US20090053460A1 - Method for producing a ductile tufted product, a ductile tufted product, particularly a ductile tufted top carpet layer, particularly for the automobile interior area - Google Patents
Method for producing a ductile tufted product, a ductile tufted product, particularly a ductile tufted top carpet layer, particularly for the automobile interior area Download PDFInfo
- Publication number
- US20090053460A1 US20090053460A1 US12/114,159 US11415908A US2009053460A1 US 20090053460 A1 US20090053460 A1 US 20090053460A1 US 11415908 A US11415908 A US 11415908A US 2009053460 A1 US2009053460 A1 US 2009053460A1
- Authority
- US
- United States
- Prior art keywords
- tufted
- ductile
- melt
- woven fabric
- blown non
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- D—TEXTILES; PAPER
- D05—SEWING; EMBROIDERING; TUFTING
- D05C—EMBROIDERING; TUFTING
- D05C15/00—Making pile fabrics or articles having similar surface features by inserting loops into a base material
- D05C15/04—Tufting
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H11/00—Non-woven pile fabrics
- D04H11/08—Non-woven pile fabrics formed by creation of a pile on at least one surface of a non-woven fabric without addition of pile-forming material, e.g. by needling, by differential shrinking
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
- B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
- B32B5/022—Non-woven fabric
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
- B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
- B32B5/24—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer
- B32B5/26—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H13/00—Other non-woven fabrics
-
- D—TEXTILES; PAPER
- D05—SEWING; EMBROIDERING; TUFTING
- D05C—EMBROIDERING; TUFTING
- D05C15/00—Making pile fabrics or articles having similar surface features by inserting loops into a base material
-
- D—TEXTILES; PAPER
- D05—SEWING; EMBROIDERING; TUFTING
- D05C—EMBROIDERING; TUFTING
- D05C17/00—Embroidered or tufted products; Base fabrics specially adapted for embroidered work; Inserts for producing surface irregularities in embroidered products
-
- D—TEXTILES; PAPER
- D05—SEWING; EMBROIDERING; TUFTING
- D05C—EMBROIDERING; TUFTING
- D05C17/00—Embroidered or tufted products; Base fabrics specially adapted for embroidered work; Inserts for producing surface irregularities in embroidered products
- D05C17/02—Tufted products
- D05C17/023—Tufted products characterised by the base fabric
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N7/00—Flexible sheet materials not otherwise provided for, e.g. textile threads, filaments, yarns or tow, glued on macromolecular material
- D06N7/0063—Floor covering on textile basis comprising a fibrous top layer being coated at the back with at least one polymer layer, e.g. carpets, rugs, synthetic turf
- D06N7/0068—Floor covering on textile basis comprising a fibrous top layer being coated at the back with at least one polymer layer, e.g. carpets, rugs, synthetic turf characterised by the primary backing or the fibrous top layer
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
- B32B2262/02—Synthetic macromolecular fibres
- B32B2262/0253—Polyolefin fibres
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
- B32B2262/02—Synthetic macromolecular fibres
- B32B2262/0261—Polyamide fibres
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
- B32B2262/02—Synthetic macromolecular fibres
- B32B2262/0276—Polyester fibres
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2307/00—Properties of the layers or laminate
- B32B2307/50—Properties of the layers or laminate having particular mechanical properties
- B32B2307/54—Yield strength; Tensile strength
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2307/00—Properties of the layers or laminate
- B32B2307/50—Properties of the layers or laminate having particular mechanical properties
- B32B2307/582—Tearability
- B32B2307/5825—Tear resistant
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2471/00—Floor coverings
- B32B2471/02—Carpets
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2605/00—Vehicles
- B32B2605/08—Cars
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B60—VEHICLES IN GENERAL
- B60R—VEHICLES, VEHICLE FITTINGS, OR VEHICLE PARTS, NOT OTHERWISE PROVIDED FOR
- B60R13/00—Elements for body-finishing, identifying, or decorating; Arrangements or adaptations for advertising purposes
- B60R13/08—Insulating elements, e.g. for sound insulation
- B60R13/0815—Acoustic or thermal insulation of passenger compartments
- B60R13/083—Acoustic or thermal insulation of passenger compartments for fire walls or floors
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N2201/00—Chemical constitution of the fibres, threads or yarns
- D06N2201/02—Synthetic macromolecular fibres
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N2203/00—Macromolecular materials of the coating layers
- D06N2203/04—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
- D06N2203/042—Polyolefin (co)polymers
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N2203/00—Macromolecular materials of the coating layers
- D06N2203/06—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D06N2203/061—Polyesters
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N2203/00—Macromolecular materials of the coating layers
- D06N2203/06—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D06N2203/065—Polyamides
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N2209/00—Properties of the materials
- D06N2209/02—Properties of the materials having acoustical properties
- D06N2209/025—Insulating, sound absorber
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
- D06N2211/00—Specially adapted uses
- D06N2211/12—Decorative or sun protection articles
- D06N2211/26—Vehicles, transportation
- D06N2211/263—Cars
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/23907—Pile or nap type surface or component
- Y10T428/2395—Nap type surface
Definitions
- the invention relates to a method for producing a ductile tufted product, particularly a ductile tufted top carpet layer produced with it, particularly for the automotive interior area.
- tufting For the production of a tufted carpet, a method referred to as tufting is employed, which is to say a technique for producing three-dimensional surfaces, which operates based on the principle of a sewing machine.
- tufting needles introduce a tuft yarn into a base material, referred to as the tufted backing.
- the tufting needles mounted to a needle bar are disposed in the width of the base material, for example a non-woven fabric, and simultaneously pierce the base material.
- the introduced tuft yarn is held on the bottom of the base material by hooks, referred to as loopers.
- loops or pile referred to as naps, are produced, which in the finished carped form the visible top (upper layer).
- these loops can already be cut during the tufting process, using special blades. This produces the cut-pile carpets, which are used particularly in the automotive interior area, preferably at a percentage of over 95%.
- the top carpet layer produced according to the method is supposed to be used particularly in the automotive interior area, or in the properties area.
- a melt-blown non-woven fabric is placed on a ductile polyester tufted backing, and the melt-blown non-woven fabric and the polyester tufted backing are tufted together.
- the resulting tufted product is characterized by particularly good ductility and accordingly high strength, elongation and tear propagation force data.
- the tufted product is introduced in the further carpet manufacturing process solely by a thermal treatment from the tufting piercing side, particularly without latex application.
- the latex represents a pretreatment of the raw product for a variety of methods for coating the backing or tufted backing.
- the latex is intended to lock the naps into the base material and/or the tufted backing. In this way, the desired integration of the naps is achieved, preventing the pulling of threads or fraying of the pile material.
- the latex material typically comprises synthetic latex with filler material.
- the inventive method also satisfies the environmental stipulations and industrial standards, which have become more stringent, particularly in recent times.
- a polyester spun-bond non-woven is used as the polyester tufted backing, preferably having a basis weight of 70 g/m 2 up to 140 g/m 2 , more preferred from 100 g/m 2 to 120 g/m 2 .
- melt-blown non-woven fabric having a basis weight of preferably 70 g/m 2 up to 500 g/m 2 is used, more preferred from 80 g/m 2 to 200 g/m 2 , even more preferred from 80 g/m 2 to 130 g/m 2 .
- the material consumption can be kept particularly low and the processing speed can be increased, allowing additional cost savings.
- thermoplastic raw material that can be spun or processed by injection molding is used as the raw material for the melt-blown non-woven fabric, particularly one selected from polyolefins, copolyolefins, polyesters, copolyesters, polyamides, and/or copolyamides having an MFI value (melt flow index) (according to DIN 1238 or ISO 1133) of 100 to 300 g/10 min.
- MFI value melt flow index
- the penetration of the melted melt-blown non-woven wear layer in the tufted backing is favored. As a result, a three-dimensional composite layer is produced such that undesirable delamination between the wear layer and the tufted backing is prevented.
- melt-blown non-woven fabric having a thickness of 0.5 mm to 1.5 mm is used, with 0.5 mm to 1.0 mm being particularly preferred.
- the fiber titer of the melt-blown non-woven fabric is advantageously 0.06 dtex to 0.2 dtex, with 0.06 dtex to 0.1 dtex being preferred.
- the bulky, soft melt-blown non-woven wear layer having a high specific fiber surface, lower fiber titer, and high fiber mobility facilitates the tufting without needle deviation and increases the number of contact points between the melt-blown non-woven wear layer and the fibers of the tufted backing, thus evenly strengthening the bond between the wear layer and the tufted backing across the cross-section.
- the joint tufting of the melt-blown non-woven fabric and polyester tufted backing preferably occurs without prior needling or calendaring with a gauge of 1 ⁇ 8′′ to 1/16′′.
- melt-blown non-woven fabric is advantageously strengthened by an ultrasonic calendar having a bonding surface of less than 5%, preferably of less than 2%, and tufted together with the polyester tufted backing with a gauge of 1 ⁇ 8′′ to 1/16′′.
- the melt-blown non-woven fabric and the polyester tufted backing are strengthened together by an ultrasonic calendar having a bonding surface of less than 5%, preferably of less than 2%, and tufted together with the polyester tufted backing with a gauge of 1 ⁇ 8′′ to 1/16′′.
- the joint strengthened, particularly good handling and better process stability than in the case of separate layers are guaranteed. Furthermore, the combination with the very small bonding surface at the same time allows sufficiently high fiber mobility, so that fiber damage during tufting can at least be reduced, thus increasing the quality of the tufted product, particularly with respect to ductility.
- an acoustic non-woven material and/or at least one other insulating layer for example a heavy layer having basis weights of, for example, 2 to 7 kg/m 2 made of ethylene-vinyl acetate/ethylene-propylene-diene rubber, or coextruded film comprising polyethylene/polyamide (polyethylene), is applied to the tufting piercing side of the tufted product.
- a heavy layer having basis weights of, for example, 2 to 7 kg/m 2 made of ethylene-vinyl acetate/ethylene-propylene-diene rubber, or coextruded film comprising polyethylene/polyamide (polyethylene) is applied to the tufting piercing side of the tufted product.
- the tufted products produced according to the invention at a tear propagation force in the longitudinal direction at room temperature (according to DIN 53859-3) of preferably 170 N to 240 N, have a particularly high tear propagation force value, and therefore particularly good ductility, so that these tufted products are particularly well suited for use as top carpet layers in the automotive interior area as automobile top carpet layers.
- the ductile tufted products particularly the ductile tufted automobile top carpet layers, at room temperature furthermore preferably have
- a maximum tensile force in the longitudinal direction (according to EN 29073-3) of 250 N/5 cm to 400 N/5 cm, more preferred of 275 N/5 cm to 375 N/5 cm,
- a maximum tensile force in the transverse direction (according to EN 29073-3) of 180 N/5 cm to 300 N/5 cm, more preferred of 203 N/5 cm to 250 N/5 cm,
- the ductile tufted products particularly the ductile tufted automobile top carpet layers, advantageously have
- polyethylene having a melt flow index (MFI) of 155 g/10 min according to DIN 1133 is used and spun through a melt-blowing spinneret.
- MFI melt flow index
- the polyethylene fibers obtained in this way have a fiber titer of 0.07 dtex.
- the fibers are deposited in a suction drum, which has a distance of approximately 600 mm to the spinning nozzle, in order to produce a bulky and soft fibrous web, the fiber mobility of which is maintained in the tufting process.
- the fibrous web weighing 80 g produced in this way can then optionally be strengthened by means of an ultrasonic calendar using light sonotrode pressing pressures of about 0.006 bar with a bonding surface of less than 5%, preferably of less than 2%, thus obtaining a still substantially bulky non-woven fabric.
- light thermal strengthening using engraved or roughened calendaring rollers is conceivable.
- the melt-blown non-woven fabric weighing 80 g produced according to the above-described method in the present case is placed on the tufted backing in non-strengthened form and strengthened only together with the tufted backing by means of an ultrasonic calendar using light sonotrode pressing pressures of about 0.006 bar with a bonding surface of about 1.6%.
- a polyester spun-bond non-woven material, Lutradur® LDT 5312 (Freudenberg), having a basis weight of 120 g/m 2 is used as the tufted backing.
- the laboratory tufting loom has a needle working width of about 50 cm and a needle gauge of 1/10 inch (10 needles per 2.54 cm) pile quality.
- the stitch density is about 56/10 cm.
- a BCF yarn which is a bulked continuous filament, is used as the tuft yarn and has a polyamide 6 quality having a total strength of 1300 dtex and 128 individual filaments.
- Other conventional tuft yarns can likewise be used.
- the tuft yarn weight is about 400 g/m 2 .
- the complete laboratory tufting arrangement produces, in the narrow width, a carpet design that is typically used in the automotive field (with the exception of the additionally inserted layer).
- the inserted tuft yarn is held by hooks such that loops or naps are produced. In this way, a loop pile carpet is produced. If the loops, as in this example, are cut with a blade, a cut-pile carpet is produced.
- melt-blown non-woven fabric After the melt-blown non-woven fabric has been tufted together with the polyester tufted backing, thermal treatment is provided from the tufting piercing side until the polyethylene of the melt-blown non-woven fabric has melted.
- the top carpet layer produced in this way is analyzed for the following properties.
- the tear propagation force of the tufted backing alone (Lutradur® LDT 53 12, 120 g/m 2 ), which is to say without the melt-blown non-woven fabric, is 198 N
- the tear propagation force of the tufted backing (Lutradur® LDT 5312, 120 g/m 2 ) having a conventional latex or latex binder treatment (approx. 100 g/m 2 ) is 150 N.
- the tufted product manufactured according to the invention has a particularly high tear propagation force value and therefore particularly good ductility, so that this tufted product is particularly well-suited for use as a top carpet layer in the automotive interior area.
- the ductility properties of the tufted product were determined using an internal measuring method.
- circular samples of the tufted product having a diameter of 24 cm are punched out, clamped in a clamping ring, and fixed by means of brass screws and threaded bolts.
- the fixed sample is heated by infrared heating to a defined temperature, in the present example to 140° C., wherein a constant distance of 16 cm to the infrared field is maintained.
- the clamping ring with the carpet sample fixed thereon is automatically placed on a displaceable hollow cylinder, which travels upward at a speed of 50 mm/s against a metal ball.
- the metal ball is cooled with water to 18° C. and has a diameter of 10 cm.
- the carpet sample is deformed from the tufting piercing side. The deformation depths that are measured are used to compute the deformation in percent.
- maximum deformation is: 106% and the maximum deformation force is: 1543 N.
- maximum deformation is: 50% and the maximum deformation force is: 723 N.
- the example of the top carpet layer produced according to the invention has the further advantage that it can be laminated with a heavy layer, without the additional application of polyethylene powder, which is common in the conventional carpet industry. Dispensing with this polyethylene powder application can be attributed to the fact that a bonding agent layer made of polyethylene is already provided on the carpet piercing side of the top carpet layer in the example.
Landscapes
- Engineering & Computer Science (AREA)
- Textile Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Materials Engineering (AREA)
- Nonwoven Fabrics (AREA)
- Laminated Bodies (AREA)
- Carpets (AREA)
- Passenger Equipment (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE200710020818 DE102007020818B3 (de) | 2007-05-02 | 2007-05-02 | Verfahren zur Herstellung eines verformbaren Tuftprodukts |
DE102007020818.0 | 2007-05-02 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20090053460A1 true US20090053460A1 (en) | 2009-02-26 |
Family
ID=39730830
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/114,159 Abandoned US20090053460A1 (en) | 2007-05-02 | 2008-05-02 | Method for producing a ductile tufted product, a ductile tufted product, particularly a ductile tufted top carpet layer, particularly for the automobile interior area |
Country Status (10)
Country | Link |
---|---|
US (1) | US20090053460A1 (de) |
EP (1) | EP1988204B1 (de) |
KR (1) | KR101126942B1 (de) |
AR (1) | AR066365A1 (de) |
AT (1) | ATE522651T1 (de) |
AU (1) | AU2008201959B2 (de) |
BR (1) | BRPI0801265A2 (de) |
DE (1) | DE102007020818B3 (de) |
PL (1) | PL1988204T3 (de) |
TW (1) | TWI390093B (de) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20120024210A1 (en) * | 2010-07-27 | 2012-02-02 | Hasetora Spinning Co., Ltd. | Tufted carpet |
US20150167254A1 (en) * | 2013-12-13 | 2015-06-18 | Orotex Belgium Nv | Artificial turf for landscape and sports |
US10370799B2 (en) | 2013-12-13 | 2019-08-06 | Dfs Europe Nv | Tufted structure for landscape and sports |
CN112301577A (zh) * | 2020-09-03 | 2021-02-02 | 诺奥(福建)环保家居用品有限公司 | 一种阻燃有色弯头纱满铺毯制造方法 |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102009004786A1 (de) * | 2009-01-13 | 2010-07-15 | Fleissner Gmbh | Verfahren und Vorrichtung zur Verfestigung von textilem Material |
DE102009013948A1 (de) * | 2009-03-19 | 2010-09-23 | Fleissner Gmbh | Verfahren und Vorrichtung zur Verfestigung eines Teppichrückens |
PL3080346T3 (pl) * | 2013-12-13 | 2019-11-29 | Bfs Europe Nv | Struktura tuftowana do zastosowań krajobrazowych i sportowych |
DE102021106621A1 (de) | 2021-03-18 | 2022-10-20 | Adler Pelzer Holding Gmbh | Absorptives Trägervlies für Tufting-Teppich |
Citations (34)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3359934A (en) * | 1967-05-08 | 1967-12-26 | Patchogue Plymouth Company | Tufted carpet having splittable filling yarns in the primary backing |
US3360421A (en) * | 1963-05-10 | 1967-12-26 | Du Pont | Bonded nonwoven backing material having perforate selvage and carpet made therefrom |
US3630816A (en) * | 1969-07-25 | 1971-12-28 | Chevron Res | Nonwoven sheets made from rectangular cross section monofilaments |
US3855046A (en) * | 1970-02-27 | 1974-12-17 | Kimberly Clark Co | Pattern bonded continuous filament web |
US4140071A (en) * | 1977-08-09 | 1979-02-20 | E. I. Du Pont De Nemours And Company | Process for preparing tufted carpet |
US4242394A (en) * | 1979-07-09 | 1980-12-30 | Armstrong Cork Company | Reinforced primary backing for tufted pile fabrics |
US4426415A (en) * | 1981-12-11 | 1984-01-17 | V&L Manufacturing Company, Inc. | Tufted carpeting, especially artificial turf, with tufts stitched through multiple layers of pre-woven backing material of differing gauge |
US4668566A (en) * | 1985-10-07 | 1987-05-26 | Kimberly-Clark Corporation | Multilayer nonwoven fabric made with poly-propylene and polyethylene |
US5114787A (en) * | 1990-09-21 | 1992-05-19 | Amoco Corporation | Multi-layer nonwoven web composites and process |
US5256224A (en) * | 1991-12-31 | 1993-10-26 | E. I. Du Pont De Nemours And Company | Process for making molded, tufted polyolefin carpet |
US5866229A (en) * | 1996-03-12 | 1999-02-02 | Firma Carl Freudenburg | Tuft backing |
US5962101A (en) * | 1997-04-29 | 1999-10-05 | Donald A. Irwin, Sr. | Dimensionally stable tufted carpet |
US6207599B1 (en) * | 1998-08-27 | 2001-03-27 | Akzo Nobel Nv | Nonwoven backing and carpet comprising same |
US6280818B1 (en) * | 1999-03-03 | 2001-08-28 | Wayn-Tex, Inc. | Carpet backing components and methods of making and using the same |
US6475592B1 (en) * | 1997-04-29 | 2002-11-05 | Darwin Enterprises, Inc. | Carpet backing that provides dimensional stability |
US20020172795A1 (en) * | 2001-03-28 | 2002-11-21 | Gardner Hugh Chester | Tuftable and tufted fabrics |
US20030152743A1 (en) * | 1999-04-26 | 2003-08-14 | Atsushi Matsunaga | Base cloth for tufted carpet and tufted carpet using the same |
US20030175475A1 (en) * | 2002-03-13 | 2003-09-18 | Higgins Kenneth B. | Textile constructions, components or materials and related methods |
US20030175474A1 (en) * | 2002-03-13 | 2003-09-18 | Higgins Kenneth B. | Textile constructions with stabilized primary backings and related methods |
US20040028818A1 (en) * | 2001-10-23 | 2004-02-12 | Radislav Alexandrovich Potyrailo | Systems and methods for the deposition and curing of coating compositions |
US20040151870A1 (en) * | 2003-02-04 | 2004-08-05 | Freudenberg Nonwovens Na | Automotive tufted carpet with enhanced acoustical properties |
US6849565B1 (en) * | 1995-03-17 | 2005-02-01 | Bp Corporation North America Inc. | Carpet construction and carpet backings for same |
US20050022919A1 (en) * | 2003-07-28 | 2005-02-03 | Burlington Industries, Inc. | Alternate method for applying hot melt adhesives to carpet |
US20050147787A1 (en) * | 2000-08-08 | 2005-07-07 | Bailey Larry M. | Carpet construction and carpet backings for same |
US20050249912A1 (en) * | 2004-05-06 | 2005-11-10 | C&A Floorcoverings, Inc. | Floor covering containing polyvinyl butyral and method of making same |
US20050249911A1 (en) * | 2004-05-06 | 2005-11-10 | C&A Floorcoverings, Inc. | Polyvinyl butyral backed floor covering |
US20070173162A1 (en) * | 2004-04-30 | 2007-07-26 | Samuel Ethiopia | Nonwoven fabric and fibers |
US7364634B1 (en) * | 2006-08-07 | 2008-04-29 | Darwin Enterprises | Carpet construction having secondary backing |
US20080213531A1 (en) * | 2007-02-12 | 2008-09-04 | Carl Freudenberg Kg | Method for manufacturing a tufted nonwoven fabric, tufted nonwoven fabric, and use thereof |
US7437807B2 (en) * | 2001-02-19 | 2008-10-21 | Firma Carl Freusenberg Kg | Tufted backing and method of manufacturing same |
US20080260989A1 (en) * | 2007-04-17 | 2008-10-23 | Aplix, Inc. | Loop material for loop and hook type fastener used in a disposable article or garment |
US20090120048A1 (en) * | 2007-11-09 | 2009-05-14 | Hollingsworth & Vose Company | Meltblown Filter Medium |
US20100104796A1 (en) * | 2007-01-31 | 2010-04-29 | Carl Freudenberg Kg | High-strength lightweight tufted backing and method for the production thereof |
US20110014431A1 (en) * | 2009-07-17 | 2011-01-20 | Fowler Gregory D | Embossed carpet backing |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0018789A1 (de) | 1979-04-27 | 1980-11-12 | The Buckeye Cellulose Corporation | Tuften-Material, dessen primäres Rückenmaterial aus einer mehrschichtigen Folie besteht, und Verfahren zu dessen Herstellung |
EP0030126A1 (de) | 1979-11-29 | 1981-06-10 | DON BROTHERS BUIST & COMPANY LIMITED | Verfahren zur Herstellung einer Tufting-Stoffbahn, Rückenstoffbahn dafür und nach dem Verfahren hergestellte Stoffbahn |
DE19506845A1 (de) | 1995-02-28 | 1996-08-29 | Wesertechno Gmbh Produktentwic | Teppichboden sowie Verfahren zur Herstellung desselben |
US6176935B1 (en) * | 1999-05-25 | 2001-01-23 | Mg Industries | System and method for refining sugar |
US7695794B2 (en) * | 2005-01-27 | 2010-04-13 | Colbond B.V. | Tufted nonwoven, bonded nonwoven, methods for their manufacture and uses |
-
2007
- 2007-05-02 DE DE200710020818 patent/DE102007020818B3/de not_active Expired - Fee Related
-
2008
- 2008-04-17 AT AT08007480T patent/ATE522651T1/de active
- 2008-04-17 EP EP20080007480 patent/EP1988204B1/de not_active Not-in-force
- 2008-04-17 PL PL08007480T patent/PL1988204T3/pl unknown
- 2008-04-18 TW TW97114090A patent/TWI390093B/zh not_active IP Right Cessation
- 2008-04-30 AR ARP080101833 patent/AR066365A1/es unknown
- 2008-05-01 KR KR1020080041022A patent/KR101126942B1/ko not_active IP Right Cessation
- 2008-05-02 US US12/114,159 patent/US20090053460A1/en not_active Abandoned
- 2008-05-02 AU AU2008201959A patent/AU2008201959B2/en not_active Ceased
- 2008-05-02 BR BRPI0801265-2A patent/BRPI0801265A2/pt not_active IP Right Cessation
Patent Citations (43)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3360421A (en) * | 1963-05-10 | 1967-12-26 | Du Pont | Bonded nonwoven backing material having perforate selvage and carpet made therefrom |
US3359934A (en) * | 1967-05-08 | 1967-12-26 | Patchogue Plymouth Company | Tufted carpet having splittable filling yarns in the primary backing |
US3630816A (en) * | 1969-07-25 | 1971-12-28 | Chevron Res | Nonwoven sheets made from rectangular cross section monofilaments |
US3855046A (en) * | 1970-02-27 | 1974-12-17 | Kimberly Clark Co | Pattern bonded continuous filament web |
US4140071A (en) * | 1977-08-09 | 1979-02-20 | E. I. Du Pont De Nemours And Company | Process for preparing tufted carpet |
US4242394A (en) * | 1979-07-09 | 1980-12-30 | Armstrong Cork Company | Reinforced primary backing for tufted pile fabrics |
US4426415A (en) * | 1981-12-11 | 1984-01-17 | V&L Manufacturing Company, Inc. | Tufted carpeting, especially artificial turf, with tufts stitched through multiple layers of pre-woven backing material of differing gauge |
US4668566A (en) * | 1985-10-07 | 1987-05-26 | Kimberly-Clark Corporation | Multilayer nonwoven fabric made with poly-propylene and polyethylene |
US5114787A (en) * | 1990-09-21 | 1992-05-19 | Amoco Corporation | Multi-layer nonwoven web composites and process |
US5256224A (en) * | 1991-12-31 | 1993-10-26 | E. I. Du Pont De Nemours And Company | Process for making molded, tufted polyolefin carpet |
US20080017294A1 (en) * | 1995-03-17 | 2008-01-24 | Propex Inc. | Carpet Construction and Carpet Backings for Same |
US6849565B1 (en) * | 1995-03-17 | 2005-02-01 | Bp Corporation North America Inc. | Carpet construction and carpet backings for same |
US5866229A (en) * | 1996-03-12 | 1999-02-02 | Firma Carl Freudenburg | Tuft backing |
US6475592B1 (en) * | 1997-04-29 | 2002-11-05 | Darwin Enterprises, Inc. | Carpet backing that provides dimensional stability |
US6479125B1 (en) * | 1997-04-29 | 2002-11-12 | Darwin Enterprises, Inc. | Backing for tufted carpet that imparts dimensional stability |
US5962101A (en) * | 1997-04-29 | 1999-10-05 | Donald A. Irwin, Sr. | Dimensionally stable tufted carpet |
US6207599B1 (en) * | 1998-08-27 | 2001-03-27 | Akzo Nobel Nv | Nonwoven backing and carpet comprising same |
US6280818B1 (en) * | 1999-03-03 | 2001-08-28 | Wayn-Tex, Inc. | Carpet backing components and methods of making and using the same |
US20030152743A1 (en) * | 1999-04-26 | 2003-08-14 | Atsushi Matsunaga | Base cloth for tufted carpet and tufted carpet using the same |
US20050147787A1 (en) * | 2000-08-08 | 2005-07-07 | Bailey Larry M. | Carpet construction and carpet backings for same |
US7437807B2 (en) * | 2001-02-19 | 2008-10-21 | Firma Carl Freusenberg Kg | Tufted backing and method of manufacturing same |
US20020172795A1 (en) * | 2001-03-28 | 2002-11-21 | Gardner Hugh Chester | Tuftable and tufted fabrics |
US6740385B2 (en) * | 2001-03-28 | 2004-05-25 | Bp Corporation North America Inc. | Tuftable and tufted fabrics |
US20040028818A1 (en) * | 2001-10-23 | 2004-02-12 | Radislav Alexandrovich Potyrailo | Systems and methods for the deposition and curing of coating compositions |
US20030175475A1 (en) * | 2002-03-13 | 2003-09-18 | Higgins Kenneth B. | Textile constructions, components or materials and related methods |
US6866912B2 (en) * | 2002-03-13 | 2005-03-15 | Milliken & Company | Textile constructions with stabilized primary backings and related methods |
US20090081406A1 (en) * | 2002-03-13 | 2009-03-26 | Higgins Kenneth B | Textile products and methods |
US20030175474A1 (en) * | 2002-03-13 | 2003-09-18 | Higgins Kenneth B. | Textile constructions with stabilized primary backings and related methods |
US20040151870A1 (en) * | 2003-02-04 | 2004-08-05 | Freudenberg Nonwovens Na | Automotive tufted carpet with enhanced acoustical properties |
US6808786B2 (en) * | 2003-02-04 | 2004-10-26 | Freudenberg Nonwovens | Automotive tufted carpet with enhanced acoustical properties |
US20050022919A1 (en) * | 2003-07-28 | 2005-02-03 | Burlington Industries, Inc. | Alternate method for applying hot melt adhesives to carpet |
US20070173162A1 (en) * | 2004-04-30 | 2007-07-26 | Samuel Ethiopia | Nonwoven fabric and fibers |
US20080271840A1 (en) * | 2004-05-06 | 2008-11-06 | Randall Brian S | Floor Covering Containing Polyvinyl Butyral and Method of Making the Same |
US20050249911A1 (en) * | 2004-05-06 | 2005-11-10 | C&A Floorcoverings, Inc. | Polyvinyl butyral backed floor covering |
US20050249912A1 (en) * | 2004-05-06 | 2005-11-10 | C&A Floorcoverings, Inc. | Floor covering containing polyvinyl butyral and method of making same |
US7364634B1 (en) * | 2006-08-07 | 2008-04-29 | Darwin Enterprises | Carpet construction having secondary backing |
US20100104796A1 (en) * | 2007-01-31 | 2010-04-29 | Carl Freudenberg Kg | High-strength lightweight tufted backing and method for the production thereof |
US20080213531A1 (en) * | 2007-02-12 | 2008-09-04 | Carl Freudenberg Kg | Method for manufacturing a tufted nonwoven fabric, tufted nonwoven fabric, and use thereof |
US20080260989A1 (en) * | 2007-04-17 | 2008-10-23 | Aplix, Inc. | Loop material for loop and hook type fastener used in a disposable article or garment |
US20100291341A1 (en) * | 2007-04-17 | 2010-11-18 | Lester Jr Donald H | Loop material for loop and hook type fastener used in a disposable article or garment |
US7960008B2 (en) * | 2007-04-17 | 2011-06-14 | Aplix, Inc. | Loop material for loop and hook type fastener used in a disposable article or garment |
US20090120048A1 (en) * | 2007-11-09 | 2009-05-14 | Hollingsworth & Vose Company | Meltblown Filter Medium |
US20110014431A1 (en) * | 2009-07-17 | 2011-01-20 | Fowler Gregory D | Embossed carpet backing |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20120024210A1 (en) * | 2010-07-27 | 2012-02-02 | Hasetora Spinning Co., Ltd. | Tufted carpet |
US20150167254A1 (en) * | 2013-12-13 | 2015-06-18 | Orotex Belgium Nv | Artificial turf for landscape and sports |
US10190267B2 (en) * | 2013-12-13 | 2019-01-29 | Bfs Europe Nv | Artificial turf for landscape and sports |
US10370799B2 (en) | 2013-12-13 | 2019-08-06 | Dfs Europe Nv | Tufted structure for landscape and sports |
CN112301577A (zh) * | 2020-09-03 | 2021-02-02 | 诺奥(福建)环保家居用品有限公司 | 一种阻燃有色弯头纱满铺毯制造方法 |
Also Published As
Publication number | Publication date |
---|---|
KR20080097940A (ko) | 2008-11-06 |
DE102007020818B3 (de) | 2009-01-02 |
EP1988204A2 (de) | 2008-11-05 |
PL1988204T3 (pl) | 2012-01-31 |
BRPI0801265A2 (pt) | 2008-12-16 |
AU2008201959B2 (en) | 2011-01-27 |
EP1988204A3 (de) | 2009-12-02 |
ATE522651T1 (de) | 2011-09-15 |
TW200912080A (en) | 2009-03-16 |
KR101126942B1 (ko) | 2012-03-20 |
EP1988204B1 (de) | 2011-08-31 |
AU2008201959A1 (en) | 2008-11-20 |
TWI390093B (zh) | 2013-03-21 |
AR066365A1 (es) | 2009-08-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20090053460A1 (en) | Method for producing a ductile tufted product, a ductile tufted product, particularly a ductile tufted top carpet layer, particularly for the automobile interior area | |
KR100235419B1 (ko) | 성형가능한 폴리올레핀 터프티드 카페트(turfted carpet)의 제조방법 | |
EP2510141B1 (de) | Primäre faservliesteppichrückseite | |
US7892622B2 (en) | Method for manufacturing a tufted product, tufted product, and use thereof | |
US4199644A (en) | Method for the production of a needled nonwoven fabric | |
EP3433404B1 (de) | Teppich umfassend eine vliesstruktur mit durch einen metallocenkatalysator katalysierten fasern | |
US20190009701A1 (en) | Automotive carpet with solid multilobal fibre | |
CA3074055C (en) | Nonwoven fabric having enhanced withdrawal force for carpet backing fabric and production method thereof | |
KR20200006969A (ko) | 니들 펀치 벨루어 카펫을 제조하는 방법 | |
US20230077606A1 (en) | Recyclable tufted fabric and method of making the same | |
KR20180103077A (ko) | 중실 다엽형 섬유를 갖는 이벤트용 또는 전시회용 카펫 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CARL FREUDENBERG KG, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:EMIRZE, ARARAD, DR.;SANDER, PETER;MAASS, ULRIKE;REEL/FRAME:021756/0175;SIGNING DATES FROM 20081013 TO 20081020 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |