799,012
Other languages
English (en)
Inventor
Christopher J. Bischof
Michael J. Minor
Paul M. Pellet
Jason E. Huxol
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Raytheon Technologies Corp
Original Assignee
United Technologies Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=39708874&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20090068446(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by United Technologies Corp filed Critical United Technologies Corp
Priority to US11/799,012 priority Critical patent/US20090068446A1/en
Assigned to UNITED TECHNOLOGIES CORPORATION reassignment UNITED TECHNOLOGIES CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BISCHOF, CHRISTOPHER J., HUXOL, JASON E., MINOR, MICHAEL J., PELLET, PAUL M.
Priority to EP08251540.4A priority patent/EP1987903B2/de
Publication of US20090068446A1 publication Critical patent/US20090068446A1/en
Priority to US13/233,418 priority patent/US8413877B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/0008—Soldering, e.g. brazing, or unsoldering specially adapted for particular articles or work
    • B23K1/0018—Brazing of turbine parts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/20—Preliminary treatment of work or areas to be soldered, e.g. in respect of a galvanic coating
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
    • F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or antivibration means on the blades or the members
    • F01D5/30—Fixing blades to rotors; Blade roots ; Blade spacers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2101/00—Articles made by soldering, welding or cutting
    • B23K2101/001—Turbines
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K2103/00—Materials to be soldered, welded or cut
    • B23K2103/18—Dissimilar materials
    • B23K2103/26—Alloys of Nickel and Cobalt and Chromium
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49316—Impeller making
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49316—Impeller making
    • Y10T29/49336—Blade making
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
    • Y10T428/264—Up to 3 mils
    • Y10T428/265—1 mil or less
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31678—Of metal

Definitions

  • the present invention relates to manufacturing components and processes for aerospace applications.
  • the present invention relates to gas turbine engine components and brazing operations for manufacturing gas turbine engine components.
  • many turbine engine components are secured together with brazing operations.
  • cover plates e.g., meter plates
  • the cover plates are tack welded onto the airfoil component, and then a brazing alloy is applied externally to fill the gaps between the cover plate and the airfoil component via capillary action.
  • the resulting covered airfoil component is then placed in a furnace to fuse the cover plate to the airfoil component with the brazing alloy.
  • the steps of applying the brazing alloy and the furnace treatment are typically repeated to ensure all of the gaps are adequately filled. This increases the time required to manufacture the covered airfoil components.
  • brazing alloy can flow into the hollow regions of the airfoil component, thereby requiring extra steps for applying and stopping of the brazing alloy.
  • Excess amounts of brazing alloy may be particularly problematic if the brazing alloy flows into critical areas of the airfoil components during the brazing operation. This may result in the need to recycle or scrap the airfoil component.
  • brazing operations require monitoring by personnel. Thus, brazing operations cannot be readily automated without the use of expensive monitoring systems to apply the brazing alloys where needed.
  • turbine engine components e.g., cover plates and airfoils
  • the present invention relates to a layered structure for use with a turbine engine component, and a method of securing the layered structure to the turbine engine component.
  • the layered structure includes a base structure and a brazing alloy layer secured to a major surface of the base structure.
  • the brazing alloy layer is applied to the major surface prior to positioning the layered structure in contact with the turbine engine airfoil component.
  • FIG. 1 is a bottom perspective view of a turbine blade root containing an airfoil cover plate being secured to a surface of the turbine blade root.
  • FIG. 2 is an expanded sectional view of section 2 - 2 taken in FIG. 1 , further illustrating the airfoil cover plate, which includes a brazing alloy layer secured to a base plate.
  • FIG. 3 is an alternative expanded sectional view of section 2 - 2 taken in FIG. 1 showing an alternative airfoil cover plate that includes a pair of brazing alloy layers secured to a base plate.
  • FIG. 4 is a flow diagram of a method of forming a covered airfoil component with an airfoil cover plate of the present invention.
  • FIG. 5 is a flow diagram of an alternative method of forming a covered airfoil component with an airfoil cover plate of the present invention.
  • FIG. 1 is a bottom perspective view of blade root 10 , which is a turbine blade root that is insertable into a dovetail slot (not shown) of a supporting rotor disk (not shown).
  • Blade root 10 is an example of a suitable turbine engine component for use with the present invention, and includes surface 12 , inlet apertures 14 , and cover plate 16 .
  • Surface 12 is a wall segment extending across the bottom of blade root 10 .
  • Inlet apertures 14 are openings within surface 12 for receiving cooling air during operation.
  • Cover plate 16 is disposed over surface 12 and inlet apertures 14 . When cover plate 16 is secured to surface 12 , cover plate 16 extends over inlet apertures 14 and functions as a meter plate for restricting the flow of air through inlet apertures 14 during operation.
  • Cover plate 16 is an airfoil cover plate that includes a pre-applied layer of a brazing material (not shown in FIG. 1 ), and is an example of a suitable layered structure of the present invention.
  • cover plate 16 may be secured to surface 12 via a brazing operation without requiring a separate step of applying a brazing alloy between surface 12 and cover plate 16 .
  • Cover plate 16 is positioned in contact with surface 12 at a desired location (e.g., over inlet apertures 14 ), tack welded in place, and then placed in a furnace to fuse cover plate 16 to surface 12 with the pre-applied brazing material. This reduces the time required to perform the brazing operation, and allows the brazing operation to be performed in an automated manner without requiring expensive monitoring systems.
  • FIG. 2 is an expanded sectional view of section 2 - 2 taken in FIG. 1 , further illustrating cover plate 16 .
  • cover plate 16 includes base plate 18 and brazing layer 20 , where base plate 18 is a metallic plate that includes opposing major surfaces 22 and 24 .
  • Base plate 18 may be cast or otherwise formed from a variety of different metals and alloys used in aerospace applications. Examples of suitable materials for base plate 18 include nickel, nickel-based alloys and superalloys, cobalt, cobalt-based alloys and superalloys, and combinations thereof; and may also include one or more additional materials such as carbon, titanium, chromium, niobium, hafnium, tantalum, molybdenum, tungsten, aluminum, and iron.
  • Examples of particularly suitable alloys for base plate 18 include those that meet Aerospace Materials Specification (AMS) 5536 and 5537.
  • suitable commercially available materials for base plate 18 include nickel-chromium-iron-molybdenum-based alloys under the trademark “HASTELLOY® X” (meet AMS 5536), and nickel-cobalt-chromium-tungsten-based alloys under the trademark “HAYNES 25TM (L605)” (meet AMS 5537), both from Haynes International, Inc., Kokomo, Ind.
  • Brazing layer 20 is a layer (or multiple layers) of a brazing material secured to surface 22 .
  • the brazing material for brazing layer 20 may also be derived from a variety of different metals and alloys used in aerospace applications. Examples of suitable brazing materials for brazing layer 20 include the suitable materials discussed above for base plate 18 . Examples of particularly suitable alloys for brazing layer 20 include those that meet AMS 4777 and 4778.
  • the brazing material for brazing layer 20 may be provided in a variety of media, such as powders, dispersions, slurries, pastes, foils, and tapes.
  • the brazing material is secured to surface 22 by coating the brazing material onto surface 22 , and then fusing (e.g., sintering) the brazing material to surface 22 , thereby forming brazing layer 20 .
  • the technique for coating the brazing material onto surface 22 may vary depending on the medium of the brazing material (e.g., powder). Examples of suitable coating techniques include deposition coating, electrostatic plating, plasma deposition, and lamination coating. Deposition coating processes are beneficial for brazing materials provided as powders, dispersions, and pastes.
  • a suitable deposition coating process involves physically depositing the brazing material onto an upward-facing surface 22 , and then drying the coating (for dispersions and pastes).
  • Electrostatic plating processes are beneficial for brazing materials provided as powders and dispersions.
  • a suitable electrostatic plating process involves placing base plate 18 in a plating solution containing the brazing material, and then inducing a current between a cathode (connected to base plate 18 ) and an anode, thereby causing ions of the brazing material to deposit onto surface 22 .
  • Suitable plasma deposition processes include corona treatment processes, and may involve initiating a plasma reaction adjacent to surface 22 , thereby allowing ions of the brazing material to deposit onto surface 22 .
  • Lamination coating processes are beneficial for brazing materials provided as dispersions and pastes. Suitable lamination coating processes include extrusion and knife coating techniques, where the coated cover plate may be subsequently dried.
  • the brazing material may be fused to base plate 18 by heating (e.g., furnace heating) cover plate 16 to a suitable temperature, and for a suitable duration, to interdiffuse at least a portion of the brazing material with the material of base plate 16 .
  • Suitable temperatures and durations for fusing the braze material to base plate 18 generally depend on the brazing material and the material of base plate 18 .
  • the brazing material is heated using an initial, high-temperature, melting step, which is followed by a longer, lower-temperature, diffusion step. Examples of suitable temperatures for the melting step range from about 1200° C. (about 2200° F.) to about 1260° C.
  • suitable temperatures for the diffusion step range from about 1100° C. (about 2000° F.) to about 1200° C. (about 2200° F.), and examples of suitable durations for the diffusion step range from about 1 hour to about 20 hours.
  • the amount of brazing material coated onto surface 22 generally determines the thickness of brazing layer 20 . Correspondingly, this also dictates the amount of brazing material that is available during a brazing operation to fuse cover plate 16 to surface 12 of blade root 10 (shown in FIG. 1 ). Thus, for a particular brazing operation, an appropriate amount of brazing material may be pre-applied to base plate 18 , as measured by the thickness of brazing layer 20 . This precludes the need to manually apply brazing materials to gaps between surface 12 and cover plate 16 , which is otherwise required to ensure that the amount of brazing material applied is neither deficient nor excessive.
  • Suitable thicknesses for the brazing layer may vary depending on the particular application. However, for base plate thicknesses ranging from about 0.25 millimeters (about 0.01 inches) to about 2.5 millimeters (about 0.1 inches), examples of suitable thicknesses for the brazing layer range from about 25 micrometers (about 0.001 inches) to about 250 micrometers (about 0.01 inches), with particularly suitable thicknesses ranging from about 25 micrometers (about 0.001 inches) to about 130 micrometers (about 0.005 inches).
  • the brazing layer thicknesses discussed herein refer to thicknesses obtained after the brazing material is secured (e.g., fused) to the base plate 18 .
  • Brazing layer 20 is desirably coated onto (and secured to) base plate 18 across the entire surface area of surface 22 . This allows brazing material to be available to fuse any point across surface 22 to an airfoil component. This also precludes the need to mask or otherwise pattern surface 22 to coat the brazing material at particular locations on surface 22 . In alternative embodiments, however, brazing layer 20 may be secured to base plate 18 over only one or more portions of the surface 22 , as individual needs may necessitate.
  • the thickness of brazing layer 20 may vary at different points across surface 22 (i.e., non-uniform thicknesses). This may be accomplished by varying the amount of brazing material that is coated onto surface 22 . This is beneficial for brazing operations that require different amounts of brazing material at different locations. For example, when cover plate 16 is positioned against surface 12 of blade root 10 , a first location between surface 12 and cover plate 16 may require a first amount of brazing material to form a suitable weld, while a second location may require a second amount of brazing material to form a suitable weld. Varying the thickness of brazing layer 20 allows the appropriate amounts of brazing material to be used for each location without causing an excess or deficiency of brazing material at the other locations.
  • FIG. 3 is an alternative expanded sectional view of section 2 - 2 taken in FIG. 1 , which includes cover plate 26 .
  • Cover plate 26 is an alternative to cover plate 16 (shown in FIG. 2 ), and includes base plate 28 and brazing layers 30 a and 30 b , where base plate 28 includes opposing major surfaces 32 and 34 .
  • Base plate 28 is metallic plate similar to base plate 18 (shown in FIG. 2 ), and may be cast or otherwise molded from the same materials discussed above for base plate 18 .
  • Brazing layers 30 a and 30 b are layers of brazing materials similar to brazing layer 20 (shown in FIG. 2 ), which are secured to surface 32 and 34 , respectively. Suitable brazing materials, methods of coating and fusing, and thicknesses for brazing layers 30 a and 30 b are the same as those discussed above for brazing layer 20 .
  • Cover plate 26 is beneficial for allowing an error-free application during a brazing operation. Because both major surfaces of base plate 28 (i.e., surfaces 32 and 34 ) are covered with brazing layers (i.e., brazing layers 30 a and 30 b ), either major surface of cover plate 26 can be fused to surface 12 (shown in FIG. 1 ). As such, the manufacturer is not required to determine which major surface of cover plate 26 needs to face surface 12 . This reduces the time and effort required to secure cover plate 26 to surface 12 .
  • cover plates i.e., cover plates 16 and 26
  • layered structures of the present invention may be used with any turbine engine component (e.g., turbine blades and vanes) that require brazed base structures (e.g., base plates 18 and 28 ) during manufacturing.
  • turbine engine component e.g., turbine blades and vanes
  • base structures e.g., base plates 18 and 28
  • cover plates i.e., cover plates 16 and 26
  • suitable turbine engine components that may be used with layered structures of the present invention include high pressure turbine blades, low pressure turbine blades, high pressure turbine vanes, low pressure turbine vanes, blade outer airseals, shrouds, and structural components such as bearing housings, ducts, and supports.
  • FIG. 4 is a flow diagram of method 36 for forming a turbine engine component with a layered structure of the present invention (e.g., cover plates 16 and 26 , shown in FIGS. 1-3 ).
  • method 36 includes steps 38 - 50 , and initially involves predetermining a required amount of brazing material that is needed for a particular brazing operation (step 38 ).
  • the required amount of brazing material is desirably an appropriate amount that reduces the risk of having an excess or deficiency of brazing material.
  • the predetermined amount of brazing material may be measured as a desired thickness of a brazing layer (or thicknesses for a non-uniformly thick layer).
  • the brazing material is then coated onto a major surface of an airfoil cover plate (step 40 ).
  • Suitable cover plate materials, brazing materials, and methods of coating are the same as those discussed above for base plate 18 and brazing layer 20 (shown in FIG. 2 ).
  • the amount of brazing material coated is desirably based on the intended thickness (or thicknesses) of the brazing layer, which is correspondingly based on the predetermined amount of brazing material to be used.
  • the brazing material is then fused to the surface of the cover plate to form a brazing layer (step 42 ).
  • Suitable techniques for fusing the brazing material to the surface of the cover plate include those discussed above for brazing layer 20 .
  • each major surface of the cover plate e.g., cover plate 26
  • the cover plate is then positioned against a surface of an airfoil component such that the brazing layer contacts the surface of the airfoil component (step 44 ).
  • the cover plate is then tack welded or otherwise adhered to the surface of the airfoil component to prevent the cover plate from moving during the brazing operation (step 46 ).
  • the covered airfoil component is then heated to fuse the cover plate to the surface of the airfoil component with the brazing layer (i.e., a brazing operation) (step 48 ).
  • the heating causes the brazing material of the brazing layer to interdiffuse into the surface of the airfoil component.
  • the brazing operation may be performed in a furnace or other similar heating system. Suitable temperatures and durations for the brazing operation generally depend on the brazing material and the material and the material of the airfoil component. Examples of suitable temperatures and durations for the brazing operation includes those discussed above (e.g., the melting and diffusion steps).
  • the covered airfoil component is then cooled, thereby forming a brazed weld between the cover plate and the airfoil component (step 50 ).
  • the use of the pre-applied brazing layer precludes the need for applying a brazing material between the cover plate and the surface of the airfoil component.
  • the brazing layer provides an appropriate amount of brazing material to create a brazed weld that substantially fills the gaps between the cover plate and the surface of the airfoil component, while also reducing the amounts of excess brazing material. This accordingly reduces the time required to perform the brazing operation, and allows the brazing operation to be performed in an automated manner.
  • FIG. 5 is a flow diagram of method 52 , which is an alternative to method 36 (shown in FIG. 4 ).
  • method 52 involves the use of a master sheet that is separable into multiple cover plates, thereby allowing brazing layers to be formed on multiple cover plates with a single coating operation.
  • Method 52 includes steps 54 - 68 , and initially involves predetermining a required amount of brazing material that is needed for a particular brazing operation (step 54 ).
  • the predetermined amount of brazing material may be measured as a desired thickness of a brazing layer (or thicknesses for a non-uniformly thick layer).
  • the multiple cover plates are intended for a common purpose (e.g., all of the cover plates from the master sheet will be used in the same manner, such as meter plates).
  • the required amount of brazing material may be the same for each cover plate, thereby allowing a uniform thickness to be used over the entire master sheet.
  • the multiple cover plates are intended for different purposes.
  • the required amount of brazing material may be different for each cover plate. As such, the intended thickness of the brazing layer may vary over the surface area of the master sheet.
  • the brazing material is then coated onto a major surface of the master sheet (step 56 ).
  • Suitable master sheet materials, brazing materials, and methods of coating are the same as those discussed above for base plate 18 and brazing layer 20 (shown in FIG. 2 ).
  • the amount of brazing material coated is desirably based on the intended thickness (or thicknesses) of the brazing layer, which is correspondingly based on the predetermined amount of brazing material to be used.
  • the brazing material is then fused to the surface of the master sheet to form a brazing layer (step 58 ).
  • Suitable techniques for fusing the brazing material to the surface of the master sheet include those discussed above for brazing layer 20 .
  • each major surface of the master sheet may be coated with brazing material to form a pair of brazing layers, similar to that discussed above for meter plate 26 (shown in FIG. 3 ).
  • the master sheet is then separated into multiple cover plates, where each cover plate includes at least one brazing layer (step 60 ).
  • the master sheet may be separated into multiple cover plates using a variety of techniques, such as laser cutting, waterjet cutting, and stamping operations. As discussed above, the use of the master sheet allows a single coating operation to be used to apply brazing layers onto multiple cover sheets.
  • One of the cut-out cover plates is then positioned against a surface of an airfoil component such that the brazing layer contacts the surface of the airfoil component (step 62 ).
  • the cover plate is then tack welded or otherwise adhered to the surface of the airfoil component to prevent the cover plate from moving during the brazing operation (step 64 ).
  • the covered airfoil component is then heated (step 66 ) and cooled (step 68 ), thereby forming a brazed weld between the cover plate and the surface of the airfoil component.
  • Steps 62 - 68 may then be repeated for each cover sheet cut-out of the master sheet (as represented by arrow 70 ). Accordingly, a single coating operation can be used to apply brazing layers on multiple cover plates. This precludes the need to manually apply brazing materials during each brazing operation, thereby increasing manufacturing throughput.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Turbine Rotor Nozzle Sealing (AREA)
US11/799,012 2007-04-30 2007-04-30 Layered structures with integral brazing materials Abandoned US20090068446A1 (en)

Priority Applications (3)

Application Number Priority Date Filing Date Title
US11/799,012 US20090068446A1 (en) 2007-04-30 2007-04-30 Layered structures with integral brazing materials
EP08251540.4A EP1987903B2 (de) 2007-04-30 2008-04-28 Schichtstrukturen mit integrierten Lötmaterialien
US13/233,418 US8413877B2 (en) 2007-04-30 2011-09-15 Layered structures with integral brazing materials

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US11/799,012 US20090068446A1 (en) 2007-04-30 2007-04-30 Layered structures with integral brazing materials

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/233,418 Division US8413877B2 (en) 2007-04-30 2011-09-15 Layered structures with integral brazing materials

Publications (1)

Publication Number Publication Date
US20090068446A1 true US20090068446A1 (en) 2009-03-12

Family

ID=39708874

Family Applications (2)

Application Number Title Priority Date Filing Date
US11/799,012 Abandoned US20090068446A1 (en) 2007-04-30 2007-04-30 Layered structures with integral brazing materials
US13/233,418 Active US8413877B2 (en) 2007-04-30 2011-09-15 Layered structures with integral brazing materials

Family Applications After (1)

Application Number Title Priority Date Filing Date
US13/233,418 Active US8413877B2 (en) 2007-04-30 2011-09-15 Layered structures with integral brazing materials

Country Status (2)

Country Link
US (2) US20090068446A1 (de)
EP (1) EP1987903B2 (de)

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100183930A1 (en) * 2009-01-20 2010-07-22 Adaptive Materials, Inc. Method for controlling a water based fuel reformer
US20110189587A1 (en) * 2010-02-01 2011-08-04 Adaptive Materials, Inc. Interconnect Member for Fuel Cell
US20110189572A1 (en) * 2009-01-30 2011-08-04 Adaptive Materials, Inc. Fuel cell system with flame protection member
US20110189578A1 (en) * 2010-02-01 2011-08-04 Adaptive Materials, Inc. Fuel cell system including a resilient manifold interconnecting member
US20130174659A1 (en) * 2012-01-11 2013-07-11 Hamilton Sundstrand Corporation Speed sensor module
US20130228322A1 (en) * 2011-01-20 2013-09-05 Toyota Jidosha Kabushiki Kaisha Brazing method and brazed structure
US20130256388A1 (en) * 2009-06-30 2013-10-03 Adaptive Materials, Inc. Method of forming a solid oxide tube coupled to a current collector
US8796888B2 (en) 2010-07-07 2014-08-05 Adaptive Materials, Inc. Wearable power management system
US20150352673A1 (en) * 2013-03-15 2015-12-10 Siemens Energy, Inc. Component repair using brazed surface textured superalloy foil
JP2016030263A (ja) * 2014-07-25 2016-03-07 三菱重工業株式会社 部材接合方法及び部材接合システム
EP3231548A1 (de) * 2016-04-14 2017-10-18 Siemens Energy, Inc. Verfahren zum hartlöten breiter spalten in superlegierungen auf nickelbasis ohne wesentliche verschlechterung der eigenschaften
US10174414B2 (en) * 2017-02-16 2019-01-08 General Electric Company Manufactured article and method

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9925623B2 (en) 2012-09-28 2018-03-27 United Technologies Corporation Case assembly and method
ES2710226T3 (es) 2013-10-30 2019-04-23 United Technologies Corp Reprocesamiento por soldadura por deposición láser de polvo para piezas fundidas de níquel soldables sin fusión del metal base pertenecientes a motores de turbina de gas
EP3062953B1 (de) 2013-10-30 2023-05-17 Raytheon Technologies Corporation Schweissnahtnachbesserung mit laserpulverauftragung für einen gasturbinenmotor mit nicht-schmelzschweissbaren nickelgussstücken
US20150308449A1 (en) * 2014-03-11 2015-10-29 United Technologies Corporation Gas turbine engine component with brazed cover
SE541917C2 (en) * 2018-01-16 2020-01-07 Swep Int Ab Method for producing a brazed plate heat exchanger
US11571762B2 (en) 2019-11-15 2023-02-07 Rolls-Royce North American Technologies Inc. Printing method to selectively deposit braze powders at one or more predetermined locations on a surface
US11420279B2 (en) 2019-11-15 2022-08-23 Rolls-Royce Corporation Method of selectively bonding braze powders to a surface
US11298768B2 (en) * 2019-11-15 2022-04-12 Rolls-Royce Corporation Method of preparing a surface for diffusion bonding and method of diffusion bonding
US11565336B2 (en) 2019-11-15 2023-01-31 Rolls-Royce North American Technologies Inc. Method of selectively bonding braze powders to a surface

