US20090053656A1 - Process to form a mold of nanoimprint technique for making diffraction grating for DFB-LD - Google Patents
Process to form a mold of nanoimprint technique for making diffraction grating for DFB-LD Download PDFInfo
- Publication number
- US20090053656A1 US20090053656A1 US12/222,671 US22267108A US2009053656A1 US 20090053656 A1 US20090053656 A1 US 20090053656A1 US 22267108 A US22267108 A US 22267108A US 2009053656 A1 US2009053656 A1 US 2009053656A1
- Authority
- US
- United States
- Prior art keywords
- mold
- resist
- pattern
- substrate
- diffraction grating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A process using the nanoimprint technique to form the diffraction grating for the DFB-LD is disclosed. The process includes (a) coating a resist for the EB exposure on a dummy substrate, (b) irradiating the resist as varying the acceleration voltage, (c) forming a resist pattern by developing the irradiated resist, (d) coating the SOG film on the patterned resist, (e) attaching the silica substrate on the cured SOG film, and (f) removing the dummy substrate with the resist from the SOG film and the silica substrate. Using the mold thus formed, the diffraction grating for the DFB-LD is formed by the nanoimprint technique.
Description
- 1. Field of the Invention
- The present invention related to a process to form a mold, for the nanoimprint technique, the mold having a pattern for the diffraction grating, a process to form the diffraction grating and a process to form the distributed feedback laser diode (hereafter denoted as DFB-LD) with the diffraction grating.
- 2. Related Prior Art
- Conventionally, the diffraction grating for the DFB-LD has been formed by, after preparing the resist pattern by the interference lithography or the electron beam lithography (EB lithography), etching the semiconductor material with resist pattern as the etching mask. Recently, another technique to form the diffraction grating has been known in which a mold having the grating pattern is pressed against a resin to transfer the grating pattern on this resin, which is often called as the nanoimprint technique. Prior documents, such as the United States Patent U.S. Pat. No. 7,165,957, and Journal of Vacuum Science and Technology, vol. B14(6), pp. 4129-4133 (1996), have disclosed the nanoimprint technique.
- Because the interference lithography, or the EB lithography, is inevitable to form the patterns with an uniform depth, that is, the aspect ratio of the obtained patterns is uniform within a wafer; accordingly, it is quite hard to modify the depth of the diffraction grating in a limited portion thereof or to control the depth of the resist patterns intentionally so as to compensate the inhomogeneous etching rate within the wafer. Moreover, it is further difficult to grade the duty ratio of the patterns optionally within the wafer. Here, the duty ratio of the pattern means the ratio of the width of the rib against the width of the valley of the pattern. It is also hard or at least necessary for a long time to distribute the pitch of the patterns optionally in the wafer. Thus, the conventional technique of the interference lithography fundamentally limits to the uniform resist patterns within the wafer. That is, only one type of the patterns may be realized in the single wafer by the conventional technique.
- An aspect of the present invention relates to a process to form a mold for the nanoimprint technique. This mold is used to form the diffraction grating for the DFB-LD. The process includes: (a) coating a dummy substrate with a photo resist for the electron beam lithography; (b) irradiating the photo resist by electron beams as varying the acceleration voltage of the electron beams; (c) developing the irradiated resist to form a resist pattern; (d) coating this resist pattern with a mold resin, which is to be converted into the mold; (e) curing the mold resin; and (f) removing the dummy substrate and the resist pattern from the cured mold resin. The mold resin may be a spin on glass (SOG).
- Because the irradiation of the electron beams are carried out as varying its acceleration voltage, the resultant resist pattern shows a non-uniform dimensions. For instance, the depth (or the height), the duty ratio, the aspect ratio, the pitch and so on of the pattern are varied within the dummy substrate. Accordingly, the diffraction grating obtained by using thus prepared mold shows the non-uniform characteristic.
- Another process to form the mold according to the present invention includes: (a)coating a substrate with a first photo resist; (b) irradiating a first limited region of this first photo resist by the electron beams; (c) developing the irradiated first photo resist to prepare a first resist pattern; (d) etching the substrate under a first condition with the patterned first photo resist as the etching mask to form a first pattern on the substrate and removing the patterned first photo resist after the etching; (e) coating the substrate with a second photo resist for the electron beam lithography; (f) irradiating a second limited region, different from the first limited region, of the second photo resist by the electron beams; (g) developing the irradiated second photo resist to prepare a second resist pattern; and (h) etching the substrate under a second condition different from the first condition with the patterned second photo resist as the etching mask to form a second pattern on the substrate and removing the patterned second photo resist after the etching. The first pattern and the second pattern each formed in the substrate constitute at least a portion of patterns provided in the mold.
- Still another process to form the mold according to the present invention includes: (a) coating a substrate with a photosensitive film; (b) irradiating the photosensitive film by electron beams as varying the acceleration voltage of the electron beams; and (c) developing the irradiated photosensitive film to form a pattern for the diffraction grating. The photosensitive film may be a spin on glass material.
-
FIGS. 1A to 1C schematically illustrate the first process to form the mold according to the invention; -
FIGS. 2A to 2C schematically illustrate the first process performed subsequent toFIG. 1C ; -
FIG. 3 images a mold viewed from a side where the patterns are formed; -
FIGS. 4A to 4D schematically illustrate the second process to form the mold according to the invention; -
FIGS. 5A to 5C schematically illustrate the second process performed subsequent toFIG. 4D ; -
FIGS. 6A to 6C schematically illustrate the third process to form the mold according to the invention; -
FIGS. 7A to 7C schematically illustrate a process to form the diffraction grating using the mold formed by any one of first to third processes; -
FIGS. 8A to 8C schematically illustrate a process to form the diffraction grating performed subsequent toFIG. 7C ; -
FIGS. 9A to 9C schematically illustrate a process to form the DFB-LD that provides the diffraction grating formed by the process illustrated inFIGS. 7A to 8C ; and -
FIG. 10 is a perspective view, a portion of which is broken to indicate the layer stacking, of the DFB-LD formed by the process shown inFIGS. 9A to 9C . - Next, preferred embodiments according to the present invention will be described as referring to accompanying drawings. In the description of the drawings, the same elements will be referred by the same numerals or the same symbols without overlapping explanations. Further, dimensions illustrated in the drawings do not always reflect the practical one or that of the descriptions. First, a method to prepare the mold will be described.
- (First Method to Prepare the Mold)
-
FIGS. 1A and 2C illustrate a process to prepare themold 10 according to the first method. As illustrated inFIG. 1A , the process coats a photo resist 102 for the electron beam (hereafter denoted as EB) lithography on thedummy substrate 101, typically a silicon substrate. Thephoto resist 102 may be a positive type photo resist such as ZEP-520 provided from Zeon Corp. - Next, the electron beam EB irradiates on the
surface 102 a of the photo resist 102 as varying the acceleration voltage, the exposure dose, and the scanning patterns thereof (FIG. 1B ). InFIG. 1B , the length of the arrowhead corresponds to the acceleration voltage, while, the spans between the arrowheads denotes the scanning width of the electron beams. - Developing the photo resist 102, we can obtain the resist
patterns 103 as illustrated inFIG. 1C . Because the irradiation of the electron beam is carried out as varying the acceleration voltage, the exposure dose and the scanning patterns, which varies the irradiation depth and area of the electron beam, the resultant patterns obtained in the photo resist 103 varies its depth, an aspect ratio, a pattern pitch, and so on. - Next, the process coats the spin-on-glass (hereafter denoted as SOG)
film 104 on the patterned photo resist 103, as illustrated inFIG. 2A . ThisSOG film 104 will be converted to thepattern 10A of themold 10, which will be described later. - Next, the
silica substrate 106 is attached to theSOG film 104 with an adhesive 105 after theSOG film 104 is cured (FIG. 2B ). Thissilica substrate 106 will be thesubstrate 10B of themold 10. Subsequently, thedummy substrate 101 and the patterned resist 103 are removed; thus, the mold with thepattern 10A of theSOG film 104 on thesilica substrate 10B is completed as illustrated inFIG. 2C . -
FIG. 3 shows themold 10 viewed from the side where thepattern 10A is formed. Themold 10 provides a plurality of regions each having particular patterns specific to the region, for example, patterns in the regions, A to D, provide particular aspect ratio of 1.0 to 2.5 with a step of 0.5, respectively. When the irradiation of the electron beams is carried out as varying its acceleration voltage, the depths (or the height) and the duty ratios of patterns in each region, A to D, are different from each other. Or, when the irradiation is carried out as varying the pitch of the patterns, the pitch of the patterns in respective sections, A to D, shows the different pitch. Here, the aspect ratio means a ratio of the pattern width to the depth, the duty ratio means a ratio of the pattern width to the pattern span, and the pitch means the distance from one pattern in the top thereof to the next pattern also in the top thereof. - According to the process thus described, the
patterns 10A formed on themold 10 varies their depth, the duty ratio, the pitch and so on reflecting the acceleration voltage of the electron beams, the exposure dose and the scanning patterns. Accordingly, using thismold 10 with various patterns of the depth, the duty ratio, the pitch and so on for forming the diffraction grating for the DFB-LD, diffraction gratings with various configurations may be obtained within a semiconductor wafer. - (Second Method to Form Mold)
-
FIGS. 4A to 5C show a process to form amold 11 according to one embodiment of the invention. - First, the process coats a photo resist 112 for the electron beam lithography on the
substrate 111, typically a silicon substrate, as illustrated inFIG. 4A . The photo resist 112 may be a positive type photo resist such as ZEP-520 provided from Zeon Corp. - Next, the electron beam EB irradiates on the
surface 112 a of the photo resist 112. In this process, the acceleration voltage and the exposure dose of the electron beam may be varied as those of the first embodiment described above. Further, the process may irradiate the electron beam such that the scanning patterns or the pitch thereof has a predetermined distribution. Developing the irradiated resist 112, we obtain the first resistpattern 113 as shown inFIG. 4C . - Carrying out the first etching of the
substrate 111 using the first resistpattern 113 as the etching mask and subsequently removing the resist 112, afirst pattern 111 a may be obtained with the depth of dl on thesubstrate 111. The portion except for the region P1 leaves no patterns because it is covered with the resist 112. - Next, the process coats the second resist 114 on the
substrate 111 with thefirst pattern 111 a again as illustrate inFIG. 5A . This second resist 114 may be the same with the first resist 112. Subsequently, the process irradiates the electron beams on a region P2 except for the first region P1. In this process, the acceleration voltage and the exposure dose of the electron beams may be varied in each irradiation, or the patterns to be irradiated may have a preset distribution in the shape thereof. - Developing the second resist 114, the
second pattern 115 as illustrated inFIG. 5B may be obtained. Etching thesubstrate 111 with the second resist 115 as the etching mask and removing the second resist 115, thesecond pattern 111 b with a depth of d2 may be obtained. The process conditions of the second etching may be different from those of the first etching. In this process, the region except for the region P2 is covered with second resist 115 and no patterns are left. Iterating the formation of the resist patterns and the etching of thesubstrate 111 by distinguishable conditions, themold 11 according to the second method may be obtained. -
FIG. 3 shows themold 11 viewed from the side where the patterns, 111 a and 111 b, are formed, where each region forms particular patterns specific to the region, for instance, patterns in the region, A to D, provide particular aspect ratio of 1.0 to 2.5 by a step of 0.5, respectively. When the irradiation of the electron beams is carried out as varying its acceleration voltage, the depths (or the height) and the duty ratios of patterns in each section, A to D, are different from each other. Or, when the exposure is carried out as varying the pitch of the scanning patterns, the pitch of the resultant patterns formed in the mold in respective regions, A to D, shows the different pitches. - According to the second process described above, the
patterns 11A in respective regions provide the depth, d1 or d2 shown inFIG. 5C , specific to the region and different from the other regions. Forming the diffraction grating using thismold 11 with thepatterns 11A, the resultant gratings have different characteristics within the wafer. - Moreover, using this
mold 11 to form the diffraction grating within the wafer, the process may avoid the iteration of the resist coating, the irradiation on the resist, the developing, and the removal of the resist to form the various gratings, which may protect the wafer from the process damage, such as due to the irradiation of the electron beams and the etching. As described later, the process cost and the term thereof to form the pattern for the diffraction grating by the nanoimprint technique using this mold may be remarkably shortened, and the process damage applied to the semiconductor material may be reduced. - (Third Method to Form Mold)
-
FIGS. 6A to 6C schematically illustrate the process to form themold 12 according to the third embodiment of the invention. This process first coats theSOG film 122 on the silicon (Si)substrate 121 by the spin coater (FIG. 6A ). As described later, theSi substrate 121 becomes the base 12B of themold 12, while, theSOG 122 converts thepattern 12A of themold 12. - Next, the process irradiates the electron beams on the
surface 122 a of the SOG film as varying its acceleration voltage or the exposure dose, or varying the scanning patterns within the substrate, as illustrated inFIG. 6B . - Subsequently, the process etches the
irradiated SOG 122 by the buffered fluoric acid to form thepatterns 12A as shown inFIG. 6C . Since the irradiation of the electron beams is carried out as varying the condition thereof, the penetration depth of the beams into theSOG film 122 and the spreading width of the beams within theSOG film 122 show variety, which results in the etchedpatterns 12A with various depths, duty ratios, pitches and so on. Thus, themold 12 is completed with thepatterns 12A on thebase 12B. - According to the method described above to form the
mold 12, thepatterns 12A in themold 12 varies the depth, the duty ratio, the pitch and so on depending on the acceleration voltage and the exposure doses of the electron beams, or the scanning patterns. Such amold 12 may vary the characteristic of the diffraction grating to be formed by using themold 12 within the semiconductor wafer. - (Method to Form Diffraction Grating)
- Next, a method to form the diffraction grating according to an embodiment of the invention will be described.
FIGS. 7A to 8C schematically illustrate the process to form the grating. - First, the mold is prepared by at least one of the first to third method aforementioned. The explanation explained below assumes, for convenience's sake, that the
mold 10 is formed by the first method and provides thepatterns 10A. Thepatterns 10A, as already explained, have various depths, duty ratios, and the pitches depending on the position. - Second, the nanoimprint technique is carried out. That is, the
mold 10 with thepattern 10A is pressed against the resist 21 on thesemiconductor substrate 20 by the force F whose magnitude may be estimated beforehand depending on the process conditions (FIG. 7A ). Thesubstrate 20 may include semiconductor epitaxial layers of the multiple quantum well (MQW) active layer and the cladding layers. - Next, the resist 21 on the
substrate 20 may be cured as themold 21 is pressed thereat, which forms thepattern 23 for the diffraction grating in the cured resist 24. Various techniques may be applicable to cure the resist 24, for instance, the ultra-violet (UV) curing, which is often called as the optical nanoimprint technique, or the thermal curing using the heat treatment, which is often called as the thermal nanoimprint technique. In the optical nanoimprint technique, themold 10 is preferably made of material with a high transmissivity for the ultraviolet rays, while, the resist 21 is preferably a type of the UV-curable resist. - On the other hand, the thermal nanoimprint technique cures the resist 21, which is once softened by raising the temperature thereof, by cooing it down. Thus, the
mold 10 is preferably made of metal, typically nickel (Ni), while, the resist 21 is preferably made of thermoplastic material with a glass transition temperature. - Next, as illustrated in
FIG. 7C , the process exfoliates themold 10 from the resist 24 with the patterns for the grating. As already explained, the resist 24 has grooves with various depths dependent on positions thereof. -
FIG. 8A illustrates the process to etch thesemiconductor substrate 20 by the resist 24 with thepatterns 23 as the etching mask. The etching may be the reactive ion etching (RIE) whose conditions are so selected that both the resist 24 and thesubstrate 20 are etched. - Advancing the etching, the
semiconductor substrate 20 in a portion where the resistpattern 23 has a deeper groove is going to be exposed, and thesubstrate 20 exposed in the bottom of the groove is etched in a order that the resistpattern 23 has the deeper groove by the further etching. Finally, the process forms thediffraction grating 25 on thesubstrate 20, where the grating 25 has grooves with various depths depending on the resistpattern 23. That is, when themold 10 provides the plural regions shown inFIG. 3 and each region shows patterns specific to respective regions, for instance, the pattern in the region provides an aspect ratio specific to the region, the aspect ratio in the groove on thesubstrate 20 reflects that of the resistpattern 23 and themold 10 in respective regions. However, depending on the etching rate of the resist 24 and that of thesubstrate 20, which is often called as the selection ratio of the etching, the relative aspect ratio in respective regions may be reflected in the pattern on thesubstrate 20 but the absolute value thereof are different from each other. In other words, when the aspect ratios of the resist are 1.0 to 2.5 with 0.5 steps for the regions A to D, respectively, the aspect ratios of the grooves on thesubstrate 20 may be 0.5 to 1.25 with 0.25 steps for the regions A to D, respectively. That is, the aspect ratio of the grating 25 finally formed on thesubstrate 20 may be optionally varied by setting the selection ratio of the etching. Finally, removing the resist 24 after completing the etching, thediffraction grating 25 may be completed. - According to the process to form the
diffraction grating 25 above described, the process applies the nanoimprint technique by using themold 10 with thepattern 10A, where the dimensions such as the depth of the pattern varies therein. Accordingly, theresultant diffraction grating 25 may vary the dimensions such as the depth of the groove. The description above concentrates the subject to be varied on the depth of the groove, but the process may vary the other physical parameters such as the duty ratio, the pitch, and so on. - The process thus described may be applicable to a case when various types of the diffraction gratings are necessary. The process may also be applicable to enhance the homogeneity of the dimensions of the diffraction grating within a wafer. That is, evaluating the inhomogeneity of the etching rate within the wafer in advance, and forming
mold 10 whose patterns, in particular, the depth, the duty ratio, the pitch of the groove and so on, are formed so as to compensate the inhomogeneity of the etching, the resultant diffraction grating realizes improved homogeneity. As an example, when the etching rate shows a concentric circular distribution such that the rate in a peripheral portion of the wafer is about 10% higher that that of the center portion, thehomogeneous diffraction grating 25 may be obtained through the nanoimprint technique using themold 10 with the grooves in the peripheral portion of the wafer about 10% shallower than those in the center portion. - Moreover, the present method mentioned above is also applicable in a case where one diffraction grating built in the device, for instance, in the single distributed feedback (DFB) laser, has variety of dimensions. This enables to modify the optical coupling coefficient between the active layer and the diffraction grating within the device; accordingly, the optical power distribution along the optical axis of the device becomes controllable such that the homogeneous distribution of the optical power is attained; accordingly, the device may suppress the hole-burning effect along its optical axis.
- (Process to Form DFB-LD)
- Next, a process to form the DFB-LD according to one embodiment of the present invention will be described.
FIGS. 9A to 9C illustrate, in cross sections of the device, the process to form the DFB-LD 40, while,FIG. 10 is a perspective view of the DFB-LD, a portion of which is broken to show the layer structure thereof, obtained through the process of the embodiment. - First, the process forms, on the
semiconductor substrate 20, afirst cladding layer 30, a first separate optical confinement (SCH)layer 31, anactive layer 32, asecond SCH layer 33, alayer 34, and a resist 21 in this order. Here, both SCH layers, 31 and 33, may be saved. Second, themold 10 with thepattern 10A is pressed against the resist 21 to transfer thepattern 10A on the cured resist 24 (FIG. 9B ). Etching the cured resist 24 and thelayer 34 according to the method described inFIGS. 8A to 8C , and removing the resist 24 after the etching, the diffraction grating shown inFIG. 9C may be obtained in thelayer 34, which is often called as the guiding layer. - Next, on the
guiding layer 34 formed with thediffraction grating 25 is grown with a second cladding layer with a refractive index different from that of the guiding layer so as to bury thediffraction grating 25. Subsequently, the second cladding layer, the guidinglayer 34, thesecond SCH layer 33, theactive layer 32, the first SCH layer and thefirst cladding layer 30 are wet-etched to form the mesa. Further, the process buries thus formed mesa by the buryinglayer 35, and on the second cladding layer and the buryinglayer 35 are grown with thethird cladding layer 36. Thisthird cladding layer 36 may be saved. On thethird cladding layer 36, or on the second cladding layer and the buryinglayer 35, is grown with thecontact layer 37, and on thecontact layer 37 is formed with theupper electrode 38, while, the whole back surface of thesubstrate 20 is formed with thelower electrode 39. Thus, the DFB-LD 40 is completed. - The process to form the DFB-LD above described adopts the nanoimprint technique using the
mold 10 with the pattern whose dimensions such as the pattern depth are non-uniform; accordingly, the resultant diffraction grating may reflect this distributed dimensions. Because the process of the invention may form the diffraction gratings with various dimensions in a wafer, various DFB-LD s 40 with different types of the is diffraction gratings may be intermingled within the wafer, which shows a great advantage for the multi-objective but low production. - When the etching to form the diffraction grating shows an inhomogeneous rate within the wafer, the process may compensate the inhomogeneous rate by using the mold with the
imprint pattern 10A whose dimensions are varied. In this case, because the depth of the groove in the diffraction grating may be homogeneous, the DFB-LD with this diffraction grating may also enhance its homogeneity. - Moreover, using the
mold 10 with theimprint pattern 10A with a non-uniform dimensions, the DFB-LD with the non-uniform diffraction grating may be obtained. In this case, the optical coupling coefficient between the diffraction grating and the active layer varies within the device, the optical power distribution along the optical axis may be modified, which effectively suppresses the hole-burning effect.
Claims (6)
1. A method to produce a mold for the nanoimprint technique, said mold being used for fabricating a diffraction grating for a distributed feedback laser diode, comprising steps of:
(a) coating a dummy substrate with a photo resist for the electron beam lithograph;
(b) irradiating said photo resist by electron beams as varying an acceleration voltage of said electron beams;
(c) developing said irradiated resist to form a resist pattern;
(d) coating said resist pattern with a mold resin to be converted into said mold;
(e) curing said mold resin; and
(f) removing said dummy substrate and said resist pattern from said cured mold resin.
2. The method according to claim 1 ,
wherein said resin to be converted into said mold is a spin on glass film.
3. A method to produce a mold for the nanoimprint technique, said mold being used for fabricating a diffraction grating for a distributed feedback laser diode, comprising steps of:
(a) coating a substrate with a first resist for the electron beam lithography;
(b) irradiating a first limited region of said first photo resist by electron beams;
(c) developing said irradiated first photoresist to prepare a first resist pattern;
(d) etching said substrate under a first condition with said patterned first photo resist as an etching mask to form a first pattern on said substrate and removing said patterned first photo resist after said etching;
(e) coating said substrate with a second photo resist for the electron beam lithography;
(f) irradiating a second limited region of said second photo resist by electron beams, said second limited region being different from said first limited region;
(g) developing said irradiated second photo resist to prepare a second resist pattern; and
(h) etching said substrate under a second condition different from said first condition with said patterned second photo resist as an etching mask to form a second pattern on said substrate and removing said patterned second photo resist after said etching,
wherein said first pattern and said second pattern constitute at least a potion of patterns provided in said mold.
4. The method according to claim 2 ,
wherein said etching to form said first pattern has a different process time from said etching to form said second pattern.
5. A method to produce a mold for the nanoimprint technique, said mold being used for fabricating a diffraction grating for a distributed feedback laser diode and having a pattern for said diffraction grating, comprising steps of:
(a) coating a substrate with a photosensitive film;
(b) irradiating said photosensitive film by electron beams as varying an acceleration voltage of said electron beams; and
(c) developing said irradiated photosensitive film to form said pattern.
6. The method according to claim 5 ,
wherein said photosensitive film is made of spin on glass material.