US20080169080A1 - Casting Mould, Process, and Device For Casting Metal Melts - Google Patents
Casting Mould, Process, and Device For Casting Metal Melts Download PDFInfo
- Publication number
- US20080169080A1 US20080169080A1 US11/817,941 US81794106A US2008169080A1 US 20080169080 A1 US20080169080 A1 US 20080169080A1 US 81794106 A US81794106 A US 81794106A US 2008169080 A1 US2008169080 A1 US 2008169080A1
- Authority
- US
- United States
- Prior art keywords
- mould
- melt
- casting
- casting mould
- cavity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A casting mould for manufacturing a cast part from a metal melt includes a mould cavity for reproducing a cast part and comprising an inlet for pouring metal melt into the mould cavity and also to a device and a process for casting metal melts of this type. The casting mould provides further optimized casting results even under hard practical operating conditions. In addition, the use or application of the device according to the invention and the process minimizes the risk of jamming during casting. This is achieved in that the casting mould has at least one compensation chamber which is linked to the mould cavity via a channel and comprises at least one portion which is arranged above the maximum filling level (Fmax) of the casting mould during solidification of the metal melt.
Description
- This application is a National Phase Application of International Application No. PCT/EP2006/060171, filed Feb. 22, 2006, which claims the benefit of and priority to German Application No. 10 2005 010 838.5, filed Mar. 7, 2005, which is owned by the assignee of the instant application. The disclosure of each of the above applications is incorporated herein by reference in its entirety.
- The present invention relates to a casting mould for manufacturing a cast part from a metal melt which is, for example, a light metal melt, especially an aluminium melt. In addition, the invention relates to a device and a process for casting metal melts of this type to form a cast part using a casting mould of this type.
- One possibility for producing cast parts using casting moulds of the above-mentioned type is what is known as “contact casting”. In this casting process, the casting moulds, each of which is to be filled with melt, are gradually moved below a melt container containing the metal melt. Formed in the base of the melt container is an outlet which merges with a supply channel, to the free end of which the inlet in each casting mould is docked. The outflow of melt out of the melt container is in this case conventionally regulated via a stopper which can be moved from a completely lowered position, in which it seals the outlet, into a raised position, in which the outlet is released and melt is able to flow into the casting mould via the supply channel.
- Another casting process which has enjoyed practical success is what is known as “low-pressure casting”. In this process, the melt is conveyed counter to gravity from a melt container docked to the bottom of the casting mould into the mould cavity in the casting mould via an inlet arranged on the bottom of the casting mould. For this purpose, there is a pressure applied to the melt contained in the melt container, which forces the melt to flow into the mould cavity in the casting mould via a riser pipe which acts in this case as the supply channel.
- Regardless of the manner in which the mould is filled, there is the problem that what is known as “jamming” occurs once the mould has been completely filled. This jamming is manifested in a sudden rise in static pressure acting on the walls of the casting mould. It is a result of the kinetic energy with which the melt flows into the casting mould suddenly being converted, once the mould has been completely filled, into static energy and, at the same time, the amount of melt which has accumulated in each supply channel exerts a pressure on the melt which is already present in the casting mould. This pressure surge not only presses the melt into the gaps which are inevitably present between the individual moulded parts of the casting mould; the casting mould walls surrounding the mould cavity are also penetrated to a greater extent. This has proven especially problematic in the case of casting moulds which are made of a porous moulding material and are destroyed for demoulding the cast part once the melt has solidified. In the case of “expendable” casting moulds of this type, in particular, jamming causes the cast parts obtained to have a rough surface and necessitates increased effort for releasing the cast parts, once they have solidified, from the moulding material of the casting mould.
- To minimise the extent to which the metal melt penetrates a casting mould made of sandy moulding material, the filling level in the mould cavity in the casting mould is, in the case of a device known from DE 196 23 720 A1 for contact casting, monitored while the melt is being poured out and, on reaching a provided filling height, the filling process is terminated prematurely to the extent that the superfluous amount of melt which still burdens the melt once the mould has been completely filled is minimised and the risk of jamming is thus reduced. For this purpose, the casting moulds used in the known device have in their lid an inspection opening which leads rectilinearly into the mould cavity and through which a laser beam is directed onto the surface of the melt introduced into the casting mould. The beam reflected by the melt is intercepted by a sensor which forwards its measurement signal to a control and evaluation means which, based on the laser beam transmitted and received, determines the respective filling level of the casting mould and, on reaching a critical filling height, issues a control signal to seal the outlet in the melt container. The critical filling height is in this case adjusted in such a way as to avoid any undesirable jamming even if any melt continues to flow in the supply channel.
- In practice, it has been found that, under the rough conditions provided in practical casting operation, monitoring the height of the filling level and prematurely terminating the flow of melt on the model of the procedure described in DE 196 23 720 A1 still do not rule out the undesirable penetration of the inner walls of the casting mould with the requisite degree of certainty.
- The invention, in one embodiment, features a casting mould in which further optimized casting results are ensured even under hard practical operating conditions. In addition, a device and a process, the use or application of which, can minimize the risk of jamming during casting.
- With regard to a casting mould for manufacturing a cast part by casting a metal melt, which mould has a mould cavity for reproducing a cast part and an inlet for pouring metal melt into the mould cavity, the invention features a casting mould of this type with at least one compensation cavity which is linked to the mould cavity via a channel and comprises at least one portion which is arranged above the maximum filling level of the casting mould during solidification of the metal melt.
- With regard to a device for casting metal melt to form a cast part in a casting mould configured in accordance with the invention and is equipped with a melt container, comprising an outlet, for the metal melt, with a supply channel connected to the outlet, with a means for docking the casting mould to the melt container in such a way that the inlet in the casting mould is connected to the supply channel when docked, with a measuring means for detecting the amount of melt introduced into the casting mould, with a regulating means for regulating the flow of melt from the melt container into the casting mould and with a control and evaluation means which evaluates the amount of melt detected by the measuring means and issues a control signal for sealing the outlet in the container once a specific filling level in the casting mould has been reached, the invention features the control and evaluation means issuing the control signal once the amount of melt poured into the casting mould has reached a limit value at which the amount of metal melt which is then still present in the supply channel is sufficient to fill the mould cavity completely and at most a portion of the compensation cavity.
- With regard to a process for casting metal melt to form a cast part in a casting mould, wherein the metal melt is guided in a regulated manner from a container into the casting mould via a supply channel and the inflow of metal melt into the supply channel is interrupted once a specific amount of metal melt has been introduced into the mould cavity, the invention features a casting mould configured such that the inflow of melt into the supply channel is interrupted once the metal melt in the mould cavity has reached a filling level at which the amount of metal melt which is still present in the supply channel is sufficient to fill the mould cavity completely and at most a portion of the compensation cavity.
- To avoid as far as possible penetration of a casting mould as a result of jamming, the invention proposes the formation in the casting mould of a compensation cavity which is designed to absorb, as a buffer, the amount of excess melt which is no longer required for complete filling of the casting mould and, as a result of this process, inevitably remains, even after the melt container has been sealed, in the supply channel via which the melt flows into the casting mould. The metallostatic pressure, which would otherwise prevail, of the amount of melt present in the supply channel is thus prevented from acting on the melt present in the casting mould.
- At the same time, in the event of pressure peaks in the casting mould, the compensation cavity acts as a damper by which, for example, jamming, which is especially critical in the prior art with regard to the surface quality and subsequent processability of the cast part obtained, is effectively buffered. The melt infiltrating the mould cavity in the casting mould is able to escape into the compensation cavity, thus preventing, in particular, the sudden rise in pressure which occurs in conventional casting moulds, once the mould has been completely filled, as a result of the conversion of the kinetic energy, inherent to the melt during filling, into static energy.
- In terms of the process and device, the embodiment according to the invention of a casting mould allows the inflow of melt into the supply channel to be interrupted as soon as the casting mould is filled, the tolerance range within which this interruption is carried out being widened by the buffering effect of the compensation cavity. It is thus ensured, even under crude practical operating conditions, that the flow of melt is in each case terminated in good time in such a way as reliably to rule out, with incorporation of the effect of the compensation cavity, the production of pressure peaks in the casting mould.
- The linking of the compensation cavity via a channel firstly serves, in this case, the purpose of allowing the casting compound remaining in the region of the compensation cavity to be easily separated from the cast part after solidification. The channel is therefore preferably formed in such a way that the webs remaining in the region of the channels after solidification are thin and easily separable. The surface area of the passage of the melt to the chambers is in this case preferably selected so as to be as large as possible in that the linking of the channel is as broad as possible at a given low linking height.
- A particular advantage of the embodiment according to the invention of a casting mould is that the compensation chamber is formed in the casting mould itself, so the casting mould as a whole remains closed. This allows the casting mould easily to be turned in order, for example, to cause purposefully oriented solidification of the cast part.
- The amount of melt which remains unused in the compensation chambers is negligible compared to the overall volume of melt required for the cast part. A suitably sophisticated configuration of each connecting channel between the mould cavity and compensation chamber allows the casting material which collects in the chamber easily to be broken off from the finished cast part. It has been found to be especially beneficial for the practical application of the invention that casting moulds configured in accordance with the invention may easily be inserted into existing casting devices and that these existing casting devices may easily be retrofitted to devices according to the invention or be operated in the manner according to the invention.
- The cast parts obtained using the invention have a much smoother surface than those manufactured in the known manner. Especially in the field of sophisticated moulded elements of the cast part, such as, for example, the oil channels of engine units, the levels of surface roughness are much lower, as is accordingly the flow resistance as liquids flow through. The cast parts obtained in accordance with the invention are especially simple to clean, as little moulding material clings to them after demoulding. The effort required for cleaning the finished cast part is therefore greatly reduced. Finally, the reduced penetration of pressure of the inner surfaces by the melt lowers the requirements placed on the quality of the moulding material used for manufacturing the casting mould. More economical coarse-grain moulding materials may thus be used without detracting from the surface quality.
- The invention therefore provides a casting mould, a casting device and a casting process which provide, even under hard practical operating conditions, casting results which not only ensure optimized surfaces but also allow simplified removal from the casting mould once the cast part has solidified.
- The options for use of casting moulds according to the invention may be extended in that the cross section of the channel is delimited in such a way as to be sealed, as soon as the mould has been filled with metal melt which has already solidified. This can be achieved in that the cross-sectional course of the channel is adapted to the heat dissipated via the casting mould in the region of the channel in such a way that the solidification of the melt contained in the channel is completed very rapidly. It is thus very easy to prevent cast metal from flowing out of the compensation chamber into the mould cavity and back once the mould has been filled. This has been found to be especially beneficial for casting processes of the type in which the casting mould, once filled with melt, is rotated about a longitudinal or transverse axis to bring about purposefully oriented solidification of the cast part.
- In principle, the advantages of the invention may be utilized in all casting moulds and casting processes, regardless of the material from which the casting mould is made. However, the good demouldability makes the invention especially suitable for expendable casting moulds which are usually made of a moulding sand and a moulding material comprising a binder.
- An especially uniform effect of the configuration according to the invention of a casting mould may be achieved in that there are provided a plurality of compensation chambers which are connected to mould cavity regions which are, in each case, critical with regard to the effect of pressure peaks. However, it is also conceivable to provide a larger chamber which is connected to the mould cavity via a suitably configured connecting channel or via a plurality of channels leading into the critical regions.
- The casting mould may, in principle, be provided for all known casting processes. Examples include contact casting or else rising casting. The casting mould according to the invention may be provided for the manufacture of cast parts for the automotive industry, especially of engine components such as, for example, cylinder blocks.
- A constructionally simple embodiment of a casting mould according to the invention is obtained if the compensation chamber is linked to a portion of the mould cavity that is located on top while the metal melt is being poured in. In the case of casting moulds composed of a plurality of moulded parts, the compensation chamber may for this purpose be incorporated, for example, into the casting mould lid which is arranged on top during filling.
- The amount of melt guided into the casting mould can, in principle, be detected by a weight measurement or other known processes. The amount of melt may in this case be detected, in a particularly reliable manner adapted to the actual conditions, in that the measuring means monitors the filling level in the casting mould and the evaluation means issues the control signal once the metal melt in the mould cavity has reached a filling height at which the volume of metal melt which is still present in the supply channel is sufficient to fill the mould cavity completely and at most a portion of the compensation cavity. In order, for this purpose, to be able to utilize the possibility, known from DE 196 23 720 A1, of an especially precise and practical measurement of the filling level of a casting mould, the casting mould is advantageously provided with an inspection opening leading to the mould cavity for inspecting the filling level of the metal melt in the mould cavity. The compensation chamber and the inspection opening are in this case preferably oriented in such a way that the inspection opening to the mould cavity and the compensation cavity intersect a common horizontal plane. The filling level of the chambers may thus be gauged, in each case, via the inspection opening.
- If the casting mould has an inspection opening of the type described hereinbefore, the measuring means of the device according to the invention may comprise, in a manner known from DE 196 23 720 A1, a laser, which directs a laser beam through the inspection opening onto the surface of the melt introduced into the casting mould, and a sensor which detects the laser beam reflected by the surface of the melt.
- The risk of the occurrence of a pressure surge may be further reduced in that the filling speed is reduced toward the end of the mould-filling process by reducing the flow through the outlet in the melt container. For this purpose, in the case of a device according to the invention, the regulating means may, in a manner known per se, comprise a stopper for sealing the outlet in the container and an adjustment means for raising the stopper out of and lowering it into its sealed position, the adjustment movement of the stopper preferably being regulated by the regulating means stopper, especially when the approaches the outlet.
- The invention will be described hereinafter in greater detail with reference to drawings which illustrate an embodiment and in which:
-
FIG. 1 is a schematic cross section of a casting mould for casting a cast part of an internal-combustion engine; -
FIG. 2 is a schematic cross section of a device for casting an Al/Si melt in a first operating position; and -
FIG. 3 shows the device according toFIG. 2 in a second operating position. - The casting mould 1 is composed, as a core packet, from a plurality of lateral moulded
parts 2, 3, a base part and a lid mouldedpart 4 which is arranged at the top, in the casting mould filling position shown in the figures, and covers the top of themould cavity 5 surrounded by the mouldedparts parts - Incorporated into the cover moulded
part 4 of the casting mould 1 are an inlet 6, which runs toward themould cavity 5 in the manner of a funnel and merges therewith, and a cylindrical inspection opening 7 which also leads rectilinearly from the top of the cover mouldedpart 4 into themould cavity 5. - The cover moulded
part 4 comprises aperipheral edge portion 4 a which is thicker toward the bottom of the cover mouldedpart 4 than theinner portion 4 b, surrounded by theedge portion 4 a, of the cover mouldedpart 4. Theedge portion 4 a of the cover mouldedpart 4 rests on thelateral parts 2, 3, whereas the bottom of itsinner portion 4 b defines the top of the cast part and thus the height at which the casting mould 1 is completely filled with melt. - Incorporated into the
edge portion 4 a of the cover mouldedpart 4 are a large number of small-volume compensation chambers lateral parts 2, 3. One row ofcompensation chambers 8 are in this case associated with onelateral part 2, whereas the other row ofcompensation chambers 9 are positioned above the other lateral part 3 of the casting mould 1. Within their rows, thecompensation chambers compensation chamber compensation chambers - The
compensation chambers mould cavity 5. The total volume of all of thecompensation chambers mould cavity 5. - The
base 8 a of thecompensation chambers inner portion 4 b of the cover mouldedpart 4, whereas theroof 8 b of thecompensation chambers part 4, in each case well above the bottom of theinner portion 4 b. Theupper portion compensation chambers - The
portion 8 d, arranged below the maximum filling level Fmax of the casting mould 1, of thecompensation chambers mould cavity 5 in the casting mould 1 in each case via a horizontally extendingchannel lid core 4. The opening, associated with themould cavity 5, of thechannels mould cavity 5, of the edge portion. Thechannels channels compensation chambers channels part 4 that surrounds thechannels mould cavity 5 has been filled. - For casting of the cast part G, the casting mould 1 is positioned by a conveying and lifting
device 12 below the opening of asupply channel 13 in such a way that the inlet 6 in the casting mould 1 is docked tightly at the opening of thesupply channel 13. In this position, the inspection opening 7 in the casting mould 1 is arranged below alaser 14 which directs its laser beam through the inspection opening 7 into themould cavity 5 in the casting mould 1. - The
supply channel 13 is configured in aconnector 15 which is configured on the bottom of amelt container 16 and connected to theoutlet 17 in themelt container 16, which outlet may be sealed and opened using astopper 18. For this purpose, thestopper 18 can be raised by an adjustment means 19 from a closed position, in which its thickened end seals theoutlet 17, into an open position, in which it releases theoutlet 17, thus allowing the Al/Si melt S contained in themelt container 16 to flow into thesupply channel 13. In the same way, thestopper 18 may be lowered by the adjustment means 19 to seal theoutlet 17. Both the raising process and the lowering process are carried out in this case in a regulated manner in that the adjustment means 19 is able to stop thestopper 18 in any position in order to regulate the volume flow of melt S passing through theoutlet 17. - The adjustment means 19 receives the control signals for raising and lowering the
stopper 18 from a regulating and control means 20. The regulating and control means 20 is coupled to a measuring and evaluation means 21 with which there are associated, in turn, thelaser 14 and asensor 22 which detects the laser beam L reflected at the surface of the melt S passing into themould cavity 5. - During filling of the casting mould 1 with melt S (
stopper 18 raised to the maximum degree), the measuring and evaluation means 21 continuously calculates, from the laser beam L issued by thelaser 14 and detected by thesensor 22, the filling level F in themould cavity 5 and delivers the corresponding measured results to the regulating and control means 20. If the filling level F reaches a filling height Fkrit1, the regulating and control means 20 issues to the adjustment means 19 a first control signal in response to which the adjustment means lowers thestopper 18 into a position in which, although theoutlet 17 in themelt container 12 is still open, the flow of melt S is nevertheless slowed down. The filling height Fkrit1 is sufficiently remote from the maximum filling level Fmax of the casting mould 1 that the filling of the casting mould is slowed down toward the end of the filling process. - As soon as the filling level F has thus reached a second critical filling height Fkrit2, the regulating and control means 20 issues to the adjustment means 19 a second control signal in response to which the adjustment means presses the
stopper 18 fully into theoutlet 17, thus preventing any further melt S from entering thesupply channel 13. The position of the filling height Fkrit2 is in this case designed in such a way that the amount of melt SZ still present in thesupply channel 13 is sufficient to fill with melt S themould cavity 5 completely and thecompensation cavities lower region 8 b, 9 b. Depending on the configuration of the casting mould 1, the filling height Fkrit2 may correspond to the maximum filling level Fmax. - Alternatively, the regulating and control means may issue merely one control signal to the adjustment means 19, i.e. when the critical filling height is reached, so the
stopper 18 is completely closed. If the times required for filling the mould are substantially constant, the stopper may be partially lowered in advance in a time-controlled manner, thus also slowing down the filling of the casting mould toward the end of the filling process. - On account of its low volume, the amount of melt which passes into the
channels compensation chambers mould cavity 5 in the casting mould 1. The casting mould 1 may then easily be forwarded for subsequent processing by being rotated, for example, through 180° about its longitudinal axis in order to allow the cast part G purposefully to solidify with solidification oriented counter to the direction of introduction. - 1 Casting mould
- 2, 3 Lateral moulded parts
- 4 Cover moulded part
- 5 Mould cavity
- G Cast part
- 6 Inlet
- 7 Inspection opening
- 4 a Edge portion of the cover moulded
part 4 - 4 b Inner portion of the
cover core 4 - 8, 9 Compensation chambers
- 8 a Base of the
compensation chambers - 8 b Roof of the
compensation chambers - 8 c, 9 c Upper portions of the
compensation chambers - 8 d Lower portion of the
compensation chambers - 10, 11 Channels
- 12 Conveying and lifting device
- 13 Supply channel
- 14 Laser
- 15 Connector
- 16 Melt container
- 17 Outlet in the
melt container 16 - 18 Stopper
- 19 Adjustment means
- 20 Regulating and control means
- 21 Measuring and evaluation means
- 22 Sensor
- Fmax Maximum filling level of the casting mould 1
- F Filling level in the casting mould 1
- Fkrit1 First critical filling height
- Fkrit2 Second critical filling height
- L Laser beam
- S Al/Si melt
- SZ Amount of melt still present in the
supply channel 13 after theoutlet 17 has been closed
Claims (18)
1. A casting mould for manufacturing a cast part from a metal melt, the casting mould comprising a mould cavity for reproducing a cast part and comprising an inlet for pouring metal melt into the mould cavity, wherein the mould cavity includes at least one compensation chamber which is linked to the mould cavity via a channel, the at least one compensation chamber including at least one portion which is arranged above the maximum filling level of the casting mould during solidification of the metal melt.
2. The casting mould of claim 1 , wherein the cross section of the channel is delimited in such a way as to be sealed immediately with metal melt that solidifies after completion of the mould filling process.
3. The casting mould of claim 1 wherein the casting mould is made of a molding sand and a molding material comprising a binder.
4. The casting mould of claim 1 wherein the at least one compensation cavity is linked to a portion of the mould cavity that is located on top while the metal melt is being poured in.
5. The casting mould of claim 1 wherein the casting mould has an inspection opening to the mould cavity for inspecting the filling level of the metal melt in the mould cavity.
6. The casting mould of claim 5 , wherein the inspection opening to the mould cavity and the at least one compensation cavity intersect a common horizontal plane.
7. The casting mould of claim 1 wherein the casting mould includes a plurality of molded parts.
8. The casting mould of claim 7 , wherein the at least one compensation cavity is incorporated into a lid molded part.
9. (canceled)
10. A device for casting metal melt to form a cast part, comprising:
a casting mould defining a mould cavity for reproducing the cast part and comprising an inlet for pouring the metal melt into the mould cavity, wherein the mould cavity includes at least one compensation chamber which is linked to the mould cavity via a channel, the at least one compensation chamber including at least one portion which is arranged above the maximum filling level of the casting mould during solidification of the metal melt;
a melt container, comprising an outlet for the metal melt;
a supply channel connected to the outlet;
a means for docking the casting mould to the melt container in such a way that the inlet in the casting mould is connected to the supply channel when docked;
a measuring means for detecting the amount of melt introduced into the casting mould;
a regulating means for regulating the flow of melt from the melt container into the casting mould; and
a control means which evaluates the amount of melt detected by the measuring means and issues a control signal for sealing the outlet in the melt container once a specific filling level in the casting mould has been reached, wherein the control means issues the control signal once the amount of melt poured into the casting mould has reached a limit value at which the amount of metal melt which is then still present in the supply channel is sufficient to fill the mould cavity completely and at most a portion of the at least one compensation cavity.
11. The device of claim 10 , wherein the measuring means monitors the filling level in the casting mould and the control means issues the control signal once the metal melt in the mould cavity has reached the limit value.
12. The device of claim 11 , wherein the casting mould includes an inspection opening to the mould cavity for inspecting the filling level of the metal melt in the mould cavity, the measuring means comprising a laser that directs a laser beam through the inspection opening onto the surface of the melt introduced into the casting mould, and (ii) a sensor that detects the laser beam reflected by the surface of the melt.
13. The device of claim 10 wherein the regulating means comprises a stopper for sealing the outlet in the melt container and an adjustment means for raising the stopper out of and lowering it into its sealed position.
14. The device of claim 13 , wherein the regulating means regulates the adjustment movement of the stopper.
15. A process for casting metal melt to form a cast part, comprising:
providing a casting mould comprising a mould cavity and at least one compensation cavity;
guiding in a regulated manner the metal melt from a melt container into the casting mould via a supply channel; and
interrupting the inflow of the metal melt into the supply channel once the metal melt in the mould cavity has reached a filling level at which the amount of metal melt which is still present in the supply channel is sufficient to fill the mould cavity completely and at most a portion of the at least one compensation cavity.
16. The process of claim 15 , wherein the filling level in the casting mould is monitored and the inflow of metal melt into the supply channel is interrupted once the filling level has reached a height at which the volume of metal melt which is then still present in the supply channel is sufficient to fill the mould cavity completely and at most a portion of the compensation cavity (8, 9).
17. The device of claim 10 wherein the casting mould includes an inspection opening to the mould cavity for inspecting the filling level of the metal melt in the mould cavity, the measuring means comprising (i) a laser that directs a laser beam through the inspection opening onto the surface of the melt introduced into the casting mould, and (ii) a sensor that detects the laser beam reflected by the surface of the melt.
18. The process of claim 15 wherein the casting mould defines a mould cavity for reproducing the cast part and comprises an inlet for pouring the metal melt into the mould cavity, wherein the mould cavity includes at least one compensation chamber which is linked to the mould cavity via a channel, the at least one compensation chamber including at least one portion which is arranged above the maximum filling level of the casting mould during solidification of the metal melt.