Citations (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4026677A (en) * 1975-02-13 1977-05-31 United Technologies Corporation High temperature titanium braze foil
US4034454A (en) * 1975-02-13 1977-07-12 United Technologies Corporation Composite foil preform for high temperature brazing
US4034906A (en) * 1975-02-13 1977-07-12 United Technologies Corporation Diffusion bonding utilizing eutectic fugitive liquid phase
US4795313A (en) * 1986-05-28 1989-01-03 Alsthom Protective tip for a titanium blade and a method of brazing such a tip
US5068084A (en) * 1986-01-02 1991-11-26 United Technologies Corporation Columnar grain superalloy articles
US5284290A (en) * 1993-04-23 1994-02-08 The United States Of America As Represented By The Adminstrator Of The National Aeronautics And Space Administration Fusion welding with self-generated filler metal
US5318406A (en) * 1992-11-02 1994-06-07 General Electric Company Multipart gas turbine blade
US5464146A (en) * 1994-09-29 1995-11-07 Ford Motor Company Thin film brazing of aluminum shapes
US5788823A (en) * 1996-07-23 1998-08-04 Howmet Research Corporation Platinum modified aluminide diffusion coating and method
US5989733A (en) * 1996-07-23 1999-11-23 Howmet Research Corporation Active element modified platinum aluminide diffusion coating and CVD coating method
US6129991A (en) * 1994-10-28 2000-10-10 Howmet Research Corporation Aluminide/MCrAlY coating system for superalloys
US6530971B1 (en) * 2001-01-29 2003-03-11 General Electric Company Nickel-base braze material and braze repair method
US6531005B1 (en) * 2000-11-17 2003-03-11 General Electric Co. Heat treatment of weld repaired gas turbine engine components
US20030200835A1 (en) * 2002-04-02 2003-10-30 Snecma Services Diffusion-brazing filler powder for parts made of an alloy based on nickel, cobalt or iron
US6685431B2 (en) * 2001-10-24 2004-02-03 United Technologies Corporation Method for repairing a turbine vane
US20040050913A1 (en) * 2002-01-24 2004-03-18 Siemens Westinghouse Power Corporation High strength diffusion brazing utilizing nano-powders
US20040131877A1 (en) * 1999-05-03 2004-07-08 Hasz Wayne Charles Article having turbulation and method of providing turbulation on an article
US20040169063A1 (en) * 2000-12-22 2004-09-02 Triumph Brands, Inc. Method of diffusion bonding superalloy laminates
US6921014B2 (en) * 2002-05-07 2005-07-26 General Electric Company Method for forming a channel on the surface of a metal substrate
US20060042082A1 (en) * 2004-08-26 2006-03-02 Michael Minor Turbine component restoration using cathodic ARC/LPPS
US20060049236A1 (en) * 2004-08-26 2006-03-09 Michael Minor Turbine component crack repair using cathodic arc and/or low pressure plasma spraying and hip
US7051435B1 (en) * 2003-06-13 2006-05-30 General Electric Company Process for repairing turbine components
US7073247B2 (en) * 2003-04-30 2006-07-11 General Electric Company Method of brazing a liquid-cooled stator bar
US20060242816A1 (en) * 2005-04-29 2006-11-02 Pratt & Whitney Canada Corp. Method of manufacturing thin-walled structures
US20070087208A1 (en) * 2005-10-18 2007-04-19 United Technologies Corporation Sacrificial coating for fluoride ion cleaning

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5847270B2 (ja) † 1978-07-21 1983-10-21 富士電機株式会社 ろう付け品の製造方法
GB2198667B (en) * 1986-12-20 1991-08-07 Refurbished Turbine Components Parts for and methods of repairing machines
JPH01157794A (ja) † 1987-09-09 1989-06-21 Nippon Denso Co Ltd ろう付用アルミニウム素材，その製法及びアルミニウム合金製熱交換器の製法
DE68906594T2 (de) † 1988-04-25 1993-08-26 United Technologies Corp Staubabscheider fuer eine luftgekuehlte schaufel.
GB2227190B (en) * 1989-01-24 1992-12-16 Refurbished Turbine Components Turbine blade repair
DE4310896C1 (de) * 1993-04-02 1994-03-24 Thyssen Industrie Verfahren zum Herstellen von verschleißfesten Kanten an Turbinenschaufeln
US6199746B1 (en) * 1999-08-02 2001-03-13 General Electric Company Method for preparing superalloy castings using a metallurgically bonded tapered plug
DE10008257A1 (de) * 2000-02-23 2001-08-30 Alstom Power Schweiz Ag Baden Verfahren zur Reparatur einer Gasturbinenkomponente
US6454156B1 (en) * 2000-06-23 2002-09-24 Siemens Westinghouse Power Corporation Method for closing core printout holes in superalloy gas turbine blades
DE10065406A1 (de) * 2000-12-27 2002-07-04 Alstom Switzerland Ltd Verfahren zum Reparieren von Schadstellen an einem Metallbauteil
FR2823794B1 (fr) † 2001-04-19 2003-07-11 Snecma Moteurs Aube rapportee et refroidie pour turbine
US7063250B2 (en) * 2001-05-31 2006-06-20 Mitsubishi Heavy Industries, Ltd. Coating forming method and coating forming material, and abrasive coating forming sheet
US20030034379A1 (en) † 2001-08-16 2003-02-20 Jackson Melvin Robert Method of repairing superalloy directional castings
US6575702B2 (en) * 2001-10-22 2003-06-10 General Electric Company Airfoils with improved strength and manufacture and repair thereof
EP1312437A1 (de) * 2001-11-19 2003-05-21 ALSTOM (Switzerland) Ltd Verfahren zum Reparieren eines Risses
SE525660C2 (sv) † 2002-06-12 2005-03-29 Saab Ab Metod för fixering av metallskum mot en metallplåt
US7017793B2 (en) † 2003-06-26 2006-03-28 United Technologies Corporation Repair process
US7343676B2 (en) † 2004-01-29 2008-03-18 United Technologies Corporation Method of restoring dimensions of an airfoil and preform for performing same
US7331755B2 (en) * 2004-05-25 2008-02-19 General Electric Company Method for coating gas turbine engine components
US7303112B2 (en) * 2004-10-29 2007-12-04 United Technologies Corporation Repair of braze joint and article repaired
JP4548829B2 (ja) * 2004-11-16 2010-09-22 住友軽金属工業株式会社 アルミニウム熱交換器
JP4507942B2 (ja) * 2005-03-28 2010-07-21 日立電線株式会社 ろう付け用クラッド材及びそれを用いたろう付け製品
DE102005030848A1 (de) * 2005-07-01 2007-01-11 Mtu Aero Engines Gmbh Verfahren zum Herstellen einer Schaufelspitzenpanzerung
US7293688B2 (en) * 2005-11-14 2007-11-13 General Electric Company Gold/nickel/copper/aluminum/silver brazing alloys for brazing WC-Co to titanium alloys
US20090286102A1 (en) * 2008-05-15 2009-11-19 Tubine Overhaul Services Pte Ltd. Induced capillary action brazing using metallic foam matrix
US8366386B2 (en) * 2009-01-27 2013-02-05 United Technologies Corporation Method and assembly for gas turbine engine airfoils with protective coating
CN102581573B (zh) † 2012-03-19 2014-01-22 沈阳航新金属复合科技有限公司 一种热喷涂预置钎料热轧制备复合板的方法

Patent Citations (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4026677A (en) * 1975-02-13 1977-05-31 United Technologies Corporation High temperature titanium braze foil
US4034454A (en) * 1975-02-13 1977-07-12 United Technologies Corporation Composite foil preform for high temperature brazing
US4034906A (en) * 1975-02-13 1977-07-12 United Technologies Corporation Diffusion bonding utilizing eutectic fugitive liquid phase
US5068084A (en) * 1986-01-02 1991-11-26 United Technologies Corporation Columnar grain superalloy articles
US4795313A (en) * 1986-05-28 1989-01-03 Alsthom Protective tip for a titanium blade and a method of brazing such a tip
US5318406A (en) * 1992-11-02 1994-06-07 General Electric Company Multipart gas turbine blade
US5284290A (en) * 1993-04-23 1994-02-08 The United States Of America As Represented By The Adminstrator Of The National Aeronautics And Space Administration Fusion welding with self-generated filler metal
US5464146A (en) * 1994-09-29 1995-11-07 Ford Motor Company Thin film brazing of aluminum shapes
US6129991A (en) * 1994-10-28 2000-10-10 Howmet Research Corporation Aluminide/MCrAlY coating system for superalloys
US5788823A (en) * 1996-07-23 1998-08-04 Howmet Research Corporation Platinum modified aluminide diffusion coating and method
US5989733A (en) * 1996-07-23 1999-11-23 Howmet Research Corporation Active element modified platinum aluminide diffusion coating and CVD coating method
US20040131877A1 (en) * 1999-05-03 2004-07-08 Hasz Wayne Charles Article having turbulation and method of providing turbulation on an article
US6531005B1 (en) * 2000-11-17 2003-03-11 General Electric Co. Heat treatment of weld repaired gas turbine engine components
US20040169063A1 (en) * 2000-12-22 2004-09-02 Triumph Brands, Inc. Method of diffusion bonding superalloy laminates
US6530971B1 (en) * 2001-01-29 2003-03-11 General Electric Company Nickel-base braze material and braze repair method
US6685431B2 (en) * 2001-10-24 2004-02-03 United Technologies Corporation Method for repairing a turbine vane
US20040050913A1 (en) * 2002-01-24 2004-03-18 Siemens Westinghouse Power Corporation High strength diffusion brazing utilizing nano-powders
US20030200835A1 (en) * 2002-04-02 2003-10-30 Snecma Services Diffusion-brazing filler powder for parts made of an alloy based on nickel, cobalt or iron
US6921014B2 (en) * 2002-05-07 2005-07-26 General Electric Company Method for forming a channel on the surface of a metal substrate
US7073247B2 (en) * 2003-04-30 2006-07-11 General Electric Company Method of brazing a liquid-cooled stator bar
US7051435B1 (en) * 2003-06-13 2006-05-30 General Electric Company Process for repairing turbine components
US20060042082A1 (en) * 2004-08-26 2006-03-02 Michael Minor Turbine component restoration using cathodic ARC/LPPS
US20060049236A1 (en) * 2004-08-26 2006-03-09 Michael Minor Turbine component crack repair using cathodic arc and/or low pressure plasma spraying and hip
US20060242816A1 (en) * 2005-04-29 2006-11-02 Pratt & Whitney Canada Corp. Method of manufacturing thin-walled structures
US20070087208A1 (en) * 2005-10-18 2007-04-19 United Technologies Corporation Sacrificial coating for fluoride ion cleaning

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8409760B2 (en) 2009-01-20 2013-04-02 Adaptive Materials, Inc. Method for controlling a water based fuel reformer
US20100183930A1 (en) * 2009-01-20 2010-07-22 Adaptive Materials, Inc. Method for controlling a water based fuel reformer
US8936888B2 (en) 2009-01-30 2015-01-20 Adaptive Materials, Inc. Fuel cell system with flame protection member
US20110189572A1 (en) * 2009-01-30 2011-08-04 Adaptive Materials, Inc. Fuel cell system with flame protection member
US20130256388A1 (en) * 2009-06-30 2013-10-03 Adaptive Materials, Inc. Method of forming a solid oxide tube coupled to a current collector
US20110189587A1 (en) * 2010-02-01 2011-08-04 Adaptive Materials, Inc. Interconnect Member for Fuel Cell
US20110189578A1 (en) * 2010-02-01 2011-08-04 Adaptive Materials, Inc. Fuel cell system including a resilient manifold interconnecting member
US8796888B2 (en) 2010-07-07 2014-08-05 Adaptive Materials, Inc. Wearable power management system
US20130228322A1 (en) * 2011-01-20 2013-09-05 Toyota Jidosha Kabushiki Kaisha Brazing method and brazed structure
US9238275B2 (en) * 2011-01-20 2016-01-19 Toyota Jidosha Kabushiki Kaisha Brazing method and brazed structure
US20130174659A1 (en) * 2012-01-11 2013-07-11 Hamilton Sundstrand Corporation Speed sensor module
US8763458B2 (en) * 2012-01-11 2014-07-01 Hamilton Sundstrand Corporation Speed sensor module
US20150352673A1 (en) * 2013-03-15 2015-12-10 Siemens Energy, Inc. Component repair using brazed surface textured superalloy foil
US9782862B2 (en) 2013-03-15 2017-10-10 Siemens Energy, Inc. Component repair using brazed surface textured superalloy foil
JP2016030263A (ja) * 2014-07-25 2016-03-07 三菱重工業株式会社 部材接合方法及び部材接合システム
US10105777B2 (en) 2014-07-25 2018-10-23 Mitsubishi Heavy Industries, Ltd. Joining method and joining system
EP3231548A1 (de) * 2016-04-14 2017-10-18 Siemens Energy, Inc. Verfahren zum hartlöten breiter spalten in superlegierungen auf nickelbasis ohne wesentliche verschlechterung der eigenschaften
CN107414224A (zh) * 2016-04-14 2017-12-01 西门子能源有限公司 硬钎焊镍基超级合金中的宽间隙而不显著劣化特性的方法
US9839980B2 (en) 2016-04-14 2017-12-12 Siemens Energy, Inc. Methods of brazing wide gaps in nickel base superalloys without substantial degradation of properties
US10174414B2 (en) * 2017-02-16 2019-01-08 General Electric Company Manufactured article and method

Also Published As

Publication number Publication date
EP1987903A2 (de) 2008-11-05
US20120000967A1 (en) 2012-01-05
EP1987903A3 (de) 2009-08-05
EP1987903B1 (de) 2015-11-11
US8413877B2 (en) 2013-04-09
EP1987903B2 (de) 2022-07-27

Similar Documents

Publication Publication Date Title
US8413877B2 (en) Layered structures with integral brazing materials
US5836075A (en) Process for forming combustion turbine components by transient liquid phase bonding
US9926785B2 (en) Method for reconditioning a hot gas path part of a gas turbine
US6609894B2 (en) Airfoils with improved oxidation resistance and manufacture and repair thereof
EP1049561B1 (de) Turbinenbauteile mit dünnen folien die auf ein substrat aus superlegierung aufgebracht sind
EP1378583B1 (de) Herstellungsverfahren für einen Hohlkanal auf der Oberfläche eines metallischen Substrats, und verwandte Artikel
EP1759799B1 (de) Verfahren zur Formgebung oder Herstellung von Turbinenmotorelementen
KR20030095330A (ko) 용접수리용 난용성 금속 받침물질
EP2182092B1 (de) Verfahren zum Reparieren einer Aluminid-Beschichtung auf einem Artikel
JP2014177938A (ja) マイクロ冷却レーザ堆積材料層を備えた構成要素並びにその製造方法
US7093335B2 (en) Coated article and method for repairing a coated surface
US6895650B2 (en) Process for producing a spatially shaped carrier layer
US9782862B2 (en) Component repair using brazed surface textured superalloy foil
US4208222A (en) In situ interlayer formation for transient liquid phase diffusion bonding
US6426152B1 (en) Salvaged castings and methods of salvaging castings with defective cast cooling bumps
EP3277930B1 (de) Schaufelsegment für eine gasturbine
CN102762778B (zh) 用于电解沉积涂层的方法和组件
US5968299A (en) Foil coating on a local region of a component and its method of production and installation
EP3825054B1 (de) Verfahren zur vorbereitung einer oberfläche zum diffusionsschweissen und diffusionsschweissverfahren
US11504774B2 (en) Manufacturing method for hard-to-weld materials
CN110630342A (zh) 具有用于隔热的捕获涂层的特征的涡轮机构件
JPS60234742A (ja) 耐食・耐摩耗用薄板材料の製造法

Legal Events

Date Code Title Description
AS Assignment

Owner name: UNITED TECHNOLOGIES CORPORATION, CONNECTICUT

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BISCHOF, CHRISTOPHER J.;MINOR, MICHAEL J.;PELLET, PAUL M.;AND OTHERS;REEL/FRAME:019313/0820

Effective date: 20070430

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION