US20070244243A1 - Stabilized Kaolin Slurry and Methods for Improving Kaolin Slurry Stability - Google Patents
Stabilized Kaolin Slurry and Methods for Improving Kaolin Slurry Stability Download PDFInfo
- Publication number
- US20070244243A1 US20070244243A1 US11/573,709 US57370905A US2007244243A1 US 20070244243 A1 US20070244243 A1 US 20070244243A1 US 57370905 A US57370905 A US 57370905A US 2007244243 A1 US2007244243 A1 US 2007244243A1
- Authority
- US
- United States
- Prior art keywords
- slurry
- kaolin
- stabilized
- kaolin slurry
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 239000002002 slurry Substances 0.000 title claims abstract description 170
- NLYAJNPCOHFWQQ-UHFFFAOYSA-N kaolin Chemical compound O.O.O=[Al]O[Si](=O)O[Si](=O)O[Al]=O NLYAJNPCOHFWQQ-UHFFFAOYSA-N 0.000 title claims abstract description 159
- 239000005995 Aluminium silicate Substances 0.000 title claims abstract description 154
- 235000012211 aluminium silicate Nutrition 0.000 title claims abstract description 154
- 238000000034 method Methods 0.000 title claims abstract description 54
- 239000002245 particle Substances 0.000 claims abstract description 37
- 238000012360 testing method Methods 0.000 claims abstract description 31
- 239000003381 stabilizer Substances 0.000 claims abstract description 24
- 239000007787 solid Substances 0.000 claims description 25
- 229920002134 Carboxymethyl cellulose Polymers 0.000 claims description 24
- 239000001768 carboxy methyl cellulose Substances 0.000 claims description 22
- 235000010948 carboxy methyl cellulose Nutrition 0.000 claims description 22
- 239000008112 carboxymethyl-cellulose Substances 0.000 claims description 22
- 239000002270 dispersing agent Substances 0.000 claims description 22
- 238000001914 filtration Methods 0.000 claims description 15
- 229920000058 polyacrylate Polymers 0.000 claims description 11
- 239000002562 thickening agent Substances 0.000 claims description 11
- 150000003839 salts Chemical group 0.000 claims description 9
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 8
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 6
- 238000004519 manufacturing process Methods 0.000 claims description 6
- 229920000388 Polyphosphate Polymers 0.000 claims description 4
- 238000005189 flocculation Methods 0.000 claims description 4
- 230000016615 flocculation Effects 0.000 claims description 4
- 239000001205 polyphosphate Substances 0.000 claims description 4
- 235000011176 polyphosphates Nutrition 0.000 claims description 4
- 150000004760 silicates Chemical class 0.000 claims description 4
- IXPNQXFRVYWDDI-UHFFFAOYSA-N 1-methyl-2,4-dioxo-1,3-diazinane-5-carboximidamide Chemical compound CN1CC(C(N)=N)C(=O)NC1=O IXPNQXFRVYWDDI-UHFFFAOYSA-N 0.000 claims description 3
- 229920002126 Acrylic acid copolymer Polymers 0.000 claims description 3
- 229920000663 Hydroxyethyl cellulose Polymers 0.000 claims description 3
- 229920002153 Hydroxypropyl cellulose Polymers 0.000 claims description 3
- 229920013820 alkyl cellulose Polymers 0.000 claims description 3
- GUJOJGAPFQRJSV-UHFFFAOYSA-N dialuminum;dioxosilane;oxygen(2-);hydrate Chemical compound O.[O-2].[O-2].[O-2].[Al+3].[Al+3].O=[Si]=O.O=[Si]=O.O=[Si]=O.O=[Si]=O GUJOJGAPFQRJSV-UHFFFAOYSA-N 0.000 claims description 3
- 235000019326 ethyl hydroxyethyl cellulose Nutrition 0.000 claims description 3
- 229920003089 ethylhydroxy ethyl cellulose Polymers 0.000 claims description 3
- 230000003311 flocculating effect Effects 0.000 claims description 3
- 235000019447 hydroxyethyl cellulose Nutrition 0.000 claims description 3
- 229920003063 hydroxymethyl cellulose Polymers 0.000 claims description 3
- 235000010977 hydroxypropyl cellulose Nutrition 0.000 claims description 3
- NEMFQSKAPLGFIP-UHFFFAOYSA-N magnesiosodium Chemical compound [Na].[Mg] NEMFQSKAPLGFIP-UHFFFAOYSA-N 0.000 claims description 3
- 239000000391 magnesium silicate Substances 0.000 claims description 3
- 229910052919 magnesium silicate Inorganic materials 0.000 claims description 3
- 235000019792 magnesium silicate Nutrition 0.000 claims description 3
- 229910052901 montmorillonite Inorganic materials 0.000 claims description 3
- 229920000570 polyether Polymers 0.000 claims description 3
- 235000013855 polyvinylpyrrolidone Nutrition 0.000 claims description 3
- 229920000036 polyvinylpyrrolidone Polymers 0.000 claims description 3
- 239000001267 polyvinylpyrrolidone Substances 0.000 claims description 3
- 239000000377 silicon dioxide Substances 0.000 claims description 3
- 229910021647 smectite Inorganic materials 0.000 claims description 3
- 235000010413 sodium alginate Nutrition 0.000 claims description 3
- 239000000661 sodium alginate Substances 0.000 claims description 3
- 229940005550 sodium alginate Drugs 0.000 claims description 3
- 150000003673 urethanes Chemical class 0.000 claims description 3
- 239000000230 xanthan gum Substances 0.000 claims description 3
- 235000010493 xanthan gum Nutrition 0.000 claims description 3
- 229920001285 xanthan gum Polymers 0.000 claims description 3
- 229940082509 xanthan gum Drugs 0.000 claims description 3
- 238000001694 spray drying Methods 0.000 claims description 2
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 17
- 239000000523 sample Substances 0.000 description 15
- 239000004927 clay Substances 0.000 description 13
- 241000276425 Xiphophorus maculatus Species 0.000 description 9
- 230000000087 stabilizing effect Effects 0.000 description 5
- 230000000052 comparative effect Effects 0.000 description 4
- 230000007774 longterm Effects 0.000 description 3
- 239000000047 product Substances 0.000 description 3
- 238000013112 stability test Methods 0.000 description 3
- CDBYLPFSWZWCQE-UHFFFAOYSA-L Sodium Carbonate Chemical compound [Na+].[Na+].[O-]C([O-])=O CDBYLPFSWZWCQE-UHFFFAOYSA-L 0.000 description 2
- 238000013459 approach Methods 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 230000000694 effects Effects 0.000 description 2
- 238000002474 experimental method Methods 0.000 description 2
- 239000000945 filler Substances 0.000 description 2
- 239000012065 filter cake Substances 0.000 description 2
- 239000012530 fluid Substances 0.000 description 2
- 239000000463 material Substances 0.000 description 2
- 238000005259 measurement Methods 0.000 description 2
- 238000012544 monitoring process Methods 0.000 description 2
- 238000004062 sedimentation Methods 0.000 description 2
- 238000000974 shear rheometry Methods 0.000 description 2
- 238000010008 shearing Methods 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 238000010998 test method Methods 0.000 description 2
- QGZKDVFQNNGYKY-UHFFFAOYSA-O Ammonium Chemical compound [NH4+] QGZKDVFQNNGYKY-UHFFFAOYSA-O 0.000 description 1
- HHMUQYPXZARAFI-UHFFFAOYSA-N CCCCC(CC)C(C)C(CCCCC(CCC)CCC)CC(CCC)CCC Chemical compound CCCCC(CC)C(C)C(CCCCC(CCC)CCC)CC(CCC)CCC HHMUQYPXZARAFI-UHFFFAOYSA-N 0.000 description 1
- OYPRJOBELJOOCE-UHFFFAOYSA-N Calcium Chemical compound [Ca] OYPRJOBELJOOCE-UHFFFAOYSA-N 0.000 description 1
- BPQQTUXANYXVAA-UHFFFAOYSA-N Orthosilicate Chemical compound [O-][Si]([O-])([O-])[O-] BPQQTUXANYXVAA-UHFFFAOYSA-N 0.000 description 1
- 239000004115 Sodium Silicate Substances 0.000 description 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 1
- 229910052782 aluminium Inorganic materials 0.000 description 1
- -1 aluminum and calcium Chemical class 0.000 description 1
- 239000012736 aqueous medium Substances 0.000 description 1
- 239000011575 calcium Substances 0.000 description 1
- 229910052791 calcium Inorganic materials 0.000 description 1
- 239000000919 ceramic Substances 0.000 description 1
- 230000005465 channeling Effects 0.000 description 1
- 238000005352 clarification Methods 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 238000000576 coating method Methods 0.000 description 1
- 238000007796 conventional method Methods 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 238000005520 cutting process Methods 0.000 description 1
- 239000008367 deionised water Substances 0.000 description 1
- 230000001627 detrimental effect Effects 0.000 description 1
- 239000003792 electrolyte Substances 0.000 description 1
- 230000001747 exhibiting effect Effects 0.000 description 1
- 239000004615 ingredient Substances 0.000 description 1
- PAZHGORSDKKUPI-UHFFFAOYSA-N lithium metasilicate Chemical compound [Li+].[Li+].[O-][Si]([O-])=O PAZHGORSDKKUPI-UHFFFAOYSA-N 0.000 description 1
- 229910052912 lithium silicate Inorganic materials 0.000 description 1
- 238000011068 loading method Methods 0.000 description 1
- 239000000203 mixture Substances 0.000 description 1
- 239000003973 paint Substances 0.000 description 1
- 239000000049 pigment Substances 0.000 description 1
- 229920001495 poly(sodium acrylate) polymer Polymers 0.000 description 1
- 229920000867 polyelectrolyte Polymers 0.000 description 1
- 238000011085 pressure filtration Methods 0.000 description 1
- 238000005086 pumping Methods 0.000 description 1
- 239000013049 sediment Substances 0.000 description 1
- 229910000029 sodium carbonate Inorganic materials 0.000 description 1
- 235000017550 sodium carbonate Nutrition 0.000 description 1
- JVBXVOWTABLYPX-UHFFFAOYSA-L sodium dithionite Chemical compound [Na+].[Na+].[O-]S(=O)S([O-])=O JVBXVOWTABLYPX-UHFFFAOYSA-L 0.000 description 1
- NNMHYFLPFNGQFZ-UHFFFAOYSA-M sodium polyacrylate Chemical compound [Na+].[O-]C(=O)C=C NNMHYFLPFNGQFZ-UHFFFAOYSA-M 0.000 description 1
- NTHWMYGWWRZVTN-UHFFFAOYSA-N sodium silicate Chemical compound [Na+].[Na+].[O-][Si]([O-])=O NTHWMYGWWRZVTN-UHFFFAOYSA-N 0.000 description 1
- 229910052911 sodium silicate Inorganic materials 0.000 description 1
- 239000007921 spray Substances 0.000 description 1
- 230000006641 stabilisation Effects 0.000 description 1
- 238000011105 stabilization Methods 0.000 description 1
- 238000003828 vacuum filtration Methods 0.000 description 1
- 238000005406 washing Methods 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B33/00—Clay-wares
- C04B33/02—Preparing or treating the raw materials individually or as batches
- C04B33/04—Clay; Kaolin
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/624—Sol-gel processing
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/62605—Treating the starting powders individually or as mixtures
- C04B35/62625—Wet mixtures
- C04B35/6263—Wet mixtures characterised by their solids loadings, i.e. the percentage of solids
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/62605—Treating the starting powders individually or as mixtures
- C04B35/62625—Wet mixtures
- C04B35/6264—Mixing media, e.g. organic solvents
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
- C04B35/632—Organic additives
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/40—Compounds of aluminium
- C09C1/42—Clays
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/20—Particle morphology extending in two dimensions, e.g. plate-like
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/51—Particles with a specific particle size distribution
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/54—Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/22—Rheological behaviour as dispersion, e.g. viscosity, sedimentation stability
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/40—Electric properties
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/80—Compositional purity
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
- C04B2235/54—Particle size related information
- C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
- C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
Definitions
- Disclosed herein are stabilized kaolin slurries and methods of making such stabilized kaolin slurries.
- Kaolin clay has many known applications in industry, including, for example, use as a filler in papermaking, a coating for paper, and a pigment in paint.
- Kaolin products are often shipped in a high solid slurry form. Slurries of coarse platy clays tend to settle quickly, making them difficult to transport.
- thickening agents such as carboxymethylcellulose (CMC)
- CMC carboxymethylcellulose
- the present disclosure relates to a stabilized kaolin slurry comprising:
- the stabilized kaolin slurry has a solids content of at least about 40%, and a 28-day pour test result of at least about 80% poured, such as at least 85% and further such as at least 89% poured.
- Such stabilized kaolin slurries are generally sufficiently stable to permit normal shipping and handling.
- the present disclosure relates to a method for making a stabilized kaolin slurry by reducing the levels of residual salts in a kaolin slurry, prior to addition of a conventional thickener or stabilizer such as carboxymethylcellulose (CMC) or the like.
- CMC carboxymethylcellulose
- the present inventors hypothesize that residual salts (electrolytes), such as aluminum and calcium, are released over a short period of time after slurry makedown. These residual salts are weakly absorbed by large kaolin particles because of their relatively large proportion of surface areas. Once released, the residual salts react with the stabilizer to reduce its efficacy and preventing effective slurry stabilization.
- one aspect of the present disclosure relates to a method of making a stabilized kaolin slurry, comprising:
- the conductivity of the kaolin after filtering and rinsing can be, for example, no more than about 100 ⁇ S, such as no more than about 80 ⁇ S, and even such as no more than about 60 ⁇ S.
- Another aspect of the present disclosure provides a method of stabilizing a kaolin slurry comprising:
- Another aspect of the present disclosure provides a method of stabilizing a kaolin slurry comprising:
- kaolin slurry having a solids content of greater than 40% and comprising no more than about 80% by weight of particles having an equivalent spherical diameter (ESD) of less than 2 microns;
- the pH can be adjusted to a value ranging from about 5.0 to about 6.0, or even from about 5.5 to about 6.0.
- slurries falling into these pH ranges can often be stabilized without addition of any stabilizer. It may, however, be necessary in some cases to add a small amount of a dispersant to adjust the viscosity of the partially stabilized slurry into a range suitable for pumping.
- ESD equivalent spherical diameter
- SEDIGRAPHTM instrument e.g., SEDIGRAPH 5100, obtained from Micromeritics Corporation, USA.
- a coarse and platy kaolin clay refers to, for example, a kaolin comprising no more than about 80% by weight of particles having an ESD of less than 2 microns, such as no more than about 70% by weight of particles having an ESD of less than 2 microns, further such as no more than about 60% by weight of particles having an ESD of less than 2 microns, even further such as no more than about 50% by weight of particles having an ESD of less than 2 microns, and even further such as no more than about 40% by weight of particles having an ESD of less than 2 microns.
- the coarse and platy kaolin clay refers to a kaolin comprising no more than about 50%, such as no more than about 40%, by weight of particles having an ESD of less than 2 microns.
- the coarse and platy kaolin clay refers to a kaolin comprising from about 20% to about 65% by weight, such as from about 25% to about 60% by weight, further such as from about 25% to about 45% by weight, and even further such as 35% by weight of particles having an ESD of less than 2 microns.
- the kaolin disclosed herein can have a shape factor of, for example, at least about 25, such as at least about 30 and further such as at least about 45.
- shape factor as used herein is a measure of an average value (on a weight average basis) of the ratio of mean particle diameter to particle thickness for a population of particles of varying size and shape as measured using the electrical conductivity method and apparatus described in GB-A-2240398/U.S. Pat. No. 5,128,606/EP-A-0528078, which are incorporated herein by reference in their entirety, and using the equations derived in these patent specifications.
- the stabilized kaolin slurry disclosed herein can have a solids content ranging from about 40% to about 60% by weight relative to the total weight of the slurry, such as from about 45% to about 55%, and further such as from about 50% to about 60% by weight relative to the total weight of the slurry.
- the stabilized kaolin slurry has a solids content of at least 40%, such as at least 45%, and further such as at least 50% by weight relative to the total weight of the slurry.
- Viscosity is a measure of a clay's resistance to changes in flow. Those having ordinary skill in the art are familiar with typical ways of measuring viscosity, which include, for example, Brookfield viscosity and Hercules viscosity.
- Brookfield viscometers provide a measure of a clay slurry's low shear viscosity, expressed in units of centipoise (cp).
- centipoise is equal to one centimeter-gram-second unit.
- One centipoise is one hundredth (10 ⁇ 2 ) of a poise.
- a 100 centipoise sample has a lower viscosity than a 500 centipoise sample.
- Hercules viscometers provide a measure of a clay slurry's high shear viscosity. Hercules viscosity is typically measured by placing a cylinder (bob) of appropriate diameter and length (typically the A-bob) into a sample clay slurry. Hercules viscosities of various samples can be compared by holding constant the percent solids concentration of the sample, the bob size, and the applied force. The Hercules viscometer applies a force to the bob which causes it to spin at a controlled accelerating rate. As the viscometer increases the bob spin rate, the viscous drag on the cup increases.
- Clay slurries with poor high shear rheology will exert the maximum measurable force on the cup at a lower bob rpm than clay slurries with “good” high shear rheology.
- Hercules viscosity is therefore typically expressed in terms of bob spin rates, or revolutions per minute (rpm) as a function of the relative applied force (dynes).
- rpm revolutions per minute
- a “dyne endpoint” is an indication of very low Hercules viscosity. A dyne endpoint is reached when the bob reaches its maximum rpm before the maximum measurable force is exerted on the cup.
- the stabilized kaolin slurry disclosed herein can have a Brookfield viscosity at 50% adjusted solids ranging, for example, from about 300 cps to about 700 cps as determined by a Brookfield model DV.1 digital viscometer using a #2 spindle at 20 rpm.
- the stabilized kaolin slurry can also have a Brookfield viscosity at 50% adjusted solids of, for example, at least about 400 cps as determined by a Brookfield model DV.1 digital viscometer using a #2 spindle at 20 rpm.
- the stabilized kaolin slurry has a Hercules viscosity at 50% adjusted solids of less than 10 dynes at 4400 rpm using an “A” bob.
- the stabilized kaolin slurry can have a pH ranging, for example, from about 5.5 to about 9.5, and further, for example, from about 6.5 to about 7.5.
- the pH can typically range from about 4.5 to about 7.5, such as from about 5.0 to about 6.5, further such as from about 5.0 to about 6.0, even further such as from about 5.5 to about 6.0, and even further such as from about 5.7 to about 5.8.
- the pour test can be used as an indicator of the long term stability of the kaolin slurries.
- a number of samples of the slurry are placed into beakers and weighed. At the selected time intervals, one of the beakers is upended and the sample is allowed to pour out for a period of 1 minute. The beaker is then re-weighed and the percentage of sample that successfully poured from the beaker is determined as a percentage of the total initial sample weight. Generally, the higher the pour-test percentage, the more stable the slurry against settling.
- the at least one stabilizer disclosed herein comprises, for example, at least one cellulosic thickener, such as CMC.
- the at least one cellulosic thickener can be chosen, for example, from alkyl celluloses, ethylhydroxyethyl celluloses, hydroxymethyl celluloses, hydroxyethyl celluloses, and hydroxypropyl celluloses.
- the at least one stabilizer disclosed herein can be chosen, for example, from montmorillonite, smectite clays, hydrophobically modified ethoxylated urethanes, high molecular weight polyacrylates, polyvinyl pyrrolidone, sodium alginate, xanthan gum, silica thickeners, sodium magnesium silicate, acrylic acid copolymers, and nonionic hydrophobically modified polyethers.
- the at least one stabilizer disclosed herein can be present in an amount ranging from about 0.01% to about 4% by weight, such as from about 0.01% to about 2% by weight, relative to the total weight of the slurry.
- the stabilized kaolin slurry disclosed herein is substantially free of any dispersant (i.e., comprising less than 100 ppm by weight of dispersant on a dry basis).
- the stabilized kaolin slurry disclosed herein further comprises at least one dispersant.
- the at least one dispersant is present in an amount of, for example, less than about 250 ppm on a dry basis, such as ranging from about 100 ppm to about 200 ppm by weight on a dry basis relative to the total weight of the slurry.
- the at least one dispersant is present in an amount from about 100 ppm to about 500 ppm by weight on a dry basis, relative to the total weight of the slurry.
- the at least one dispersant disclosed herein can comprise, for example, at least one polyelectrolyte chosen, for example, from polyacrylates and copolymers comprising at least one polyacrylate, polyphosphates, and silicates such as sodium silicate, lithium silicate, and ammonium silicate.
- the filtering and rinsing operation of a kaolin slurry by water to remove salt residue can be conducted by any conventional process known in the field.
- a lab ceramic filter funnel attached with a flask can be used for the filtering and rinsing operation, which simulates the filtering/dewatering action by a typical rotary vacuum filter.
- the top of the funnel has a shape of a large cup with a flat and porous bottom. Filter paper is placed on the porous bottom of the funnel cup. Slurry is poured into the cup.
- the flask attached below the funnel is connected to a vacuum pump that pulls the water through filter paper into the flask.
- a moisten cake of the kaolin forms in the cup. Additional water may then be poured into the cup one or more times to effect the rinsing operation.
- Other conventional dewatering methods that may be used in accordance with the present invention further include clarification, settling, centrifugal washing, rotary vacuum filtration and pressure filtration.
- a kaolin slurry is stabilized using the method disclosed herein and has a 28-day pour test result of at least 80% poured, such as at least 85% poured, and further such as at least 89% poured.
- substantially no dispersant is added to the kaolin slurry in the method disclosed herein.
- the method of making a stabilized kaolin slurry disclosed herein further comprises adding at least one dispersant.
- the at least one dispersant can be the same as described as above. It can be present in an amount ranging, for example, from about 100 ppm to about 200 ppm by weight, relative to the total weight of the slurry on a dry basis.
- the method of making a stabilized kaolin slurry disclosed herein can further comprise flocculating a kaolin slurry prior to the filtering and rinsing operation.
- the flocculation can be accomplished by any conventional process known in the field.
- the flocculation can be accomplished by lowering the pH of the kaolin slurry to a value of about 5 or less.
- the method of making a stabilized kaolin slurry can further comprise spray drying a kaolin slurry prior to the filtering and rinsing operation.
- the kaolin slurry comprises kaolin having no more than about 80% by weight particles having an ESD of less than 2 microns;
- a coarse platy kaolin clay having a particle size distribution such that about 56% by weight of the particles have an ESD of less than 2 microns and about 9% by weight of the particles have an ESD of less than 0.25 microns.
- This coarse platy kaolin clay was first spray-dried, and then subjected to one of the six methods as shown below—control, A, B, C, D, and E:
- the T-bar method was used to measure the vertical viscosity distribution of the samples, which changes as settling occurs over time. Typically, the viscosity of the top portion of a sample will decrease and that of the lower portion will increase as settling occurs. T-bar measurements are made using a Brookfield viscometer fitted with a Brookfield Helipath Stand and a special “T-bar” type spindle. The Helipath stand slowly raises or lowers the Brookfield viscometer so that the rotating shearing element of the T-bar spindle describes a helical path through the test sample. By always cutting into fresh material, the problems of channeling or separating are minimized. In the current example, samples can be considered fully settled when the upper T-bar viscosity approaches “0” cps and the lower approaches 400,000 cps. In the current example, monitoring of a given sample was terminated after a full settling measurement.
- the pour test method was also used to assess the long term stability of the kaolin slurries.
- a number of samples of the slurry were placed into beakers and weighed. At the selected time intervals, one of the beakers was upended and the sample was allowed to pour out for a period of 1 minute. The beaker was then re-weighed and the percentage of sample that successfully poured from the beaker was determined as a percentage of the total initial sample weight.
- the samples were then poured into a pint jar for a 28 day stability test in accordance with the procedures described below. The samples were tested for solids concentration, Brookfield viscosity at 20 rpm, pH, and Hercules viscosity before beginning the stability test.
- the stability test includes monitoring the viscosity of the slurry over a 28 day period using a T-bar spindle. Readings were taken at 7 day intervals and were read at about 1 ⁇ 2 inch from the top surface of the slurry for the upper reading and about 1 ⁇ 2 inch from the bottom for the lower reading. After 28 days, the weight percent of the slurry that poured out of the jar in 1 minute was measured and was designated as the first pour. The sample was returned to the jar and shaken for a few seconds and again poured out for 1 minute to obtain the weight percent of the slurry for the second pour. Brookfield viscosity and Hercules viscosity were then measured on this material.
- pH alone could be used to make a stable slurry from the coarse hydrous kaolin slurry.
- the pH may range from about 5.5 to about 6.0.
- the slurry solids should be maintained lower than about 50% in order to be fluid enough to pump easily.
- the addition of just 0.5 pounds per ton i.e., about 0.25 kilograms per ton
- results could be achieved when the polyacrylate was added after the soda ash or at the same time. Excessive shearing can also have a detrimental effect on the slurry solids. For example, a test that sheared the slurry for 30 minutes in a Waring blender reduced the solids of the final slurry from 57% to 54%.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Inorganic Chemistry (AREA)
- Dispersion Chemistry (AREA)
- Paper (AREA)
- Detergent Compositions (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Treatment Of Sludge (AREA)
- Preparation Of Clay, And Manufacture Of Mixtures Containing Clay Or Cement (AREA)
- Colloid Chemistry (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/573,709 US20070244243A1 (en) | 2004-08-16 | 2005-08-16 | Stabilized Kaolin Slurry and Methods for Improving Kaolin Slurry Stability |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US60161904P | 2004-08-16 | 2004-08-16 | |
US11/573,709 US20070244243A1 (en) | 2004-08-16 | 2005-08-16 | Stabilized Kaolin Slurry and Methods for Improving Kaolin Slurry Stability |
PCT/US2005/029062 WO2006023473A2 (en) | 2004-08-16 | 2005-08-16 | Stabilized kaolin slurry and methods for improving kaolin slurry stability |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2005/029062 A-371-Of-International WO2006023473A2 (en) | 2004-08-16 | 2005-08-16 | Stabilized kaolin slurry and methods for improving kaolin slurry stability |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/910,295 Division US8702860B2 (en) | 2004-08-16 | 2010-10-22 | Stabilized kaolin slurry and methods for improving kaolin slurry stability |
Publications (1)
Publication Number | Publication Date |
---|---|
US20070244243A1 true US20070244243A1 (en) | 2007-10-18 |
Family
ID=35429469
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/573,709 Abandoned US20070244243A1 (en) | 2004-08-16 | 2005-08-16 | Stabilized Kaolin Slurry and Methods for Improving Kaolin Slurry Stability |
US12/910,295 Expired - Fee Related US8702860B2 (en) | 2004-08-16 | 2010-10-22 | Stabilized kaolin slurry and methods for improving kaolin slurry stability |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/910,295 Expired - Fee Related US8702860B2 (en) | 2004-08-16 | 2010-10-22 | Stabilized kaolin slurry and methods for improving kaolin slurry stability |
Country Status (5)
Country | Link |
---|---|
US (2) | US20070244243A1 (de) |
EP (1) | EP1791916B1 (de) |
BR (1) | BRPI0514429A8 (de) |
ES (1) | ES2685774T3 (de) |
WO (1) | WO2006023473A2 (de) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BRPI0514429A8 (pt) | 2004-08-16 | 2018-04-24 | Imerys Pigments Inc | lama de caulim estabilizada, e, métodos para produzir uma lama de caulim estabilizada, para estabilizar uma lama de caulim, e para melhorar a estabilidade de uma lama de caulim |
Citations (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3130063A (en) * | 1961-03-23 | 1964-04-21 | Huber Corp J M | Stabilization of fluid suspensions of filler grade clay |
US4451440A (en) * | 1982-10-28 | 1984-05-29 | Georgia Kaolin Company, Inc. | Utilization of ion exchange resin in the processing of kaolins |
US4806167A (en) * | 1986-10-14 | 1989-02-21 | E.C.C. America Inc. | Kaolin aggregation using combination of organic and inorganic bases |
US4820554A (en) * | 1985-11-27 | 1989-04-11 | E.C.C. America Inc. | Coated paper and process |
US4849246A (en) * | 1985-10-09 | 1989-07-18 | Wolfgang Schmidt | Process for producing an administration or dosage form for drugs, reagents or other active ingredients |
US4859246A (en) * | 1987-04-21 | 1989-08-22 | Engelhard Corporation | Use of high molecular weight sulfonate as auxiliary dispersants for structured kaolins |
US5061461A (en) * | 1989-05-04 | 1991-10-29 | Engelhard Corporation | Cationic processing of kaolin ores |
US5082887A (en) * | 1989-12-29 | 1992-01-21 | Ecc American Inc. | Aggregated composite mineral pigments |
US5098583A (en) * | 1990-06-04 | 1992-03-24 | Ecc America Inc. | Method for producing high solids slurries of clay water products |
US5100472A (en) * | 1990-03-19 | 1992-03-31 | The Mead Corporation | Deionized clay and paper coatings containing the same |
US5128606A (en) * | 1990-01-22 | 1992-07-07 | Ecc International Limited | Aspect radio measurement |
US5151124A (en) * | 1990-06-04 | 1992-09-29 | Ecc America Inc. | Method for forming aggregated kaolin pigment |
US5227349A (en) * | 1989-09-20 | 1993-07-13 | Ecc International Inc. | Process for producing a kaolin clay product |
US5232881A (en) * | 1992-06-12 | 1993-08-03 | Engelhard Corporation | Use of surfactants in processing abrasive pigments |
US5236989A (en) * | 1989-12-29 | 1993-08-17 | Ecc International Inc. | Aggregated composite mineral pigments |
US20030141224A1 (en) * | 2001-09-14 | 2003-07-31 | Imerys Pigments, Inc. | Integrated process for simultaneous beneficiation, leaching, and dewatering of kaolin clay suspension |
US6616749B1 (en) * | 1998-04-04 | 2003-09-09 | Imerys Pigments, Inc. | Pigment products |
Family Cites Families (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3171718A (en) | 1962-02-16 | 1965-03-02 | Freeport Sulphur Co | Delaminated domestic sedimentary clay products and method of preparation thereof |
GB1498086A (en) | 1975-06-30 | 1978-01-18 | Yara Engineering Corp | High bulking clay pigments and methods of making same |
US4078941A (en) | 1976-12-06 | 1978-03-14 | Yara Engineering Corporation | High bulking calcined clay pigments and methods of making the same |
US4738726A (en) * | 1985-05-06 | 1988-04-19 | Engelhard Corporation | Treatment of clays with cationic polymers to prepare high bulking pigments |
JPH0739533B2 (ja) | 1986-12-10 | 1995-05-01 | ポリプラスチックス株式会社 | 液晶性ポリエステル樹脂組成物 |
JP3213630B2 (ja) | 1991-07-25 | 2001-10-02 | 三菱製紙株式会社 | インクジェット記録シート |
GB9405275D0 (en) | 1994-03-17 | 1994-04-27 | Ecc Int Ltd | Aqueous suspensions of inorganic materials |
US5925454A (en) | 1995-07-11 | 1999-07-20 | W.R. Grace & Co.-Conn. | Film having modified surface characteristics through use of combination of spherical and lamellar particulates |
WO2000059841A1 (en) | 1999-04-01 | 2000-10-12 | Imerys Pigments, Inc. | Kaolin clay pigments, their preparation and use |
WO2000066509A1 (en) | 1999-04-29 | 2000-11-09 | Imerys Pigments, Inc. | Pigment composition for paper coating, paper coating using the same and method of coating paper |
WO2000066510A1 (en) | 1999-04-29 | 2000-11-09 | Imerys Pigments, Inc. | Pigment composition for employment in paper coating and coating composition and method employing the same |
GB0020179D0 (en) | 2000-08-17 | 2000-10-04 | Imerys Minerals Ltd | Kaolin products and their use |
US6610136B2 (en) * | 2001-04-03 | 2003-08-26 | Thiele Kaolin Company | Pigments for ink jet paper |
US20030085012A1 (en) * | 2001-09-07 | 2003-05-08 | Jones J Philip E | Hyperplaty clays and their use in paper coating and filling, methods for making same, and paper products having improved brightness |
BRPI0514429A8 (pt) | 2004-08-16 | 2018-04-24 | Imerys Pigments Inc | lama de caulim estabilizada, e, métodos para produzir uma lama de caulim estabilizada, para estabilizar uma lama de caulim, e para melhorar a estabilidade de uma lama de caulim |
-
2005
- 2005-08-16 BR BRPI0514429A patent/BRPI0514429A8/pt not_active Application Discontinuation
- 2005-08-16 US US11/573,709 patent/US20070244243A1/en not_active Abandoned
- 2005-08-16 WO PCT/US2005/029062 patent/WO2006023473A2/en active Application Filing
- 2005-08-16 ES ES05786678.2T patent/ES2685774T3/es active Active
- 2005-08-16 EP EP05786678.2A patent/EP1791916B1/de not_active Not-in-force
-
2010
- 2010-10-22 US US12/910,295 patent/US8702860B2/en not_active Expired - Fee Related
Patent Citations (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3130063A (en) * | 1961-03-23 | 1964-04-21 | Huber Corp J M | Stabilization of fluid suspensions of filler grade clay |
US4451440A (en) * | 1982-10-28 | 1984-05-29 | Georgia Kaolin Company, Inc. | Utilization of ion exchange resin in the processing of kaolins |
US4849246A (en) * | 1985-10-09 | 1989-07-18 | Wolfgang Schmidt | Process for producing an administration or dosage form for drugs, reagents or other active ingredients |
US4820554A (en) * | 1985-11-27 | 1989-04-11 | E.C.C. America Inc. | Coated paper and process |
US4806167A (en) * | 1986-10-14 | 1989-02-21 | E.C.C. America Inc. | Kaolin aggregation using combination of organic and inorganic bases |
US4859246A (en) * | 1987-04-21 | 1989-08-22 | Engelhard Corporation | Use of high molecular weight sulfonate as auxiliary dispersants for structured kaolins |
US5061461A (en) * | 1989-05-04 | 1991-10-29 | Engelhard Corporation | Cationic processing of kaolin ores |
US5227349A (en) * | 1989-09-20 | 1993-07-13 | Ecc International Inc. | Process for producing a kaolin clay product |
US5082887A (en) * | 1989-12-29 | 1992-01-21 | Ecc American Inc. | Aggregated composite mineral pigments |
US5236989A (en) * | 1989-12-29 | 1993-08-17 | Ecc International Inc. | Aggregated composite mineral pigments |
US5128606A (en) * | 1990-01-22 | 1992-07-07 | Ecc International Limited | Aspect radio measurement |
US5100472A (en) * | 1990-03-19 | 1992-03-31 | The Mead Corporation | Deionized clay and paper coatings containing the same |
US5098583A (en) * | 1990-06-04 | 1992-03-24 | Ecc America Inc. | Method for producing high solids slurries of clay water products |
US5151124A (en) * | 1990-06-04 | 1992-09-29 | Ecc America Inc. | Method for forming aggregated kaolin pigment |
US5232881A (en) * | 1992-06-12 | 1993-08-03 | Engelhard Corporation | Use of surfactants in processing abrasive pigments |
US6616749B1 (en) * | 1998-04-04 | 2003-09-09 | Imerys Pigments, Inc. | Pigment products |
US20030141224A1 (en) * | 2001-09-14 | 2003-07-31 | Imerys Pigments, Inc. | Integrated process for simultaneous beneficiation, leaching, and dewatering of kaolin clay suspension |
US7122080B2 (en) * | 2001-09-14 | 2006-10-17 | Imerys Pigments, Inc. | Integrated process for simultaneous beneficiation, leaching, and dewatering of kaolin clay suspension |
Also Published As
Publication number | Publication date |
---|---|
EP1791916A2 (de) | 2007-06-06 |
ES2685774T3 (es) | 2018-10-11 |
WO2006023473A2 (en) | 2006-03-02 |
BRPI0514429A (pt) | 2008-06-10 |
BRPI0514429A8 (pt) | 2018-04-24 |
US8702860B2 (en) | 2014-04-22 |
WO2006023473A3 (en) | 2007-09-27 |
EP1791916B1 (de) | 2018-05-30 |
US20110155018A1 (en) | 2011-06-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP0382427B1 (de) | Kationische dispergierte Schlämme von calciniertem Kaolinton | |
US4772332A (en) | Use of mixture of high molecular weight sulfonates as auxiliary dispersant for structured kaolins | |
SE435804B (sv) | Sett att pulverisera ett fast material innefattande kalciumkarbonat | |
US4880759A (en) | Ball clay slurry | |
US3130063A (en) | Stabilization of fluid suspensions of filler grade clay | |
KR102166716B1 (ko) | 유용한 칼코-마그네시아 현탁액 | |
EA022621B1 (ru) | Водная суспензия аморфного кремнезема и способ ее производства | |
US5537934A (en) | Cationically stabilized slurries of calcined kaolin clay | |
US4812427A (en) | Clay slurry | |
US8702860B2 (en) | Stabilized kaolin slurry and methods for improving kaolin slurry stability | |
DE3877940T2 (de) | Kaolinbrei, seine herstellung und dafuer geeignetes dispergierungsmittel. | |
US7105466B2 (en) | Siliceous clay slurry | |
US2995458A (en) | Reducing dilatancy of clays | |
WO2008077877A2 (en) | Method for processing crude bentonite | |
WO2005028395A1 (en) | Stabilized slurry composition and method of making the same | |
US8206680B2 (en) | Calco-magnesian aqueous suspension and method for the production thereof | |
WO2010080453A2 (en) | Methods for stabilizing hydrous kaolin | |
KR101492547B1 (ko) | 탄산칼슘 포함 물질의 수성 현탁액 내의 첨가제로서의 2-아미노에탄올의 용도 | |
US20070054797A1 (en) | Siliceous clay slurry | |
Nettleship et al. | Aggregation of clay in the hydrometer test | |
KR101553103B1 (ko) | 탄산칼슘 함유 물질의 수성 현탁액에서 첨가제로서의 2-((1-메틸프로필))아미노에탄올의 용도 | |
WO2020210215A1 (en) | Anti-tack formulation of high solids content, diluted anti-tack formulation and method of use of diluted anti-tack formulation | |
US7091148B2 (en) | Silicious clay slurry | |
DE3210480C2 (de) | Verfahren zur Herstellung von Zeolithaufschlämmungen mit guter statischer und dynamischer Stabilität | |
JPH054927B2 (de) |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: IMERYS PIGMENTS, INC., GEORGIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YUAN, JUN;PRUETT, ROBERT;GARSKA, MIKE (MICHAEL);REEL/FRAME:018889/0343;SIGNING DATES FROM 20041007 TO 20041027 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |